DE102008061051A1 - Producing conductive structures on surface of polymer molded bodies, comprises providing polymer molded body from a polymer phase containing carbon nanotubes and thermally treating a surface of the polymer molded body - Google Patents

Producing conductive structures on surface of polymer molded bodies, comprises providing polymer molded body from a polymer phase containing carbon nanotubes and thermally treating a surface of the polymer molded body Download PDF

Info

Publication number
DE102008061051A1
DE102008061051A1 DE200810061051 DE102008061051A DE102008061051A1 DE 102008061051 A1 DE102008061051 A1 DE 102008061051A1 DE 200810061051 DE200810061051 DE 200810061051 DE 102008061051 A DE102008061051 A DE 102008061051A DE 102008061051 A1 DE102008061051 A1 DE 102008061051A1
Authority
DE
Germany
Prior art keywords
polymer
electrically conductive
circuit board
carbon nanotubes
printed circuit
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Withdrawn
Application number
DE200810061051
Other languages
German (de)
Inventor
Peter Putsch
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
PP-MID GmbH
PP MID GmbH
Original Assignee
PP-MID GmbH
PP MID GmbH
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by PP-MID GmbH, PP MID GmbH filed Critical PP-MID GmbH
Priority to DE200810061051 priority Critical patent/DE102008061051A1/en
Priority to US13/058,013 priority patent/US20110134617A1/en
Priority to CN200980139620.0A priority patent/CN102171770B/en
Priority to PCT/EP2009/005757 priority patent/WO2010015420A1/en
Priority to EP20090804527 priority patent/EP2311048B1/en
Publication of DE102008061051A1 publication Critical patent/DE102008061051A1/en
Withdrawn legal-status Critical Current

Abstract

Producing conductive structures on the surface of no or only slightly conductive polymer molded bodies, comprises: (a) providing a polymer molded body from at least one polymer phase containing carbon nanotubes; and (b) thermally treating at least one surface of the polymer molded body to produce the conductive structures on the surface of the polymer molded body, where the thermal treatment comprises heating at a temperature, which corresponds to at least the melting temperature of at least one polymer phase. Independent claims are included for: (1) the polymer molded body with conductive structures on the surface, produced by the above process, preferably comprising at least one polymer phase with carbon nanotubes, where the polymer molded body exhibits electrically or thermally conductive structure on the surface and the concentration of carbon nanotubes in the area of the electrically conductive surface structure is higher than in the non-electrically conductive surface area, and the non-electrically conductive surface area contains carbon nanotubes; (2) a printed circuit board-arrangement comprising at least one printed circuit board, which is preferably a polymer molded body, with at least one electrically conductive trace pitch, where the printed circuit board contains the polymer molded body with 0.1-10 wt.% of carbon nanotubes, relative to the mass of the polymer phase, and at least one electrically conductive trace pitch comprises a metal layer, preferably a copper layer, and/or at least one electronic component, which is bonded by an organic adhesive composition comprising 0.05-10 wt.% of carbon nanotubes, relative to the mass of the adhesive composition, and/or by a bond comprising the carbon nanotubes containing material, preferably one or more carbon nanotubes containing polymer phases, and/or by a solder connection with at least one electrically conductive trace pitch of the printed circuit board; (3) a process for producing the printed circuit board arrangement, comprising the steps (a) and (b), (c) galvanizing the electrically conductive structure with a metal, preferably copper, and/or (d) providing at least one electronic component, and (e) connecting, preferably thermally and/or electrically conductive connections, the electronic component having at least one electrically conductive trace pitch or at least an electrically conductive area using the adhesive composition, by producing a bond and/or by a solder connection; (4) use of an adhesive composition comprising carbon nanotubes for electrically conductive connecting of an electronic component with another electrically conductive component or molded part, preferably an electrically conductive trace pitch or an electrically conductive area on a trace pitch; and (5) use of a device for producing conductive structures on the surface of a polymer molded body of at least one polymer phase, where the device has an energy source with at least one electrode, which is provided to lose an energy with which the body to be processed is at least partially heated.

Description

Die Erfindung betrifft eine Leiterplatten-Anordnung, umfassend mindestens eine Leiterplatte mit mindestens einer elektrisch leitfähigen Leiterbahn und mindestens einem elektronischen Bauelement, wobei die Leiterplatte einen Polymerformkörper mit 0,1–10 Gew.-% Carbon Nanotubes (CNT), bezogen auf die Masse der Polymerphase/n, aufweist, und wobei das mindestens eine elektronische Bauelement durch eine organische Klebstoff-Zusammensetzung enthaltend 0,05–10 Gew.-% Carbon-Nanotubes (CNT), bezogen auf die Masse der Klebstoff-Zusammensetzung, mit mindestens einer elektrisch leitfähigen Leiterbahn der Leiterplatte verbunden ist. Des Weiteren betrifft die Erfindung eine erfindungsgemäß geeignete Klebstoff-Zusammensetzung und deren Verwendung, sowie ein Verfahren zum Aufbringen mindestens eines Bauelements auf eine Leiterplatte.The The invention relates to a printed circuit board assembly comprising at least a printed circuit board with at least one electrically conductive Conductor track and at least one electronic component, wherein the printed circuit board a polymer molding with 0.1-10 % By weight of carbon nanotubes (CNT), based on the mass of the polymer phase (s), and wherein the at least one electronic component by an organic adhesive composition containing 0.05-10 % By weight of carbon nanotubes (CNT), based on the mass of the adhesive composition, with at least one electrically conductive conductor track the circuit board is connected. Furthermore, the invention relates an inventively suitable adhesive composition and their use, as well as a method of applying at least a component on a circuit board.

Des Weiteren betrifft die Erfindung Leiterplatten-Anordnungen die Leiterplatten aus Polymerformkörpern umfassen, wobei die Leiterbahnen eine Kupferschicht aufweisen. Die Erfindung be trifft auch Verfahren zur Herstellung der erfindungsgemäßen Leiterplatten-Anordnungen.Of Furthermore, the invention relates to printed circuit board assemblies the printed circuit boards comprising polymer moldings, wherein the conductor tracks have a copper layer. The invention be also applies method Production of the printed circuit board arrangements according to the invention.

Elektrisch leitfähige Kunststoffe sind seit langem bekannt. US 4,404,125 beschreibt die Herstellung derartiger Kunststoffe durch Beimengung von Kohlenstofffasern, gegebenenfalls zusammen mit leitfähigen Rußen, in einen thermoplastischen Kunststoff. In US 4,664,971 werden an Stelle der Kohlenstofffasern elektrisch leitfähige Metallfasern eingesetzt. In all diesen Kunststoffmischungen sind große Mengen an elektrisch leitfähigen Zusatzstoffen erforderlich, die im Regelfall in einem Bereich von 10–30 Gew.-% liegen. Dennoch ist die elektrische Leitfähigkeit dieser Kunststoffe, insbesondere an der Oberfläche, noch nicht ausreichend für viele technische Anwendungen.Electrically conductive plastics have long been known. US 4,404,125 describes the production of such plastics by admixing carbon fibers, optionally together with conductive carbon blacks, into a thermoplastic. In US 4,664,971 In place of the carbon fibers, electrically conductive metal fibers are used. In all these plastic mixtures, large amounts of electrically conductive additives are required, which are usually in a range of 10-30 wt .-%. Nevertheless, the electrical conductivity of these plastics, especially on the surface, is not yet sufficient for many technical applications.

WO 02/19346 beschreibt den Einsatz metallbeschichteter Carbonfasern zur Herstellung elektrisch leitfähiger Kunststoffe. Hierbei wird z. B. ein energiereicher Laser eingesetzt, um den an der Oberfläche befindlichen Kunststoff zu verdampfen und die darunterliegenden Schichten der elektrisch leitfähigen Zusatzstoffe freizulegen. Ein Nachteil ist die dabei häufig auftretende Leitfähigkeit über das ganze Volumen des Kunststoffes, auch quer zur und über die laserbehandelte Bahn hinaus, und die resultierenden Probleme bei der Anordnung von nebeneinander liegenden Leiterbahnen. WO 02/19346 describes the use of metal-coated carbon fibers for the production of electrically conductive plastics. This z. As a high-energy laser used to evaporate the plastic located on the surface and expose the underlying layers of electrically conductive additives. One drawback is the conductivity which frequently occurs over the entire volume of the plastic, also transversely to and beyond the laser-treated web, and the resulting problems in the arrangement of adjacent printed conductors.

Ein anderes Verfahren zur Erzeugung elektrisch leitfähiger Strukturen auf beliebigen Substratmaterialien wird in der DD 263 179 beschrieben, wobei die Substratmaterialien mit einem elektrisch leitfähigen Zusatzstoff und Vernetzungsinitiatoren enthaltendem Prepolymer beschichtet, das Prepolymer durch Einwirken energiereicher Strahlen gezielt vernetzt und die nicht vernetzten Anteile der Kunststoffmischung mit Hilfe geeigneter Lösungsmittel wieder entfernt werden. Dieses Verfahren ist sehr aufwendig und mit nicht unerheblichen Problemen hinsichtlich einer ausreichenden Haftung der Strukturen auf der Substratoberfläche verbunden.Another method for producing electrically conductive structures on any substrate materials is disclosed in U.S. Patent Nos. 4,767,859 DD 263 179 described, wherein the substrate materials coated with an electrically conductive additive and crosslinking initiators containing prepolymer, the prepolymer selectively crosslinked by the action of high-energy radiation and the non-crosslinked portions of the plastic mixture with the aid of suitable solvents are removed. This method is very complex and associated with significant problems with respect to a sufficient adhesion of the structures on the substrate surface.

Die DE 102 59 498 beschreibt elektrisch leitfähige Thermoplaste, in denen neben teilchenförmigen Kohlenstoffmodifikationen wie Ruß oder Graphit auch Carbon Nanotubes (CNT) eingesetzt werden. Durch Zusatz von derartigen Kohlenstoff-Modifikationen lässt sich die elektrische Leitfähigkeit im Vergleich zu Metallfasern schon bei geringen Zusatzmengen realisieren. Die elektrische Leitfähigkeit verteilt sich dabei mehr oder weniger gleichmäßig über das gesamte Kunststoffvolumen und die Oberfläche. Dabei tritt die elektrische Leitfähigkeit in der Regel erst oberhalb einer gewissen Mindestzusatzmenge an elektrisch leitfähigen Zusatzstoffen auf. Unterhalb dieser Konzentration ist die Leitfähigkeit nahezu auf dem Ausgangsniveau der nicht leitfähigen Kunststoffe. Die Grenze, ab der Leitfähigkeit zu beobachten ist, richtet sich im Wesentlichen nach dem Kunststoff selbst, dem zugesetzten Füllstoff bzw. der zugesetzten Füllstoffmischung sowie nach den Misch- und Verarbeitungsbedingungen, denen die Kunststoffmischung unterzogen worden ist.The DE 102 59 498 describes electrically conductive thermoplastics in which carbon nanotubes (CNT) are used in addition to particulate carbon modifications such as carbon black or graphite. By adding such carbon modifications, the electrical conductivity compared to metal fibers can be realized even with small amounts added. The electrical conductivity is distributed more or less evenly over the entire plastic volume and the surface. The electrical conductivity usually occurs only above a certain minimum addition of electrically conductive additives. Below this concentration, the conductivity is almost at the initial level of the non-conductive plastics. The limit from which conductivity is observed depends essentially on the plastic itself, the added filler or the added filler mixture and on the mixing and processing conditions to which the plastic mixture has been subjected.

Um eine gute elektrische Leitfähigkeit zu erzielen, sind bei all diesen Verfahren ausreichende Mengen an Zusatzstoffen erforderlich und die Leitfähigkeit ist weitgehend gleichmäßig über das Volumen der Kunststoffformteils verteilt. Mit dem steigenden Füllgrad ist aber im Regelfall eine Verschlechterung der mechanischen Eigenschaften verbunden, so dass bei hohen Füllgraden beispielsweise die Zähigkeit sowie Zug- und Reißfestigkeit deutlich reduziert sind.Around To achieve a good electrical conductivity are at All these procedures require sufficient amounts of additives and the conductivity is largely uniform across the volume of the plastic molding distributed. With the rising Filling degree is but usually a deterioration of associated with mechanical properties, so at high fill levels for example, toughness and tensile and tear strength are significantly reduced.

Eine weitere Möglichkeit zur Erzeugung elektrisch leitfähiger Strukturen auf Oberflächen wurde von T. Dekker (Carbon-Nanotubes as Molecular Quantum Wires, Physics Today, S. 22-28, 1999) beschrieben. Hierbei werden Carbon Nanotubes aus der Gasphase auf einem Substrat abgeschieden. Dieses Verfahren ist ebenfalls mit einem hohen technischen Aufwand verbunden.Another possibility for producing electrically conductive structures on surfaces was T. Dekker (Carbon Nanotubes as Molecular Quantum Wires, Physics Today, pp. 22-28, 1999) described. Carbon nanotubes from the gas phase are deposited on a substrate. This method is also associated with a high technical complexity.

Elektronische Schaltkreise werden in der Regel durch Aufbringen einer Kupferschicht auf ein Substrat hergestellt, wobei die für den Schaltkreis nicht benötigten Teile der Kupferschicht durch chemische Prozesse weggeätzt werden. Die Herstellung solcher Schaltkreise ist in der Regel sehr aufwändig und umfasst viele Verfahrensschritte.electronic Circuits are usually made by applying a copper layer made on a substrate, taking care of the circuit unneeded parts of the copper layer by chemical Processes are etched away. The production of such circuits is usually very complex and involves many process steps.

Bei der Erzeugung von leitfähigen Strukturen kann insbesondere das Galvanisierverfahren eingesetzt werden. Um dieses Verfahren auch für Kunststoffoberflächen verwenden zu können, muss auf der Kunststoffoberfläche zuerst eine leitende Schicht aufgebracht werden, bevor auf galvanischem Wege eine metallische Schicht abgeschieden werden kann. Hierzu geeignete Verfahren sind bekannt und umfassen mehrere einzelne Behandlungsschritte, die aufwändig und umständlich sind. Es wäre daher vorteilhaft, wenn die Kunststoffoberflächen direkt galvanisiert werden könnten.at in particular, the generation of conductive structures the electroplating process can be used. To this procedure also to use for plastic surfaces, must first have a conductive on the plastic surface Layer are applied before galvanically a metallic layer can be deposited. Suitable methods for this purpose are known and include several individual treatment steps that are laborious and are awkward. It would therefore be advantageous when the plastic surfaces are galvanized directly could.

Eine Variante von Kunststoffbauteilen, die unter Verwendung des Galvanisierverfahrens erzeugt werden können sind Molded Interconnect Devices (MIDs). Bei diesen spritzgegossenen Bauteilen werden metallische Leiterbahnen auf Kunststoffträger aufgebracht. Diese MIDs können auf unterschiedliche Arten hergestellt werden. Eine Möglichkeit besteht darin, den Schaltungsträger im Zweikomponentenspritzguss herzustellen. Ein Kunststoff bildet hierbei den Grundkörper, ein weiterer ist metallisierbar und bildet das Leiterbahnlayout ab. In dem SKW-Verfahren wird zunächst die Leiterbahnstruktur als Vertiefung aus der nicht-metallisierbaren Komponente gespritzt. Anschließend werden diese Bereiche mit der metallisierbaren Komponente aufgefüllt. In den nachfolgenden Schritten werden die entsprechenden Metalle auf den metallisierbaren Kunststoff aufgebracht. Hierbei wird zu nächst die Oberfläche des metallisierbaren Kunststoffs aktiviert. Auf diese Oberfläche wird galvanisch Kupfer bis zur gewünschten Stärke aufgebracht.A Variant of plastic components made using the galvanizing process can be generated are Molded interconnect devices (MIDs). In these injection molded components are metallic Printed conductors applied to plastic substrates. These MIDs can be made in different ways. A Possibility is the circuit carrier in two-component injection molding. A plastic forms in this case the main body, another is metallizable and maps the trace layout. In the SKW procedure becomes first the conductor track structure as a recess of the non-metallizable component injected. Subsequently, these areas with the metallizable Component filled. In the following steps will be the corresponding metals applied to the metallizable plastic. In this case, the surface of the metallizable is next to Plastic activated. On this surface becomes galvanic Copper applied to the desired thickness.

Ein weiteres Problem in der Technik stellt das Befestigen der elektronischen Bauteile auf den Leiterplatten dar. Die Bauteile müssen hierbei auf einfache Weise so befestigt werden, dass optimale elektrische Eigenschaften erzielt werden können. Hierzu geeignete Klebstoffe sind beispielsweise aus der EP 0 914 027 oder EP 0 870 418 bekannt. Um eine elektrisch leitfähige Verbindung zwischen den Leiterbahnen und den elektronischen Bauelementen zu erzeugen werden den Kunststoffen hierbei elektrisch leitfähige Stoffe zugesetzt. Allerdings erreichen diese Klebeverbindungen oftmals nicht die gewünschte Leitfähigkeit und Festigkeit und es besteht insbesondere eine Bedarf an neuen Klebstoff-Zusammensetzungen die optimal mit den Eigenschaften der Leiterplatten zusammenwirken.Another problem in the art is the mounting of the electronic components on the printed circuit boards. The components must be fastened in a simple manner so that optimum electrical properties can be achieved. For this purpose, suitable adhesives are for example from EP 0 914 027 or EP 0 870 418 known. In order to produce an electrically conductive connection between the strip conductors and the electronic components, electrically conductive substances are added to the plastics. However, these adhesive bonds often do not achieve the desired conductivity and strength and, in particular, there is a need for new adhesive compositions which interact optimally with the properties of the printed circuit boards.

Eine Aufgabe der vorliegenden Erfindung ist es daher Leiterplatten-Anordnungen bereitzustellen, wobei die Leiterplatten Polymerformkörper umfassen, die elektrisch leitfähige Strukturen aufweisen, wobei die elektrisch leitfähigen Strukturen gegebenenfalls Kupfer enthalten. Zudem soll ein einfaches Verfahren zum Verbinden von elektronischen Bauteilen mit den Leiterplatten zur Verfügung gestellt werden.A Object of the present invention is therefore printed circuit board assemblies to provide, wherein the printed circuit boards polymer molding comprise, which have electrically conductive structures, where appropriate, the electrically conductive structures Copper included. In addition, a simple method for connecting of electronic components with the printed circuit boards available be put.

In einem ersten Aspekt betrifft die Erfindung daher einen Polymerformkörper mit leitfähigen, insbesondere elektrisch leitfähigen, Strukturen auf der Oberfläche, sowie ein Verfahren zur Herstellung dieser Polymerformkörper.In In a first aspect, therefore, the invention relates to a polymer molding with conductive, in particular electrically conductive, Structures on the surface, as well as a method for Production of these polymer moldings.

Eine Aufgabe der vorliegenden Erfindung war es, die bekannten Verfahren zur Erzeugung von leitfähigen Strukturen auf Polymerformkörpern zu vereinfachen und zu verbessern und insbe sondere Polymerformkörper mit besonders guten Eigenschaften zur Verfügung zu stellen.A Object of the present invention was the known methods for the production of conductive structures on polymer moldings to simplify and improve and in particular special polymer moldings to provide with particularly good properties.

