US20050249978A1 - Gradient polycrystalline cubic boron nitride materials and tools incorporating such materials - Google Patents
Gradient polycrystalline cubic boron nitride materials and tools incorporating such materials Download PDFInfo
- Publication number
- US20050249978A1 US20050249978A1 US11/097,476 US9747605A US2005249978A1 US 20050249978 A1 US20050249978 A1 US 20050249978A1 US 9747605 A US9747605 A US 9747605A US 2005249978 A1 US2005249978 A1 US 2005249978A1
- Authority
- US
- United States
- Prior art keywords
- recited
- boron nitride
- layer
- cubic boron
- phase
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Abandoned
Abstract
Gradient polycrystalline cubic boron nitride (PCBN) materials are provided as well as tools incorporating such materials.
Description
- This application is based upon and claims priority on U.S. Provisional Application No. 60/558,836, filed on Apr. 2, 2004, the contents of which are fully incorporated herein by reference.
- The present invention is directed to functionally gradient polycrystalline cubic boron nitride materials, to tools incorporating such materials.
- Polycrystalline cubic boron nitride has been used extensively as a cutting surface in various cutting tools. Polycrystalline cubic boron nitride (PCBN) is formed by placing cubic boron nitride grains, a second phase and a binder phase within a refractory metal enclosure and then sintering the enclosure with its contents at high pressure and high temperature (HPHT) conditions for forming the PCBN. PCBN materials may be tailored to either provide better strength, better toughness, better chemical wear, or better thermal stability. However, as the magnitude of any of these properties is increased, the magnitudes of the remaining properties may be decreased. To overcome this problem, PCBN material layers which have been used in cutting tools, have in many instances, been coated with a thin film, such as Al2O3 or TiN, which is more chemically and thermally stable than PCBN during severe cutting conditions. These films reduce the initial chemical wear and the mechanical wear of the PCBN. The problem however with these coatings is that they tend to debond, flake off or wear off from the PCBN layer. This is especially prevalent during machining with a coated PCBN layer.
- Polycrystalline cubic boron nitride materials are provided as well as tools incorporating such materials. In one exemplary embodiment, a polycrystalline cubic boron nitride material is provided having a first layer of polycrystalline cubic boron nitride formed from cubic boron nitride grains, and a second layer of polycrystalline cubic boron nitride bonded to the first layer, where the second layer is formed from cubic boron nitride grains which are coarser than the cubic boron nitride grains forming the first layer. In a further exemplary embodiment, a third layer of polycrystalline cubic boron nitride is formed from cubic boron nitride grains which are finer than the grains of cubic boron nitride forming the second layer. The second layer may be sandwiched between the first and third layers. Moreover, the first and third layers may be made of the same material. Furthermore, the first and third layers may have the same type of cubic boron nitride and the same second phase compositions. In another exemplary embodiment, the first and third layers may include a ceramic binder phase.
- In a further exemplary embodiment, a third layer of polycrystalline cubic boron nitride may be formed from cubic boron nitride grains which are coarser than the grains of cubic boron nitride forming the first layer. With this embodiment, the first layer may be sandwiched between the second and third layers. Furthermore, the second and third layers may include a ceramic second phase and a binder phase. Moreover, the second and third layers may be made of the same material. In addition, the second and third layers may include the same type of cubic boron nitride and the same second phase compositions. With any of the aforementioned exemplary embodiments, at least one of the layers may include a ceramic binder phase.
- In another exemplary embodiment, a polycrystalline cubic boron nitride material is provided having a first layer of polycrystalline cubic boron nitride formed from cubic boron nitride grains and a second phase material, and a second layer of polycrystalline cubic boron nitride bonded to the first layer, where the second layer is formed from cubic boron nitride grains having the same size as the grains forming the first layer. The second layer may include a second phase material different from the second phase material of the first layer. In one exemplary embodiment, the first layer includes from about 50% to about 80% by volume cubic boron nitride, a binder phase and a ceramic phase, where at least one of the binder and ceramic phases forms the second phase of the first layer. In a further exemplary embodiment, the second layer includes from about 80% to about 95% by volume cubic boron nitride, a metallic second phase and a binder phase.
