US20090269505A1 - Method for manufacturing a substrate with surface structure by employing photothermal effect - Google Patents
Method for manufacturing a substrate with surface structure by employing photothermal effect Download PDFInfo
- Publication number
- US20090269505A1 US20090269505A1 US12/362,131 US36213109A US2009269505A1 US 20090269505 A1 US20090269505 A1 US 20090269505A1 US 36213109 A US36213109 A US 36213109A US 2009269505 A1 US2009269505 A1 US 2009269505A1
- Authority
- US
- United States
- Prior art keywords
- substrate
- nanoparticles
- predetermined pattern
- surface structure
- manufacturing
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Abandoned
Abstract
A method for manufacturing a substrate with a surface substrate by employing photothermal effect is described. Nanoparticles on the surface of the substrate excited by a beam convert light energy to thermal energy. The surface structure on the substrate is formed through the thermal energy generated by the excited nanoparticles. The substrate with a layer of the predetermined pattern is thus formed.
Description
- This non-provisional application claims priority under 35 U.S.C. § 119(a) on Patent Application No(s). 097103802 filed in Taiwan, R.O.C. on Jan. 31, 2008 and Patent Application No(s). 097151822 filed in Taiwan, R.O.C. on Dec. 31, 2008 the entire contents of which are hereby incorporated by reference.
- 1. Field of the Invention
- The present invention relates to a method for manufacturing a substrate, and more particularly to a method for manufacturing a substrate with surface structure by employing photothermal effect.
- 2. Related Art
- Recently, many technologies were developed to form micro/nano-structure on surface of a substrate, such as nano-imprinting lithography (NIL), semiconductor manufacturing process or micro-electro-mechanical process (MEM) etc. Although these technologies can be used to fabricate micro/nano-structure, the fabricated process is complex and expensive. For example, when semiconductor manufacturing process or MEMS process is used to fabricate micro/nano-structure, the sample was treated by several processes, including spinning coat, exposure/development, etching and imprinting process. Therefore, it is difficulty and there is high cost to fabricate micro/nano-structure employing these technologies. The NIL technology also need many processes to fabricate template with micro/nano-structure on its surface and then imprint on a substrate. This technology also exhibits it is difficulty to manufacture micro/nano structure surface in large area.
- During making a printed circuit board (PCB), there is a process for forming gold fingers (also called as an edge connector). The edge connector is used as an interface for connecting the PCB and outside element through inserting to the outside element. The gold fingers are made with gold because gold has superior conductivity and superior oxidation resistance. However, the cost of gold is very expensive, so only the gold finger is only partially formed with gold using platting or chemical bonding, such as bonding pad. During platting, it is necessary to appropriately control parameters, to avoid some questions such as contamination with other metal and bad adhesion etc.
- Furthermore, a subtractive process and an additive process are the methods for making a conductive structure. For the subtractive process, the etching formulation and the etching angle errors result in copper residues. Thus, the subtractive process is not suitable for manufacturing fine circuits. The additive process needs a mask to define circuits, and then to manufacture circuits through copper-cladding processes such as plasma sputtering, electroplating, or electroless plating. In general, the flow of the additive process is rather complicated and the cost is relatively high. Therefore, a method for manufacturing conductive wires through inkjet technology is proposed.
- Currently, the method for manufacturing conductive wires through the inkjet technology has already been applied in manufacturing flexible circuit boards. Conventionally, the inkjet technology is used to spray conductive ink with low melting point on an organic substrate, so as to manufacture a flexible circuit board having conductive wires at a high speed and a low cost. However, the conductive ink should be sintered into a film at a high temperature to form conductive wires and meanwhile to enhance the conductivity thereof. During such sintering process, a sintering temperature of 200° C. is required, and the sintering duration should be over about 30 minutes. Accordingly, residual thermal stress is easily generated between the substrate and the formed conductive wires. Besides the heat treatment, another method is to use ultraviolet (UV) laser to sinter, but this method easily damages the substrate.
- This invention provides a method for manufacturing a substrate with surface structure by employing photothermal effect, which is a novel and simple method and can directly manufacture micro/nano-structure on surface of a substrate in large area through photothermal effect of nanoparticles. Compare with above technologies, the method for manufacturing a substrate with surface structure by employing photothermal effect according to this invention is rather simple, relatively low cost, and possible to form pattern on surface of a substrate in large amount.
- In one embodiment, a method for manufacturing a substrate with surface structure by employing photothermal effect involves steps of providing a substrate; distributing a plurality of nanoparticles on the provided substrate; irradiating the nanoparticles on the provided substrate with a specific wavelength, such that the nanoparticles convert irradiating energy (i.e. light energy) to thermal energy; and forming a layer of the predetermined pattern on the surface of the provided substrate through the thermal energy generated by the nanoparticles.
- In a case, the nanoparticles on the provided substrate can be melted through the thermal energy generated by the nanoparticles to form a nanoparticle-melted thin layer of the predetermined pattern, so as to obtain the substrate with the layer of the predetermined pattern. The predetermined pattern can be a pattern of at least one conductive wire and/or at least one conductive area. In the situation of the predetermined pattern being a pattern having at least one conductive wire, the substrate with the conductive wire may be obtained. In the situation of the predetermined pattern is a pattern having at least one conductive area, the substrate having a conductive area may be obtained.
- Herein, the nanoparticles can be directly distributed on the provided substrate in accordance with the predetermined pattern.
- Alternatively, the nanoparticles can be first distributed on the provided substrate as a whole layer, and then, the nanoparticles on the substrate is irradiated by a beam with specific wavelength through moving the beam along with the predetermined pattern, to excite the irradiated nanoparticles. In this case, the excited nanoparticles and nanoparticles around the excited nanoparticles on the provided substrate are melted through the thermal energy generated by the excited nanoparticles, and the melted nanoparticles are fixed on the provided substrate through thermal energy generated by the excited nanoparticles. Finally, unmelted nanoparticles are removed from the provided substrate to form a nanoparticle-melted thin layer of the predetermined pattern on the provided surface, so as to obtain the substrate with the layer of the predetermined pattern.
