DE68915042T2 - Film mit geringerer Emission für Hochtemperaturbehandlung. - Google Patents

Film mit geringerer Emission für Hochtemperaturbehandlung.

Info

Publication number
DE68915042T2
DE68915042T2 DE68915042T DE68915042T DE68915042T2 DE 68915042 T2 DE68915042 T2 DE 68915042T2 DE 68915042 T DE68915042 T DE 68915042T DE 68915042 T DE68915042 T DE 68915042T DE 68915042 T2 DE68915042 T2 DE 68915042T2
Authority
DE
Germany
Prior art keywords
high temperature
temperature treatment
emission film
lower emission
film
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Expired - Lifetime
Application number
DE68915042T
Other languages
English (en)
Other versions
DE68915042D1 (de
Inventor
James Joseph Finley
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
PPG Industries Ohio Inc
Original Assignee
PPG Industries Inc
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by PPG Industries Inc filed Critical PPG Industries Inc
Application granted granted Critical
Publication of DE68915042D1 publication Critical patent/DE68915042D1/de
Publication of DE68915042T2 publication Critical patent/DE68915042T2/de
Anticipated expiration legal-status Critical
Expired - Lifetime legal-status Critical Current

Links

Classifications

    • C—CHEMISTRY; METALLURGY
    • C03—GLASS; MINERAL OR SLAG WOOL
    • C03C—CHEMICAL COMPOSITION OF GLASSES, GLAZES OR VITREOUS ENAMELS; SURFACE TREATMENT OF GLASS; SURFACE TREATMENT OF FIBRES OR FILAMENTS MADE FROM GLASS, MINERALS OR SLAGS; JOINING GLASS TO GLASS OR OTHER MATERIALS
    • C03C17/00—Surface treatment of glass, not in the form of fibres or filaments, by coating
    • C03C17/06—Surface treatment of glass, not in the form of fibres or filaments, by coating with metals
    • C—CHEMISTRY; METALLURGY
    • C03—GLASS; MINERAL OR SLAG WOOL
    • C03C—CHEMICAL COMPOSITION OF GLASSES, GLAZES OR VITREOUS ENAMELS; SURFACE TREATMENT OF GLASS; SURFACE TREATMENT OF FIBRES OR FILAMENTS MADE FROM GLASS, MINERALS OR SLAGS; JOINING GLASS TO GLASS OR OTHER MATERIALS
    • C03C17/00—Surface treatment of glass, not in the form of fibres or filaments, by coating
    • C03C17/34—Surface treatment of glass, not in the form of fibres or filaments, by coating with at least two coatings having different compositions
    • C03C17/36—Surface treatment of glass, not in the form of fibres or filaments, by coating with at least two coatings having different compositions at least one coating being a metal
    • C03C17/3602—Surface treatment of glass, not in the form of fibres or filaments, by coating with at least two coatings having different compositions at least one coating being a metal the metal being present as a layer
    • C03C17/3618—Coatings of type glass/inorganic compound/other inorganic layers, at least one layer being metallic
    • C—CHEMISTRY; METALLURGY
    • C03—GLASS; MINERAL OR SLAG WOOL
    • C03C—CHEMICAL COMPOSITION OF GLASSES, GLAZES OR VITREOUS ENAMELS; SURFACE TREATMENT OF GLASS; SURFACE TREATMENT OF FIBRES OR FILAMENTS MADE FROM GLASS, MINERALS OR SLAGS; JOINING GLASS TO GLASS OR OTHER MATERIALS
    • C03C17/00—Surface treatment of glass, not in the form of fibres or filaments, by coating
    • C03C17/34—Surface treatment of glass, not in the form of fibres or filaments, by coating with at least two coatings having different compositions
    • C03C17/36—Surface treatment of glass, not in the form of fibres or filaments, by coating with at least two coatings having different compositions at least one coating being a metal
    • C—CHEMISTRY; METALLURGY
    • C03—GLASS; MINERAL OR SLAG WOOL
    • C03C—CHEMICAL COMPOSITION OF GLASSES, GLAZES OR VITREOUS ENAMELS; SURFACE TREATMENT OF GLASS; SURFACE TREATMENT OF FIBRES OR FILAMENTS MADE FROM GLASS, MINERALS OR SLAGS; JOINING GLASS TO GLASS OR OTHER MATERIALS
    • C03C17/00—Surface treatment of glass, not in the form of fibres or filaments, by coating
    • C03C17/34—Surface treatment of glass, not in the form of fibres or filaments, by coating with at least two coatings having different compositions
    • C03C17/36—Surface treatment of glass, not in the form of fibres or filaments, by coating with at least two coatings having different compositions at least one coating being a metal
    • C03C17/3602—Surface treatment of glass, not in the form of fibres or filaments, by coating with at least two coatings having different compositions at least one coating being a metal the metal being present as a layer
    • C03C17/3644—Surface treatment of glass, not in the form of fibres or filaments, by coating with at least two coatings having different compositions at least one coating being a metal the metal being present as a layer the metal being silver
    • C—CHEMISTRY; METALLURGY
    • C03—GLASS; MINERAL OR SLAG WOOL
    • C03C—CHEMICAL COMPOSITION OF GLASSES, GLAZES OR VITREOUS ENAMELS; SURFACE TREATMENT OF GLASS; SURFACE TREATMENT OF FIBRES OR FILAMENTS MADE FROM GLASS, MINERALS OR SLAGS; JOINING GLASS TO GLASS OR OTHER MATERIALS
    • C03C17/00—Surface treatment of glass, not in the form of fibres or filaments, by coating
    • C03C17/34—Surface treatment of glass, not in the form of fibres or filaments, by coating with at least two coatings having different compositions
    • C03C17/36—Surface treatment of glass, not in the form of fibres or filaments, by coating with at least two coatings having different compositions at least one coating being a metal
    • C03C17/3602—Surface treatment of glass, not in the form of fibres or filaments, by coating with at least two coatings having different compositions at least one coating being a metal the metal being present as a layer
    • C03C17/3652—Surface treatment of glass, not in the form of fibres or filaments, by coating with at least two coatings having different compositions at least one coating being a metal the metal being present as a layer the coating stack containing at least one sacrificial layer to protect the metal from oxidation
    • C—CHEMISTRY; METALLURGY
    • C03—GLASS; MINERAL OR SLAG WOOL
    • C03C—CHEMICAL COMPOSITION OF GLASSES, GLAZES OR VITREOUS ENAMELS; SURFACE TREATMENT OF GLASS; SURFACE TREATMENT OF FIBRES OR FILAMENTS MADE FROM GLASS, MINERALS OR SLAGS; JOINING GLASS TO GLASS OR OTHER MATERIALS
    • C03C17/00—Surface treatment of glass, not in the form of fibres or filaments, by coating
    • C03C17/34—Surface treatment of glass, not in the form of fibres or filaments, by coating with at least two coatings having different compositions
    • C03C17/36—Surface treatment of glass, not in the form of fibres or filaments, by coating with at least two coatings having different compositions at least one coating being a metal
    • C03C17/3602—Surface treatment of glass, not in the form of fibres or filaments, by coating with at least two coatings having different compositions at least one coating being a metal the metal being present as a layer
    • C03C17/3657—Surface treatment of glass, not in the form of fibres or filaments, by coating with at least two coatings having different compositions at least one coating being a metal the metal being present as a layer the multilayer coating having optical properties
    • C03C17/366—Low-emissivity or solar control coatings
    • C—CHEMISTRY; METALLURGY