- In another exemplary embodiment, a friction stir welding tool is provided having a base formed of a first material having cubic boron nitride grains, and a pin extending from the base. In the exemplary embodiment, the pin is formed from a second material including cubic boron nitride grains, where one of the first and second materials includes cubic boron nitride grains that are coarser than the cubic boron nitride grains of the other of the first and second materials. In another exemplary embodiment tool, the first and second materials include cubic boron nitride grains in the range of about 80% to about 95% by volume. In yet a further exemplary embodiment, each of the first and second materials includes at least one of a carbide and a nitride, and at least one of a ceramic and an oxide phase. In another exemplary embodiment, the second material includes cubic boron nitride grains having grain sizes in the range of about 10 microns to about 50 microns, and the first material includes cubic boron nitride grains having grains sizes in the range of about 2 microns to about 30 microns. In a further exemplary embodiment, the first material may include a metallic rich second phase. Furthermore the cubic boron nitride grains of the first material may be coarser than the cubic boron nitride grains of the second material. Alternatively, the cubic boron nitride grains of the first material may be finer than the cubic boron nitride grains of the second material.
- In another exemplary embodiment, a friction stir welding tool is provided including a base formed of a first material including cubic boron nitride grains and a second material including cubic boron nitride grains, and a pin extending from the base, the pin formed from the second material, where one of the first and second materials cubic boron nitride grains are coarser than the cubic boron nitride grains of the other of the first and second materials. In a further exemplary embodiment, the base includes a first portion including the first material and a second portion including the second material. The second portion may be a layer adjacent the first portion and the pin may extend from the second portion. The cubic boron nitride grains forming the second material may be coarser than the cubic boron nitride grains forming the first material. The second material may include cubic boron nitride grains in the range of about 80% to about 95% by volume.
- In an exemplary embodiment the second material includes at least one of a carbide and a nitride, and at least one of a ceramic and an oxide phase. Furthermore, the second material cubic boron nitride grains may have grain sizes in the range of about 10 microns to about 50 microns, and the first material cubic boron nitride grains may have grain sizes in the range of about 2 microns to about 30 microns. The first material may include cubic boron nitride grains in the range of about 50% to about 80% by volume.
- In a further exemplary embodiment, the pin and second portion may be integrally formed and the pin with second portion may be sintered to the first portion. In another exemplary embodiment, the second portion is concentric with the first portion. The first portion may circumferentially surround the second portion, and the pin may extend from the second portion. In yet another exemplary embodiment, the pin may be cylindrical having a diameter. The second portion may also be cylindrical having a diameter. The diameter of the second portion may be greater than the diameter of the pin. In another exemplary embodiment, the diameter of the second portion may be the same as the diameter of the pin.
- The first material may have a higher cubic boron nitride content than the first material. The second material may have cubic boron nitride grains in the range of about 80% to about 95% by volume. Furthermore, the second material may included at least one of a carbide and a nitride, and at least one of a ceramic and an oxide phase.
-
FIGS. 1-4 are partial cross-sectional schematic views of exemplary embodiment multilayered PCBN composite material of the present invention. -
FIG. 5 is a partial cross-sectional schematic view of an exemplary embodiment compact of the present invention having an exemplary embodiment functionally gradient PCBN composite material over a substrate. -
FIG. 6 is a partial cross-sectional schematic view of friction welding apparatus joining two pieces of metal. -
FIGS. 7-11 are cross-sectional schematic views of exemplary embodiment friction welding tools incorporating exemplary embodiment functionally gradient PCBN materials according to principles of the present invention. - The present invention provides for functionally gradient polycrystalline cubic boron nitride (PCBN) material and/or material composites which can be tailored for optimal combinations of strength, toughness, chemical wear and thermal stability, to tools incorporating such materials, and to methods of making the same. The exemplary embodiment materials may be used to form, or as part of, cutting tools or other types of tools subjected to wear.
- To prepare the functionally gradient PCBN materials, different layers of cBN may be used in particulate form along with a binder. In an exemplary embodiment, any of the layers can be in a high shear compaction (HSCTM) form which is well known in the art and is, for example, described in U.S. Pat. Nos. 5,766,394; 6,193,001 and 6,325,165. In such case, the high shear compaction layers may need to be heated in a vacuum to remove the organic binders. Whether using particulate stock feeds or high shear compaction layer(s), the layers of materials are sealed in an HPHT cell such as a refractory material cell and are subjected to HPHT PCBN sintering conditions for forming the functionally gradient PCBN material. Applicant was able to obtain improved bonding between the PCBN layers when using high shear compaction layers.