- In view of the above, the method for manufacturing a substrate with surface structure by employing photothermal effect according to this invention form micro/nano-structure on/in surface of a substrate. Use of the method according to this invention to fabricate micro/nano-structure on/in surface of the substrate can exhibit several advantages, such as the fabricated process is more simple and cheaper, and the sample can be manufactured in large area. Furthermore, when manufacturing the substrate with the layer of the predetermined pattern, residual stress can be reduced, as well as the thermal power, and adhesion between the predetermined pattern and the substrate can be increased. Further, energy loss can be reduced.
- The present invention will become more fully understood from the detailed description given herein below for illustration only, which thus is not limitative of the present invention, and wherein:
-
FIG. 1 is a general flowchart of a method for manufacturing a substrate with surface structure by employing photothermal effect according to a first embodiment of the present invention; -
FIG. 2 shows the calculated rate of light energy dissipation in Au, Ag, CdTe and CdSe nanoparticles; -
FIG. 3 shows the calculated temperature increase at the surface of single Au nanoparticle in water is a function of illumination power at the plasmon resonance; -
FIG. 4 shows relationship curves between particle size and melting-point of Au nanoparticle; -
FIGS. 5A-5E are general flowcharts of a method for manufacturing the substrate with the surface structure by employing photothermal effect according to a second embodiment of the present invention; -
FIGS. 6A-6D are general flowcharts of a method for manufacturing the substrate with the surface structure by employing photothermal effect according to a third embodiment of the present invention; -
FIGS. 7A-7B are general flowcharts of an embodiment of forming a substrate in the method for manufacturing the substrate with the surface structure by employing photothermal effect according to the present invention; -
FIG. 8 is a schematic sectional view of an embodiment of distribution of nanoparticles in the method for manufacturing the substrate with the surface structure by employing photothermal effect according to the present invention; -
FIG. 9A is a micrograph view of a surface structure on a substrate observed with an atomic force microscopy (AFM) before being illuminated with laser in a first example according to the method for manufacturing the substrate with the surface structure by employing photothermal effect of the present invention; -
FIG. 9B is a micrograph view of a surface structure on a substrate observed with an AFM after being illuminated with laser in the first example manufactured according to the method for manufacturing the substrate with the surface structure by employing photothermal effect of the present invention; -
FIG. 10A is a micrograph view of a surface structure on a substrate observed with an AFM before nanoparticles are distributed in thesubstrate 1 in the first example according to the method for manufacturing the substrate with the surface structure by employing photothermal effect of the present invention; -
FIG. 10B is a micrograph view of a surface structure on a substrate observed with an AFM before nanoparticles are distributed in thesubstrate 2 in the first example according to the method for manufacturing substrate with the surface structure by employing photothermal effect of the present invention; -
FIG. 10C is a micrograph view of a surface structure on a substrate observed with an AFM before nanoparticles are distributed in the substrate 3 in the first example according to the method for manufacturing the substrate with the surface structure by employing photothermal effect of the present invention; -
FIG. 11A is a micrograph view of a surface structure on a substrate observed with an AFM before being illuminated with laser in a second example according to the method for manufacturing the substrate with the surface structure by employing photothermal effect of the present invention; -
FIG. 11B is a micrograph view of a surface structure on a substrate observed with an AFM after being illuminated with laser in the second example according to the method for manufacturing the substrate with the surface structure by employing photothermal effect of the present invention; -
FIG. 12A is a micrograph view of a surface structure on a substrate observed with an AFM before being illuminated with laser in a third example according to the method for manufacturing the substrate with the surface structure by employing photothermal effect of the present invention; -
FIG. 12B is a micrograph view of a surface structure on a substrate observed with an AFM after being illuminated with laser in the third example according to the method for manufacturing the substrate with the surface structure by employing photothermal effect of the present invention; -
FIG. 13A is a micrograph view of a surface structure on a substrate observed with an AFM before being illuminated with laser in a fourth example according to the method for manufacturing the substrate with the surface structure by employing photothermal effect of the present invention; -
FIG. 13B is a micrograph view of a surface structure on a substrate observed with an AFM after being illuminated with laser in the fourth example according to the method for manufacturing the substrate with the surface structure by employing photothermal effect of the present invention; -
FIG. 14A is a micrograph view of a surface structure on a substrate observed with an AFM before being illuminated with laser in structure on a fifth example according to the method for manufacturing the substrate with the surface structure by employing photothermal effect of the present invention; -
FIG. 14B is a micrograph view of a surface structure on a substrate observed with an AFM after being illuminated with laser in the fifth example according to the method for manufacturing the substrate with the surface structure by employing photothermal effect of the present invention; -
FIG. 15A is a micrograph view of a surface structure on a substrate observed with an AFM before being illuminated with laser in a sixth example according to the method for manufacturing the substrate with the surface structure on substrate by employing photothermal effect of the present invention; -
FIG. 15B is a micrograph view of a surface structure on a substrate observed with an AFM after being illuminated with laser in the sixth example according to the method for manufacturing the substrate with the surface structure by employing photothermal effect of the present invention; -
FIGS. 16A-16D are general flowcharts of the method for manufacturing structure on substrate by employing photothermal effect according to a fourth embodiment of the present invention; -
FIG. 17 is a schematic top view corresponding toFIG. 16D ; -
FIG. 18A is a micrograph view of a surface structure on a substrate observed with an AFM before being illuminated with laser in a seventh example according to the method for manufacturing the substrate with the surface structure by employing photothermal effect of the present invention; -
FIG. 18B is a micrograph view of a surface structure on a substrate observed with an AFM after being illuminated with laser in the seventh example according to the method for manufacturing the substrate with the surface structure by employing photothermal effect of the present invention; -
FIGS. 19A-19D are general flowcharts of the method for manufacturing the substrate with the surface structure by employing photothermal effect according to a fifth embodiment of the present invention; -
FIG. 20 is a general sectional view corresponding toFIG. 19B ; -
FIG. 21 is a general sectional view corresponding toFIG. 19C ; -
FIG. 22A is a micrograph view of a surface structure on a substrate observed with an electron microscope before being illuminated with laser in eighth, ninth, and tenth examples according to the method for manufacturing the substrate with the surface structure by employing photothermal effect of the present invention; -