    • C03—GLASS; MINERAL OR SLAG WOOL
    • C03C—CHEMICAL COMPOSITION OF GLASSES, GLAZES OR VITREOUS ENAMELS; SURFACE TREATMENT OF GLASS; SURFACE TREATMENT OF FIBRES OR FILAMENTS MADE FROM GLASS, MINERALS OR SLAGS; JOINING GLASS TO GLASS OR OTHER MATERIALS
    • C03C17/00—Surface treatment of glass, not in the form of fibres or filaments, by coating
    • C03C17/34—Surface treatment of glass, not in the form of fibres or filaments, by coating with at least two coatings having different compositions
    • C03C17/36—Surface treatment of glass, not in the form of fibres or filaments, by coating with at least two coatings having different compositions at least one coating being a metal
    • C03C17/3602—Surface treatment of glass, not in the form of fibres or filaments, by coating with at least two coatings having different compositions at least one coating being a metal the metal being present as a layer
    • C03C17/3681—Surface treatment of glass, not in the form of fibres or filaments, by coating with at least two coatings having different compositions at least one coating being a metal the metal being present as a layer the multilayer coating being used in glazing, e.g. windows or windscreens
    • C—CHEMISTRY; METALLURGY
    • C03—GLASS; MINERAL OR SLAG WOOL
    • C03C—CHEMICAL COMPOSITION OF GLASSES, GLAZES OR VITREOUS ENAMELS; SURFACE TREATMENT OF GLASS; SURFACE TREATMENT OF FIBRES OR FILAMENTS MADE FROM GLASS, MINERALS OR SLAGS; JOINING GLASS TO GLASS OR OTHER MATERIALS
    • C03C17/00—Surface treatment of glass, not in the form of fibres or filaments, by coating
    • C03C17/34—Surface treatment of glass, not in the form of fibres or filaments, by coating with at least two coatings having different compositions
    • C03C17/36—Surface treatment of glass, not in the form of fibres or filaments, by coating with at least two coatings having different compositions at least one coating being a metal
    • C03C17/3602—Surface treatment of glass, not in the form of fibres or filaments, by coating with at least two coatings having different compositions at least one coating being a metal the metal being present as a layer
    • C03C17/3689—Surface treatment of glass, not in the form of fibres or filaments, by coating with at least two coatings having different compositions at least one coating being a metal the metal being present as a layer one oxide layer being obtained by oxidation of a metallic layer
    • G—PHYSICS
    • G02—OPTICS
    • G02B—OPTICAL ELEMENTS, SYSTEMS OR APPARATUS
    • G02B1/00—Optical elements characterised by the material of which they are made; Optical coatings for optical elements
    • G02B1/10—Optical coatings produced by application to, or surface treatment of, optical elements
    • G—PHYSICS
    • G02—OPTICS
    • G02B—OPTICAL ELEMENTS, SYSTEMS OR APPARATUS
    • G02B1/00—Optical elements characterised by the material of which they are made; Optical coatings for optical elements
    • G02B1/10—Optical coatings produced by application to, or surface treatment of, optical elements
    • G02B1/11—Anti-reflection coatings
    • G02B1/113—Anti-reflection coatings using inorganic layer materials only
    • G02B1/115—Multilayers
    • G02B1/116—Multilayers including electrically conducting layers
    • G—PHYSICS
    • G02—OPTICS
    • G02B—OPTICAL ELEMENTS, SYSTEMS OR APPARATUS
    • G02B5/00—Optical elements other than lenses
    • G02B5/20—Filters
    • G02B5/208—Filters for use with infrared or ultraviolet radiation, e.g. for separating visible light from infrared and/or ultraviolet radiation
    • C—CHEMISTRY; METALLURGY
    • C03—GLASS; MINERAL OR SLAG WOOL
    • C03C—CHEMICAL COMPOSITION OF GLASSES, GLAZES OR VITREOUS ENAMELS; SURFACE TREATMENT OF GLASS; SURFACE TREATMENT OF FIBRES OR FILAMENTS MADE FROM GLASS, MINERALS OR SLAGS; JOINING GLASS TO GLASS OR OTHER MATERIALS
    • C03C2217/00—Coatings on glass
    • C03C2217/70—Properties of coatings
    • C03C2217/78—Coatings specially designed to be durable, e.g. scratch-resistant
    • Y—GENERAL TAGGING OF NEW TECHNOLOGICAL DEVELOPMENTS; GENERAL TAGGING OF CROSS-SECTIONAL TECHNOLOGIES SPANNING OVER SEVERAL SECTIONS OF THE IPC; TECHNICAL SUBJECTS COVERED BY FORMER USPC CROSS-REFERENCE ART COLLECTIONS [XRACs] AND DIGESTS
    • Y10—TECHNICAL SUBJECTS COVERED BY FORMER USPC
    • Y10T—TECHNICAL SUBJECTS COVERED BY FORMER US CLASSIFICATION
    • Y10T428/00—Stock material or miscellaneous articles
    • Y10T428/12—All metal or with adjacent metals
    • Y10T428/12493—Composite; i.e., plural, adjacent, spatially distinct metal components [e.g., layers, joint, etc.]
    • Y10T428/12535—Composite; i.e., plural, adjacent, spatially distinct metal components [e.g., layers, joint, etc.] with additional, spatially distinct nonmetal component
    • Y10T428/12542—More than one such component
    • Y10T428/12549—Adjacent to each other
    • Y—GENERAL TAGGING OF NEW TECHNOLOGICAL DEVELOPMENTS; GENERAL TAGGING OF CROSS-SECTIONAL TECHNOLOGIES SPANNING OVER SEVERAL SECTIONS OF THE IPC; TECHNICAL SUBJECTS COVERED BY FORMER USPC CROSS-REFERENCE ART COLLECTIONS [XRACs] AND DIGESTS
    • Y10—TECHNICAL SUBJECTS COVERED BY FORMER USPC
    • Y10T—TECHNICAL SUBJECTS COVERED BY FORMER US CLASSIFICATION
    • Y10T428/00—Stock material or miscellaneous articles
    • Y10T428/12—All metal or with adjacent metals
    • Y10T428/12493—Composite; i.e., plural, adjacent, spatially distinct metal components [e.g., layers, joint, etc.]
    • Y10T428/12535—Composite; i.e., plural, adjacent, spatially distinct metal components [e.g., layers, joint, etc.] with additional, spatially distinct nonmetal component
    • Y10T428/12611—Oxide-containing component
    • Y—GENERAL TAGGING OF NEW TECHNOLOGICAL DEVELOPMENTS; GENERAL TAGGING OF CROSS-SECTIONAL TECHNOLOGIES SPANNING OVER SEVERAL SECTIONS OF THE IPC; TECHNICAL SUBJECTS COVERED BY FORMER USPC CROSS-REFERENCE ART COLLECTIONS [XRACs] AND DIGESTS
    • Y10—TECHNICAL SUBJECTS COVERED BY FORMER USPC
    • Y10T—TECHNICAL SUBJECTS COVERED BY FORMER US CLASSIFICATION
    • Y10T428/00—Stock material or miscellaneous articles
    • Y10T428/12—All metal or with adjacent metals
    • Y10T428/12493—Composite; i.e., plural, adjacent, spatially distinct metal components [e.g., layers, joint, etc.]
    • Y10T428/12771—Transition metal-base component
    • Y10T428/12806—Refractory [Group IVB, VB, or VIB] metal-base component
    • Y—GENERAL TAGGING OF NEW TECHNOLOGICAL DEVELOPMENTS; GENERAL TAGGING OF CROSS-SECTIONAL TECHNOLOGIES SPANNING OVER SEVERAL SECTIONS OF THE IPC; TECHNICAL SUBJECTS COVERED BY FORMER USPC CROSS-REFERENCE ART COLLECTIONS [XRACs] AND DIGESTS
    • Y10—TECHNICAL SUBJECTS COVERED BY FORMER USPC
    • Y10T—TECHNICAL SUBJECTS COVERED BY FORMER US CLASSIFICATION
    • Y10T428/00—Stock material or miscellaneous articles
    • Y10T428/12—All metal or with adjacent metals
    • Y10T428/12493—Composite; i.e., plural, adjacent, spatially distinct metal components [e.g., layers, joint, etc.]
    • Y10T428/12771—Transition metal-base component
    • Y10T428/12861—Group VIII or IB metal-base component
    • Y10T428/12896—Ag-base component
DE68915042T 1988-04-01 1989-03-28 Film mit geringerer Emission für Hochtemperaturbehandlung. Expired - Lifetime DE68915042T2 (de)

