US20060292862A1 - Method for forming barrier metal of semiconductor device - Google Patents

Method for forming barrier metal of semiconductor device Download PDF

Info

Publication number
US20060292862A1
US20060292862A1 US11/512,085 US51208506A US2006292862A1 US 20060292862 A1 US20060292862 A1 US 20060292862A1 US 51208506 A US51208506 A US 51208506A US 2006292862 A1 US2006292862 A1 US 2006292862A1
Authority
US
United States
Prior art keywords
layer
tisin
forming
gas
sih
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Abandoned
Application number
US11/512,085
Inventor
Han-Choon Lee
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
DB HiTek Co Ltd
Original Assignee
Dongbu Electronics Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Dongbu Electronics Co Ltd filed Critical Dongbu Electronics Co Ltd
Priority to US11/512,085 priority Critical patent/US20060292862A1/en
Assigned to DONGBU ELECTRONICS CO., LTD. reassignment DONGBU ELECTRONICS CO., LTD. ASSIGNMENT OF ASSIGNORS INTEREST (SEE DOCUMENT FOR DETAILS). Assignors: LEE, HAN-CHOON
Publication of US20060292862A1 publication Critical patent/US20060292862A1/en
Abandoned legal-status Critical Current

Abstract

A method for forming a barrier metal of a semiconductor device includes forming an insulating layer on a semiconductor substrate and forming an opening in the insulating layer and forming a TiSiN layer having a desired thickness by repeatedly performing a process of forming a TiSiN layer having an atomic layer thickness in a reaction chamber. The process of forming a TiSiN layer having an atomic layer thickness includes performing deposition of a SiH4 layer inside the opening and on the insulating layer using an atomic layer deposition process, discharging a gas remaining in the reaction chamber by using an inert gas, performing deposition of a certain precursor layer on the SiH4 layer, and discharging a gas of precursor material remaining in the reaction chamber by using an inert gas. The method of forming a barrier metal further includes performing plasma processing for the TiSiN layer so as to remove impurities contained in the TiSiN layer.

