US20110210060A1 - Expanded composite filter media including nanofiber matrix and method - Google Patents
Expanded composite filter media including nanofiber matrix and method Download PDFInfo
- Publication number
- US20110210060A1 US20110210060A1 US13/032,227 US201113032227A US2011210060A1 US 20110210060 A1 US20110210060 A1 US 20110210060A1 US 201113032227 A US201113032227 A US 201113032227A US 2011210060 A1 US2011210060 A1 US 2011210060A1
- Authority
- US
- United States
- Prior art keywords
- fibers
- component
- fine fibers
- substrate
- filter media
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Abandoned
Abstract
A composite filter media includes an expanded substrate media carrying fine fibers, wherein the fine fibers are extended with the expanding substrate media, thereby improving dust holding capacity and slowing down pressure drop increase.
Description
- This patent application claims the benefit of U.S. Provisional Patent Application No. 61/308,488 filed Feb. 26, 2010; and U.S. Provisional Patent Application No. 61/330,462 filed May 3, 2010; and U.S. Provisional Patent Application No. 61/383,487 filed Sep. 16, 2010; and U.S. Provisional Patent Application No. 61/383,569 filed Sep. 16, 2010, the entire teachings and disclosure of which are incorporated herein by reference thereto.
- This invention generally relates to a filter media, and in particular to a composite filter media comprising an expanded substrate and fine fibers carried thereon, and method of making the same.
- Fluid streams such as liquid flows and gaseous flows (e.g. air flows) often carry particulates that are often undesirable contaminants entrained in the fluid stream. Filters are commonly employed to remove some or all of the particulates from the fluid stream.
- Filter media including fine fibers formed using an electrostatic spinning process is also known. Such prior art includes Filter Material Construction and Method, U.S. Pat. No. 5,672,399; Cellulosic/Polyamide Composite, U.S. Patent Publication No. 2007/0163217; Filtration Medias, Fine Fibers Under 100 Nanometers, And Methods, U.S. Provisional Patent Application No. 60/989,218; Integrated Nanofiber Filter Media, U.S. Provision Patent Application No. 61/047,459; Filter Media Having Bi-Component Nanofiber Layer, U.S. Provisional Patent No. 61,047,455, the entire disclosures of which are incorporated herein by reference thereto. As shown in these references nanofibers are commonly laid upon a finished preformed filtration media substrate.
- The invention provides improvement in filter media including fine fibers. These and other advantages of the invention, as well as additional inventive features, will be apparent from the description of the invention provided herein.
- Fine fibers, such as and most preferably electrospun nanofibers according to certain embodiments, laid upon a substrate media can be reoriented after laying by modifying the substrate media, such as by modifying the thickness of that substrate media after the fine fibers are deposited. For example, an at least partially compacted substrate media (such as calendared media) can be expanded, in which larger fibers carry with them the smaller fibers thus also expanding the fine fiber layer. As a consequence, several advantages can flow from this, including greater volumetric coverage of nanofibers (more volumetric coverage for a same basis weight application—as the expansion can open up and expand the nanofibers into a 3D matrix); reduced pressure drop due to expansion; and/or slower pressure drop increase as it loads. Additionally, the undulating 3 dimensional characteristics of the nanofiber or other such fine fiber layer greatly increase dust holding capacity as it is believed to effectively create an undulating surface with a much greater volumetric holding area as opposed to merely flat, as in the case of prior systems—thus the effective volumetric area of the nanofiber layer can be increased.
- In one embodiment, the substrate is a bi-component scrim including a high melt component and a low melt component. The fine fibers are electrospun polymer nanofibers. The high melt component and the electrospun polymer nanofibers have a higher melting temperature than the low melt component. The bi-component scrim has an unexpanded state and an expanded state, wherein the expanded bi-component scrim has a thickness greater than the unexpanded state. For example, the scrim in the unexpanded state may be preformed and calendared and thereby or otherwise at least partially compressed in which the fibers held in position in a biased state by being bonded and thereby held to one another (large fiber to fiber bonds holding these large fibers in place). In one embodiment, the unexpanded bi-component scrim carrying the fine fibers is expanded by heating, wherein the low melt component melts or softens and bonds with the fine fibers. During this heating, the larger fibers of the substrate are also freed from at least partially compressed state and allowed to slide about and move back toward a more natural state—such as at least partially toward uncompressed and expanded state (e.g. toward the uncompressed that occurred prior to the formation of the scrim in the first place). During heating, the larger fibers of the bi-component scrim are relaxed and reoriented, carrying the much smaller fine fibers therewith, wherein the fine fibers extend with expanding bi-component scrim. The resulting composite filter media has an undulating surface and an expanded thickness causing the fine fibers to not merely have a planar characteristic as is the case with conventional nanofiber laying techniques, but a 3 dimensional matrix. The expanded filter media has improved dust holding capacity, a slower pressure drop increase as dust loads, and/or lower initial pressure drop.
- In one aspect, the invention provides a method of making a filter media. The method includes steps of depositing fine fibers on a surface of a substrate having a first thickness, the fine fibers having an average diameter of less than 1 micron, and expanding the substrate to a second thickness greater than the first thickness carrying the fine fibers therewith.
- In another aspect, the invention provides a filter media comprising a substrate of first fibers having an average fiber diameter of greater than 1 micron carrying fine fibers having an average fiber diameter of less than 1 micron. The substrate has an undulating surface, wherein the fine fibers are integrated into 3-dimensional matrix with the first fibers of the undulating surface.
- Other aspects, objectives and advantages of the invention will become more apparent from the following detailed description when taken in conjunction with the accompanying drawings.
- The accompanying drawings incorporated in and forming a part of the specification illustrate several aspects of the present invention and, together with the description, serve to explain the principles of the invention. In the drawings:
-
FIG. 1 is a schematic cross-sectional view of an expanded composite filter media having an undulating surface comprising fine fibers carried by a substrate media according to an embodiment of the present invention; -
FIG. 2 is a schematic cross-sectional view of the composite filter media ofFIG. 1 in its unexpanded state having a generally flat surface; -
FIG. 3 is a schematic illustration of a concentric sheath/core type bi-component fiber of a substrate media according to an embodiment of the present invention; -
FIG. 4 is a schematic illustration of an eccentric sheath/core type bi-component fiber of a substrate media according to an embodiment of the present invention; -
FIG. 5 is a schematic illustration of a side-by-side type bi-component fiber of a substrate media according to an embodiment of the present invention; -
FIG. 6 is a schematic illustration of a pie wedge type bi-component fiber of a substrate media according to an embodiment of the present invention; -
FIG. 7 is a schematic illustration of a hollow pie wedge type bi-component fiber of a substrate media according to an embodiment of the present invention; -
FIG. 8 is a schematic illustration of an islands/sea type bi-component fiber of a substrate media according to an embodiment of the present invention; -
FIG. 9 is a schematic illustration of a trilobal type bi-component fiber of a substrate media according to an embodiment of the present invention; -
FIG. 10 is a schematic illustration of tipped typed bi-component fiber of a substrate media according to an embodiment of the present invention; -
FIG. 11 is a schematic cross-sectional view of a composite filter media in an unexpanded state according to an embodiment of the present invention; -
FIG. 12 is a schematic cross-sectional view of the composite filter media ofFIG. 11 in its expanded stated; -
FIG. 13 is a schematic cross-sectional view of an expanded composite filter media according to a different embodiment of the present invention; -
FIG. 14 is a schematic illustration of a system for making an expanded composite filter media according to an embodiment of the present invention; -
FIG. 15(A) is a Scanning Electron Microscopic image of bi-component fibers and the fine fibers proximate the surface of the substrate media of the expanded composite filter media ofFIG. 1 taken at a magnification level ×300; -
FIG. 15(B) is a Scanning Electron Microscopic image of bi-component fibers and the fine fibers proximate the surface of the substrate media of the expanded composite filter media ofFIG. 1 taken at a magnification level ×1,000; -
FIG. 15(C) is a Scanning Electron Microscopic image of bi-component fibers and the fine fibers proximate the surface of the substrate media of the expanded composite filter media ofFIG. 1 taken at a magnification level ×2,000; -
FIG. 15(D) is a Scanning Electron Microscopic image of bi-component fibers and the fine fibers proximate the surface of the substrate media of the expanded composite filter media ofFIG. 1 taken at a magnification level ×10,000; -
FIG. 16 is a schematic illustration of a system for making an expanded composite filter media according to another embodiment of the present invention; -
FIG. 17 is a graph showing MFP Efficiency test results of an expanded composite filter media according to an embodiment of the present invention and two other conventional filter medias; -
FIG. 18 is a graph showing MFP Dust Holding test results over a 200 minutes test period of the expanded composite filter media ofFIG. 17 and two other conventional filter medias; -
FIG. 19 is a graph showing MFP Dust Holding test results over a 650 minutes test period of the expanded composite filter media ofFIG. 17 and two other conventional filter medias; -
FIG. 20 is an optical microscopic image of an unexpanded substrate media in the form of a scrim before heat expansion, taken at a magnification level ×120, according to an embodiment of the present invention; -
FIG. 21 is an optical microscopic image of an expanded composite media including two fine fiber coated substrate medias laminated together with the fine fiber layers facing each other, such as the expanded composite media ofFIG. 12 , taken at a magnification level ×120, according to an embodiment of the present invention; -
FIG. 22 is a perspective view of a pleated filter element according to an embodiment of the present invention, wherein the pleated filter media is formed by pleating an expanded composite filer media; -
FIG. 23 is a perspective view of a fluted filter element according to an embodiment of the present invention, wherein the fluted filter media is formed of an expanded composite filter media; -
FIG. 24 is a Scanning Electron Microscopic image taken at a magnification level ×2,500 of a composite filter media including two medias coated with fine fibers and laminated together such that the fine fibers are facing each other, according to an embodiment of the present invention; and -
FIG. 25 is a perspective view of a panel filter according to an embodiment of the present invention, wherein the pleated filter media is formed of an expanded composite filter media; -
FIG. 26 is a schematic illustration of a system for making an expanded composite filter media including two layers of fine fiber coated medias laminated together with the fine fibers facing each other, according to an embodiment of the present invention; and -
FIG. 27 is a schematic illustration of a system for making an expanded composite filter media including two layers of fine fiber coated media and another layer of media laminated together with each layer of fine fibers sandwiched between medias, according to an embodiment of the present invention. - While the invention will be described in connection with certain preferred embodiments, there is no intent to limit it to those embodiments. On the contrary, the intent is to cover all alternatives, modifications and equivalents as included within the spirit and scope of the invention as defined by the appended claims.
