US20060189020A1 - Method for manufacturing nitride based single crystal substrate and method for manufacturing nitride based light emitting diode using the same - Google Patents
Method for manufacturing nitride based single crystal substrate and method for manufacturing nitride based light emitting diode using the same Download PDFInfo
- Publication number
- US20060189020A1 US20060189020A1 US11/214,685 US21468505A US2006189020A1 US 20060189020 A1 US20060189020 A1 US 20060189020A1 US 21468505 A US21468505 A US 21468505A US 2006189020 A1 US2006189020 A1 US 2006189020A1
- Authority
- US
- United States
- Prior art keywords
- nitride
- layer
- zno
- temperature
- single crystal
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Abandoned
Abstract
A method for manufacturing a nitride based single crystal substrate and a method for manufacturing a nitride based light emitting diode using the same. The method for manufacturing the nitride based single crystal substrate includes forming a ZnO layer on a base substrate; forming a low-temperature nitride buffer layer on the ZnO layer using dimethyl hydragine (DMHy) as an N source; growing a nitride single crystal on the low-temperature nitride buffer layer; and separating the nitride single crystal from the base substrate by chemically eliminating the ZnO layer.
Description
- The present application is based on, and claims priority from, Korean Application Number 2005-0014424, filed Feb. 22, 2005, the disclosure of which is incorporated by reference herein in its entirety.
- 1. Field of the Invention
- The present invention relates to a method for manufacturing a nitride based single crystal substrate, and more particularly to a method for manufacturing a nitride based single crystal substrate using a ZnO layer and a method for manufacturing a nitride based light emitting diode using the same.
- 2. Description of the Related Art
- Generally, a gallium nitride single crystal is manufactured on a substrate made of a material differing from the gallium nitride single -crystal by vapor growth, such as metal organic chemical vapor deposition (MOCVD) or hydride vapor phase epitaxy (HVPE), or molecular beam epitaxy (MBE).
- Here, a sapphire (α-Al2O3) substrate or a SiC substrate is used as the above substrate. The substrate may be cracked by a difference of lattice constants between the substrate and the gallium nitride single crystal and a difference of thermal expansion coefficients between the substrate and the gallium nitride single crystal. For example, since a difference of lattice constants between sapphire and gallium nitride is approximately 13% and a difference of thermal expansion coefficients between sapphire and gallium nitride is −34%, stress is applied on an interface between the sapphire substrate and the gallium nitride single crystal. Since a temperature at which a nitride layer is grown on the substrate is high, the thermal stress caused by a high difference of thermal expansion coefficients therebetween generates the cracks of the substrate and the gallium nitride single crystal.
- In order to solve the above problem, two methods have been proposed. One method is that a nitride single crystal is manufactured on a substrate made of a nitride based material using a freestanding nitride based single crystal substrate, and the other method is that a nitride based light emitting structure is separated from a substrate made of a material differing from the nitride single crystal. Here, the freestanding nitride based single crystal substrate is obtained by forming a nitride single crystal on a substrate made of a material differing from the nitride single crystal and then separating the nitride single crystal from the substrate. Accordingly, the above two methods require a technique for separating the nitride single crystal (or the nitride based light emitting structure) from the substrate made of a material differing from nitride.
- A laser lift off process is conventionally used to separate the nitride single crystal from the substrate. In the laser lift off process, as shown in
FIG. 1 , a laser beam is irradiated so that a GaN basedsingle crystal bulk 15 is separated from asapphire substrate 11 by decomposing the GaN basedsingle crystal bulk 15, located on an interface between thesapphire substrate 11 and the GaN basedsingle crystal bulk 15, into gallium (Ga) and nitride (1/2N2). - However, when a crystal having a diameter of 2 inches or more or a designated thickness or more is grown on the a substrate, the laser lift off process causes severe warpage and cracks (C) of the substrate and the crystal due to a difference of lattice constants therebetween and a difference of thermal expansion coefficients therebetween.
- Another conventional technique is that ZnO is used as a buffer layer for growing a nitride crystal. Since a difference of lattice constants between a ZnO single crystal oriented along the c-axis and GaN is only 2% and the ZnO single crystal has a wurzite structure the same as that of GaN, the ZnO single crystal facilitates the growth of a nitride crystal and is eliminated by conventional wet etching, thus being advantageously used in separation of the nitride crystal from the substrate. However, since the ZnO single crystal is thermally and chemically unstable and is easily decomposed even at a relatively low temperature (approximately 500° C.), there is a limit to substantially apply the ZnO single crystal to a step of growing the nitride single crystal performed at a high temperature.
