DE4317693C2 - Variable molded part, especially from renewable raw materials - Google Patents
Variable molded part, especially from renewable raw materialsInfo
- Publication number
- DE4317693C2 DE4317693C2 DE19934317693 DE4317693A DE4317693C2 DE 4317693 C2 DE4317693 C2 DE 4317693C2 DE 19934317693 DE19934317693 DE 19934317693 DE 4317693 A DE4317693 A DE 4317693A DE 4317693 C2 DE4317693 C2 DE 4317693C2
- Authority
- DE
- Germany
- Prior art keywords
- molding according
- filling
- shaped
- foam
- indicates
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Revoked
Description
Die Erfindung betrifft ein variables Formteil, insbesondere auf Stärkebasis, das besonders bei Transporten für die Stoßabsorption empfindlicher Güter mit unterschiedlichster Form und Masse sowie für die Wärmedämmung verwendet wird.The invention relates to a variable molded part, in particular based on starch, especially for transports for the Shock absorption of sensitive goods with a wide variety Shape and mass as well as for thermal insulation is used.
Formschäume aus Kunststoff (z. B. EPS) und/oder Formteile aus Karton, Wellpappe und Faserguß schützen empfindliche Pro dukte wie Glaswaren, Porzellan, Erzeugnisse der Elektro-, Haushalts-, Maschinenbau-, Automobil-, Elektronik-, Lebens mittel- und Spielwarenindustrie etc. beim Transport. Form teile müssen für jedes zu schützende Produkt paßgenau herge stellt werden. Daraus ergibt sich eine ebenso große Vielzahl an Verpackungsformteilen wie an zu schützenden Erzeugnissen, mit der Konsequenz von hohen Kosten für die Schutzver packung, insbesondere bei kleinen Stückzahlen. Neuere Akti vitäten umweltfreundliche Schutzverpackungsmaterialien zu entwickeln, führen zunehmend zu Faserguß- und Pulp-Produkten auf Basis von Recycling-Papier/-Karton und/oder Cellulose und/oder anderen Naturfasern. Diese Produkte haben aber eine im Vergleich zum EPS weniger gute Schockabsorption und ein viel höheres Gewicht.Molded foams made of plastic (e.g. EPS) and / or molded parts Cardboard, corrugated cardboard and fiber casting protect sensitive pro products such as glassware, porcelain, electrical products, Household, mechanical, automotive, electronics, life medium and toy industry etc. during transport. Shape Parts must be made to fit every product to be protected be put. This results in an equally large number on molded packaging parts as well as on products to be protected, with the consequence of high costs for the protection pack, especially for small quantities. Newer shares environmentally friendly protective packaging materials develop, increasingly lead to fiber casting and pulp products based on recycled paper / cardboard and / or cellulose and / or other natural fibers. But these products have one less good shock absorption and a compared to EPS much heavier weight.
Aus der DE 38 39 225 A1 ist es bekannt, Strohfasern in kis senförmige Hüllen zu füllen und als stoßdämpfendes Material in Verpackungsbehältern zu verwenden. Für diesen Zweck ist es ebenso bekannt, zu Kugeln gepreßtes, fein zerkleinertes Stroh als Kissenfüllung zu verwenden. (DE 40 25 257 C2).DE 38 39 225 A1 discloses straw fibers in kis to fill sen-shaped shells and as a shock-absorbing material to be used in packaging containers. Is for this purpose it is also known, finely crushed into balls Use straw as a pillow filling. (DE 40 25 257 C2).
Stroh als Dämpfungsmaterial hat jedoch ebenfalls die Nach teile eines hohen Gewichtes und einer im Verhältnis dazu zu geringen Elastizität, so daß dessen Verwendungsmöglichkeiten stark eingeschränkt sind. Die gegen Stöße schützende Dämp fungswirkung dieser Strohkugeln gestaltet sich bei größeren auf das Transportgut wirkenden Kräften oder einem hohen Ge wicht des Transportgutes nicht zufriedenstellend. Darüber hinaus zerfallen Strohfasern bei zu hoher Beanspruchung und verursachen Staub.However, straw as a cushioning material also has its night parts of a high weight and one in proportion to it low elasticity, so that its uses are severely restricted. The shock-absorbing damper The effect of these straw balls is larger forces acting on the cargo or a high Ge importance of the goods being transported is unsatisfactory. About that In addition, straw fibers disintegrate if they are subjected to too high loads cause dust.