Description

    CROSS REFERENCE TO RELATED APPLICATIONS
  • This application is a divisional of U.S. application Ser. No. 10/725,381, filed Dec. 3, 2003, which claimed priority to Korean Application 10-2002-0080010, filed Dec. 14, 2002, the entire contents of both applications being incorporated herein by reference.
    • BACKGROUND OF THE INVENTION
  • 1. Field of the Invention
  • The present invention relates to a method for forming a barrier metal of a semiconductor device, particularly for forming a thick layer of TiSiN for a barrier metal having a low resistivity, using an atomic layer deposition (ALD) process.
  • 2. Description of the Prior Art
  • Generally, with high integration of semiconductor devices, a design rule also becomes elaborated, and thus a size of a source/drain and a line width of a gate electrode of a MOS transistor and a line width of metallization become diminished. In particular, when the line width of the metallization is diminished, a size of a contact hole is also diminished, in which the contact hole is either for contacting the gate electrode and the metallization or for contacting the source/drain and the metallization. If so, since contact resistances of the gate electrode and the metallization are incased, a resistance of the metalization is increased. Consequently, an operation speed of the semiconductor device is delayed. Nevertheless, it is true that a demand for speedup of the semiconductor device is more enhanced together with its high integration.
  • As one scheme for satisfying this demand, a layer of a high fusion metal, e.g. tungsten (W) has been recently used to reduce the contact resistance. Further, in order to reduce contact resistances of the tungsten layer and the contact region, a barrier metal is formed between the tungsten layer and the contact region. Among the barrier metals, it is a TiSiN layer that is considered as one having an excellent characteristic. However, the TiSiN layer is generally layered by a sputtering process, thus having a very high resistivity. As a result, the TiSiN layer has no choice but to have limited application as the barrier metal. Recently, in order to solve this problem, a method for forming a new layer of TiSiN has been proposed.
  • According to a conventional method for forming a layer of TiSiN, as shown in FIGS. 1 to 3, an insulating layer 11 is formed on a semiconductor substrate 10. Here, even though not shown in the drawings, it is apparent to those skilled in the art that, in order to define an active region of the substrate 10, a field oxide layer may be formed on a field region of the substrate 10, while a source/drain, a gate electrode, etc. of a transistor may be previously formed on the active region of the substrate 10. Subsequently, in order to expose a contact part (not shown) of the semiconductor substrate 10 using a photolithography process, the insulating layer 11 on the contact part of the semiconductor substrate 10 is etched to form a contact hole 12. Next, a precursor layer 13, for exampleatetakis dimethyl amido titanium (“TDMAT”) layer is layered inside the contact hole 12 and on the insulating layer 11 at a desired thickness. Then, the precursor layer 13 is plasma processed and transformed into a TN layer 15. Finally, the surface of the TiN layer 15 is brought into a repetitive contact with a SiH4 gas using a chemical vapor deposition (CVD) process, so that the TiN layer 15 is transformed into a TiSiN layer 17.
  • However, it is difficult to perform thick deposition of the TiSiN layer 17. Further, because resistivity of the TiSiN layer 17 is rather high, the TiSiN layer 17 can be only used as the barrier metal within a limited range.
  • Meanwhile, U.S. Pat. No. 6,271,136, titled “MULTI-STEP PLASMA PROCESS FOR FORMING TiSiN BARRIER” and issued to TSMC Company of Tiwan, discloses a method for improving a TiSiN layer as a copper barrier metal by means of Metal Organic Chemical Vapor Deposition (MOCVD) and multi-step plasma process. However, the disclosed document does not offer a solution to form a TiSiN layer for a barrier metal having a low specific resistance and a thick thickness.
    • SUMMARY OF THE INVENTION
  • Accordingly, the present invention has been made to solve the above-mentioned problems occurring in the prior art, and an object of the present invention is to provide a method for forming a barrier metal, capable of reducing a contact resistance of a TiSiN layer for the barrier metal using an atomic layer deposition process.
  • It is another object of the present invention is to provide a method for forming a barrier metal, capable of readily performing deposition of a TiSiN layer at a desired thickness.
  • It is yet another object of the present invention is to provide a method for forming a barrier metal, capable of reducing resistivity of a TiSiN layer.
  • In order to accomplish these objects, there is provided a method for forming a barrier metal of a semiconductor device, including: forming an insulating layer on a semiconductor substrate and forming an opening in the insulating layer, forming a TiSN layer having a desired thickness by repeatedly performing a process of forming a TiSIN layer having an atomic layer thickness, which performs deposition of a SiH4 layer inside the opening and on the insulating layer using an atomic layer deposition process and performs deposition of a certain precursor layer on the SiH4 layer, and performing plasma processing for the TiSiN layer so as to remove impurities contained in the TiSIN layer.
  • Preferably, an Si layer may be deposited, instead of the Si layer.
  • The SiH4 layer may be preferably deposited using an SiH4 gas.
  • Further, the Si layer may be preferably deposited using the SiH4 gas.
  • Preferably, the precursor layer may be formed by any one of a Tetrakis DiMethyl Amido Titanium (TDMAT) layer, a Tetrakis DiEthyl Amido Titanium (TDEAT) layer and a TiCl4 layer.
  • Particularly, the TiSiN layer having the atomic layer thickness is formed by reacting the precursor layer by thermal decomposition at a temperature ranging from 350 to 450□.
  • Preferably, the TiSiN layer may be plasma processed so as to remove CH based impurities contained in the TiSIN layer.
  • Specifically, the TiSIN layer may be plasma processed under any one atmosphere of a nitrogen gas and a hydrogen gas, or an ammonia gas.
  • Preferably, the opening may be formed into any one of a contact hole and a via hole.
  • Therefore, according to the present invention, it is easy to thickly form the TiSIN layer for the barrier metal. It is possible to reduce resistivity of the TiSiN layer to a relatively low level. Thereby, it is possible to reduce a contact resistance of the TiSIN layer and, further, to enhance an electrical characteristic of the semiconductor device.