- Therefore, the present invention has been made in view of the above problems, and it is an object of the present invention to provide a method for manufacturing a nitride based single crystal substrate, in which a low-temperature nitride buffer layer is formed under the condition that a ZnO single crystal layer is not decomposed so that a high-quality crystal based on the ZnO single crystal layer is grown, and a method for manufacturing a nitride based light emitting diode using the same.
- It is another object of the present invention to provide a method for manufacturing a nitride based single crystal substrate, in which a seed for a nano pattern is formed from a ZnO polycrystalline layer on an additional sacrificial layer and is then used to grow a nitride single crystal, and a method for manufacturing a nitride based light emitting diode using the same.
- In accordance with one aspect of the present invention, the above and other objects can be accomplished by the provision of a method for manufacturing a nitride based single crystal substrate comprising: forming a ZnO layer on a base substrate; forming a low-temperature nitride buffer layer on the ZnO layer using dimethyl hydragine (DMHy) as an N source; growing a nitride single crystal on the low-temperature nitride buffer layer; and separating the nitride single crystal from the base substrate by chemically eliminating the ZnO layer.
- Preferably, the formation of the low-temperature nitride buffer layer may be performed at a temperature of less than approximately 400° C. so as to sufficiently prevent pyrolysis of the ZnO layer. Such a low temperature is employed by using dimethyl hydragine (DMHy) as the N source.
- In this aspect, the base substrate may be made of one selected from the group consisting of sapphire, SiC, and silicon, and the low-temperature nitride buffer layer may satisfy the composition of AlxGayIn1-x-yN (Here, 0≦x≦1 and 0≦y≦1).
- In accordance with a -further aspect of the present invention, there is provided a method for manufacturing a nitride based single crystal substrate comprising: forming a sacrificial layer made of an oxide film or a nitride film on a base substrate; forming a ZnO layer in a polycrystalline state on the sacrificial layer; forming a nano-sized ZnO pattern by partially decomposing the ZnO layer; forming a low-temperature nitride buffer layer using the ZnO pattern as a seed; growing a nitride single crystal on the low-temperature nitride buffer layer; and separating the nitride single crystal from the base substrate by chemically eliminating the sacrificial layer.
- In this aspect, the base substrate may be made of one selected from the group consisting of sapphire, SiC, and silicon,, and the low-temperature nitride buffer layer may satisfy the composition of AlxGayIn1-x-yN (Here, 0≦x≦1 and 0≦y≦1).
- Preferably, the formation of the nano-sized ZnO pattern is performed by pyrolysis performed at a temperature at which the low-temperature nitride buffer layer is grown, and the formation of the low-temperature nitride buffer layer may be performed at a temperature of 400˜700° C.
- Further, preferably, in the separation of the nitride single crystal from the base substrate, the ZnO pattern may be eliminated together with the elimination of the sacrificial layer so that the surface of the nitride single crystal, from which the ZnO pattern is separated, has an uneven pattern.
- In accordance with another aspect of the present invention, there is provided a method for manufacturing a nitride based light emitting diode, particularly a vertical-structured light emitting diode.
- The method comprises forming a ZnO layer on a base substrate; forming a first conductivity type low-temperature nitride buffer layer on the ZnO layer using dimethyl hydragine (DMHy) as an N source; forming a light emitting structure including a first conductivity type nitride layer, an active layer, and a second conductivity type layer on the low-temperature nitride buffer layer; and separating the light emitting structure from the base substrate by chemically eliminating the ZnO layer.
- Preferably, the formation of the low-temperature nitride buffer layer may be performed at a temperature of less than approximately 400° C.
- In accordance with yet another aspect of the present invention, there is provided a method for manufacturing a nitride based light emitting diode comprising: forming a sacrificial layer made of an oxide film or a nitride film on a base substrate; forming a ZnO layer in a polycrystalline state on the sacrificial layer; forming a nano-sized ZnO pattern by partially decomposing the ZnO layer; forming a first conductivity type low-temperature nitride buffer layer using the ZnO pattern as a seed; forming a light emitting structure including a first conductivity type nitride layer, an active layer, and a second conductivity type nitride layer on the low-temperature nitride buffer layer; and separating the light emitting structure from the base substrate by chemically eliminating the sacrificial layer.
