DE68915042D1 - Film mit geringerer Emission für Hochtemperaturbehandlung. - Google Patents
Film mit geringerer Emission für Hochtemperaturbehandlung.Info
- Publication number
- DE68915042D1 DE68915042D1 DE68915042T DE68915042T DE68915042D1 DE 68915042 D1 DE68915042 D1 DE 68915042D1 DE 68915042 T DE68915042 T DE 68915042T DE 68915042 T DE68915042 T DE 68915042T DE 68915042 D1 DE68915042 D1 DE 68915042D1
- Authority
- DE
- Germany
- Prior art keywords
- high temperature
- temperature treatment
- emission film
- lower emission
- film
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Lifetime
Links
Classifications
-
- C—CHEMISTRY; METALLURGY
- C03—GLASS; MINERAL OR SLAG WOOL
- C03C—CHEMICAL COMPOSITION OF GLASSES, GLAZES OR VITREOUS ENAMELS; SURFACE TREATMENT OF GLASS; SURFACE TREATMENT OF FIBRES OR FILAMENTS MADE FROM GLASS, MINERALS OR SLAGS; JOINING GLASS TO GLASS OR OTHER MATERIALS
- C03C17/00—Surface treatment of glass, not in the form of fibres or filaments, by coating
- C03C17/06—Surface treatment of glass, not in the form of fibres or filaments, by coating with metals
-
- C—CHEMISTRY; METALLURGY
- C03—GLASS; MINERAL OR SLAG WOOL
- C03C—CHEMICAL COMPOSITION OF GLASSES, GLAZES OR VITREOUS ENAMELS; SURFACE TREATMENT OF GLASS; SURFACE TREATMENT OF FIBRES OR FILAMENTS MADE FROM GLASS, MINERALS OR SLAGS; JOINING GLASS TO GLASS OR OTHER MATERIALS
- C03C17/00—Surface treatment of glass, not in the form of fibres or filaments, by coating
- C03C17/34—Surface treatment of glass, not in the form of fibres or filaments, by coating with at least two coatings having different compositions
- C03C17/36—Surface treatment of glass, not in the form of fibres or filaments, by coating with at least two coatings having different compositions at least one coating being a metal
- C03C17/3602—Surface treatment of glass, not in the form of fibres or filaments, by coating with at least two coatings having different compositions at least one coating being a metal the metal being present as a layer
- C03C17/3618—Coatings of type glass/inorganic compound/other inorganic layers, at least one layer being metallic
-
- C—CHEMISTRY; METALLURGY
- C03—GLASS; MINERAL OR SLAG WOOL
- C03C—CHEMICAL COMPOSITION OF GLASSES, GLAZES OR VITREOUS ENAMELS; SURFACE TREATMENT OF GLASS; SURFACE TREATMENT OF FIBRES OR FILAMENTS MADE FROM GLASS, MINERALS OR SLAGS; JOINING GLASS TO GLASS OR OTHER MATERIALS
- C03C17/00—Surface treatment of glass, not in the form of fibres or filaments, by coating
- C03C17/34—Surface treatment of glass, not in the form of fibres or filaments, by coating with at least two coatings having different compositions
- C03C17/36—Surface treatment of glass, not in the form of fibres or filaments, by coating with at least two coatings having different compositions at least one coating being a metal
-
- C—CHEMISTRY; METALLURGY
- C03—GLASS; MINERAL OR SLAG WOOL
- C03C—CHEMICAL COMPOSITION OF GLASSES, GLAZES OR VITREOUS ENAMELS; SURFACE TREATMENT OF GLASS; SURFACE TREATMENT OF FIBRES OR FILAMENTS MADE FROM GLASS, MINERALS OR SLAGS; JOINING GLASS TO GLASS OR OTHER MATERIALS
- C03C17/00—Surface treatment of glass, not in the form of fibres or filaments, by coating
- C03C17/34—Surface treatment of glass, not in the form of fibres or filaments, by coating with at least two coatings having different compositions
- C03C17/36—Surface treatment of glass, not in the form of fibres or filaments, by coating with at least two coatings having different compositions at least one coating being a metal
- C03C17/3602—Surface treatment of glass, not in the form of fibres or filaments, by coating with at least two coatings having different compositions at least one coating being a metal the metal being present as a layer
- C03C17/3644—Surface treatment of glass, not in the form of fibres or filaments, by coating with at least two coatings having different compositions at least one coating being a metal the metal being present as a layer the metal being silver
-
- C—CHEMISTRY; METALLURGY
- C03—GLASS; MINERAL OR SLAG WOOL
- C03C—CHEMICAL COMPOSITION OF GLASSES, GLAZES OR VITREOUS ENAMELS; SURFACE TREATMENT OF GLASS; SURFACE TREATMENT OF FIBRES OR FILAMENTS MADE FROM GLASS, MINERALS OR SLAGS; JOINING GLASS TO GLASS OR OTHER MATERIALS
- C03C17/00—Surface treatment of glass, not in the form of fibres or filaments, by coating
- C03C17/34—Surface treatment of glass, not in the form of fibres or filaments, by coating with at least two coatings having different compositions
- C03C17/36—Surface treatment of glass, not in the form of fibres or filaments, by coating with at least two coatings having different compositions at least one coating being a metal
- C03C17/3602—Surface treatment of glass, not in the form of fibres or filaments, by coating with at least two coatings having different compositions at least one coating being a metal the metal being present as a layer
- C03C17/3652—Surface treatment of glass, not in the form of fibres or filaments, by coating with at least two coatings having different compositions at least one coating being a metal the metal being present as a layer the coating stack containing at least one sacrificial layer to protect the metal from oxidation
-
- C—CHEMISTRY; METALLURGY
- C03—GLASS; MINERAL OR SLAG WOOL
- C03C—CHEMICAL COMPOSITION OF GLASSES, GLAZES OR VITREOUS ENAMELS; SURFACE TREATMENT OF GLASS; SURFACE TREATMENT OF FIBRES OR FILAMENTS MADE FROM GLASS, MINERALS OR SLAGS; JOINING GLASS TO GLASS OR OTHER MATERIALS