Die oben beschriebene Aufgabe wird durch die hierin definierten Polymerformkörper und das Verfahren zu deren Herstellung gelöst.The The object described above is achieved by the shaped polymer bodies defined herein and solved the process for their preparation.

Im Rahmen der vorliegenden Erfindung wurde überraschenderweise festgestellt, dass das partielle Anschmelzen der Oberfläche eines Polymerformkörpers, der Carbon Nanotubes enthält, zu einer Migration der CNT an die Oberfläche des Polymerformkörpers führt. Durch gezieltes Anschmelzen der Oberfläche in definierten Bereichen ist es somit auf vorteilhafte Weise möglich, die Konzentration der CNT in diesen Bereichen zu erhöhen und die elektrische und thermische Leitfähigkeit dieser Bereiche zu erhöhen. Ein Nachweis für die höhere Konzentration der CNT in den elektrisch leitfähigen (thermisch behandelten) Bereichen kann z. B. über lichtmikroskopische oder elektronenmikroskopische Aufnahmen geliefert werden. Hierbei erscheinen beispielsweise bei einem Polymerformkörper aus Polycarbonat und CNT im Lichtmikroskop die Stellen mit hoher CNT-Dichte in schwarzer Farbe, wohingegen die Stellen mit geringer CNT-Dichte weiß sind.in the The scope of the present invention has been surprisingly found that the partial melting of the surface a polymer molding containing carbon nanotubes, to a migration of the CNT to the surface of the polymer molding leads. By targeted melting of the surface in defined areas, it is thus possible in an advantageous manner to increase the concentration of CNT in these areas and the electrical and thermal conductivity of these Increase areas. A proof of the higher Concentration of CNT in the electrically conductive (thermal treated) areas may z. B. on light microscopic or electron micrographs. in this connection appear, for example, in a polymer molding Polycarbonate and CNT in the light microscope, the sites with high CNT density in black color, whereas those with low CNT density are white.

Im Gegensatz dazu wurde im Rahmen der vorliegenden Erfindung überraschenderweise festgestellt, dass die Verwendung von Polymerformkörpern mit anderen elektrisch leitenden Zusatzstoffen nicht zu einer Migration der leitfähigen Stoffe an die Oberfläche führt. Beispielsweise führte das Anschmelzen von Polymerformkörpern mit leitfähigen Fasersystemen, wie z. B. Aluflakes (Hersteller Alufllakes der Fa. Silverline, GB; verwendete Polymermischung Polycarbonat/Polypropylen, siehe Beispiel) oder Stahlfasern nicht zu einer Migration der leitfähigen Fasern an die Oberfläche. Bei diesen Polymerformkörpern ist daher nur das oben beschriebene Verfahren aus WO 02/19346 anwendbar. Im erfindungsgemäßen Verfahren ist jedoch vorteilhafterweise kein Verdampfen des Polymers auf der Oberfläche des Polymerformkörpers notwendig.In contrast, it was surprisingly found in the present invention that the use of polymer moldings with other electrically conductive additives not to a Migration of conductive substances leads to the surface. For example, the melting of polymer moldings with conductive fiber systems, such as. Aluflakes (manufacturer Alufllakes of the company Silverline, GB, used polymer blend polycarbonate / polypropylene, see example) or steel fibers does not lead to a migration of the conductive fibers to the surface. In these polymer moldings, therefore, only the method described above is made WO 02/19346 applicable. In the process of the invention, however, advantageously no evaporation of the polymer on the surface of the polymer molding is necessary.

Bei dem erfindungsgemäßen Verfahren ist die Geschwindigkeit der Migration sowohl von der Viskosität der Polymerphasen, durch die sich die CNT bewegen müssen, als auch von der jeweilige Kompatibilität der Oberflächen der CNT und der Polymerphasen, und von der Behandlungsdauer, d. h. der Zeit, die den CNT zur Verfügung steht, um durch das aufgeschmolzene Polymer an die Oberfläche vorzudringen, abhängig. Je länger die Anschmelzung erfolgt, desto besser können die CNT an die Oberfläche wandern, und desto besser ist auch die Erhöhung der elektrischen Leitfähigkeit in den thermisch behandelten Bereichen.at the method according to the invention is the speed the migration of both the viscosity of the polymer phases, through which the CNT must move, as well as from the respective compatibility of the surfaces of the CNT and the polymer phases, and the duration of treatment, d. H. currently, which is the CNT available to melt through the Polymer to advance to the surface, depending. The longer the melting, the better the CNTs go to the surface, and the better the increase in electrical conductivity in the thermally treated areas.

Des Weiteren wurde überraschenderweise festgestellt, dass sich durch Dehnen oder Verbiegen des Polymerformkörpers der Oberflächenwiderstand desselben ändert. Insbesondere wird der Oberflächenwiderstand größer je mehr der Polymerformkörper gedehnt wird. Dies ermöglicht die Anwendung der erfindungsgemäßen Polymerformkörper in Dehnungsmessstreifen.Of Furthermore, it was surprisingly found that by stretching or bending the polymer molding of the Surface resistance of the same changes. Especially the surface resistance becomes larger the more the polymer molding is stretched. this makes possible the application of the polymer molding according to the invention in strain gauges.

Die vorliegende Erfindung betrifft daher nach einem Aspekt Polymerformkörper mit leitfähigen, insbesondere elektrisch leitfähigen, Strukturen auf der Oberfläche, sowie ein Verfahren zur Herstellung dieser Polymerformkörper.The The present invention therefore relates in one aspect to polymer moldings with conductive, in particular electrically conductive, Structures on the surface, as well as a method for Production of these polymer moldings.

Ein Polymerformkörper im Sinne der vorliegenden Erfindung ist ein beliebig geformter dreidimensionaler Körper oder eine Polymerschicht aus einem oder mehreren verschiedenen Polymeren, die nachfolgend sowohl für das erfindungsgemäße Verfahren als auch für die erfindungsgemäßen Polymerformkörper beschrieben werden.One Polymer molding in the context of the present invention an arbitrarily shaped three-dimensional body or a Polymer layer of one or more different polymers, the following both for the inventive Process as well as for the invention Polymer moldings are described.

Erfindungsgemäß geeignete Polymere sind Thermoplaste, Duroplaste, Elastomere sowie anorganische Polymere und Mischung daraus, bevorzugt werden Thermoplaste und Duroplaste verwendet. Bevorzugte Polymere sind Polycarbonat, Acrylnitril-Butadien-Styrol (ABS), Polyamide wie Polyamid 6 (PA 6), Polyamid 6.6 (PA 6.6), Polyamid 6.4 (PA 6.4)), Polyamid 12 (PA 12), aromatisches Polyamid, Polyvinylchlorid, Nylon 6,6, Polyvinylfluorid, Polyvinylidenfluorid, Polyphenylenether, Polystyrol, Polyolefine wie Polypropylen oder Polyethylen, Polysulfon, thermoplastisches Polyurethan, Polyethylenterephthalat, Polybutylenterephthalat, thermoplastische Elastomerlegierungen, Acetal, Styrol-Maleinsäureanhydrid, Butadien-Styrol, Polyetheretherketon, Polyethersulfon, Polytetrafluorethen, Polyalkylacrylate, Polymethylmethacrylat, ungesättigte Polyester, Polylactone, Polyepoxide, Polyimide, Polybutadiene, Polyphosphazene, Styrolmaleinsäureanhydrid (SMA), Styrolmethylmethacrylat (SMMA), Polysulfon, Polyvinylacetat und Polyacrylamid. Des Weiteren kann Phenolharz, Polyesterharz, natürlicher oder synthetischer Kautschuk oder Silikonkautschuk verwendet werden. Spezielle Beispiele anorganischer Polymere umfassen Phosphor basierte Verbindungen und Silikone. Die vorstehend aufgezählten Polymere können auf dem Fachmann bekannte Weise hergestellt und verarbeitet werden. Bevorzugterweise werden mindestens zwei, weiter bevorzugt mindestens drei, verschiedene Polymere zur Herstellung des Polymerformkörpers verwendet.According to the invention suitable Polymers are thermoplastics, thermosets, elastomers and inorganic Polymers and mixtures thereof, are preferred thermoplastics and Thermosets used. Preferred polymers are polycarbonate, acrylonitrile-butadiene-styrene (ABS), polyamides such as polyamide 6 (PA 6), polyamide 6.6 (PA 6.6), polyamide 6.4 (PA 6.4)), polyamide 12 (PA 12), aromatic polyamide, polyvinyl chloride, Nylon 6,6, polyvinyl fluoride, polyvinylidene fluoride, polyphenylene ether, Polystyrene, polyolefins such as polypropylene or polyethylene, polysulfone, thermoplastic polyurethane, polyethylene terephthalate, polybutylene terephthalate, thermoplastic elastomer alloys, acetal, styrene-maleic anhydride, Butadiene-styrene, polyetheretherketone, polyethersulfone, polytetrafluoroethene, Polyalkylacrylates, polymethyl methacrylate, unsaturated Polyesters, polylactones, polyepoxides, polyimides, polybutadienes, polyphosphazenes, Styrene maleic anhydride (SMA), styrene methyl methacrylate (SMMA), polysulfone, polyvinyl acetate and polyacrylamide. Furthermore Can be phenolic resin, polyester resin, more natural or synthetic Rubber or silicone rubber can be used. Special examples Inorganic polymers include phosphorus based compounds and Silicones. The polymers listed above may be prepared and processed in a manner known to those skilled in the art. Preferably, at least two, more preferably at least three, different polymers for the preparation of the polymer molding used.

Bevorzugte Polymerblends sind: Polycarbonat/Polyolefin (insbesondere Polypropylen oder Polyethylen), Polyethylenterephthalate (PET)/Polyvinylidenfluorid, PET/Nylon 6,6, PET/Polypropylen, PET/Polyethylenmischungen mit hoher Dichte, Polyamid 6 (PA6)/Acrylonitril-Butadiene-Styrol und Polycarbonat/Polyolefine (bevorzugt Polypropylen), Polyamid 6 (PA6)/Polyamid 12 (PA12), Polyamid 6.6 (PA 6.6)/Polyamid 12 (PA 12), aromatisches Polyamid/Polyamid 12 (PA 12), Polybutylenterephthalat/thermoplastisches Polyester, und Polyethylen terephthalat/thermoplastisches Polyester. Geeignete Polymerblends wurden beispielsweise von Wu et al. (Journal of applied polymer science, 2006, vol. 99, no2, pp. 477-488) im Zusammenhang mit CNT beschrieben. Bei Verwendung mehrerer verschiedener Polymere kann, je nach Eigenschaft der Polymere, ein einphasiges oder mehrphasiges System entstehen.Preferred polymer blends are: polycarbonate / polyolefin (especially polypropylene or polyethylene), polyethylene terephthalate (PET) / polyvinylidene fluoride, PET / nylon 6,6, PET / polypropylene, high density PET / polyethylene blends, polyamide 6 (PA6) / acrylonitrile-butadiene-styrene and polycarbonate / polyolefins (preferably polypropylene), polyamide 6 (PA6) / polyamide 12 (PA12), polyamide 6.6 (PA 6.6) / polyamide 12 (PA 12), aromatic polyamide / polyamide 12 (PA 12), polybutylene terephthalate / thermoplastic polyester, and polyethylene terephthalate / thermoplastic polyester. Suitable polymer blends have been used, for example, by Wu et al. (Journal of applied polymer science, 2006, vol. 99, no2, pp. 477-488) described in connection with CNT. When using a plurality of different polymers, depending on the property of the polymers, a single-phase or multi-phase system can arise.

Erfindungsgemäß besteht der Polymerformkörper bevorzugt aus mindestens zwei miteinander im Wesentlichen nicht mischbaren (phasenunverträglichen) Polymeren. Werden zwei oder mehr phasenunverträgliche Polymere verwendet, so können diese selbst nach dem Anschmelzen des Polymerformkörpers ein zwei- oder mehrphasiges System ausbilden. Phasenunverträgliche Systeme sind dem Fachmann bekannt. Werden die beiden Polymersorte vermengt, liegen sie in getrennten Phasen nebeneinander vor. Wird eine derartige Mischung über einen längeren Zeitraum in der Schmelze gehalten, koaleszieren die aus jeweils einer Polymersorte gebildeten Domänen, d. h. es findet eine Phasenseparierung statt.According to the invention, the polymer molding preferably consists of at least two mutually substantially immiscible polymers (phase incompatible). If two or more phase-incompatible polymers are used, they can form a two-phase or multi-phase system even after the polymer molding has melted on. Phase-incompatible systems are known to the person skilled in the art. If the two types of polymer are mixed, they are present side by side in separate phases. If such a mixture is kept in the melt for an extended period of time, they coalesce from one polymer each formed domains, ie there is a phase separation instead.

Beispielsweise sind Polymere, ausgewählt aus der Gruppe bestehend aus Polystyrol (PS), Polymethylmetacrylat (PMMA) und Acrylnitrit-Butadien-Styrol (ABS), sowie thermoplastischen Polyestern, wie Polyethylenterephthalat (PET) oder Polybutylenterephthalat (PBT), und Polycarbonate nicht mischbar mit Polypropylen und/oder Polypropylencopolymeren. Des Weiteren sind Polystyrol und Polyamid-6 nicht mit Polyethylen oder Polypropylen mischbar. Kombinationen aus zwei oder mehr der vorstehend genannten Polymere sind erfindungsgemäß bevorzugt, wobei die Verwendung von Polycarbonat in Kombination mit Polypropylen besonders bevorzugt ist.For example are polymers selected from the group consisting of Polystyrene (PS), polymethylmethacrylate (PMMA) and acrylonitrile-butadiene-styrene (ABS), as well as thermoplastic polyesters, such as polyethylene terephthalate (PET) or polybutylene terephthalate (PBT), and polycarbonates not miscible with polypropylene and / or polypropylene copolymers. Of Further, polystyrene and polyamide-6 are not polyethylene or Polypropylene miscible. Combinations of two or more of the above mentioned polymers are preferred according to the invention, the use of polycarbonate in combination with polypropylene is particularly preferred.

Bei Verwendung von Polypropylen und/oder einem Polypropylencopolymer in einem Gemisch mit dazu phasenunverträglichen Polymeren ist es bevorzugt, jeweils bezogen auf die gesamte Masse des Polymergemisches (inklusive der eventuell verwendeten Hilfsstoffe und Carbon Nanotubes), mindestens 40 Gew.-%, weiter bevorzugt mindestens 60 Gew.-%, noch weiter bevorzugt mindestens 80 Gew.-%, weiter bevorzugt mindestens 90 Gew.-%, und am meisten bevorzugt mindestens 99 Gew.-%, Polypropylen und/oder Polypropylencopolymer zu verwenden. Weitere bevorzugte Mengenbereich sind: 40 bis 99 Gew.-%, weiter bevorzugt 60 bis 95 Gew.-%, noch weiter bevorzugt 70 bis 95 Gew.-%, Polypropylen und/oder Polypropylencopolymer.at Use of polypropylene and / or a polypropylene copolymer in a mixture with phase-incompatible polymers it is preferred, in each case based on the total mass of the polymer mixture (including any auxiliary substances and carbon nanotubes), at least 40% by weight, more preferably at least 60% by weight, still more preferably at least 80% by weight, more preferably at least 90% by weight, and most preferably at least 99% by weight, of polypropylene and / or polypropylene copolymer. Further preferred Amount range are: 40 to 99 wt .-%, more preferably 60 to 95 Wt .-%, more preferably 70 to 95 wt .-%, polypropylene and / or Polypropylene copolymer.

Carbon Nanotubes (CNT), auch Kohlenstoffnanoröhrchen oder Kohlenstoffnanotubes genannt, sind aus Kohlenstoffatomen in bestimmter molekularer Anordnung ausgebildete, faserartige Strukturen. CNT bestehen aus Wandabschnitten, die Hohlräume umschließen. Die Wände sind hierbei aus Kohlenstoffatomen mit jeweils drei Bindungspartnern aufgebaut, die eine wabenartige Struktur aus Sechsecken bilden. Je nach Anordnung der Wandstrukturen spricht man von einlagigen Kohlenstoffnanotubes (single wall carbon nanotubes, SWCNT), die aus einzelnen Röhren aufgebaut sind und einen Innendurchmesser von 1–3 nm aufweisen, oder von mehrlagigen Kohlenstoffnanotubes (multi wall carbon nanotubes, MWCNT), die aus mehreren konzentrisch ineinander geschachtelten Röhren bestehen. Die Außendurchmesser der Carbon Nanotubes betragen zwischen 1 nm und 400 nm, wobei Carbon Nanotubes mit einem Außendurchmesser zwischen 10 und 400 nm häufig als Kohlenstoffnanofaser (Carbon Nano Fibre, CNF) bezeichnet werden.carbon Nanotubes (CNT), also carbon nanotubes or carbon nanotubes called, are made of carbon atoms in a certain molecular arrangement trained, fibrous structures. CNTs consist of wall sections, enclose the cavities. The walls are here made of carbon atoms with three bonding partners constructed, which form a honeycomb-like structure of hexagons. Depending on the arrangement of the wall structures one speaks of single-layered Kohlenstoffnanotubes (single wall carbon nanotubes, SWCNT), the are constructed of individual tubes and an inner diameter of 1-3 nm, or of multi-layered carbon nanotubes (multi wall carbon nanotubes, MWCNT) consisting of several concentric consist of nested tubes. The outside diameter The carbon nanotubes are between 1 nm and 400 nm, with carbon Nanotubes with an outer diameter between 10 and 400 nm often as a carbon nanofiber (Carbon Nano Fiber, CNF).

Die Herstellung von Carbon Nanotubes ist dem Fachmann bekannt und kann beispielsweise im Lichtbogenverfahren ( Iijima, Nature 354, 1991, 56-8 ) oder mittels Abscheideverfahren aus der Gasphase (Chemical Vapor Deposition, CVD) erfolgen ( P. M. Ajayan, Nanotubes from Carbon, Chem. Rev. 99, S. 1787-1799, 1999 ). Ein weiteres Verfahren ist in der WO 99/13127 , DE 19946182 und WO 98/39250 beschrieben. Hierbei dienen gepulste Laser zur Verdampfung von kohlenstoffhaltigen Materialien, die in einer Vakuumkammer angeordnet sind. Ein Teil der verdampften Kohlenstoffmoleküle kondensiert auf sogenannten Auffängern, deren Temperatur durch externe Heizung und Kühlung gesteuert wird wodurch das Wachstum von Nanoröhren bewirkt wird. Weitere Herstellungsmethoden umfassen beispielsweise Lichtbogen-, Laserablations und katalytische Verfahren. WO 86/03455 und WO 2006/050903 beschreiben Herstellungsverfahren, worin aliphatische oder aromatische Kohlenwasserstoffe in Gegenwart eines Eisen enthaltenden Katalysators bei Temperaturen von 800–900°C zersetzt werden. Bei den bekannten Verfahren werden oft Ruß, amorpher Kohlenstoff und Fasern mit hohen Durchmessern als Nebenprodukte gebildet. Bei der katalytische Abscheidung von Kohlenstoff aus gasförmigen Kohlenwasserstoffen (Catalytic Carbon Vapour Deposition) können beispielsweise Acetylen, Methan, Ethan, Ethylen, Butan, Buten, Butadien, oder Benzol verwendet werden. Als Katalysatoren können z. B. Metalle wie Fe oder Ni oder auch Metalloxide verwendet werden. Die unter Verwendung der vorstehenden Verfahren hergestellten Carbon Nanotubes fallen meist als CNT-Pulver an und können direkt mit den Polymeren vermischt werden.The production of carbon nanotubes is known to the person skilled in the art and can be carried out, for example, in the arc process (US Pat. Iijima, Nature 354, 1991, 56-8 ) or by means of vapor deposition processes (chemical vapor deposition, CVD) ( PM Ajayan, Nanotubes from Carbon, Chem. Rev. 99, pp. 1787-1799, 1999 ). Another method is in the WO 99/13127 . DE 19946182 and WO 98/39250 described. In this case, pulsed lasers are used for the vaporization of carbonaceous materials which are arranged in a vacuum chamber. Part of the vaporized carbon molecules condenses on so-called scavengers, whose temperature is controlled by external heating and cooling, which causes the growth of nanotubes. Other manufacturing methods include, for example, arc, laser ablation and catalytic processes. WO 86/03455 and WO 2006/050903 describe production processes in which aliphatic or aromatic hydrocarbons are decomposed in the presence of an iron-containing catalyst at temperatures of 800-900 ° C. In the known processes, carbon black, amorphous carbon and high-diameter fibers are often formed as by-products. In the catalytic deposition of carbon from gaseous hydrocarbons (Catalytic Carbon Vapor Deposition), for example, acetylene, methane, ethane, ethylene, butane, butene, butadiene, or benzene can be used. As catalysts z. As metals such as Fe or Ni or metal oxides can be used. The carbon nanotubes produced using the above methods are most likely to be CNT powders and can be mixed directly with the polymers.