- Exemplary inventive PCBN material may be formed in a blank which can be cut and ground or finished to a desired shape and dimension. In an alternate exemplary embodiment, a substrate such as a cemented WC—Co substrate may also be added to the cell such that a compact, e.g., a cutting element, is formed having a WC—Co substrate and a functionally gradient layer of PCBN material. In other words, the inventive materials of the present invention may be used as self standing cutting tool materials or may be HPHT sintered on to a cemented WC—Co substrate to form a cutting element or tool.
- In one exemplary embodiment, a thin layer of Al2O3 is sintered during the HPHT process on to a PCBN matrix resulting in a PCBN layer having increased chemical wear resistance. In an alternate exemplary embodiment, a fine TiCN-rich material and/or a PCBN/TiCN—Al composite is HPHT sintered on to a coarse grain PCBN base achieving increased thermal stability and increased toughness. In yet a further exemplary embodiment, different cubic boron nitride (cBN) grain sizes and second phase materials are mixed for obtaining a PCBN material layer having tailored hardness and toughness. In other exemplary embodiments, including but not limited to the aforementioned exemplary embodiments, coarse cBN grains having a size in the range of about 2 to 30 microns are selected as necessary for obtaining the desired properties.
- It should be noted that the terms “coarse” and “fine” when used in reference to grain sizes are relative terms and should be interpreted such that a material having coarser grains has a median or an average grain size that is greater than the median or average grain size, respectively of material having finer grains.
- Following are provided some further exemplary embodiment material composites of the present invention.
- An exemplary embodiment multilayered PCBN composite with similar PCBN compositions but different cBN grain sizes in each layer is provided, as for example shown in
FIG. 1 . A fine-grain PCBN layer 10 with desirable thickness is HPHT sintered onto a coarse-grain PCBN center core 12. All layers are composed of similar or the same cBN and 2nd phase types and compositions. An exemplary embodiment composite may in one exemplary embodiment have three layers as shown inFIG. 1 where the fine-grain layers 10 sandwich the coarse-grain center layer 12, or only a single fine-grain layer 10 may be attached to one side of the a coarse-grain layer 12. Such an exemplary PCBN composite will be beneficial in applications demanding cutting tools having high toughness desirable for interrupted machining. Owing to the fine-grain PCBN microstructure of the outer layer(s), the outer cutting edges of this exemplary embodiment PCBN composite cutting tool possess higher strength and thus, are more resistant to wear allowing the tool to maintain a sharp edge achieving a higher surface finish through out the tool life. - This exemplary embodiment material composite, shown in
FIG. 2 , is also a multilayered PCBN composite with similar PCBN compositions but different cBN grain sizes in each layer. This exemplary embodiment material is opposite to the material described in Example A in that a coarse-grained PCBN layer 14 with desirable thickness is HPHT sintered onto a fine-grainPCBN center core 16 with all layers having similar or the same cBN and 2nd phase types and compositions. - An exemplary embodiment composite may in one exemplary embodiment have three layers as shown in
FIG. 2 where the coarse-grain layers 14 sandwich the fine-grain core orcenter layer 16 or only a single coarse-grain outer layer 14 attached to one side of a fine-graininner layer 16. This multilayered PCBN composite when used as a cutting tool will have a good combination of edge toughness and bulk strength which is beneficial when the cutting tool is used in rough machining operations providing for large material removal, where surface finish is less critical. This exemplary embodiment PCBN composite cutting tool will have an improved tool life in interrupted machining conditions. - In Examples A and B, the cBN contents in all PCBN layers can range from 50% to 95% by volume balanced with a metallic phase and a ceramic phase. The metallic and ceramic phases may in an exemplary embodiment be Co, Ni, Fe, WC, carbides and/or nitrides, as for example AlN, TiN, TiC, TiCN, carbides and/or nitrides of the IVB, VB and VIB elements of the Periodic Table of Elements. An oxide phase such as Al2O3, SiO2, TiO2 may also be present in the layers. The cBN grain size in the fine PCBN layer(s) in an exemplary embodiment ranges from less than 1 micron to about 10 microns and the cBN grain size in the coarser PCBN layer(s) ranges from about 2 to about 30 microns.