Applications Claiming Priority (1)

Application Number Priority Date Filing Date Title
US07/176,511 US4898790A (en) 1986-12-29 1988-04-01 Low emissivity film for high temperature processing

Publications (2)

Publication Number Publication Date
DE68915042D1 DE68915042D1 (de) 1994-06-09
DE68915042T2 true DE68915042T2 (de) 1994-11-17

Family

ID=22644647

Family Applications (1)

Application Number Title Priority Date Filing Date
DE68915042T Expired - Lifetime DE68915042T2 (de) 1988-04-01 1989-03-28 Film mit geringerer Emission für Hochtemperaturbehandlung.

Country Status (8)

Country Link
US (1) US4898790A (de)
EP (1) EP0335309B1 (de)
JP (1) JP2505278B2 (de)
KR (1) KR920005471B1 (de)
BR (1) BR8901510A (de)
CA (1) CA1337483C (de)
DE (1) DE68915042T2 (de)
ES (1) ES2056136T3 (de)

Families Citing this family (143)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US5112693A (en) * 1988-10-03 1992-05-12 Ppg Industries, Inc. Low reflectance, highly saturated colored coating for monolithic glazing
US5153062A (en) * 1989-02-13 1992-10-06 Hoechst Aktiengesellschaft Process and device for producing laminated safety glass and laminated safety glass produced thereby
US5215832A (en) * 1990-04-25 1993-06-01 Cardinal Ic Company Lead-free mirrors and environmentally safe manufacture thereof
US5296302A (en) * 1992-03-27 1994-03-22 Cardinal Ig Company Abrasion-resistant overcoat for coated substrates
US5972527A (en) * 1992-12-15 1999-10-26 Idemitsu Kosan Co., Ltd. Transparent electrically conductive layer, electrically conductive transparent substrate and electrically conductive material
DE69428253T2 (de) 1993-11-12 2002-06-27 Ppg Ind Ohio Inc Haltbare Sputterschicht aus Metalloxid
DE4409934A1 (de) * 1994-03-23 1995-09-28 Ver Glaswerke Gmbh Verfahren und Vorrichtung zum Beschichten einer Glasscheibe mit wenigstens einer Schicht aus Zinndioxid durch reaktive Katodenzerstäubung
CA2161283A1 (en) 1994-12-27 1996-06-28 Ppg Industries Ohio, Inc. Annealed low emissivity coating
US6086210A (en) * 1995-06-29 2000-07-11 Cardinal Ig Company Bendable mirrors and method of manufacture
US6142642A (en) * 1995-06-29 2000-11-07 Cardinal Ig Company Bendable mirrors and method of manufacture
US5821001A (en) * 1996-04-25 1998-10-13 Ppg Industries, Inc. Coated articles
US20020155299A1 (en) 1997-03-14 2002-10-24 Harris Caroline S. Photo-induced hydrophilic article and method of making same
US7096692B2 (en) * 1997-03-14 2006-08-29 Ppg Industries Ohio, Inc. Visible-light-responsive photoactive coating, coated article, and method of making same
US20030039843A1 (en) * 1997-03-14 2003-02-27 Christopher Johnson Photoactive coating, coated article, and method of making same
US20050096288A1 (en) * 1997-06-13 2005-05-05 Aragene, Inc. Lipoproteins as nucleic acid vectors
DE69804866T9 (de) 1997-10-31 2007-10-31 Cardinal Cg Co., Eden Prairie Hitzebiegbare spiegel
US6833194B1 (en) 1998-05-12 2004-12-21 Ppg Industries Ohio, Inc. Protective layers for sputter coated article
US6899953B1 (en) 1998-05-08 2005-05-31 Ppg Industries Ohio, Inc. Shippable heat-treatable sputter coated article and zinc cathode sputtering target containing low amounts of tin
EP1154963B1 (de) 1998-12-18 2004-09-01 Glaverbel Verglasungsscheibe
US6610410B2 (en) 1998-12-18 2003-08-26 Asahi Glass Company, Limited Glazing panel
US6582799B1 (en) 1999-06-02 2003-06-24 Ppg Industries Ohio, Inc. Laminated transparency
US6849328B1 (en) 1999-07-02 2005-02-01 Ppg Industries Ohio, Inc. Light-transmitting and/or coated article with removable protective coating and methods of making the same
US20020136905A1 (en) * 1999-11-24 2002-09-26 Medwick Paul A. Low shading coefficient and low emissivity coatings and coated articles
CA2390404A1 (en) 1999-11-24 2001-05-31 Ppg Industries Ohio, Inc. Low shading coefficient and low emissivity coatings and coated articles
US20070036989A1 (en) * 1999-11-24 2007-02-15 Ppg Industries Ohio, Inc. Low shading coefficient and low emissivity coatings and coated articles
US6495263B2 (en) 1999-12-06 2002-12-17 Guardian Industries Corp. Low-E matchable coated articles and methods of making same
US6475626B1 (en) 1999-12-06 2002-11-05 Guardian Industries Corp. Low-E matchable coated articles and methods of making same
US6514620B1 (en) 1999-12-06 2003-02-04 Guardian Industries Corp. Matchable low-E I G units and laminates and methods of making same
US7361404B2 (en) 2000-05-10 2008-04-22 Ppg Industries Ohio, Inc. Coated article with removable protective coating and related methods
US7267879B2 (en) 2001-02-28 2007-09-11 Guardian Industries Corp. Coated article with silicon oxynitride adjacent glass