- C03C17/00—Surface treatment of glass, not in the form of fibres or filaments, by coating
- C03C17/34—Surface treatment of glass, not in the form of fibres or filaments, by coating with at least two coatings having different compositions
- C03C17/36—Surface treatment of glass, not in the form of fibres or filaments, by coating with at least two coatings having different compositions at least one coating being a metal
- C03C17/3602—Surface treatment of glass, not in the form of fibres or filaments, by coating with at least two coatings having different compositions at least one coating being a metal the metal being present as a layer
- C03C17/3657—Surface treatment of glass, not in the form of fibres or filaments, by coating with at least two coatings having different compositions at least one coating being a metal the metal being present as a layer the multilayer coating having optical properties
- C03C17/366—Low-emissivity or solar control coatings
-
- C—CHEMISTRY; METALLURGY
- C03—GLASS; MINERAL OR SLAG WOOL
- C03C—CHEMICAL COMPOSITION OF GLASSES, GLAZES OR VITREOUS ENAMELS; SURFACE TREATMENT OF GLASS; SURFACE TREATMENT OF FIBRES OR FILAMENTS MADE FROM GLASS, MINERALS OR SLAGS; JOINING GLASS TO GLASS OR OTHER MATERIALS
- C03C17/00—Surface treatment of glass, not in the form of fibres or filaments, by coating
- C03C17/34—Surface treatment of glass, not in the form of fibres or filaments, by coating with at least two coatings having different compositions
- C03C17/36—Surface treatment of glass, not in the form of fibres or filaments, by coating with at least two coatings having different compositions at least one coating being a metal
- C03C17/3602—Surface treatment of glass, not in the form of fibres or filaments, by coating with at least two coatings having different compositions at least one coating being a metal the metal being present as a layer
- C03C17/3681—Surface treatment of glass, not in the form of fibres or filaments, by coating with at least two coatings having different compositions at least one coating being a metal the metal being present as a layer the multilayer coating being used in glazing, e.g. windows or windscreens
-
- C—CHEMISTRY; METALLURGY
- C03—GLASS; MINERAL OR SLAG WOOL
- C03C—CHEMICAL COMPOSITION OF GLASSES, GLAZES OR VITREOUS ENAMELS; SURFACE TREATMENT OF GLASS; SURFACE TREATMENT OF FIBRES OR FILAMENTS MADE FROM GLASS, MINERALS OR SLAGS; JOINING GLASS TO GLASS OR OTHER MATERIALS
- C03C17/00—Surface treatment of glass, not in the form of fibres or filaments, by coating
- C03C17/34—Surface treatment of glass, not in the form of fibres or filaments, by coating with at least two coatings having different compositions
- C03C17/36—Surface treatment of glass, not in the form of fibres or filaments, by coating with at least two coatings having different compositions at least one coating being a metal
- C03C17/3602—Surface treatment of glass, not in the form of fibres or filaments, by coating with at least two coatings having different compositions at least one coating being a metal the metal being present as a layer
- C03C17/3689—Surface treatment of glass, not in the form of fibres or filaments, by coating with at least two coatings having different compositions at least one coating being a metal the metal being present as a layer one oxide layer being obtained by oxidation of a metallic layer
-
- G—PHYSICS
- G02—OPTICS
- G02B—OPTICAL ELEMENTS, SYSTEMS OR APPARATUS
- G02B1/00—Optical elements characterised by the material of which they are made; Optical coatings for optical elements
- G02B1/10—Optical coatings produced by application to, or surface treatment of, optical elements
-
- G—PHYSICS
- G02—OPTICS
- G02B—OPTICAL ELEMENTS, SYSTEMS OR APPARATUS
- G02B1/00—Optical elements characterised by the material of which they are made; Optical coatings for optical elements
- G02B1/10—Optical coatings produced by application to, or surface treatment of, optical elements
- G02B1/11—Anti-reflection coatings
- G02B1/113—Anti-reflection coatings using inorganic layer materials only
- G02B1/115—Multilayers
- G02B1/116—Multilayers including electrically conducting layers
-
- G—PHYSICS
- G02—OPTICS
- G02B—OPTICAL ELEMENTS, SYSTEMS OR APPARATUS
- G02B5/00—Optical elements other than lenses
- G02B5/20—Filters
- G02B5/208—Filters for use with infrared or ultraviolet radiation, e.g. for separating visible light from infrared and/or ultraviolet radiation
-
- C—CHEMISTRY; METALLURGY
- C03—GLASS; MINERAL OR SLAG WOOL
- C03C—CHEMICAL COMPOSITION OF GLASSES, GLAZES OR VITREOUS ENAMELS; SURFACE TREATMENT OF GLASS; SURFACE TREATMENT OF FIBRES OR FILAMENTS MADE FROM GLASS, MINERALS OR SLAGS; JOINING GLASS TO GLASS OR OTHER MATERIALS
- C03C2217/00—Coatings on glass
- C03C2217/70—Properties of coatings
- C03C2217/78—Coatings specially designed to be durable, e.g. scratch-resistant
-
- Y—GENERAL TAGGING OF NEW TECHNOLOGICAL DEVELOPMENTS; GENERAL TAGGING OF CROSS-SECTIONAL TECHNOLOGIES SPANNING OVER SEVERAL SECTIONS OF THE IPC; TECHNICAL SUBJECTS COVERED BY FORMER USPC CROSS-REFERENCE ART COLLECTIONS [XRACs] AND DIGESTS
- Y10—TECHNICAL SUBJECTS COVERED BY FORMER USPC
- Y10T—TECHNICAL SUBJECTS COVERED BY FORMER US CLASSIFICATION
- Y10T428/00—Stock material or miscellaneous articles
- Y10T428/12—All metal or with adjacent metals
- Y10T428/12493—Composite; i.e., plural, adjacent, spatially distinct metal components [e.g., layers, joint, etc.]