-
FIG. 1 is a schematic cross-sectional view of acomposite filter media 10 according to an embodiment of the present invention. As shown, thecomposite filter media 10 comprises asubstrate media 12 andfine fibers 14 carried along asurface 16 of thesubstrate media 12. Thecomposite media 10 has an undulatingsurface 18, which is illustrated only very schematically inFIG. 1 , which is formed by expansion of thesubstrate media 12. - To form the expanded
composite filter media 10 ofFIG. 1 , compressed and at least partially compacted media is used as shown inFIG. 2 .FIG. 2 is a schematic cross-sectional view of acomposite filter media 10 ofFIG. 1 in an unexpanded state prior to the expansion, which can also be seen as thefine fibers 14 that have been deposited prior to the expansion. As shown, thecomposite filter media 10 has a generallyflat surface 20 prior to expansion, wherein thefine fibers 14 form a generally flat layer. Thesubstrate media 12 in the unexpanded state has a thickness t′. When thecomposite filter media 10 is subjected to the expansion, the thickness of thesubstrate media 12 expands to t as shown inFIG. 1 and the surface relaxes to form the undulatedsurface 18 ofFIG. 1 . In some embodiments, the thickness t can be a least 1.5 times the original thickness, and more preferably nearly doubles or triples or increases even more. - In one embodiment, the expansion of the
filter media 10 is accomplished through a heat treatment, although other relaxants such as a solvent spray (partially soluble to the substrate only), or other processing may be used for relaxing. For example, the scrim in the unexpanded state may be preformed and calendared or otherwise at least partially compressed in which the fibers are held in position in a biased state by being bonded and thereby held to one another (large fiber to large fiber bonds holding these large fibers in place). In one embodiment, the unexpanded bi-component scrim carrying the fine fibers is expanded by heating, wherein the low melt component melts or softens and bonds with the fine fibers. During this heating, the larger fibers of the substrate are also freed from at least partially compressed state and allowed to slide about and move back toward a more natural state—such as at least partially toward uncompressed and expanded state (e.g. toward the uncompressed state that occurred prior to the formation of the scrim in the first place). During the heat treatment, according to certain preferred embodiments, fibers of thesubstrate media 12 relax and reorient to increase an average distance between the fibers. As such, thesubstrate media 12 expands, wherein the thickness of thesubstrate media 12 increases and the surface of thesubstrate media 12 becomes undulated as opposed to flat in character. Further, as the fibers proximate the surface of thesubstrate media 12 relax and reorient, thefine fibers 14, which are carried by these fibers move and reorient with the fibers. Thus,fine fibers 14 are extended, pushed and pulled with the larger fibers. - Now that the composite filter media having an expanded thickness and an undulated surface is generally described, according to an embodiment of the present invention, some of its advantages will be discussed before providing further details and other embodiments of the composite filter media.
- There are several factors that affect characteristics of a filter media. Filter or filtration capacity is the amount of particles that a filter captures during its service life. Generally, a higher filter capacity will provide a longer filter life, which can reduce a frequency of filter change or service. Filter capacity is often related to pressure drop or restriction, when the restriction to the desired fluid flow becomes too high (hence increased pressure drop), a filter needs to be changed to facilitate the desired amount of fluid flow. Pressure drop is related to resistance to a fluid flow created by the filter media. Pressure drop is the pressure differential from the dirty side to the clean side of the media. Generally, the higher the resistance, the greater the energy required and/or higher the pressure drop at a given flow rate. Thus, all other considerations being equal, the filter with a lower pressure drop is preferred. Filter efficiency is the percentage of particles that are removed from a fluid stream by the filter media, and is usually given for a particular particle size or sizes. Of course, it is often desirable to remove more particles from the fluid stream, but at the same time not be overly restrictive to fluid flow. The filter life is a duration before a filter needs to be changed or serviced due to the pressure drop becoming too large or blow-throughs.
- The composite filter media, according to embodiments of the present invention, has an expanded thickness and undulating surface providing a greater filter media volume when compared to the unexpanded filter medias which have not been subjected to an expansion process. As it relates to the
nanofiber layer 14 specifically, this is considered a surface loading type layer and by having the area expanded from planar to undulating in nature the effective volumetric area is increased. Thus, based on the expansion, more particles can be captured throughout the increased filter media volume. Further and as discussed above, the fibers of the substrate media and the fine fibers carried thereon are reoriented during the expansion process. Such reorientation of fibers can create improved filter media pore structures to capture particles more efficiently with a less fluid flow resistance. It may also allow a higher coverage level of nanofibers without causing increased resistance because of the nanofiber reorientation. Thus, an expanded composite filter media can improve filter efficiency while maintaining a same level of pressure drop, or lower pressure drop while maintaining a same filter efficiency, when compared to the composite filter media in its unexpanded state. Therefore, the composite filter media having an expanded thickness and an undulating surface can improve the filtration quality by providing an increased dust holding capacity, a reduced pressure drop and/or restriction, and/or a longer filter life. - Returning to
FIGS. 1 and 2 , more detailed construction of thecomposite filter media 10 will now be discussed. Thesubstrate media 12 can be formed of any suitable porous material. Preferably, thesubstrate media 12 is formed of a multi-component filter media. - As used herein, the term “multi-component filter media”, “multi-component media” and other similar terms can be used interchangeably to refer to filter medias including at least two different materials. For example, a multi-component filter media can comprise fibers formed of a first material and fibers formed of a second material, wherein the first material and the second material are different materials. Alternatively, a multi-component filter media can be formed of fibers including at least two different materials, such as fibers including a core formed of the first material and a sheath formed of the second material, as described in detail below. A multi-component filter media including two different materials is refer to herein as “bi-component filter media”, “bi-component media”, and like terms.