- In this aspect, in the separation of the nitride single crystal from the base substrate, the ZnO pattern is eliminated together with the elimination of the sacrificial layer so that the surface of the nitride single crystal, from which the ZnO pattern is separated, has an uneven pattern. The uneven pattern greatly improves the light-extracting efficiency of the light emitting diode.
- The above and other objects, features and other advantages of the present invention will be more clearly understood from the following detailed description taken in conjunction with the accompanying drawings, in which:
-
FIG. 1 is a sectional view illustrating the conventional separation of a GaN based single crystal bulk from a sapphire substrate using a laser beam; -
FIGS. 2A to 2D are sectional views illustrating a method for manufacturing a nitride based single crystal substrate in accordance with one embodiment of the present invention; -
FIGS. 3A to 3F are sectional views illustrating a method for manufacturing a nitride based single crystal substrate in accordance with another embodiment of the present invention; and -
FIGS. 4A to 4C are sectional views illustrating a method for manufacturing a nitride based light emitting diode of the present invention. - Now, preferred embodiments of the present invention will be described in detail with reference to the annexed drawings.
-
FIGS. 2A to 2D are sectional views illustrating a method for manufacturing a nitride based single crystal substrate in accordance with one embodiment of the present invention. - As shown in
FIG. 2A , the method in accordance with this embodiment begins with formation of aZnO layer 23 on abase substrate 21. Although a sapphire substrate is mainly used as thebase substrate 21, a SiC substrate or a silicon substrate may be used as thebase substrate 21. TheZnO layer 23 is formed on thebase substrate 21, such as a sapphire substrate, by a publicly-known deposition process, such as sputtering. Preferably, theZnO layer 23 is a layer made of a ZnO single crystal oriented along the c-axis. A difference of lattice constants between theZnO layer 23 and a nitride single crystal is smaller than a difference of lattice constants between the sapphire substrate and the nitride single crystal, and theZnO layer 23 has the same wurzite structure as that of the nitride single crystal. Accordingly, the ZnOlayer 23 facilitates growth of a high-quality nitride crystal thereon. However, in the present invention, since a low-temperature nitride buffer layer (24 ofFIG. 2B ) is provided on theZnO layer 23, theZnO layer 23 may not require complete single crystal. - Thereafter, as shown in
FIG. 2B , the low-temperaturenitride buffer layer 24 is formed on theZnO layer 23 using dimethyl hydragine (DMHy) (N2H2(CH3)2) as an N source. The low-temperaturenitride buffer layer 24 satisfies the composition of AlxGayIn1-x-yN (Here, 0≦x≦1 and 0≦y≦1). When such a low-temperaturenitride buffer layer 24 is formed, Trimethyl aluminum (TMAl), trimethyl gallium (TMGa), and trimethyl indium (TMIn) are respectively used as Al, Ga, and In sources. For example, TMGa is decomposed even at a temperature of 300° C., thus being used under the condition that theZnO layer 23 is not decomposed. Here, since ammonia (NH3) used as the N source has high binding energy, the low-temperaturenitride buffer layer 24 requires a growth temperature of at least 500° C. However, theZnO layer 23 is easily decomposed at the above growth temperature. In order to solve such a problem, dimethyl hydragine (DMHy) is-used as the N source-for growing the low-temperaturenitride buffer layer 24. When dimethyl hydragine (DMHy) is used as the N source, the low-temperaturenitride buffer layer 24 is formed at a temperature of less than 400° C., and it is possible to prevent pyrolysis of theZnO layer 23 during the formation of the low-temperaturenitride buffer layer 24. - Thereafter, as shown in
FIG. 2C , a nitridesingle crystal 25 is grown on the low-temperaturenitride buffer layer 24. Since the low-temperaturenitride buffer layer 24 is formed on theZnO layer 23 having a difference of lattice constants lower than that of the sapphire substrate (particularly, when theZnO layer 23 is made of a single crystal), the low-temperaturenitride buffer layer 24 has a higher quality than that of a buffer layer directly formed on the sapphire substrate. Accordingly, the nitridesingle crystal 25 grown at a high temperature has more improved crystallinity. Although theZnO layer 23 is partially decomposed under high-temperature conditions, since the nitridesingle crystal 25 is formed on the low-temperaturenitride buffer layer 24, the decomposition of theZnO layer 23 does not affect the growth of the nitridesingle crystal 25. - Finally, as shown in
