US20130302252A1

US20130302252A1 - Polyarginine-coated magnetic nanovector and methods of use thereof

Info

Publication number: US20130302252A1
Application number: US13/893,137
Authority: US
Inventors: Miqin Zhang; Omid Veiseh; Chen Fang; Forrest Kievit
Original assignee: University of Washington Center for Commercialization
Current assignee: University of Washington Center for Commercialization
Priority date: 2012-05-11
Filing date: 2013-05-13
Publication date: 2013-11-14
Also published as: US20160153976A1; US11307197B2

Abstract

Polyarginine-coated nanoparticle, and methods for making and using the nanoparticle. The nanoparticle can have a core that includes a material that imparts magnetic resonance imaging activity to the particle and, optionally, include one or more of an associated therapeutic agent, targeting agent, and diagnostic agent.

Description

CROSS-REFERENCE TO RELATED APPLICATION

This application claims the benefit of U.S. Patent Application No. 61/646,101, filed May 11, 2012, expressly incorporated herein by reference in its entirety.

STATEMENT OF GOVERNMENT LICENSE RIGHTS

This invention was made with government support under Grant Nos. RO1CA134213 and RO1EB006043 awarded by the National Institutes of Health. The government has certain rights in the invention.

STATEMENT REGARDING SEQUENCE LISTING

The sequence listing associated with this application is provided in text format in lieu of a paper copy and is hereby incorporated by reference into the specification. The name of the text file containing the sequence listing is 41027_SEQ_FINAL.txt. The text file is 631 Bytes; was created on May 7, 2013; and is being submitted via EFS-Web with the filing of the specification.

BACKGROUND OF THE INVENTION

Small interfering RNAs (siRNAs) can silence gene expression in a highly specific manner for treating genetic disorders, signifying a new approach in cancer therapy through the regulation of aberrant gene expression inherent to cancer. However, the physicochemical characteristics of siRNA (e.g., high molecular weight, anionic charge, and hydrophilic character) hinder its passive diffusion across cell membranes precluding any therapeutic function. Furthermore, siRNA molecules are highly vulnerable to degradation. Thus, for effective siRNA delivery, siRNA carriers are needed to protect siRNA, facilitate cellular entry, avoid endosomal compartmentalization, and promote localization in the cytoplasm where the siRNA cargo can be recognized by the RNA-induced silencing complex (RISC). Inorganic nanoparticles (NPs) designed for this application are propitious as they can be engineered for simultaneous diagnostics and therapeutics (theranostics). Currently, many NP core material formulations such as gold, silica, semiconductors, and metal oxides are being evaluated as siRNA carriers (nanovectors). Among them superparamagnetic iron oxide NPs possess superior physicochemical and biological properties ideal for in vivo magnetic resonance imaging (MRI) and drug delivery.
The success of nanovectors relies on the apt design and integration of coatings that ensure biocompatibility and stability in a biologic milieu and proper intracellular trafficking. To date, most nanovectors developed for gene delivery applications are coated with cationic synthetic polymers (e.g., polyethylenimine (PEI), poly amidoamines (PAMAM)) or lipids. A common characteristic among these carriers is their high cationic charge density at physiological pH, which contributes to both the complex formation with anionic siRNA and interaction with the negatively charged cell membrane. This interaction with cell membranes typically leads to the endocytosis of the nanovector, entrapping the nanovector within cellular endosomal vesicles. Within the cellular endosomes the amino groups of cationic polymers function as proton sponges causing the swelling and eventual rupture of the endosome releasing the nanovector into the cytoplasm, a process known as endosomal escape. However, the high cationic charge density of these synthetic polymers also renders them highly cytotoxic.
Despite the advances in the development of siRNA carriers, a need exists for an siRNA carrier that is effective intracellular delivery of siRNA and that provides a safer alternative to the highly cationic nanovectors. The present invention seeks to fulfill this need and provides further related advantages.

