CN104062697A - High-brightness colored reflective cloth - Google Patents
High-brightness colored reflective cloth Download PDFInfo
- Publication number
- CN104062697A CN104062697A CN201410111798.7A CN201410111798A CN104062697A CN 104062697 A CN104062697 A CN 104062697A CN 201410111798 A CN201410111798 A CN 201410111798A CN 104062697 A CN104062697 A CN 104062697A
- Authority
- CN
- China
- Prior art keywords
- layer
- reflective cloth
- microns
- resin layer
- thickness
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to a reflective material and specifically discloses high-brightness colored reflective cloth; a fabric layer is adopted as a substrate, a colored resin layer is arranged on the fabric layer, at least one glass bead is embedded into the colored resin layer, and a coating film layer is arranged between the colored resin layer and the glass bead. Compared with the prior art, the high-brightness colored reflective cloth has the advantages of high reflectance and bright and high-fidelity in color.
Description
Technical field
The present invention relates to a kind of reflectorized material, specifically a kind of highlighted level color reflective cloth.
Background technology
In highway construction management, fire-fighting, maritime affairs, transportation, mining or carry out other whens operation, for personal security, on working cloth, be equipped with reflectorized material.Along with the raising of people's awareness of safety, reflectorized material is more and more expanded to civilian garment industry, and this has just proposed requirement to color and reflective combination, although and the brightness bright in luster of existing color reflective cloth is on the low side, be not well positioned to meet safety requirements.
Summary of the invention
For the deficiency existing in background technology, the object of the present invention is to provide a kind of highlighted level color reflective cloth.
For achieving the above object, the invention provides following technical scheme:
A highlighted level color reflective cloth, take tissue layer as basic unit, and in tissue layer, is provided with color resin layer, is inlaid with at least one glass microballoon, and is provided with film plating layer between color resin layer and glass microballoon in described color resin layer; The thickness of described tissue layer is 70～600 microns; The thickness of described color resin layer is 30～70 microns; The thickness of described film plating layer is 100～200 dusts; The diameter of described glass microballoon is 50～100 microns; Described color resin layer consists of acrylate resin and mill base, and weight ratio is: acrylate resin 80%～90%, mill base 10%～20%.
As the further scheme of the present invention: the thickness of described tissue layer is 200～400 microns; The thickness of described color resin layer is 45～55 microns; The thickness of described film plating layer is 130～170 dusts; The diameter of described glass microballoon is 65～85 microns.
As the further scheme of the present invention: described tissue layer comprises cotton, polyester cotton blending, chemical fibre.
As the further scheme of the present invention: described color resin layer consists of acrylate resin and mill base, and weight ratio is: acrylate resin 85%, mill base 15%.
As the further scheme of the present invention: described film plating layer is the skim that aluminium or silver form by vacuum evaporation.
As the further scheme of the present invention: the episphere of described glass microballoon is exposed to outside, and lower semisphere is embedded in film plating layer.
As the further scheme of the present invention: described glass microballoon adopts the high refractive index glass micro pearl that refractive index is 1.90-1.95.
Compared with prior art, the invention has the beneficial effects as follows: reflectance of the present invention is high the advantage of fidelity bright in luster.
Accompanying drawing explanation
Fig. 1 is the structural representation of highlighted level color reflective cloth;
In figure: 1-tissue layer; 2-color resin layer; 3-film plating layer; 4-glass microballoon.
Embodiment
Below in conjunction with the accompanying drawing in the embodiment of the present invention, the technical scheme in the embodiment of the present invention is clearly and completely described, obviously, described embodiment is only the present invention's part embodiment, rather than whole embodiment.Embodiment based in the present invention, those of ordinary skills, not making the every other embodiment obtaining under creative work prerequisite, belong to the scope of protection of the invention.
Refer to Fig. 1, a kind of highlighted level color reflective cloth, take tissue layer 1 as basic unit, and in tissue layer 1, is provided with color resin layer 2, is inlaid with at least one glass microballoon 4, and is provided with film plating layer 3 between color resin layer 2 and glass microballoon 4 in described color resin layer 2.
As the further scheme of the present invention: described tissue layer 1 comprises cotton, polyester cotton blending, chemical fibre, and its thickness is 70～600 microns; Described color resin layer 2 consists of acrylate resin and mill base, and weight ratio is: acrylate resin 80%～90%, mill base 10%～20%; In addition, the thickness of color resin layer 2 is 30～70 microns; Described film plating layer 3 is skims that aluminium or silver form by vacuum evaporation, and its thickness is 100～200 dusts; Described glass microballoon 4 adopts the high refractive index glass micro pearl that refractive index is 1.90-1.95, and its diameter is 50～100 microns; And the episphere of glass microballoon 4 is exposed to outside, and lower semisphere is embedded in film plating layer 3; In practical application, adopt that a plurality of glass microballoons 4 are uniform to be embedded in film plating layer 3.
To those skilled in the art, obviously the invention is not restricted to the details of above-mentioned one exemplary embodiment, and in the situation that not deviating from spirit of the present invention or essential characteristic, can realize the present invention with other concrete form.Therefore, no matter from which point, all should regard embodiment as exemplary, and be nonrestrictive, scope of the present invention is limited by claims rather than above-mentioned explanation, is therefore intended to include in the present invention dropping on the implication that is equal to important document of claim and all changes in scope.Any Reference numeral in claim should be considered as limiting related claim.
In addition, be to be understood that, although this instructions is described according to embodiment, but not each embodiment only comprises an independently technical scheme, this narrating mode of instructions is only for clarity sake, those skilled in the art should make instructions as a whole, and the technical scheme in each embodiment also can, through appropriately combined, form other embodiments that it will be appreciated by those skilled in the art that.
Claims (8)
1. a highlighted level color reflective cloth, is characterized in that, take tissue layer as basic unit, and in tissue layer, is provided with color resin layer, is inlaid with at least one glass microballoon, and is provided with film plating layer between color resin layer and glass microballoon in described color resin layer; The thickness of described tissue layer is 70～600 microns; The thickness of described color resin layer is 30～70 microns; The thickness of described film plating layer is 100～200 dusts; The diameter of described glass microballoon is 50～100 microns; Described color resin layer consists of acrylate resin and mill base, and weight ratio is: acrylate resin 80%～90%, mill base 10%～20%.
2. highlighted level color reflective cloth according to claim 1, is characterized in that, the thickness of described tissue layer is 200～400 microns; The thickness of described color resin layer is 45～55 microns; The thickness of described film plating layer is 130～170 dusts; The diameter of described glass microballoon is 65～85 microns.
3. highlighted level color reflective cloth according to claim 1, is characterized in that, described tissue layer comprises cotton, polyester cotton blending, chemical fibre.
4. highlighted level color reflective cloth according to claim 1, is characterized in that, described color resin layer consists of acrylate resin and mill base, and weight ratio is: acrylate resin 85%, mill base 15%.
5. highlighted level color reflective cloth according to claim 1, is characterized in that, described film plating layer is the skim that aluminium or silver form by vacuum evaporation.
6. according to the highlighted level color reflective cloth one of claim 1-5 Suo Shu, it is characterized in that, the episphere of described glass microballoon is exposed to outside, and lower semisphere is embedded in film plating layer.
7. highlighted level color reflective cloth according to claim 6, is characterized in that, described glass microballoon adopts the high refractive index glass micro pearl that refractive index is 1.90-1.95.
8. highlighted level color reflective cloth according to claim 6, is characterized in that, adopts that a plurality of glass microballoons are uniform to be embedded in film plating layer.