DE-OS 40 39 505 und die DE-GM 90 17 904 zeigen Verfahren zum Herstellen schüttfähiger Packmaterialkörper aus Stärke in einer Extruderanlage, die in einer anschließenden Nachexpansionseinheit auf ihre endgültigen Abmessungen expandiert werden. Die Feinporigkeit und damit das Schüttgewicht wird dabei allein durch die Zuschlagmenge an Nukleierungsmittel bestimmt.DE-OS 40 39 505 and DE-GM 90 17 904 show methods for Manufacture of pourable packing material bodies from starch in one Extruder line that in a subsequent Post expansion unit to its final dimensions be expanded. The fine porosity and therefore that Bulk weight is determined solely by the quantity added Nucleating agent determined.
DE-PS 32 06 751 zeigt ein Verfahren zur Herstellung aufgeschäumter gelatinierter Stärkeprodukte in einer Extruderpresse, wobei von einem relativ starren Schaum ausgegangen wird.DE-PS 32 06 751 shows a process for the production foamed gelatinized starch products in one Extruder press, being made of a relatively rigid foam is assumed.
Die WO 93/03976 zeigt ein Verfahren zum Herstellen neuer Verpackungsstoffe aus u. a. stärkehaltigen Rohstoffen und organischen Abfallstoffen sowie Additiven zur Verbesserung der elastischen Eigenschaften in einem Extrusionsverfahren, wobei zusätzlich - auf das Extrudat ein Überzug aus faserigen organischen Abfallstoffen aufgebracht wird.WO 93/03976 shows a method for producing new ones Packaging materials from u. a. starchy raw materials and organic waste materials and additives to improve the elastic properties in an extrusion process, wherein in addition - on the extrudate a coating of fibrous organic waste is applied.
Die US 48 36 655 zeigt ein biologisch abbaubares Verpackunggmaterial und ein Extrusionsverfahren zu seiner Herstellung ohne den Einsatz von Hüllmaterial.The US 48 36 655 shows a biodegradable Packaging material and an extrusion process for it Manufactured without the use of wrapping material.
Die US 46 27 947 beschreibt einen Kunststoff als schüttfähiges Verpackungsmaterial sowie dessen Herstellung.The US 46 27 947 describes a plastic as pourable packaging material and its production.
Die US 51 85 009 beschreibt eine biologisch abbaubare Windel bestehend aus einer äußeren wasserdichten, abbaubaren Folie und einer inneren abbaubaren, wasserdurchlässigen Schicht, die mit der äußeren Folie verbunden ist und ein definiertes Volumen formt sowie weiteren spezifischen Teilen für Windeln. Die äußere Hülle einer derartigen Windel kann aus Rayon oder Polypropylen, die innere Hülle aus Polyethylen bestehen.US 51 85 009 describes a biodegradable Diaper consisting of an outer waterproof, degradable Foil and an inner degradable, water-permeable Layer that is connected to the outer film and a defined volume forms as well as other specific parts for diapers. The outer shell of such a diaper can be made of Rayon or polypropylene, the inner shell made of polyethylene consist.
Die US 51 85 382 und 52 08 267 beschreiben auf Stärke basierendes, biologisch abbaubares Füllmaterial in Form von expandierten, kompressiblen und elastischen Formkörpern.US 51 85 382 and 52 08 267 describe Starch-based, biodegradable filling material in the form of expanded, compressible and elastic molded bodies.
Der CAPLUS-Abstract Nr. 1986 : 408185 beschreibt das Aufbringen von aufgeschäumtem Stärkematerial auf Papier mit hoher Geschwindigkeit.CAPLUS abstract No. 1986: 408185 describes this Applying foamed starch material to paper with high speed.
Aufgabe der Erfindung ist es, ein variables Formteil zur Verwendung als Transportschutz zu schaffen, das unterschied lichste Belastungsarten dämpfen kann, mehrfach verwendet werden kann, den Verpackungsaufwand minimiert und völlstän dig biologisch abbaubar ist. Ferner soll ein Baudämmstoff geschaffen werden.The object of the invention is to provide a variable molding To create use as transport protection that made a difference can dampen the most diverse types of stress, used several times the packaging effort can be minimized and complete dig is biodegradable. Furthermore, a building insulation material be created.
Diese Aufgabe wird mit den Merkmalen der Patentansprüche 1-10 ge löst.This object is ge with the features of claims 1-10 solves.