Erfindungsgemäß werden bevorzugt CNT mit einem mittleren Durchmesser von 2 bis 100 nm, weiter bevorzugt 5 bis 80 nm, und besonders bevorzugt 6 bis 50 nm verwendet. Bevorzugt werden MWCNT verwendet. Des Weiteren ist dem Fachmann bekannt, dass die Carbon Nanotubes je nach Symmetrie bzw. Anordnung der Kohlenstoffsechsecke in den Röhrenwänden unterschiedliche Elektronenzustände aufweisen und somit Eigenschaften von Metallen oder Halbleitern aufweisen können. Je nach Anwendung wird der Fachmann daher die geeigneten, in der Literatur beschriebenen, Carbon Nanotubes auswählen können.According to the invention preferably CNT with an average diameter of 2 to 100 nm, more preferably 5 to 80 nm, and more preferably 6 to 50 nm used. Preference is given to using MWCNT. Furthermore, the Skilled in the art that the carbon nanotubes depending on the symmetry or Arrangement of carbon hexagons in the tube walls have different electronic states and thus Properties of metals or semiconductors may have. Depending on the application, the person skilled in the art, therefore, the appropriate, in the Literature described, carbon nanotubes can select.

Erfindungsgemäß können auch „funktionalisierte Carbon Nanotubes” verwendet werden, solange diese Carbon Nanotubes sich nicht derart mit den Polymeren verbinden, dass eine Migration verhindert wird. „funktionalisierte Carbon Nanotubes” weisen eine modifizierte Oberfläche auf und sind beispielsweise in US 6,203,814 und US 08/812,856 beschrieben."Functionalized carbon nanotubes" can also be used according to the invention as long as these carbon nanotubes do not combine with the polymers in such a way that migration is prevented. "Functionalized carbon nanotubes" have a modified surface and are for example in US 6,203,814 and US 08 / 812,856 described.

Anstelle von oder zusätzlich zu den Carbon Nanotubes können nach einer möglichen erfindungsgemäßen Ausführungsform auch Graphene anstelle der CNTs oder zusammen mit diesen eingesetzt werden. Graphene und Verfahren zu deren Herstellung sind dem Fachmann bekannt. Graphene sind einatomare Graphitschichten, die beispielsweise durch epitaktisches Aufwachsen auf einem Siliziumoxid-Substrat hergestellt werden können. CNTs sind erfindungsgemäß jedoch bevorzugt.Instead of of or in addition to the carbon nanotubes after a possible inventive Embodiment also graphene instead of the CNTs or together be used with these. Graphene and process for its preparation are known in the art. Graphenes are monatomic graphite layers, for example by epitaxial growth on a silica substrate can be produced. However, CNTs are according to the invention prefers.

Erfindungsgemäß bevorzugt werden Carbon Nanotubes in einem Mengenanteil (bezogen auf die Gesamtmasse der Polymerphase/n des Polymerformkörpers) verwendet, so dass der Polymerformkörper ohne die erfindungsgemäßen leitfähigen Strukturen nicht oder nur gering leitfähig ist. Bei reinen Polycarbonatwerkstoffen können daher beispielsweise insgesamt nur weniger als etwa 5 Gew.-% an CNT eingesetzt werden. Für Polypropylen können maximal etwa 8–10 Gew.-% CNT verwendet werden. Ein Fachmann wird je nach Anwendung des erfindungsgemäßen Polymerformkörpers die geeignete Gesamtmenge an CNT durch Testversuche bestimmen.According to the invention preferred are carbon nanotubes in a proportion (based on the total mass the polymer phase (s) of the polymer molding), so that the polymer molding without the inventive conductive structures not or only slightly conductive is. For pure polycarbonate materials, therefore, for example in total, only less than about 5% by weight of CNT can be used. For Polypropylene can not exceed about 8-10 wt .-% CNT be used. A person skilled in the art will depend on the application of the invention Polymer molding the appropriate total amount of CNT Determine test experiments.

Zusätzlich bevorzugt können im erfindungsgemäßen Verfahren bzw. in den erfindungsgemäßen Polymerformkörpern Nanocomposits verwendet werden. Derartige Stoffe und deren Anwendung sind dem Fachmann bekannt und beispielsweise in der EP 1 776 418 beschrieben. Bevorzugt werden hierbei Nano-Schichtsilikate, wie beispielsweise Aluminiumschichtsilikat, verwendet. Bevorzugterweise werden Nanocomposits in einem Anteil, bezogen auf die Gesamtmasse der Polymerphase/n im Poly merformkörper, von 0,1 bis 10 Gew.-%, vorzugsweise von 0,5 bis 5 Gew.-%, insbesondere bevorzugt von 0,5 bis 2 Gew.-% eingesetzt.In addition, nanocomposites may additionally be used in the process according to the invention or in the polymer moldings according to the invention. Such substances and their application are known in the art and, for example, in the EP 1 776 418 described. Nano-layered silicates, such as, for example, aluminum layered silicate, are preferably used here. Preferably, nanocomposites in a proportion, based on the total mass of the polymer phase / n in the poly merformkörper, from 0.1 to 10 wt .-%, preferably from 0.5 to 5 wt .-%, particularly preferably from 0.5 to 2 % By weight used.

Zusätzlich bevorzugt kann/können die Polymerphase/n des Polymerformkörpers weitere Stoffe enthalten, die die elektrische Leitfähigkeit des Polymerformkörpers erhöhen können. Beispielsweise können metallbeschichtete Carbonfaser oder ähnliches enthalten sein.additionally Preferably, the polymer phase (s) of the polymer molding can / can Other substances that contain the electrical conductivity of the polymer molding can increase. For example, metal-coated carbon fiber or the like be included.

Zusätzlich bevorzugt enthält der Polymerformkörper außer polymeren Bestandteilen, CNT und Nanocomposits maximal 20 Gew.-%, weiter bevorzugt maximal 10 Gew.-%, an weiteren Stoffen wie Verarbeitungshilfsmittel, Dispergierhilfsmittel, Haft- und Verträglichkeitsvermittler, Licht- und Alterungsschutzmittel, Farbstoffe etc.additionally Preferably, the polymer molding contains except polymeric constituents, CNT and nanocomposites not more than 20% by weight, more preferably not more than 10% by weight, of other substances, such as processing aids, Dispersing agents, adhesion and compatibilizer, Light and aging inhibitors, dyes, etc.

Der Ausdruck „elektrisch leitfähig”, so wie hier verwendet, bezeichnet einen Körper mit einem Oberflächenwiderstand von weniger als 109, bevorzugt weniger als 10 Ohm, weiter bevorzugt weniger als 105, und besonders bevorzugt weniger als 104 Ohm. Dementsprechend betreffen die Ausdrücke „nicht elektrisch leitfähig” und „gering elektrisch leitfähig”, so wie hier verwendet, einen Körper mit einem Oberflächenwiderstand von mehr als 109 Ohm, bevorzugt mehr als 107 Ohm, weiter bevorzugt mehr als 105, und besonders bevorzugt mehr als 104 Ohm. Durch das erfindungsgemäße Verfahren ist es möglich, den Oberflächenwiderstand in definierten Bereichen um den Faktor 10, insbesondere 100, insbesondere 1000 oder mehr zu verringern, um elektrisch leitfähige Strukturen zu erzeugen.The term "electrically conductive" as used herein refers to a body having a surface resistance of less than 10 9 , preferably less than 10 ohms, more preferably less than 10 5 , and most preferably less than 10 4 ohms. Accordingly, the terms "non-electrically conductive" and "low electrical conductivity" as used herein refer to a body having a surface resistance of greater than 10 9 ohms, preferably greater than 10 7 ohms, more preferably greater than 10 5 , and most preferably more than 10 4 ohms. The method according to the invention makes it possible to reduce the surface resistance in defined regions by a factor of 10, in particular 100, in particular 1000 or more, in order to produce electrically conductive structures.

Eine elektrisch leitfähige Struktur im Sinne der vorliegenden Erfindung ist eine geometrische Anordnung von elektrisch leitfähigen Bereichen auf der Oberfläche eines Polymerformkörpers, wobei die elektrisch leitfähigen Bereiche an elektrisch nicht leitfähige Bereiche auf der Oberfläche angrenzen. Insbesondere können die elektrisch leitfähigen Strukturen für elektronische Anwendungen ausgebildet sein. Die elektrisch leitfähigen Strukturen können daher beliebige geometrische Formen aufweisen, insbesondere die Form von Linien, Flächen oder Mustern, vorzugsweise immer abgegrenzt durch nicht behandelte (und somit nicht elektrisch leitfähige) Bereiche.A electrically conductive structure in the sense of the present Invention is a geometric arrangement of electrically conductive Areas on the surface of a polymer molding, wherein the electrically conductive regions to electrically adjoin non-conductive areas on the surface. In particular, the electrically conductive Structures for electronic applications be formed. The electrically conductive structures can therefore have any geometric shapes, in particular the shape of Lines, areas or patterns, preferably always delimited by untreated (and thus not electrically conductive) Areas.

Zusätzlich zu der elektrischen Leitfähigkeit erhöht sich auch die thermische Leitfähigkeit der thermisch behandelten Bereiche der Oberfläche des Polymerformkörpers. Dies ermöglicht weitere technische Anwendungsmöglichkeiten.additionally to the electrical conductivity increases also the thermal conductivity of the thermally treated Regions of the surface of the polymer molding. This allows further technical applications.

Das erfindungsgemäße Verfahren umfasst in einem ersten Schritt das Bereitstellen eines Polymerformkörpers aus mindestens einer Polymerphase, die Carbon Nanotubes (CNT) enthält.The inventive method comprises in a first Step, providing a polymer molding at least one polymer phase containing carbon nanotubes (CNT).

Hierbei wird/werden ein oder mehrere der oben aufgeführten Polymere, unter Schmelzen der Polymere, mit den Carbon Nanotubes vermischt. Die Vermischung der einzelnen Bestandteile kann in an sich beliebiger Weise erfolgen. Bekannte Verfahren zur Herstellung von Polymeren mit CNT bestehen darin, das synthetisierte Polymer, welches regelmäßig als Granulat, Pulver oder auch in Blockform vorliegt, durch Wärmezufuhr aufzuschmelzen und so in einen flüssig-viskosen Zustand zu überführen. Dadurch kann die Viskosität des Polymers abgesenkt, und die CNT in das Polymer eingemischt werden. Ein solches Verfahren kann der US 4,157,325 entnommen werden. Aus der kanadischen Offenlegungsschrift CA 2,324,353 A1 ist bekannt, Füllstoffe in ein Monomer einzumischen, eine in-situ-Polymerisation zu starten und den so synthetisierten Thermoplast nachfolgend aufzuschmelzen, um weitere Füllstoffe darin einzubringen. Hierbei können die Carbon Nanotubes vor oder während dem Schmelzvorgang zugeben werden.In this case, one or more of the polymers listed above are mixed with the carbon nanotubes while melting the polymers. The mixing of the individual components can be done in any desired manner. Known methods for producing polymers with CNT are to melt the synthesized polymer, which is present regularly as granules, powder or in block form, by supplying heat and thus to convert it into a liquid-viscous state. This can lower the viscosity of the polymer and mix the CNT into the polymer. Such a method may be the US 4,157,325 be removed. From the Canadian disclosure CA 2,324,353 Al It is known to mix fillers in a monomer, to initiate an in situ polymerization and subsequently to melt the thus synthesized thermoplastic in order to introduce further fillers therein. Here, the carbon nanotubes can be added before or during the melting process.

Zum Einmischen von Stoffen in niederviskose Kunststoffvorprodukte können beispielsweise die bekannten Dispergierverfahren unter Verwendung einer Perlmühle, Ultraschallsonde, einem Dreirollenwalzwerk oder einem Hochdruckdispergator eingesetzt werden. Zum Einmischen in hochviskose Kunststoffschmelzen finden die bekannten Verfahren wie z. B. der Einsatz von gleichlaufenden Doppelschneckenextrudern z. B. von der Fa. Coperion (DE) oder Fa. Leistritz (DE), von gegenläufigen Doppelschneckenextrudern Fa. Pomini (IT) und Fa. Farell (US) oder der von der Fa. Buss (CH) hergestellte Ko-Kneter Verwendung.To the Mixing of substances in low-viscosity plastic precursors can for example, the known dispersing using a bead mill, ultrasonic probe, a three-roll mill or a high-pressure disperser can be used. To interfere in high-viscosity plastic melts find the known methods such as z. B. the use of co-rotating twin-screw extruders z. B. from the company. Coperion (DE) or Fa. Leistritz (DE), of opposing Twin screw extruders from Pomini (IT) and Farell (US) or the co-kneader made by the company Buss (CH) use.

Diese Verfahren können auch eingesetzt werden, wenn phasenunverträgliche Polymere verwendet werden. Beispielsweise können Polypropylen und/oder Polypropylencopolymer mit phasenunverträglichen Polymeren auf diese Weise vermischt und dann gemeinsam aufgeschmolzen und vermengt werden. Bei Verwendung von Nanocomposits können diese ebenfalls vor oder während dem Aufschmelzen zugegeben werden.These Methods can also be used if phase incompatible Polymers are used. For example, polypropylene and / or polypropylene copolymer with phase incompatible Polymers are mixed in this way and then melted together and be mixed up. When using nanocomposites can these also added before or during the melting become.

Bevorzugterweise wird/werden die Polymerphase/n durch Vermischen von geschmolzenem Polymer mit 0,1–10 Gew.-% Carbon Nanotubes, bezogen auf die Gesamtmasse der Polymerphase/n des Polymerformkörpers, hergestellt.preferably, The polymer phase (s) are / are prepared by mixing molten Polymer with 0.1-10% by weight of carbon nanotubes, based on the total mass of the polymer phase (s) of the polymer molding, produced.

Zudem ist es möglich, das Vermischen aller Bestandteile in mehreren, aufeinander folgenden Arbeitsschritten durchzuführen. Beispielsweise kann zunächst ein Polymer mit den Carbon Nanotubes unter Schmelzen vermischt und das so erhaltene Masterbatch in einem nachfolgenden Schritt, beispielsweise nach dem Abkühlen und Granulieren, mit den übrigen Polymeren vermischt und geschmolzen werden. Die Herstellung derartiger Masterbatches ist z. B. in US 5,643,502 beschrieben. Durch den Einsatz derartiger Masterbatches kann die Verteilung der Carbon Nanotubes in der Kunststoffmasse verbessert werden.In addition, it is possible to carry out the mixing of all components in several successive steps. For example, a polymer may first be melt-mixed with the carbon nanotubes and the resulting masterbatch mixed and melted in a subsequent step, for example after cooling and granulation, with the remaining polymers. The preparation of such masterbatches is z. In US 5,643,502 described. By using such masterbatches, the distribution of the carbon nanotubes in the plastic composition can be improved.

Hierbei ist es zusätzlich bevorzugt, dass der Polymerformkörper durch Verschmelzen mindestens einer Polymerphase, die Carbon Nanotubes (CNT) in einem Anteil (bezogen auf die Polymerphase) zwischen 1 und 40 Gew.-%, weiter bevorzugt zwischen 5 und 30 Gew.-%, weiter bevorzugt 15 und 30 Gew.-%, enthält, mit mindestens einer weiteren Polymerphase mit geringerem Carbon Nanotubes (CNT)-Anteil, erhalten wird. Hierbei sollte der Gesamtgehalt an CNT dennoch nicht so hoch sein, dass der Polymerformkörper bereits ohne die erfindungsgemäßen leitfähigen Strukturen leitfähig ist. Die Polymerphasen mit unterschiedlichen Carbon Nanotubes (CNT)-Anteilen können hierbei, wie oben beschrieben, unter Verschmelzen der Polymere oder Polymergemische mit den Carbon Nanotubes erhalten werden. Weiter bevorzugt wird die Polymerphase mit dem höheren Carbon Nanotubes-Anteil in geringeren Gewichtsanteilen als die Polymerphasen mit niedrigeren Carbon Nanotubes-Anteilen verwendet. Bevorzugt weisen die Polymerphasen mit niedrigeren Carbon Nanotubes-Anteilen zwischen 0 und 10 Gew.-% CNT (bezogen auf die Polymerphase), weiter bevorzugt zwischen 0 und 5 Gew.-% CNT, auf. Bevorzugterweise wird die Polymerphase mit dem höheren Carbon Nanotubes-Anteil in einem Anteil zwischen 0,5 und 40 Gew.-%, weiter bevorzugt zwischen 1 und 40 Gew.-%, weiter bevorzugt zwischen 1 und 30 Gew.-%, weiter bevorzugt zwischen 1 und 20 Gew.-%, und am meisten bevorzugt zwischen 1 und 10 Gew.-%, bezogen auf die Gesamtmasse der Polymerphasen des Polymerformkörpers, enthalten sein.in this connection it is additionally preferred that the polymer molding by fusing at least one polymer phase, the carbon nanotubes (CNT) in a proportion (based on the polymer phase) between 1 and 40 wt .-%, more preferably between 5 and 30 wt .-%, more preferably 15 and 30 wt .-%, containing at least one other Polymer phase with lower carbon nanotubes (CNT) content, obtained becomes. Nevertheless, the total content of CNT should not be that high be that the polymer molding already without the inventive conductive structures is conductive. The polymer phases with different carbon nanotube (CNT) proportions here, as described above, with melting of the polymers or Polymer blends with the carbon nanotubes are obtained. Further preferred is the polymer phase with the higher carbon Nanotubes content in lower proportions by weight than the polymer phases used with lower carbon nanotube proportions. Preferably have the polymer phases with lower carbon nanotube portions between 0 and 10 wt .-% CNT (based on the polymer phase), more preferably between 0 and 5 wt .-% CNT, on. Preferably, the polymer phase with the higher carbon nanotubes share in one share between 0.5 and 40% by weight, more preferably between 1 and 40% by weight, more preferably between 1 and 30% by weight, more preferably between 1 and 20% by weight, and most preferably between 1 and 10% by weight, based on the total mass of the polymer phases of the polymer molding, be included.