FIG. 2D , the nitridesingle crystal 25 is separated from thebase substrate 21 by chemically eliminating theZnO layer 23. Since ZnO is chemically unstable as described above, theZnO layer 23 may be easily eliminated by a conventional chemical step, such as wet etching. Through the elimination of theZnO layer 23, the desired nitridesingle crystal 25 can be separated from thebase substrate 21. Such a separation step using the wet etching is easily applied to a mass-production process compared to the conventional laser lift off step, and is applicable to a wafer having a large diameter. The obtained nitridesingle crystal 25 is used as a freestanding nitride based single crystal substrate. - In the method for manufacturing the nitride based single crystal substrate of the present invention, a vertically-structured nitride based light emitting diode is manufactured by dividing the step of forming the nitride
single crystal 25 into sub-steps of forming a first conductivity-type nitride layer, an active layer, and a second conductivity type nitride layer. In this case, since thenitride buffer layer 24 remains on the lower surface of the finally obtained nitridesingle crystal 25, in order to manufacture the vertically-structured nitride based light emitting diode, thenitride buffer layer 24 is doped with a first conductivity type impurity. - The above embodiment provides a method for manufacturing a nitride based single crystal substrate using the
ZnO layer 23 as a sacrificial layer for the separation step. Differently from this embodiment, another embodiment of the present invention provides a method for manufacturing a nitride based single crystal substrate, which uses another or an additional sacrificial layer made of an oxide film or a nitride film, and partially decomposes a ZnO layer made of a polycrystal to form a seed for growing a nitride single crystal. -
FIGS. 3A to 3F are sectional views illustrating a method for manufacturing a nitride based single crystal substrate in accordance with another embodiment of the present invention. - As shown in
FIG. 3A , asacrificial layer 32, such as an oxide film or a nitride film, is formed on abase substrate 31. Although a sapphire substrate is mainly used as thebase substrate 31, a SiC substrate or a silicon substrate may be used as thebase substrate 31. Thesacrificial layer 32 is made of SiO2 or SiNx, but is not limited thereto so long as thesacrificial layer 32 is made of amorphous material which is easily etched. - Thereafter, as shown in
FIG. 3B , aZnO layer 33 made of a polycrystal is formed on thesacrificial layer 32. TheZnO layer 33 is formed on thebase substrate 31, such as the sapphire substrate, by a publicly-known deposition step, such as sputtering. Here, since thesacrificial layer 32 is amorphous, theZnO layer 33 is not grown in a single crystal state, but is grown in a polycrystalline state. - As shown in
FIG. 3C , theZnO layer 33 is partially decomposed so that a nano-sized ZnO pattern 33′ is formed. The above partial decomposition of theZnO layer 33 is achieved by a thermal or chemical method. Preferably, the partial decomposition of theZnO layer 33 is continuously performed in a chamber by applying a temperature at which theZnO layer 33 is decomposable in a subsequent step of forming a nitride buffer layer. The nano-sized ZnO pattern 33′ obtained by the above decomposition is irregular, and serves as a seed when a low-temperature nitride buffer layer (34 ofFIG. 3D ) is grown. - Thereafter, as shown in
FIG. 3D , the low-temperaturenitride buffer layer 34 is formed using theZnO pattern 33′. The low-temperaturenitride buffer layer 34 may be made of the same material as that of the low-temperaturenitride buffer layer 24 of the preceding embodiment, which satisfies the composition of AlxGayIn1-x-yN (Here,0≦x≦1 and 0≦y≦1). In the case that the nano-sized ZnO pattern 3′ is formed by pyrolysis in this embodiment, the formation of the low-temperaturenitride buffer layer 34 is performed at a temperature of at least 400° C., thus not requiring any additional step of forming the seed. In order to perform the above pyrolysis, preferably, the formation of the low-temperaturenitride buffer layer 34 is performed at a temperature of 400˜700° C. - Then, as shown in
FIG. 3E , a nitridesingle crystal 35 is grown on the low-temperaturenitride buffer layer 34. Although high-temperature conditions are applied to this step, since the low-temperaturenitride buffer layer 34 is formed on theZnO pattern 33′, the high-temperature conditions do not affect theZnO pattern 33′. - Finally, as shown in
