US20010001656A1 - Crystalline microporous and mesoporous metal silicates and use thereof - Google Patents

Crystalline microporous and mesoporous metal silicates and use thereof Download PDF

Info

Publication number
US20010001656A1
US20010001656A1 US09/293,949 US29394999A US2001001656A1 US 20010001656 A1 US20010001656 A1 US 20010001656A1 US 29394999 A US29394999 A US 29394999A US 2001001656 A1 US2001001656 A1 US 2001001656A1
Authority
US
United States
Prior art keywords
sio
binder
shaped object
metal
object according
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Abandoned
Application number
US09/293,949
Inventor
Steffen Hasenzahl
Helmut Mangold
Eckehart Roland
Mario Scholz
Georg Thiele
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Evonik Operations GmbH
Original Assignee
Degussa GmbH
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Priority claimed from DE19624340A external-priority patent/DE19624340A1/en
Application filed by Degussa GmbH filed Critical Degussa GmbH
Priority to US09/293,949 priority Critical patent/US20010001656A1/en
Assigned to DEGUSSA-HULS AKTIENGESELLSCHAFT reassignment DEGUSSA-HULS AKTIENGESELLSCHAFT ASSIGNMENT OF ASSIGNORS INTEREST (SEE DOCUMENT FOR DETAILS). Assignors: ROLAND, ECKEHART, THIELE, GEORG, SCHOLZ, MARIO, MANGOLD, HELMUT, HASENZAHL, STEFFEN
Publication of US20010001656A1 publication Critical patent/US20010001656A1/en
Priority to US09/931,025 priority patent/US6710193B2/en
Assigned to DEGUSSA AG reassignment DEGUSSA AG MERGER (SEE DOCUMENT FOR DETAILS). Assignors: DEGUSSA-HULS AKTIENGESELLSCHAFT
Abandoned legal-status Critical Current

Abstract

Microporous and mesoporous metal silicates are prepared by the hydrothermal reaction of a silicon and metal source in the presence of a template. The choice of raw materials influences the purity and hence the catalytic activity of the products. A pyrogenic mixed oxide is used as the silicon and metal source. Prepared products have the composition (SiO2)1−x(AmOn)x, where A is Ti, Al, B, V or Zr and x is 0.005 to 0.1. Shaped objects of the microporous and mesoporous metal silicates are obtained directly by using a shaped object of the pyrogenic mixed oxide. The products obtained are used as oxidation catalysts.

Description

    REFERENCE TO A RELATED APPLICATION
  • This is a divisional application based on copending application Ser. No. 08/878,509 filed Jun. 19, 1998 which is relied on and incorporated herein by reference. [0001]
  • INTRODUCTION AND BACKGROUND
  • The present invention relates to a process for the preparation of crystalline microporous and mesoporous metal silicates composed of silicon dioxide and one or more metal oxides. In another aspect, the present invention relates to products obtainable by said process. Still further, the present invention relates to the use of these products. [0002]
  • A variety of crystalline microporous and mesoporous metal silicates are known. According to the IUPAC definition, micropores are understood as meaning pores with a diameter of less than 2 nm, and mesopores are understood as meaning pores with a diameter of 2 to 50 nm. These definitions are used herein. [0003]
  • Some crystalline metal silicates with regular micropores or mesopores are extremely effective catalysts in a very wide variety of applications. In particular, microporous products of the composition (SiO[0004] 2)1−x(TiO2)x, in which titanium atoms replace some of the silicon atoms in the crystal lattice, have achieved industrial importance as oxidation catalysts. The structures of these metal silicates differ according to the starting materials and conditions of preparation. Thus, for example, so-called titanium silicalite-1, titanium silicalite-2 and titanium beta-zeolite have the MFI, MEL and BEA crystal structures, respectively. Crystal structure types of known zeolites and silicalites are described in W. M. Meier, D. H. Olson, Atlas of Zeolite Structure Types, Butterworth-Heinemann, 1993. Known structures with regular mesopores are the MCM-41 and MCM-48 structures described in C. T. Kresge et al., Nature, 359 (1992), pp. 710-712. A survey of structures with regular mesopores is also given in S. Behrens, Angew, Chemie, 1996, 108 (5), pp. 561-564.
  • It is known that the catalytic efficacy of generic metal silicates is substantially dependent on their phase purity and the morphology and, hence, on the conditions of preparation. For example, the catalytic activity of titanium silicalite is reduced by other titanium-containing phases, for instance TiO[0005] 2, and by an increase in the crystal size; see, B. Notari in (a) Catal. Today 18 (1993), p. 163 and (b) Stud. Surf. Sci. Catal., 67 (1991), p. 243.
