CN1287990A - Microcrystalline glass ceramic composite sheet material and its production method - Google Patents
Microcrystalline glass ceramic composite sheet material and its production method Download PDFInfo
- Publication number
- CN1287990A CN1287990A CN 00130117 CN00130117A CN1287990A CN 1287990 A CN1287990 A CN 1287990A CN 00130117 CN00130117 CN 00130117 CN 00130117 A CN00130117 A CN 00130117A CN 1287990 A CN1287990 A CN 1287990A
- Authority
- CN
- China
- Prior art keywords
- glass
- frit
- ceramic
- following
- scope
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The present invention relates to the production method of composite microcrystal glass-ceramic plate material. It is composed of the following steps: (1) preparing glass ceramic fused frit; (2) preparing ceramic base plate: (3) uniformly distributing the glass ceramic frit on to the biscuit fired ceramic base plate and sintering in roller kiln; (4) edge cutting, polishing, inspecting and packaging into product. The invented composite plate is high in integral strength, large and thin in surface area, it has the visual texture and operation effect like microcrystal glass and may be produced in low energy consumption, low cost and high speed.
Description
The present invention relates to the ceramic building material technical field, particularly a kind of glass-ceramics composite board and production method thereof.
Simple crystallizing glass sheet material, from appearance, it is strong to have beautiful texture, and the turbid shape of gala, water-intake rate be near zero, do not inhale dirtyly, and polishing back glossiness height than the ceramic polished brick top grade, is a kind of metope and floor decorative material of top grade.The technology production process of crystallizing glass sheet material, two kinds of technologies are arranged at present, rolling process and sintering process, the sheet metal thickness of production are generally the thick vitreum of 8-20mm, because the sintering period second time is oversize, be about 20 hours, thereby, cost of manufacture height, fetch long price, basically fail to enter household consumption, its market is very restricted.And ceramic polished brick is big because of its turnout, and firing period is short, and production cost is low, price is low, by vast family the user is accepted.How to accomplish both to have kept the beautiful texture of devitrified glass and superior result of use, and high-speed production low-costly and in high volume, the direction of crystallized glass article just become in the exhibition of building material industry relaying supervention.
The objective of the invention is to propose a kind of glass-ceramics composite board and production method thereof, the glass ceramics frit that it utilizes common process to produce, with this devitrified glass coefficient of expansion basically identical and carry this glass ceramics frit through uniform distribution on the unglazed ceramic substrate, be positioned over to fire in the kiln and form.
Another object of the present invention is to provide a kind of glass-ceramics composite board with the aforementioned production method preparation.
The object of the present invention is achieved like this: a kind of glass-ceramics composite board, it is composited by top glass-ceramic layer and following ceramic substrate tight bond.The production method of described glass-ceramics composite board comprises the following steps: that (one) prepares a kind of glass ceramics frit, its composition range following (weight percent): SiO
258-65%; Al
2O
34-8%; KNaO 0-4%; CaO15-25%; MgO 0-2%; BaO 0-2%; ZnO 4-9% and an amount of finings and tinting material, the glass frit preparation of this scope, carry out through the following steps: (1) evenly disposes admixtion by the mentioned component scope; (2) under 1400-1580 ℃ of temperature range, found into glass metal; (3) the glass metal water-cooled becomes the glass ceramics frit grain of 1-8mm scope, then oven dry or seasoning; (2) preparation ceramic substrate, its composition range is (weight percent): SiO
260-70%; Al
2O
313-20%; KNaO 3-8%; CaO 2-6%; MgO 0-2%; Fe
2O
30-2%; Its mineral composition scope is weathered feldspar, quartz, clay, Wingdale, calcite, lime carbonate, wollastonite; Carry out through the following step: (1) above-mentioned each mineral batching, evenly be mixed with admixtion by the composition scope, through wet ball grinding, spray drying granulation, the slurry fineness is the surplus 1-10% of 10000-hole sieve; (2) powder moisture content 5-8%, powder particle are to be to be 50-90% on＜1%, 60 mesh sieves on 20 mesh sieves; (3) powder is shaped through the automatic brick pressing machine of pottery, and specification limit is 200 * 200mm to 1000 * 1000mm; (4) biscuiting in 600-1200 ℃ of temperature range.(3) the glass ceramics frit grain is uniformly distributed on the unglazed ceramic substrate, this frit grain thickness is 2-8mm, spray an amount of fixing agent, be positioned in the ceramic roller kiln and burn till, firing temperature is 1140-1250 ℃, firing period is 1-3.5 hour, and cooled work in-process become finished product after cutting edge, polish, check, packing.