FIG. 3F , the nitridesingle crystal 35 is separated from thebase substrate 31 by chemically eliminating thesacrificial layer 32. The elimination of thesacrificial layer 32 is easily achieved by wet etching. Here, preferably, theZnO pattern 33′ is eliminated together with the elimination of thesacrificial layer 32. Since ZnO is chemically unstable, theZnO pattern 33, is easily eliminated together with the elimination of thesacrificial layer 32. The obtained nitridesingle crystal 35 is used as a freestanding nitride based single crystal substrate. - This embodiment is beneficially applied to the manufacture of a vertically-structured nitride based light emitting diode. Particularly, the surface of the obtained nitride
single crystal 35, from which theZnO pattern 33′ serving as the seed is separated, has an irregularly uneven pattern (P), thus greatly improving light=extracting efficiency. -
FIGS. 4A to 4C are sectional views illustrating a method for manufacturing a nitride based light emitting diode of the present invention. This method uses the method for manufacturing the nitride based single crystal substrate as shown inFIGS. 3A to 3F. -
FIG. 4A illustrates abase substrate 41, on which asacrificial layer 42 made of an oxide film or a nitride film, a nano-sized ZnO pattern 43, a first conductivity typenitride buffer layer 44, and a light emitting structure are sequentially formed. Here, the light emitting structure includes a first conductivitytype nitride layer 45, anactive layer 46, and a second conductivitytype nitride layer 47. In this method, a process for obtaining the structure of thebase substrate 41 shown inFIG. 4A is omitted, but the process shown inFIGS. 3A to 3C is used. However, in this method, in order to obtain a vertically-structured light emitting diode, anitride buffer layer 44, which is doped with a first conductivity type impurity, is formed. - Thereafter, as shown in
FIG. 4B , the light emitting structure is separated from thebase substrate 41 by chemically eliminating thesacrificial layer 42. The low-temperaturenitride buffer layer 44 is formed on the lower surface of the separated light emitting structure. Here, the ZnO pattern, 43 is eliminated together with the elimination of thesacrificial layer 42, and the surface of the obtained light emitting structure, from which theZnO pattern 43 is separated, has an irregularly uneven pattern(P). The uneven pattern (P) formed on the surface of the light emitting structure reduces a critical angle at which light is extracted, thereby greatly improving light-extracting efficiency. The present invention is advantageous in that the uneven pattern (P) is easily obtained by the nitride growth step and the nitride separation step without any additional pattern formation step. - Finally, as shown in
FIG. 4C , afirst electrode 48 and asecond electrode 49 are respectively formed on upper and lower surfaces of the obtained light emitting structure, thereby completing the manufacture of a desired vertically-structured light emitting diode. The vertically-structured light emitting diode has an improved current distribution effect, compared to a light emitting diode, in which twoelectrodes ZnO pattern 43 and the elimination of theZnO pattern 43. - As apparent from the above description, the present invention provides a method for manufacturing a high-quality nitride based single crystal substrate, which uses a ZnO layer as a sacrificial layer or uses an additional sacrificial layer and a nano-sized ZnO pattern under the condition that the decomposition of ZnO is prevented during the growth of nitride, and easily performs the separation of the nitride from a base substrate. Further, the present invention provides a method for manufacturing a vertically-structured light emitting diode having improved light-extracting efficiency.
- Although the preferred embodiments of the present invention have been disclosed for illustrative purposes, those skilled in the art will appreciate that various modifications, additions and substitutions are possible, without departing from the scope and spirit of the invention as disclosed in the accompanying claims.
Claims (20)
1. A method for manufacturing a nitride based single crystal substrate comprising:
forming a ZnO layer on a base substrate;
forming a low-temperature nitride buffer layer on the ZnO layer using dimethyl hydragine (DMHy) as an N source;
growing a nitride single crystal on the low-temperature nitride buffer layer; and
separating the nitride single crystal from the base substrate by chemically eliminating the ZnO layer.
