CA1174225A - Components and catalysts for the polymerization of olefines - Google Patents
Components and catalysts for the polymerization of olefinesInfo
- Publication number
- CA1174225A CA1174225A CA000383709A CA383709A CA1174225A CA 1174225 A CA1174225 A CA 1174225A CA 000383709 A CA000383709 A CA 000383709A CA 383709 A CA383709 A CA 383709A CA 1174225 A CA1174225 A CA 1174225A
- Authority
- CA
- Canada
- Prior art keywords
- compound
- dihalide
- polymerization
- component
- supported
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired
Abstract
ABSTRACT OF DISCLOSURE
Catalyst-forming components and catalysts for the polymerization of olefins based on said components are dis-closed. The catalysts comprise the reaction product of:
(a) an Al alkyl compound;
(b) a silicon compound containing at least one Si-OR or Si-OCOR or Si-NR2 bond, R being a hydrocarbyl radical; and (c) a solid comprising, as essential support, a Mg dihalide in active form and, supported thereon, a Ti halide or a halo-Ti-alcoholate or said halogenated Ti compound and a silicon compound as defined in (b) in a molar ratio with the supported Ti compound from 1.0 mole to 5 moles of silicon compound per mole of Ti compound.
Catalyst-forming components and catalysts for the polymerization of olefins based on said components are dis-closed. The catalysts comprise the reaction product of:
(a) an Al alkyl compound;
(b) a silicon compound containing at least one Si-OR or Si-OCOR or Si-NR2 bond, R being a hydrocarbyl radical; and (c) a solid comprising, as essential support, a Mg dihalide in active form and, supported thereon, a Ti halide or a halo-Ti-alcoholate or said halogenated Ti compound and a silicon compound as defined in (b) in a molar ratio with the supported Ti compound from 1.0 mole to 5 moles of silicon compound per mole of Ti compound.
Description
~ ~74225 ., .
, . .. . . . . . . ......... . _ .. .... . . . . . . . .. . . . . .
DESCRIPTION
The present invention refers to new supported com-ponents of catalysts for the polymerization of CH2=CHR olefins wherein R is an alkyl radical with 1 to 4 carbon atoms, or an aryl radical, and mixtures of said olefins with ethylene, and to the catalysts obtained from said components.
, .
.
, ~ 17422~
BACKGROUND OF THE INVENTION
The supported highly active and highly stereospecifie catalysts for the polymerization of propylene and higher olefins known up to now are obtained by the reaetion of an Al alkyl compound partially complexed with an electron-donor compound (outside donor) with a solid component comprising a Ti compound and an electron-donor compound (inside donor) supported on a Mg dihalide in active form.
Examples of such catalysts have been described in lQ British Patent No. 1,559,194 and Belgian Patent No. 868,682.
Those supported catalysts require the use of an inside donor in order to obtaln polymers having a high isotactie index. If the inside donor is omitted, polymers having a low isotactic index are obtained.
THE PRESENT INVENTION
One object of this invention is to provide catalyst components which comprise a silicon compound as defined herein-above and which yield catalysts that polymerize the alpha-olefins to high yields of polymers having a high isotacticity index.
This and other objects are achieved by the present invention in accordance with which it has been found, unex-pectedly, that it is possible to obtain, with high yield, polymers of alpha-olefins having a high isotactic index by using Ti-containing Mg dihalides-supported catalysts free from inside electron-donor compounds, iE an outside donor is used which is a silicon compound containing Si-OR, Si-oCoR or Si-NR2 bonds.
~ ~74225 It has also been found,even more unexpectedly, that the activity and stereospecificity of the catalysts can be further increased if the silicon compound used as outside donor is present as inside donor also in the Ti-containing Mg dihalide-supported component in amounts corresponding to molar ratios between the silicon compound and the supported halo-genated Ti- compound comprised between 0.1 and 5.
The above results are surprising if one considers that catalysts are known which are prepared by using, as both inside and outside donor, a silicon compound containing Si-O-C
bonds and the activity and stereospecificity of which are not -increased over the activlty and stereospecificity obtainable with catalysts in which an ester of benzoic acid is used as inside and outside donor.
. 15 The rather poor performance of the above prior art catalysts is due to the fact that the Si-containing inside donor is substantially removed from the Ti-containing supported component as a result of the method by which said component is prepared.
The catalysts of this invention comprise the product of the reaction between the following components:
; (a) an Al trialkyl or Al alkyl compound containing 2 or more aluminum atoms linked to each other through oxygen or nitrogen atoms or through SO4 or SO3 groups;
(b) a silicon compound containing one or more Si-OR
Si-OCOR or Si-NR2 bonds (R being a hydrocarbyl radical); and (c) a solid comprising, as essential suppor-t, an anhydrous Mg dihalide in the active form as defined infra and, supported on said dihalide, a . .
~3--.. . . .
~ ~74225 .
Ti halide or Ti haloalcoholate, or the solid (c) containing supported therein also a silicon com-pound as defined in (b) in an amount corres-ponding to a molar ratio between the supported silicon compound and the supported halogenated Ti compound comprised between 0.1 and 5.