Glass-ceramics composite board and production method thereof that the present invention proposes have following advantage:
1, ceramic substrate intensity height can cause the big and thin substrate of area, thereby glass-ceramics composite board bulk strength height, area are approached greatly, is suitable for inner, external wall and ground decoration and uses.
2, firing period is less than 3.5 hours, thereby has saved the energy; Because adopt roller kiln to burn till, thereby can accomplish high-speed production low-costly and in high volume, product price is easily accepted by the human consumer.
By following embodiment the present invention is further elaborated.
Embodiment 1:
1, make glass ceramics frit:
1. the chemical constitution of glass ceramics frit admixtion (weight percent):
Adopt mineral such as quartz, kaolin, Wingdale, talcum, zinc oxide, soda ash, barium carbonate, borax to satisfy following chemical constitution (weight percent):
SiO
2 Al
2O
3?KNaO CaO MgO BaO ZnO
62％ 6％ 3％ 15％ 1％ 1％ 6％
2. with above-mentioned raw mineral materials scale material, mixing, 1520 ℃ of temperature fusings, liquation is quenching in water.
2, preparation ceramic substrate:
1. ceramic substrate prescription:
Adopt mineral such as weathered feldspar, quartz, clay, Wingdale, calcite, lime carbonate, wollastonite to satisfy following chemical constitution (weight percent):
SiO
2 Al
2O
3 CaO MgO KNaO
70％ 20％ 4％ 1％ 5％
2. be that 10000-hole sieve surpluss 1% with above feed proportioning through wet ball grinding to fineness, spray-dried again granulation, its granularity is on 60 mesh sieves 75%, powder moisture is 7%, through brick pressing machine shaping automatically, specification is 1000 * 1000mm, and dry again back is in 1000 ℃ of temperature biscuitings.
3, the making of glass-ceramics composite board:
Use the dry method granule applicator; on glazing line; the glass ceramics frit grain evenly is sprinkled upon on the unglazed ceramic substrate; this frit grain thickness is 5mm; spray is burnt till in roller kiln with an amount of fixing agent, and firing temperature is 1200 ℃; firing period is 3.5 hours, and cooled work in-process become finished product after cutting edge, polish, check, packing.
Embodiment 2:
1, make glass ceramics frit:
1. glass ceramics frit prescription (weight percent):
Adopt the mineral substance of example 1, be to satisfy chemical constitution:
SiO
2 Al
2O
3 CaO MgO ZnO
58％ 8％ 25％ 2％ 4％
2. with above-mentioned raw mineral materials mixing, 1580 ℃ of temperature fusings, liquation is quenching in water.
2, preparation ceramic substrate:
1. ceramic substrate prescription (weight percent):
Adopt example 1 described mineral substance to be to satisfy chemical constitution:
SiO
2 Al
2O
3?KNaO CaO MgO Fe
2O
3
60％ 17％ 8％ 6％ 2％ 1％
2. be that 10000-hole sieve surpluss 10% with above feed proportioning through wet ball grinding to fineness, spray-dried again granulation, its granularity is to be 0.3% on 20 mesh sieves, be 50% on 60 mesh sieves, powder moisture content is 5%, through brick pressing machine shaping automatically, specification 600 * 600mm is through 1200 ℃ of temperature biscuitings.