SUMMARY OF THE INVENTION

In one aspect, the present invention provides a nanoparticle having a polyarginine coating. In certain embodiments, the nanoparticle has a core that includes a material that imparts magnetic resonance imaging activity to the particle. The nanoparticle can further include one or more of a therapeutic agent that can be delivered by the particle, a targeting agent to target the nanoparticle to a site of interest, and a diagnostic agent that allows for imaging of the particle.
In one embodiment, the nanoparticle, comprises:
(a) a core having a surface and comprising a core material; and
(b) a polyarginine coating covalently coupled to the surface of the core.
In certain embodiments, the nanoparticle further comprises a therapeutic agent covalently coupled to the nanoparticle. In other embodiments, the nanoparticle further comprises a targeting agent covalently coupled to the nanoparticle. In further embodiments, the nanoparticle further comprises a therapeutic agent and a targeting agent covalently coupled to the nanoparticle.
Suitable therapeutic agents include small organic molecules, peptides, aptamers, proteins, and nucleic acids. In certain embodiments, the therapeutic agent is an RNA (e.g., siRNA) or a DNA. In certain embodiments, the therapeutic agent is covalently coupled to the coating is coupled through a cleavable linkage.
Suitable targeting agents include small organic molecules, peptides, aptamers, proteins, and nucleic acids.
In certain embodiments, the nanoparticles of the invention further comprise a diagnostic agent. Representative diagnostic agents include optical agents, such as fluorescent agents.
In certain embodiments, the nanoparticle's core material is a magnetic material.
In another aspect, the invention provides a composition comprising a nanoparticle of the invention and a carrier suitable for administration to a warm-blooded subject.
In a further aspect of the invention, a method for introducing a nanovector into a cell via transcytosis is provided. In one embodiment, the method includes contacting a cell with a nanoparticle of the invention.
In another aspect of the invention, a method for silencing or reducing the expression level of a gene is provided. In one embodiment, the method includes contacting a cell of interest with a nanoparticle of the invention.
In another aspect, the invention provides a method for treating a tissue. In one embodiment, the method includes contacting a tissue of interest with a nanoparticle of the invention.
In a further aspect of the invention, a method for silencing or reducing the expression level of a gene is provided. In one embodiment, the method includes contacting a cell of interest with a nanoparticle of the invention.
In another aspect, the invention provides a method for detecting cells or tissues by magnetic resonance imaging. In one embodiment, the method includes:
(a) contacting cells or tissues of interest with a nanoparticle of the invention; and
(b) measuring the level of binding of the nanoparticle, wherein an elevated level of binding, relative to normal cells or tissues, is indicative of binding to the cells or tissues of interest.

DESCRIPTION OF THE DRAWINGS

The foregoing aspects and many of the attendant advantages of this invention will become more readily appreciated as the same become better understood by reference to the following detailed description, when taken in conjunction with the accompanying drawings.

FIGS. 1A-1D illustrate chemical schemes for synthesis of representative magnetic nanovectors of the invention. FIG. 1A is a schematic illustration of a representative amidated PEG-passivated iron oxide nanoparticle (NP) useful for making representative transfection vectors of the invention. FIG. 1B illustrates the chemical structures and the pKa's of cationic polymers pLys, pArg, and PEI used to functionalize the NP. FIG. 1C illustrates the covalent coupling of the cationic polymer to NP. to provide the cationic polymer coated nanoparticle. FIG. 1D illustrates the coupling of the fluorophore-modified siRNA to the cationic polymer coated nanoparticle to provide a representative magnetic nanovector of the invention.

FIGS. 2A-2C illustrate the proton NMR spectra of representative nanovectors verifying cation polymer coating attachment. FIG. 2A compares the spectra of NP, PEI, and NP-PEI. FIG. 2B compares the spectra of NP, pLys, and NP-pLys. FIG. 2C compares the spectra NP, pArg, and NP-pArg. All samples were analyzed in D₂O.

FIGS. 3A-3D provides the characterization of representative nanovectors. FIG. 3A compares gel retardation assay results for representative evaluating covalent attachment of siRNA to NPs under normal electrophoresis conditions (Normal Gel) and under heparin treatment (Heparin Gel) to disrupt electrostatic interactions between cationic NPs and anionic siRNA. FIG. 3B compares Z-average hydrodynamic sizes of representative nanovectors before and after siRNA attachment. FIG. 3C compares zeta potentials of representative nanovectors before and after siRNA attachment. FIG. 3D compares TEM images of representative nanovectors at two magnifications (scale bars correspond to 10 nm).