- Y10T428/12535—Composite; i.e., plural, adjacent, spatially distinct metal components [e.g., layers, joint, etc.] with additional, spatially distinct nonmetal component
- Y10T428/12542—More than one such component
- Y10T428/12549—Adjacent to each other
-
- Y—GENERAL TAGGING OF NEW TECHNOLOGICAL DEVELOPMENTS; GENERAL TAGGING OF CROSS-SECTIONAL TECHNOLOGIES SPANNING OVER SEVERAL SECTIONS OF THE IPC; TECHNICAL SUBJECTS COVERED BY FORMER USPC CROSS-REFERENCE ART COLLECTIONS [XRACs] AND DIGESTS
- Y10—TECHNICAL SUBJECTS COVERED BY FORMER USPC
- Y10T—TECHNICAL SUBJECTS COVERED BY FORMER US CLASSIFICATION
- Y10T428/00—Stock material or miscellaneous articles
- Y10T428/12—All metal or with adjacent metals
- Y10T428/12493—Composite; i.e., plural, adjacent, spatially distinct metal components [e.g., layers, joint, etc.]
- Y10T428/12535—Composite; i.e., plural, adjacent, spatially distinct metal components [e.g., layers, joint, etc.] with additional, spatially distinct nonmetal component
- Y10T428/12611—Oxide-containing component
-
- Y—GENERAL TAGGING OF NEW TECHNOLOGICAL DEVELOPMENTS; GENERAL TAGGING OF CROSS-SECTIONAL TECHNOLOGIES SPANNING OVER SEVERAL SECTIONS OF THE IPC; TECHNICAL SUBJECTS COVERED BY FORMER USPC CROSS-REFERENCE ART COLLECTIONS [XRACs] AND DIGESTS
- Y10—TECHNICAL SUBJECTS COVERED BY FORMER USPC
- Y10T—TECHNICAL SUBJECTS COVERED BY FORMER US CLASSIFICATION
- Y10T428/00—Stock material or miscellaneous articles
- Y10T428/12—All metal or with adjacent metals
- Y10T428/12493—Composite; i.e., plural, adjacent, spatially distinct metal components [e.g., layers, joint, etc.]
- Y10T428/12771—Transition metal-base component
- Y10T428/12806—Refractory [Group IVB, VB, or VIB] metal-base component
-
- Y—GENERAL TAGGING OF NEW TECHNOLOGICAL DEVELOPMENTS; GENERAL TAGGING OF CROSS-SECTIONAL TECHNOLOGIES SPANNING OVER SEVERAL SECTIONS OF THE IPC; TECHNICAL SUBJECTS COVERED BY FORMER USPC CROSS-REFERENCE ART COLLECTIONS [XRACs] AND DIGESTS
- Y10—TECHNICAL SUBJECTS COVERED BY FORMER USPC
- Y10T—TECHNICAL SUBJECTS COVERED BY FORMER US CLASSIFICATION
- Y10T428/00—Stock material or miscellaneous articles
- Y10T428/12—All metal or with adjacent metals
- Y10T428/12493—Composite; i.e., plural, adjacent, spatially distinct metal components [e.g., layers, joint, etc.]
- Y10T428/12771—Transition metal-base component
- Y10T428/12861—Group VIII or IB metal-base component
- Y10T428/12896—Ag-base component
Applications Claiming Priority (1)
Application Number | Priority Date | Filing Date | Title |
---|---|---|---|
US07/176,511 US4898790A (en) | 1986-12-29 | 1988-04-01 | Low emissivity film for high temperature processing |
Publications (2)
Publication Number | Publication Date |
---|---|
DE68915042D1 true DE68915042D1 (de) | 1994-06-09 |
DE68915042T2 DE68915042T2 (de) | 1994-11-17 |
Family
ID=22644647
Family Applications (1)
Application Number | Title | Priority Date | Filing Date |
---|---|---|---|
DE68915042T Expired - Lifetime DE68915042T2 (de) | 1988-04-01 | 1989-03-28 | Film mit geringerer Emission für Hochtemperaturbehandlung. |
Country Status (8)
Country | Link |
---|---|
US (1) | US4898790A (de) |
EP (1) | EP0335309B1 (de) |
JP (1) | JP2505278B2 (de) |
KR (1) | KR920005471B1 (de) |
BR (1) | BR8901510A (de) |
CA (1) | CA1337483C (de) |
DE (1) | DE68915042T2 (de) |
ES (1) | ES2056136T3 (de) |
Families Citing this family (141)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
US5112693A (en) * | 1988-10-03 | 1992-05-12 | Ppg Industries, Inc. | Low reflectance, highly saturated colored coating for monolithic glazing |
US5153062A (en) * | 1989-02-13 | 1992-10-06 | Hoechst Aktiengesellschaft | Process and device for producing laminated safety glass and laminated safety glass produced thereby |
US5215832A (en) * | 1990-04-25 | 1993-06-01 | Cardinal Ic Company | Lead-free mirrors and environmentally safe manufacture thereof |
US5296302A (en) * | 1992-03-27 | 1994-03-22 | Cardinal Ig Company | Abrasion-resistant overcoat for coated substrates |
DE69328197T2 (de) * | 1992-12-15 | 2000-08-17 | Idemitsu Kosan Co | Transparente, leitende schicht, transparentes, leitendes basismaterial und leitendes material |
DE69428253T2 (de) | 1993-11-12 | 2002-06-27 | Ppg Ind Ohio Inc | Haltbare Sputterschicht aus Metalloxid |
DE4409934A1 (de) * | 1994-03-23 | 1995-09-28 | Ver Glaswerke Gmbh | Verfahren und Vorrichtung zum Beschichten einer Glasscheibe mit wenigstens einer Schicht aus Zinndioxid durch reaktive Katodenzerstäubung |
CA2161283A1 (en) | 1994-12-27 | 1996-06-28 | Ppg Industries Ohio, Inc. | Annealed low emissivity coating |
US6142642A (en) * | 1995-06-29 | 2000-11-07 | Cardinal Ig Company | Bendable mirrors and method of manufacture |
