CN105216193A - A kind of waterproof composite fabric production technology - Google Patents

A kind of waterproof composite fabric production technology Download PDF

Info

Publication number
CN105216193A
CN105216193A CN201510207537.XA CN201510207537A CN105216193A CN 105216193 A CN105216193 A CN 105216193A CN 201510207537 A CN201510207537 A CN 201510207537A CN 105216193 A CN105216193 A CN 105216193A
Authority
CN
China
Prior art keywords
mass parts
fabric
production technology
waterproof composite
temperature
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201510207537.XA
Other languages
Chinese (zh)
Inventor
汪卫芬
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Anhui Chuan Rong Garment Accessories Co Ltd
Original Assignee
Anhui Chuan Rong Garment Accessories Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Anhui Chuan Rong Garment Accessories Co Ltd filed Critical Anhui Chuan Rong Garment Accessories Co Ltd
Priority to CN201510207537.XA priority Critical patent/CN105216193A/en
Publication of CN105216193A publication Critical patent/CN105216193A/en
Pending legal-status Critical Current

Abstract

The invention discloses a kind of waterproof composite fabric production technology, first batch mixing, manufacture first surface material and the second fabric, carrying out compound by sheet film extruder, the present invention, when ensureing water resistance, promotes the water vapour permeability of fabric itself.

Description

A kind of waterproof composite fabric production technology
Technical field
The present invention relates to fabric and manufacture field, particularly relate to a kind of waterproof composite fabric production technology.
Background technology
Water-proof breathable fabric is a kind of novel weaving face fabric, its composition by macromolecule waterproof ventilative material (PTFE film) add that cloth is composited, the major function of Water-proof breathable fabric has: waterproof, moisture-inhibiting, ventilative, insulation, windproof, warming.Its vapor transfer rate is every 24 hours every square metre of 16000g, and anti-hydraulic pressure can reach 8000-20000mm water column, and insulation reaches as high as 100,000 volts.This fabric also can keep its optimal efficacy in rugged environment, can adaptive temperature be: 427 degree to subzero 200 degree.From manufacture craft, the technical requirement of Water-proof breathable fabric is more much higher than general waterproof fabrics; Simultaneously quality, Water-proof breathable fabric also has the functional characteristics not available for other waterproof fabrics.Water-proof breathable fabric is while reinforcement cloth air-tightness, watertightness, the permeability performance of its uniqueness, inside configuration steam can be made to discharge rapidly, structure is avoided to multiply mould, and keeping human body dry and comfortable all the time, perfection solves ventilative and windproof, waterproof, the problem such as warming is a kind of novel fabric of health environment-friendly.
Summary of the invention
A kind of waterproof composite fabric production technology, it is characterized in that, its step comprises:
1) 1-2 mass parts oleoyl amino acid sodium, 13-15 mass parts diisooctyl phthalate, 75-80 mass parts Corvic, 7-8 mass parts Celogen Az, 1-2 mass parts phenyl silicone oil, 3-4 mass parts toner, 6-8 mass parts zinc stearate, 5-7 mass parts talcum powder, 8-9 mass parts TCPP, 2-3 mass parts white oil is got, mix, obtained first slurry;
2) add in sheet film extruder by the material after mixing, melt blending temperature 200-205 DEG C, extrusion temperature 173-175 DEG C, obtain the first fabric;
3) 1-2 mass parts lauramide SES, 130 mass parts polyurethane resins, 5-6 mass parts 1 is got, 6-diisocyanato-Hexane, 60-65 mass parts water, 17-19 mass parts butanone, 6-7 mass parts N-methylethanolamine, 40-45 mass parts toluene mix, cross 200 order nylon wires, leave standstill 75 minutes under vacuum again, obtained second slurry;
4) add in sheet film extruder by the material after mixing, melt blending temperature 180-190 DEG C, extrusion temperature 175-185 DEG C, obtain the second fabric;
5) the first fabric and the second fabric are entered calendering compound machine simultaneously carry out calendering compound, obtain composite material.
Preferably, corona discharge, carries out Corona discharge Treatment by composite material, and use high-frequency alternating current, its voltage is 5-25Kv, and discharging distance is 2-20mm.
Preferably, web surface process, after with medicament being processed the face of fabric, bonding lining, carry out compound after lining bonding, temperature is 120-140 degree, and pressure is 4-6bar, and the time is 15-20s.
Beneficial effect: the invention provides a kind of waterproof composite fabric production technology, add Organic fluoride water-proof aagent in fabric in process, Organic fluoride add the waterproof effect that can not only strengthen fabric, the effect refusing oil can be played simultaneously; Fabric adopts treble cloths laminating, and be double applying fabric, double applying fabric more abrasion-proof corrosion-proof, effectively can protect the poly tetrafluoroethylene of compound in fabric, makes the waterproof and breathable performance of fabric more lasting; Gluing uses PU glue, and PU glue has excellent firmness, and heat-resisting weather resistance is good, semi-transparent clear, and environment-protecting asepsis is easy to operate, is suitable for production line balance; Spread is 15g/m2, gluing number decide cost number, be set to the spread of 15g/m2, the viscosity of fabric compound can be met on the one hand, saved cost on the other hand; Use to obtain the medicament ammonia solution that is sodium metal in face process, face can improve the hydrophobic performance of face through process, can make the sticky glutinous lining of face.
Detailed description of the invention
The technological means realized for making the present invention, creation characteristic, reaching object and effect is easy to understand, below in conjunction with detailed description of the invention, setting forth the present invention further.
A kind of waterproof composite fabric production technology, it is characterized in that, its step comprises:
1) 2 mass parts oleoyl amino acid sodium, 14 mass parts diisooctyl phthalates, 80 mass parts Corvics, 7 mass parts Celogen Azs, 1 mass parts phenyl silicone oil, 4 mass parts toners, 8 mass parts zinc stearates, 7 mass parts talcum powder, 8 mass parts TCPPs, 2 mass parts white oils are got, mix, obtained first slurry;
2) add in sheet film extruder by the material after mixing, melt blending temperature 200 DEG C, extrusion temperature 175 DEG C, obtains the first fabric;
3) 2 mass parts lauramide SESs, 130 mass parts polyurethane resins, 5 mass parts 1 are got, 6-diisocyanato-Hexane, 60 mass parts water, 19 mass parts butanone, 6 mass parts N-methylethanolamines, 45 mass parts toluene mixing, cross 200 order nylon wires, leave standstill 75 minutes under vacuum again, obtained second slurry;
4) add in sheet film extruder by the material after mixing, melt blending temperature 190 DEG C, extrusion temperature 185 DEG C, obtains the second fabric;
5) the first fabric and the second fabric are entered calendering compound machine simultaneously carry out calendering compound, obtain composite material.
Preferably, corona discharge, carries out Corona discharge Treatment by composite material, and use high-frequency alternating current, its voltage is 25Kv, and discharging distance is 20mm.
Preferably, web surface process, after with medicament being processed the face of fabric, bonding lining, carry out compound after lining bonding, temperature is 130 degree, and pressure is 6bar, and the time is 20s.
Obvious specific implementation of the present invention is not subject to the restrictions described above; as long as have employed the improvement of the various unsubstantialities that method of the present invention is conceived and technical scheme is carried out; or design of the present invention and technical scheme directly applied to other occasion, all within protection scope of the present invention without to improve.