Bei der Lösung geht die Erfindung von dem Grundgedanken aus, elastische Formteile aus Stärkeschaum zu fertigen und in eine Hülle aus ebenfalls biologisch abbaubarem Material zu füllen. Der Stärkeschaum ist in variabler Form, Größe und Dichte ausgeführt und besitzt daher auch eine, variable Elastizität. Der Volumenanteil der Füllung wird an den Ver wendungszweck z. B. die Transportanforderungen bei der Ver wendung als Transportschutz und das Gewicht des Packgutes angepaßt. Die Verwendung der variablen Formteile erfolgt auch als Füllmaterial für Baudämmstoffsysteme.In the solution, the invention is based on the basic idea to produce elastic molded parts from starch foam and in a cover made of biodegradable material to fill. The starch foam is of variable shape, size and Dense and therefore has a variable Elasticity. The volume fraction of the filling is transferred to the ver purpose z. B. the transport requirements at Ver Use as transport protection and the weight of the packaged goods customized. The variable molded parts are used also as filling material for building insulation systems.
Das variable Formteil besitzt folgende Vorteile:
The variable molded part has the following advantages:
- - Mit wenigen unterschiedlichen Kissenvolumen können ver schieden große Erzeugnisse auf dem Transport vor Beschädi gung durch Schockbelastung wirkungsvoll geschützt werden.- With a few different pillow volumes, ver separated large products from damage during transport effective protection from shock.
- - Durch die Variation der Kissenfüllung aus expandierter Stärke sowie durch das Schüttgewicht und die Formgestal tung (Kugeln, Zylinder bzw. Hohlzylinder) wird das Schutz polster auf leichte oder schwere Erzeugnisse angepaßt.- By varying the pillow filling from expanded Starch as well as the bulk density and the shape protection (balls, cylinders or hollow cylinders) becomes the protection Upholstery adapted to light or heavy products.
- - Die Formteile sind sehr leicht (5 bis 50 kg/m3), sie kön nen mehrfach verwendet werden, sind antistatisch, voll ständig biologisch abbaubar und kompostierbar.- The molded parts are very light (5 to 50 kg / m 3 ), they can be used several times, are antistatic, completely biodegradable and compostable.
- - Die Herstellung der Formteile direkt beim Anwender, führt zu erheblicher Reduzierung der Maschinen-, Personal- und Raumkosten und vereinfacht den Transport, da im Vergleich zu fertig geschäumten Chips das Transportvolumen erheblich geringer ist.- The production of the molded parts directly at the user, leads to significant reduction in machine, personnel and Space costs and simplifies transportation, as compared transport volume to the foamed chips considerably is less.
- - Bei der Verwendung für Baudämmstoffsysteme läßt sich Stär keschaum gegenüber bisher gebräuchlichen Mineralfasern sehr einfkach verarbeiten, da sowohl der übliche Juckreiz durch Faserstaub als auch die Gefahr der Gesundheitsschä digung aufgrund der krebserregenden Wirkung entfällt.- When used for building insulation systems, starch can be k foam compared to previously used mineral fibers Process very easily, as both the usual itching due to fiber dust as well as the risk of health damage No damage due to the carcinogenic effects.
Im folgenden wird die Erfindung anhand der Zeichnungen näher erläutert. Es zeigen: The invention will be described in more detail below with reference to the drawings explained. Show it:
Fig. 1a-1g erfindungsgemäße Ausführungsformen der Stärke schaumkörper, Fig. 1a-1g embodiments of the invention the starch foam body,
Fig. 2 das Verfahrensprinzip zur Herstellung erfin dungsgemäßer Baudämmstoffsysteme, Fig. 2 shows the principle method for producing OF INVENTION dung according Baudämmstoffsysteme,
Fig. 3 eine Ansicht des Baudämmstoffes mit aneinander gereihten Baudämmstoffbeuteln von oben und Fig. 3 is a view of the insulation material with construction insulation bags lined up from above and
Fig. 4 einen Schnitt durch die Fig. 3. Fig. 4 is a section through the FIG. 3.