US6086210A (en) * | 1995-06-29 | 2000-07-11 | Cardinal Ig Company | Bendable mirrors and method of manufacture |
US5821001A (en) * | 1996-04-25 | 1998-10-13 | Ppg Industries, Inc. | Coated articles |
US20020155299A1 (en) | 1997-03-14 | 2002-10-24 | Harris Caroline S. | Photo-induced hydrophilic article and method of making same |
US7096692B2 (en) * | 1997-03-14 | 2006-08-29 | Ppg Industries Ohio, Inc. | Visible-light-responsive photoactive coating, coated article, and method of making same |
US20030039843A1 (en) * | 1997-03-14 | 2003-02-27 | Christopher Johnson | Photoactive coating, coated article, and method of making same |
US20050096288A1 (en) * | 1997-06-13 | 2005-05-05 | Aragene, Inc. | Lipoproteins as nucleic acid vectors |
ATE215911T1 (de) | 1997-10-31 | 2002-04-15 | Cardinal Cg Co | Hitzebiegbare spiegel |
US6899953B1 (en) * | 1998-05-08 | 2005-05-31 | Ppg Industries Ohio, Inc. | Shippable heat-treatable sputter coated article and zinc cathode sputtering target containing low amounts of tin |
US6833194B1 (en) * | 1998-05-12 | 2004-12-21 | Ppg Industries Ohio, Inc. | Protective layers for sputter coated article |
CZ20012219A3 (cs) | 1998-12-18 | 2002-02-13 | Glaverbel | Zasklívací tabule a způsob její výroby |
US6610410B2 (en) | 1998-12-18 | 2003-08-26 | Asahi Glass Company, Limited | Glazing panel |
US6582799B1 (en) | 1999-06-02 | 2003-06-24 | Ppg Industries Ohio, Inc. | Laminated transparency |
US6849328B1 (en) | 1999-07-02 | 2005-02-01 | Ppg Industries Ohio, Inc. | Light-transmitting and/or coated article with removable protective coating and methods of making the same |
US20070036989A1 (en) * | 1999-11-24 | 2007-02-15 | Ppg Industries Ohio, Inc. | Low shading coefficient and low emissivity coatings and coated articles |
US20020136905A1 (en) * | 1999-11-24 | 2002-09-26 | Medwick Paul A. | Low shading coefficient and low emissivity coatings and coated articles |
CA2390404A1 (en) | 1999-11-24 | 2001-05-31 | Ppg Industries Ohio, Inc. | Low shading coefficient and low emissivity coatings and coated articles |
US6475626B1 (en) | 1999-12-06 | 2002-11-05 | Guardian Industries Corp. | Low-E matchable coated articles and methods of making same |
US6495263B2 (en) | 1999-12-06 | 2002-12-17 | Guardian Industries Corp. | Low-E matchable coated articles and methods of making same |
US6514620B1 (en) | 1999-12-06 | 2003-02-04 | Guardian Industries Corp. | Matchable low-E I G units and laminates and methods of making same |
US7361404B2 (en) | 2000-05-10 | 2008-04-22 | Ppg Industries Ohio, Inc. | Coated article with removable protective coating and related methods |
US6887575B2 (en) * | 2001-10-17 | 2005-05-03 | Guardian Industries Corp. | Heat treatable coated article with zinc oxide inclusive contact layer(s) |
US7267879B2 (en) | 2001-02-28 | 2007-09-11 | Guardian Industries Corp. | Coated article with silicon oxynitride adjacent glass |
US7462397B2 (en) * | 2000-07-10 | 2008-12-09 | Guardian Industries Corp. | Coated article with silicon nitride inclusive layer adjacent glass |
US6576349B2 (en) | 2000-07-10 | 2003-06-10 | Guardian Industries Corp. | Heat treatable low-E coated articles and methods of making same |
US6445503B1 (en) | 2000-07-10 | 2002-09-03 | Guardian Industries Corp. | High durable, low-E, heat treatable layer coating system |
US7323249B2 (en) * | 2000-08-31 | 2008-01-29 | Ppg Industries Ohio, Inc. | Methods of obtaining photoactive coatings and/or anatase crystalline phase of titanium oxides and articles made thereby |
US6677063B2 (en) | 2000-08-31 | 2004-01-13 | Ppg Industries Ohio, Inc. | Methods of obtaining photoactive coatings and/or anatase crystalline phase of titanium oxides and articles made thereby |
US6869644B2 (en) * | 2000-10-24 | 2005-03-22 | Ppg Industries Ohio, Inc. | Method of making coated articles and coated articles made thereby |
US7311961B2 (en) * | 2000-10-24 | 2007-12-25 | Ppg Industries Ohio, Inc. | Method of making coated articles and coated articles made thereby |
US20020172775A1 (en) * | 2000-10-24 | 2002-11-21 | Harry Buhay | Method of making coated articles and coated articles made thereby |
DE10063180A1 (de) * | 2000-12-18 | 2002-06-27 | Bayer Ag | Vorrichtung zur Erzeugung von Lichtsignalen |
US20020120916A1 (en) * | 2001-01-16 | 2002-08-29 | Snider Albert Monroe | Head-up display system utilizing fluorescent material |
WO2002081390A1 (en) * | 2001-03-20 | 2002-10-17 | Ppg Industries Ohio, Inc. | Method and apparatus for forming patterned and/or textured glass and glass articles formed thereby |
US20030049464A1 (en) | 2001-09-04 | 2003-03-13 | Afg Industries, Inc. | Double silver low-emissivity and solar control coatings |