  • Generic metal silicates, for instance titanium silicalite-1, can be prepared by hydrothermal synthesis. In the first step, a silicon source and a titanium source, conventionally tetraalkyl orthosilicate and tetraalkyl orthotitanate, and water are condensed to a gel in the presence of a structure-determining quaternary ammonium cation, usually used in the form of the quaternary ammonium hydroxide, and the gel is then crystallized under hydrothermal conditions, usually above 100°C. and under autogenous pressure. The solid formed is separated off, washed, dried and calcined above 300°C. The way in which the Ti component is introduced is liable to cause problems, it often being impossible to exclude contamination of the product by TiO[0006] 2 as a foreign phase—loc. cit. B. Notari (b). According to EP 543 247, the quaternary ammonium hydroxide can be replaced as the template with a combination of a quaternary ammonium salt and a base such as ammonia, although the crystals obtained are relatively large. According to U.S. Pat. No. 5,198,203 a mesoporous titanium silicate of the MCM-41 structure can be prepared with cetyltrimethylammonium hydroxide as the template.
  • Another known silicon source is pyrogenic silicic acid. According to R. Kumar et al. in [0007] Stud. Surf. Sci. Catal., 84 (1994) p. 109, titanium silicalite-1 can be obtained by hydrothermal synthesis from pyrogenic silicic acid and tetrabutyl orthotitanate. The use of a tetraalkyl orthotitanate carries the risk of obtaining a product of insufficient phase purity.
  • According to EP 0 311 983, titanium silicalites are prepared by impregnating a coprecipitated porous TiO[0008] 2—SiO2 material, which can be amorphous or crystalline, with a template compound and then subjecting the product to hydrothermal synthesis. Suggestions of using coprecipitates with other metals, or pyrogenic mixed oxides, are not to be found in said document.
  • In known synthesis processes the generic microporous metal silicates are formed as crystallites with a size usually of less than one micrometer, which can only be separated from a liquid at considerable expenses. For many industrial applications the fine material is therefore coarsened by a subsequent agglomeration step. According to EP 0 265 018, the agglomeration is effected using oligomeric SiO[0009] 2 as a binder.
  • According to EP 0 299 430, a preformed amorphus SiO[0010] 2 matrix is impregnated with an aqueous solution containing a soluble titanium compound and a suitable template, and crystallized under hydrothermal conditions, the shape and size of the SiO2 matrix remaining essentially unchanged. This process again has the disadvantage that the use of a soluble titanium compound carries the risk of reducing the phase purity and hence the catalytic activity.
  • Accordingly, it is an object of the invention to produce generic metal silicates of high phase purity and high catalytic activity. [0011]
  • Another object of the invention is to provide a process suitable not only for the preparation of products based on (SiO[0012] 2)1−x(TiO2)x, but also for the preparation of products in which titanium is replaced with one or more other metals in the crystal lattice.
  • Still further, another object of the invention is to carry out the process in such a way that binder-free shaped objects of the crystalline microporous and mesoporous metal silicates can be obtained directly, i.e., without a subsequent agglomeration step. [0013]
  • SUMMARY OF THE INVENTION
  • In achieving the above and other objects, a feature of the invention resides in a process for the preparation of microporous and mesoporous metal silicates, comprising the hydrothermal reaction of a silicon source in the presence of a metal source and a template wherein a pyrogenic metal-silicon mixed oxide is used as the silicon and metal source. Any suitable template can be used for purposes of the invention. [0014]
  • DETAILED DESCRIPTION OF THE INVENTION
  • The general composition of the pyrogenic mixed oxides and hence also of the crystalline microporous and mesoporous metal silicates to be prepared is represented as follows: [0015]
  • (SiO2)1−x(AmOn)x   (Ia), (SiO2)1−x((AmOn)1-y(A′m,On,)y)x   (Ib).