    • BRIEF DESCRIPTION OF THE DRAWINGS
  • The above and other objects, features and advantages of the present invention will be more apparent from the following detailed description taken in conjunction with the accompanying drawings, in which:
  • FIGS. 1 to 3 illustrate a related art method for forming a barrier metal of a semiconductor device; and
  • FIGS. 4 to 9 illustrate a method for forming a barrier metal of a semiconductor device according to the present invention.
    • DETAILED DESCRIPTION
  • Hereinafter, a preferred embodiment of the present invention will be described with reference to the accompanying drawings. In the following description and drawings, the same reference numerals are used to designate the same or similar components, and so repetition of the description on the same or similar components will be omitted
  • FIGS. 4 to 9 illustrate a method for forming a barrier metal of a semiconductor device according to the present invention.
  • Referring to FIG. 4, first, an insulating layer 11 is formed on a semiconductor substrate 10. Here, even though not shown in the figure, it is apparent to those skilled in the art that, in order to define an active region of the substrate 10, a field oxide layer may be formed on a field region of the semiconductor substrate 10, while a source/drain, a gate electrode, etc. of a transistor may be previously formed on the active region of the semiconductor substrate 10. Subsequently, in order to expose a contact part (not shown) of the semiconductor substrate 10 using a photolithography process, the insulating layer 11 on the contact part of the semiconductor substrate 10 is etched to form an opening, for example a contact hole 12. Of course, it is possible to form a via hole instead of the contact hole 12.
  • Subsequently, referring to FIGS. 5 to 7, a TiSiN layer 25 is formed in a reaction chamber (not shown) using an atomic layer deposition (ALD) process. In this case, the reaction chamber is preferably maintained at a predetermined temperature ranging from 350 to 450□ and at a predetermined pressure ranging from 90 to 300 Torr.
  • To be more specific, as shown in FIG. 5, after the semiconductor substrate 10 is mounted in the reaction chamber, a gas of SiH4 is injected into the reaction chamber for a predetermined time, so that an SiH4 layer 21 is deposited inside the contact hole and on the insulating layer 11 at a desired thickness which is relatively thin. Here, instead of the SiH4 layer 21, an Si layer may be deposited using the SiH4 gas.
  • Next, as shown in FIG. 6, after injection of the SiH4 gas is stopped, an inert gas such as a nitrogen (N2) gas or argon (Ar) gas is injected for a predetermined time, and thus the SiH4 gas which may remain in the reaction chamber is completely discharged.
  • Subsequently, a gas for a precursor is injected into the reaction chamber for a predetermined time, so that a relatively thin precursor layer 23 is deposited on the SiH4 layer 21 at a desired thickness. Here, as the precursor gas, any one of Tetrakis DiMethyl Amido Titanium (TDMAT), Tetrakis DiEthyl Amido Titanium (TDEAT) and TiCl4 may be used. The precursor layer 23 may be formed by any one of a TDMAT layer, a TDEAT layer and a TiCl4 layer according to the gas for the precursor.
  • Here, materials of the SiH4,layer 21 and the precursor layer 23 are reacted by thermal decomposition at the temperature of the reaction chamber, for example in the temperature range from 350 to 450□, so that the TiSiN layer 25 is formed at an atomic layer thickness, as shown in FIG. 7.
  • Subsequently, after injection of the gas for the precursor is stopped, the inert gas such as nitrogen (N2) gas or argon (Ar) gas is injected for a predetermined time, and thus the gas for the precursor which may remain in the reaction chamber is completely discharged.
  • In this manner, the ALD process is performed at desired repetition times, for example 3 times. To be specific, as shown in FIG. 8, the TiSiN layer 25 is continuously deposited inside the contact hole 12 and on the insulating layer 11 at three layers. As a result, the TiSiN layer 25 is changed into a thicker TiSiN layer 27.
  • Meanwhile, for the sake of convenience of description, the thicker TiSiN layer 27 is shown as constituted of three TiSiN layers 25, but it is apparent that in reality, by changing the repetition times of the foregoing process, the thicker TiSIN layer 27 may be constituted of either three or more TiSiN layers 25 or three or less TiSiN layers 25.
  • Then, referring to FIG. 9, in order to remove impurities contained in the thicker TiSIN layer 27 of FIG. 8, for example CH based impurities, the thicker TiSiN layer 27 is plasma processed under the atmosphere of a hydrogen (H2) gas and a nitrogen (N2) gas, or an ammonia (NH3) gas, thus forming a final TiSiN layer 29. Here, the final TiSiN layer 29 has a relatively low resistivity to such an extent appropriate for the barrier metal, compared with the TiSiN layer 17 of FIG. 3.
  • Thus, according to the present invention, it is possible to form a thick TiSiN layer for a preferable barrier metal having a low resistivity, which reduces a contact resistance of a semiconductor device and, further, increases an electrical characteristic, such as an operation speed of the semiconductor device.
  • Thereafter, even though not shown in the Figures, additional process for the contact hole, for example a metal layer plug process or a metallization process may be performed.
  • As described above, in the method for forming a barrier metal of a semiconductor device according to the present invention, TiSiN layer is formed at an atomic layer thickness by performing deposition of an SiH4 layer inside a contact hole of the semiconductor device using an ALD process and by performing deposition of a precursor layer on the SiH4 layer. By repetition of this ALD process, the TiSiN layer can be thickly formed at a desired thickness. Then, the TiSiN layer is plasma processed under the atmosphere of a hydrogen (H2) gas and a nitrogen (N2) gas, or an ammonia (NH3) gas, thus removing impurities in the TiSiN layer.
  • Therefore, according to the present invention, it is easy to thickly form the TiSiN layer for the barrier metal. Further, it is possible to reduce resistivity of the TiSiN layer to a relatively low level. As a result, it is possible to reduce a contact resistance of the TiSiN layer and, further, to enhance an electrical characteristic of the semiconductor device.
  • Although a preferred embodiment of the present invention has been described for illustrative purposes, those skilled in the art will appreciate that various modifications, additions and substitutions are possible, without departing from the scope and spirit of the invention as disclosed in the accompanying claims.