The active anhydrous Mg dihalides forming the essential support of component (c) are the Mg dihalides showing in the X-rays powder spectrum of component (c) a braodening of at least 30% of the most intense diffraction line which appears in the powder spectrum of the corresponding dihalide having 1 m /g of surface area, or are the Mg dihalides showing an X-rays powder soectrum in which said most intense diffraction line is replaced by a halo with the intensity peak shifted with respect to the interplanar distance of the most intense line;
and/or are the Mg dihalides having a surface area greater than 3 m /g-The measurement of the surface area of the Mg dihalides is made on component (c) after treatment with boiling TiC14 for 2 hours. The found value is considered as surface area of the Mg dihalide.
Very active forms of Mg dihalides are those givinq an X-rays powder spectrum in which the most intense diffraction ' line appearing in the spectrum of the corresponding halide having 1 m /g of surface area is decreased in relative intensity and broadened to form a halo, or are those in which said most intense line is replaced by a halo having its intensity peak shifted with respect to the interplanar distance of the most intense line. Generally, the surface area of the above forms is higher than 30-40 m /g and is comprised in particular between ~00-300 m2/g.
~ 174225 Active forms are also those deriving from the above forms by heat-treatment in inert hydrocarbon solvents and showing, in the X-rays spectrum,sharp diffraction lines in place of the hal~os.
The shilrp, most intense line of these forms shows a broadening of at least 30% with respect to the corresponding line of the Mg dihalide having 1 m /g of surface area.
Prefer~ed Mg dihalides are Mg dichloride and Mg dibromide. The content in water of the dihalides is generally less than 1% by ~eight.
By Ti halides or Ti haloalcoholates and esters supported on the active Mg dihalide is meant the above compounds which may be chemically or physically fixed on the support, and not extractable from component (c) by treatment of the same with boiling 1,2-dichloroethane for 2 hours.
Components (a), (b) and (c) are made to react with each other in any order; preferably, however, components (a~
and (b) are premixed before being contacted with component (c).
The pre-mixing of (a) and (b) is conducted at -tem-peratures comprised, usually, between room temperature and the temperature used in the polymerization process.
The pre-reaction of (c) and (b) may be carried out also at-higher temperatures. Also, compound (b) may be incor-porated and made to react with component (c) itself. Component (b) is made to react in a molar ratio with respect to the halogenated Ti compound supported on component (c) of at least 1 and in a molar ratio with respect to the Al alkyl compound used as component (a) of less than 20 and preferably comprised between 0.05 and 0.3.
In component (c), the molar ratio between the Mq ' dihallde and the halogenated Ti compound supported therein is , ., 1 17~225 .
comprised between 1 and 500 and the molar ratio between sald halogenated Ti compound and the electron-donor supported on the Mg dihalide is comprised between 0.1 and 50.
The silicon compounds set forth in (b) include compounds of general formula:
RmSiY~lXp wherein:
R is an alkyl, alkenyl, aryl, arylalkyl or cycloalkyl - radical with from 1 to 20 carbon atoms;
Y is an -OR', -OCOR', -NR' 2 group wherein R', either equal to or different from R, has the same meaning as R;
X is either a halogen or hydrogen atom or an -OCOR"
or -NR"2 group wherein R", either equal to or different from R', has the same meaning as R';
m, .n and p are numbers comprised, respectively, between: 0 and 3 for m, 1 and 4 for n and 0 and 1 for p; and m + n + p is equal to 4.
Other silicon compounds that may be used are compounds in which two or more silicon atoms are bound to each other -through oxygen or nitrogen atoms.
Examples of these compounds are hexaethoxydisiloxane and symmetrical diphenyltetraethoxydisiloxane:
(C H O~ -Si-O-CH -CH2 O-Si-(OC2H5)2 Preferred silicon compounds are: phenylalkoxysilanes such as phenyltriethoxy or trimethoxysilane, diphenyldimethoxy and diethoxysilane, monochlorophenyldiethoxysilane; alkyl-alkoxysilanes as, e.g., ethyltriethoxysilane and ethyltri--isopropoxysilane.
.
.
~ 174225 Examples of other suitable compounds are: chloro-triethoxysilane, acetoxytriethoxysilane, vinyltriethoxysilane, butyltriethoxysiiane, triphenylmonoethoxysilane, phenyltri-cycloethoxysilane, phenyldiethoxydiethylaminosilane, tetra-phenoxysilane and tetralkoxysilanes such as tetramethoxysilane.
The silicon compound can be also formed in situ by reaction of, for instance, a halogenated silicon compound such as SiC14 with an alcohol or an alcoholate of Mg or Al.
In the catalysts of the invention the silicon com-pound i5 present in a combined form in the solid product of the reaction between the various catalyst-forming components, in a molar ratio between the silicon compound and the halogenated Ti compound greater than 0.05 and generally comprised between 0.1 and 5.