- In one preferred embodiment, the
substrate media 12 is formed of bi-component fibers including two different materials having different melting points. A composite filter media comprising fine fibers and a substrate media formed of such multi-component fibers are described in Multi-Component Filter Media with Nanofiber Attachment, PCT Patent Application No. PCT/US09/50392, which is assigned to the assignee of the present application, the entire disclosure of which are incorporated herein by reference thereto. - In this embodiment, one component of the bi-component fibers of
substrate 12 has a lower melting point than the other component. The low melt component can be any suitable polymers such as polypropylene, polyethylene, or polyester. The other component may be a polymer having a higher melting point than the low melt component, or other suitable fiber materials such as glass and/or cellulose. Preferably, the fibers are compressed to form thesubstrate media 12 in the form of a web of media or scrim having a certain thickness. - In one embodiment, the
substrate media 12 is a scrim formed of bi-component fibers including a high melt polymer component and a low melt polymer component. For example the bi-component may comprise a high-melt polyester and a low-melt polyester, in which one has a higher melting temperature than the other.FIG. 3 schematically illustrates abi-component fiber 22 according to one embodiment. As shown, the bi-component 22 is a concentric sheath/core type, wherein acore 24 is formed of a high melt polymeric component and asheath 26 is formed of a low melt polymeric component. - The high melt polymer component is formed of a polymer having a higher melting temperature than the low melt polymer component. Suitable high melt polymers include, but are not limited to, polyester and polyamide. Suitable low melt polymers include polypropylene, polyethylene, co-polyester, or any other suitable polymers having a lower melting temperature than the selected high melt polymer. For example, bi-component fibers may be formed of a polyester core and a polypropylene sheath. In this embodiment, the bi-component fibers are formed of two different types of polyesters, one having a higher melting point than the other.
- The fibers of the
substrate media 12 are formed to have a larger average fiber diameter than that of thefine fibers 14. Preferably, the fibers of thesubstrate media 12 has an average fiber diameter of greater than about 1 micron, and more preferably, greater than 5 micron. In one embodiment, an average diameter of the fibers of thesubstrate media 12 are between about 1 micron and about 40 micron. In the unexpanded state, the coarser fibers are compressed, for example via a set of calendering rollers, to form thesubstrate media 12 having a thickness between about 0.05 and 1.0 mm, preferably between about 0.1 and 0.5 mm. Such bi-componentfiber substrate media 12 can provide a structural support necessary for thefine fibers 14. Various thicknesses bi-component scrims suitable for thesubstrate media 12 are commercially available through HDK Industries, Inc. of Rogersville, Tenn., or other filter media suppliers. Thus, the substrate may be preformed off the shelf bi-component media. - Other types of bi-component fibers may be used to form the
substrate media 12 in other embodiments. Some examples of different types of bi-component fibers are schematically illustrated inFIGS. 4-10 . An eccentric sheath/coretype bi-component fiber 28 comprising acore 30 and asheath 32 is shown inFIG. 4 . This fiber is similar to the concentricsheath core fiber 22, but with the core 30 shifted off-center. The different shrinkage rates of the two polymer components can cause the fiber to curl into a helix when heated. This allows an otherwise flat fiber to develop crimp and bulk, and can result in different fiber reorientation, expansion and/or undulation of surface under heat. -
FIG. 5 schematically illustrates a side-by-sidetype bi-component fiber 34 including afirst polymer component 36 and asecond polymer component 38. Depending on an application, the first polymer component may be a higher or lower melt polymer than the second polymer component. This is a further extension of the eccentric sheath/core fiber, in which both polymers occupy a part of the fiber surface. With proper polymer selection, this fiber can develop higher levels of latent crimp than the eccentric sheath/core fiber 28. - A pie wedge
type bi-component fiber 40 is schematically illustrated inFIG. 6 . Thepie wedge fiber 40 comprises a plurality of adjacent wedges formed of afirst polymer component 42 and asecond polymer component 44. Each of thefirst polymer component 42 has asecond polymer component 44 on either side. Thefirst polymer component 42 may be a higher or lower melt polymer than thesecond polymer component 44. These fibers are designed to be split into the component wedges by mechanical agitation (typically hydroentangling), yielding microfibers of 0.1 to 0.2 denier in the filter media. -
FIG. 7 is a schematic illustration of a hollow pie wedgetype bi-component fiber 46 comprisingfirst polymer wedges 48 andsecond polymer wedges 50. Again, depending on an application, thefirst polymer wedges 48 may be formed of a higher or lower melt polymer than thesecond polymer wedges 50. The hollowpie wedge fiber 46 is similar to thepie wedge fiber 40 but with ahollow center 52 core that prevents the inner tips of the wedges from joining, thus making splitting easier. -
FIG. 8 is a schematic illustration of a islands/seatype bi-component fiber 54. This fiber is also known as the “pepperoni pizza” configuration where afirst polymer component 56 is the pepperoni and asecond polymer component 58 is the cheese. In some embodiments, thefirst polymer component 56 is formed of a higher melt polymer than thesecond polymer component 58, or thesecond polymer component 58 is formed of a soluble polymer. In such embodiments, this fiber allows the placement of many fine strands ofhigh melt polymer 56 within a matrix of low melt orsoluble polymer 58 that is subsequently melted or dissolved away. This allows the production of a media made of fine microfiber because the fibers are easier to process in the “pizza” form rather than as individual “pepperonis.” Staple fibers can be made of 37 pepperonis on each pizza, producing fibers about 0.04 denier (about 2 microns diameter), or even finer. - The bi-component fibers may be formed into different shapes. For example, some bi-component fibers may not have a cylindrical shape with a circular cross section as the bi-component fibers described above.
FIGS. 9 and 10 illustrate some examples of bi-component fibers with irregular shapes. Although, these fibers do not have a circular cross section, each has a diameter in context of the present invention. The diameter of the fibers having a non-circular cross section is measured from the outer perimeter of the fiber.FIG. 9 is a schematic illustration of a trilobaltype bi-component fibers trilobal fibers first polymer component second polymer component trilobal fibers diameter first polymer component second polymer component -
FIG. 10 is a schematic illustration of a tippedtype bi-component fibers fiber 78 is a tipped trilobal bi-component fiber with afirst polymer center 82 andsecond polymer tips 84. Thefiber 80 is a tipped cross bi-component fiber with afirst polymer center 86 andsecond polymer tips 88. Preferably, thefirst polymer center second polymer tips - The
fine fibers 14 can be deposited on thesubstrate media 12 as they are formed. Alternatively, thefine fibers 14 may be separately prepared as a web of a media, then laminated with thesubstrate media 12. Although, thefine fibers 14 may comprise fibers having various fiber diameters, preferably, thefine fibers 14 are nanofibers having very fine fiber diameter. Suchfine fibers 14 can be formed by electrospinning or other suitable processes. In one embodiment, thefine fibers 14 are electrospun nanofibers having an average fiber diameter less than about 1 micron, preferably less than 0.5 micron, and more preferably between 0.01 and 0.3 microns. Such small diameter fine fibers can pack more fibers together without significantly increasing overall solidity of the filter, thus can increase filter efficiency without increasing pressure drop. - The
