CA2414498A1 - Adhesive alpha-olefin inter-polymers - Google Patents
Adhesive alpha-olefin inter-polymers Download PDFInfo
- Publication number
- CA2414498A1 CA2414498A1 CA002414498A CA2414498A CA2414498A1 CA 2414498 A1 CA2414498 A1 CA 2414498A1 CA 002414498 A CA002414498 A CA 002414498A CA 2414498 A CA2414498 A CA 2414498A CA 2414498 A1 CA2414498 A1 CA 2414498A1
- Authority
- CA
- Canada
- Prior art keywords
- mol
- determined
- inter
- less
- polymer
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention relates to novel adhesive alpha-olefin inter-polymers which are largely amorphous and have a rheological behavior that makes them suitable for adhesive use, both without and with minimized amounts of tackifying resins. Specifically, the invention poly-alpha olefin inter-polymer may be composed of A) from 60 to 94 % of units derived from one alpha mono-olefin having from 3 to 6 carbon atoms and B) from 6 to 40 mol % of units derived from one or more other mono-olefins having from 4 to 10 carbon atoms and at least one carbon atom more than A); and C) optionally from 0 to 10 mol % of units derived from another copolymerizable unsaturated hydrocarbon, different from A) and B); the diad distribution of component A in the polymer as determined by 13C NMR as described herein showing a ratio of experimentally determined diad distribution over the calculated Bernoullian diad distribution of less than 1.07; and the storage modulus G' of said polymer, determined upon cooling as described herein, intersecting a value of 3.10 5 Pa at a temperature of less than 85 °C. The invention also describes polymerization processes suitable for the manufacture of these adhesive alpha-olefin inter-polymers.
Claims (33)
1. A poly-alpha olefin inter-polymer comprising A) from 60 to 94 % of units derived from one alpha mono-olefin having from 3 to 6 carbon atoms and B) from 6 to 40 mol % of units derived from one or more other mono-olefins having from 4 to 10 carbon atoms and at least one carbon atom more than A);
and C) optionally from 0 to 10 mol % of units derived from another copolymerizable unsaturated hydrocarbon, different from A) and B);
the diad distribution of component A in the polymer as determined by 13C NMR
as described herein showing a ratio of experimentally determined diad distribution over the calculated Bernoullian diad distribution of less than 1.07; and the storage modulus G' of said polymer, determined upon cooling as described herein, intersecting a value of 3.10 5 Pa at a temperature of less than 85 °C.
and C) optionally from 0 to 10 mol % of units derived from another copolymerizable unsaturated hydrocarbon, different from A) and B);
the diad distribution of component A in the polymer as determined by 13C NMR
as described herein showing a ratio of experimentally determined diad distribution over the calculated Bernoullian diad distribution of less than 1.07; and the storage modulus G' of said polymer, determined upon cooling as described herein, intersecting a value of 3.10 5 Pa at a temperature of less than 85 °C.
2. An inter-polymer according to claim 1 in which the content of B) combined with C) is at least 8 mol % and/or less than 40 mol % and the storage modulus G' of said polymer determined upon cooling as described herein, intersecting a storage modulus G' of 3.10 5 Pa at a temperature of less than 70 °C.
3. An inter-polymer according to claim 1 or claim 2 in which the reactivity ratio as determined by NMR as described herein, has a value of R A x R B, wherein R A
is the reactivity ratio of component A over component B and R B is the ratio of component B over component A, of less than 1.4.
is the reactivity ratio of component A over component B and R B is the ratio of component B over component A, of less than 1.4.
4. An inter-polymer according to any of the preceding claims where the weight average molecular weight of the polymer as determined by GPC as described herein, is less than 120 000, preferably less than 90 000, and most preferably less than 70 000 and/or at least 20 000, preferably at least 30 000 and especially at least 40 000, the storage modulus G' of said polymer, determined upon cooling as described herein, intersecting a storage modulus G' of 3.10 5 Pascal at a temperature of less than 70 °C.
5. An inter-polymer according to any of the preceding claims in which A) is derived from units having from 3 to 6 carbon atoms and preferably propylene; B) is derived from units having from 4 to 8 carbon atoms, preferably at least two more carbon atoms than A), and is preferably butene-1, hexene-1 or octene-1, and C) is derived from ethylene.
6. An inter-polymer according to any of the preceding claims in which said polymer having a melting behavior as determined by DSC, as described herein, wherein the major peak melting point varies with content of component B) plus C) so that T m (interpolymer) is less than 153 - 2.78 x [C B+C] for any given concentration of B) and/or C) components. Where T m is the major melting peak of the interpolymer at a given content of components B) and C) in mol %; [C B-C] is the mol % of component B) plus C).