The Al alkyl compounds forming component (a) include Al trialkyls as, for instance, Al triethyl, Al triisobutyl, Al triisopropyl, and compounds containing two or more Al atoms linked to each other through hetero-atoms as:
(C2H5)2Al-0-Al(C2H5)2, (C2H5)2Al-l_Al(C2H5)2, and (C2H5)2Al-O-ll-O-Al(c2H5)2 As indicated, Al alkyl compounds in which Al atoms are linked through groups such as SO4 or SO3 are also suitable.
The Al alkyl compounds may be used in mixture with Al alkyl halides, e.g., AlEt2Cl.
Component (c) is prepared according to various methods, one of which, and also one of the preferred methods, consists in co-milling the Mg dihalide, the Ti halide or Ti haloalcoholate and the ~silicon compound when it is used, until appearance in the X-rays spectrum of the milled product of the modiEications above set forth for the spectrum of the Mg . . -7-~ 174225 dihalide and in heat-treating the milled product in suspension in a halogenated hydrocarbon as, e.g., 1,2 dichloroethane, separating the solid product and washing it with heptane or a similar hydrocarbon solvent. The duration of the treatment is generally comprised between 1 and 4 hours and depends on the temperature of treatment.
According to another method, an adduct between a Mg dihalide and an alcohol is reacted with TiC13. The reactions are described in Belgian patent 868,682 and published German patent No. 3,022,738.
In all the above methods, -the final product contains a Mg dihalide, present in the active form as set forth supra.
Other known methods which lead to the formation of Mg dihalide in active form or to Ti-containing Mg dihalide supported components, in which the dihalide is present in active form, are based on the following reactions:
reaction of a Grignard reagent or a MgR2 compound (R being a hydrocarbyl radical) or complexes of said MgR2 compounds with Al trialkyls, with halogenating agents as AlX3 or AlRmXn compounds (X is halogen, R is a hydrocarbyl, m + n = 3, SiC14 or HSiC13;
reaction of a Grignard reagent with a silanol or polysiloxane, H2O or with an alcohol and further reaction with a halogenating agent, or with TiC14;
reaction of Mg with an alcohol and a halogenhydric acid, or of Mg with a hydrocarbyl halide and an alcohol;
reaction of MgO with C12 or AlC13;
reaction of MgX2.nH2O (X = halogen) with a halogen-ating agent or TiC14;
reaction of Mg mono or dialcoholates or Mg carboxy-lates with a halogenating agent.
.
~ 174225 The Ti halides or Ti halogenalcoholates include, in particular, the Ti tetrahalides, Ti trihalides and Ti trihalogenalcoholates. Preferred compounds are: TiCl4, TiBr4,
, . .. . . . . . . ......... . _ .. .... . . . . . . . .. . . . . .
DESCRIPTION
The present invention refers to new supported com-ponents of catalysts for the polymerization of CH2=CHR olefins wherein R is an alkyl radical with 1 to 4 carbon atoms, or an aryl radical, and mixtures of said olefins with ethylene, and to the catalysts obtained from said components.
, .
.
, ~ 17422~
BACKGROUND OF THE INVENTION
The supported highly active and highly stereospecifie catalysts for the polymerization of propylene and higher olefins known up to now are obtained by the reaetion of an Al alkyl compound partially complexed with an electron-donor compound (outside donor) with a solid component comprising a Ti compound and an electron-donor compound (inside donor) supported on a Mg dihalide in active form.
Examples of such catalysts have been described in lQ British Patent No. 1,559,194 and Belgian Patent No. 868,682.
Those supported catalysts require the use of an inside donor in order to obtaln polymers having a high isotactie index. If the inside donor is omitted, polymers having a low isotactic index are obtained.
THE PRESENT INVENTION
One object of this invention is to provide catalyst components which comprise a silicon compound as defined herein-above and which yield catalysts that polymerize the alpha-olefins to high yields of polymers having a high isotacticity index.
This and other objects are achieved by the present invention in accordance with which it has been found, unex-pectedly, that it is possible to obtain, with high yield, polymers of alpha-olefins having a high isotactic index by using Ti-containing Mg dihalides-supported catalysts free from inside electron-donor compounds, iE an outside donor is used which is a silicon compound containing Si-OR, Si-oCoR or Si-NR2 bonds.
~ ~74225 It has also been found,even more unexpectedly, that the activity and stereospecificity of the catalysts can be further increased if the silicon compound used as outside donor is present as inside donor also in the Ti-containing Mg dihalide-supported component in amounts corresponding to molar ratios between the silicon compound and the supported halo-genated Ti- compound comprised between 0.1 and 5.
The above results are surprising if one considers that catalysts are known which are prepared by using, as both inside and outside donor, a silicon compound containing Si-O-C
bonds and the activity and stereospecificity of which are not -increased over the activlty and stereospecificity obtainable with catalysts in which an ester of benzoic acid is used as inside and outside donor.
. 15 The rather poor performance of the above prior art catalysts is due to the fact that the Si-containing inside donor is substantially removed from the Ti-containing supported component as a result of the method by which said component is prepared.