fine fibers 14 may be formed by various suitable polymeric materials. In one embodiment, thefine fibers 14 can be formed of nylon-6 (polyamide-6, also referred to as “PA-6” herein) via electrospinning, wherein the electrospunfine fibers 14 are deposited directly on thesubstrate media 12, although any polymer may be used. To avoid destruction of the fine fibers during heat expansion, thefine fibers 14 are formed of a material having a higher melt temperature than the low-melt polymer of the bi-component. In this embodiment, thesubstrate media 12 is a scrim formed of bi-component staple fibers having a high melt polyester core and a low melt polyester sheath. The bi-component staple fibers are compressed between a set of calendering rollers to form a web of scrim. The bonding between thesubstrate media 12 and thefine fibers 14 may involve solvent bonding, pressure bonding, and/or thermal bonding. In one embodiment, the low melt may be used to bond the fine fibers to the coarser fibers of the substrate, as shown inFIGS. 15A-15D . In this manner, when the coarser substrate fibers are mobilized through the relaxing process and slide around, they carry the more delicate fine fibers therewith which are bonded thereto. - The
composite filter media 10 before expansion has a thickness t′ and a substantiallyflat surface 20 as shown inFIG. 2 . This unexpandedcomposited filter media 10 is heat treated, for example at 250° F. for 5 minutes, wherein the compressed fibers of thesubstrate media 12 are relaxed and reoriented, thereby expanding thesubstrate media 12. As a result, the thickness of thesubstrate media 12 expands to t, and the substantiallyflat surface 20 ofFIG. 2 relaxes to form an undulatingsurface 18 as shown in FIG. 1—it will be appreciated that the undulated surface will be irregular as opposed to the ordinarily planar nature of a substrate/scrim such as those commercially available. Indeed, filter media rolls typically come in prewound rolls of media that is usually characterized for many medias as generally flat in character. As the coarser substrate fibers proximate, the surface of thesubstrate media 12 are relaxed and reoriented, thefine fibers 16 carried by these fibers also move with the fibers and are extended and integrated into 3-dimensional matrix with fibers of the undulating surface. Further, the low melt polyester of the bi-component fibers melts or becomes soft during the heat treatment, which allows the adjacent fine fibers to embed in the low melt polyester and enhance bonding between the bi-component fibers and thefine fibers 14. - In one embodiment, the
substrate media 12 is formed of a bi-component fiber scrim having an average fiber diameter between about 1 and 40 microns and a base weight between about 0.5 and 15 oz/yd2. Thefine fibers 14 have an average fiber diameter between about 0.01 and 0.5 microns and fine fiber coverage between about 0.012 g/m2 and 0.025 g/m2. In this embodiment, the expandedcomposite filter media 10 has a Frazier air permeability between about 100 and 200 CFM; a MFP efficiency equivalent to MERV 11-16; and a MFP dust holding weight of about 400-600 mg/100 cm2 with a final pressure drop of about 1.5 inch W.G. -
FIGS. 11 and 12 illustrate acomposite filter media 90 according to a different embodiment of the present invention. Thecomposite filter media 90 comprises amedia 92 andfine fibers 93 in addition to thesubstrate media 12 and thefine fibers 14 of thecomposite filter media 10 ofFIG. 2 . As shown, thefine fibers composite filter media 90 are sandwiched between thesubstrate media 12 and themedia 92. Themedia 92 and thesubstrate media 12 may be formed of a same scrim or filter media or different scrims or filter medias. Thecomposite filter media 90 can be constructed, for example, by laminating two layers ofcomposite filter media 10 ofFIG. 2 , such that the fine fibers face each other, and expanding the substrate media layers, wherein fine fibers are reoriented with the adjacent substrate media. - In one embodiment, the
substrate media 12 is a scrim formed of low melt polyester/high melt polyester bi-component fibers as described in the previous embodiment. Thefine fibers 14 are electrospun nylon-6 nanofibers deposited on thesubstrate media 12. Similarly, themedia 92 is deposited with the electrospun nylon-6 nanofibers forming thefine fibers 93. Thesubstrate media 12 deposited with thefine fibers 14 and themedia 92 deposited with thefine fibers 93 are laminated together such that thefine fibers 14 and thefine fibers 93 are facing each other to form thecomposite filter media 90 ofFIG. 11 . In this embodiment, themedia 92 is formed of the same scrim used for thesubstrate media 12. Thefine fibers 14 and thefine fibers 93 may have a same fine fiber coverage level or different fine fiber coverage levels. For example, thefine fibers 14 has a fine fiber coverage level between about 0.005 g/m2 and 0.030 g/m2, preferably between about 0.012 g/m2 and 0.025 g/m2. Similarly, thefine fibers 93 has a fine fiber coverage level between about 0.005 g/m2 and 0.030 g/m2, preferably between about 0.012 g/m2 and 0.025 g/m2. Therefore, when laminated, the two layers of thefine fibers composite filter media 90 may optionally be compressed using a set of rollers to facilitate bonding amonglayers FIG. 11 , the unexpandedcomposite filter media 90 has a substantiallyflat surface 94 and a thickness t″. The unexpandedcomposite filter media 90 is then heat treated as it was with the previous embodiments. The heat treatment can be performed at or near the melting temperature of the low melt component of the bi-component fibers. In this embodiment, the unexpandedcomposite filter media 90 is heated to or near the melting temperature of the low melt polyester. - During the heat treatment, the bi-component fibers of the
substrate media 12 and themedia 92 are relaxed and reoriented to expand the thickness of thecomposite filter media 90 to t′″ and form an undulatingsurface 96, as shown inFIG. 12 . As the bi-component fibers of thesubstrate media 12 relax and reorient, thefine fibers 14 also move with the adjacent bi-component fibers of thesubstrate media 12. Similarly as the bi-component fibers of themedia 92 relax and reorient, thefine fibers 93 also move with the adjacent bi-component fibers ofmedia 92. - Such
composite filter media 90 having an expanded thickness and an undulating surface can have superior dust holding capability and reduced pressure drop when compared to the unexpanded composite filter media or other conventional filter medias. Further, the increased filter media volume due to the filter media expansion via the relaxation make the expanded composite filter media 90 (FIG. 12 ) well suited for a depth filter media having improved dust holding capacity and lower pressure drop, wherein more particles can be trapped throughout the increased volume of thecomposite filter media 90, and the fine fiber layer can in large part set a maximum particle capture efficiency without being unduly restrictive. - While
FIGS. 11 and 12 are schematic,FIGS. 20-21 show actual optical microscopic images of a substrate media and an expanded composite filter media taken at ×120 magnification.FIG. 20 is an optical microscopic image of a substrate media, such as themedias FIG. 11 , before the fine fiber deposition and expansion.FIG. 21 is an optical microscopic image of an expanded composite filter media, wherein two samples of the media ofFIG. 20 are deposited with fine fibers and laminated such that the fine fibers on the two sample medias are facing each other, such as the expandedcomposite filter media 90 shown inFIG. 12 . While the composite filter media ofFIG. 21 includes fine fibers, at this magnification of the image, only the coarse fibers of the media layers can be seen. The fine fibers are much smaller and carried by the coarser fibers, which can be seen with reference toFIG. 24 , which is a Scanning Electron Microscopic image of a composite filter media taken at a magnification level ×2,500. InFIG. 24 , the fine fibers coated on one media layer are in focus in the image, while the fine fibers coated on the other media layer are out of focus in the image. The two layers of fine fiber coated medias are laminated with the fine fibers facing each other, and heat expanded to form an expanded composite filter media. - Depth filter medias load particulates substantially throughout the volume or depth, and thus, the depth medias can be loaded with a higher weight and volume of particulates as compare with surface loading systems over the lifespan of the filter. Usually, however, depth media arrangements suffer from efficiency drawbacks. To facilitate such high holding capacity, a low solidity of media is often chosen for use. This results in large pore sizes that have the potential to allow some particulates to pass more readily. The expanded composite filter media according to embodiments of the present invention can provide superior dust holding capability and filtration efficiency while maintaining a same low level of pressure drop via expanded media and fine fibers.
- In other embodiments, an expanded composite filter media can include multiple layers of fine fibers and multiple filter layers.