US6942923B2 (en) | 2001-12-21 | 2005-09-13 | Guardian Industries Corp. | Low-e coating with high visible transmission |
US7232615B2 (en) * | 2001-10-22 | 2007-06-19 | Ppg Industries Ohio, Inc. | Coating stack comprising a layer of barrier coating |
US6730389B2 (en) | 2001-10-25 | 2004-05-04 | Ppg Industries Ohio, Inc. | Coated substrate having a frequency selective surface |
US6602608B2 (en) | 2001-11-09 | 2003-08-05 | Guardian Industries, Corp. | Coated article with improved barrier layer structure and method of making the same |
US6830817B2 (en) | 2001-12-21 | 2004-12-14 | Guardian Industries Corp. | Low-e coating with high visible transmission |
MXPA04007578A (es) * | 2002-02-11 | 2004-11-10 | Ppg Ind Ohio Inc | Recubrimiento de control solar. |
US20030155065A1 (en) * | 2002-02-13 | 2003-08-21 | Thomsen Scott V. | Method of making window unit |
US6827977B2 (en) * | 2002-03-07 | 2004-12-07 | Guardian Industries Corp. | Method of making window unit including diamond-like carbon (DLC) coating |
US7231787B2 (en) * | 2002-03-20 | 2007-06-19 | Guardian Industries Corp. | Apparatus and method for bending and/or tempering glass |
US6983104B2 (en) * | 2002-03-20 | 2006-01-03 | Guardian Industries Corp. | Apparatus and method for bending and/or tempering glass |
EP1497235B1 (de) * | 2002-04-25 | 2017-12-27 | Vitro, S.A.B. de C.V. | Herstellungsverfahren für beschichtete artikel mit einer sauerstoff-barriere beschichtung und dadurch hergestellte beschichtete artikel |
AU2003239167B2 (en) * | 2002-04-25 | 2007-01-18 | Ppg Industries Ohio, Inc. | Coated articles having a protective coating and cathode targets for making the coated articles |
WO2003093188A1 (en) | 2002-05-03 | 2003-11-13 | Ppg Industries Ohio, Inc. | Substrate having thermal management coating for an insulating glass unit |
US6632491B1 (en) | 2002-05-21 | 2003-10-14 | Guardian Industries Corp. | IG window unit and method of making the same |
US7588829B2 (en) * | 2002-05-31 | 2009-09-15 | Ppg Industries Ohio, Inc. | Article having an aesthetic coating |
US7125462B2 (en) | 2002-06-18 | 2006-10-24 | Centre Luxembourgeois De Recherches Pour Le Verre Et Al Ceramique S.A. (C.R.V.C.) | Method of making vehicle windshield using coating mask |
US7140204B2 (en) * | 2002-06-28 | 2006-11-28 | Guardian Industries Corp. | Apparatus and method for bending glass using microwaves |
US20040112411A1 (en) * | 2002-09-10 | 2004-06-17 | Boykin Cheri M. | Method and apparatus for cleaning a photoactive and/or hydrophilic surface |
CA2499949C (en) * | 2002-09-27 | 2012-02-07 | Ppg Industries Ohio, Inc. | Method for producing float glass having reduced defect density |
US7005190B2 (en) * | 2002-12-20 | 2006-02-28 | Guardian Industries Corp. | Heat treatable coated article with reduced color shift at high viewing angles |
US6811884B2 (en) * | 2002-12-24 | 2004-11-02 | Ppg Industries Ohio, Inc. | Water repellant surface treatment and treated articles |
US20040202890A1 (en) * | 2003-04-08 | 2004-10-14 | Kutilek Luke A. | Methods of making crystalline titania coatings |
US6967060B2 (en) * | 2003-05-09 | 2005-11-22 | Guardian Industries Corp. | Coated article with niobium zirconium inclusive layer(s) and method of making same |
US7998602B2 (en) * | 2003-05-30 | 2011-08-16 | Ppg Industries Ohio, Inc. | Appliance with coated transparency |
WO2004108618A2 (en) * | 2003-05-30 | 2004-12-16 | Ppg Industries Ohio, Inc. | Appliance with coated transparency |
US7153579B2 (en) * | 2003-08-22 | 2006-12-26 | Centre Luxembourgeois de Recherches pour le Verre et la Ceramique S.A, (C.R.V.C.) | Heat treatable coated article with tin oxide inclusive layer between titanium oxide and silicon nitride |
US7087309B2 (en) * | 2003-08-22 | 2006-08-08 | Centre Luxembourgeois De Recherches Pour Le Verre Et La Ceramique S.A. (C.R.V.C.) | Coated article with tin oxide, silicon nitride and/or zinc oxide under IR reflecting layer and corresponding method |
US7060322B2 (en) * | 2003-09-02 | 2006-06-13 | Guardian Industries Corp. | Method of making heat treatable coated article with diamond-like carbon (DLC) coating |
US7507442B2 (en) * | 2003-11-04 | 2009-03-24 | Guardian Industries Corp. | Heat treatable coated article with diamond-like carbon (DLC) and/or zirconium in coating |
US20050208319A1 (en) * | 2004-03-22 | 2005-09-22 | Finley James J | Methods for forming an electrodeposited coating over a coated substrate and articles made thereby |
US20050238923A1 (en) * | 2004-04-27 | 2005-10-27 | Thiel James P | Hybrid coating stack |
US7223940B2 (en) * | 2005-02-22 | 2007-05-29 | Ppg Industries Ohio, Inc. | Heatable windshield |