The catalysts of this invention comprise the product of the reaction between the following components:
; (a) an Al trialkyl or Al alkyl compound containing 2 or more aluminum atoms linked to each other through oxygen or nitrogen atoms or through SO4 or SO3 groups;
(b) a silicon compound containing one or more Si-OR
Si-OCOR or Si-NR2 bonds (R being a hydrocarbyl radical); and (c) a solid comprising, as essential suppor-t, an anhydrous Mg dihalide in the active form as defined infra and, supported on said dihalide, a . .
~3--.. . . .
~ ~74225 .
Ti halide or Ti haloalcoholate, or the solid (c) containing supported therein also a silicon com-pound as defined in (b) in an amount corres-ponding to a molar ratio between the supported silicon compound and the supported halogenated Ti compound comprised between 0.1 and 5.
The active anhydrous Mg dihalides forming the essential support of component (c) are the Mg dihalides showing in the X-rays powder spectrum of component (c) a braodening of at least 30% of the most intense diffraction line which appears in the powder spectrum of the corresponding dihalide having 1 m /g of surface area, or are the Mg dihalides showing an X-rays powder soectrum in which said most intense diffraction line is replaced by a halo with the intensity peak shifted with respect to the interplanar distance of the most intense line;
and/or are the Mg dihalides having a surface area greater than 3 m /g-The measurement of the surface area of the Mg dihalides is made on component (c) after treatment with boiling TiC14 for 2 hours. The found value is considered as surface area of the Mg dihalide.
Very active forms of Mg dihalides are those givinq an X-rays powder spectrum in which the most intense diffraction ' line appearing in the spectrum of the corresponding halide having 1 m /g of surface area is decreased in relative intensity and broadened to form a halo, or are those in which said most intense line is replaced by a halo having its intensity peak shifted with respect to the interplanar distance of the most intense line. Generally, the surface area of the above forms is higher than 30-40 m /g and is comprised in particular between ~00-300 m2/g.
~ 174225 Active forms are also those deriving from the above forms by heat-treatment in inert hydrocarbon solvents and showing, in the X-rays spectrum,sharp diffraction lines in place of the hal~os.
The shilrp, most intense line of these forms shows a broadening of at least 30% with respect to the corresponding line of the Mg dihalide having 1 m /g of surface area.
Prefer~ed Mg dihalides are Mg dichloride and Mg dibromide. The content in water of the dihalides is generally less than 1% by ~eight.
By Ti halides or Ti haloalcoholates and esters supported on the active Mg dihalide is meant the above compounds which may be chemically or physically fixed on the support, and not extractable from component (c) by treatment of the same with boiling 1,2-dichloroethane for 2 hours.
Components (a), (b) and (c) are made to react with each other in any order; preferably, however, components (a~
and (b) are premixed before being contacted with component (c).
The pre-mixing of (a) and (b) is conducted at -tem-peratures comprised, usually, between room temperature and the temperature used in the polymerization process.
The pre-reaction of (c) and (b) may be carried out also at-higher temperatures. Also, compound (b) may be incor-porated and made to react with component (c) itself. Component (b) is made to react in a molar ratio with respect to the halogenated Ti compound supported on component (c) of at least 1 and in a molar ratio with respect to the Al alkyl compound used as component (a) of less than 20 and preferably comprised between 0.05 and 0.3.
In component (c), the molar ratio between the Mq ' dihallde and the halogenated Ti compound supported therein is , ., 1 17~225 .
comprised between 1 and 500 and the molar ratio between sald halogenated Ti compound and the electron-donor supported on the Mg dihalide is comprised between 0.1 and 50.
The silicon compounds set forth in (b) include compounds of general formula:
RmSiY~lXp wherein:
R is an alkyl, alkenyl, aryl, arylalkyl or cycloalkyl - radical with from 1 to 20 carbon atoms;
Y is an -OR', -OCOR', -NR' 2 group wherein R', either equal to or different from R, has the same meaning as R;
X is either a halogen or hydrogen atom or an -OCOR"
or -NR"2 group wherein R", either equal to or different from R', has the same meaning as R';
m, .n and p are numbers comprised, respectively, between: 0 and 3 for m, 1 and 4 for n and 0 and 1 for p; and m + n + p is equal to 4.
Other silicon compounds that may be used are compounds in which two or more silicon atoms are bound to each other -through oxygen or nitrogen atoms.
Examples of these compounds are hexaethoxydisiloxane and symmetrical diphenyltetraethoxydisiloxane:
(C H O~ -Si-O-CH -CH2 O-Si-(OC2H5)2 Preferred silicon compounds are: phenylalkoxysilanes such as phenyltriethoxy or trimethoxysilane, diphenyldimethoxy and diethoxysilane, monochlorophenyldiethoxysilane; alkyl-alkoxysilanes as, e.g., ethyltriethoxysilane and ethyltri--isopropoxysilane.
.
.
~ 174225 Examples of other suitable compounds are: chloro-triethoxysilane, acetoxytriethoxysilane, vinyltriethoxysilane, butyltriethoxysiiane, triphenylmonoethoxysilane, phenyltri-cycloethoxysilane, phenyldiethoxydiethylaminosilane, tetra-phenoxysilane and tetralkoxysilanes such as tetramethoxysilane.