US6887575B2 (en) * 2001-10-17 2005-05-03 Guardian Industries Corp. Heat treatable coated article with zinc oxide inclusive contact layer(s)
US6576349B2 (en) 2000-07-10 2003-06-10 Guardian Industries Corp. Heat treatable low-E coated articles and methods of making same
US6445503B1 (en) 2000-07-10 2002-09-03 Guardian Industries Corp. High durable, low-E, heat treatable layer coating system
US7462397B2 (en) * 2000-07-10 2008-12-09 Guardian Industries Corp. Coated article with silicon nitride inclusive layer adjacent glass
US6677063B2 (en) 2000-08-31 2004-01-13 Ppg Industries Ohio, Inc. Methods of obtaining photoactive coatings and/or anatase crystalline phase of titanium oxides and articles made thereby
US7323249B2 (en) * 2000-08-31 2008-01-29 Ppg Industries Ohio, Inc. Methods of obtaining photoactive coatings and/or anatase crystalline phase of titanium oxides and articles made thereby
US20020172775A1 (en) * 2000-10-24 2002-11-21 Harry Buhay Method of making coated articles and coated articles made thereby
US7311961B2 (en) * 2000-10-24 2007-12-25 Ppg Industries Ohio, Inc. Method of making coated articles and coated articles made thereby
US6869644B2 (en) * 2000-10-24 2005-03-22 Ppg Industries Ohio, Inc. Method of making coated articles and coated articles made thereby
DE10063180A1 (de) * 2000-12-18 2002-06-27 Bayer Ag Vorrichtung zur Erzeugung von Lichtsignalen
US20020120916A1 (en) * 2001-01-16 2002-08-29 Snider Albert Monroe Head-up display system utilizing fluorescent material
CN1501892A (zh) * 2001-03-20 2004-06-02 PPG��ҵ����˾ 形成压花和/或花纹玻璃的方法和设备及由其形成的玻璃制品
US20030049464A1 (en) 2001-09-04 2003-03-13 Afg Industries, Inc. Double silver low-emissivity and solar control coatings
US6942923B2 (en) 2001-12-21 2005-09-13 Guardian Industries Corp. Low-e coating with high visible transmission
US7232615B2 (en) * 2001-10-22 2007-06-19 Ppg Industries Ohio, Inc. Coating stack comprising a layer of barrier coating
US6730389B2 (en) 2001-10-25 2004-05-04 Ppg Industries Ohio, Inc. Coated substrate having a frequency selective surface
US6602608B2 (en) * 2001-11-09 2003-08-05 Guardian Industries, Corp. Coated article with improved barrier layer structure and method of making the same
US6830817B2 (en) * 2001-12-21 2004-12-14 Guardian Industries Corp. Low-e coating with high visible transmission
JP4949609B2 (ja) * 2002-02-11 2012-06-13 ピーピージー・インダストリーズ・オハイオ・インコーポレイテッド 日射コントロール被覆
US20030155065A1 (en) * 2002-02-13 2003-08-21 Thomsen Scott V. Method of making window unit
US6827977B2 (en) * 2002-03-07 2004-12-07 Guardian Industries Corp. Method of making window unit including diamond-like carbon (DLC) coating
US7231787B2 (en) * 2002-03-20 2007-06-19 Guardian Industries Corp. Apparatus and method for bending and/or tempering glass
US6983104B2 (en) * 2002-03-20 2006-01-03 Guardian Industries Corp. Apparatus and method for bending and/or tempering glass
EP1509481B1 (de) * 2002-04-25 2017-04-12 Vitro, S.A.B. de C.V. Beschichtete artikel mit einer schutzschicht
CZ307527B6 (cs) * 2002-04-25 2018-11-14 Vitro, S.A.B. De C.V. Výrobek s povlakovým souvrstvím obsahujícím bariérový povlak a způsob výroby tohoto výrobku
CA2484181C (en) 2002-05-03 2010-02-23 Ppg Industries Ohio, Inc. Substrate having thermal management coating for an insulating glass unit
US6632491B1 (en) 2002-05-21 2003-10-14 Guardian Industries Corp. IG window unit and method of making the same
US7588829B2 (en) * 2002-05-31 2009-09-15 Ppg Industries Ohio, Inc. Article having an aesthetic coating
US7125462B2 (en) 2002-06-18 2006-10-24 Centre Luxembourgeois De Recherches Pour Le Verre Et Al Ceramique S.A. (C.R.V.C.) Method of making vehicle windshield using coating mask
US7140204B2 (en) * 2002-06-28 2006-11-28 Guardian Industries Corp. Apparatus and method for bending glass using microwaves
US20040112411A1 (en) * 2002-09-10 2004-06-17 Boykin Cheri M. Method and apparatus for cleaning a photoactive and/or hydrophilic surface
CA2499949C (en) * 2002-09-27 2012-02-07 Ppg Industries Ohio, Inc. Method for producing float glass having reduced defect density
US7005190B2 (en) * 2002-12-20 2006-02-28 Guardian Industries Corp. Heat treatable coated article with reduced color shift at high viewing angles
US6811884B2 (en) * 2002-12-24 2004-11-02 Ppg Industries Ohio, Inc. Water repellant surface treatment and treated articles
US20040202890A1 (en) * 2003-04-08 2004-10-14 Kutilek Luke A. Methods of making crystalline titania coatings
US6967060B2 (en) * 2003-05-09 2005-11-22 Guardian Industries Corp. Coated article with niobium zirconium inclusive layer(s) and method of making same
WO2004108618A2 (en) * 2003-05-30 2004-12-16 Ppg Industries Ohio, Inc. Appliance with coated transparency