Claims (11)

1. A method for forming a barrier metal of a semiconductor device, comprising:
forming an insulating layer on a semiconductor substrate and forming an opening in the insulating layer,
forming a TiSiN layer having a desired thickness by repeatedly performing a process of forming a TiSiN layer having an atomic layer thickness in a reaction chamber, wherein the process of forming a TiSiN layer having an atomic layer thickness comprises
performing deposition of a SiH4 layer inside the opening and on the insulating layer using an atomic layer deposition process,
discharging a gas remaining in the reaction chamber by using an inert gas,
performing deposition of a certain precursor layer on the SiH4 layer, and
discharging a gas of precursor material remaining in the reaction chamber by using an inert gas; and
performing plasma processing for the TiSiN layer so as to remove impurities contained in the TiSiN layer.
2. The method of claim 1, wherein the SiH4 layer is deposited using a SiH4 gas.
3. The method of claim 2, wherein the precursor layer is formed by any one of a Tetrakis DiMethyl Amido Titanium (TDMAT) layer, a Tetrakis DiEthyl Amido Titanium (TDEAT) layer and a TiCl4 layer.
4. The method of claim 3, wherein the TiSiN layer having the atomic layer thickness is formed by reacting the precursor layer by thermal decomposition at a temperature ranging from 350 to 450° C.
5. The method of claim 1, wherein the precursor layer is formed by any one of a Tetrakis DiMethyl Amido Titanium (TDMAT) layer, a Tetrakis DiEthyl Amido Titanium (TDEAT) layer and a TiCl4 layer.
6. The method of claim 5, wherein the TiSiN layer having the atomic layer thickness is formed by reacting the precursor layer by thermal decomposition at a temperature ranging from 350 to 450° C.
7. The method of claim 1, wherein the TiSiN layer is plasma processed so as to remove CH based impurities contained in the TiSiN layer.
8. The method of claim 7, wherein the TiSiN layer is plasma processed under any one atmosphere of a nitrogen gas and a hydrogen gas, or an ammonia gas.
9. The method of claim 1, wherein the opening is formed into any one of a contact hole and a via hole.
10. The method of claim 1, wherein the inert gas is a nitrogen or argon gas.
11. The method of claim 1, wherein a pressure of the reaction chamber is between 90 and 300 Torr.
US11/512,085 2002-12-14 2006-08-30 Method for forming barrier metal of semiconductor device Abandoned US20060292862A1 (en)