The silicon compound can be also formed in situ by reaction of, for instance, a halogenated silicon compound such as SiC14 with an alcohol or an alcoholate of Mg or Al.
In the catalysts of the invention the silicon com-pound i5 present in a combined form in the solid product of the reaction between the various catalyst-forming components, in a molar ratio between the silicon compound and the halogenated Ti compound greater than 0.05 and generally comprised between 0.1 and 5.
The Al alkyl compounds forming component (a) include Al trialkyls as, for instance, Al triethyl, Al triisobutyl, Al triisopropyl, and compounds containing two or more Al atoms linked to each other through hetero-atoms as:
(C2H5)2Al-0-Al(C2H5)2, (C2H5)2Al-l_Al(C2H5)2, and (C2H5)2Al-O-ll-O-Al(c2H5)2 As indicated, Al alkyl compounds in which Al atoms are linked through groups such as SO4 or SO3 are also suitable.
The Al alkyl compounds may be used in mixture with Al alkyl halides, e.g., AlEt2Cl.
Component (c) is prepared according to various methods, one of which, and also one of the preferred methods, consists in co-milling the Mg dihalide, the Ti halide or Ti haloalcoholate and the ~silicon compound when it is used, until appearance in the X-rays spectrum of the milled product of the modiEications above set forth for the spectrum of the Mg . . -7-~ 174225 dihalide and in heat-treating the milled product in suspension in a halogenated hydrocarbon as, e.g., 1,2 dichloroethane, separating the solid product and washing it with heptane or a similar hydrocarbon solvent. The duration of the treatment is generally comprised between 1 and 4 hours and depends on the temperature of treatment.
According to another method, an adduct between a Mg dihalide and an alcohol is reacted with TiC13. The reactions are described in Belgian patent 868,682 and published German patent No. 3,022,738.
In all the above methods, -the final product contains a Mg dihalide, present in the active form as set forth supra.
Other known methods which lead to the formation of Mg dihalide in active form or to Ti-containing Mg dihalide supported components, in which the dihalide is present in active form, are based on the following reactions:
reaction of a Grignard reagent or a MgR2 compound (R being a hydrocarbyl radical) or complexes of said MgR2 compounds with Al trialkyls, with halogenating agents as AlX3 or AlRmXn compounds (X is halogen, R is a hydrocarbyl, m + n = 3, SiC14 or HSiC13;
reaction of a Grignard reagent with a silanol or polysiloxane, H2O or with an alcohol and further reaction with a halogenating agent, or with TiC14;
reaction of Mg with an alcohol and a halogenhydric acid, or of Mg with a hydrocarbyl halide and an alcohol;
reaction of MgO with C12 or AlC13;
reaction of MgX2.nH2O (X = halogen) with a halogen-ating agent or TiC14;
reaction of Mg mono or dialcoholates or Mg carboxy-lates with a halogenating agent.
.
~ 174225 The Ti halides or Ti halogenalcoholates include, in particular, the Ti tetrahalides, Ti trihalides and Ti trihalogenalcoholates. Preferred compounds are: TiCl4, TiBr4,
2,6-dimethylphenoxytrichlorotitanium.
The Ti trihalides are obtained according to known methods, for instance by reduction of TiC14 with Al or an organometallic Al compound or~with hydrogen.
In the case of Ti trihalides, it may be convenient, for the purpose oE improving the performance of the catalysts, to carry out an oxidization, even if partial, of the titanium, either during or after the preparation of component (c). To this purpose there may be used halogens, iodine halides.
Preferred catalysts are those in which: component (c) is obtained from MgCl2, TiCl4 a silicon compound selected from the groups of phenyl or ethyltriethoxysilane or diphenyl-dime-thoxy or diethoxysilane, and Component (a) is an Al trialkyl, such as Al triethyl or Al triisobutyl.
One of the preferred methods of preparing component (c) consists in co-milling MgCl2, TiC14 and the silicon com-pound and in treating the milled product with a halogenated hydrocarbon such as, for instance, 1,2-dichloroethane.
The ca-talysts according to this invention are used to polymerize the alpha-o].efins according to known methods, that is, by carrying out the polymeriza-tion in a liquid phase, either in the presence or absence of an inert hydrocarbon solvent, or in gas phase or by combining, for instance, a liquid phase polymerization step with a gas phase step.
In general, the polymerization temperature is com-prised between 40 and 160C, but preferably between 60 and .
_9_ ~ 17~225 90C, operating either at atmospheric or at yreater than atmospheric pressure.
~s a molecular weight regulator hydrogen or other regulators of known type are used.
The catalysts are particularly suitable Eor poly-merizing propylene, butene-l, styrene and 4-methylpentene. The catalysts may also be used acoording to known methods to polymerize mixtures of propylene and ethylene to Eorm modified polypropylenes having improved shock-resistance at low temperatures (the so called block copolymers of propylene and ethylene) or to obtain random crystalline copolymers of propylene with m1nor proportions of ethylene.
` The following examples are given for merely illus-trative purposes and are not intended to be in any way limiting of the scope of the invention.