Es hat sich überraschenderweise gezeigt, dass die Verwendung von zwei phasenunverträglichen Polymerphasen, von denen eine Polymerphase einen hohen Carbon Nanotubes-Anteil aufweist, eine besonders hohe Leitfähigkeit der erzeugten Strukturen ermöglicht. Es hat sich hierbei gezeigt, dass die Polymerphasen auch nach dem Schmelzen (bei der Herstellung des Polymerformkörpers) noch unterschiedliche Carbon Nanotubes-Anteile aufweisen. Im Gegensatz dazu führt die bekannte Verwendung von Masterbatches mit erhöhtem Ruß-Anteil, beispielsweise bei Verfahren zur Einfärbung von Polymerformkörpern, zu einer gleichmäßigen Verteilung der Rußpartikel auf die Polymerphasen.It Surprisingly, it has been shown that the use of two phase incompatible polymer phases, of which a polymer phase has a high carbon nanotube content, a particularly high conductivity of the structures produced allows. It has been shown that the polymer phases also after melting (in the preparation of the polymer molding) still have different carbon nanotubes shares. In contrast this is due to the familiar use of masterbatches increased soot content, for example, in processes for coloring polymer moldings, to a uniform distribution of the soot particles on the polymer phases.

Weiter bevorzugt wird hierbei die Polymerphase, die Carbon Nanotubes (CNT) in einem höheren Anteil enthält, aus einem oder mehreren Polymeren, ausgewählt aus der Gruppe bestehend aus Polycarbonat, Polystryrol, Acrylnitrit-Butadien-Styrol (ABS), Styrolmaleinsäureanhydrid (SMA), Styrolmethylmethacrylat (SMMA), Polymethylmethacrylat (PMMA), Polybutylenterephthalat (PBT), Polyethylenterephthalat (PET), Polyamid 6 (PA6), Polyamid 6.6 (PA 6.6), Polyamid 6.4 (PA6.4), Polyamid 12 (PA 12), aromatischem Polyamid, Polysulfon, hergestellt. Bevorzugterweise besteht diese Polymerphase zu mindestens 50 Gew.-%, weiter bevorzugt zu mindestens 60 Gew.-%, weiter bevorzugt zu mindestens 70 Gew.-%, noch weiter bevorzugt zu mindestens 80 Gew.-%, und am meisten bevorzugt zu mindestens 90 Gew.-% aus Polycarbonat.Further preferred here is the polymer phase containing carbon nanotubes (CNT) in a higher proportion of one or more polymers selected from the group consisting of polycarbonate, polystyrene, acrylonitrile-butadiene-styrene (ABS), styrene-maleic anhydride (SMA), styrene-methyl methacrylate (SMMA), polymethyl methacrylate (PMMA), polybutylene terephthalate (PBT), polyethylene terephthalate (PET), polyamide 6 (PA6), polyamide 6.6 (PA 6.6), polyamide 6.4 (PA6.4), polyamide 12 (PA 12), aromatic polyamide, Polysulfone, manufactured. Preferably, this polymer phase is at least 50 wt .-%, more preferably at least 60 wt .-%, more preferably at least 70 wt .-%, even more preferably to min at least 80% by weight, and most preferably at least 90% by weight, of polycarbonate.

Die gewünschten Polymerformkörper können dann auf übliche Weise durch Extrusions- oder Spritzgussverfahren aus den Polymergemischen erhalten werden.The desired polymer molding can then in the usual way by extrusion or injection molding are obtained from the polymer mixtures.

In einem zweiten Schritt des erfindungsgemäßen Verfahrens erfolgt eine thermische Behandlung mindestens einer Oberfläche des Polymerformkörpers zur Erzeugung der leitfähigen, insbesondere der elektrisch leitfähigen, Strukturen auf der Oberfläche des Polymerformkörpers, wobei die thermische Behandlung das Erhitzen des Bereichs der Oberfläche auf eine Temperatur umfasst, die mindestens der Schmelztemperatur der mindestens einen Polymerphase entspricht. Nach einer bevorzugten Ausführungsform erfolgt nach dem Abkühlen der thermisch behandelten Bereiche (bis sich die Polymerphasen wieder verfestigt haben), eine (oder auch mehrere) weitere thermische Behandlung derselben Bereiche.In a second step of the method according to the invention a thermal treatment of at least one surface takes place of the polymer molding to produce the conductive, in particular the electrically conductive structures the surface of the polymer molding, wherein the thermal treatment heating the area of the surface to a temperature that is at least the melting temperature which corresponds to at least one polymer phase. After a preferred Embodiment takes place after cooling the thermally treated areas (until the polymer phases are again solidified), one (or more) further thermal treatment same areas.

Bevorzugterweise erfolgt die thermische Behandlung der Oberfläche/n des Polymerformkörpers durch Kontakt mit einem erhitzten Körper, Gas (z. B. Heißluft) oder Flüssigkeit, oder durch elektromagnetische Strahlung oder unter Verwendung des erfindungsgemäßen Geräts (das unten beschrieben wird). Ein Fachmann kann das jeweils geeignete Mittel auswählen, um einen definierter Bereich der Oberfläche anzuschmelzen.preferably, the thermal treatment of the surface (s) of the Polymer molding by contact with a heated body, Gas (eg hot air) or liquid, or through electromagnetic radiation or using the invention Device (described below). A specialist can select each appropriate means to a defined Melt area of the surface.

Hierbei ist es möglich, die thermische Behandlung entweder nach vorhergehender Erzeugung des Polymerformkörpers, d. h. nachdem der Polymerformkörper das „Formwerkzeug” verlassen hat, oder bereits bei der Herstellung eines solchen Formkörpers im Formwerkzeug, durchzuführen. Es sind bereits Werkzeuge bekannt, bei denen einzelne Teile eines Formkörpers im Werkzeug gezielt erhitzt oder länger heiß gehalten werden können.in this connection is it possible to either post the thermal treatment previous generation of the polymer molding, d. H. after the polymer molding leave the "molding tool" has, or already in the production of such a shaped body in the mold, perform. There are already tools known in which individual parts of a shaped body in Tool specifically heated or kept hot for longer can be.

Bevorzugterweise wird jedoch elektromagnetische Strahlung zur thermischen Behandlung der Oberfläche des Polymerformkörpers verwendet. Weiter bevorzugt ist es hierbei, Laserstrahlung oder IR-Strahlung, weiter bevorzugt Laserstrahlung, zu verwenden. Hierbei können bekannte Lithographieverfahren zur gezielten Bestrahlung von definierten Bereichen von Substratoberflächen eingesetzt werden. Verfahren zur gezielten Bestrahlung von Oberflächen sind dem Fachmann bekannt und beispielsweise in der EP 0 847 329 A oder WO 02/079881 A offenbart.Preferably, however, electromagnetic radiation is used for the thermal treatment of the surface of the polymer molding. It is further preferred here to use laser radiation or IR radiation, more preferably laser radiation. In this case, known lithographic processes can be used for the targeted irradiation of defined areas of substrate surfaces. Methods for targeted irradiation of surfaces are known in the art and for example in the EP 0 847 329 A or WO 02/079881 A disclosed.

Geeignete Laser für das erfindungsgemäße Verfahren sind: He-Ne-Laser, Nd:YAG-Laser, Kohlendioxidlaser (CO2-Laser), Kohlenmonoxidlaser (CO-Laser), Stickstofflaser (N2-Laser), Argon-Ionen-Laser, Helium-Cadmium-Laser (HeCd-Laser), Krypton-Ionen-Laser, Sauerstoff-Ionen-Laser, Xenon-Ionen-Laser, Mischgas-Laser (beispielsweise mit Argon und Krypton), Excimerlaser, Metalldampflaser (beispielsweise Kupferdampflaser) und Metallhalogenid-Laser (beispielsweise Kupferbromid-Laser), bevorzugt sind Kohlendioxidlaser (CO2-Laser) und Nd:YAG-Laser.Suitable lasers for the method according to the invention are: He-Ne laser, Nd: YAG laser, carbon dioxide laser (CO 2 laser), carbon monoxide laser (CO laser), nitrogen laser (N 2 laser), argon ion laser, helium Cadmium lasers (HeCd lasers), krypton ion lasers, oxygen ion lasers, xenon ion lasers, mixed gas lasers (eg, argon and krypton), excimer lasers, metal vapor lasers (eg, copper vapor lasers), and metal halide lasers (For example, copper bromide laser), preferred are carbon dioxide (CO 2 ) laser and Nd: YAG laser.

Bevorzugterweise wird eine Stelle der Oberfläche des Polymerformkörpers für 0,001 bis 1 Sekunde erhitzt. Die Zeitdauer des Erhitzens bezieht sich hierbei auf die Zeitdauer, in der sich die Oberfläche des Polymerformkörpers in geschmolzenem Zustand befindet. Diese Zeitdauer kann vom Fachmann für die gewünschte Anwendung und die verwendeten Polymere leicht gewählt werden. Insbesondere ist es möglich, durch die Zeitdauer des Erhitzens, in der die Oberfläche angeschmolzen ist, den Oberflächenwiderstand einzustellen. Je länger die Oberfläche angeschmolzen wird und umso tiefer sich der angeschmolzene Bereich in die Oberfläche hinein erstreckt, desto mehr Carbon Nanotubes migrieren an die Oberfläche, wodurch die elektrische Leitfähigkeit der Struktur erhöht wird.preferably, becomes a position of the surface of the polymer molded body heated for 0.001 to 1 second. The period of heating refers to the length of time in which the surface of the polymer molding is in a molten state. This period of time can be selected by the person skilled in the art Application and the polymers used are easily chosen. In particular, it is possible, by the duration of the heating, in which the surface is melted, the surface resistance adjust. The longer the surface melted and the deeper the melted area gets into the surface extends into it, the more carbon nanotubes migrate to the surface, whereby the electrical conductivity of the structure increases becomes.

Es ist zusätzlich bevorzugt, dass die Oberfläche des Polymerformkörpers auf eine Temperatur erhitzt wird, die zum Schmelzen der Polymerphase/n ausreicht, jedoch nicht zu einem merklichen Verdampfen der Polymerphase/n führt. Der Ausdruck „merkliches Verdampfen” bedeutet hierbei, dass die erzeugte leitfähige Struktur weniger als 1 Mikrometer, weiter bevorzugt weniger als 500 nm, tief in der Oberfläche des Polymerformkörpers liegt.It is additionally preferred that the surface of the polymer molding is heated to a temperature which is sufficient to melt the polymer phase (s), but not too a noticeable evaporation of the polymer phase / s leads. Of the Expression "appreciable evaporation" means that the generated conductive structure is less than 1 micron, more preferably less than 500 nm, deep in the surface of the polymer molding is.

Das erfindungsgemäße Verfahren kann insbesondere zur Herstellung von elektronischen Schaltkreisen auf der Oberfläche des Polymerformkörpers verwendet werden. Somit können auf einfache Weise insbesondere sehr kleine Bauteile, beispielsweise als MIDs (moulded interconnected devices) hergestellt werden. Hierbei werden die Polymerformkörper erfindungsgemäß beispielsweise in einem Standard-Spritzgießverfahren als belie bige Formteile hergestellt und anschließend die elektrisch leitfähigen Strukturen erzeugt.The inventive method can in particular for Production of electronic circuits on the surface be used of the polymer molding. Thus, you can in a simple way, in particular very small components, for example produced as MIDs (molded interconnected devices). in this connection For example, the polymer moldings are used according to the invention in a standard injection molding as belie bige moldings and then the electrically conductive Structures generated.

Des Weiteren betrifft die Erfindung einen Polymerformkörper, umfassend mindestens eine Polymerphase und zwischen 0,01 und 10 Gew.-%, bevorzugt zwischen 0,1 und 10 Gew.-%, weiter bevorzugt zwischen 0,1 und 10 Gew.-%, weiter bevorzugt zwischen 0,1 und 8 Gew.-%, und am meisten bevorzugt zwischen 0,1 und 6 Gew.-%. Carbon Nanotubes (CNT) (bezogen auf die Gesamtmasse der Polymerphase/n des Polymerformkörpers), wobei der Polymerformkörper auf der Oberfläche elektrisch oder thermisch, bevorzugt elektrisch, leitfähige Strukturen aufweist, wobei die Konzentration der CNT in den Bereichen der leitfähigen Oberflächenstrukturen höher ist als in den nicht leitfähigen Oberflächenbereichen.Furthermore, the invention relates to a polymer molding comprising at least one polymer phase and between 0.01 and 10 wt .-%, preferably between 0.1 and 10 wt .-%, more preferably between 0.1 and 10 wt .-%, more preferably between 0.1 and 8 wt .-% , and most preferably between 0.1 and 6% by weight. Carbon nanotubes (CNT) (based on the total mass of the polymer phase / s of the polymer molding), wherein the polymer molding on the surface electrically or thermally, preferably electrically, having conductive structures, wherein the concentration of CNT in the regions of the conductive surface structures is higher than in the non-conductive surface areas.

Bevorzugterweise besteht der Polymerformkörper aus den im Vorangegangenen beschriebenen, insbesondere als bevorzugt erwähnten, Polymeren. Insbesondere bevorzugt enthält der Polymerformkörper mindestens eine Polymerphase die ein Polymer enthält, ausgewählt aus der Gruppe bestehend aus: Polycarbonat, Polystryrol, Acrylnitrit-Butadien-Styrol (ABS), Styrolmaleinsäureanhydrid (SMA), Styrolmethylmethacrylat (SMMA), Polymethylmethacrylat (PMMA), Polybutylenterephthalat (PBT), Polyethylenterephthalat (PET), Polyamid 6 (PA 6), Polyamid 6.6 (PA 6.6), Polyamid 6.4 (PA6.4), Polyamid 12 (PA 12), aromatischem Polyamid und Polysulfon, Polypropylen.preferably, the polymer molding consists of the above described, in particular as preferred mentioned, polymers. Particularly preferably, the polymer molding contains at least one polymer phase containing a polymer selected from the group consisting of: polycarbonate, polystyrene, acrylonitrile-butadiene-styrene (ABS), styrene-maleic anhydride (SMA), styrene methyl methacrylate (SMMA), Polymethyl methacrylate (PMMA), polybutylene terephthalate (PBT), polyethylene terephthalate (PET), polyamide 6 (PA 6), polyamide 6.6 (PA 6.6), polyamide 6.4 (PA6.4), Polyamide 12 (PA 12), aromatic polyamide and polysulfone, polypropylene.

Zusätzlich bevorzugt enthält der Polymerformkörper Nanocomposits. Geeignete Nanocomposits und geeignete Mengen wurden im Vorangegangenen beschrieben.additionally The polymer molding preferably contains nanocomposites. Suitable nanocomposites and appropriate amounts have been previously mentioned described.

In einer weiteren bevorzugten Ausführungsform der Erfindung weist der Polymerformkörper mindestens zwei getrennte Polymerphasen auf. Besonders bevorzugt enthält der Polymerformkör per mindestens zwei, weiter bevorzugt zwei, Polymerphasen, wobei die eine Polymerphase aus Polymeren besteht, ausgewählt aus der Gruppe bestehend aus Polystyrol (PS), Polymethylmetacrylat (PMMA) und Acrylnitrit-Butadien-Styrol (ABS), sowie thermoplastischen Polyestern, wie Polyethylenterephthalat (PET) oder Polybutylenterephthalat (PBT), und Polycarbonat, sowie Mischungen daraus. Die zweite Polymerphase besteht aus Polypropylen und/oder Polypropylencopolymeren. Alternativ dazu können die beiden Polymerphasen aus Polystyrol und/oder Polyamid-6 in Kombination mit Polyethylen und/oder Polypropylen bestehen. Besonders bevorzugt ist die Verwendung von Polycarbonat in Kombination mit Polyolefinen, insbesondere Polypropylen. Die bevorzugten Mengenanteile der Polypropylen und/oder Polypropylencopolymere sind im Vorangegangenen beschrieben.In a further preferred embodiment of the invention the polymer molding has at least two separate polymer phases on. The polymer molding composition particularly preferably comprises at least two, more preferably two, polymer phases, wherein the a polymer phase consists of polymers selected from the group consisting of polystyrene (PS), polymethyl methacrylate (PMMA) and acrylonitrile-butadiene-styrene (ABS), as well as thermoplastic polyesters, such as polyethylene terephthalate (PET) or polybutylene terephthalate (PBT), and polycarbonate, as well as mixtures thereof. The second polymer phase consists of polypropylene and / or polypropylene copolymers. alternative For this purpose, the two polymer phases of polystyrene and / or Polyamide-6 in combination with polyethylene and / or polypropylene consist. Particularly preferred is the use of polycarbonate in combination with polyolefins, in particular polypropylene. The preferred ones Amounts of polypropylene and / or polypropylene copolymers are described above.

Die Analyse des fertig gestellten Polymerformkörpers hinsichtlich der vorhandenen Polymerphase/n ist im Methodenteil beschrieben. Die leitfähigen Strukturen (mit erhöhtem CNT Anteil) auf der Oberfläche des Polymerformkörpers können, wie bereits erwähnt, mit üblichen optischen Messmethoden nachgewiesen werden. Weiter bevorzugt enthält eine der Polymerphasen einen höheren Anteil an Carbon Nanotubes (CNT) als die andere/n Phasen.The Analysis of the finished polymer molding in terms of the existing polymer phase (s) is described in the Methods section. The conductive structures (with increased CNT content) on the surface of the polymer molding, as already mentioned, with conventional optical measuring methods be detected. More preferably, one of the Polymer phases have a higher proportion of carbon nanotubes (CNT) as the other phases.

Es ist zudem bevorzugt, dass die elektrisch leitfähigen Strukturen des Polymerformkörpers maximal bis 10 μm, bevorzugt maximal bis 1 μm, weiter bevorzugt maximal bis 100 nm in das Innere des Polymerformkörpers (von der äußeren Oberfläche an gerechnet) hineinreichen.It is also preferred that the electrically conductive structures of the polymer molding to a maximum of 10 microns, preferably not more than 1 μm, more preferably not more than 100 nm in the inside of the polymer molding (from the outer Surface on).

In einer besonders bevorzugten Ausführungsform der Erfindung enthält der Polymerformkörper eine Polypropylenphase und eine Polycarbonatphase, wobei bevorzugterweise zwischen 50 und 80 Gew.-%, weiter bevorzugt zwischen 60 und 80 Gew.-%, und noch weiter bevorzugt zwischen 70 und 80 Gew.-% Polypropylen, bezogen auf die gesamte Masse des Polymergemisches, verwendet werden. Besonders geeignete Polycarbonate können, wie beispielsweise in DE 13 002 66 oder DE 14 957 30 beschrieben, hergestellt werden.In a particularly preferred embodiment of the invention, the polymer molding contains a polypropylene phase and a polycarbonate phase, preferably between 50 and 80% by weight, more preferably between 60 and 80% by weight, and even more preferably between 70 and 80% by weight. Polypropylene, based on the total mass of the polymer mixture used. Particularly suitable polycarbonates can be used, such as in DE 13 002 66 or DE 14 957 30 described, are produced.