FIG. 22B is a micrograph view of a surface structure on a substrate observed with an electron microscope after being illuminated with laser of 1.8 W in the eighth example according to the method for manufacturing the substrate with the surface structure by employing photothermal effect of the present invention; -
FIG. 22C is a micrograph view of a surface structure on a substrate observed with an electron microscope after being illuminated with laser of 1.5 W in the ninth example according to the method for manufacturing the substrate with the surface structure by employing photothermal effect of the present invention; -
FIG. 22D is a micrograph view of a surface structure on a substrate observed with an electron microscope after being illuminated with laser of 1.2 W in the tenth example according to the method for manufacturing the substrate with the surface structure by employing photothermal effect of the present invention; -
FIG. 23A is a micrograph view of a surface structure on a substrate observed with an electron microscope before being annealed in a eleventh example according to the method for manufacturing the substrate with the surface structure by employing photothermal effect of the present invention; -
FIG. 23B is a micrograph view of a surface structure on a substrate observed with an electron microscope after being annealed in the eleventh example according to the method for manufacturing the substrate with the surface structure by employing photothermal effect of the present invention; -
FIG. 24A is a micrograph view of a surface structure on a substrate observed with an electron microscope before being annealed in a twelfth example according to the method for manufacturing the substrate with the surface structure by employing photothermal effect of the present invention; and -
FIG. 24B is a micrograph view of a surface structure on a substrate observed with an electron microscope after being annealed in the twelfth example according to the method for manufacturing the substrate with the surface structure by employing photothermal effect of the present invention. - In this present invention, a substrate with surface structure(s) is manufactured based on the principle of surface plasma resonance (SPR). When nanoparticles are irradiated by a beam with a specific wavelength, the excited nanoparticles can convert light energy of the beam into thermal energy, thereby forming the surface structure on the substrate through the thermal energy and thus obtaining the substrate with a specific surface structure (for example, but not limited to, plural pores and a layer of a predetermined pattern). The principle of SPR may be explained as that, if the diameter of precious metal particles is much smaller than a wavelength of the irradiating beam, the electrons in the surface of the metal particles initiate collective dipole oscillation upon being excited by the irradiating beam, thereby employing polarization of the surface electrons, and producing resonance phenomenon of free electrons in the surface of the metal particles. Therefore, the light energy absorbed by the precious metal particles can be rapidly converted into thermal energy due to SPR.
- The “photothermal effect” is defined as that, the light energy absorbed by the nanoparticle is converted into the thermal energy due to SPR after the nanoparticle is irradiated by a beam with a specific wavelength. Herein, terms, such as “a”, “an” and “the,” are not intended to limit to only a singular entity.
-
FIG. 1 shows a method for manufacturing a substrate with surface structure by photothermal effect according to a first embodiment of the present invention. - First, a substrate is provided (Step 10). The provided substrate may be made of, but not limited to, an organic material, an inorganic material (for example, glass, metal, or ceramic), a hybrid material or any combination thereof.
- Next, nanoparticles are distributed on the provided substrate (Step 30). The nanoparticles are made of a material capable of generating surface plasma resonance and photothermal effect. The nanoparticles may be metal nanoparticles, which is formed by, for example, (but not limited to) Au, Cu, Ag, Cd, Te, CdSe, or any combination thereof. The nanoparticle can be presented with a large particle aggregated by plural small metal particles with different materials or the same materials or aggregated by plural small metal particles with different particle sizes or the same particle sizes, or a particle structure with large size formed through bonging one or more metal particles to the surface of the larger particle by using surface modification. The particle structure with large size can be that, for example, the surface of metal particle with nano size or micro size is bonded with one or more nanoparticles, the surface of SiO2 with nano size or micro size is bonded with one or more nanoparticles, or the surface of carbon tube is bonded with one or more nanoparticles, etc. The particle size of the nanoparticles used herein may be much smaller than a wavelength of the light for excitation. Moreover, the diameter, i.e. particle size, of the nanoparticles may be smaller than 500 nm. The nanoparticles are not restricted in shape, which may be, but not limited to, spheroid-shaped, ellipse-shaped, triangle-shaped, strip-shaped, bar-shaped, asteroid-shaped, or any other irregular three-dimensional geometric shape.
- These nanoparticles used to be distributed on the provided substrate can have the same particle size, or have two or more particle sizes. These nanoparticles used to be distributed on the provided substrate can have the same material, or have two or more materials. These nanoparticles used to be distributed on the provided substrate can have the same shape, or have two or more shapes.
- Then, light with a specific wavelength are used to irradiate the nanoparticles on provided substrate, so as to excite the nanoparticles to convert light energy into thermal energy (Step 50). Herein, the predetermined time for irradiating the nanoparticles is determined according to the following process parameters, such as a surface material of the substrate (i.e., the surface material contacting with the nanoparticles), a material of the nanoparticles, a particle size of the nanoparticles, a concentration of the nanoparticles, types of light for irradiation (for example, but not limited to, types and wavelengths of the light), and intensity of light for irradiation (for example, but not limited to, power).
- Then, a surface structure is formed on the provided substrate through the thermal energy generated by the nanoparticles which are excited due to the plasma resonance (Step 70).
- In this manner, the substrate with specific surface structure, e.g. the nano or micro pores or the layer of the predetermined pattern, may be obtained.
-
FIG. 2 shows the calculated rate of light energy dissipation in Au, Ag, CdTe and CdSe nanoparticles. InFIG. 2 , Ag nanoparticle, Au nanoparticle, CdSe nanoparticle and CdTe nanoparticle, which have particle size of 60 nm and are within water, are individually irradiated by the beam with light flux of 5*104 W/cm2 (I0=5*104 W/cm2). The vertical axle represents a ratio of total absorption rate to heat generation (qtot), and a unit is uW. The total absorption rate represents the amount of the light energy absorbed by the nanoparticle. The heat generation represents the amount of the thermal energy generated by the nanoparticle. The lateral axle represents wavelength of the beam, and the unit is nm. Dielectric constant (∈o) of medium around the nanoparticle is equal to that (∈water) of water, that is, the dielectric constant is 1.8. - Referring to
FIG. 2 , compare with CdSe nanoparticle and CdTe nanoparticle, Ag nanoparticle and Au nanoparticle generate a larger amount of the thermal energy when they are irradiated by a beam with a specific wavelength, i.e. absorption band for exciting SPR. - Photothermal effect relates to the absorption of SPR and SPR depends on the size, shape, and degree of particle-to-particle coupling.