Into an inox steel autoclave of 2000 ml holding capacity, e~uipped with a magnetized stirrer and a thermometer, heat stabilized at 60C and kept under pressure by a nitrogen atmosphere, there were introduced 5 m moles of triethyl-aluminum, l.5 m moles oE phenyltriethoxysilane, the solid catalytic component obtained by reacting TiCl4 with MgCl2.2.3C2H~OH, operating under the same conditions described in Example l of Belyian patent No. 868,682 and 700 ml of degassed and anhydrous n-heptane, while propylene was also fed in.
The catalytic component thus prepared showed an X-rays powder spectrum in which the most intense diffraction line appearing in the spectrum of MgCl2 having l m2/g of ~ 17~225 surface area was decreased in relative intensity and broadened to form a halo.
Thereupon there was fed in 0 2 atm of hydrogen and then the whole was rapidly heated up to 70C, while contem-poraneously further propylene was fed in to reach a total pres~
sure of 7 atm. This latter pressure was maintained constant ~throughout the polymerization by feeding in the monomer.
After 4 hours, the polymerization was interrupted, the polymer was isolated by filtering and then was dried. The quantity of polymer dissolved in the filtrate was thereupon isolated, weighed and summed to the polymer soluble in boiling n-heptane, for calculation of the isotacticity index.
The quantity of catalytic component used and the content of Ti in said component, the yield in polymer with respect to the introduced Ti, the isotacticity index (I.I.) and the inherent viscosity determined in tetralin at 35C, are all reported in Table I.
Example I was repeated but using a so]id catalytic component prepared as follows:
Anhydrous MgC12, phenyltriethoxysilane in molar ratio Mg/Si of 6, and TiCl~ in molar ratio of 1:1 with respect to the phenyltriethoxysilane were co-milled in a vibrating miil of the ~ type VIBRATOM manufactured by N.V. Tema's, Gravenhage, Holland, having a total volume or one liter and containing 3 kg of stainless steel balls of 16 mm diameter.
Grinding ~Jas affected employing a filling coefficient equal to 100 g/l of total volume tvacuum), at an interior temperature of the mill of 25C, and with grinding time oE 72 ~0 hours~
ale ~A~
13 174~25 Charging of the mill with the materials to be ground, and the grindiny and discharging of the product of the co-grinding from the mill, occurred in a nitrogen atmosphere.
10 g o~ the co-ground product was contacted with 100 ml of 1,2-dichloroethane at 80C for 2 hours. After this period, 1,2-dicllloroethane was removed by filtration at 80C
and the residual solid product' was repeatedly washed with n-heptane at ro~m temperature until the chlorine ions dis-appeared from the filtrate and was then kept in suspension in heptane.
The catalytic components thus prepared showed an X-rays powder spectrum in which the most intense diffraction line appearing in the spectrum of MgC12 having 1 m2/g of sur-face area was decreased in relative intensity and broadened to form a halo.
The characteristics of the solid catalytic component, and the results of the polymerization test are reported in Table I.
EXAMP~E 3 62 g of MgC12 and 12.5 g of TiC14 were introduced in the mill described in Example 2 and co-milled or 60 hours at room temperature. The content of titanium was 3.9~ by weight.
10 g of the co-ground product.were contacted with 100 ml of 1,2-dichloroethane at 80C for 2 hours. The solid was separated by filtering and then washed with heptane at said temperature until the disappearance of the chlorine ions from the filtrate. The X-rays powder spectrum was similar to that of the catalytic component of Example 1.
The solid catalytic component obtained was used in the polymerization of propylene under the same polymerization : -12-., .
74~2~
conditions described in Example 1. The results oE the poly-merization have been reported in Table I.
EX~MPLE 4 40 g of M~C12 and g. of TiC14 ~às milled in S the mill described in Example 2 for 200 hours at room temperaturc.
10 g of the ground product were treated with 150 ml of TiC14 for 2 hours at 135C. After hot filtering, the treatment with TiC14 was repeated. After washing with heptane o at 80C and drying, the dry solid was used under the same polymerization conditions as described in Example 1. The solid catalytic component showed an X-rays powder spectrum similar to that of the catalytic component of Example 1.
- The results of th~e polymerization are shown in Table I.
COMP~RATIVE EXAMPLE 1 --200 mg of the solid catalytic component prepared according to Example 4 were used in the polymerization of propylene under the same conditions described in Example 1 but o using ethyl P-toluate instead of PES.~ The results of the polymerization are reported in Table I.
.~ ' . ., -, .
Compara-tive Example 1 was repeated, but using the solid catalytic component prepared according to Example 3.
The results of the polymerization test have been recorded in Table I.
- , .
~ ~74225 .
C ~ ~ o - o - ~r s~ . ..,.
. ~ o G ~ ~ c5 N
C hl~ O o O 0 0~ O .
t:. Q) O V o O ('7 ~` O
. ~ i` ~ N ~-~ ! ~ ~
_ . . ..... .
;~ a ,0~ ~ ~ ~ o o 1`
.~ . .
~ C 1- ~ ~
~ Ql ~ '' O ~ ` 3 ~a g o o :~ u~
O ~ C U r~ ~ - O O ~ . .