Der erfindungsgemäße Polymerformkörper kann insbesondere so ausgestaltet sein, dass dessen elektrisch leitfähigen Oberflächenstrukturen Leiterbahnen bzw. elektronische Schaltkreise darstellen. Damit kann der Polymerformkörper als Platine in einem elektronischen Bauteil verwendet werden. Auf diese Platine können nach herkömmlichen Verfahren, wie beispielsweise Löten, Schweißen oder Ultraschall-Schweißen, beliebige Bauteile oder (elektronische) Bauelemente aufgebracht werden.Of the Polymer molding according to the invention can be designed in particular so that its electrically conductive Surface structures Circuits or electronic circuits represent. Thus, the polymer molding as a board be used in an electronic component. On this board can according to conventional methods, such as soldering, Welding or ultrasonic welding, any Components or (electronic) components are applied.

Ein weiterer Aspekt der Erfindung betrifft ein Gerät zur oben beschriebenen thermischen Behandlung mindestens einer Oberfläche des Polymerformkörpers zur Erzeugung der leitfähigen, insbesondere der elektrisch leitfähigen, Strukturen auf der Oberfläche des Polymerformkörpers.One Another aspect of the invention relates to a device for above described thermal treatment of at least one surface of the polymer molding to produce the conductive, in particular the electrically conductive structures the surface of the polymer molding.

Dieses Gerät zum Erzeugen einer Struktur an einem zu bearbeitenden Körper weist eine Energiequelle auf. Die Energiequelle weist mindestens eine Elektrode auf, über die Energie abgegeben werden kann. Diese abgegebene Energie erwärmt zumindest teilweise den zu bearbeitenden Körper und ermöglicht das oben beschriebene Aufschmelzen des Polymerformkörpers, um die gewünschten leitfähigen Strukturen zu erzeugen.This device for producing a structure on a body to be processed has an energy source. The energy source has at least one electrode, via which energy can be released. This released energy at least partially heats the body to be processed and allows the above-described melting of the polymer molding to produce the desired conductive structures gene.

Die Erfindung ist besonders geeignet, wenn der Körper ein Polymerformkörper aus mindestens einer Polymerphase ist, die Carbon-Nanotubes enthält, da in diesem Körper durch Anlegen einer Energie an ganz spezifischen Positionen die Leitfähigkeit verändert werden kann. Somit lassen sich Leiterbahnen auf einem zu bearbeitenden Körper ohne Aufbringen einer leitfähigen Material schicht und anschließendem Wegätzen der nicht-benötigten Bereiche der leitfähigen Materialschicht herstellen. Auf diese Weise werden Arbeitsschritte eingespart, die Produktion der Leiterplatte beschleunigt und so die Wirtschaftlichkeit der Produktion erhöht.The Invention is particularly suitable when the body is a polymer molding is at least one polymer phase containing carbon nanotubes, there in this body by applying an energy to very specific Positions the conductivity are changed can. Thus, tracks can be processed on one Body without applying a conductive material layer and then erasing the unneeded Create areas of the conductive material layer. On this way work steps are saved, the production of the PCB accelerates and so the profitability of the production elevated.

Der zu bearbeitende Körper lässt sich besonders effektiv erzeugen, wenn die Energiequelle mindestens zwei Elektroden aufweist, die an den zu bearbeitenden Körper anlegbar sind, wobei mit den zwei Elektroden ein Strom durch den zu bearbeitenden Körper leitbar ist bzw. eine Spannung anlegbar ist, der den zu bearbeitenden Körper aufwärmt und, wie weiter unten näher beschrieben, vorzugsweise in definierten Bereichen z. B. an der Oberfläche aufgeschmolzen. Durch diese einfache technische Maßnahme lassen sich am zu bearbeitenden Körper nach einer möglichen Ausführungsform auch dreidimensionale Strukturen erstellen, da die beiden Elektroden beispielsweise an der Vorderseite und an der Rückseite des zu bearbeitenden Körpers anlegbar sind. Beispielsweise lassen sich so auf einfache Weise Löcher in den zu bearbeitenden Körper einbrennen oder, im Falle der zuvor beschriebenen Leiterplatte, Kontaktierungen zwischen zwei Ebenen herstellen. Somit lassen sich mit dem Gerät der vorliegenden Erfindung kostengünstig Multilager-Leiterplatten herstellen.Of the The body to be processed is particularly effective generate if the energy source has at least two electrodes, which can be applied to the body to be processed, wherein with the two electrodes a current through the body to be processed is conductive or a voltage can be applied, the to be processed Body warms up and, as further below described, preferably in defined ranges z. B. at the Surface melted. Through this simple technical Measure can be taken on the body to be processed according to a possible embodiment also three-dimensional Create structures, as the two electrodes, for example, on the front and at the back of the machined Body can be applied. For example, it can be opened like this easy way holes in the body to be processed burn in or, in the case of the printed circuit board described above, Establish contacts between two levels. Thus can be inexpensive with the device of the present invention Produce multilayer printed circuit boards.

Zum Herstellen einfacher Leiterbahnen in einer Ebene des zu bearbeitenden Körpers kann eine Elektrode der Energiequelle an einem Punkt fixiert werden, wobei die andere Elektrode auf dem Körper beliebig bewegt wird, wodurch insbesondere im Falle einer Leiterplatte die elektrischen Leiterbahnen erzeugt werden. Alternativ können aber auch beide oder mehrere Elektroden gleichzeitig bewegt werden. Nach einer weiteren Ausführungsform der Erfindung können die beiden Elektroden auch mit einem Abstandshalter auf einem vorbestimmten Abstand zueinander gehalten werden, so dass beide Elektroden gemeinsam über den zu bearbeiten den Körper bei der Erzeugung der Struktur bewegt werden. Die Elektroden bzw. die dem Polymerformkörper zugewandten Teile davon, z. B. in Stiftform, können grundsätzlich jede beliebige Form aufweisen, wobei die Form in Hinblick auf die Form der gewünschten zu erzeugenden Leiterbahnen vom Fachmann frei wählbar ist. Auch die angelegte Spannung bzw. der Strom können frei gewählt werden, wobei der Fachmann in Abhängigkeit von dem verwendeten Polymerformkörper, dessen Zusammensetzung sowie dem Grad und Bereich der gewünschten Erwärmung des Formkörpermaterials die geeigneten Werte einfach empirisch ermitteln kann. In vielen Fällen wird z. B. eine Spannung von mehr als 500 V, insbesondere von 1000 V oder mehr günstig sein.To the Create simple traces in a plane of the machined Body can connect one electrode of the energy source to one Point to be fixed, with the other electrode on the body is moved arbitrarily, whereby, in particular in the case of a printed circuit board the electrical conductors are generated. Alternatively you can but also both or more electrodes are moved simultaneously. According to a further embodiment of the invention the two electrodes also with a spacer on a predetermined Distance apart, so that both electrodes together via to edit the body while creating the structure to be moved. The electrodes or the polymer molding facing parts thereof, z. B. in pencil form, in principle have any shape, wherein the shape in terms of Shape of the desired conductor tracks to be produced by a person skilled in the art is freely selectable. The applied voltage or the Electricity can be chosen freely, with the expert depending on the polymer molding used, its composition and the degree and range of the desired Heating the molding material the appropriate Simply empirically determine values. In many cases is z. B. a voltage of more than 500 V, in particular of 1000 V or more favorable.

Nach einer bevorzugten erfindungsgemäßen Ausführungsform wird eine erste Elektrode in einem ersten Bereich des Polymerformkörpers (bzw. seiner Oberfläche) an dem bereits eine Leitfähigkeit besteht bzw. erzeugt wurde, angelegt, während eine zweite Elektrode ausgehend von einem Punkt auf dem Polymerformkörpers (bzw. seiner Oberfläche), der in dem gleichen leitfähigen Bereich liegt, oder der mit diesem Bereich über einen leitfähigen Bereich (z. B. eine Leiterbahn) verbunden ist, über den Polymerformkörpers (bzw. seiner Oberfläche) bewegt, um eine (neue) Leiterbahn zu erzeugen, den leitfähigen Bereich zu vergrößern oder zwei bestehende leitfähige Bereiche (z. B. Leiterbahnen) zu verbinden. Diese Vorgehensweise ermöglicht eine große Flexibilität bei der Erzeugung bzw. Gestaltung der leitfähigen Strukturen auf dem Polymerformkörper.To a preferred embodiment of the invention becomes a first electrode in a first region of the polymer molding (or its surface) on the already a conductivity exists or created, while a second Electrode starting from a point on the polymer molding (or its surface), in the same conductive Range, or with this area via a conductive Area (such as a track) is connected via the Polymer molding (or its surface) moves, to create a (new) trace, the conductive Enlarge area or two existing conductive ones To connect areas (eg tracks). This approach allows a great deal of flexibility the generation or design of the conductive structures on the polymer molding.

Das Gerät gemäß der vorliegenden Erfindung kann nach einer möglichen Ausführungsform besonders effektiv in einen Plotter, in einen Matrixdrucker oder in einen Stift eingebaut werden. In einem Verfahren zum Erzeugen einer Struktur auf einem zu bearbeitenden Körper wird der zu bearbeitende Körper durch eine Energiequelle mit mindestens einer Elektrode, die zum Abgeben einer Energie vorgesehen ist, wenigstens teilweise erwärmt.The Apparatus according to the present invention may be particularly effective according to one possible embodiment built into a plotter, matrix printer or pen become. In a method for creating a structure on a The body to be processed becomes the body to be processed by an energy source having at least one electrode leading to Delivering an energy is provided, at least partially heated.

In dem Verfahren gemäß der Erfindung lassen sich die zuvor genannten Vorrichtungsmerkmale wirkungsgleich anwenden.In the method according to the invention can be apply the aforementioned device characteristics with the same effect.

Die Erfindung wird im Folgenden anhand zweier nicht einschränkender Ausführungsbeispiele näher beschrieben. In den Zeichnungen zeigen:The Invention will be described below with reference to two non-limiting Embodiments described in more detail. In the Drawings show:

1 eine Vorrichtung mit einem Gerät gemäß einem ersten Ausführungsbeispiel der vorliegenden Erfindung; 1 a device with a device according to a first embodiment of the present invention;

2 eine Vorrichtung mit einem Gerät gemäß einem zweiten Ausführungsbeispiel der Erfindung; 2 a device with a device according to a second embodiment of the invention;

3 das Gerät gemäß dem zweiten Ausführungsbeispiel der Erfindung; und 3 the device according to the second embodiment of the invention; and

4 das Gerät gemäß dem ersten Ausführungsbeispiel der Erfindung. 4 the device according to the first embodiment of the invention.

In den Figuren werden folgende Bezugszeichen verwendet:In the figures use the following reference numerals:

1010
Gerätdevice
12, 1412 14
Stiftepencils
16, 1816 18
Kontakt StiftContact pen
20, 2220 22
Kontakt SteckerContact plug
2424
Steckerplug
2626
Polymerkörperpolymer body
2828
Leiterbahnconductor path
3030
Umgebungsbereichsurrounding area
3232
Gezeichnete Liniendrawn lines
3434
Kontaktstellecontact point
3636
Unterseitebottom
3838
Gerätdevice
4040
Stiftpen
4242
Heizspiraleheating coil
4444
Schutzkörperprotective body
4646
Steckerplug

In einem ersten Ausführungsbeispiel der Erfindung, das in den 1 und 4 gezeigt ist, weist das Gerät 10 einen ersten Stift 12 und einen zweiten Stift 14 auf. Beide Stifte weisen jeweils an ihrer Unterseite einen Kontakt 16, 18 auf, die jeweils mit einem Kontakt 20, 22 eines Steckers 24 elektrisch verbunden sind.In a first embodiment of the invention, which in the 1 and 4 shown points the device 10 a first pen 12 and a second pen 14 on. Both pins each have a contact on their underside 16 . 18 on, each with a contact 20 . 22 a plug 24 are electrically connected.

Beim Anlegen der Kontakte 16, 18 der Stifte 12, 14 an einen Polymerkörper 26 aus mindestens einer Polymerphase mit Carbonnanotubes lässt sich, wenn die Kontakte 16, 18 der Stifte 12, 14 voneinander beabstandet sind und einen Strom durch den Polymerkörper 26 leiten, der Polymerkörper 26 gezielt erwärmen. Durch die gezielte Erwärmung des Polymerkörpers 26 lassen sich auf diesem Leiterbahnen 28 aufbringen, die den Strom aus den Kontakten 16, 18 der Stifte 12, 14 ebenfalls führen können. Wird beispielsweise der erste Stift 12 mit dem ersten Kontakt 20 an einer Position fest fixiert und nur der zweite Stift 14 mit dem zweiten Kontakt 18 auf der Leiterplatte bewegt, so ist der Abstand zwischen der bereits erzeugten Leiterbahn und der aktuellen Position des zweiten Kontaktes 18 abhängig von der Bewegungsgeschwindigkeit sehr gering. Aus diesem geringen Abstand folgt ein geringer Widerstand zwischen der Leiterbahn 28 und dem zweiten Kontakt 18, wodurch die Leiterbahn 26 in einem Umgebungsbereich 30 um den zweiten Kontakt 18 des zweiten Stiftes 14 erwärmt wird, und sich so die Leiterbahn 28 fortsetzt.When creating the contacts 16 . 18 of the pens 12 . 14 to a polymer body 26 from at least one polymer phase with carbon nanotubes can be when the contacts 16 . 18 of the pens 12 . 14 spaced apart and a current through the polymer body 26 lead, the polymer body 26 to heat specifically. By targeted heating of the polymer body 26 can be on this tracks 28 muster up the electricity from the contacts 16 . 18 of the pens 12 . 14 can also lead. For example, becomes the first pen 12 with the first contact 20 firmly fixed at one position and only the second pin 14 with the second contact 18 moved on the circuit board, so is the distance between the already created trace and the current position of the second contact 18 very low depending on the speed of movement. From this small distance follows a low resistance between the conductor track 28 and the second contact 18 , causing the conductor track 26 in a surrounding area 30 for the second contact 18 of the second pen 14 is heated, and so the trace 28 continues.

Auf praktische Weise können nach einer möglichen Ausführungsform die zu erzeugenden Leiterbahnen auf dem Polymerkörper 26 mit vorgezeichneten Linien 32 angedeutet werden, um den Herstellungsprozess der Leiterplatte zu unterstützen. Weiter können am Polymerkörper 26 Kontaktstellen 34 hergestellt werden, die den Polymerkörper 26 durchdringen. Dazu muss lediglich der zweite Stift 12 von dem Polymerkörper 26 entfernt werden, und an der Unterseite 36 des Polymerkörpers 26 in etwa unter der bereits erzeugten Leiterbahn 28 angebracht werden. Dadurch wird wieder über die Leiterbahn 28 ein Strom zwischen den beiden Kontakten 16, 18 der beiden Stifte 12, 14 geleitet, der die Kontaktstelle 34 durch den Polymerkörper 26 erzeugt.In a practical way, according to a possible embodiment, the printed conductors to be produced on the polymer body 26 with marked lines 32 be hinted to assist the manufacturing process of the circuit board. Further, on the polymer body 26 contact points 34 are prepared, which the polymer body 26 penetrate. All you need is the second pin 12 from the polymer body 26 be removed, and at the bottom 36 of the polymer body 26 approximately below the already created trace 28 be attached. This will turn over the track again 28 a current between the two contacts 16 . 18 the two pins 12 . 14 headed the contact point 34 through the polymer body 26 generated.

In den 2 und 3 ist ein Gerät gemäß einem zweiten Ausführungsbeispiel der Erfindung gezeigt. Danach umfasst das Gerät 38 einen Stift 40, an dessen Unterseite sich eine Heizspirale 42 anschließt. Diese Heizspirale ist vorzugsweise von einem Schutzkörper 44 umgeben. Der Schutzkörper kann dazu vorgesehen sein, die Erwärmung zu regulieren, oder aber auch um die Heizspirale 42 vor Verschmutzung oder anderen äußeren Einflüssen zu schützen. Weiter weist das Gerät 38 gemäß dem zweiten Ausführungsbeispiel der Erfindung einen Stecker 46 auf, mit dem die Heizspirale 42 mit elektrischer Energie versorgbar ist.In the 2 and 3 a device according to a second embodiment of the invention is shown. After that, the device includes 38 a pen 40 , on the underside of which is a heating spiral 42 followed. This heating coil is preferably of a protective body 44 surround. The protective body may be provided to regulate the heating, or else to the heating coil 42 to protect against contamination or other external influences. Next points the device 38 according to the second embodiment of the invention, a plug 46 on, with the heating coil 42 can be supplied with electrical energy.

Im Einsatz wird das Gerät 38, wie im ersten Ausführungsbeispiel gezeigt, über die vorgezeichneten Linien 32 gezogen, so dass die bereits diskutierten Leiterbahnen 28 entstehen. In der vorliegenden Ausführungsform ist es nicht notwendig, einen ersten Stift an einer vorbestimmten Stelle des Polymerkörpers 26 zu positionieren.In use is the device 38 as shown in the first embodiment, over the pre-drawn lines 32 pulled, so that the already discussed interconnects 28 arise. In the present embodiment, it is not necessary to have a first pin at a predetermined location of the polymer body 26 to position.

Mit der Erfindung lassen sich auf einfache Weise Strukturen auf einem Körper erzeugen, ohne dass es dem Auftragen eines Grundmaterials und dem Entfernen der nicht benötigten Stellen des Grundmaterials bedarf. Dadurch werden Prozessschritte bei der Herstellung gespart, so dass die Produktion des zu bearbeitenden Körpers wirtschaftlicher wird. Demnach betrifft ein weiterer Aspekt der vorliegenden Erfindung die Verwendung der vorstehend beschriebenen Geräte, Vorrichtungen und Verfahren zur Erzeugung von (leitfähigen) Strukturen auf Polymerformkörpern.With The invention can be easily structures on a Create body without it applying a base material and removing the unneeded locations of the base material needed. As a result, process steps are saved in the production, so that the production of the body to be worked more economically becomes. Accordingly, another aspect of the present invention relates the use of the devices, devices described above and methods for producing (conductive) structures on polymer moldings.

Die vorstehenden Geräte, Vorrichtungen und Verfahren bieten besondere Vorteile bei der Verwendung der erfindungsgemäßen Polymerformkörper mit leitfähigen Strukturen auf der Oberfläche, wobei auch Verfahren zu dessen Herstellung beschrieben werden.The provide the above devices, devices and methods particular advantages in the use of the invention Polymer moldings with conductive structures on the surface, including methods for its preparation to be discribed.

Für technische Anwendungen müssen elektronische Bauteile auf den leitfähigen Strukturen der erfindungsgemäßen Polymerformkörpern aufgebracht werden. Hierzu ist es einerseits notwendig, dass eine ausreichende Stabilität der Bauteile auf den Leiterplatten gewährleistet und andererseits eine elektrisch leitfähige Verbindung zwischen den Leiterbahnen und den elektronischen Bauteilen hergestellt wird.For technical applications need electronic components the conductive structures of the invention Polymer moldings are applied. This is on the one hand necessary that sufficient stability of the components guaranteed on the circuit boards and on the other hand a electrically conductive connection between the tracks and the electronic components is manufactured.