-
FIG. 3 shows the calculated temperature increase at the surface of single Au nanoparticle in water is a function of illumination power at the plasmon resonance. InFIG. 3 , the Au nanoparticles with particle sizes of 10 nm, 20 nm, 30 nm, 40 nm, 50 nm, and 100 nm and in water are individually irradiated by the beam with a wavelength of 520 nm (λexcitation=520 nm). The vertical axle represents the temperate increase (□Tmax) caused by the thermal energy generated by single Au nanoparticle, and the unit is K. The lateral axle represents the light flux of the irradiating beam, and the unit is W/cm2. - Referring to
FIG. 3 , the heat generated from an AuNP in water is increasing with particle size when illuminated the same light flux. - Furthermore, different types of the nanomaterials, such as nanopellet, nanoline, nanotube, etc., can be observed phenomenon of decreasing melting-point thereof. As to substances with the same material, under a macroscope scale, melting point depression is most evident in nanowires, nanotubes and nanoparticles, which all melt at lower temperatures than bulk amounts of the same material. Changes in melting point occur because nanoscale materials have a much larger surface to volume ratio than bulk materials, drastically altering their thermodynamic and thermal properties. This difference results from that, the nano-structured substance has larger specific surface area, such that thermodynamic and thermal properties of the nano-structured substance and the bulk substance have fairly large difference.
-
FIG. 4 shows the relationship curves between particle size and melting-point of Au nanoparticle. InFIG. 4 , the vertical axle represents the melting-point (Tm) of Au nanoparticle, and the unit is K. The lateral axle represents the particle size (2r) of Au nanoparticle, i.e. the diameter of Au nanoparticle, and the unit is nm. - Referring to
FIG. 4 , when the particle size of Au nanoparticle is lower than 5 nm, the melting-points of Au nanoparticle decrease dramatically. - Hence, when the substrate with the pores is manufactured by employing the photothermal effect, the particle size of nanoparticles is decided according to melting-point and pyrolysis temperature of the provided substrate.
- Since an amount of the thermal energy generated by the nanoparticles with small particle size is less than lager ones, the nanoparticles with small and large particle sizes are simultaneously used when the substrate with the layer of the predetermined pattern is manufactured by employing the photothermal effect. Therefore, the layer of the predetermined pattern can be formed by melting the nanoparticle(s) with the small particle size to weld the nanoparticle(s) with the large particle size.
-
FIGS. 5A-5E show a method for manufacturing a substrate with surface structure by employing photothermal effect. - First, a
substrate 112 is provided, as shown inFIG. 5A . The substrate may be made of, but not limit to, an organic material, an inorganic material (for example, glass, metal, and ceramic), a hybrid material or any combination thereof. - Next,
nanoparticles 130 are distributed on the providedsubstrate 112, as shown inFIG. 5B . Thesenanoparticles 130 used to be distributed on the provided substrate can have the same particle size, or have two or more particle sizes. Thesenanoparticles 130 used to be distributed on the provided substrate can have the same material, or have two or more materials. Thesenanoparticles 130 used to be distributed on the provided substrate can have the same shape, or have two or more shapes. - Then, the
beam 150 with a specific wavelength are used to irradiate thenanoparticles 130 on thesubstrate 112,excited nanoparticles 130 can convert the light energy into thermal energy, as shown inFIG. 5C . At this time, the beam continuously irradiates the nanoparticles for a predetermined time. For example, the beam with a specific wavelength irradiates the nanoparticles for, but not limited to, about more than 5 seconds. - Then, a plurality of
pores 116 corresponding to thenanoparticles 130 is formed on surface of thesubstrate 112 through the thermal energy generated by thenanoparticles 130 upon being irradiated by the beam, as shown inFIG. 5D . - Finally, the
nanoparticles 130 are removed from thesubstrate 112, the appliedsubstrate 110 withpores 116 can be obtained, as shown inFIG. 5E . - Furthermore, the
nanoparticles 130 also can bond on surface of anothersubstrate 102 which is transparent, as shown inFIG. 6A . Thetransparent substrate 102 may be made of any transparent material capable of carrying the nanoparticles, for example, glass or quartz. Thesenanoparticles 130 used to be distributed on the provided substrate can have the same particle size, or have two or more particle sizes. Thesenanoparticles 130 used to be distributed on the provided substrate can have the same material, or have two or more materials. Thesenanoparticles 130 used to be distributed on the provided substrate can have the same shape, or have two or more shapes. Herein, a way, such as, but not limited to, spray printing, spin coating, coating, and covalent bonding, etc., can be used to fix thenanoparticles 130 on thetransparent substrate 102. Based on the property of thetransparent substrate 102, that is, the material of thetransparent substrate 102, such as metal material, inorganic material, organic material, hybrid material, or any combination thereof. The way to fix thenanoparticles 130 on thetransparent substrate 102 can be selected from a physical way and a chemical way. The physical way can be, for example, employing static adsorbability, ionic adsorbability or van der Waals' forces to fix thenanoparticles 130 on the surface of thetransparent substrate 102. The chemical way can be, for example, forming a self-assembly monolayer in the surface of thetransparent substrate 102 or surface modification of thenanoparticles 130 or thetransparent substrate 102, to fix thenanoparticles 130 on the surface of thetransparent substrate 102. Under the surface modification, the surface of thenanoparticles 130 or the surface of thetransparent substrate 102 is modified, such that thenanoparticles 130 can be fixed on the surface of thetransparent substrate 102 via the modified surface in chemical bonding, such as ion bonding, covalent bonding, etc., manner. After modifying the surface of thenanoparticles 130 or the surface of thetransparent substrate 102, the surface thereof forms function groups thereon. The function groups can be, but not limited to, N-hydroxy succinimide (NHS) groups, amino groups, aldehyde groups, epoxy groups, carboxyl groups, hydroxyl groups, acyl groups, acetyl groups, hydrazonos, hydrophobic groups, thiol groups, photoreactive groups, cysteine groups, disulfide groups, alkyl halide groups, acyl halide groups, azide groups, phosphate groups, or their combination, etc. - One side of the