7. An inter-polymer according to any of the preceding claims in which there are at least 65 mol %, preferably at least 75 mol % of units derived from A) and/or no more than 94 mol %, preferably no more than 90 mol % of A); at least 6 mol %, preferably at least 10 mol % of B) and/or no more than 30 mol %, preferably no more than 25 mol % of B); and/or no more than 5 mol %, most preferably no more than 2 mol % of C).
8. An inter-polymer according to any of the preceding claims which has a heat of fusion of at least 5 J/g, preferably at least 10 J/g and/or no more than 40 J/g, preferably no more than 30 J/g, and most preferably no more than 20 J/g as determined by DSC as described herein.
9. An inter-polymer according to any of the preceding claims which has a major melting peak as determined by DSC, as described herein, of at least 40 °C, preferably of at least 50 °C and/or has a melting point as determined by DSC of no more than 130 °C, preferably no more than 90 °C .
10. An inter-polymer according to any of the preceding claims which has a Tg determined by DSC, as described herein, of no more than minus 5 °C, preferably no more than minus -15 °C, and/or at least minus 40 °C, preferably at least minus 30 °C.
11. An inter-polymer according to any of the preceding claims which G' at 120 °C is not greater than 1000 Pascal, preferably not greater than 500 Pascal and most preferably no greater than 100 Pascal.
12. An inter-polymer according to any of the preceding claims having an Mw/Mn as determined by GPC, as described herein, of from 1.5 to 4, more preferably less than 3, most preferably less than 2.2 and/or at least 1.6.
13. A poly-alpha olefin inter-polymer having (I) A) from 60 to 94 % of units derived from one alpha mono-olefin having from 3 to 6 carbon atoms and B) from 6 to 40 mol % of units derived from one or more other mono-olefins having from 4 to 10 carbon atoms and at least one carbon atom more than A);
and C) optionally from 0 to 10 mol % of units derived from another copolymerizable unsaturated hydrocarbon, different from A) and B);
the diad distribution of component A in the polymer as determined by 13C NMR
as described herein showing a ratio of experimentally determined diad distribution over the calculated Bernoullian diad distribution of less than 1.07;
and said polymer having a melting behavior as determined by DSC, as described herein, so that T m (interpolymer) is less than 153 - 2.78 x [C B+C] for any given concentration of B) and/or C) components where T m is the major melting peak of the interpolymer at a given content of components B) and C) in mol %; [C B+C]
is the mol % of component B) plus C).
and C) optionally from 0 to 10 mol % of units derived from another copolymerizable unsaturated hydrocarbon, different from A) and B);
the diad distribution of component A in the polymer as determined by 13C NMR
as described herein showing a ratio of experimentally determined diad distribution over the calculated Bernoullian diad distribution of less than 1.07;
and said polymer having a melting behavior as determined by DSC, as described herein, so that T m (interpolymer) is less than 153 - 2.78 x [C B+C] for any given concentration of B) and/or C) components where T m is the major melting peak of the interpolymer at a given content of components B) and C) in mol %; [C B+C]
is the mol % of component B) plus C).
14. An interpolymer according to claim 13 in which the storage modulus G' of said polymer, determined upon cooling as described herein, intersecting a value of 3.10 5 Pascal at a temperature of less than 85 °C.
15. An inter-polymer according to any of the preceding claims 13 or 14 which the content of B) combined with C) is at least 8 mol % and/or less than 40 mol %
and the storage modulus G' of said polymer, determined upon cooling as described herein, intersecting a storage modulus G' of 3.10 5 Pascal at a temperature of less than 70 °C.
and the storage modulus G' of said polymer, determined upon cooling as described herein, intersecting a storage modulus G' of 3.10 5 Pascal at a temperature of less than 70 °C.
16. An inter-polymer according to any of the preceding claims 13 to 15 in which the reactivity ratio as determined by NMR as described herein, has a value of R A
x R B, wherein R A is the reactivity ratio of component A over component B and R B is the ratio of component B over component A, of less than 1.4.
x R B, wherein R A is the reactivity ratio of component A over component B and R B is the ratio of component B over component A, of less than 1.4.
17. An inter-polymer according to any of the preceding claims 13 to 16 in which the weight average molecular weight of the polymer as determined by GPC as described herein, is less than 120 000, preferably less than 90 000, and most preferably less than 70 000 and/or at least 20 000, preferably at least 30 000 and especially at least 40 000, the storage modulus G' of said polymer, determined upon cooling as described herein, intersecting a storage modulus G' of 3.10 5 Pascal at a temperature of less than 70 °C.