Im Rahmen der vorliegenden Erfindung wurde überraschend festgestellt, dass besonders vorteilhafte Leiterplatten-Anordnungen hergestellt werden können, wenn Polymerformkörper mit CNTs als Leiterplatten verwendet werden und auf die durch thermische Behandlung erzeugten leitfähigen Strukturen bzw. Leiterbahnen unter Verwendung einer erfindungsgemäßen organischen Klebstoff-Zusammensetzung, die ebenfalls CNTs enthält, elektronische Bauelemente aufgebracht werden. Überraschenderweise ermöglicht die Verwendung eines CNT-haltigen Klebstoffes auf einer CNT-haltigen Leiterplatte eine besonders gute Fixierung der elektronischen Bauteile. Hingegen führt die Verwendung von Klebstoffen mit leitfähigen Stoffen wie beispielweise Silberpartikeln zu einer schlechten Adhäsion auf CNT-haltigen Substraten.in the Within the scope of the present invention, it has surprisingly been found that produces particularly advantageous printed circuit board assemblies can be when polymer moldings with CNTs can be used as printed circuit boards and on by thermal Treatment generated conductive structures or tracks using an organic according to the invention Adhesive composition, which also contains CNTs, electronic components are applied. Surprisingly allows the use of a CNT-containing adhesive on a CNT-containing circuit board a particularly good fixation the electronic components. On the other hand leads the use of adhesives with conductive substances such as Silver particles cause poor adhesion to CNT-containing Substrates.

Hierbei hat sich gezeigt, dass besonders gute elektrische Eigenschaften durch die kombinierte Verwendung eines CNT-haltigen Klebstoffs und einer CNT-haltigen Leiterplatte erzielt werden.in this connection has been shown to have particularly good electrical properties by the combined use of a CNT-containing adhesive and a CNT-containing circuit board can be achieved.

Eine bevorzugte Leiterplatten-Anordnung umfasst daher mindestens eine Leiterplatte mit mindestens einer elektrisch leitfähigen Leiterbahn und mindestens einem elektronischen Bauelement, wobei die Leiterplatte einen Polymerformkörper mit 0,1–10 Gew.-%, weiter bevorzugt 1–10 Gew.-%, und noch weiter bevorzugt 5–10 Gew.-%, Carbon Nanotubes (CNT), bezogen auf die Masse der Polymerphase/n, umfasst, und wobei das mindestens eine elektronische Bauelement durch eine organische Klebstoff-Zusammensetzung enthaltend 0,05–10 Gew.-%, weiter bevorzugt 0,1–10 Gew.-%, weiter bevorzugt 1–10 Gew.-%, und am meisten bevorzugt 5–10 Gew.-%, Carbon-Nanotubes (CNT), bezogen auf die Masse der Klebstoff-Zusammensetzung, mit mindestens einer elektrisch leitfähigen Leiterbahn der Leiterplatte verbunden ist. Die elektrisch leitfähigen Leiterbahnen werden hierbei durch Bereiche der Oberfläche des Polymerformkörpers gebildet, die eine erhöhte CNT-Konzentration aufweisen.A preferred circuit board assembly therefore comprises at least one Printed circuit board with at least one electrically conductive Conductor track and at least one electronic component, wherein the printed circuit board a polymer molding with 0.1-10 Wt%, more preferably 1-10 wt%, and still more preferably 5-10 Wt .-%, carbon nanotubes (CNT), based on the mass of the polymer phase / n, includes, and wherein the at least one electronic component by an organic adhesive composition containing 0.05-10 Wt .-%, more preferably 0.1-10 wt .-%, more preferably 1-10% by weight, and most preferably 5-10% by weight, Carbon Nanotubes (CNT), based on the mass of the adhesive composition, with at least one electrically conductive conductor track the circuit board is connected. The electrically conductive Tracks are here by areas of the surface of the polymer molding, which has an increased CNT concentration exhibit.

Für die Leiterplatten-Anordnung können alle erfindungsgemäßen Klebstoff-Zusammensetzungen, die hier beschrieben sind, verwendet werden. Besonders bevorzugt wird ein Urethanacrylat-Klebstoff verwendet. Weiter bevorzugt weist die Verbindung zwischen der mindestens einen elektrisch leitfähigen Leiterbahn und dem mindestens einen elektronischen Bauelement einen elektrischen Widerstand von weniger als 50 Ohm auf.For the circuit board assembly can all of the invention Adhesive compositions described herein are used become. More preferably, a urethane acrylate adhesive is used. Further Preferably, the connection between the at least one electrically conductive trace and the at least one electronic Component has an electrical resistance of less than 50 ohms on.

Des Weiteren betrifft die Erfindung eine Klebstoff-Zusammensetzung enthaltend 0,05–10 Gew.-% Carbon-Nanotubes (CNT). Die Klebstoff-Zusammensetzung kann durch Vermischen der CNTs mit den Klebstoff-Komponenten erfolgen. Hierzu geeignete Verfahren sind dem Fachmann bekannt.Of Furthermore, the invention relates to an adhesive composition containing 0.05-10 wt% carbon nanotubes (CNT). The adhesive composition can be done by mixing the CNTs with the adhesive components. Suitable methods for this purpose are known to the person skilled in the art.

Bevorzugterweise kommen hierbei solche Klebstoffe zum Einsatz, welche eine Substanz enthalten, die unter Einfluss von Strahlung oder Wärme reagieren oder eine Substanz freisetzen, die mit den reaktiven Bestandteilen des Klebstoffs reagieren oder deren Po lymerisation auslösen oder katalysieren. Bevorzugt enthält die Klebstoff-Zusammensetzung Acrylat-Klebstoffe, Phenol-Formaldehydharz-Klebstoffe, Silicon-Klebstoffe, oder Polyurethan-Klebstoffe, bevorzugt Acrylat-Klebstoffe. Weiter bevorzugt ist die Klebstoffzusammensetzung ausgewählt aus der Gruppe bestehend aus Cyanacrylat-Klebstoffen, Methylmethacrylat-Klebstoffen, Urethanacrylat-Klebstoff, Butylacrylat, und strahlenhärtbaren Acrylat-Klebstoffen, insbesondere wird ein Urethanacrylat-Klebstoff verwendet. Besonders bevorzugt besteht die erfindungsgemäße Klebstoffzusammensetzung nur aus CNTs und den vorgenannten Klebstoffen oder Gemischen davon.preferably, In this case, such adhesives are used, which are a substance contain those under the influence of radiation or heat react or release a substance containing the reactive ingredients react the adhesive or cause their Po lymerisation or catalyze. Preferably, the adhesive composition contains Acrylate adhesives, phenol-formaldehyde resin adhesives, silicone adhesives, or polyurethane adhesives, preferably acrylate adhesives. Further Preferably, the adhesive composition is selected from the group consisting of cyanoacrylate adhesives, methyl methacrylate adhesives, urethane acrylate adhesive, Butyl acrylate, and radiation curable acrylate adhesives, In particular, a urethane acrylate adhesive is used. Especially The adhesive composition according to the invention preferably exists only from CNTs and the aforementioned adhesives or mixtures thereof.

Bevorzugterweise beträgt der elektrische Widerstand der Klebstoff-Zusammensetzung weniger als 100, insbesondere weniger als 50 Ohm.preferably, is the electrical resistance of the adhesive composition less than 100, especially less than 50 ohms.

Die vorliegende Erfindung betrifft zudem die Verwendung einer erfindungsgemäßen Klebstoff-Zusammensetzung zum elektrisch leitfähigen Verbinden eines elektronischen Bauelements mit einem anderen elektrisch leitfähigen Bauteil oder Formteil, insbesondere einer elektrisch leitfähigen Leiterbahn oder einem elektrisch leitfähigen Bereich auf einer Leiterbahn.The The present invention also relates to the use of a method according to the invention Adhesive composition for electrically conductive bonding an electronic component with another electrically conductive Component or molded part, in particular an electrically conductive Conductor or an electrically conductive area a trace.

Des Weiteren betrifft die Erfindung ein Verfahren zum Aufbringen mindestens eines elektronischen Bauelements auf eine Leiterplatte umfassend die folgenden Schritte:

  • a) Bereitstellen einer Leiterplatte mit mindestens einer elektrisch leitfähigen Leiterbahn oder mindestens einem elektrisch leitfähigen Bereich, wobei die Leiterplatte einen Polymerformkörper mit 0,1–10 Gew.-% Carbon Nanotubes (CNT), bezogen auf die Masse der Polymerphase/n, darstellt,
  • b) Bereitstellen mindestens eines elektronischen Bauelements, und
  • c) Verbinden des elektronischen Bauelements mit der elektrisch leitfähigen Leiterbahn unter Verwendung der erfindungsgemäßen Klebstoff-Zusammensetzung gemäß.
Furthermore, the invention relates to a method for applying at least one electronic component to a printed circuit board, comprising the following steps:
  • a) providing a printed circuit board having at least one electrically conductive strip or at least one electrically conductive region, wherein the printed circuit board is a polymer molded article with 0.1-10 wt .-% carbon nanotubes (CNT), based on the mass of the polymer phase / s,
  • b) providing at least one electronic component, and
  • c) connecting the electronic component to the electrically conductive conductor track using the adhesive composition according to the invention according to.

Bevorzugterweise wird in Schritt a) des Verfahrens der Polymerformkörper mit elektrisch leitfähigen Strukturen mit dem erfindungsgemäßen Verfahren, wie im Vorangegangenen beschrieben, hergestellt. Bevorzugterweise wird hierbei mit dem erfindungsgemäßen Gerät eine leitfähige Struktur erzeugt.preferably, in step a) of the process, the polymer molding with electrically conductive structures with the invention Process as described above. preferably, is in this case with the device according to the invention generates a conductive structure.

Geeignete elektronische Bauteile, die auf Leiterplatten aufgebracht werden können, sind dem Fachmann bekannt. Diese Bauteile weisen üblicherweise „metallische Beinchen” auf, die in Kontakt mit der Leiterplatte bzw. den hierauf befindlichen leitfähigen Strukturen gebracht werden müssen. Da die erfindungsgemäße Klebstoffzusammensetzung leitfähig ist, kann sich auch Klebstoff zwischen den Beinchen und der leitfähigen Struktur befinden. Um die Bauteile auf die Leiterplatte aufzubringen, können die Beinchen der Bauteile beispielsweise in die Klebstoff-Zusammensetzung eingetaucht werden und anschließend auf die Leiterplatte aufgesetzt werden. Dabei muss die Menge an Klebstoff so gewählt werden, dass eine ausreichende Stabilität zwischen dem Bauteil und der Leiterplatte erzeugt wird, jedoch keine benachbarten Leiterbahnen mit Klebstoff in Kontakt kommen. Das Aushärten der Klebstoff-Zusammensetzung kann dann auf übliche Weise, beispielsweise unter Verwendung einer UV-Lampe, erfolgen.suitable electronic components that are applied to printed circuit boards can, are known in the art. These components usually have "metallic Little bit "in contact with the printed circuit board or placed on the conductive structures located thereon Need to become. As the adhesive composition of the invention Conductive is also adhesive between the legs and the conductive structure are located. To the components can apply to the circuit board, the legs of the components, for example, immersed in the adhesive composition and then placed on the circuit board become. The amount of adhesive must be chosen that sufficient stability between the component and the circuit board is produced, but no adjacent tracks come in contact with adhesive. Curing the adhesive composition can then in the usual way, for example, using a UV lamp, done.

Ein weiterer Aspekt der Erfindung betrifft eine Leiterplatten-Anordnung, wobei die Leiterplatte einen erfindungsgemäßen Polymerformkörper umfasst. Der erfindungsgemäße Polymerformkörper kann, wie oben beschrieben, hergestellt und mit elektrisch leitfähigen Strukturen bzw. Leiterbahnen versehen werden. Um die elektrische Leitfähigkeit der Strukturen mit erhöhter CNT-Konzentration weiter zu erhöhen ist es bevorzugt, eine Kupferschicht aufzubringen.One Another aspect of the invention relates to a printed circuit board assembly, wherein the circuit board according to the invention Polymer molding comprises. The inventive Polymer molding may be prepared as described above and with electrically conductive structures or conductor tracks be provided. To the electrical conductivity of the structures continue to increase with increased CNT concentration it is preferable to apply a copper layer.

Überraschenderweise wurde im Rahmen der vorliegenden Erfindung festgestellt, dass die Polymerformkörper mit den elektrisch leitfähigen Strukturen direkt in einem Galvanisierverfahren verwendet werden können und eine Kupferschicht direkt gezielt auf die Polymerformkörper aufgebracht werden kann. Im Vergleich zu bisher verwendeten Galvanisierverfahren für Polymerformkörper entfallen daher die bislang notwendigen folgenden Schritte: Beizen, Aktivieren und Erzeugung einer Zwischenschicht (siehe beispielsweise ”Kunststoffgalvanisierung”, LPW-Taschenbuch für Galvanotechnik, Band 1, Verfahrenstechnik, 13. Ausgabe 1988, Seiten 443 bis 449 ). Erfindungsgemäß kann daher beispielsweise nach der Reinigung der Oberfläche des Polymerformkörpers der Schichtaufbau direkt erfolgen.Surprisingly, it was found in the context of the present invention that the polymer moldings having the electrically conductive structures can be used directly in a galvanizing process and a copper layer can be applied directly to the polymer moldings directly. In comparison to previously used electroplating processes for polymer moldings, the steps which have hitherto been necessary are therefore eliminated: pickling, activation and generation of an intermediate layer (see, for example, US Pat "Kunststoffgalvanisierung", LPW Taschenbuch für Galvanotechnik, Volume 1, Process Engineering, 13th Edition 1988, pages 443 to 449 ). According to the invention, therefore, the layer structure can be carried out directly, for example, after the surface of the polymer molding has been cleaned.

Überraschenderweise ist es auch möglich, die erfindungsgemäßen Polymerformkörper mittels badfreier Galvanisierung mit einem Metall zu beschichten. Hier kann auf das übliche Eintauchen der zu beschichtenden Werkstücke in elektrolytgefüllte Behälter, die so genannten Galvanisierbäder, verzichtet werden. Stattdessen werden die benötigten Elektrolyte von saugfähigen Materialien aufgenommen, die wiederum von Beschichtungswerkzeugen gehalten werden. Durch Anpressen der Werkzeuge an die zu beschichtende Bauteiloberfläche wird die Abscheidung ermöglicht, wobei der benötigte Gleichstrom ebenfalls vom Werkzeug übertragen wird.Surprisingly it is also possible, the invention Polymer moldings by means of bath electroplating with to coat a metal. Here can be on the usual Immersion of the workpieces to be coated in electrolyte-filled Containers, the so-called galvanizing, waived become. Instead, the required electrolytes of Absorbent materials added, in turn, by coating tools being held. By pressing the tools to be coated Component surface allows the deposition, wherein the required DC also transmitted from the tool becomes.

Hierbei wird die Leiterplatte mit den leitfähigen Strukturen auf übliche Weise in ein elektrolytisches Galvanisierungsbad eingebracht (siehe beispielsweise ”Kunststoffgalvanisierung”, LPW-Taschenbuch für Galvanotechnik, Band 1, Verfahrenstechnik, 13. Ausgabe 1988, Seiten 443 bis 449 ). Das Galvanisierbad enthält beispielsweise eine Kupfer(II)-sulfat-Lösung mit einer Anode. Durch das Anlegen einer negativen Spannung (Kathode) an die elektrisch leitfähigen Strukturen auf der Oberfläche der Polymerformkörpern sowie an die Gegenelektrode aus Kupfer kann ge zielt Kupfer aus der Lösung auf den Strukturen abgeschieden werden und eine metallische Schicht bilden. Die hierzu geeigneten Elektrolytlösungen, das elektrische Spannungspotential sowie die geeignete Dauer der Abscheidung kann vom Fachmann je nach Anwendung und gewünschter Eigenschaft der Leiterbahnen gewählt werden. Überraschenderweise führt die Verwendung der erfindungsgemäßen CNT-Mengen zu einer gezielten Abscheidung des Kupfers auf den bereits vorhandenen leitfähigen Strukturen mit erhöhter CNT-Konzentration auf der Oberfläche des Polymerformkörpers. Bei der Verwendung der erfindungsgemäßen CNT-Anteile in dem Polymerformkörpern entsteht an den Stellen der Oberfläche des Polymerformkörpers, die nicht thermisch behandelt wurden und daher keine leitfähigen Strukturen enthalten, kein zur Abscheidung von Kupfer ausreichend hohes Spannungspotential. Demgegenüber kann es bei Verwendung höherer CNT-Anteile in den Polymerformkörpern zu einer ungezielten Abscheidung von Kupfer auf der gesamten Oberfläche des Polymerformkörpers kommen. Andererseits ist die erfindungsgemäße Mindestmenge an CNT im Polymerformkörper notwendig, um leitfähige Strukturen zu erzeugen, die ein ausreichend hohes Spannungspotential zur Abscheidung des Kupfers auf den leitfähigen Strukturen ermöglichen.Here, the printed circuit board with the conductive structures in a conventional manner in an electrolytic plating bath is introduced (see, for example "Kunststoffgalvanisierung", LPW Taschenbuch für Galvanotechnik, Volume 1, Process Engineering, 13th Edition 1988, pages 443 to 449 ). The plating bath contains, for example, a copper (II) sulfate solution having an anode. By applying a negative voltage (cathode) to the electrically conductive structures on the surface of the polymer moldings and to the Ge copper can be targeted from the solution to be deposited on the structures and form a metallic layer. The suitable electrolyte solutions, the electrical voltage potential and the appropriate duration of the deposition can be selected by the skilled person depending on the application and desired property of the interconnects. Surprisingly, the use of CNT amounts according to the invention leads to a selective deposition of the copper on the already existing conductive structures with increased CNT concentration on the surface of the polymer molding. When using the CNT fractions according to the invention in the polymer moldings, at the points of the surface of the polymer molded body which have not been thermally treated and therefore contain no conductive structures, there is no sufficiently high voltage potential for the deposition of copper. In contrast, when higher CNT contents are used in the polymer moldings, untargeted deposition of copper on the entire surface of the polymer molding may occur. On the other hand, the minimum amount of CNT according to the invention in the polymer molding is necessary in order to produce conductive structures that allow a sufficiently high voltage potential for the deposition of copper on the conductive structures.

Mit dem erfindungsgemäßen Verfahren wird es auf einfache Weise möglich, leitfähige Strukturen auf einer Leiterplatte zu erzeugen, ohne dass beispielsweise das Abdecken von Bereichen, die nicht mit Kupfer beschichtet werden sollen, notwendig ist. Da das Kupfer gezielt auf die bereits vorhandenen leitfähigen Strukturen aufgebracht wird, muss zudem anschließend auch kein Ätzprozess zum Entfernen von überschüssigem Kupfer durchgeführt werden.With The process of the invention is based on simple Way possible, conductive structures on one To produce circuit board without, for example, the covering of areas not to be coated with copper is. Because the copper targeted to the already existing conductive In addition, structures must also be applied afterwards no etching process to remove excess copper be performed.