transparent substrate 102 having thenanoparticles 130 fixed thereon faces and is placed on a surface of thesubstrate 112 to be desired to form the pores thereon, so that thenanoparticles 130 are distributed on thesubstrate 112 and closely contact with the surface of thesubstrate 112. In other words, thenanoparticles 130 are sandwiched between thetransparent substrate 102 and thesubstrate 112, as shown inFIG. 6B . - Then, the
beam 150 with a specific wavelength is used to irradiate thenanoparticles 130 on thetransparent substrate 102, theexcited nanoparticles 130 can convert the light energy of thebeam 150 into thermal energy, as shown inFIG. 6C . At this time, the beam with a specific wavelength irradiates the nanoparticles for a predetermined time. For example, the beam with a specific wavelength irradiates the nanoparticles for, but not limited to, about more than 5 seconds. - Then, the positions of
pores 116 corresponding to thenanoparticles 130 are formed on thesubstrate 112 through the thermal energy generated by thenanoparticles 130 upon being irradiated by the beam, as shown inFIG. 6D . - Finally, the
transparent substrate 102 is removed from thesubstrate 112, thereby obtaining thesubstrate 110 having thepores 116, as shown inFIG. 5E . Since thenanoparticles 130 are fixed on thetransparent substrate 102, thenanoparticles 130 are removed together with thetransparent substrate 102 when thetransparent substrate 102 is removed. Furthermore, once thetransparent substrate 102 is removed, the surface of thesubstrate 112 may be rinsed with a solution (for example, but not limited to, water or cleaning solution) or become clean by means of blowing, so as to eliminate the residual nanoparticle(s) 130 and/or impurities such as dusts adhered thereon, which facilitates the subsequent use or process. - The
substrate 112 may be formed through the following steps. First, a sub-substrate 113 is provided, as shown inFIG. 7A . Next, asurface layer 114 with low melting point is formed on the sub-substrate 113 employing a material with a melting temperature lower than or equal to a temperature caused by thenanoparticles 130 duo to the thermal energy generated, as shown inFIG. 7B . At this time, thenanoparticles 130 are distributed on a surface of thesurface layer 114 with low melting point, as shown inFIG. 8 . The sub-substrate 113 may be made of an organic material, an inorganic material (for example, glass, metal, and ceramic), a hybrid material, or any combination thereof. Thesurface layer 114 with low melting point may be made of a material having a melting temperature lower than or equal to that of the thermal energy generated by thenanoparticles 130, i.e., lower than or equal to a temperature of the nanoparticles that is raised as the thermal energy is generated. Thesurface layer 114 with low melting point may be made of an organic material, an inorganic material, a hybrid material, or any combination thereof, etc. The organic material may be, but not limited to, polyethylene, polystyrene, polyvinyl chloride, polyacetals, epoxy resin, polyamides, polyester, phenol formaldehyde, amino resin, but not limited to, polyurethane (PU), polymethylmethacrylate (PMMA) or polydimethylsiloxane (PDMS). - In other words, at least the material on the surface of the
substrate 112 where it contacts with thenanoparticles 130 has a melting temperature lower than or equal to the temperature by thenanoparticles 130 due to thermal energy generated thereby. That is, the melting temperature at the surface of the substrate is lower than or equal to a temperature of the nanoparticles. - The Au-nanoparticles (i.e., the nanoparticle was made of Au) with a particle size of about 20 nm were fixed on a transparent substrate, and then placed on a surface of a substrate made of a polymer material. The Au-nanoparticles closely contacted the surface of the substrate. Then, the green laser with a wavelength of 532 nm was used to irradiate the transparent substrate with Au-nanoparticles for about 15 seconds. The Au-nanoparticles were excited on the substrate. At this time, the Au-nanoparticles generated temperature of up to 200° C. within 15 seconds upon being irradiated by the green laser. After exposed time, i.e. the time of irradiation, of 15 seconds, the transparent substrate and the Au-nanoparticles were removed from the substrate to obtain the substrate with pores. Before being irradiated by the green laser, the surface of the substrate having the Au-nanoparticles was observed with an atomic force microcopy (AFM), as shown in
FIG. 9A . After being irradiated by the green laser, the obtained substrate with the pores was also observed by the AFM, as shown inFIG. 9B . Furthermore, as seen fromFIGS. 9A and 9B that, many pores was formed on the surface of the substrate obtained according to the method for manufacturing a substrate with surface structure by employing photothermal effect of the present invention. - Furthermore, three types of substrates were provided. In order to illustrate conveniently, they are respectively referred as the
substrate 1, thesubstrate 2, and the substrate 3 hereinafter. Thesubstrate 1 was formed by a sub-substrate made of glass and a surface layer with low melting point made of PU. Thesubstrate 2 was formed by a sub-substrate made of glass and a surface layer with low melting point made of PMMA/ethanol. The substrate 3 was formed by a sub-substrate made of glass and a surface layer with low melting point made of PDMS. First, the surfaces of the surface layers with low melting point opposite to the sub-substrates of thesubstrates FIGS. 10A , 10B, and 10C, respectively. - Herein, the Au-nanoparticles with a particle size of about 20 nm were fixed on the transparent substrate, and then the transparent substrate was placed on the substrate. Herein, the Au-nanoparticles closely contacted surface of the surface layer with low melting point. Then, three types of the substrates having pores were manufactured according to the following parameters (in order to illustrate conveniently, they are respectively referred as the
substrate 1′, thesubstrate 2′, and the substrate 3′ hereinafter), and these substrates were respectively observed with the AFM. - The green laser with a wavelength of 532 nm and a power of 100 mW was used to irradiate the Au-nanoparticles where was placed on the
substrate 1 through the transparent substrate for about 10 minutes. Once the irradiation was completed, the transparent substrate and Au-nanoparticles were removed, so as to obtain thesubstrate 1′. Before being irradiated by the green laser, the substrate having the Au-nanoparticles was observed with an AFM, as shown inFIG. 11A . After being irradiated by the green laser, thesubstrate 1′ obtained was observed with an AFM, as shown inFIG. 11B . - The green laser with a wavelength of 514.5 nm and a power of 1 W irradiated the Au-nanoparticles placed on the