Nach einem Ausführungsbeispiel der Erfindung zur Ausbildung eines Transportschutzes wird ein Kissenpolster aus einem Hüllenmaterial, bestehend aus Papier, insbesondere Filterpa pier, Teebeutelpapier, Cellulosefaservlies und/oder Textil material gefertigt und mit einer Polsterfüllung aus einem elastischen, flexiblen Stärkeschaum mit kugeliger und/oder zylindrischer Gestalt auf Basis natürlicher Pflanzenstärke versehen (Fig. 1a bis 1g). Das Volumen des Hüllenmate rials ist teilweise 50 bis 90% mit Stärkeschaumkugeln ge füllt, so daß das Schutzpolster sich der Form des zu schüt zenden Erzeugnisses und der Form des Verpackungsmittels (Um karton, Kiste, Dose) selbständig anpaßt.According to an embodiment of the invention for forming a transport protection, a cushion pad is made of a cover material consisting of paper, in particular filter paper, tea bag paper, cellulose fiber fleece and / or textile material and with a padding made of an elastic, flexible starch foam with a spherical and / or cylindrical shape provided on the basis of natural plant starch ( Fig. 1a to 1g). The volume of the Hüllenmate rials is partially 50 to 90% ge filled with starch foam balls, so that the protective pad adapts itself to the shape of the product to be protected and the shape of the packaging material (order box, box, can).
Durch die allseitige Umhüllung des stoßempfindlichen Erzeug nisses mit den elastischen, aufgeblähten, eingehüllten Stär kekugeln wird das Erzeugnis hervorragend gegen Transportbe schädigungen geschützt. Die Stärkeschaumfüllung kann durch Einstellung des Schüttgewichtes zwischen 5 und 50 kg/m3 je nach Anforderungen für leichte oder schwere zu schützende Gegenstände variieren. Ebenso kann die Kissenform auf die geforderte Verpackungsgröße mit einer großen Variations breite eingestellt werden.Due to the all-round covering of the shock-sensitive product with the elastic, inflated, enveloped starch balls, the product is superbly protected against transport damage. The starch foam filling can vary by adjusting the bulk density between 5 and 50 kg / m 3 depending on the requirements for light or heavy objects to be protected. The pillow shape can also be adjusted to the required packaging size with a wide range of variations.
Für die bedarfsgerechte Verwendung der Formteile ist es mög lich, direkt beim Anwender in einem geeigneten kleineren Heißluft- oder Mikrowellengerät geschnittene Hohlstränge oder Granulate zu Stärkeschaumchips aufzublähen. It is possible for the molded parts to be used as required Lich, directly at the user in a suitable smaller one Hot air or microwave oven cut hollow strands or inflate granules into starch foam chips.
Somit kann die Form, Größe, Elastizität und benötigte Menge der Formteile vom Anwender selbst am Einsatzort bestimmt werden.Thus, the shape, size, elasticity and quantity required of the molded parts determined by the user himself at the place of use will.
Im Rahmen der Erfindung werden auch solche Formteile bean sprucht, die geformte Schaumteile aus Kunststoffschaum, z. B. Polystyrol enthalten und deren Hülle aus Naturprodukten oder auch aus Kunststoffen besteht.In the context of the invention, such molded parts are also bean says, the molded foam parts made of plastic foam, for. B. Contain polystyrene and their shell from natural products or also consists of plastics.
Nach der Erfindung wird der geformte Stärkeschaum auch als Füllmaterial für Baudämmstoffsysteme verwendet. Dazu wird schüttfähiger Stärkeschaum in eine Hülle, insbesondere in Papierschläuche gefüllt, die Baudämmstoffbeutel bilden. Diese werden quer abgesteppt, so daß der Stärkeschaum in seinem jeweiligen Volumenabschnitt des Beutels verbleibt.According to the invention, the shaped starch foam is also used as Filling material used for building insulation systems. This will pourable starch foam in a shell, especially in Filled paper hoses that form building insulation bags. These are quilted crosswise, so that the starch foam in its respective volume section of the bag remains.
Die Volumenabschnitte des Beutels können unterschiedlich ge füllt oder der abgesteppte Beutel aufgerollt oder gefaltet werden. Die Beutel sind in variablen Abmessungen herstellbar und mit seitlich angeordneten Befestigungslaschen versehen.The volume sections of the bag can be different fills or the quilted bag is rolled up or folded will. The bags can be manufactured in variable dimensions and provided with fastening tabs on the side.
Über die Schüttdichte des Stärkeschaumes und den Grad der Beutelfüllung sind die Baudämmstoffbeutel auf einen ge wünschten Wärmedämmwert einstellbar.About the bulk density of the starch foam and the degree of Bag filling are the insulation bags on a ge desired thermal insulation value adjustable.
Für die Herstellung der Baudämmstoffbeutel wird als Hülle vorzugsweise Papier, beschichtetes Papier, ein Papier-Alumi niumverbund und/oder Kunststoffolie verwendet.For the production of the insulation bag is used as a sleeve preferably paper, coated paper, a paper aluminum nium composite and / or plastic film used.