FIG. 13 shows acomposite filter media 100 comprising two layers offine fibers filter layers filter layer 104 may not increase or increase very slightly. - Further, the fine fiber layers 16, 102 may include a same amount of fine fibers or different amount of fine fibers. The materials of the filter layers 12, 92, 104 and the amount of fine fibers of the fine fiber layers 16, 102 can be selected to create a gradient depth media. For example, filter layers 12, 92, 104 can be formed of the bi-component fiber scrim similar to the bi-component scrim used for the
substrate media 12 and thefilter layer 92 of the previous embodiments. However, the bi-component fiber scrim of thefilter layer 104 can have less solid density, and thereby less filtration efficiency, than the scrim selected for thefilter layer 92. Further, the scrim selected for thesubstrate media 12 can have more solid density than the scrim used for thefilter layer 92. Further, thefine fiber layer 16 can be formed to include more fine fibers than thefine fiber layer 102. For example, thefine fiber layer 102 can be formed to include electrospun fine fibers of PA-6 at about 0.015 g/m2, while thefine fiber layer 16 is formed to include electrospun fine fibers of PA-6 at about 0.025 g/m2. Preferably, each of the fine fiber layer(s) in the various embodiments has a nanofiber coverage level between about 0.005 g/m2 and 0.030 g/m2, and more preferably between about 0.012 g/m2 and 0.025 g/m2. It should be noted that due to the reorientation of fibers after the deposition/coverage into an undulating 3D matrix, much more fine fibers can be deposited (greater fine fiber coverage or basis weight) without unduly causing restriction or pressure drop issues, and in fact the reverse is true due to the greater effective volumetric area as a result of the expansion. Such gradientcomposite filter media 100 can allow more dust particles to be loaded throughout the thickness of thecomposite filter media 100. - In an embodiment, the
composite filter media 100 in its unexpanded state includes the filter layers 12, 92, 104 formed of a bi-component fiber scrim having a thickness of about 0.005″ and the fine fiber layers 16, 102 comprising electrospun PA-6 nanofibers at a coverage level of about 0.019 g/m2. The unexpandedcomposite filter media 100 has a total thickness of about 0.015″. After the heat expansion, the thickness of the each of the filter layers 12, 92, 104 can increase about 2 to 3 times or even higher, thereby providing the expandedcomposite filter media 100 having the total thickness of 0.030″ or 0.045″ or higher. - Other configurations of the expanded composite filter media may be beneficial to different filtration applications to optimize dust holding and pressure drop characteristics. In other embodiments, an expanded composite filter media may include more than three filter layers and more than two fine fiber layers configured in various orders.
- Additionally, after the expansion of the media resulting in the reorientation of fine fibers, the expanded composite filter media may then be configured into a filter element with a gathered configuration such as a fluted filter or a pleated filter or other such typical filter element arrangement. Such gathered filter arrangements may be in the form of a cylindrical or oval element with end caps, frames and the like and often times with an annular sealing gasket as indicated in some of the patents incorporated by reference herein. This media may also be incorporated into such filter elements. Further, the expanded composite filter media can be pleated and used in a panel filter.
-
FIG. 22 shows apleated filter element 300 including apleated filter media 302 wound about acylindrical core 304, and endcaps pleated filter media 302 can be formed by pleating an expanded composite filter media having an undulating surface, such as the expanded filter medias ofFIGS. 1 , 12 and 13. Such pleated filter element is disclosed in U.S. Pat. No. 4,184,966, the teachings and disclosures of which are hereby incorporated by reference in its entirety to the extent not inconsistent with the present invention. -
FIG. 23 shows afluted filter element 320 according to a different embodiment of the present invention. The fluted filter element includes aframe 324, afilter media seal 326, anannular seal 328, and afluted filter media 330. Thefluted filter media 330 includes a face sheet and a convoluted sheet secured together and wound about acenter frame 332 to define a plurality offlutes 334 including first flutes closed proximate one face and second flutes closed proximate the other face. In this embodiment the face sheet and/or the convoluted sheet can be formed of an expanded composite filter media having an undulating surface, such as the expanded composite filter medias ofFIGS. 1 , 12 and 13. Such fluted filter element is disclosed in U.S. Patent Application Publication No. 2009-0320424, Filter Frame Attachment and Fluted Filter Having Same, assigned to the present assignee, the teachings and disclosures of which are hereby incorporated by reference in its entirety to the extent not inconsistent with the present disclosure. -
FIG. 25 shows apanel filter 350 according to an embodiment of the present invention. Thefilter media 352 comprises an expanded composite filter media such as the expandedcomposite filter media 90 shown inFIG. 12 . The expanded composite filter media is pleated to form thefilter media 352, which is enclosed in aframe 354 to form thepanel filter 350. - Now that different embodiments of the expanded composite filter media, according to the present invention are described, methods of forming the expanded composite filter media will be explained.
-
FIG. 14 schematically illustrates a representative process of making an expanded composite filter media, which may produce any of the embodiments discussed above, according to a processing embodiment of the present invention. Thesystem 200 include anunwinding station 202, anelectrospinning station 204, aheat treatment station 206 and a rewindingstation 208. - In the
system 200, a roll ofscrim 210 is unwound from the unwindingstation 202. In one embodiment, the roll ofscrim 210 is formed of high melt polyester core/low melt polyester sheath bi-component staple fibers, which were already compressed via a set of calendering rollers to form the roll ofscrim 210 having a desired thickness and solidity. The web ofscrim 212 travels in amachine direction 214 toward theelectrospinning station 204. In theelectrospinning station 204,fine fibers 216 are formed and deposited on the web ofscrim 212 to form acomposite filer media 218. Thecomposite filer media 218 then enters theheat treatment station 206, wherein thecomposite filter media 218 is heated to or near a melting temperature of the low melt polyester. During the heat treatment, thecomposite filter media 218 relaxes and expands to form an expandedcomposite filter media 220, which is rewound on the rewindingstation 208. The bonding between the web ofscrim 212 and thefine fibers 216 is also enhanced during the heat treatment. Each component of thesystem 200 is discussed in detail below. - The scrim may be formed in an upstream process of the system 200 (and either part of a continuous I line process or interrupted 2 line process) or may be purchased in a roll form from a suitable supplier such as HDK or other suitable media supplier such as H&V or Ahlstrom or the like. The scrim can be formed of various suitable materials, such as bi-component fibers of
FIGS. 3-10 as discussed above. Alternatively, the media may be other single component media that may be compressed and held in place via a solvent bond, heat bond or the like. In the case of a bi-component, for example, the concentric sheath/core type bi-component fibers may be coextruded using a high melt polyester as the core and a low melt polyester as the sheath. Such bi-component fibers can then be used to form a scrim or a filter media. In one embodiment, the bi-component fibers are used as staple fibers to form a multi-component filter media or a scrim via conventional dry laying or air laying process. The staple fibers used in this process are relatively short and discontinuous but long enough to be handled by conventional equipment. Bales of the bi-component fibers can be fed through a chute feed and separated into individual fibers in a carding device, which are then air laid into a web of fibers (which itself for purposes of the present disclosure may be considered a substrate). The web of fibers is then compressed using a set of calendering rollers to form the roll of scrim 210 (also which can be considered a substrate). The web of the fibers may optionally be heated before entering the set of calendering rollers. Since thescrim 210 of this embodiment comprises bi-component fibers, including a high melt component and a low melt component, it is also referred to as a bi-component filter media. In some embodiments, the web of fibers are folded before being calendered to form a thicker bi-component filter media. - In a different embodiment, a web comprising high melt polymer fibers such as polyester fibers and a web comprising low melt polymer fibers such as polypropylene fibers can be formed, separated and laminated together to form the roll of bi-component filter media or scrim. In such embodiment, the
fine fibers 216 are deposited on the low melt side of thescrim 212. In this embodiment, the low melt web is substantially thinner than the high melt web, such that the low melt component does not clog the surface of the high melt web when heated and melted. - In another embodiment, the bi-component fiber scrim can be formed via a melt blowing process. For example, molten polyester and molten polypropylene can be extruded and drawn with heated, high velocity air to form coarse fibers. The fibers can be collected as a web on a moving screen to form a
bi-component scrim 210. - The multi-component fiber filter media or scrim may also be spun-bounded using at least two different polymeric materials. In a typical spun-bounding process, a molten polymeric material passes through a plurality of extrusion orifices to form a multifilamentary spinline. The multifilamentary spinline is drawn in order to increase its tenacity and passed through a quench zone wherein solidification occurs which is collected on a support such as a moving screen. The spun-bounding process is similar to the melt blowing process, but melt blown fibers are usually finer than spun-bounded fibers.