  • In the above formulae, A and A′ are each the same or different metal of valency p selected from the group consisting of: [0016]
  • B, Al, Ga, In, Ge, Sn and Pb or from subgroups 3 to 8 of the Periodic Table of Elements; [0017]
  • m and m′ and n and n′ are the number of atoms, where m·p=2n and m′·p=2n′; [0018]
  • x is a number from 0.0001 to 0.25, preferably from 0.001 to 0.2 and especially from 0.005 to 0.1; and [0019]
  • y in formula (Ib) is a number greater than 0 and less than 1. [0020]
  • Apart from SiO[0021] 2, pyrogenic mixed oxides which are preferably to be used contain one or more oxides selected from the group consisting of Al2O3, B2O3, TiO2, ZrO2, V2O5, Cr2O3 and Fe2O3. Oxides of the subgroup elements are optionally present not only in the highest oxidation state but also in a lower oxidation state. Generic metal silicates which are to be used as oxidation catalysts are prepared with mixed oxides which are free of aluminum oxide, the process according to the invention giving metal silicalites in this case. Generic metal silicates of the composition
  • (SiO2)1−x(MrAmOn,)   (II)
  • are prepared using mixed oxides of composition (Ia). M in composition (II) is a cation of valency q selected from the group consisting of alkali metals, alkaline earth metals, H[0022] +, NH4 +and N(alkyl)4 +; m·p+r·q=2n″ in (II). In the process according to the invention, M is introduced into the metal silicate either via the template or via alkali metal or alkaline earth metal hydroxide or ammonia present in the hydrothermal synthesis. After the calcination of a generic metal silicate of composition (II), M is a proton or an alkali metal or alkaline earth metal ion. However, said cations M or other cations can also be incorporated into the microporous and mesoporous metal silicates at a later stage by means of conventional ion exchange reactions.
  • The pyrogenic mixed oxides to be used in the process according to the invention can be prepared in a manner known per se from a mixture of a volatile silicon compound and one or more volatile metal compounds (compounds of A and/or A′), for example, by flame hydrolysis or the luminous arc process. The process according to the invention is preferably carried out using pyrogenic mixed oxides of silicon which have been prepared by flame hydrolysis, for example, those known from Ullmann's [0023] Encyklopädie der Technischen Chemie (Ullmann's Encyclopedia of Chemical Technology), 4th edition, vol. 21, pp. 464-465 (1982) and DE-A 36 11 449.
  • The process according to the invention can be carried out using both the pulverulent pyrogenic mixed oxides and shaped objects thereof. [0024]
  • The shaped objects of the metal-silicon mixed oxide can be produced by known processes, for example, spray granulation, fluidized bed granulation, extrusion, pelleting or tableting. In a preferred embodiment of the invention the shaped objects can be produced by means of spray granulation, as described, for example, in DE-A 36 11 449. [0025]
  • In the process according to the invention the pyrogenic metal/silicon mixed oxide, in powder form or in the form of a binder-free shaped object produced therefrom, is brought into contact with an aqueous solution of a suitable template; when using coarser shaped objects of mixed oxide, for instance extrudates, this is conventionally an impregnation process. After intermediate drying, if appropriate, this step is followed by the hydrothermal reaction to convert the pyrogenic metal-silicon mixed oxide to the crystalline microporous or mesoporous metal silicate according to the invention. After the hydrothermal reaction, the template is removed from the metal silicate in a manner known, per se, conventionally by extraction or, preferably by calcination. [0026]
  • Suitable template compounds are amines having one or more amino groups, amino alcohols or tetrasubstituted ammonium compounds. Tetraalkylammonium compounds are particularly suitable, especially tetraalkylammonium hydroxide. The nature of the alkyl groups in said tetraalkylammonium compounds is significant in terms of the pore structure. The tetraalkylammonium compounds used to prepare microporous metal silicates according to the invention are preferably those in which alkyl is ethyl, propyl and butyl, preferably n-propyl. Thus, for example, metal silicates according to the invention of the MFI, MEL and BEA structure can be prepared using tetra-n-propylammonium, tetra-n-butylammonium and tetraalkylammonium compounds, respectively. The tetraalkylammonium compounds used to prepare mesoporous metal silicates according to the invention are preferably those which have surfactant properties. Accordingly, these compounds contain an alkyl group or an alkenyl group having at least 7 C atoms in the longest chain. Particularly preferred ammonium compounds are those of the general formula RNR′[0027] 3 +X, in which R contains 12 to 18 C atoms and is preferably unbranched and saturated, R′ has 1 or 2 C atoms, and X is the anion, conventionally hydroxide or halide. Cetyltrimethylammonium chloride or bromide and lauryltrimethylammonium chloride or bromide are particularly suitable for the preparation of mesoporous structures. When using tetraalkylammonium halides as the template, a base, such as ammonia, a primary, secondary or tertiary amine or an alkali metal or alkaline earth metal hydroxide, is added to the template solution used for the contacting/impregnation process. The template compound is conventionally used in a molar ratio of template to SiO2 of 0.05 to 2.0. For the preparation of microporous metal silicates, a molar ratio template to SiO2 of from 0.05 to 1.0, especially from 0.10 to 0.45, is preferred. For the preparation of mesoporous metal silicates according to the invention of the MCM-41 or MCM-48 structure, a molar ratio of template to SiO2 of from 0.05 to 2.0, especially of from 0.1 to 0.8, is preferred.