- This exemplary embodiment material composite is a multilayered composite with different layers having different PCBN compositions and/or sizes, as for example shown in
FIG. 3 . An exemplary embodiment includes a cBN-ceramic composite (e.g., a cBN layer with a ceramic binder phase)outer layer 20 and a high cBN volume and coarser cBN grain inner layer 22. An exemplary embodiment composite may in one exemplary embodiment have three layers as shown inFIG. 3 , where the cBN-ceramic compositeouter layers 20 sandwich the high cBN volume coarser cBN grain inner or center layer 22, or may have only a single cBN-ceramic compositeouter layer 20 attached to one side of the a high cBN volume coarser-grain inner layer 22. - In an exemplary embodiment material, the cBN content in the outer PCBN (cBN-ceramic composite) layers 20 ranges from about 50% to 80% by volume balanced with a metallic phase and a ceramic phase. The metallic phase may be Co, WC, Ni, Fe. The ceramic phase may include a carbide and/or nitride such as AlN, TiN, TiC, TiCN, and/or a carbide and/or nitride of the IVB, VB, and VIB elements of the Periodic Table of Elements, and combinations thereof. An oxide phase may be also present in the layers and may be a phase such as Al2O3, SiO2, TiO2. The inner PCBN layer 22 includes a higher volume cBN which in an exemplary embodiment is in a range of about 60% to about 95% by volume. The inner layer may be selectively balanced with a Co—WC rich 2nd phase. In other words, more than 50% by volume of the second phase comprises of Co—WC. Stated differently, when a phase is said to be a particular material rich, such phase comprises more than 50% of the particular material. The cBN grain size in the outer PCBN layers in an exemplary embodiment range from less than 1 micron to about 10 microns and the cBN grain size in the inner layer ranges from about 2 to about 30 microns.
- The exemplary material of this example when used as a cutting tool will have improved machining efficiency and toughness but still maintain a high chemical tool wear resistance. Moreover, when the inner PCBN layer is made of cBN and Co—WC metallic phase and the outer layer(s) is made of cBN and a ceramic binder phase, a compressive favorable residual stress to the outer PCBN layer will develop which will increase the tool life by delaying the crack nucleation and propagation. Furthermore, the combination of different cBN grain sizes and 2nd phase types incorporated in this exemplary material benefits not only from the different cBN grains sizes, as in Examples A and B, but also from different 2nd phases.
- Currently commercially available single-layer cBN-ceramic composites bonded on a carbide substrate which are used as cutting surfaces perform well in resisting chemical or diffusion wear but need more mechanical toughness and strength to achieve a higher cutting efficiency. Using a multilayered composite, such as the exemplary composite material of this example provides for improved mechanical toughness and strength while retaining chemical and diffusion wear resistance.
- This exemplary embodiment material composite is also a multilayered composite with different layers having different PCBN compositions, as for example shown in
FIG. 4 . This exemplary embodiment material composite is formed from comparable cBN grain-sized PCBN layers. However, different 2nd phase materials can also be HPHT sintered to the layers to form a cutting tool with a high chemical-tool-wear resistant outer layer or layers and very high mechanical strength inner layer. This exemplary embodiment composite may in one exemplary embodiment have twoouter layers 24 sandwiching an inner layer 26 as shown inFIG. 4 or have an outer layer over an inner layer. - In an exemplary embodiment composite of this example, the cBN content in the outer PCBN layer(s) 24 ranges from about 50% to about 80% by volume balanced with a binder phase and a ceramic phase. The binder phase or the ceramic phase may form the second phase of the material. The binder phase may be Co, Ni, Fe, WC. The ceramic phase may include a carbide and/or nitride such as AlN, TiN, TiC, TiCN and/or a carbide and/or nitride of the IVB, VB and VIB elements of the Periodic Table of Elements, and combinations thereof. An oxide phase may also be present in the outer PCBN layer(s) and may be a phase such as Al2O3, SiO2, TiO2. The inner PCBN layer 26 incorporates a similar cBN grain size as the outer layer(s) 24, but has a higher cBN content. In an exemplary embodiment the inner layer has a cBN content in the range from about 80% to 95% by volume which can be selectively balanced with a Co—WC rich metallic 2nd phase. The cBN grain sizes for both layers in an exemplary embodiment ranges from less than 1 micron to about 10 microns.