KR101386806B1 (ko) * | 2005-05-12 | 2014-04-21 | 에이지씨 플랫 글래스 노스 아메리카, 인코퍼레이티드 | 저태양열 획득 계수, 향상된 화학적 및 기계적 특성을 갖는 저방사율 코팅 및 이의 제조 방법 |
US7335421B2 (en) * | 2005-07-20 | 2008-02-26 | Ppg Industries Ohio, Inc. | Heatable windshield |
US7572511B2 (en) * | 2005-10-11 | 2009-08-11 | Cardinal Cg Company | High infrared reflection coatings |
US7342716B2 (en) * | 2005-10-11 | 2008-03-11 | Cardinal Cg Company | Multiple cavity low-emissivity coatings |
US7339728B2 (en) * | 2005-10-11 | 2008-03-04 | Cardinal Cg Company | Low-emissivity coatings having high visible transmission and low solar heat gain coefficient |
US8025941B2 (en) * | 2005-12-01 | 2011-09-27 | Guardian Industries Corp. | IG window unit and method of making the same |
CA2636662C (en) * | 2006-01-17 | 2011-08-16 | Ppg Industries Ohio, Inc. | Method of producing particles by physical vapor deposition in an ionic liquid |
US20070264479A1 (en) * | 2006-05-09 | 2007-11-15 | Thiel James P | Aesthetic transparency |
US7767310B2 (en) * | 2006-10-23 | 2010-08-03 | Ppg Industries Ohio, Inc. | Primer composition and articles incorporating the primer |
CN101058486B (zh) * | 2007-04-26 | 2011-08-17 | 天津南玻工程玻璃有限公司 | 可热处理的磁控溅射方法制备的低辐射镀膜玻璃 |
US20080280147A1 (en) * | 2007-05-09 | 2008-11-13 | Thiel James P | Vehicle transparency |
US8686319B2 (en) * | 2007-05-09 | 2014-04-01 | Ppg Industries Ohio, Inc. | Vehicle transparency heated with alternating current |
US8728634B2 (en) * | 2007-06-13 | 2014-05-20 | Ppg Industries Ohio, Inc. | Appliance transparency |
US8658289B2 (en) * | 2007-11-16 | 2014-02-25 | Ppg Industries Ohio, Inc. | Electromagnetic radiation shielding device |
US7901781B2 (en) * | 2007-11-23 | 2011-03-08 | Agc Flat Glass North America, Inc. | Low emissivity coating with low solar heat gain coefficient, enhanced chemical and mechanical properties and method of making the same |
FR2927897B1 (fr) * | 2008-02-27 | 2011-04-01 | Saint Gobain | Vitrage antisolaire presentant un coefficient de transmission lumineuse ameliore. |
FR2928461B1 (fr) * | 2008-03-10 | 2011-04-01 | Saint Gobain | Substrat transparent comportant un revetement antireflet |
US8628820B2 (en) * | 2008-03-11 | 2014-01-14 | Ppg Industries Ohio, Inc. | Reflective article and method of making a reflective article |
US8085460B2 (en) * | 2008-08-28 | 2011-12-27 | Ppg Industries Ohio, Inc | Electrochromic device |
US8049949B2 (en) * | 2008-08-29 | 2011-11-01 | Ppg Industries Ohio, Inc. | Multi-layer electrode for high contrast electrochromic devices |
US7907322B2 (en) * | 2008-10-23 | 2011-03-15 | Ppg Industries Ohio, Inc. | Electrochromic device |
EP2429965B1 (de) * | 2009-05-08 | 2020-07-08 | Vitro Flat Glass LLC | Solarbeschichtung mit hohem sonnenwärmegewinnungskoeffizient |
CA2763423A1 (en) * | 2009-06-12 | 2010-12-16 | Ppg Industries Ohio, Inc. | Aircraft transparency with solar control properties |
CA2766133C (en) | 2009-07-21 | 2015-06-02 | Ppg Industries Ohio, Inc. | Enhanced bus bar system for aircraft transparencies |
US10654747B2 (en) | 2010-03-29 | 2020-05-19 | Vitro Flat Glass Llc | Solar control coatings with subcritical copper |
US9932267B2 (en) | 2010-03-29 | 2018-04-03 | Vitro, S.A.B. De C.V. | Solar control coatings with discontinuous metal layer |
US10654748B2 (en) | 2010-03-29 | 2020-05-19 | Vitro Flat Glass Llc | Solar control coatings providing increased absorption or tint |
US9397240B2 (en) | 2010-12-09 | 2016-07-19 | Ppg Industries Ohio, Inc. | Corrosion resistant solar mirror |
US9758426B2 (en) | 2011-06-29 | 2017-09-12 | Vitro, S.A.B. De C.V. | Reflective article having a sacrificial cathodic layer |
JP6121326B2 (ja) | 2011-08-10 | 2017-04-26 | 太陽誘電ケミカルテクノロジー株式会社 | プライマー薄膜を含む印刷用孔版及び該印刷用孔版の製造方法 |
US9919959B2 (en) | 2012-05-31 | 2018-03-20 | Guardian Glass, LLC | Window with UV-treated low-E coating and method of making same |
US9469565B2 (en) | 2012-05-31 | 2016-10-18 | Guardian Industries Corp. | Window with selectively writable image(s) and method of making same |
US20140113120A1 (en) | 2012-10-19 | 2014-04-24 | Ppg Industries Ohio, Inc. | Anti-color banding topcoat for coated articles |
US10871600B2 (en) | 2012-12-17 | 2020-12-22 | Guardian Glass, LLC | Window for reducing bird collisions |
JP2014167162A (ja) | 2013-01-31 | 2014-09-11 | Nitto Denko Corp | 赤外線反射フィルムの製造方法 |
JP2014167163A (ja) | 2013-01-31 | 2014-09-11 | Nitto Denko Corp | 赤外線反射フィルムの製造方法 |
US9873633B2 (en) * | 2013-11-20 | 2018-01-23 | Guardian Europe S.A.R.L. | Heat treatable coated article with low-E coating having zinc stannate based layer between IR reflecting layers and corresponding method |
JP6303559B2 (ja) * | 2014-02-07 | 2018-04-04 | 東レ株式会社 | 積層フィルムおよびその製造方法 |