  • The molar ratio OH/SiO[0028] 2 is generally from 0.05 to 2.0 and preferably from 0.1 to 1.0. In the hydrothermal reaction to the molar ratio H2O/SiO2 is from 1 to 200 and preferably from 4 to 100. Seed crystals of the same structural type can be added to the reaction mixture if necessary. The molar ratio H2O/SiO2 is generally lower when using shaped objects of pyrogenic mixed oxides than when using pyrogenic mixed oxides as obtained directly by flame hydrolysis.
  • In the process according to the invention for the preparation of microporous metal silicates, the hydrothermal reaction is conventionally carried out under autogenous pressure at a temperature from 100 to 200°C. and preferably from 150 to 190°C. Mesoporous metal silicates according to the invention can also be prepared at lower temperature, the conventional temperature range being from 25 to 200°C., preferably from 50 to 175°C. and especially from 70 to 150°C. The hydrothermal reaction is carried out until the pyrogenic mixed oxide used has been completely converted to the crystalline microporous or mesoporous metal silicate according to the invention at the given reaction temperature. The degree of completion of the reaction can be determined by known methods of structural analysis. Under optimized conditions the reaction time is conventionally from 1 to 50 hours. [0029]
  • To remove the template compound from the solid obtained in the hydrothermal reaction, said solid is usually calcined at from 300 to 1000°C., optionally after a prior washing process, it being possible for the calcination step to include a shaping process at the same time. In the case of the mesoporous metal silicates according to the invention, at least some of the template compound can also be removed by extraction with an organic solvent. [0030]
  • In one particular embodiment of the process according to the invention, the pyrogenic metal-silicon mixed oxide, for instance as obtained by flame hydrolysis, is suspended in an aqueous template solution. The molar ratios used here can be the same as those indicated above. This suspension is spray-dried, and the resulting granules containing the template are treated in an autoclave at elevated temperature, for example, at 175°C., optionally in a steam atmosphere. The spray drying is advantageously carried out by setting the temperature of the drying air in the range of 100 to 500°C. so that the resulting granules have a water content of 5 to 50 wt. %. After the hydrothermal reaction, the shaped objects obtained are calcined at a temperature of 300 to 1000°C., preferably of 400 to 800°C., to remove the template. [0031]
  • The process according to the invention can be carried out reproducibly and is easy to control. The use of the pyrogenic mixed oxides avoids problems due to the presence of foreign phases of the metal oxides in question. A high catalytic activity is a characteristic feature of the crystalline microporous and mesoporous metal silicates obtainable by the process according to the invention. The generic metal silicates can moreover be obtained not only in the form of very finely powdered materials but also in the form of different shaped objects. When using shaped objects of pyrogenic mixed oxides or forming such shaped objects directly before the hydrothermal reaction, a subsequent agglomeration step is not necessary. The addition of catalytically inactive binders is also superfluous. [0032]
  • A further advantage of shaped objects of crystalline microporous and mesoporous metal silicates obtainable according to the invention is that they can be separated more easily from liquids filtration than unshaped catalysts, thereby facilitating their use as suspension catalysts. As pyrogenic mixed oxides are easy to shape, for instance into spheres, extrudates, pellets or tablets and the shape remains essentially unchanged in the process according to the invention, said process directly produces suitable shaped objects for use as catalysts in fixed bed reactions. [0033]
  • Although it is know from EP 0 311 983 B that coprecipitated TiO[0034] 2—SiO2 material can be used for the preparation of titanium silicates, the copreciptates to be used are very porous products. It was therefore surprising that crystalline microporous and mesoporous metal silicates are easily obtainable by using pore-free pyrogenic mixed oxides such as those used in the process according to the invention.
  • As such, preferably in the form of shaped objects, the crystalline microporous and mesoporous metal silicates obtainable according to the invention are used as catalysts. Titanium silicalites and other aluminum-free products are particularly suitable as catalysts for oxidation reactions with hydrogen peroxide or organic hydroperoxides. Examples are the use of titanium silicalite-1 as a catalyst for the reaction of olefins, i.e., propene, with hydrogen peroxide to give epoxides (EP 100 119), the reaction of aromatics with hydrogen peroxide to give hydroxyaromatics (DE 31 35 559), the reaction of aliphatic hydrocarbons with hydrogen peroxide to give alcohols and ketones (EP 376 453) and the reaction of cyclohexanone with hydrogen peroxide and ammonia to give cyclohexanone oxime (EP 208 311). Titanium silicalite-2 is used as a catalyst for the hydroxylation of phenol (J. S. Reddy, S. Sivasanker, P. Ratnasamy, [0035] J. Mol. Catal. 71 (1992) p. 373) and for the reaction of cyclohexanone with hydrogen peroxide and ammonia to give cyclohexanone oxime (J. S. Reddy, Reddy, S. Sivasanker, P. Ratnasamy, J. Mol. Catal. 71 (1992) p. 383) . Titanium beta-zeolite can be used as a catalyst for the reaction of olefins with hydrogen peroxide or organic hydroperoxides to give epoxides (A. Corma, P. Esteve, A. Martinez, S. Valencia, J. Catal. 152 (1995) p. 18 and EP 659 685).
