CN102114620A - Resin matrix composite for flexible grinding and polishing - Google Patents
Resin matrix composite for flexible grinding and polishing Download PDFInfo
- Publication number
- CN102114620A CN102114620A CN 201010590817 CN201010590817A CN102114620A CN 102114620 A CN102114620 A CN 102114620A CN 201010590817 CN201010590817 CN 201010590817 CN 201010590817 A CN201010590817 A CN 201010590817A CN 102114620 A CN102114620 A CN 102114620A
- Authority
- CN
- China
- Prior art keywords
- polishing
- grinding
- matrix composite
- resin matrix
- flexible grinding
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention discloses a resin matrix composite for flexible grinding and polishing, belongs to the technical field of composites, and relates to a preparation method of the resin matrix composite for flexible grinding and polishing. The preparation method of the resin matrix composite comprises the following steps of: mixing cement, quartz sand of 100 to 200 meshes and alumina powder of 100 to 200 meshes according to a certain weight percentage ratio, adding water and a polycarboxylic acid water reducer, stirring in a mortar mixer for 3 to 5 minutes, coating slurry on the surface of resin foam to allow the slurry to enter the resin foam, and curing in a standard curing box at the temperature of between 19 and 21 DEG C and the humidity of more than 90 percent for 3 to 7 days, wherein the composite can meet grinding and polishing requirements. The method is simple in process, low in production cost, and high in application value in grinding and polishing the surface of a special-shaped complex workpiece and improving the surface finish of the special-shaped complex workpiece.
Description
Technical field
The present invention is specifically related to a kind of polymer matrix composites preparation method who is used for flexible grinding and polishing, and the grinding-polishing that is used for special-shaped complex surface is handled.
Background technology
Grinding is one of metal material processing method commonly used with polishing processing, at present with the most use is the grinding tool material of similar emery wheel, but the emery wheel of rigidity only is suitable for the processing of plane metalloid workpiece, to similar mould, have the parts of more special-shaped complex surface, when needing to improve surface smoothness, it is powerless that wheel grinding just seems.A kind of grinding tool material of realizing flexible grinding and polishing that the present invention obtains can solve this class problem.
Summary of the invention
The invention provides a kind of polymer matrix composites preparation method who is used for flexible grinding and polishing.The preparation process of its polymer matrix composites is: with cement, quartz sand 100-200 order, alumina powder 100-200 order etc. is pressed the constant weight percentage mix, add entry and polycarboxylate water-reducer, in the glue sand agitator, stir the 3-5 branch, slurry is coated on the resin foam surface, slurry is entered wherein, put into 19-21 ℃ then, the standard curing case maintenance of humidity＞90% 3-7 days, composite can satisfy the requirement of grinding and polishing.The method technology is simple, and production cost is low, needs the industry of grinding and polishing that good using value is arranged in waste and old galvanized sheet dezincification and other.It is characterized in that: (1) cement, quartz sand 100-200 order, alumina powder 100-200 order and water and polycarboxylate water-reducer (accounting for the percentage by weight of cement) mix by a certain percentage, cement 20-60%, quartz sand powder 30-80%, water 10-30%, polycarboxylate water-reducer 0.05-0.2%, alumina powder 10%-30%, mixing time 3-5 minute; (2) after the stirring, slurry is coated on the resin foam surface, slurry is infiltrated wherein; (3) composite is put into 19-21 ℃, the standard curing case maintenance of humidity＞90% 3-7 days.
The specific embodiment
Below in conjunction with implementing example content of the present invention is further described.
Embodiment 1 is with cement 40%, 100 order quartz sands 40%, water 20%, polycarboxylate water-reducer 0.05%, in mixer, stirred 3-5 minute, on coating and the resin foam, composite is put into 19-21 ℃ then then, the standard curing case maintenance of humidity＞90% 3-7 days, but the composite of grinding and polishing promptly obtained.
Embodiment 2 is with cement 45%, 140 order quartz sands 20%, 100 order aluminium oxide 15%, water 20%, polycarboxylate water-reducer 0.05% stirred 3-5 minute in mixer, then on coating and the resin foam, composite is put into 19-21 ℃ then, the standard curing case maintenance of humidity＞90% 3-7 days, but promptly obtain the composite of grinding and polishing.
Embodiment 3 is with cement 35%, 100 order quartz sands 50%, water 15%, polycarboxylate water-reducer 0.1%, in mixer, stirred 3-5 minute, on coating and the resin foam, composite is put into 19-21 ℃ then then, the standard curing case maintenance of humidity＞90% 3-7 days, but the composite of grinding and polishing promptly obtained.
Claims (5)
1. preparation method who is used for the polymer matrix composites of flexible grinding and polishing, it is characterized in that: with cement, quartz sand, alumina powder, water and polycarboxylate water-reducer stir certain hour by a certain percentage, then slurry is coated on the resin foam surface, behind maintenance certain hour under certain curing condition, promptly can be used as flexible grinding and polishing material;
2. one of right 1 described material rate is: cement 20-60%, quartz sand powder 30-80%, water 10-30%, polycarboxylate water-reducer 0.05-0.2%, alumina powder 10%-30%;
3. right 1 described quartz sand size 100-200 order, alumina powder 100-200 order;
4. right 1 described mixing time is 3-5 minute;
5. right 1 described curing condition is temperature 19-21 ℃, humidity＞90%, curing time 3-7 days.