Eine erfindungsgemäß bevorzugte Leiterplatten-Anordnung umfasst mindestens eine Leiterplatte mit mindestens einer elektrisch leitfähigen Leiterbahn, wobei die Leiterplatte einen Polymer formkörper mit 0,1–10 Gew.-% Carbon Nanotubes (CNT), bezogen auf die Masse der Polymerphase/n, aufweist, und die mindestens eine elektrisch leitfähige Leiterbahn eine Kupferschicht aufweist.A According to the invention preferred circuit board assembly includes at least one printed circuit board with at least one electrically conductive interconnect, wherein the circuit board is a polymer molded body with 0.1-10 wt .-% carbon nanotubes (CNT), based on the Mass of the polymer phase / s, and having at least one electrical conductive trace has a copper layer.

Des Weiteren ist es bevorzugt, dass die Leiterplatten-Anordnung mindestens ein elektronisches Bauelement aufweist, das durch eine erfindungsgemäße organische Klebstoff-Zusammensetzung, wie sie nachfolgend beschrieben wird, mit mindestens einer elektrisch leitfähigen Leiterbahn der Leiterplatte verbunden ist.Of Further, it is preferable that the circuit board assembly at least has an electronic component that by an inventive organic adhesive composition as described below is, with at least one electrically conductive trace the circuit board is connected.

Die Erfindung betrifft auch ein Verfahren zur Herstellung einer erfindungsgemäßen Leiterplatten-Anordnung, umfassend die Schritte:

  • a) Bereitstellen eines Polymerformkörpers aus mindestens einer Polymerphase die Carbon Nanotubes (CNT) enthält,
  • b) Thermisches Behandeln mindestens einer Oberfläche des Polymerformkörpers zur Erzeugung der leitfähigen Strukturen auf der Oberfläche des Polymerformkörpers, wobei die thermische Behandlung ein Erhitzen auf eine Temperatur umfasst, die mindestens der Schmelztemperatur der mindestens einen Polymerphase entspricht, und
  • c) Galvanisieren der elektrisch leitfähigen Strukturen.
The invention also relates to a method for producing a printed circuit board arrangement according to the invention, comprising the steps:
  • a) providing a polymer molding comprising at least one polymer phase containing carbon nanotubes (CNT),
  • b) thermally treating at least one surface of the polymer shaped body to produce the conductive structures on the surface of the polymer molded body, the thermal treatment comprising heating to a temperature which corresponds at least to the melting temperature of the at least one polymer phase, and
  • c) electroplating the electrically conductive structures.

Zusätzlich bevorzugt wird in dem Verfahren zur Herstellung einer erfindungsgemäßen Leiterplatten-Anordnung in einem zusätzlichen Schritt d) mindestens ein elektronisches Bauteil unter Verwendung einer erfindungsgemäßen Klebstoffzusammensetzung mit mindestens einer Leiterbahn der Leiterplatte verbunden.additionally is preferred in the process for preparing a novel Circuit board arrangement in an additional step d) at least one electronic component using an inventive Adhesive composition with at least one conductor track of the printed circuit board connected.

METHODENMETHODS

Zur Bestimmung der Parameter der erfindungsgemäßen Polymerformkörper werden die nachstehenden Methoden eingesetzt:
Die Bestimmung der elektrischen Oberflächenleitfähigkeit erfolgte anhand der Messung des Oberflächenwiderstands mit einem Ohmmeter ”Metra Hit Plus” der Firma Gossen Metrawatt GmbH nach Angaben des Herstellers. Es wurde sowohl der Widerstand auf der unbehandelten Oberfläche als auch jeweils an verschiedenen Stellen der mit dem Laser behandelten Oberflächenausschnitte mittels zweier Elektroden im Abstand von 2 mm gemessen. Zum Vergleich wurde die Oberfläche an einer Stelle mechanisch abgetragen und der elektrische Widerstand im Material gemessen.
The following methods are used to determine the parameters of the polymer shaped bodies according to the invention:
The determination of the electrical surface conductivity was based on the measurement of the surface resistance with an ohmmeter "Metra Hit Plus" from Gossen Metrawatt GmbH according to the manufacturer. Both the resistance on the untreated surface and in each case at different points of the laser-treated surface sections were measured by means of two electrodes at a distance of 2 mm. For comparison, the surface was mechanically removed at one point and the electrical resistance in the material was measured.

Die Analyse ob ein Polymerformkörper getrennte Polymerphasen aufweist kann unter Verwendung der Differential-Scanning-Calorimetry (DSC) nach DIN EN ISO 11357 erfolgen. Hierbei kann die Zahl der Polymerphasen anhand der Phasenübergänge beim Schmelzen des Polymerformkörpers festgestellt werden.The analysis of whether a polymer molding has separate polymer phases can be performed using Differential Scanning Calorimetry (DSC) DIN EN ISO 11357 respectively. In this case, the number of polymer phases can be determined on the basis of the phase transitions during melting of the polymer molding.

Die Bestimmung der Schmelztemperatur der Polymerphasen bzw. des Polymerformkörpers kann gemäß DIN EN ISO 3146 erfolgen.The determination of the melting temperature of the polymer phases or the polymer molding can according to DIN EN ISO 3146 respectively.

Der Gesamtgehalt an CNT im Polymerformkörper kann durch das pyrolytische Messverfahren gemäß DIN EN ISO 3451 bestimmt werden.The total content of CNT in the polymer molding can be determined by the pyrolytic measurement method according to DIN EN ISO 3451 be determined.

BEISPIELEEXAMPLES

Herstellung eines Polymerformkörpers mit leitfähigen StrukturenProduction of a polymer molding with conductive structures

Es wird eine Polymermischung aus 75 Polypropylen (Repol HP-12 der Firma Reliance, Indien), 3,75 CNT (Baytubes C 150 P, Fa. Bayer) und 21,25 Gew.-% Polycarbonat (Makrolon 2805, Fa. Bayer) hergestellt.It is a polymer blend of polypropylene (Repol HP-12 of the company Reliance, India), 3.75 CNT (Baytubes C 150 P, Bayer) and 21.25 % By weight polycarbonate (Makrolon 2805, Bayer).

Die Mischung wird in einem ZSE 27/44D Doppelschneckenextruder der Firma Leistritz, Nürnberg mit einem Durchmesser von 27 mm und einem Verhältnis LID von 44 bei einem Durchsatz von 10 kg/h mit einer Leistung von 18 kWh aufgeschmolzen und vermengt. Im Extruder wurde ein von 200°C auf 260°C ansteigendes Temperaturprofil eingestellt. Anschließend erfolgte eine Granulierung.The Mixture is in a ZSE 27 / 44D twin screw extruder company Leistritz, Nuremberg with a diameter of 27 mm and a ratio LID of 44 at a throughput of 10 kg / h with a capacity of 18 kWh melted and mixed. In the extruder was from 200 ° C to 260 ° C increasing Temperature profile set. Subsequently, a Granulation.

Der Polymerformkörper wurde im Spritzgussverfahren (Gerätetyp: Arburg 270) bei einer Temperatur von 220–240°C in der Form von runden Plattchen mit 4 cm Durchmesser ausgeformt. Für die thermische Behandlung wurde ein CO2-Laser verwendet. Die Messwerte der Oberflächenwiderstände sind in der nachfolgenden Tabelle angegeben. Tabelle: Messstelle Oberflächenwiderstand Mittelwert Maßeinheit unbehandelt keine Leitfähigkeit (< 10 MOhm) Laserspur 2 133 122 146 1,34 kOhm Laserspur 3 64,3 58,9 69,1 64,1 kOhm Laserspur 4 23,2 21,2 24,4 22,9 kOhm abgeschliffen keine Leitfähigkeit (< 10 MOhm) The polymer molded article was injection molded (device type: Arburg 270) at a temperature of 220-240 ° C in the form of round plates with 4 cm diameter. For the thermal treatment, a CO 2 laser was used. The measured values of the surface resistances are given in the following table. Table: measuring point surface resistivity Average Unit of measurement untreated no conductivity (<10 MOhm) Laser track 2 133 122 146 1.34 kohm Laser track 3 64.3 58.9 69.1 64.1 kohm Laser track 4 23.2 21.2 24.4 22.9 kohm abraded no conductivity (<10 MOhm)

Herstellung einer Leiterplatten-Anordnung mit elektronischen BauteilenProduction of a printed circuit board arrangement with electronic components

Zunächst wird eine erfindungsgemäße Klebstoff-Zusammensetzung hergestellt. Diese besteht aus 35 g Photobond PB 437 (Hersteller: Delo, Deutschland), 0,35 g Nanocyl 7000 (Hersteller: Nanocyl, Belgien). Die Komponenten der Klebstoff-Zusammensetzung werden für 20 min bei 45°C unter Verwendung einer Heizplatte IKA RH-KT/C mit einem Rührer (Heidoiph RZ RO/4) bei 300 U/min gerührt.First becomes an adhesive composition according to the invention produced. This consists of 35 g Photobond PB 437 (Manufacturer: Delo, Germany), 0.35 g Nanocyl 7000 (manufacturer: Nanocyl, Belgium). The components of the adhesive composition are used for 20 min at 45 ° C using a hot plate IKA RH-KT / C with a stirrer (Heidoiph RZ RO / 4) stirred at 300 U / min.

Der Kleber wurde zur Bestimmung des elektrischen Widerstands auf eine nicht leitende Oberfläche aufgebracht und unter einer UV-Lampe (Siemens UV Lampe 6ES5985-1AA11) für 7 min ausgehärtet. Anschließend wurde mit dem Messgerät Messcontrol M-860 D ein Widerstand von 57 Ohm/cm gemessen.Of the Adhesive was used to determine the electrical resistance on a non-conductive surface applied and under a UV lamp (Siemens UV lamp 6ES5985-1AA11) cured for 7 min. Subsequently, with the measuring device Messcontrol M-860 D measured a resistance of 57 ohms / cm.

Um eine Diode auf eine Leiterplatte aufzubringen, wurden die Metallbeinchen der Diode in die Klebstoff-Zusammensetzung eingetaucht und die Dioden in Kontakt mit der Leiterplatte gebracht, so dass der Klebertropfen eine Verbindung zwischen der Leiterbahn und den Beinchen herstellt. Durch Aushärten mit der UV-Lampe ergab sich eine feste Verbindung. Nach Anlegen einer Spannung von 50 V leuchtete die Diode.Around To apply a diode to a printed circuit board, the metal legs were the diode immersed in the adhesive composition and the diodes brought into contact with the circuit board, leaving the glue drop creates a connection between the track and the legs. By curing with the UV lamp resulted in a solid Connection. After applying a voltage of 50 V, the diode lit up.

Nachfolgend werden bevorzugte Ausführungsformen der Erfindung beschrieben. Die erfindungsgemäßen Polymerformkörper können für die erfindungsgemäßen Leiterplatten-Anordnungen verwendet werden. Das erfindungsgemäße Gerät ist zur thermischen Behandlung der Oberfläche des Polymerformkörpers geeignet (Schritt b des Verfahrens zur Erzeugung leitfähiger Strukturen).

  • 1. Verfahren zur Erzeugung leitfähiger Strukturen auf der Oberfläche von nicht oder nur gering leitfähigen Polymerformkörpern, umfassend die folgenden Schritte: a) Bereitstellen eines Polymerformkörpers aus mindestens einer Polymerphase, die Carbon Nanotubes (CNT) enthält; b) thermische Behandlung mindestens einer Oberfläche des Polymerformkörpers zur Erzeugung der leitfähigen Strukturen auf der Oberfläche des Polymerformkörpers, wobei die thermische Behandlung ein Erhitzen auf eine Temperatur umfasst, die mindestens der Schmelztemperatur der mindestens einen Polymerphase entspricht.
Hereinafter, preferred embodiments of the invention will be described. The polymer shaped bodies according to the invention can be used for the printed circuit board arrangements according to the invention. The device according to the invention is suitable for the thermal treatment of the surface of the polymer molding (step b of the method for producing conductive structures).
  • 1. A process for producing conductive structures on the surface of non-conductive or only slightly conductive polymer moldings, comprising the following steps: a) providing a polymer molding of at least one polymer phase containing carbon nanotubes (CNT); b) thermal treatment of at least one surface of the polymer molding to produce the conductive structures on the surface of the polymer molding, wherein the thermal treatment comprises heating to a temperature which corresponds at least to the melting temperature of the at least one polymer phase.

Verfahren gemäß Anspruch 1, dadurch gekennzeichnet, dass die Polymerphase/n durch Vermischen von geschmolzenem Polymer mit 0,1–10 Gew.-% Carbon Nanotubes, bezogen auf die Masse der Polymerphase/n, erhalten wird/werden.

  • 2. Verfahren gemäß Punkt 1, dadurch gekennzeichnet, dass die Polymerphase/n durch Vermischen von geschmolzenem Polymer mit 0,1–10 Gew.-% Carbon Nanotubes, bezogen auf die Masse der Polymerphase/n, erhalten wird/werden.
  • 3. Verfahren gemäß Punkt 1 oder 2, dadurch gekennzeichnet, dass der Polymerformkörper durch Verschmelzen mindestens einer Polymerphase, die Carbon Nanotubes (CNT) in einem Anteil zwischen 1 und 40 Gew.-% enthält, mit mindestens einer weiteren Polymerphase mit geringerem Carbon Nanotubes (CNT)-Anteil, erhalten wird.
  • 4. Verfahren gemäß einem der vorhergehenden Punkte, dadurch gekennzeichnet, dass die Polymerphase, die Carbon Nanotubes (CNT) in einem Anteil zwischen 1 und 40 Gew.-% enthält, ein oder mehrere Polymer/e umfasst, ausgewählt aus der Gruppe bestehend aus Polycarbonat, Polystryrol, Acrylnitrit-Butadien-Styrol (ABS), Styrolmaleinsäureanhydrid (SMA), Styrolmethylmethacrylat (SMMA), Polymethylmethacrylat (PMMA), Polybutylenterephthalat (PBT), Polyethylenterephthalat (PET), Polyamid 6 (PA 6), Polyamid 6.6 (PA 6.6), Polyamid 6.4 (PA 6.4), Polyamid 12 (PA 12), aromatischem Polyamid und Polysulfon.
  • 5. Verfahren gemäß einem der vorhergehenden Punkte, dadurch gekennzeichnet, dass die thermische Behandlung der Oberfläche/n des Polymerformkörpers durch Kontakt mit einem erhitzten Körper, Gas oder Flüssigkeit, oder durch elektromagnetische Strahlung erfolgt.
  • 6. Verfahren gemäß einem der vorhergehenden Punkte, dadurch gekennzeichnet, dass als elektromagnetische Strahlung Laserstrahlung oder IR-Strahlung verwendet wird.
  • 7. Polymerformkörper, umfassend mindestens eine Polymerphase mit Carbon Nanotubes (CNT), wobei der Polymerformkörper auf der Oberfläche elektrisch oder thermisch leitfähige Strukturen aufweist, wobei die Konzentration der CNT in den Berei chen der elektrisch leitfähigen Oberflächenstrukturen höher ist als in den nicht elektrisch leitfähigen Oberflächenbereichen.
  • 8. Polymerformkörper gemäß Punkt 7, dadurch gekennzeichnet, dass mindestens eine Polymerphase ein Polymer enthält, ausgewählt aus der Gruppe bestehend aus: Polycarbonat, Polystryrol, Acrylnitrit-Butadien-Styrol (ABS), Styrolmaleinsäureanhydrid (SMA), Styrolmethylmethacrylat (SMMA), Polymethylmethacrylat (PMMA), Polybutylenterephthalat (PBT), Polyethylenterephthalat (PET), Polyamid 6 (PA 6), Polyamid 6.6 (PA 6.6), Polyamid 6.4 (PA 6.4), Polyamid 12 (PA 12), aromatischem Polyamid und Polysulfon.
  • 9. Polymerformkörper gemäß einem der Punkte 7 oder 8, dadurch gekennzeichnet, dass zwischen 0,01 und 10 Gew.-% CNT, bezogen auf die Gesamtmasse der Polymerphase/n des Polymerformkörpers, enthalten sind.
  • 10. Polymerformkörper gemäß einem der Punkte 7 bis 9, dadurch gekennzeichnet, dass der Polymerformkörper mindestens zwei getrennte Polymerphasen enthält.
  • 11. Polymerformkörper gemäß einem der Punkte 7 bis 10, dadurch gekennzeichnet, dass eine der Polymerphasen einen höheren Anteil an Carbon Nanotubes (CNT) als die andere/n Phasen aufweist.
  • 12. Polymerformkörper gemäß einem der vorstehenden Punkte, wobei für den Polymerformkörper eine Polymerblend aus Polycarbonat mit Polyolefin, insbesondere mit Polypropylen oder Polyethylen, verwendet wird.
  • 13. Verfahren gemäß Anspruch 1, worin die die Polymerphase/n durch Vermischen von geschmolzenem Polymer mit 0,1–10 Gew.-% Carbon Nanotubes, bezogen auf die Masse der Polymerphase/n, erhalten wird/werden.
  • 14. Gerät zum Erzeugen einer Struktur an einem zu bearbeitenden Körper gekennzeichnet durch eine Energiequelle mit mindestens einer Elektrode, die zum Abgeben einer Energie vorgesehen ist, mit welcher der zu bearbeitenden Körper wenigstens teilweise erwärmbar ist. Bevorzugterweise dient das Gerät zur thermischen Behandlung der Oberfläche von Polymerformkörpern, wobei an den thermisch behandelten Stellen definierte elektrisch leitfähige Strukturen entstehen.
  • 15. Gerät nach Punkt 14, dadurch gekennzeichnet, dass der zu bearbeitende Körper ein Polymerformkörper aus mindestens einer Polymerphase ist, die Carbon-Nanotubes enthält.
  • 16. Gerät nach Punkt 14 oder 15, dadurch gekennzeichnet, dass die Energiequelle eine elektrische Energiequelle ist.
  • 17. Gerät nach Punkt 16, dadurch gekennzeichnet, dass die Energiequelle mindestens zwei Elektroden aufweist, die an den zu bearbeitenden Körper anlegbar sind, wobei mit den zwei Elektroden ein Strom durch den zu bearbeitenden Körper leitbar ist, der den zu bearbeitenden Körper aufwärmt.
  • 18. Gerät nach Punkt 16 oder 17, dadurch gekennzeichnet, dass die elektrische Energiequelle eine Spannungsquelle vorzugsweise mit einer Leerlaufspannung größer als 500 V und insbesondere mit einer Leerlaufspannung von 1000 V ist.
  • 19. Gerät nach einem der vorstehenden Punkte, dadurch gekennzeichnet, dass die zu erzeugende Struktur ein elektronischer Schaltkreis ist.
  • 20. Gerät nach einem der vorstehenden Punkte, dadurch gekennzeichnet, dass die erste Elektrode und die zweite Elektrode in einer Ebene oder in zwei verschiedenen Ebenen des zu bearbeitenden Körpers angeordnet sind.
  • 21. Gerät nach einem der vorstehenden Punkte, dadurch gekennzeichnet, dass der Abstand zwischen der ersten und zweiten Elektrode weniger als 1 mm ist.
  • 22. Gerät nach einem der vorstehenden Punkte, gekennzeichnet durch einen Abstandshalter, der die erste und zweite Elektrode miteinander verbindet.
  • 23. Vorrichtung zum Erzeugen einer Struktur auf einem zu bearbeitenden Körper mit dem zu bearbeitenden Körper und einem Gerät, nach einem der Ansprüche 1–9, das den zu bearbeitenden Körper wenigstens teilweise erwärmt.
  • 24. Plotter mit einer Vorrichtung nach einem der vorstehenden Punkte.
  • 25. Matrixdrucker mit einer Vorrichtung nach einem der vorstehenden Punkte als Druckmatrix.
  • 26. Stift mit einer Vorrichtung nach einem der vorstehenden Punkte als Stiftspitze.
  • 27. Verfahren zum Erzeugen einer Struktur auf einem zu bearbeitenden Körper, dadurch gekennzeichnet, dass zwischen zwei verschiedenen Punkten des zu bearbeitenden Körpers eine elektrische Energie geleitet wird.
A method according to claim 1, characterized in that the polymer phase (s) is / are obtained by mixing molten polymer with 0.1-10% by weight of carbon nanotubes, based on the mass of the polymer phase (s).
  • 2. Method according to item 1, characterized in that the polymer phase (s) is / are obtained by mixing molten polymer with 0.1-10% by weight of carbon nanotubes, based on the mass of the polymer phase (s).
  • 3. The method according to item 1 or 2, characterized in that the polymer molded article by fusion of at least one polymer phase containing carbon nanotubes (CNT) in an amount between 1 and 40 wt .-%, with at least one further polymer phase with a lower carbon nanotubes ( CNT) portion.
  • 4. The method according to one of the preceding points, characterized in that the polymer phase containing carbon nanotubes (CNT) in an amount of between 1 and 40 wt .-% comprises one or more polymer / s selected from the group consisting of polycarbonate , Polystyrene, acrylonitrile butadiene styrene (ABS), styrene maleic anhydride (SMA), styrene methyl methacrylate (SMMA), polymethyl methacrylate (PMMA), polybutylene terephthalate (PBT), polyethylene terephthalate (PET), polyamide 6 (PA 6), polyamide 6.6 (PA 6.6) , Polyamide 6.4 (PA 6.4), polyamide 12 (PA 12), aromatic polyamide and polysulfone.
  • 5. The method according to any one of the preceding points, characterized in that the thermal treatment of the surface / s of the polymer molding is effected by contact with a heated body, gas or liquid, or by electromagnetic radiation.
  • 6. Method according to one of the preceding points, characterized in that laser radiation or IR radiation is used as the electromagnetic radiation.
  • 7. A polymer molding comprising at least one polymer phase with carbon nanotubes (CNT), wherein the polymer molding has electrically or thermally conductive structures on the surface, wherein the concentration of CNT in the preparation surfaces of the electrically conductive surface structures is higher than in the non-electrically conductive surface regions ,
  • 8. The polymer molding according to item 7, characterized in that at least one polymer phase contains a polymer selected from the group consisting of: polycarbonate, polystyrene, acrylonitrile butadiene styrene (ABS), styrene maleic anhydride (SMA), styrene methyl methacrylate (SMMA), polymethyl methacrylate ( PMMA), polybutylene terephthalate (PBT), polyethylene terephthalate (PET), polyamide 6 (PA 6), polyamide 6.6 (PA 6.6), polyamide 6.4 (PA 6.4), polyamide 12 (PA 12), aromatic polyamide and polysulfone.
  • 9. Polymer molding according to one of the items 7 or 8, characterized in that between 0.01 and 10 wt .-% CNT, based on the total mass of the polymer phase / n of the polymer molding, are included.
  • 10. Polymer molding according to one of the items 7 to 9, characterized in that the polymer molding contains at least two separate polymer phases.
  • 11. Polymer molding according to one of the items 7 to 10, characterized in that one of the polymer phases has a higher proportion of carbon nanotubes (CNT) than the other phases.
  • 12. Polymer molding according to one of the preceding points, wherein for the polymer molding a polymer blend of polycarbonate with polyolefin, in particular polypropylene or polyethylene, is used.
  • The process of claim 1, wherein the polymer phase (s) are obtained by blending molten polymer with 0.1-10 wt.% Carbon nanotubes based on the weight of polymer phase (s).
  • 14. An apparatus for producing a structure on a body to be processed characterized by a power source having at least one electrode which is provided for discharging an energy with which the body to be processed is at least partially heated. Preferably, the device is used for the thermal treatment of the surface of shaped polymer bodies, wherein at the thermally treated sites defined electrically conductive structures arise.
  • 15. Apparatus according to item 14, characterized in that the body to be processed is a polymer molding of at least one polymer phase containing carbon nanotubes.
  • 16. Apparatus according to item 14 or 15, characterized in that the energy source is an electrical energy source.
  • 17. Device according to item 16, characterized in that the energy source has at least two electrodes which can be applied to the body to be processed, wherein the two electrodes, a current through the body to be processed can be conducted, which warms up the body to be processed.
  • 18. Device according to item 16 or 17, characterized in that the electrical energy source is a voltage source, preferably with an open circuit voltage greater than 500 V and in particular with an open circuit voltage of 1000 V.
  • 19. Device according to one of the preceding points, characterized in that the structure to be generated is an electronic circuit.
  • 20. Device according to one of the preceding points, characterized in that the first electrode and the second electrode are arranged in one plane or in two different planes of the body to be machined.
  • 21. Device according to one of the preceding points, characterized in that the distance between the first and second electrode is less than 1 mm.
  • 22. Device according to one of the preceding points, characterized by a spacer which connects the first and second electrodes together.
  • 23. A device for producing a structure on a body to be machined with the body to be machined and a device according to any one of claims 1-9, which at least partially heats the body to be processed.
  • 24. Plotter with a device according to one of the preceding points.
  • 25. Dot matrix printer with a device according to one of the preceding points as a pressure matrix.
  • 26. Pen with a device according to one of the above points as a pen tip.
  • 27. A method for producing a structure on a body to be machined, characterized in that between two different points of the body to be processed an electrical energy is passed.