- Any of the aforementioned PCBN composites may be bonded or formed over a substrate, such as a cemented tungsten carbide substrate forming compacts. Such compacts have enhanced electro-discharge-machining (EDM) cut-ability and braze-ability allowing for brazing onto a variety of metallic tool carriers. Conventional PCBN materials without substrates typically do not have good EDM cut-ability or braze-ability.
- In an exemplary embodiment, to ensure better EDM cut-ability with conventional EDM setups, the PCBN composite may be formed from cBN having a grain size less than 10 microns. In one exemplary embodiment, as shown in
FIG. 5 , a two-layer PCBN composite 31, having aninner layer 30 and anouter layer 32 is formed over WC—Co substrate 28. In an exemplary embodiment, the cBN content for each of the PCBN layers formed over the substrate includes about 50% to about 95% volume cBN balanced with metallic phase and a binder phase. The metallic phase may be Co, Ni, Fe, WC. The binder phase may be included a carbide and/or nitride such as AlN, TiN, TiC, TiCN, and/or a carbide and/or nitride of the IVB, VB and VIB elements of the Periodic Table of Elements, and combinations thereof. An oxide phase such as Al2O3, SiO2, TiO2 may also be present in the layers. - The exemplary embodiment composite materials of the present invention may be also used to form various cutting tools, including cutting elements or inserts which are mounted on earth boring bits. However, the exemplary materials also have application in other types of tools, such as wear tools, as for example friction stir welding (FSW) tools. An
FSW tool 36 of aFSW apparatus 41 is shown inFIG. 6 . AnFSW tool 36 as shown inFIG. 6 mechanically joins twometallic materials FSW spindle 41 which “stirs” the materials to be joined. The FSW tool has a base 42 from which extends apin 44 which penetrates the materials to be joined and does the stirring. Because of different wear mechanisms induced by different geometries, linear speeds, and temperatures of the FSW tool, different localized failure modes are observed on different parts of the tool. Use of the inventive PCBN materials to form the FSW tool will result in a tool having enhanced resistance to the various tool wear mechanisms and increased tool life. Following are some exemplary embodiment FSW tools formed with the inventive material(s). - In this example, shown in
FIG. 7 , an FSW tool is made with a coarse grain-sized PCBN pin 44 and a finer grain-sized PCBN base 42 so that a combination of a higher toughness pin with a higher strength base is achieved. The cBN content in both the pin and base in an exemplary embodiment ranges from about 80% to about 95% by volume. The cBN content is balanced with carbides and/or nitrides such as AlN, TiN, TiC, TICN, carbides and/or nitrides of the IVB, VB and VIB elements of the Periodic Table of Elements and a ceramic or oxide phase such as Al2O3, SiO2, TiO2. In an exemplary embodiment, cBN grain size for the pin ranges from about 10 to about 50 microns and from about 2 to about 30 microns for the base. If a fine cBN grain and a metallic-rich 2nd phase PCBN composite is chosen for the base, a favorable compressive stress is generated in the pin which will delay the onset of mechanical wear damage, and thus, prolong the tool life. - In this example, an FSW tool is provided made with a coarse PCBN grade base and finer PCBN pin combination, as shown in
FIG. 8 . This exemplary FSW tool has greater toughness at thebase 42 and increased wear resistance at thepin 44 due to pin's higher mechanical strength. In this example, the cBN content in both the pin and base ranges from about 80% to 95% by volume balanced with a ceramic or oxide phase such as Al2O3, SiO2, TiO2, carbides and/or nitrides such as AlN, TiN, TiC, TiCN, and carbides and/or nitrides of the IVB, VB and VIB elements of the Periodic Table of Elements. In an exemplary embodiment, cBN grain size for the pin ranges from about 2 to about 30 microns and from about 10 to about 50 microns for the base. - In this example as shown in