  • The following examples serve to illustrate the present invention. [0036]
  • EXAMPLE 1
  • Preparation of Titanium Silicalite-1 Powder [0037]
  • 137.0 g of tetrapropylammonium hydroxide solution (40 wt. %) and 434.2 g of deionized water are placed in a polyethylene beaker and 111.1 g of pyrogenic silicon-titanium mixed oxide containing 3.0 wt. % of TiO[0038] 2 are added, with stirring. The resulting synthetsis gel is first aged for four hours at 80°C., with stirring, and then crystallized in an autoclave for 24 hours at 175°C. The solid obtained is separated from the mother liquor by centrifugation, washed with three times 250 ml of deionized water, dried at 90°C. and calcined in an air atmosphere for four hours at 550°C. The yield is 98.3 g.
  • The X-ray diffraction diagram of the catalyst prepared in this way shows the diffraction pattern typical of the MFI structure, and the IR spectrum shows the band at 960 cm[0039] −1 characteristic of titanium-containing molecular sieves. Wet chemical analysis gives a titanium content of 2.3 wt. % of TiO2. The DR-UV-Vis spectrum also shows that the sample is free of titanium dioxide.
  • EXAMPLE 2
  • Application Example of the Epoxidation of Propylene With Hydrogen Peroxide [0040]
  • 1.0 g of the catalyst prepared according to Example 1 in 300 ml of the methanol is placed in a thermostated laboratory autoclave with gas dispersion stirrer, at 40°C. under a propylene atmosphere, and the solvent is saturated with propylene under an excess pressure of 3 bar. 13.1 g of 30 wt. % aqueous hydrogen peroxide solution is then added all at once, with stirring, and the reaction mixture is kept at 40°C. and 3 bar, additional propylene being metered in via a pressure regulator in order to make up the quantity consumed by the reaction. Samples are taken at regular intervals via a filter, and hydrogen peroxide content of the reaction mixture is determined by redox titration with cerium (IV) sulphate solution. The plot of 1n(c/c[0041] 0) against the time t, c being the measured H2O2 concentration at time t and c0 being the calculated H2O2 concentration at the start of the reaction, gives a straight line. An activity coefficient k of 25.4 min−1 is determined from the gradient of the lines by means of the relationship dc/dt=−k·c·ccat, where ccat is the catalyst concentration in kg of catalyst per kg of reaction mixture.
  • EXAMPLE 3
  • Preparation of Titanium Silicalite-1 Microgranules [0042]
  • 800 g of deionized water and 30 g of acetic acid are placed in a polyethylene beaker and 200 g of pyrogenic silicon-titanium mixed oxide containing 3.6 wt. % of TiO[0043] 2 are added, with stirring. This mixture is sheared for five minutes in an Ultraturax stirrer. The resulting suspension is dried by means of a spray dryer (NIRO-Atomizer model 1638; inlet temperature 380°C.; outlet temperature 102°C.; speed of rotation of the spray disk 15,000 min−1). 20 g of the resulting microgranules, with a mean particle diameter of 30 μm, are impregnated with a mixture of 20 g of tetrapropylammonium hydroxide solution (40 wt. %) and 20 g of deionized water. The impregnated microgranules are charged into an autoclave with a Teflon inliner and crystallized for 24 hours at 175°C. under static conditions. The solid obtained is separated from the mother liquor by centrifugation, washed three times with 100 ml of deionized water, dried at 90°C. and calcined in an air atmosphere for four hours at 550°C. The yield is 17 g.