- In yet another embodiment, the multi-component filter media is web-laid. In a wet laying process, high melt fibers and low melt fibers are dispersed on a conveying belt, and the fibers are spread in a uniform web while still wet. Wet-laid operations typically use ¼″ to ¾″ long fibers, but sometimes longer if the fiber is stiff or thick. The above discussed fibers, according to various embodiments, are compressed to form a
scrim 210 or a filter media having a desired thickness. - Referring back to
FIG. 14 , the web ofscrim 212 enters theelectrospinning station 204, wherein thefine fibers 216 are formed and deposited on the web ofscrim 212. In theelectrospinning station 204, thefine fibers 216 are electrospun fromeletrospinning cells 222 and deposited on the web ofscrim 212. The electrospinning process of thesystem 200 can be substantially similar to the electrospinning process disclosed in Fine Fibers Under 100 Nanometers, And Methods, U.S. Patent Application Publication No. U.S. 2009/0199717, assigned to the assignee of the present application, the entire disclosure of which has been incorporated herein by reference thereto. Alternatively, nozzle banks or other electrospinning equipment can be utilized to form the fine fibers. Such alternative electrospinning devices or rerouting of chain electrodes of thecells 222 can permit the fibers to be deposited in any orientation desired (e.g. upwardly is shown although fibers can also be spun downwardly, horizontally or diagonally onto a conveyor carrying coarser fibers). - The electrospinning process produces synthetic fibers of small diameter, which are also known as nanofibers. The basic process of electrostatic spinning involves the introduction or electrostatic charge to a stream of polymer melt or solution in the presence of a strong electric field, such as a high voltage gradient. Introduction of electrostatic charge to polymeric fluid in the
electrospinning cells 222 results in formation of a jet of charged fluid. The charged jet accelerates and thins in the electrostatic field, attracted toward a ground collector. In such process, viscoelastic forces of polymeric fluids stabilize the jet, forming a small diameter filaments. An average diameter of fibers may be controlled by the design ofeletrospinning cells 222 and formulation of polymeric solutions. - The polymeric solutions used to form the fine fibers can comprise various polymeric materials and solvents. Examples of polymeric materials include polyvinyl chloride (PVC), polyolefin, polyacetal, polyester, cellulous ether, polyalkylene sulfide, polyarylene oxide, polysulfone, modified polysulfone polymers and polyvinyl alcohol, polyamide, polystyrene, polyacrylonitrile, polyvinylidene chloride, polymethyl methacrylate, polyvinylidene fluoride. Solvents for making polymeric solution for electrostatic spinning may include acetic acid, formic acid, m-cresol, tri-fluoro ethanol, hexafluoro isopropanol chlorinated solvents, alcohols, water, ethanol, isopropanol, acetone, and N-methylpyrrolidone, and methanol. The solvent and the polymer can be matched for appropriated use based on sufficient solubility of the polymer in a given solvent and/or solvent mixture (both of which may be referred to as “solvent”.) For example, formic acid may be chosen for polyamide, which is also commonly known as nylon-6. Reference can be had to the aforementioned patents for further details on electrospinning of fine fibers.
- In the
system 200, an electrostatic field is generated between electrodes in theelectrospinning cells 222 and avacuum collector conveyor 224, provided by a high voltage supply generating a high voltage differential. As shown inFIG. 14 , there may be multipleelectrospinning cells 222, whereinfine fibers 216 are formed. Thefine fibers 216 formed at the electrodes of theelectrospinning cells 222 are drawn toward thevacuum collector conveyor 224 by the force provided by the electrostatic field. Thevacuum collector conveyor 224 also holds and transfers the web of thescrim 212 in themachine direction 214. As configured, the web ofscrim 212 is positioned between theelectrospinning cells 222 and thevacuum collector conveyor 224, such that thefine fibers 216 are deposited on the web ofscrim 212. In embodiments, wherein the web ofscrim 212 is a multi-component filter media including a low melt component on one surface and a high melt component on the other surface, themulti-component scrim 212 is positioned between theelectrospinning cells 222 and thevacuum collector conveyor 224, such that the low melt component surface of the multi-component scrim faces theelectrospinning cells 222. - In one embodiment, the
electrospinning cells 222 contain a polymeric solution comprising polyamide-6 (PA-6) and a suitable solvent consisting of ⅔ acetic acid and ⅓ formic acid. In such a solvent, both acetic acid and formic acid act as a dissolving agent to dissolve PA-6, and acetic acid controls conductivity and surface tension of the polymeric solution. Theelectrospinning cells 222 generate fine fibers formed of PA-6, which are deposited onto the surface of the web ofscrim 212. As thefine fibers 216 are deposited on the surface of the web ofscrim 212, somefine fibers 216 entangle with fibers of the scrim proximate the surface facing theelectrospinning cells 222. When somefine fibers 216 entangle with some fibers proximate the surface of the scrim, some solvent remaining in thefine fibers 216 from the electrospinning process can effectuate a solvent bonding between thefine fibers 216 and the fibers of the web ofscrim 212. To effectuate the solvent bonding, the fibers of the web ofscrim 212 need to be soluble or at least react with the solvent in the fine fibers. A cross-sectional view of thecomposite filter media 218 formed in theelectrospinning station 202 may look like the unexpandedcomposite filter media 10 ofFIG. 2 . - Upon exiting the
electrospinning station 206, thecomposite filter media 218 proceeds to an expansion process. In this embodiment, the expansion of thecomposite filter media 218 is accomplished in theheat treatment station 206. Theheat treatment station 206 can be any suitable conventional oven such as a convection oven, or a heating device utilizing other suitable types of heating mechanism such as an infrared oven. Wherein thescrim 212 comprises high melt/low melt bi-component fibers, thecomposite filter media 218 is heated to or near a melting temperature of the low melt polymer component of the bi-component fibers. As the bi-component fibers of thescrim 212 are heated to or near the melting temperature of the low melt polymer component, the bi-component fibers relax and reposition. Some bi-component fibers, such as the eccentric sheath/core type bi-component fibers ofFIG. 4 , may curl and twist in various directions when subjected to the heat treatment. Further, the bi-component fibers which were compressed together during the forming of the scrim, for example via a set of calendering rollers, are decompressed as the heat releases the compressive force and allows the bi-component fibers to reposition to increase an average distance between the fibers. As such, the web ofscrim 212 expands in its thickness and becomes wavy to form an undulating surface. - Further, as the bi-component fibers proximate the surface carrying the
fine fibers 216 move and reorient, thefine fibers 216 also move with the bi-component fibers. As discussed above, thefine fibers 216 are deposited on the surface of the web ofscrim 212, wherein somefine fibers 216 come in contact with the bi-component fibers proximate the surface of the web ofscrim 212 and may be bonded via solvent bonding. The bonding between bi-component fibers and thefine fibers 216 is enhanced during the heat treatment as the outer low melt polymer component of the bi-component fibers softens or melts and embeds thefine fibers 216. During the heat treatment, thecomposite filter media 218 is heated to at least above the glass transition temperature of the low melt component, and more preferably to or near the melting temperature of the low melt component. For example, thecomposite filter media 218 is heated to or near the melt point of low melt polyester, such that the outer low melt polyester layer of the bi-component fibers melts and bonds with thefine fibers 216 formed of PA-6. In such embodiments, PA-6fine fibers 216 and the high melt polyester core of the bi-component fibers do not melt, since PA-6 and the high melt polyester have a significantly higher melting temperature than that of the low melt polyester. The low melt polyester, which has the lowest melting temperature, melts or softens, and adjacent PA-6fine fibers 216 are embedded in the softened or melted low melt polyester, thereby bonding thefine fibers 216 and the web ofscrim 212 together. Thus, the low melt polyester acts as a bonding agent between thebi-component fiber scrim 212 and thefine fibers 216. -
FIGS. 15(A)-15(D) are Scanning Electron Microscopic (SEM) images of the bi-component fibers ofscrim 212 and thefine fibers 216 proximate the surface of the web ofscrim 212 taken at various magnification levels. As shown in the SEM images taken at magnification levels ×300 and ×1000 ofFIGS. 15(A) and 15(B) , thefine fibers 216 deposited on the web ofscrim 212 form a spider web like fiber structure between the coarser bi-component fibers that are located proximate the surface of thescrim 212. The SEM images taken at higher magnifications (FIG. 15(C) at ×2,000 andFIG. 15(D) at ×10,000) show the bonding between thefine fibers 216 and the bi-component fibers. As shown clearly inFIG. 15(D) , thefine fibers 216 are embedded on the low melt polyester surface of the bi-component fibers. - The
fine fibers 216 which are embedded on the surface of the bi-component fibers move with the bi-component fibers as the bi-component fibers are relaxed and reoriented during the heat treatment. The bi-component fibers may curl, twist and move in different directions as the bi-component fibers are heated. Some bi-component fibers carrying thefine fibers 216 may move outwardly expanding the surface while some bi-component carrying thefine fibers 216 may stay at the original surface level or even move inwardly in the opposite direction. As such, the substantially flat surface of thecomposite filter media 218 becomes undulated as the fibers orient during the heat treatment. Further, the finedfibers 216 which were deposited at the surface level of thescrim 212 are extended as they move with the bi-component fibers, thereby increasing the depth of thefine fibers 216 integration into the web ofscrim 212 as thecomposite filter media 218 expands during the heat treatment. The reorientation of the bi-component fibers and thefine fibers 216 can also improve overall pore structure of the expandedcomposite filter media 218. Therefore, the decrease in percent solid due to the expansion (same amount of fibers with increased volume) and the improved pore structure of the expandedcomposite filter media 218 provide improved filter capacity and a slower pressure drop increase. The expandedcomposite filter media 220 may resemble the expanded composite filter media ofFIG. 1 having the undulating surface and the expanded thickness. - In some embodiments, the expanded