EO F .
The Ti trihalides are obtained according to known methods, for instance by reduction of TiC14 with Al or an organometallic Al compound or~with hydrogen.
In the case of Ti trihalides, it may be convenient, for the purpose oE improving the performance of the catalysts, to carry out an oxidization, even if partial, of the titanium, either during or after the preparation of component (c). To this purpose there may be used halogens, iodine halides.
Preferred catalysts are those in which: component (c) is obtained from MgCl2, TiCl4 a silicon compound selected from the groups of phenyl or ethyltriethoxysilane or diphenyl-dime-thoxy or diethoxysilane, and Component (a) is an Al trialkyl, such as Al triethyl or Al triisobutyl.
One of the preferred methods of preparing component (c) consists in co-milling MgCl2, TiC14 and the silicon com-pound and in treating the milled product with a halogenated hydrocarbon such as, for instance, 1,2-dichloroethane.
The ca-talysts according to this invention are used to polymerize the alpha-o].efins according to known methods, that is, by carrying out the polymeriza-tion in a liquid phase, either in the presence or absence of an inert hydrocarbon solvent, or in gas phase or by combining, for instance, a liquid phase polymerization step with a gas phase step.
In general, the polymerization temperature is com-prised between 40 and 160C, but preferably between 60 and .
_9_ ~ 17~225 90C, operating either at atmospheric or at yreater than atmospheric pressure.
~s a molecular weight regulator hydrogen or other regulators of known type are used.
The catalysts are particularly suitable Eor poly-merizing propylene, butene-l, styrene and 4-methylpentene. The catalysts may also be used acoording to known methods to polymerize mixtures of propylene and ethylene to Eorm modified polypropylenes having improved shock-resistance at low temperatures (the so called block copolymers of propylene and ethylene) or to obtain random crystalline copolymers of propylene with m1nor proportions of ethylene.
` The following examples are given for merely illus-trative purposes and are not intended to be in any way limiting of the scope of the invention.
Into an inox steel autoclave of 2000 ml holding capacity, e~uipped with a magnetized stirrer and a thermometer, heat stabilized at 60C and kept under pressure by a nitrogen atmosphere, there were introduced 5 m moles of triethyl-aluminum, l.5 m moles oE phenyltriethoxysilane, the solid catalytic component obtained by reacting TiCl4 with MgCl2.2.3C2H~OH, operating under the same conditions described in Example l of Belyian patent No. 868,682 and 700 ml of degassed and anhydrous n-heptane, while propylene was also fed in.
The catalytic component thus prepared showed an X-rays powder spectrum in which the most intense diffraction line appearing in the spectrum of MgCl2 having l m2/g of ~ 17~225 surface area was decreased in relative intensity and broadened to form a halo.
Thereupon there was fed in 0 2 atm of hydrogen and then the whole was rapidly heated up to 70C, while contem-poraneously further propylene was fed in to reach a total pres~
sure of 7 atm. This latter pressure was maintained constant ~throughout the polymerization by feeding in the monomer.
After 4 hours, the polymerization was interrupted, the polymer was isolated by filtering and then was dried. The quantity of polymer dissolved in the filtrate was thereupon isolated, weighed and summed to the polymer soluble in boiling n-heptane, for calculation of the isotacticity index.
The quantity of catalytic component used and the content of Ti in said component, the yield in polymer with respect to the introduced Ti, the isotacticity index (I.I.) and the inherent viscosity determined in tetralin at 35C, are all reported in Table I.
Example I was repeated but using a so]id catalytic component prepared as follows:
Anhydrous MgC12, phenyltriethoxysilane in molar ratio Mg/Si of 6, and TiCl~ in molar ratio of 1:1 with respect to the phenyltriethoxysilane were co-milled in a vibrating miil of the ~ type VIBRATOM manufactured by N.V. Tema's, Gravenhage, Holland, having a total volume or one liter and containing 3 kg of stainless steel balls of 16 mm diameter.
Grinding ~Jas affected employing a filling coefficient equal to 100 g/l of total volume tvacuum), at an interior temperature of the mill of 25C, and with grinding time oE 72 ~0 hours~
ale ~A~
13 174~25 Charging of the mill with the materials to be ground, and the grindiny and discharging of the product of the co-grinding from the mill, occurred in a nitrogen atmosphere.
10 g o~ the co-ground product was contacted with 100 ml of 1,2-dichloroethane at 80C for 2 hours. After this period, 1,2-dicllloroethane was removed by filtration at 80C
and the residual solid product' was repeatedly washed with n-heptane at ro~m temperature until the chlorine ions dis-appeared from the filtrate and was then kept in suspension in heptane.
The catalytic components thus prepared showed an X-rays powder spectrum in which the most intense diffraction line appearing in the spectrum of MgC12 having 1 m2/g of sur-face area was decreased in relative intensity and broadened to form a halo.
The characteristics of the solid catalytic component, and the results of the polymerization test are reported in Table I.
EXAMP~E 3 62 g of MgC12 and 12.5 g of TiC14 were introduced in the mill described in Example 2 and co-milled or 60 hours at room temperature. The content of titanium was 3.9~ by weight.