3, the making of glass-ceramics composite board:
Use the dry method granule applicator; on glazing line; the glass ceramics frit grain evenly is sprinkled upon on the unglazed ceramic substrate; this frit grain thickness is 8mm; spray is burnt till in roller kiln with an amount of fixing agent, and firing temperature is 1250 ℃; firing period is 2.5 hours, and cooled work in-process become finished product after cutting edge, polish, check, packing for sale.
Embodiment 3:
1, make glass ceramics frit:
1. glass ceramics frit prescription (weight percent):
Adopt example 1 described mineral substance to be to satisfy chemical constitution:
SiO
2 Al
2O
3 KNaO CaO BaO ZnO
65％ 4％ 4％ 19％ 2％ 9％
2. with above-mentioned raw mineral materials mixing, in the fusing of 1400 ℃ of temperature, liquation is quenching in water.
2, preparation ceramic substrate:
1. ceramic base stage prescription (weight percent):
Adopt example 1 described mineral substance to be to satisfy chemical constitution:
SiO
2 Al
2O
3 KNaO CaO Fe
2O
3
65％ 13％ 3％ 2％ 2％
2. be that 10000-hole sieve surpluss 4% with the above-mentioned raw materials batching through wet ball grinding to fineness, spray-dried again granulation, its granularity is to be 0.9% on 20 mesh sieves, be 88% on 60 mesh sieves, powder moisture content is 8%, through brick pressing machine shaping automatically, specification 400 * 400mm is through 600 ℃ of temperature biscuitings.
3, the making of glass-ceramics composite board:
Use the dry method granule applicator; on the glazing line glass ceramics frit grain evenly is being sprinkled upon on the unglazed ceramic substrate; this frit grain thickness is 2mm; spray is with an amount of fixing agent; in roller kiln, burn till; firing temperature is 1140 ℃, and firing period is 1 hour, and cooled work in-process become finished product after cutting edge, polish, check, packing for sale.
Claims (2)
1, a kind of glass-ceramics composite board is characterized in that it is composited by top glass-ceramic layer and following ceramic substrate tight bond.
2, a kind of production method of making the described glass-ceramics composite board of claim 1, it is characterized in that: it comprises the following steps:
(1) prepares a kind of glass ceramics frit, its composition range following (weight percent): SiO
258-65%; Al
2O
34-8%; KNaO 0-4%; CaO 15-25%; MgO 0-2%; BaO 0-2%; ZnO 4-9% and an amount of finings and tinting material, the glass frit preparation of this scope, carry out through the following steps: (1) evenly disposes admixtion by the mentioned component scope; (2) under 1400-1580 ℃ of temperature range, found into glass metal; (3) the glass metal water-cooled becomes the glass ceramics frit grain of 1-8mm scope, then oven dry or seasoning; (2) preparation ceramic substrate, its composition range is (weight percent): SiO
260-70%; Al
2O
313-20%; KNaO 3-8%; CaO 2-6%; MgO 0-2%; Fe
2O
30-2%; Its mineral composition scope is weathered feldspar, quartz, clay, Wingdale, calcite, lime carbonate, wollastonite; Carry out through the following step: (1) above-mentioned each mineral batching, evenly be mixed with admixtion by the composition scope, through wet ball grinding, spray drying granulation, the slurry fineness is the surplus 1-10% of 10000-hole sieve; (2) powder moisture content is 5-8%, and the powder particle is to be to be 50-90% on＜1%, 60 mesh sieves on 20 mesh sieves; (3) powder is shaped through the automatic brick pressing machine of pottery, and specification limit is 200 * 200mm to 1000 * 1000mm; (4) biscuiting in the 600-1200 temperature range.(3) the glass ceramics frit grain is uniformly distributed on the unglazed ceramic substrate, this frit grain thickness is 2-8mm, spray an amount of fixing agent, be positioned in the ceramic roller kiln and burn till, firing temperature is 1140-1250 ℃, firing period is 1-3.5 hour, and cooled work in-process become finished product after cutting edge, polish, check, packing.