2. The method as set forth in claim 1 , wherein the base substrate is made of one selected from the group consisting of sapphire, SiC, and silicon.
3. The method as set forth in claim 1 , wherein the low-temperature nitride buffer layer satisfies the composition of AlxGayIn1-x-yN (Here, 0≦x1 and 0≦y≦1).
4. The method as set forth in claim 1 , wherein the formation of the low-temperature nitride buffer layer is performed at a temperature of less than approximately 400° C.
5. A method for manufacturing a nitride based single crystal substrate comprising:
forming a sacrificial layer made of an oxide film or a nitride film on a base substrate;
forming a ZnO layer in a polycrystalline state on the sacrificial layer;
forming a nano-sized ZnO pattern by partially decomposing the ZnO layer;
forming a low-temperature nitride buffer layer using the ZnO pattern as a seed;
growing a nitride single crystal on the low-temperature nitride buffer layer; and
separating the nitride single crystal from the base substrate by chemically eliminating the sacrificial layer.
6. The method as set forth in claim 5 , wherein the base substrate is made of one selected from the group consisting of sapphire, SiC, and silicon.
7. The method as set forth in claim 5 , wherein the low-temperature nitride buffer layer satisfies the composition of AlxGayIn1-x-yN (Here, 0≦x1 and 0≦y≦1).
8. The method as set forth in claim 5 , wherein the formation of the nano-sized ZnO pattern is performed by pyrolysis performed at a temperature at which the low-temperature nitride buffer layer is grown.
9. The method as set forth in claim 8 , wherein the formation of the low-temperature nitride buffer layer is performed at a temperature of 400˜700° C.
10. The method as set forth in claim 5 , wherein, in the separation of the nitride single crystal from the base substrate, the ZnO pattern is eliminated together with the elimination of the sacrificial layer so that the surface of the nitride single crystal, from which the ZnO pattern is separated, has an uneven pattern.
11. A method for manufacturing a nitride based light emitting diode comprising:
forming a ZnO layer on a base substrate;
forming a first conductivity type low-temperature nitride buffer layer on the ZnO layer using dimethyl hydragine (DMHy) as an N source;
forming a light emitting structure including a first conductivity type nitride layer, an active layer, and a second conductivity type layer on the low-temperature nitride buffer layer; and
separating the light emitting structure from the base substrate by chemically eliminating the ZnO layer.
12. The method as set forth in claim 11 , wherein the base substrate is made of one selected from the group consisting of sapphire, SiC, and silicon.
13. The method as set forth in claim 11 , wherein the low-temperature nitride buffer layer satisfies the composition of AlxGayIn1-x-yN (Here, 0≦x1 and 0≦y≦1).
14. The method as set forth in claim 11 , wherein the formation of the low-temperature nitride buffer layer is performed at a temperature of less than approximately 400° C.
15. A method for manufacturing a nitride based light emitting diode comprising:
forming a sacrificial layer made of an oxide film or a nitride film on a base substrate;
forming a ZnO layer in a polycrystalline state on the sacrificial layer;
forming a nano-sized ZnO pattern by partially decomposing the ZnO layer;
forming a first conductivity type low-temperature nitride buffer layer using the ZnO pattern as a seed;
forming a light emitting structure including a first conductivity type nitride layer, an active layer, and a second conductivity type nitride layer on the low-temperature nitride buffer layer; and
separating the light emitting structure from the base substrate by chemically eliminating the sacrificial layer.
16. The method as set forth in claim 15 , wherein the base substrate is made of one selected from the group consisting of sapphire, SiC, and silicon.
17. The method as set forth in claim 15 , wherein the low-temperature nitride buffer layer satisfies the composition of AlxGayIn1-x-yN (Here, 0≦x1 and 0≦y≦1).
18. The method as set forth in claim 15 , wherein the formation of the nano-sized ZnO pattern is performed by pyrolysis performed at a temperature at which the low-temperature nitride buffer layer is grown.
19. The method as set forth in claim 18 , wherein the formation of the low-temperature nitride buffer layer is performed at a temperature of 400˜700° C.
20. The method as set forth in claim 15 , wherein, in the separation of the nitride single crystal from the base substrate, the ZnO pattern is eliminated together with the elimination of the sacrificial layer so that the surface of the nitride single crystal, from which the ZnO pattern is separated, has an uneven pattern.