FIG. 9 , the FSW has apin 44 and a layer 46 of the base 42 from which the pin extends made from a coarse and high volume cBN grade. Asecond layer 48 of the base adjacent layer 46 and opposite thepin 44 is made with a finer cBN and ceramic second-phase composite. The layer 46 withpin 44 is HPHT-sintered to thesecond layer 48. This FSW tool has a stronger and tougher PCBN grade forming the pin and thesurface 50 of the base layer 46 which will be in contact with the materials to be welded during the friction stir process. This FSW tool will have reduced heat losses from the FSW tool base to the spindle because of the lower CBN content in the base layer in contact with the spindle, consequently, increasing the FSW tool welding efficiency. In an exemplary embodiment, the cBN content in the pin and layer 46 of the base interfacing with the pin ranges from about 80% to about 95% by volume balanced with carbides and/or nitrides such as AlN, TiN, TiC, TiCN, carbides and/or nitrides of the IVB, VB and VIB elements of the Periodic Table of Elements, and with a ceramic or oxide phase such as Al2O3, SiO2, TiO2. In the exemplary embodiment, the cBN grain size in the pin and layer 46 ranges from about 10 to about 50 microns. The cBN content of thesecond layer 48 of the base, not in contact with the welded metals, ranges from about 50% to about 80% by volume and has a grain size from about 2 to 30 microns. - FSWs may also be formed from different PCBN grades which are HPHT-sintered concentrically so that desirable mechanical and thermal properties from the different PCBN grades can be optimized for different FSW requirements, as for example the requirements of the center pin, the portion of the base surrounding the pin, and the circumferential, or ring portion of the base. For example, as shown in
FIGS. 10 and 11 , theFSW tool base 42 may have anouter ring portion 51 surrounding a surroundedportion 52 from which extends thepin 44. In the exemplary embodiment shown inFIG. 10 , the base surroundedportion 52 has a diameter greater than the pin. In the exemplary embodiment shown inFIG. 11 , the base surroundedportion 52 has a diameter equal to the diameter of thepin 44. In an exemplary embodiment, the base surroundedportion 52 and pin have a higher cBN content than thering portion 51. Owing to the different thermal expansion coefficients of the different portions of these exemplary FSW tools and the temperature gradients to which they are subjected, favorable thermal stresses may develop which may apply beneficial compressive radial stresses towards to the center pin, therefore, delaying the mechanical wear damage and prolonging the tool life. - In the examples shown in
FIGS. 10 and 11 , the cBN content of the outerPCBN ring portion 51 ranges from about 50% to about 80% by volume balanced with carbides and/or nitrides such as AlN, TiN, TiC, TiCN, carbides and/or nitrides of the IVB, VB and VIB elements of the Periodic Table of Elements, a metallic phase such as Co, Ni, Fe, WC, and a ceramic or oxide phase such as Al2O3, SiO2, TiO2. The cBN content in the base surroundedportion 52 andpin 44 is in the range from about 60% to about 95% by volume, and is balanced with a ceramic binder phase with substantially less metal inclusions. In an exemplary embodiment, cBN grain size in the outerPCBN ring portion 51 ranges from about 2 to 30 microns and the cBN grain size in the surroundedportion 52 andpin 44 ranges from about 10 to about 50 microns. - In other exemplary embodiments, the base surrounded
portion 52 may be made from multiple PCBN layers forming a composite. In further exemplary embodiments, such a composite may be any of the aforementioned exemplary PCBN composites. Any of the aforementioned exemplary embodiment FSW tools may be integrally formed using well known sintering methods.
Claims (38)
1. A polycrystalline cubic boron nitride material comprising:
a first layer of polycrystalline cubic boron nitride formed from cubic boron nitride grains; and
a second layer of polycrystalline cubic boron nitride bonded to the first layer, wherein the second layer is formed from cubic boron nitride grains which are coarser than the cubic boron nitride grains forming the first layer.
2. A material as recited in claim 1 further comprising a third layer of polycrystalline cubic boron nitride formed from cubic boron nitride grains which are finer than the grains of cubic boron nitride forming the second layer.
3. A material as recited in claim 2 wherein the second layer is sandwiched between the first and third layers.
4. A material as recited in claim 3 wherein the first and third layers are made of the same material.
5. A material as recited in claim 3 wherein the first and third layers comprise the same type of cubic boron nitride and the same second phase compositions.
6. A material as recited in claim 5 wherein the first and third layers comprise a ceramic binder phase.
7. A material as recited in claim 1 further comprising a third layer of polycrystalline cubic boron nitride formed from cubic boron nitride grains which are coarser than the grains of cubic boron nitride forming the first layer.