US7998602B2 (en) * 2003-05-30 2011-08-16 Ppg Industries Ohio, Inc. Appliance with coated transparency
US7153579B2 (en) * 2003-08-22 2006-12-26 Centre Luxembourgeois de Recherches pour le Verre et la Ceramique S.A, (C.R.V.C.) Heat treatable coated article with tin oxide inclusive layer between titanium oxide and silicon nitride
US7087309B2 (en) * 2003-08-22 2006-08-08 Centre Luxembourgeois De Recherches Pour Le Verre Et La Ceramique S.A. (C.R.V.C.) Coated article with tin oxide, silicon nitride and/or zinc oxide under IR reflecting layer and corresponding method
US7060322B2 (en) * 2003-09-02 2006-06-13 Guardian Industries Corp. Method of making heat treatable coated article with diamond-like carbon (DLC) coating
US7507442B2 (en) * 2003-11-04 2009-03-24 Guardian Industries Corp. Heat treatable coated article with diamond-like carbon (DLC) and/or zirconium in coating
US20050208319A1 (en) * 2004-03-22 2005-09-22 Finley James J Methods for forming an electrodeposited coating over a coated substrate and articles made thereby
US20050238923A1 (en) * 2004-04-27 2005-10-27 Thiel James P Hybrid coating stack
US7223940B2 (en) * 2005-02-22 2007-05-29 Ppg Industries Ohio, Inc. Heatable windshield
KR101386806B1 (ko) * 2005-05-12 2014-04-21 에이지씨 플랫 글래스 노스 아메리카, 인코퍼레이티드 저태양열 획득 계수, 향상된 화학적 및 기계적 특성을 갖는 저방사율 코팅 및 이의 제조 방법
US7335421B2 (en) * 2005-07-20 2008-02-26 Ppg Industries Ohio, Inc. Heatable windshield
US7572511B2 (en) * 2005-10-11 2009-08-11 Cardinal Cg Company High infrared reflection coatings
US7339728B2 (en) * 2005-10-11 2008-03-04 Cardinal Cg Company Low-emissivity coatings having high visible transmission and low solar heat gain coefficient
US7342716B2 (en) 2005-10-11 2008-03-11 Cardinal Cg Company Multiple cavity low-emissivity coatings
US8025941B2 (en) * 2005-12-01 2011-09-27 Guardian Industries Corp. IG window unit and method of making the same
RU2404024C2 (ru) * 2006-01-17 2010-11-20 Ппг Индастриз Огайо, Инк. Способ получения частиц физическим осаждением из паровой фазы в ионной жидкости
US20070264479A1 (en) * 2006-05-09 2007-11-15 Thiel James P Aesthetic transparency
US7767310B2 (en) * 2006-10-23 2010-08-03 Ppg Industries Ohio, Inc. Primer composition and articles incorporating the primer
CN101058486B (zh) * 2007-04-26 2011-08-17 天津南玻工程玻璃有限公司 可热处理的磁控溅射方法制备的低辐射镀膜玻璃
US8686319B2 (en) * 2007-05-09 2014-04-01 Ppg Industries Ohio, Inc. Vehicle transparency heated with alternating current
US20080280147A1 (en) * 2007-05-09 2008-11-13 Thiel James P Vehicle transparency
US8728634B2 (en) * 2007-06-13 2014-05-20 Ppg Industries Ohio, Inc. Appliance transparency
US8658289B2 (en) * 2007-11-16 2014-02-25 Ppg Industries Ohio, Inc. Electromagnetic radiation shielding device
US7901781B2 (en) * 2007-11-23 2011-03-08 Agc Flat Glass North America, Inc. Low emissivity coating with low solar heat gain coefficient, enhanced chemical and mechanical properties and method of making the same
FR2927897B1 (fr) * 2008-02-27 2011-04-01 Saint Gobain Vitrage antisolaire presentant un coefficient de transmission lumineuse ameliore.
FR2928461B1 (fr) * 2008-03-10 2011-04-01 Saint Gobain Substrat transparent comportant un revetement antireflet
US8497015B2 (en) * 2008-03-11 2013-07-30 Ppg Industries Ohio, Inc. Reflective article
US8085460B2 (en) * 2008-08-28 2011-12-27 Ppg Industries Ohio, Inc Electrochromic device
US8049949B2 (en) * 2008-08-29 2011-11-01 Ppg Industries Ohio, Inc. Multi-layer electrode for high contrast electrochromic devices
US7907322B2 (en) * 2008-10-23 2011-03-15 Ppg Industries Ohio, Inc. Electrochromic device
CN102438961A (zh) * 2009-05-08 2012-05-02 Ppg工业俄亥俄公司 具有高的阳光得热系数的阳光控制涂层
EP2440403B1 (de) * 2009-06-12 2020-03-11 PPG Industries Ohio, Inc. Flugzeugtransparenzsystem mit sonnensteuerungsfunktion
WO2011011357A1 (en) 2009-07-21 2011-01-27 Ppg Industries Ohio, Inc. Enhanced bus bar system for aircraft transparencies
US10654747B2 (en) 2010-03-29 2020-05-19 Vitro Flat Glass Llc Solar control coatings with subcritical copper
US10654748B2 (en) 2010-03-29 2020-05-19 Vitro Flat Glass Llc Solar control coatings providing increased absorption or tint
US9932267B2 (en) 2010-03-29 2018-04-03 Vitro, S.A.B. De C.V. Solar control coatings with discontinuous metal layer
US9397240B2 (en) 2010-12-09 2016-07-19 Ppg Industries Ohio, Inc. Corrosion resistant solar mirror
US9758426B2 (en) 2011-06-29 2017-09-12 Vitro, S.A.B. De C.V. Reflective article having a sacrificial cathodic layer
CN103717403B (zh) 2011-08-10 2016-08-31 太阳诱电化学科技株式会社 包含薄底漆膜的结构体和包含薄底漆膜的镂空版印刷版
US9469565B2 (en) 2012-05-31 2016-10-18 Guardian Industries Corp. Window with selectively writable image(s) and method of making same