  • The catalyst prepared in this way consists of titanium silicalite-1 microgranules. [0044]
  • EXAMPLE 4
  • Preparation of Titanium Silicalite-1 Microgranules [0045]
  • 720.7 g of deionized water and 179.3 g of tetrapropylammonium hydroxide solution (40 wt. %) are placed in a polyethylene beaker and 100 g of pyrogenic silicon-titanium mixed oxide containing 3.6 wt. % of TiO[0046] 2 are added, with stirring. This mixture is sheared for five minutes in an Ultraturax stirrer. The resulting suspension is dried by means of a spray dryer (NIRO-Atomizer model 1638; inlet temperature 380°C.; outlet temperature 90° C.; speed of rotation of the spray disk 15,000 min−1). 20 g of the resulting microgranules, with a mean particle diameter of 30 μm, a loss on drying of 23 wt. % (10 h at 105°C.; corresponds to the water content) and a loss on calcination of 43 wt. % (5 h at 550°C.; corresponds to the water and template content), are charged into an autoclave with a Teflon inliner and crystallized for 4 days at 180°C. under static conditions. The solid is then dried at 90°C. and calcined in an air atmosphere for four hours at 550°C.
  • The catalyst prepared in this way consists of titanium silicalite-1 microgranules. [0047]
  • EXAMPLE 5
  • Preparation of a Titanium Beta-Zeolite Powder [0048]
  • 435.3 g of tetraethylammonium hydroxide solution (35 wt. %) and 236.3 g of deionized water are placed in a polyethylene beaker and 109.6 g of pyrogenic silicon-titanium mixed oxide containing 3.0 wt. % of TiO[0049] 2 is added. The resulting mixture is aged for four hours at 80° C. and, after cooling to room temperature, 12 g of beta-zeolite seed crystals with an SiO2/Al2O3 ratio of 27 are added. This synthesis gel is crystallized in an autoclave for 3 days at 150°C., with stirring.
  • The solid obtained is separated from the mother liquor by centrifugation, washed three times, each time with 250 ml of deionized water, dried at 90°C. and calcined in an air atmosphere for four hours at 550°C. [0050]
  • The X-ray diffraction diagram of the catalyst prepared in this way shows the diffraction pattern typical of the BEA structure. Wet chemical analysis gives a titanium content of 1.8 wt. % of TiO[0051] 2.
  • EXAMPLE 6
  • Preparation of a Mesoporous Titanium Silicate of the MCM-41 Structure [0052]
  • 114.2 of tetramethylammonium hydroxide solution (10% wt. %) is placed in a polyethylene beaker and 30.0 g of pyrogenic silicon-titanium mixed oxide containing 3.6 wt. % of TiO[0053] 2 are added, with stirring. This mixture is stirred for one hour. A suspension of 29.1 g of cetyltrimethylammonium bromide (C16H33(CH3)3NBr) in 109.2 g of deionized water is then added, with stirring, and stirring is continued for 10 minutes. The resulting synthesis gel (molar composition: SiO2: 0.17 C16H33(CH3)3N+:0.26 Me4NOH:25 H2O) is crystallized in an autoclave for 48 hours at 140°C. under static conditions. The solid obtained is filtered off and washed with deionized water until the filtrate is neutral. The solid is dried at 90°C. and then calcined in an air atmosphere for four hours at 640°C. The yield is 28 g.
  • The X-ray diffraction diagram of the catalyst prepared in this way shows the diffraction pattern typical of the MCM-41 materials, with d[0054] 100 reflection at 3.60 nm. Examination by sorption analysis with nitrogen at 77 K shows a mean pore diameter of 3.16 nm, a BET specific surface area of 1040 m2 g−1 and a pore volume of 0.89 ml/g. Wet chemical analysis gives a titanium content of 4.6 wt. % of TiO2. The material is catalytically active in the epoxidation of propene with hydrogen peroxide.
  • EXAMPLE 7
  • Preparation of a Mesoporous Titanium Silicate of the MCM-48 Structure [0055]
  • 114.2 g of tetramethylammonium hydroxide solution (10% wt. %) is placed in a polyethylene beaker and 30.0 g of pyrogenic silicon-titanium mixed oxide containing 3.6 wt. % of TiO[0056] 2 are added, with stirring. This mixture is stirred for one hour. A suspension of 114.2 g of cetyltrimethylammonium bromide (C16H33(CH3)3NBr) in 435.2 g of deionized water is then added, with stirring, and stirring is continued for 10 minutes. The resulting synthesis gel (molar composition: SiO2:0.65 C16H33(CH3)3NBr:0.26 Me4NOH :62 H2O) is crystallized in an autoclave for 48 hours at 140°C. under static conditions. The solid obtained is filtered off and washed with deionized water until the filtrate is neutral. The solid is dried at 90°C. and then calcined in an air atmosphere for four hours at 640°C.