Claims (3)

1. a waterproof composite fabric production technology, is characterized in that, its step comprises:
1) 1-2 mass parts oleoyl amino acid sodium, 13-15 mass parts diisooctyl phthalate, 75-80 mass parts Corvic, 7-8 mass parts Celogen Az, 1-2 mass parts phenyl silicone oil, 3-4 mass parts toner, 6-8 mass parts zinc stearate, 5-7 mass parts talcum powder, 8-9 mass parts TCPP, 2-3 mass parts white oil is got, mix, obtained first slurry;
2) add in sheet film extruder by the material after mixing, melt blending temperature 200-205 DEG C, extrusion temperature 173-175 DEG C, obtain the first fabric;
3) 1-2 mass parts lauramide SES, 130 mass parts polyurethane resins, 5-6 mass parts 1 is got, 6-diisocyanato-Hexane, 60-65 mass parts water, 17-19 mass parts butanone, 6-7 mass parts N-methylethanolamine, 40-45 mass parts toluene mix, cross 200 order nylon wires, leave standstill 75 minutes under vacuum again, obtained second slurry;
4) add in sheet film extruder by the material after mixing, melt blending temperature 180-190 DEG C, extrusion temperature 175-185 DEG C, obtain the second fabric;
5) the first fabric and the second fabric are entered calendering compound machine simultaneously carry out calendering compound, obtain composite material.
2. a waterproof composite fabric production technology according to claim 1, is characterized in that, corona discharge, and composite material is carried out Corona discharge Treatment, and use high-frequency alternating current, its voltage is 5-25Kv, and discharging distance is 2-20mm.
3. a waterproof composite fabric production technology according to claim 1, is characterized in that, web surface process, after with medicament being processed the face of fabric, bonding lining, carries out compound after lining bonding, temperature is 120-140 degree, and pressure is 4-6bar, and the time is 15-20s.
CN201510207537.XA 2015-04-28 2015-04-28 A kind of waterproof composite fabric production technology Pending CN105216193A (en)