US9919959B2 (en) 2012-05-31 2018-03-20 Guardian Glass, LLC Window with UV-treated low-E coating and method of making same
US20140113120A1 (en) 2012-10-19 2014-04-24 Ppg Industries Ohio, Inc. Anti-color banding topcoat for coated articles
US10871600B2 (en) 2012-12-17 2020-12-22 Guardian Glass, LLC Window for reducing bird collisions
JP2014167163A (ja) 2013-01-31 2014-09-11 Nitto Denko Corp 赤外線反射フィルムの製造方法
JP2014167162A (ja) 2013-01-31 2014-09-11 Nitto Denko Corp 赤外線反射フィルムの製造方法
US9873633B2 (en) 2013-11-20 2018-01-23 Guardian Europe S.A.R.L. Heat treatable coated article with low-E coating having zinc stannate based layer between IR reflecting layers and corresponding method
JP6303559B2 (ja) * 2014-02-07 2018-04-04 東レ株式会社 積層フィルムおよびその製造方法
US9650290B2 (en) 2014-05-27 2017-05-16 Centre Luxembourgeois De Recherches Pour Le Verre Et La Ceramique (C.R.V.C.) Sarl IG window unit for preventing bird collisions
JP6423198B2 (ja) 2014-08-05 2018-11-14 日東電工株式会社 赤外線反射フィルム
WO2016171779A1 (en) * 2015-04-20 2016-10-27 3M Innovative Properties Company Durable low emissivity window film constructions
CN108349792A (zh) * 2015-10-29 2018-07-31 伊扎维克技术有限责任公司 复合光学涂层及其制造方法（变型）
WO2018181433A1 (ja) * 2017-03-30 2018-10-04 日東電工株式会社 遮熱断熱基板
US20190041550A1 (en) 2017-08-04 2019-02-07 Vitro Flat Glass Llc Flash Annealing of Transparent Conductive Oxide and Semiconductor Coatings
US11220455B2 (en) 2017-08-04 2022-01-11 Vitro Flat Glass Llc Flash annealing of silver coatings
EP3684613A1 (de) 2017-09-18 2020-07-29 Guardian Glass, LLC Ig-fenstereinheit mit laminierten substraten zur verhinderung von vogelkollisionen
EP3638507B1 (de) 2017-09-29 2021-01-06 NIKE Innovate C.V. Verfahren zur herstellung und verwendung von strukturgefärbten artikeln
US11078718B2 (en) 2018-02-05 2021-08-03 Vitro Flat Glass Llc Solar control coatings with quadruple metallic layers
US10479724B2 (en) 2018-02-15 2019-11-19 Vitro Flat Glass Llc Coated article having a protective coating containing silicon nitride and/or silicon oxynitride
US10562812B2 (en) 2018-06-12 2020-02-18 Guardian Glass, LLC Coated article having metamaterial-inclusive layer, coating having metamaterial-inclusive layer, and/or method of making the same
US10830933B2 (en) 2018-06-12 2020-11-10 Guardian Glass, LLC Matrix-embedded metamaterial coating, coated article having matrix-embedded metamaterial coating, and/or method of making the same
US11329389B2 (en) * 2018-07-26 2022-05-10 Board Of Regents, The University Of Texas System Method for fabricating a hyperbolic metamaterial having a near-zero refractive index in the optical regime
BR112020025651A2 (pt) 2018-08-15 2021-04-06 Guardian Glass, LLC Unidade de janela com revestimento padronizado para reduzir colisão de pássaro e método para produzir a mesma
MX2021011429A (es) 2019-03-28 2021-10-13 Vitro Flat Glass Llc Articulo que tiene un alto reflejo de luz visible y un color neutro.
CN114008493A (zh) 2019-06-26 2022-02-01 耐克创新有限合伙公司 结构着色的物品以及用于制造和使用结构着色的物品的方法
WO2021021562A1 (en) 2019-07-26 2021-02-04 Nike, Inc. Structurally-colored articles and methods for making and using structurally-colored articles
US20210026055A1 (en) * 2019-07-26 2021-01-28 Nike, Inc. Structurally-colored articles and methods for making and using structurally-colored articles
US20210274657A1 (en) 2020-02-14 2021-09-02 Vitro Flat Glass Llc Low Sheet Resistance Coating
US11859439B2 (en) 2020-04-15 2024-01-02 Vitro Flat Glass Llc Low thermal conducting spacer assembly for an insulating glazing unit
US11092726B1 (en) 2020-06-19 2021-08-17 Guardian Glass, LLC Window unit having UV reflecting coating with high contrast ratio at large viewing angles for reducing bird collisions
US11889894B2 (en) 2020-08-07 2024-02-06 Nike, Inc. Footwear article having concealing layer
US11241062B1 (en) 2020-08-07 2022-02-08 Nike, Inc. Footwear article having repurposed material with structural-color concealing layer
US11129444B1 (en) 2020-08-07 2021-09-28 Nike, Inc. Footwear article having repurposed material with concealing layer
WO2023064111A1 (en) 2021-10-11 2023-04-20 Vitro Flat Glass Llc Heat-treatable coating having reduced haze
WO2023192460A1 (en) 2022-03-31 2023-10-05 Vitro Flat Glass Llc Article coated by a multi-layer coating stack
WO2023239778A1 (en) 2022-06-07 2023-12-14 Vitro Flat Glass Llc Asymmetric patterned reflective coating
WO2024059091A1 (en) 2022-09-14 2024-03-21 Vitro Flat Glass Llc Magnetron sputtering vapor deposition coating composition comprising light absorptive materials
WO2024059124A1 (en) 2022-09-14 2024-03-21 Vitro Flat Glass Llc Reflective coating