8. A material as recited in claim 7 wherein the first layer is sandwiched between the second and third layers.
9. A material as recited in claim 8 wherein the second and third layers are made of the same material.
10. A material as recited in claim 8 wherein the second and third layers comprise the same type of cubic boron nitride and the same second phase compositions.
11. A material as recited in claim 8 wherein the second and third layers comprise a ceramic binder phase.
12. A material as recited in claim 11 wherein the second and third layers each comprise about 50% to about 80% by volume cubic boron nitride with the balance comprising a metallic phase and the ceramic phase.
13. A material as recited in claim 12 wherein the metallic phase comprises a material selected from the group of materials consisting of Co, Ni, Fe, and Wc.
14. A material as recited in claim 12 wherein the ceramic phase comprises at least one of a carbide and a nitride.
15. A material as recited in claim 14 wherein said carbide and nitride are selected from the group consisting of AIN, TiN, TiC, TiCN and carbides or nitrides of the IVB, VB and VIB elements of the Periodic Table of Elements, and combinations thereof.
16. A material as recited in claim 12 wherein the second and third layers further comprise an oxide phase.
17. A material as recited in claim 12 wherein the oxide phase comprises a composition consisting of Al2O3, SiO2 and TiO2.
18. A material as recited in claim 12 wherein the first layer comprises about 60% to about 95% by volume cubic boron nitride.
19. A material as recited in claim 1 wherein each layer comprises cubic boron nitride in the range of about 50% to about 95% by volume, a metallic phase and a ceramic phase.
20. A material as recited in claim 19 wherein the metallic phase comprises a material selected from the group of materials consisting of Co, Ni, Fe, and Wc.
21. A material as recited in claim 19 wherein the ceramic phase comprises at least one of a carbide and a nitride.
22. A material as recited in claim 21 wherein said carbide and nitride are selected from the group consisting of AIN, TiN; TiC, TiCN and carbides or nitrides of the IVB, VB and VIB elements of the Periodic Table of Elements, and combinations thereof.
23. A material as recited in claim 19 wherein each layer further comprises an oxide phase.
24. A material as recited in claim 23 wherein the oxide phase comprises a composition consisting of Al2O3, SiO2 and TiO2.
25. A material as recited in claim 1 wherein the first layer is formed from cubic boron nitride grains having a size in the range of less than 1 micron to about 10 microns.
26. A material as recited in claim 1 wherein the second layer is formed from cubic boron nitride grains having a size in the range of about 2 microns to about 30 microns.
27. A material as recited in claim 1 wherein at least one of the layers comprises a ceramic binder phase.
28. A material as recited in claim 1 further comprising a carbide substrate bonded to at least one of said first and second layers
29. A polycrystalline cubic boron nitride material comprising:
a first layer of polycrystalline cubic boron nitride formed from cubic boron nitride grains and a second phase material; and
a second layer of polycrystalline cubic boron nitride bonded to the first layer, wherein the second layer is formed from cubic boron nitride grains having the same size as the grains forming the first layer, and wherein the second layer comprises a second phase material different from the second phase material of the first layer.
30. A material as recited in claim 29 wherein the first layer comprises from about 50% to about 80% by volume cubic boron nitride, a binder phase and a ceramic phase, wherein at least one of said binder and ceramic phases forms said second phase of said first layer.
31. A material as recited in claim 30 wherein the binder phase comprises a material selected from the group of materials consisting of Co, Ni, Fe, and Wc.
32. A material as recited in claim 30 wherein the ceramic phase comprises at least one of a carbide and a nitride.
33. A material as recited in claim 32 wherein said carbide and nitride are selected from the group consisting of AIN, TiN, TiC, TiCN and carbides or nitrides of the IVB, VB and VIB elements of the Periodic Table of Elements, and combinations thereof.
34. A material as recited in claim 30 wherein the second layer comprises from about 80% to about 95% by volume cubic boron nitride and a metallic second phase.
35. A material as recited in claim 29 wherein the second layer comprises from about 80% to about 95% by volume cubic boron nitride and a metallic second phase.
36. A material as recited in claim 35 wherein the metallic phase comprises a material selected from the group of materials consisting of Co, Ni, Fe, and Wc.
37. A material as recited in claim 29 wherein sizes of the cubic boron nitride grains forming each of the first and the second layers range from about 1 micron to about 10 microns.
38. A material as recited in claim 29 further comprising a carbide substrate bonded to at least one of said first and second layers