US9650290B2 (en) | 2014-05-27 | 2017-05-16 | Centre Luxembourgeois De Recherches Pour Le Verre Et La Ceramique (C.R.V.C.) Sarl | IG window unit for preventing bird collisions |
JP6423198B2 (ja) | 2014-08-05 | 2018-11-14 | 日東電工株式会社 | 赤外線反射フィルム |
WO2016171779A1 (en) * | 2015-04-20 | 2016-10-27 | 3M Innovative Properties Company | Durable low emissivity window film constructions |
WO2017070769A1 (ru) * | 2015-10-29 | 2017-05-04 | ШИРИПОВ, Владимир Яковлевич | Комбинированное оптическое покрытие и способ его изготовления (варианты) |
WO2018181433A1 (ja) * | 2017-03-30 | 2018-10-04 | 日東電工株式会社 | 遮熱断熱基板 |
US11220455B2 (en) | 2017-08-04 | 2022-01-11 | Vitro Flat Glass Llc | Flash annealing of silver coatings |
US20190041550A1 (en) | 2017-08-04 | 2019-02-07 | Vitro Flat Glass Llc | Flash Annealing of Transparent Conductive Oxide and Semiconductor Coatings |
KR102455259B1 (ko) | 2017-09-18 | 2022-10-19 | 가디언 글라스, 엘엘씨 | 조류 충돌을 방지하기 위한 라미네이팅된 기판을 포함하는 ig 윈도우 유닛 |
EP3672803B1 (de) | 2017-09-29 | 2023-04-05 | NIKE Innovate C.V. | Strukturell gefärbte artikel und verfahren zur herstellung und verwendung von strukturell gefärbten artikeln |
US11078718B2 (en) | 2018-02-05 | 2021-08-03 | Vitro Flat Glass Llc | Solar control coatings with quadruple metallic layers |
JP2021513950A (ja) | 2018-02-15 | 2021-06-03 | ビトロ フラット グラス エルエルシー | 窒化ケイ素及び/又は酸窒化ケイ素を含む保護コーティングを有するコーティングされた物品 |
US10562812B2 (en) | 2018-06-12 | 2020-02-18 | Guardian Glass, LLC | Coated article having metamaterial-inclusive layer, coating having metamaterial-inclusive layer, and/or method of making the same |
US10830933B2 (en) | 2018-06-12 | 2020-11-10 | Guardian Glass, LLC | Matrix-embedded metamaterial coating, coated article having matrix-embedded metamaterial coating, and/or method of making the same |
US11329389B2 (en) * | 2018-07-26 | 2022-05-10 | Board Of Regents, The University Of Texas System | Method for fabricating a hyperbolic metamaterial having a near-zero refractive index in the optical regime |
US20210222486A1 (en) | 2018-08-15 | 2021-07-22 | Guardian Glass, LLC | Window unit with patterned coating for reducing bird collisions and method of making same |
EP3948372A1 (de) | 2019-03-28 | 2022-02-09 | Vitro Flat Glass LLC | Erwärmbare windschutzscheiben |
CN114008493A (zh) | 2019-06-26 | 2022-02-01 | 耐克创新有限合伙公司 | 结构着色的物品以及用于制造和使用结构着色的物品的方法 |
CN114206149A (zh) | 2019-07-26 | 2022-03-18 | 耐克创新有限合伙公司 | 结构着色的物品以及用于制造和使用结构着色的物品的方法 |
CN114173596A (zh) * | 2019-07-26 | 2022-03-11 | 耐克创新有限合伙公司 | 结构着色的物品以及用于制造和使用结构着色的物品的方法 |
KR20220134783A (ko) | 2020-02-14 | 2022-10-05 | 비트로 플랫 글래스 엘엘씨 | 저 시트 저항 코팅 |
US11859439B2 (en) | 2020-04-15 | 2024-01-02 | Vitro Flat Glass Llc | Low thermal conducting spacer assembly for an insulating glazing unit |
US11092726B1 (en) | 2020-06-19 | 2021-08-17 | Guardian Glass, LLC | Window unit having UV reflecting coating with high contrast ratio at large viewing angles for reducing bird collisions |
US11241062B1 (en) | 2020-08-07 | 2022-02-08 | Nike, Inc. | Footwear article having repurposed material with structural-color concealing layer |
US11129444B1 (en) | 2020-08-07 | 2021-09-28 | Nike, Inc. | Footwear article having repurposed material with concealing layer |
US11889894B2 (en) | 2020-08-07 | 2024-02-06 | Nike, Inc. | Footwear article having concealing layer |
WO2023064111A1 (en) | 2021-10-11 | 2023-04-20 | Vitro Flat Glass Llc | Heat-treatable coating having reduced haze |
US20230312407A1 (en) | 2022-03-31 | 2023-10-05 | Vitro Flat Glass Llc | Article Coated by a Multi-Layer Coating Stack |
WO2023239778A1 (en) | 2022-06-07 | 2023-12-14 | Vitro Flat Glass Llc | Asymmetric patterned reflective coating |
Family Cites Families (19)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
US4094763A (en) * | 1970-07-31 | 1978-06-13 | Ppg Industries, Inc. | Sputter coating of glass with an oxide of a metal having an atomic number between 48 and 51 and mixtures thereof |
US4166018A (en) * | 1974-01-31 | 1979-08-28 | Airco, Inc. | Sputtering process and apparatus |
US4349425A (en) * | 1977-09-09 | 1982-09-14 | Hitachi, Ltd. | Transparent conductive films and methods of producing same |
US4113599A (en) * | 1977-09-26 | 1978-09-12 | Ppg Industries, Inc. | Sputtering technique for the deposition of indium oxide |
US4201649A (en) * | 1978-11-29 | 1980-05-06 | Ppg Industries, Inc. | Low resistance indium oxide coatings |
DE2924833C3 (de) * | 1979-06-20 | 1982-05-19 | Bfg Glassgroup, Paris | Wärmereflexionsscheibe mit farbneutraler Außenansicht und deren Verwendung als Außenscheibe einer Mehrscheibenanordnung |
DE3160998D1 (en) * | 1980-03-10 | 1983-11-03 | Teijin Ltd | Selectively light-transmitting laminated structure |