ZITATE ENTHALTEN IN DER BESCHREIBUNGQUOTES INCLUDE IN THE DESCRIPTION

Diese Liste der vom Anmelder aufgeführten Dokumente wurde automatisiert erzeugt und ist ausschließlich zur besseren Information des Lesers aufgenommen. Die Liste ist nicht Bestandteil der deutschen Patent- bzw. Gebrauchsmusteranmeldung. Das DPMA übernimmt keinerlei Haftung für etwaige Fehler oder Auslassungen.This list The documents listed by the applicant have been automated generated and is solely for better information recorded by the reader. The list is not part of the German Patent or utility model application. The DPMA takes over no liability for any errors or omissions.

Zitierte PatentliteraturCited patent literature

  • - US 4404125 [0003] US 4404125 [0003]
  • - US 4664971 [0003] - US 4664971 [0003]
  • - WO 02/19346 [0004, 0018] WO 02/19346 [0004, 0018]
  • - DD 263179 [0005] - DD 263179 [0005]
  • - DE 10259498 [0006] - DE 10259498 [0006]
  • - EP 0914027 [0012] - EP 0914027 [0012]
  • - EP 0870418 [0012] - EP 0870418 [0012]
  • - WO 99/13127 [0029] WO 99/13127 [0029]
  • - DE 19946182 [0029] - DE 19946182 [0029]
  • - WO 98/39250 [0029] WO 98/39250 [0029]
  • - WO 86/03455 [0029] WO 86/03455 [0029]
  • - WO 2006/050903 [0029] WO 2006/050903 [0029]
  • - US 6203814 [0031] US 6203814 [0031]
  • - US 08/812856 [0031] US 08/812856 [0031]
  • - EP 1776418 [0034] - EP 1776418 [0034]
  • - US 4157325 [0041] US 4157325 [0041]
  • - CA 2324353 A1 [0041] CA 2324353 A1 [0041]
  • - US 5643502 [0045] US 5643502 [0045]
  • - EP 0847329 A [0053] - EP 0847329 A [0053]
  • - WO 02/079881 A [0053] WO 02/079881 A [0053]
  • - DE 1300266 [0064] - DE 1300266 [0064]
  • - DE 1495730 [0064] - DE 1495730 [0064]

Zitierte Nicht-PatentliteraturCited non-patent literature

  • - T. Dekker (Carbon-Nanotubes as Molecular Quantum Wires, Physics Today, S. 22-28, 1999) [0008] T. Dekker (Carbon Nanotubes as Molecular Quantum Wires, Physics Today, pp. 22-28, 1999) [0008]
  • - Wu et al. (Journal of applied polymer science, 2006, vol. 99, no2, pp. 477-488) [0024] - Wu et al. (Journal of applied polymer science, 2006, vol. 99, no2, pp. 477-488) [0024]
  • - Iijima, Nature 354, 1991, 56-8 [0029] - Iijima, Nature 354, 1991, 56-8 [0029]
  • - P. M. Ajayan, Nanotubes from Carbon, Chem. Rev. 99, S. 1787-1799, 1999 [0029] PM Ajayan, Nanotubes from Carbon, Chem. Rev. 99, pp. 1787-1799, 1999 [0029]
  • - ”Kunststoffgalvanisierung”, LPW-Taschenbuch für Galvanotechnik, Band 1, Verfahrenstechnik, 13. Ausgabe 1988, Seiten 443 bis 449 [0100] - "Kunststoffgalvanisierung", LPW Taschenbuch für Galvanotechnik, Volume 1, Process Engineering, 13th Edition 1988, pages 443 to 449 [0100]
  • - ”Kunststoffgalvanisierung”, LPW-Taschenbuch für Galvanotechnik, Band 1, Verfahrenstechnik, 13. Ausgabe 1988, Seiten 443 bis 449 [0102] - "Kunststoffgalvanisierung", LPW Taschenbuch für Galvanotechnik, Volume 1, Process Engineering, 13th Edition 1988, pages 443 to 449 [0102]
  • - DIN EN ISO 11357 [0109] - DIN EN ISO 11357 [0109]
  • - DIN EN ISO 3146 [0110] - DIN EN ISO 3146 [0110]
  • - DIN EN ISO 3451 [0111] - DIN EN ISO 3451 [0111]

Claims (14)

Leiterplatten-Anordnung, umfassend mindestens eine Leiterplatte mit mindestens einer elektrisch leitfähigen Leiterbahn und mindestens einem elektronischen Bauelement, wobei die Leiterplatte einen Polymerformkörper mit 0,1–10 Gew.-% Carbon Nanotubes (CNT), bezogen auf die Masse der Polymerphase/n, umfasst, und wobei das mindestens eine elektronische Bauelement durch eine organische Klebstoff-Zusammensetzung enthaltend 0,05-10 Gew.-% Carbon-Nanotubes (CNT), bezogen auf die Masse der Klebstoff-Zusammensetzung, mit mindestens einer elektrisch leitfähigen Leiterbahn der Leiterplatte verbunden ist.Printed circuit board assembly comprising at least a printed circuit board with at least one electrically conductive Conductor track and at least one electronic component, wherein the printed circuit board a polymer molding with 0.1-10 % By weight of carbon nanotubes (CNT), based on the mass of the polymer phase (s), includes, and wherein the at least one electronic component by an organic adhesive composition containing 0.05-10 % By weight of carbon nanotubes (CNT), based on the mass of the adhesive composition, with at least one electrically conductive conductor track the circuit board is connected. Leiterplatten-Anordnung gemäß Anspruch 1, wobei die organische Klebstoff-Zusammensetzung einen Widerstand von weniger als 100 Ohm, insbesondere weniger als 50 Ohm aufweist.Printed circuit board arrangement according to claim 1, wherein the organic adhesive composition has a resistance of less than 100 ohms, in particular less than 50 ohms. Leiterplatten-Anordnung gemäß einem der Ansprüche 1 oder 2, wobei die organische Klebstoff-Zusammensetzung mindestens einen Klebstoff enthält, der ausgewählt ist aus der Gruppe bestehend aus: Acrylat-Klebstoffen, Phenol-Formaldehydharz-Klebstoffen, Silicon-Klebstoffen, und Polyurethan-Klebstoffen, bevorzugterweise enthält die Klebstoff-Zusammensetzung einen Urethanacrylat-Klebstoff.Printed circuit board assembly according to a of claims 1 or 2, wherein the organic adhesive composition contains at least one adhesive selected is selected from the group consisting of: acrylate adhesives, phenol-formaldehyde resin adhesives, Silicone adhesives, and polyurethane adhesives, preferably For example, the adhesive composition contains a urethane acrylate adhesive. Leiterplatten-Anordnung gemäß einem der vorangegangenen Ansprüche, wobei die Verbindung zwischen der mindestens einen elektrisch leitfähigen Leiterbahn und dem mindestens einen elektronischen Bauelement elektrisch leitfähig ist und einen Widerstand von weniger als 100 Ohm aufweist.Printed circuit board assembly according to a of the preceding claims, wherein the connection between the at least one electrically conductive conductor track and the at least one electronic component electrically conductive is and has a resistance of less than 100 ohms. Klebstoff-Zusammensetzung enthaltend 0,05–10 Gew.-% Carbon-Nanotubes (CNT).Adhesive composition containing 0.05-10 Wt% carbon nanotubes (CNT). Klebstoff-Zusammensetzung gemäß Anspruch 5, wobei die Klebstoff-Zusammensetzung mindestens einen Klebstoff enthält, der ausgewählt ist aus der Gruppe bestehend aus: Acrylat-Klebstoffen, Phenol-Formaldehydharz-Klebstoffen, Silicon-Klebstoffen, und Polyurethan-Klebstoffen, bevorzugterweise enthält die Klebstoff-Zusammensetzung einen Urethanacrylat-Klebstoff.Adhesive composition according to claim 5, wherein the adhesive composition comprises at least one adhesive contains, which is selected from the group acrylate adhesives, phenol-formaldehyde resin adhesives, silicone adhesives, and polyurethane adhesives, preferably containing Adhesive composition a urethane acrylate adhesive. Klebstoff-Zusammensetzung gemäß einem der Ansprüche 5 oder 6, wobei die organische Klebstoff-Zusammensetzung einen Widerstand von weniger als 100 Ohm, insbesondere weniger als 50 Ohm aufweist.Adhesive composition according to one of claims 5 or 6, wherein the organic adhesive composition a resistance of less than 100 ohms, in particular less than 50 ohms. Verfahren zum Aufbringen mindestens eines elektronischen Bauelements auf eine Leiterplatte umfassend die folgenden Schritte: a) Bereitstellen einer Leiterplatte mit mindestens einer elektrisch leitfähigen Leiterbahn oder mindestens einem elektrisch leitfähigen Bereich, wobei die Leiterplatte einen Polymerformkörper mit 0,1–10 Gew.-% Carbon Nanotubes (CNT), bezogen auf die Masse der Polymerphase/n, aufweist, b) Bereitstellen mindestens eines elektronischen Bauelements, und c) Verbinden des elektronischen Bauelements mit der elektrisch leitfähigen Leiterbahn unter Verwendung der Klebstoff-Zusammensetzung gemäß einem der Ansprüche 5 bis 7.Method for applying at least one electronic Device on a printed circuit board comprising the following steps: a) Providing a printed circuit board with at least one electrical conductive trace or at least one electrical conductive area, wherein the circuit board is a polymer molding with 0.1-10 wt .-% carbon nanotubes (CNT), based on the Mass of the polymer phase (s), b) Provide at least an electronic component, and c) Connecting the electronic Component with the electrically conductive trace under Use of the adhesive composition according to one of claims 5 to 7. Verwendung einer Klebstoff-Zusammensetzung gemäß einem der Ansprüche 5 bis 7 zum elektrisch leitfähigen Verbinden eines elektronischen Bauelements mit einem anderen elektrisch leitfähigen Bauteil oder Formteil, insbesondere einer elektrisch leitfähigen Leiterbahn oder einem elektrisch leitfähigen Bereich auf einer Leiterbahn.Use of an adhesive composition according to one of claims 5 to 7 for electrically conductive Connecting an electronic component with another electrically conductive component or molded part, in particular an electrical conductive trace or an electrically conductive Area on a track. Leiterplatten-Anordnung, umfassend mindestens eine Leiterplatte mit mindestens einer elektrisch leitfähigen Leiterbahn, wobei die Leiterplatte einen Polymerformkörper mit 0,1–10 Gew.-% Carbon Nanotubes (CNT), bezogen auf die Masse der Polymerphase/n, aufweist, und die mindestens eine elektrisch leitfähige Leiterbahn eine Metallschicht, bevorzugt eine Kupferschicht, umfasst.Printed circuit board assembly comprising at least one Printed circuit board with at least one electrically conductive Conductor, wherein the circuit board is a polymer molding with 0.1-10 wt .-% carbon nanotubes (CNT), based on the Mass of the polymer phase / s, and having at least one electrical conductive trace a metal layer, preferably one Copper layer, includes. Leiterplatten-Anordnung gemäß Anspruch 10, wobei mindestens ein elektronisches Bauelement durch eine organische Klebstoff-Zusammensetzung gemäß einem der Ansprüche 5–7 mit mindestens einer elektrisch leitfähigen Leiterbahn der Leiterplatte verbunden ist.Printed circuit board arrangement according to claim 10, wherein at least one electronic component by an organic An adhesive composition according to any one of the claims 5-7 with at least one electrically conductive Conductor of the circuit board is connected. Verfahren zur Herstellung einer Leiterplatten-Anordnung gemäß einem der Ansprüche 10 oder 11, umfassend die Schritte: a) Bereitstellen eines Polymerformkörpers aus mindestens einer Polymerphase die Carbon Nanotubes (CNT) enthält, b) Thermisches Behandeln mindestens einer Oberfläche des Polymerformkörpers zur Erzeugung der leitfähigen Strukturen auf der Oberfläche des Polymerformkörpers, wobei die thermische Behandlung ein Erhitzen auf eine Temperatur umfasst, die mindestens der Schmelztemperatur der mindestens einen Polymerphase entspricht, und c) Galvanisieren der elektrisch leitfähigen Strukturen mit einem Metall, bevorzugt mit Kupfer.A method for producing a printed circuit board assembly according to one of claims 10 or 11, comprising the steps: a) providing a polymer molding of at least one polymer phase containing carbon nanotubes (CNT), b) thermally treating at least one surface of the polymer molding to produce the conductive structures on the surface of the polymer molding, wherein the thermal treatment is a heating to a temperature which corresponds at least to the melting temperature of the at least one polymer phase, and c) electroplating the electrically conductive structures with a metal, preferably with copper. Verfahren zur Herstellung einer Leiterplatten-Anordnung gemäß einem der Ansprüche 11 oder 12, wobei in einem zusätzlichen Schritt d) mindestens ein elektronisches Bauteil unter Verwendung einer Klebstoffzusammensetzung gemäß einem der Ansprüche 5– 7 mit mindestens einer Leiterbahn der Leiterplatte verbunden wird.Method for producing a printed circuit board arrangement according to one of claims 11 or 12, wherein in an additional step d) at least one electronic Component using an adhesive composition according to a of claims 5-7 with at least one conductor track the circuit board is connected. Verfahren gemäß einem der Ansprüche 12 oder 13, worin die Galvanisierung in Schritt c) durch eine badfreie Galvanisierung erfolgt.Method according to one of the claims 12 or 13, wherein the electroplating in step c) by a bad Galvanization takes place.
DE200810061051 2008-08-08 2008-12-08 Producing conductive structures on surface of polymer molded bodies, comprises providing polymer molded body from a polymer phase containing carbon nanotubes and thermally treating a surface of the polymer molded body Withdrawn DE102008061051A1 (en)