substrate 2 through the transparent substrate for about 20 minutes. Once the irradiation was completed, the transparent substrate and Au-nanoparticles were removed, so as to obtain thesubstrate 2′. Before being irradiated by the green laser, the substrate having the Au-nanoparticles was observed with an AFM, as shown inFIG. 12A . After being irradiated by the green laser, the obtainedsubstrate 2′ was observed with an AFM, as shown inFIG. 12B . - The green laser with a wavelength of 514.5 nm and a power of 2 W irradiated the Au-nanoparticles placed on the substrate 3 through the transparent substrate for about 40 minutes. Once the irradiation was completed, the transparent substrate and Au-nanoparticles were removed, so as to obtain the substrate 3′. Before being irradiated by the green laser, the substrate having the Au-nanoparticles was observed with an AFM, as shown in
FIG. 13A . After being irradiated by the green laser, the obtained substrate 3′ was observed with an AFM, as shown inFIG. 13B . - Furthermore, the Au-nanoparticles with a particle size of about 60 nm were fixed on the transparent substrate, and then the transparent substrate was placed on the surface of the surface layer with low melting point of the substrate to enable the Au-nanoparticles to closely contact the substrate. Then, two types of the substrates having pores were manufactured which according to the following parameters (in order to illustrate conveniently, they are respectively called the substrate 4′ and the
substrate 5′ hereinafter), and then the manufactured substrates were observed with the AFM. - The green laser with a wavelength of 514.5 nm and a power of 2 W irradiated the Au-nanoparticles placed on the
substrate 1 through the transparent substrate for about 40 minutes. Once the irradiation was completed, the transparent substrate and Au-nanoparticles were removed, so as to obtain the substrate 4′. Before being irradiated by the green laser, the substrate having the Au-nanoparticles was observed with an AFM, as shown inFIG. 14A . After being irradiated by the green laser, the obtained substrate 4′ was observed with an AFM, as shown inFIG. 14B . - The green laser with a wavelength of 514.5 nm and a power of 2 W irradiated the Au-nanoparticles placed on the substrate 3 through the transparent substrate for about 40 minutes. Once the irradiation was completed, the transparent substrate and Au-nanoparticles were removed, so as to obtain the
substrate 5′. Before being irradiated by the green laser, the substrate having the Au-nanoparticles was observed with an AFM, as shown inFIG. 15A . After being irradiated by the green laser, the obtainedsubstrate 5′ was observed with an AFM, as shown inFIG. 15B . - Referring to
FIGS. 16A-16D , they show a method for manufacturing a substrate with surface structure by employing photothermal effect according to an embodiment of the present invention. - First, a
substrate 112 is provided, as shown inFIG. 16A . - Next, a plurality of
nanoparticles 130 is distributed on thesubstrate 112 in accordance with at least onepredetermined pattern 170, as shown inFIG. 16B . Thesenanoparticles 130 used to be distributed on the provided substrate can have the same particle size, or have two or more particle sizes. Thesenanoparticles 130 used to be distributed on the provided substrate can have the same material, or have two or more materials. Thesenanoparticles 130 used to be distributed on the provided substrate can have the same shape, or have two or more shapes. - Moreover, a way, such as, but not limited to, spray printing, spin coating, coating, and covalent bonding, etc., can be used to fix the
nanoparticles 130 on thesubstrate 112. The way to fix thenanoparticles 130 on thesubstrate 112 can be selected from a physical way and a chemical way according to the property of the material of thesubstrate 112. The physical way can be, for example, a plasma treat. Under the plasma treat, electron is gun to the surface of the substrate to rough the surface of the substrate, such that the nanoparticles can be fixed on the rough surface of the substrate. The chemical way can be, for example, forming a self-assembly monolayer in the surface of the substrate or surface modification. Under the way of forming the self-assembly monolayer in the surface of the substrate, the self-assembly monolayer of thepredetermined pattern 170 is formed in the surface of the substrate, such that the nanoparticles can be fixed on the self-assembly monolayer of thepredetermined pattern 170. Under the surface modification, the surfaces of thenanoparticles 130 are modified or a portion of surface, i.e. surface to be formed the layer of thepredetermined pattern 170, of the substrate is modified, such that thenanoparticles 130 can be fixed on the surface of the substrate via the modified surface in chemical bonding, such as ion bonding, covalent bonding, etc., manner. The surface is treated with surface modification to form function groups thereon. The function groups can be, but not limited to, N-hydroxy succinimide (NHS) groups, amino groups, aldehyde groups, epoxy groups, carboxyl groups, hydroxyl groups, acyl groups, acetyl groups, hydrazonos, hydrophobic groups, thiol groups, photoreactive groups, cysteine groups, disulfide groups, alkyl halide groups, acyl halide groups, azide groups, phosphate groups, or their combination, etc. - Then, the
beam 150 with a specific wavelength irradiates thenanoparticles 130 on thesubstrate 112, so as to excite thenanoparticles 130 to convert the light energy of the light 150 into thermal energy, as shown inFIG. 16C . At this time, the beam continuously irradiates the nanoparticles for a predetermined time. For example, the beam with a specific wavelength can irradiate the nanoparticles for, but not limited to, about more than 5 seconds. - The nanoparticles on the
substrate 112 are melted under the thermal energy generated by thenanoparticles 130 to form a nanoparticle-melted thin layer of thepredetermined pattern 170, thereby obtaining thesubstrate 110 with the layer of the predetermined pattern, as shown inFIGS. 16D and 17 . - The
nanoparticles 130 may be formed by a metal material (i.e., metal nanoparticles). At this time, the meltednanoparticles 132, i.e. the nanoparticle-melted thin layer of the predetermined pattern, can serve as one or more conductive wires and/or one or more conductive areas. That is, the nanoparticle-melted thin layer may be a conductive layer of a pattern of one or more conductive wires and/or one or more conductive areas. - Furthermore, if the material of the substrate is appropriately selected, the obtained substrate having one or more conductive wires and/or one or more conductive areas can serve as a circuit board. In other words, the material of the nanoparticles has a melting temperature lower than or equal to the generated thermal energy, i.e. a temperature caused by the nanoparticles due to the generated thermal energy. The conductive area can be, for example, a ground.
- Furthermore, the obtained substrate may be cleaned firstly before the subsequent use or processes, so as to remove those unfixed nanoparticles, unfixed but melted nanoparticles, and/or impurities on the surface of the obtained substrate. Particularly, the obtained substrate may be rinsed with a solution (for example, but not limited to, water or a cleaning solution) or become clean by means of blowing.