composite filter media 220 may be processed through a set of rollers downstream of the heat treatment station. A small amount of pressure may be applied to the expandedcomposite filter media 220 to facilitate adhesion between thefine fibers 216 and thesubstrate scrim 212 and/or to slightly reduce the thickness thecomposite filter media 220 to a desired thickness. However, the expandedcomposite filter media 220 substantially retains the undulating surface and the expanded thickness from the heat treatment through the set of rollers. -
FIG. 16 schematically illustrates asystem 230 for making an expanded composite filter media according to a different embodiment of the present invention. Thesystem 230 includes anequipment 232 for forming asubstrate media 236, anequipment 234 for forming afilter layer 238, anelectrospinning station 240, a set ofrollers 242, aheat treatment station 244 and an rewindingstation 252. - The
substrate media 236 and thefilter layer 238 may be formed of various suitable materials and methods. Further, thesubstrate media 236 and thefilter layer 238 may be formed of a same filter media or scrim, or different filter medias or scrims. In one embodiment, thesubstrate media 236 and thefilter layer 238 are formed of a same bi-component fiber scrim. In this embodiment, bi-component staple fibers comprising a high melt polyester core and a low melt polyester sheath are formed in to a web of scrim having a desired thickness and width in theequipment 232 and theequipment 234. - The
substrate media 236 comprising the bi-component fiber scrim enters theelectrospinning station 240, wherein PA-6nanofibers 254 are formed and deposited on the surface of thesubstrate media 236 in the manner described for theelectrospinning station 204 ofFIG. 14 . Thesubstrate media 236 carrying thefine fibers 254 is then laminated with thefilter layer 238 via the set ofrollers 242. As shown, thefilter layer 238 is laminated on the fine fiber deposited side of thecomposite filter media 246. The set ofrollers 242 may apply a desired amount of pressure to enhance bonding between thefine fibers 254 and thesubstrate media 236 and bonding between thefine fibers 254 and thefilter layer 238. Thecomposite filter media 248 exiting the set ofrollers 242 may look like the unexpandedcomposite filter media 90 ofFIG. 11 . - The
composite filter media 248 then enters theheat treatment station 244. In theheat treatment station 244, thecomposite filter media 248 is heated to or near the melting point of the low melt polyester component of the bi-component fibers. The bi-component fibers of thesubstrate media 236 and thefilter 238 relax and reorient as described above with regard to the embodiment ofFIG. 14 . As discussed above, thefine fibers 254 are also reoriented with the bi-component fibers. The expandedcomposite filter media 250 exiting theheat treatment station 244 may look like the expanded composite filter media ofFIG. 12 . The expandedcomposite filter media 250 has an expanded thickness and an undulating surface. Finally, the expandedcomposite filter media 250 is wound into a roll in the rewindingstation 252. In some embodiments, the expandedcomposite filter media 250 may be processed through a set of rollers downstream of the heat treatment station. A small amount of pressure may be applied to the expandedcomposite filter media 250 to facilitate adhesion between different layers and/or to slightly reduce the thickness thecomposite filter media 250 to a desired thickness. However, the expandedcomposite filter media 250 substantially retains the undulating surface and the expanded thickness from the heat treatment through the set of rollers. -
FIG. 26 schematically shows asystem 400 for making an expanded composite filter media according to a different embodiment of the present invention. Thesystem 400 includes two unwindstations oven 406, and arewind station 408. A roll of fine fiber coatedmedia 410 including asubstrate media 414 andfine fibers 418 is unwound from the unwindstation 402 with thefine fibers 418 facingfine fibers 420 of a fine fiber coatedmedia 412. The roll of fine fiber coatedmedia 412 including asubstrate media 416 andfine fibers 420 is unwound from the unwindstation 404 with thefine fibers 420 facing thefine fibers 418. Thefine fibers substrate media system 200 ofFIG. 14 . In this embodiment, thefine fibers - Two layers of the fine fiber coated
medias rollers 422, wherein a pressure is applied to facilitate adhesion betweenlayers rollers 422 may be heated to enhance adhesion betweenlayer composite filter media 424, before entering theoven 406, looks similar the unexpandedcomposite filter media 90 shown inFIG. 11 . Thecomposite filter media 424 enters theoven 406. In the oven, thecomposite filter media 424 is heated to or near a melting point of the low melt polyester, wherein thesubstrate medias substrate media 414 expands, thefine fibers 418 carried by the coarse bi-component fibers of thesubstrate media 414 also move and reorient into a 3-dimensional matrix. Similarly, as thesubstrate 416 expands, thefine fibers 420 carried by the coarse bi-component fibers of thesubstrate media 416 move and reorient into a 3-dimensional matrix. Further, as thecomposite filter media 424 is heated, a thermal bonding can be effectuated to enhance adhesion betweenlayers oven 406, the expandedcomposite filter media 426 looks similar to the expandedcomposite filter media 90 ofFIG. 12 , wherein the fine fiber layers 418, 420 are laminated facing each other. The expandedcomposite filter media 426 is wound into a roll on therewind station 408. -
FIG. 27 . schematically illustrates asystem 430 for making an expanded composite filter media according to yet another embodiment of the present invention. Thesystem 430 includes three unwindstations oven 438, and arewind station 440. A roll of fine fiber coatedmedia 442 including asubstrate media 448 andfine fibers 452 is unwound from the unwindstation 432 with thefine fibers 452 facing asubstrate media 450 of a roll of fine fiber coatedmedia 444. The roll of fine fibers coatedmedia 444 including asubstrate layer 450 andfine fibers 454 is unwound from the unwindstation 434 with thesubstrate layer 450 facing thefine fibers 452. The fine fiber coatedmedia 442 and the fine fiber coatedmedia 444 are laminated between a set ofrollers 456, wherein a pressure is applied to facilitate adhesion betweenlayers rollers 456 may be heated to enhance adhesion betweenlayers media 446 is unwound from the unwindstation 436 and laminated on top of thefine fibers 454 via a set ofrollers 458. A further pressure may be applied by the set ofrollers 458 to facilitate lamination between layers. The set ofrollers 458 may also be heated to enhance adhesion betweenlayers - The
fine fibers substrate media system 200 ofFIG. 14 . In this embodiment, thefine fibers media 446 comprise the bi-component fiber scrim including high melt polyester/low melt polyester fibers, which is described in the previous embodiments. The laminatedcomposite filter media 460 including three layers ofmedia fine fibers oven 438, wherein thecomposite filter media 460 expands via heat as described in the previous embodiments. As thecomposite filter media 460 is heated in theoven 438, a thermal bonding can be effectuated to improve adhesion betweenlayers oven 438 looks similar to the expandedcomposite filter media 100 shown inFIG. 13 . The expandedcomposite filter media 462 is wound into a roll in therewind station 440. - Test samples for the expanded
composite filter media 100 ofFIG. 13 according to an embodiment of the present invention were prepared in a laboratory. A bi-component fiber scrim comprising a high melt polyester core and a low melt polyester sheath having a basis weight of 1.25 OSY was used for thesubstrate media 12, thefilter layer 92 and thefilter layer 104. - The fine fibers were formed via an electrospinning process from a polymeric solution comprising PA-6. The PA-6 nanofibers were formed and deposited on the bi-component fiber scrim at a coverage level of about 0.019 g/m2. Two layers of such bi-component fiber scrim carrying the fine fibers and an uncoated bi-component fiber scrim were laminated together, such that the fine fibers are sandwiched between the bi-component fiber scrim layers as shown in
FIG. 13 . Then the composite filter media test samples were heated in an oven at about 250° F. for about 5 min. - The samples were tested for efficiency and dust holding capacity, and the test results of the samples were compared with that of other comparable filter medias available in the market. The test protocols for MFP Dust Holding test were: ISO Fine test dust at a concentration of 140 mg/m3, sample size of 1002 cm, face
velocity 10 cm/s. The test protocols for MFP Efficiency test were: ISO Fine test dust at a concentration of 70 mg/m3, sample size of 1002 cm, facevelocity 20 cm/s.FIGS. 17-19 show the efficiency and dust holding test results of the composite test samples compared to two comparable filter medias available through Lydall Inc. (Lydall MERV 14 Grade SC8100 andLydall MERV 11 Grade SC8110.) - As shown in
FIG. 17 , the composite media test sample (CLC Media) performed superior in the efficiency test than Lydall SC8110 and performed very close to Lydall SC8100. However, the composite media test samples (CLC Media Sample 1 and CLC Media Sample 2) performed much better in the dust holding test exhibiting lower pressure drop over the test periods as shown inFIGS. 18 and 19 . - All references, including publications, patent applications, and patents cited herein are hereby incorporated by reference to the same extent as if each reference were individually and specifically indicated to be incorporated by reference and were set forth in its entirety herein.