DE3039821A1 (de) * | 1980-10-22 | 1982-06-03 | Robert Bosch Gmbh, 7000 Stuttgart | Mehrschichtsystem fuer waermeschutzanwendung |
DE3211753C2 (de) * | 1982-03-30 | 1985-03-28 | Interpane Entwicklungs- und Beratungsgesellschaft mbH & Co. KG, 3471 Lauenförde | Hochtransparenter, in Durch- als auch Außenansicht neutral wirkender und wärmedämmender Belag für ein Substrat aus transparentem Material sowie Verwendung des Belages |
JPS5931147A (ja) * | 1982-08-17 | 1984-02-20 | 株式会社豊田中央研究所 | 可視光透過性熱線しやへい膜およびその製造方法 |
NO157212C (no) * | 1982-09-21 | 1988-02-10 | Pilkington Brothers Plc | Fremgangsmaate for fremstilling av belegg med lav emisjonsevne. |
DE3307661A1 (de) * | 1983-03-04 | 1984-09-06 | Leybold-Heraeus GmbH, 5000 Köln | Verfahren zum herstellen von scheiben mit hohem transmissionsverhalten im sichtbaren spektralbereich und mit hohem reflexionsverhalten fuer waermestrahlung |
DE3316548C2 (de) * | 1983-03-25 | 1985-01-17 | Flachglas AG, 8510 Fürth | Verfahren zur Beschichtung eines transparenten Substrates |
US4610771A (en) * | 1984-10-29 | 1986-09-09 | Ppg Industries, Inc. | Sputtered films of metal alloy oxides and method of preparation thereof |
US4716086A (en) * | 1984-12-19 | 1987-12-29 | Ppg Industries, Inc. | Protective overcoat for low emissivity coated article |
DE3543178A1 (de) * | 1985-12-06 | 1987-06-11 | Leybold Heraeus Gmbh & Co Kg | Verfahren zum herstellen von scheiben mit hohem transmissionsverhalten im sichtbaren spektralbereich und mit hohem reflexionsverhalten fuer waermestrahlung sowie durch das verfahren hergestellte scheiben |
CA1331867C (en) * | 1986-12-29 | 1994-09-06 | James Joseph Finley | Low emissivity film for high temperature processing |
US4790922A (en) * | 1987-07-13 | 1988-12-13 | Viracon, Inc. | Temperable low emissivity and reflective windows |
JPS6474806A (en) * | 1987-09-17 | 1989-03-20 | Japan Radio Co Ltd | Slop array antenna |
-
1988
- 1988-04-01 US US07/176,511 patent/US4898790A/en not_active Expired - Lifetime
-
1989
- 1989-03-22 CA CA000594445A patent/CA1337483C/en not_active Expired - Lifetime
- 1989-03-28 EP EP89105417A patent/EP0335309B1/de not_active Expired - Lifetime
- 1989-03-28 ES ES89105417T patent/ES2056136T3/es not_active Expired - Lifetime
- 1989-03-28 DE DE68915042T patent/DE68915042T2/de not_active Expired - Lifetime
- 1989-03-31 KR KR1019890004197A patent/KR920005471B1/ko not_active IP Right Cessation
- 1989-03-31 JP JP1081347A patent/JP2505278B2/ja not_active Expired - Lifetime
- 1989-03-31 BR BR898901510A patent/BR8901510A/pt not_active IP Right Cessation
Also Published As
Publication number | Publication date |
---|---|
KR920005471B1 (ko) | 1992-07-04 |
JP2505278B2 (ja) | 1996-06-05 |
BR8901510A (pt) | 1989-11-14 |
JPH01301537A (ja) | 1989-12-05 |
US4898790A (en) | 1990-02-06 |
CA1337483C (en) | 1995-10-31 |
ES2056136T3 (es) | 1994-10-01 |
EP0335309B1 (de) | 1994-05-04 |
EP0335309A1 (de) | 1989-10-04 |
KR890015969A (ko) | 1989-11-27 |
DE68915042T2 (de) | 1994-11-17 |
Similar Documents
Publication | Publication Date | Title |
---|---|---|
DE68915042D1 (de) | Film mit geringerer Emission für Hochtemperaturbehandlung. | |
DE3881843D1 (de) | Orientierte polyaethylenfolie. | |
DE68923756D1 (de) | Abgedeckte Wärmebehandlung. | |
ES513069A0 (es) | Perfeccionamientos en lamparas quirurgicas. | |
FI891327A (fi) | Roerformig protes. | |
DE3587087T2 (de) | Roentgenstrahlenquelle mit hoher intensitaet. | |
DE68908470D1 (de) | Weiche waermeleistungsfaehige zuammensetzung. | |
DE68921124D1 (de) | Heizstreifen. | |
DE3850985T2 (de) | Polyesterfolie. | |
DE68911007D1 (de) | Kassette. | |
DE69021356T2 (de) | Beschlagfreier Film. | |
DE68921033D1 (de) | Belichtungsverfahren. | |
DE68911906T2 (de) | Lichtdichte kassette. | |
DE3886549D1 (de) | Niedrigtemperaturofen. | |
DE68906946T2 (de) | Leuchte. | |
DE3850382T2 (de) | Polyester-film. | |
DE3854633D1 (de) | Speiseschaltung. | |
DE68913289D1 (de) | Entseuchungsverfahren. | |
DE68919805T2 (de) | Wärmeintegrationsverfahren. | |
FI892761A (fi) | Expressionsvektorer foer framstaellning av ofusionerade proteiner i mikroorganismer. | |
DE3883747T2 (de) | Gelatinzusammensetzung. | |
DE69007412D1 (de) | Folienträger. | |
FI893784A0 (fi) | Med en diskontinuerlig film foersedda optiska minnesmedia. | |
FI893144A0 (fi) | Substituerade azacyklohexylderivat. | |
NO894505L (no) | Vandig cisplatinloesning. |
Legal Events
Date | Code | Title | Description |
---|---|---|---|
8364 | No opposition during term of opposition | ||
8327 | Change in the person/name/address of the patent owner |
Owner name: PPG INDUSTRIES OHIO, INC., CLEVELAND, OHIO, US |