Nach einem anhand der Fig. 2 bis 4 erläutertem weiteren Ausführungsbeispiel werden zwei Bänder 1 des Hüllmaterials kontinuierlich von ihren Rollen 2 abgerollt, über Umlenkrol len 3 gespannt und horizontal übereinander verlaufend bis zu einem bestimmten Abstand zusammengeführt. Eine Umlenkrolle 4 besitzt abgesenkte Außenränder, so daß eines der Bänder 1 entlang seiner äußeren Längsseiten mit geringem Abstand von der Außenkante gefalzt wird und so der für die Füllung vor gesehene Raum vorgeformt wird. Fig. 4 verdeutlicht diese Ausbildung des oberen Bandes 1. In den Zwischenraum zwischen die Bänder 1 wird geformter Stärkeschaum 5, aus dem die Fül lung besteht, von einer Füllstoffaufgabe 6 eingebracht und die Bänder 1 gleichzeitig entlang ihrer äußeren Längsseiten zur Ausbildung eines Schlauches 7 miteinander verschweißt oder in einer anderen geeigneten Weise dicht zusammengefügt. Die Schweißnaht verläuft, wie Fig. 3 zeigt, in geringem Ab stand vom Rand der Bänder 1 und die äußeren Längsseiten des Schlauches 7 bilden somit Befestigungslaschen 8, die später das Anbringen der fertigen Baudämmstoffbeutel 9 bei deren bestimmungsgemäßem Gebrauch erleichtert.According to a further embodiment explained with reference to FIGS. 2 to 4, two tapes 1 of the wrapping material are continuously rolled off their rollers 2 , stretched over deflecting rollers 3 and merged horizontally one above the other to a certain distance. A deflection roller 4 has lowered outer edges, so that one of the strips 1 is folded along its outer longitudinal sides at a short distance from the outer edge and so the space seen before for the filling is preformed. Fig. 4 illustrates this configuration of the upper belt 1. In the space between the tapes 1 is formed starch foam 5 , which consists of the filling, introduced by a filler 6 and the tapes 1 are welded together along their outer longitudinal sides to form a tube 7 or tightly joined in another suitable manner. The weld runs, as shown in FIG. 3, in a small amount from the edge of the tapes 1 and the outer longitudinal sides of the hose 7 thus form fastening tabs 8 , which later facilitates the attachment of the finished insulation bag 9 when used as intended.
Nach einer weiteren Ausführung kann die Hülle ebenso als fertiger Schlauch mit angeformten Befestigungslaschen 9 vor liegen und mit dem Stärkeschaum 5 befüllt werden.According to a further embodiment, the sheath can also be in the form of a finished tube with integrally formed fastening tabs 9 and can be filled with the starch foam 5 .
Gleichzeitig mit dem Einbringen des Stärkeschaumes 5 in die Hülle wird dieser auch in seiner Hülle verdichtet. Durch un terschiedliche Befüllung und Dicke der Baudämmstoffbeutel 9 sind diese auf den gewünschten Wärmedämmwert einstellbar.Simultaneously with the introduction of the starch foam 5 into the casing, it is also compressed in its casing. By un different filling and thickness of the insulation bag 9 , these are adjustable to the desired thermal insulation value.
Die Breite der Baudämmstoffbeutel 9 ist entsprechend dem je weiligen Einsatzgebiet, beispielsweise bei Verwendung für Dachisolationen auf die Sparren- bzw. Balkenabstände abge stimmt und kann 40, 60 oder 80 cm betragen. Die Länge der Baudämmstoffbeutel 9 ist mittels einer Steppeinrichtung 10 einstellbar und richtet sich ebenfalls nach den Einsatzbe dingungen. Der fertige Schlauch 7 mit den aneinandergereih ten Baudämmstoffbeuteln 9 ist endlos lang ausgebildet und wird auf eine Rolle 11 aufgerollt. Bei der späteren Verar beitung ist er zweckmäßigerweise an den Steppnähten trenn bar.The width of the insulation bag 9 is in accordance with the respective area of application, for example when used for roof insulation on the rafter or beam spacing and can be 40, 60 or 80 cm. The length of the insulation bag 9 is adjustable by means of a quilting device 10 and also depends on the conditions of use. The finished hose 7 with the aneinergergehh th building insulation bags 9 is endlessly long and is rolled up on a roll 11 . In the later processing, it is conveniently separable at the stitching bar.
Claims (9)