- The use of the terms “a” and “an” and “the” and similar referents in the context of describing the invention (especially in the context of the following claims) is to be construed to cover both the singular and the plural, unless otherwise indicated herein or clearly contradicted by context. The terms “comprising,” “having,” “including,” and “containing” are to be construed as open-ended terms (i.e., meaning “including, but not limited to,”) unless otherwise noted. Recitation of ranges of values herein are merely intended to serve as a shorthand method of referring individually to each separate value falling within the range, unless otherwise indicated herein, and each separate value is incorporated into the specification as if it were individually recited herein. All methods described herein can be performed in any suitable order unless otherwise indicated herein or otherwise clearly contradicted by context. The use of any and all examples, or exemplary language (e.g., “such as”) provided herein, is intended merely to better illuminate the invention and does not pose a limitation on the scope of the invention unless otherwise claimed. No language in the specification should be construed as indicating any non-claimed element as essential to the practice of the invention.
- Preferred embodiments of this invention are described herein, including the best mode known to the inventors for carrying out the invention. Variations of those preferred embodiments may become apparent to those of ordinary skill in the art upon reading the foregoing description. The inventors expect skilled artisans to employ such variations as appropriate, and the inventors intend for the invention to be practiced otherwise than as specifically described herein. Accordingly, this invention includes all modifications and equivalents of the subject matter recited in the claims appended hereto as permitted by applicable law. Moreover, any combination of the above-described elements in all possible variations thereof is encompassed by the invention unless otherwise indicated herein or otherwise clearly contradicted by context.
Claims (20)
1. A method of making a filter media, comprising:
depositing fine fibers on a surface of a substrate having a first thickness, the fine fibers having an average diameter of less than 1 micron; and
expanding the substrate to a second thickness greater than the first thickness carrying the fine fibers therewith.
2. The method of claim 1 , further comprising forming the substrate, wherein multi-component fibers having a low melt polymer component and a high melt polymer component are compressed to form the substrate having the first thickness.
3. The method of claim 2 , wherein depositing fine fibers comprises electrospinning the fine fibers and depositing the fine fibers directly on the surface of the substrate, wherein some of the fine fibers are attached to some of the multi-component fibers proximate the surface of the substrate.
4. The method of claim 3 , electrospinning the fine fibers involves depositing the fine fibers on the surface of the substrate to obtain a fine fiber coverage between about 0.012 g/m2 and 0.025 g/m2.
5. The method of claim 3 , wherein expanding comprises heating the filter media, wherein the multi-component fibers of the substrate relax and reorient, thereby expanding the substrate to the second thickness and forming an undulating surface; wherein the fine fibers are extended as the fine fibers move with the multi-component fibers carrying the fine fibers, wherein the fine fibers are integrated into 3-dimensional matrix with multi-component fibers of the undulating surface.
6. The method of claim 5 , wherein heating comprises heating the filter media to about a melting temperature of the low melt polymer component, wherein the low melt polymer component melts or softens, wherein some of the fine fibers are embedded in the melted or softened low melt polymer component.
7. The method of claim 1 , wherein the second thickness is at least 1.5 times the first thickness after expansion.
8. The method of claim 1 , wherein the second thickness is at least double the first thickness after expansion.
9. The method of claim 1 , further comprising laminating a filter layer such that the fine fibers are sandwiched between the substrate media and the filter layer, wherein the filter media comprising the substrate media, fine fibers and the filter layer is heated, wherein the substrate and filter layer expand and the fine fibers are extended.
10. The method of claim 1 , further comprising laminating multiple layers of the substrate carrying the fine fibers and a filter layer, such that each layer of the fine fibers is sandwiched between the substrates or between the substrate and the filter layer; wherein the laminated layers are heated, wherein the substrates and the filter layer expand, and fine fibers are extended and integrated within undulating surfaces of the substrates.
11. A filter media comprising:
a substrate of first fibers having an average fiber diameter of greater than 1 micron carrying fine fibers having an average fiber diameter of less than 1 micron, the substrate having an undulating surface such that the fine fibers are integrated into 3-dimensional matrix with the first fibers of the undulating surface.
12. The filter media of claim 11 , wherein the substrate is an expanded scrim comprising multi-component fibers, the expanded scrim having a first unexpanded state, the scrim in the first unexpanded state having a generally flat surface and a thickness less than that of the expanded scrim, the undulating surface being formed during an expansion from the first expansion state to the expanded scrim.
13. The filter media of claim 12 , wherein the multi-component fibers include a first component and a second component, wherein the first component has a higher melting temperature than the second component; wherein the fine fibers are attached to the multi-component fibers of the undulating surface via the second component.
14. The filter media of claim 13 , wherein the first component is formed of a high melt polyester and the second component is formed of a low melt polyester; wherein the fine fibers are electrospun polyamide nanofibers.
15. The filter media of claim 12 , wherein the scrim carries the fine fibers on or proximate a surface level in the first unexpanded state, wherein the first fibers are reoriented in the expanded scrim, the first fibers carrying and extending the fine fibers therewith; wherein fine fibers are integrated beyond the surface level to a greater depth in the expanded scrim than in the unexpanded state.
16. The filter media of claim 15 , wherein the filter media including the expanded scrim has a higher dust holding capacity and a slower pressure drop increase than the filter media including the scrim in the first unexpanded state.
17. The filter media of claim 11 , further including a scrim, wherein the fine fibers are laminated between the substrate and the scrim.
18. The filter media of claim 11 , wherein the filter media comprises multiple layers of the substrate carrying the fine fibers; and further comprising a scrim; wherein the each layer of the fine fibers are sandwiched between layers of the substrate or the substrate and the scrim.
19. The filter media of claim 18 , wherein each layer of the substrate is formed of a multi-component scrim comprising a multi-component fibers, the multi-component fibers including a high melt component and a low melt component; wherein the fine fibers are formed of electrospun polymer nanofibers; wherein the electrospun polymer nanofibers and the high melt component has a higher melting temperature than the low melt component; wherein the multi-component scrim is expanded from an unexpanded state via heating; wherein the low melt component melts or softens during heating and bonds with the fine fibers; wherein the fine fibers are extended as the multi-component scrim expands.
20. The filter media of claim 10 , wherein the substrate is formed of a multi-component fiber scrim having an average fiber diameter between about 1 and 40 microns and a base weight between about 0.5 and 15 oz/yd2; wherein the fine fibers have an average fiber diameter between about 0.01 and 0.5 microns; and each layer of the fine fibers has a fine fiber coverage between about 0.012 g/m2 and 0.025 g/m2; wherein the filter media has a Frazier air permeability between about 100 and 200 CFM, and a MFP dust holding weight of about 400-600 mg/100 cm2 with a final pressure drop of about 1.5 inch W.G.