Family Cites Families (19)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US4094763A (en) * 1970-07-31 1978-06-13 Ppg Industries, Inc. Sputter coating of glass with an oxide of a metal having an atomic number between 48 and 51 and mixtures thereof
US4166018A (en) * 1974-01-31 1979-08-28 Airco, Inc. Sputtering process and apparatus
US4349425A (en) * 1977-09-09 1982-09-14 Hitachi, Ltd. Transparent conductive films and methods of producing same
US4113599A (en) * 1977-09-26 1978-09-12 Ppg Industries, Inc. Sputtering technique for the deposition of indium oxide
US4201649A (en) * 1978-11-29 1980-05-06 Ppg Industries, Inc. Low resistance indium oxide coatings
DE2924833C3 (de) * 1979-06-20 1982-05-19 Bfg Glassgroup, Paris Wärmereflexionsscheibe mit farbneutraler Außenansicht und deren Verwendung als Außenscheibe einer Mehrscheibenanordnung
DE3160998D1 (en) * 1980-03-10 1983-11-03 Teijin Ltd Selectively light-transmitting laminated structure
DE3039821A1 (de) * 1980-10-22 1982-06-03 Robert Bosch Gmbh, 7000 Stuttgart Mehrschichtsystem fuer waermeschutzanwendung
DE3211753C2 (de) * 1982-03-30 1985-03-28 Interpane Entwicklungs- und Beratungsgesellschaft mbH & Co. KG, 3471 Lauenförde Hochtransparenter, in Durch- als auch Außenansicht neutral wirkender und wärmedämmender Belag für ein Substrat aus transparentem Material sowie Verwendung des Belages
JPS5931147A (ja) * 1982-08-17 1984-02-20 株式会社豊田中央研究所 可視光透過性熱線しやへい膜およびその製造方法
NO157212C (no) * 1982-09-21 1988-02-10 Pilkington Brothers Plc Fremgangsmaate for fremstilling av belegg med lav emisjonsevne.
DE3307661A1 (de) * 1983-03-04 1984-09-06 Leybold-Heraeus GmbH, 5000 Köln Verfahren zum herstellen von scheiben mit hohem transmissionsverhalten im sichtbaren spektralbereich und mit hohem reflexionsverhalten fuer waermestrahlung
DE3316548C2 (de) * 1983-03-25 1985-01-17 Flachglas AG, 8510 Fürth Verfahren zur Beschichtung eines transparenten Substrates
US4610771A (en) * 1984-10-29 1986-09-09 Ppg Industries, Inc. Sputtered films of metal alloy oxides and method of preparation thereof
US4716086A (en) * 1984-12-19 1987-12-29 Ppg Industries, Inc. Protective overcoat for low emissivity coated article
DE3543178A1 (de) * 1985-12-06 1987-06-11 Leybold Heraeus Gmbh & Co Kg Verfahren zum herstellen von scheiben mit hohem transmissionsverhalten im sichtbaren spektralbereich und mit hohem reflexionsverhalten fuer waermestrahlung sowie durch das verfahren hergestellte scheiben
CA1331867C (en) * 1986-12-29 1994-09-06 James Joseph Finley Low emissivity film for high temperature processing
US4790922A (en) * 1987-07-13 1988-12-13 Viracon, Inc. Temperable low emissivity and reflective windows
JPS6474806A (en) * 1987-09-17 1989-03-20 Japan Radio Co Ltd Slop array antenna