  • The catalyst prepared in this way consists of Ti-MCM-48. [0057]
  • EXAMPLE 8
  • Preparation of a Boron Pentasil Zeolite [0058]
  • 800 g of aqueous hexamethylenediamine solution (50 wt. %) is placed in a polyethylene beaker and 70.7 g of pyrogenic silicon-boron mixed oxide containing 9.5 wt. % of B[0059] 2O3 is added, with stirring. This mixture is stirred for half an hour and then crystallized in an autoclave for five days at 170°C. The solid obtained is separated from the mother liquor by centrifugation, washed three times in 250 ml of deionized water, dried at 90°C. and calcined in an air atmosphere for six hours at 550°C.
  • The X-ray diffraction diagram of the catalyst prepared in this way shows the diffraction pattern typical of the MFI structure. Wet chemical analysis gives a B[0060] 2O3 content of 2.4 wt. %.
  • EXAMPLE 9
  • Preparation of a Boron Silicate of the MCM-41 Structure [0061]
  • 156.7 g of tetramethylammonium hydroxide solution (10 wt. %) is placed in a polyethylene beaker and 42.3 g of pyrogenic silicon-boron mixed oxide containing 5.5 wt. % of B[0062] 2O3 is added, with stirring. This mixture is stirred for one hour. A suspension of 65.5 g of cetyltrimethylammonium bromide (C16H33(CH3)3NBr) in 576.5 g of deionized water is then added, with stirring, and stirring is continued for 10 minutes. The pH is adjusted to 11.5 by the addition of dilute sulphuric acid. The resulting synthesis gel is crystallized in an autoclave for 48 hours at 140°C. under static conditions. The solid obtained is filtered off and washed with deionized water until the filtrate is neutral. The solid is dried to 90°C. and then calcined in an air atmosphere for four hours at 540°C.
  • The X-ray diffraction diagram of the catalyst obtained shows the diffraction pattern typical of the MCM-41 materials. Examination by sorption analysis with nitrogen at 77°K. shows a mean pore diameter of 2.83 nm, a BET specific surface area of 1060 m[0063] 2 /g and a pore volume of 0.89 ml/g.
  • EXAMPLE 10
  • Preparation of a Zirconium Silicalite-1 Powder [0064]
  • 62.4 g of tetrapropylammonium hydroxide solution (40 wt. %) and 229.8 g of deionized water are placed in a polyethylene beaker and 57.4 g of pyrogenic silicon-zirconium oxide containing 3.0 wt. % of ZrO[0065] 2 are added, with stirring. The resulting synthesis gel is then crystallized in an autoclave for 24 hours at 175°C. The solid obtained is separated from the mother liquor by centrifugation, washed with three times 250 ml of deionized water, dried at 90°C. and calcined in an air atmosphere for four hours at 550°C.
  • The X-ray diffraction diagram of the catalyst obtained shows the diffraction pattern typical of the MFI structure. X-ray fluorescence analysis gives ZrO[0066] 2 content of 1.0 wt. %
  • EXAMPLE 11
  • Preparation of a Zirconium Silicate of the MCM-41 Structure [0067]
  • 114.2 g of tetramethylammonium hydroxide solution (10 wt. %) are placed in a polyethylene beaker and 30.0 g of pyrogenic silicon-zirconium oxide containing 3.0 wt. % of ZrO[0068] 2 is added, with stirring. This mixture is stirred for one hour. A suspension of 29.1 g of cetyltrimethylammonium bromide (C16H33(CH3)3NBr) in 109.2 g of deionized water is then added, with stirring, and stirring is continued for 10 minutes. The resulting synthesis gel is crystallized in an autoclave for 48 hours at 140°C. under static conditions. The solid obtained is filtered off and washed with deionized water until the filtrate is neutral. The solid is dried to 90°C. and then calcined in an air atmosphere for four hours at 640°C.
  • The X-ray diffraction diagram of the catalyst obtained shows the diffraction pattern typical of the MCM-41 materials with a d[0069] 100 value of 3.25 nm. Examination by sorption analysis with nitrogen at 77 K shows a mean pore diameter of 2.4 nm, a BET specific surface area of 860 m2/g and a pore volume of 0.59 ml/g.
  • Further variations and modifications of the foregoing will be apparent to those skilled in the art and intended to be encompassed by the claims appended hereto. [0070]
  • German priority application 196 24 340.8 is relied on and incorporated hereby reference. [0071]

Claims (21)

We claim:
1. A binder-free shaped objected selected from the group consisting of microporous and mesoporous metal silicates, obtained by the hydrothermal reaction of a silicon and metal source in the presence of a template, wherein a pyrogenic metal-silicon mixed oxide is the silicon and metal source.