- The Au-nanoparticles with a particle size of about 20 nm were distributed on the substrate made of, but not limited to, an organic material in accordance with the predetermined pattern. Then, the green laser with a wavelength of 532 nm irradiated the Au-nanoparticles on the substrate for about 15 seconds. At this time, the Au-nanoparticles could generate the thermal energy with a temperature of up to 200° C. within 15 seconds upon being irradiated by the green laser, so that the surfaces of the Au-nanoparticles were melted with each other and fixed on the substrate. Once the irradiation of the green laser was completed, the substrate with the predetermined pattern was obtained. Before being irradiated by the green laser, the surface of the substrate having the Au-nanoparticles was observed with the AFM, as shown in
FIG. 18A . After being irradiated by the green laser, the obtained substrate was observed with the AFM, as shown inFIG. 18B . Referring toFIGS. 18A and 18B , the nanoparticles on the surface of the obtained substrate had already been melted together. - In another embodiment, a layer of
nanoparticles 130, e.g. a whole layer of nanoparticles, is distributed on a surface of thesubstrate 112 where a surface structure is to be formed, as shown inFIG. 19A . Thesenanoparticles 130 used to be distributed on the provided substrate can have the same particle size, or have two or more particle sizes. Thesenanoparticles 130 used to be distributed on the provided substrate can have the same material, or have two or more materials. Thesenanoparticles 130 used to be distributed on the provided substrate can have the same shape, or have two or more shapes. Moreover, thenanoparticles 130 may be distributed on thesubstrate 112 by means of, but not limited to, spray printing, spin coating, and coating, etc. Furthermore, thenanoparticles 130 may be distributed on the surface of thesubstrate 112 in a state of a solution. - Then, the
beam 150 in a specific wavelength irradiates thenanoparticles 130 on thesubstrate 112, and meanwhile, the light source for emitting thebeam 150 is moved according to the predetermined pattern to be formed, so that thebeam 150 travel above thenanoparticles 130 to excite thenanoparticles 130 at positions where the predetermined pattern is to be formed, as shown inFIGS. 19B and 20 . The beam can continuously irradiate the nanoparticles for a predetermined time. For example, the beam with a specific wavelength can irradiate the nanoparticles for, but not limited to, about more than 5 seconds. - The
excited nanoparticles 130 convert the light energy of thebeam 150 into thermal energy. Then, theexcited nanoparticles 130 are melted together with thosenanoparticles 130 there-around on thesubstrate 112 under the thermal energy generated by theexcited nanoparticles 130, and then fixed on thesubstrate 112, as shown inFIGS. 19C and 21 . In other words, theexcited nanoparticles 130 and thosenanoparticles 130 there-around are melted together on the surface, that is, thesubstrate 112 not only hasnon-melted nanoparticles 130, but also has meltednanoparticles 132. - Finally, the
nanoparticles 130 not melted together with thosenanoparticles 130 there-around are removed from the surface, so as to form a nanoparticle-melted thin layer of thepredetermined pattern 170, i.e., obtaining thesubstrate 110 with layer the predetermined pattern, as shown inFIG. 19D . In other words, once thenon-melted nanoparticles 130 are removed, merely the meltednanoparticles 132 are left on the surface of thesubstrate 112, such that the predetermined pattern is presented. At this time, thenon-melted nanoparticles 130 may be rinsed with a solution (for example, but not limited to, water or a cleaning solution) or blown off, so as to be removed from thesubstrate 112. - The
nanoparticles 130 may be made of a metal material. At this time, the meltednanoparticles 132 left on the surface of thesubstrate 112 can serve as one or more conductive wires and/or one or more conductive areas. That is, the nanoparticle-melted thin layer can be a conductive layer of the pattern of the conductive wires and/or the conductive areas. Therefore, the substrate with the conductive wires and/or the conductive areas may be obtained. - For example, when the surface structure (i.e., the layer of the predetermined pattern) to be formed is a conductive layer with the pattern of conductive wires, the beam move correspondingly to positions where the conductive wires are to be formed, so as to excite the nanoparticles at the positions on the substrate where the conductive wires are to be formed, and thus the nanoparticles are melt with each other and then fixed on the substrate. Once the non-melted nanoparticles are removed from the substrate, the melted nanoparticles (i.e., the nanoparticle-melted thin layer of the predetermined pattern) in the configuration of conductive wires are left on the substrate, thereby obtaining the substrate with the layer of the predetermined pattern, which has the substrate and the melted nanoparticles.
- Likewise, when the surface structure (i.e., the layer of the predetermined pattern) to be formed is a conductive layer with the pattern of at least one conductive area, the beam move correspondingly to positions where the conductive area is to be formed, so as to excite the nanoparticles at the positions on the substrate where the conductive area is to be formed, such that the nanoparticles are melt with each other and then fixed on the substrate. After the non-melted nanoparticles are removed from the substrate, the melted nanoparticles (i.e., the nanoparticle-melted thin layer of the predetermined pattern) in the configuration of the conductive area are left on the substrate, thereby obtaining the substrate with a conductive layer of the predetermined pattern, which is formed by the substrate and the melted nanoparticles.
- Furthermore, if the material of the substrate is appropriately selected, the obtained substrate having one or more conductive wires or one or more conductive areas can serve as a circuit board. In this case, the material of the nanoparticles has a melting temperature lower than or equal to the generated thermal energy, i.e. a temperature caused by the nanoparticles due to the generated thermal energy.