10 g of the co-ground product.were contacted with 100 ml of 1,2-dichloroethane at 80C for 2 hours. The solid was separated by filtering and then washed with heptane at said temperature until the disappearance of the chlorine ions from the filtrate. The X-rays powder spectrum was similar to that of the catalytic component of Example 1.
The solid catalytic component obtained was used in the polymerization of propylene under the same polymerization : -12-., .
74~2~
conditions described in Example 1. The results oE the poly-merization have been reported in Table I.
EX~MPLE 4 40 g of M~C12 and g. of TiC14 ~às milled in S the mill described in Example 2 for 200 hours at room temperaturc.
10 g of the ground product were treated with 150 ml of TiC14 for 2 hours at 135C. After hot filtering, the treatment with TiC14 was repeated. After washing with heptane o at 80C and drying, the dry solid was used under the same polymerization conditions as described in Example 1. The solid catalytic component showed an X-rays powder spectrum similar to that of the catalytic component of Example 1.
- The results of th~e polymerization are shown in Table I.
COMP~RATIVE EXAMPLE 1 --200 mg of the solid catalytic component prepared according to Example 4 were used in the polymerization of propylene under the same conditions described in Example 1 but o using ethyl P-toluate instead of PES.~ The results of the polymerization are reported in Table I.
.~ ' . ., -, .
Compara-tive Example 1 was repeated, but using the solid catalytic component prepared according to Example 3.
The results of the polymerization test have been recorded in Table I.
- , .
~ ~74225 .
C ~ ~ o - o - ~r s~ . ..,.
. ~ o G ~ ~ c5 N
C hl~ O o O 0 0~ O .
t:. Q) O V o O ('7 ~` O
. ~ i` ~ N ~-~ ! ~ ~
_ . . ..... .
;~ a ,0~ ~ ~ ~ o o 1`
.~ . .
~ C 1- ~ ~
~ Ql ~ '' O ~ ` 3 ~a g o o :~ u~
O ~ C U r~ ~ - O O ~ . .
EO F .
3 ~ o o ..
Claims (5)
PROPERTY OR PRIVILEGE IS CLAIMED ARE DEFINED AS FOLLOWS:
1. A solid component which in combination with:
(i) an Al-alkyl- or Al-trialkyl-compound containing two or more Al atoms linked to each other through an O or N atom, or through SO4 or SO3 groups; and (ii) a Si-compound, as defined below, forms a catalyst for polymerization of alpha-olefins; said solid component comprising an anhydrous Mg-dihalide, in active form, as an essential support, and, supported on said anhydrous Mg-dihalide, a Ti-halide or a Ti-haloalcoholate and a Si-compound containing at least one Si-OR, Si-OCOR or Si-NR2 bond, wherein R represents a hydrocarbyl radical, in an amount corresponding to a molar ratio of 0.1 to 5 moles per mole of the supported Ti-compound.
(i) an Al-alkyl- or Al-trialkyl-compound containing two or more Al atoms linked to each other through an O or N atom, or through SO4 or SO3 groups; and (ii) a Si-compound, as defined below, forms a catalyst for polymerization of alpha-olefins; said solid component comprising an anhydrous Mg-dihalide, in active form, as an essential support, and, supported on said anhydrous Mg-dihalide, a Ti-halide or a Ti-haloalcoholate and a Si-compound containing at least one Si-OR, Si-OCOR or Si-NR2 bond, wherein R represents a hydrocarbyl radical, in an amount corresponding to a molar ratio of 0.1 to 5 moles per mole of the supported Ti-compound.
2. A solid component as defined in claim 1, in which the Mg-dihalide is Mg-dichloride or Mg-dibromide; the Ti-halide is a Ti-tetrahalide; and the Si-compound is a phenyl di- or trialkoxysilane or an alkyl di- or trialkoxy-silane.
3. Catalyst for the polymerization of alpha-olefins ! comprising the reaction product of:
(a) component (i) as defined in claim 1;
(b) the Si-compound defined in claim 1; and (c) a solid component as defined in claim 1, or a solid component comprising an anhydrous Mg-dihalide, in active form, as an essential support, and, supported on said anhydrous Mg-dihalide, a Ti-halide or Ti-haloalcoholate.
(a) component (i) as defined in claim 1;
(b) the Si-compound defined in claim 1; and (c) a solid component as defined in claim 1, or a solid component comprising an anhydrous Mg-dihalide, in active form, as an essential support, and, supported on said anhydrous Mg-dihalide, a Ti-halide or Ti-haloalcoholate.
4. Catalyst as defined in claim 3, in which component (c) is the solid component as defined in claim 1 or 2.
5. Process for the polymerization of alpha-olefins, CH2=CHR, wherein R represents a (C1-C4)alkyl radical or an aryl radical, and mixtures of said alpha-olefins with ethylene; characterized in that the polymeri-zation process is carried out in liquid phase, in the presence or absence of an inert hydrocarbon solvent, or in gas phase, in presence of a catalyst as defined in claim 3.