2. The binder-free shaped object according to
claim 1
wherein the crystalline microporous and mesoporous metal silicates are represented by the composition
(SiO2)1−x(AmOn)x   (Ia), (SiO2)1−x((AmOn)1-y(A′m,On,)y)x   (Ib)
or
(SiO2)1−x(MrAmOn,)x   (II)
in which
x is a number from 0.0001 to 0.25;
y is a number greater than 0 and less than 1;
A and A′ are a metal of valency p selected from the group consisting of B, Al, Ga, In, Ge, Sn, Pb, and subgroups 3 to 8 of the Periodic Table of Elements;
M is a cation of valency q selected from the group consisting of alkali metals, alkaline earth metals, H+, NH4 +and N(alkyl)4 +
m, m′, n, n′, n″ and r are the number of atoms, where:
m·p=2n and m′·p=2n′ and
m·p+r·q=2n″,
wherein a pyrogenic mixed oxide of composition (Ia) or (Ib) is used and the cation M of formula (II) is incorporated via the template or via alkali metal or alkaline earth metal hydroxide present in the hydrothermal reaction.
3. The binder-free shaped object according to
claim 1
wherein said pyrogenic metal-silicon mixed oxide is prepared by flame hydrolysis.
4. The binder-free shaped object according to
claim 1
wherein said pyrogenic mixed oxide is selected from the group consisting of
(SiO2)1−x(TiO2)x, (SiO2)1−x(Al2O3)x, (SiO2)1−x(B2O3)x, (SiO2)1−x(V2O5)x and (SiO2)1−x (ZrO2)x.
5. The binder-free shaped object according to
claim 4
which is
(SiO2)1−x(TiO2)x
.
6. The binder-shaped object according to
claim 1
wherein said template is an amine having one or more amino groups, an amino alcohol or a tetrasubstituted ammonium compound.
7. The binder-free shaped object according to
claim 1
wherein said template is used in an amount of 0.05 to 2.0 mol per mol of SiO2 in the mixed oxide.
8. The binder-free shaped object according to
claim 1
further comprising carrying out the hydrothermal reaction for the preparation of microporous metal silicates at a temperature from 100 to 220°C.
9. The binder-free shaped object according to
claim 1
further comprising carrying out the hydrothermal reaction for preparation of microporous metal silicates at a temperature from 150 to 190°C.
10. The binder-free shaped object according to
claim 1
wherein the preparation of mesoporous metal silicates is carried out at a temperature from 50 to 175°C. under at least autogenous pressure.
11. A process for catalytic oxidation reactions, wherein a catalyst is present corresponding to an Al-free metal silicalite defined in
claim 1
.
12. The process according to
claim 11
wherein the catalyst is (SiO2)1−x(TiO2)x.
13. A process for the oxidation of an olefin wherein a catalyst is present, said catalyst being the binder-free shaped object of
claim 1
.
14. The process according to
claim 13
wherein the catalyst is (SiO2)1−x(TiO2)x.
15. The process according to
claim 11
wherein propene is oxidized with hydrogen peroxide to give the corresponding epoxide.
16. The process according to
claim 12
wherein propene is oxidized with hydrogen peroxide to give the corresponding expoxide.
17. A process for preparing a hydroxy aromatic compound comprising reacting an aromatic compound with hydrogen peroxide or an organic hydroperoxide in the presence of a binder-free shaped object according to
claim 1
.
18. A process for producing an alcohol or ketone comprising reacting an aliphatic hydrocarbon with hydrogen peroxide or an organic hydroperoxide in the presence of a binder-free shaped object according to
claim 1
.
19. The process according to
claim 18
, wherein a ketone is converted to an oxime by reacting with hydrogen peroxide and ammonia.
20. A process for the catalytic epoxidation of an olefin with hydrogen peroxide as the oxidant comprising carrying out the epoxidation in the presence of a catalyst which is a crystalline microporous titanium silicate of the composition (SiO2)1−x(TiO2)x in which x is a number from 0.001 to 0.2 wherein a pyrogenic silicon-titanium mixed oxide is reacted with tetraalkylammonium hydroxide template in a hydrothermal reaction at a temperature from 100 to 220°C., and wherein the pyrogenic silicon-titanium mixed oxide is shaped to microgranules by a spray drying process prior to the hydrothermal reaction and a crystalline microporous titanium silicate in the form at microgranules is formed.
21. The process of
claim 20
, wherein the olefin is propene.
US09/293,949 1996-06-19 1999-04-19 Crystalline microporous and mesoporous metal silicates and use thereof Abandoned US20010001656A1 (en)