- The Au-nanoparticles in a state of a solution with a particle size of about 8 nm to 9 nm were coated on a substrate made of glass. Then, the green laser (with a wavelength of 514 nm) with different powers irradiated the Au-nanoparticles on the substrate to excite the Au-nanoparticles with irradiation rate 1.25 mm/sec, such that the excited Au-nanoparticles were melted with those Au-nanoparticles there-around. In terms of a conductivity test, after being irradiated by the laser of 1.8 W, the conductivity of the melted Au-nanoparticles on the surface of the substrate was about 1.55 Ω/sq; after being irradiated by the laser of 1.5 W, the conductivity of the melted Au-nanoparticles on the surface of the substrate was about 5.21 Ω/sq; and after being irradiated with the laser of 1.2 W, the conductivity of the melted Au-nanoparticles on the surface of the substrate was about 9.02 Ω/sq. Furthermore, before being irradiated by the laser, a secondary electron image (SEI) of the substrate with the Au-
nanoparticles 130 formed on the surface thereof was observed with an electron microscope at the magnification of 220,000 and the working distance of 9.7 mm, as shown inFIG. 22A . After being irradiated by the laser of 1.8 W, the SEI of the substrate with melted Au-nanoparticles 132 on the surface thereof was observed with the electron microscope at the magnification of 200,000 and the working distance of 9.7 mm, as shown inFIG. 22B . After being irradiated by the laser of 1.5 W, the SEI of the substrate with melted Au-nanoparticles 132 on the surface thereof was observed with the electron microscope at the magnification of 65,000 and the working distance of 9.7 mm, as shown inFIG. 22C . After being irradiated by the laser of 1.2 W, the SEI of the substrate with melted Au-nanoparticles 132 on the surface thereof was observed with an electron microscope at the magnification of 140,000 and the working distance of 9.7 mm, as shown inFIG. 22D . Therefore, referring toFIGS. 22A-22D , as for the substrate obtained according to the method for manufacturing a substrate with surface structure by employing photothermal effect of the present invention, the nanoparticles on the surface of the obtained substrate had been melted together, and the melted nanoparticles had a desirable conductivity. - The Ag-nanoparticles with the particle size of about 25 nm were formed into a thin film on the substrate. The thin film of the Ag-nanoparticles was irradiated by a laser with an energy density of 159.2 W/mm2, a power of 50 mW, a beam size of 20 μm, and a wavelength of 408 nm to anneal. Before being annealed, the SEI of the substrate with the thin film of the Ag-
nanoparticles 130 formed on the surface thereof was observed with an electron microscope at the magnification of 80,000 and the working distance of 10 mm, as shown inFIG. 23A . After being annealed, the SEI of the substrate with melted Ag-nanoparticles 132 on the surface thereof was observed with the electron microscope at the magnification of 80,000 and the working distance of 10 mm, as shown inFIG. 23B . After being annealed, the Ag-nanoparticles 130 were obviously fused into larger particles. Moreover, as to the resistivity of the thin film of the Ag-nanoparticles 130, resistivity thereof was too large to measure before being annealed, but the resistance decreased to 1.48*10−6 Ωm after being annealed. - The Ag-nanoparticles with the particle sizes of about 40 nm and about 120 nm were formed into the thin film on the substrate. The thin film of the Ag-nanoparticles was irradiated by a laser with the energy density of 0.52 W/mm2, the power of 50 mW, the beam size of 350 μm, and a wavelength of 408 nm to anneal. Before being annealed, the SEI of the substrate with the thin film of the Ag-
nanoparticles 130 formed on the surface thereof was observed with an electron microscope at the magnification of 100,000 and the working distance of 10.1 mm, as shown inFIG. 24A . After being annealed, the SEI of the substrate with melted Ag-nanoparticles 132 on the surface thereof was observed with the electron microscope at the magnification of 100,000 and the working distance of 10 mm, as shown inFIG. 24B . After being annealed, the Ag-nanoparticles 130 with the particle sizes of about 40 nm were obviously fused with the Ag-nanoparticles 130 with the particle sizes of about 120 nm. Moreover, as to the resistivity of the thin film of the Ag-nanoparticles 130, resistivity thereof decreased from 9.21*10−5 Ωm (before being annealed) to 3.04*10−7 Ωm (after being annealed). - In view of the above, with the method for manufacturing a substrate with surface structure by employing photothermal effect according to the present invention, the substrate with specific surface structure can be manufactured without employing a mask, the whole flow for manufacturing the substrate with specific surface structure is quite simple, the cost for manufacturing the substrate with specific surface structure is relatively low, and the substrates with specific surface structure and a large area may be easily manufactured in mass production. Furthermore, when the substrates with the specific surface structure and the large area are manufactured in mass production, devices and machines required by specific processes and steps and the corresponding technology may not be used, thereby the manufacturing cost is reduced. When manufacturing the substrate with layer of the predetermined pattern, residual stress can be reduced, as well as the thermal power, and adhesion between the predetermined pattern and the substrate can be increased. Further, energy loss can be reduced.
- The invention being thus described, it will be obvious that the same may be varied in many ways. Such variations are not to be regarded as a departure from the spirit and scope of the invention, and all such modifications as would be obvious to one skilled in the art are intended to be included within the scope of the following claims.
Claims (9)
1. A method for manufacturing a substrate with surface structure by employing photothermal effect, comprising:
a. providing a substrate
b. distributing a plurality of nanoparticles on the provided substrate;
c. irradiating the nanoparticles on the provided substrate with a specific wavelength, so that the nanoparticles are excited to convert irradiating energy to thermal energy; and
d. forming a layer of a predetermined pattern on the surface of the provided substrate through the thermal energy formed by the nanoparticles.
2. The method of claim 1 , wherein the step b comprises:
distributing the nanoparticles in accordance with the predetermined pattern on the provided substrate; and
wherein the step d comprises:
melting the excited nanoparticles of the nanoparticles and nanoparticles around the excited nanoparticles of the nanoparticles through the thermal energy generated by the excited nanoparticles into a nanoparticle-melted thin layer of the predetermined pattern, thereby obtaining the substrate with the layer of the predetermined pattern.
3. The method of claim 2 , wherein the predetermined pattern is at least one of a pattern of at least one conductive wire and a pattern of at least one conductive area.
4. The method of claim 1 , wherein the step b comprises:
distributing the nanoparticles on the surface of the provided substrate to form a layer of the nanoparticles;
wherein the step c comprises:
irradiating the layer of the nanoparticles on the provided substrate by a beam with a specific wavelength; and
moving the beam along with the predetermined pattern to excite the nanoparticles corresponding to the predetermined pattern; and
wherein the sep d comprises:
melting the excited nanoparticles of the nanoparticles and nanoparticles around the excited nanoparticles of the nanoparticles through the thermal energy generated by the excited nanoparticles; and
removing unmelted nanoparticles of the nanoparticles from the provided substrate to form a nanoparticle-melted thin layer of the predetermined pattern on the provided substrate, thereby obtaining the substrate with the layer of the predetermined pattern.
5. The method of claim 4 , wherein the predetermined pattern is at least one of a pattern of at least one conductive wire and a pattern of at least one conductive area.
6. The method of claim 1 , wherein the substrate the provided substrate has at least one material each which is one of an organic material, an inorganic material, and a hybrid material.
7. The method of claim 1 , wherein the material of the nanoparticles comprises at least one metal material.
8. The method of claim 7 , wherein the metal material is selected from a group consisting of Au, Cu, Ag, Cd, Te, CdSe, and combination thereof.
9. The method of claim 1 , wherein the predetermined pattern is at least one of a pattern of at least one conductive wire and a pattern of at least one conductive area.