Also Published As

Publication number Publication date
JP2505278B2 (ja) 1996-06-05
DE68915042D1 (de) 1994-06-09
ES2056136T3 (es) 1994-10-01
KR920005471B1 (ko) 1992-07-04
CA1337483C (en) 1995-10-31
BR8901510A (pt) 1989-11-14
EP0335309A1 (de) 1989-10-04
KR890015969A (ko) 1989-11-27
US4898790A (en) 1990-02-06
JPH01301537A (ja) 1989-12-05
EP0335309B1 (de) 1994-05-04

Similar Documents

Publication Publication Date Title
DE68915042T2 (de) Film mit geringerer Emission für Hochtemperaturbehandlung.
DE3881843D1 (de) Orientierte polyaethylenfolie.
DE68923756D1 (de) Abgedeckte Wärmebehandlung.
ES513069A0 (es) Perfeccionamientos en lamparas quirurgicas.
FI891327A (fi) Roerformig protes.
DE3587087T2 (de) Roentgenstrahlenquelle mit hoher intensitaet.
DE68908470D1 (de) Weiche waermeleistungsfaehige zuammensetzung.
DE68921124D1 (de) Heizstreifen.
DE68911007D1 (de) Kassette.
DE68921033D1 (de) Belichtungsverfahren.
DE68911906D1 (de) Lichtdichte kassette.
DE3886549D1 (de) Niedrigtemperaturofen.
DE68906946T2 (de) Leuchte.
DE3850382T2 (de) Polyester-film.
DE68919805D1 (de) Wärmeintegrationsverfahren.
NO894128D0 (no) Kompositt-plastfilm.
FI892761A (fi) Expressionsvektorer foer framstaellning av ofusionerade proteiner i mikroorganismer.
DE3883747D1 (de) Gelatinzusammensetzung.
DE69007412D1 (de) Folienträger.
FI893784A (fi) Med en diskontinuerlig film foersedda optiska minnesmedia.
FI893144A0 (fi) Substituerade azacyklohexylderivat.
NO894505L (no) Vandig cisplatinloesning.
NO882455D0 (no) Neddykket roerbro.
NO884559D0 (no) Taueoeye for slepewire.
ATE89187T1 (de) Abgasbehandlungsapparat.

Legal Events

Date Code Title Description
8364 No opposition during term of opposition
8327 Change in the person/name/address of the patent owner

Owner name: PPG INDUSTRIES OHIO, INC., CLEVELAND, OHIO, US