18. An inter-polymer according to any of the preceding claims 13 to 17 in which A) is derived from units having from 3 to 6 carbon atoms and preferably propylene;
B) is derived from units having from 4 to 8 carbon atoms, preferably at least two more carbon atoms than A), and is preferably butene-1, hexene-1 or octene-1 and C) is derived from ethylene.
B) is derived from units having from 4 to 8 carbon atoms, preferably at least two more carbon atoms than A), and is preferably butene-1, hexene-1 or octene-1 and C) is derived from ethylene.
19. An inter-polymer according to any of the preceding claims 13 to 18 in which there are at least 65 mol %, preferably at least 75 mol of units derived from A) and/or no more than 94 mol %, preferably no more than 90 mol % of A); at least 6 mol %, preferably at least 10 mol % of B) and/or no more than 30 mol %, preferably no more than 25 mol % of B); and/or no more than 5 mol %, most preferably no more than 2 mol % of C).
20. An inter-polymer according to any of the preceding claims 13 to 19 which has a heat of fusion of at least 5 J/g, preferably at least 10 J/g and/or no more than 40 J/g, preferably no more than 30 J/g, and most preferably no more than 20 J/g as determined by DSC as described herein.
21. An inter-polymer according to any of the preceding claims 13 to 20 which has a melting peak as determined by DSC of at least 40 °C, preferably of at least 50 °C
and/or has a melting point as determined by DSC of no more than 130 °C, preferably no more than 95 °C.
and/or has a melting point as determined by DSC of no more than 130 °C, preferably no more than 95 °C.
22. An inter-polymer according to any of the preceding claims 13 to 21 which has a Tg determined by DSC of no more than minus 5 °C, preferably no more than minus 20 °C, and/or at least minus 40 °C, preferably at least minus 30 °C.
23. An inter-polymer according to any of the preceding claims 13 to 22 which the G' at 120 °C is not greater than 1000 Pascal, preferably not greater than 500 Pascal;
and most preferably no greater than 100 Pascal.
and most preferably no greater than 100 Pascal.
24. An inter-polymer according to any of the preceding claims 13 to 23 having an Mw/Mn as determined by GPC as described herein of from 1.5 to 4, more preferably less than 3, most preferably less than 2.2 and/or at least 1.6.
25. An adhesive composition or formulation containing an inter-polymer according to any of the preceding claims 1 to 24 which is substantially free of volatile components, containing less than 20 wt %, preferably less than 10 wt % of tackifier and optionally less than 3 wt % each of anti-oxidant, flow improver, wax, or crystallization aid.
26. An adhesive composition or formulation according to claim 25 further comprising from 1 to 20 wt % of a tackifier and/or from 1 to 20 wt % of a flow improver.
27. An adhesive composition or formulation according to claim 25 or 26 for use as a hot melt adhesive in which the Melt Index is from 1 to 2000 as determined under ASTM D1238 methods.
28. An adhesive composition or formulation according to any of claims 25 to 27 having a flowability of at least and being suitable for applying the adhesive composition by spraying.
29. An adhesive composition or formulation according to claim 28 or 31 for use as a pressure sensitive adhesive in which the Melt Index is from 0.1 to 200 as determined under ASTM D1238 method.
30. An adhesive composition or formulation containing an inter-polymer according to any of the preceding claims 1 to 24 which contains at least 10 wt %, preferably at least 20 wt % of the total weight of the formulation and no more than 90 wt %
of a hydrocarbon based volatile solvent, preferably no more than 60 wt % of the total weight of the formulation.
of a hydrocarbon based volatile solvent, preferably no more than 60 wt % of the total weight of the formulation.
31. A packaging material or article containing a structure, elements of which are adhered by an adhesive composition or formulation according to any of claims to 30.
32. A hygienic garment containing a structure, elements of which are adhered by an adhesive composition or formulation according to any of claims 25 to 30.
33. An process for adhering two substrates together which process comprises (I) applying a poly-alpha olefin inter-polymer having A) from 55 to 94 % of units derived from one alpha mono-olefin having from 3 to 6 carbon atoms and B) from 6 to 45 mol % of % of units derived from one or more other mono-olefins having from 4 to 10 carbon atoms and at least one carbon atom more than A); and C) optionally from 0 to 10 mol % of units derived from another copolymerizable unsaturated hydrocarbon, different from A) and B) the diad distribution of component A in the polymer as determined by 13C
NMR as described herein showing a ratio of experimentally determined diad distribution over the calculated Bernoullian diad distribution of less than 1.07 (II) to the interface between the substrate at elevated temperature of from 10 to 100 °C and/or pressure until adhesion is established.
NMR as described herein showing a ratio of experimentally determined diad distribution over the calculated Bernoullian diad distribution of less than 1.07 (II) to the interface between the substrate at elevated temperature of from 10 to 100 °C and/or pressure until adhesion is established.