FIGS. 4A and 4B compare titration curves evaluating the buffering capacity (addition of sodium hydroxide) of each nanovector formulation. FIG. 4A compares the titration curves for representative nanovectors. FIG. 4B compares the titration curves for the corresponding cationic polymers.

FIGS. 5A and 5B illustrate the magnetic properties of nanovectors. FIG. 5A compares R2 maps of gel phantoms containing representative nanovectors at different concentrations (mM). FIG. 5B compares R2 relaxivity of representative nanovectors as a function of Fe concentration were used to determine relaxivities, which yielded relaxivity values of 78.2 mM⁻¹S⁻¹for NP-PEG-siRNA, 103.7 mM⁻¹S⁻¹for NP-pArg-siRNA, 131.8 mM⁻¹S⁻¹for NP-pLys-siRNA, and 113.6 mM⁻¹S⁻¹for NP-PEI-siRNA.

FIGS. 6A-6I compare siRNA delivery, cell viability, and GFP knockdown for representative nanovectors. Relative amount of siRNA delivered to C6/GFP⁺ (FIG. 6A), MCF7/GFP⁺ (FIG. 6B), and TC2/GFP⁺ (FIG. 6C) cells by nanovectors of three different formulations. Influence of nanovector treatments on cell viability of C6/GFP⁺ (FIG. 6D), MCF7/GFP⁺ (FIG. 6E), and TC2/GFP⁺ cells (FIG. 6F) (viability was normalized to untreated cells). Efficiency of nanovector treatments on silencing GFP expression in C6/GFP⁺ (FIG. 6G), MCF/GFP⁺ (FIG. 6H), and TC2/GFP⁺ (FIG. 6I) cells (GFP expression was normalized to untreated cells).

FIGS. 7A-7C are confocal fluorescence microscopy images evaluating siRNA internalization and subsequent GFP knockdown for representative nanovectors. Images were acquired from C6/GFP+ (FIG. 7A), MCF7/GFP+ (FIG. 7B), and TC2/GFP+ (FIG. 7C) cells 48 hours post treatment with NP-pArg-siRNA, with untreated cells as a reference. Scale bar corresponds to 20 μm.

FIGS. 8A and 8B are TEM images of C6/GFP⁺ cells treated with three representative nanovector formulations (NP-pLys-siRNA, NP-pArg-siRNA, and NP-PEI-siRNA). FIG. 8A illustrates internalization of nanovectors. FIG. 8B illustrates intracellular localization of nanovectors. Scale bars represent 250 nm.

FIG. 9 is a TEM image of NP-PEG-amine (NP) useful for preparing representative nanovectors of the invention. Scale bar corresponds to 10 nm.

FIG. 10 is a schematic illustration of the preparation a nanoparticle having a modified surface (NP-SAS-PEG-NH₂) useful for preparing representative nanovectors of the invention.

DETAILED DESCRIPTION OF THE INVENTION

The present invention provides a nanoparticle having a polyarginine coating. In certain embodiments, the nanoparticle has a core that includes a material that imparts magnetic resonance imaging activity to the particle. The nanoparticle can further include one or more of a therapeutic agent that can be delivered by the particle, a targeting agent to target the nanoparticle to a site of interest, and a diagnostic agent that allows for imaging of the particle. The therapeutic, targeting, and diagnostic agents can be covalently coupled to the nanoparticle. Methods for making and using the nanoparticles are also provided.
Nanoparticle Having Polyarginine Coating
In one aspect, the invention provides a multifunctional nanoparticle having a polyarginine (pArg) coating. In one embodiment, the nanoparticle comprises (a) a core having a surface and comprising a core material and (b) a polyarginine coating covalently coupled to the surface of the core.
As used herein, the phrase “core having a surface and comprising a core material” refers to a solid nanoparticle. The nanoparticle core is not hollow (e.g., not a solid shell encapsulating a void). The core material can impart functional properties to the nanoparticle (e.g., magnetic properties). The core material is not a polymeric material (e.g., the nanoparticle is not a polymer nanoparticle or a polymeric nanosphere). As used herein the term “polymeric material” refers to an organic polymer material (e.g., poly(glycidyl methacrylate), poly(styrene), poly(alkylacrylate)). The core's surface defines the core's outermost surface. In the practice of the invention, the core's surface is chemically modified to have a coating thereon. In certain embodiments, the nanoparticle core is a solid core comprising a material having magnetic resonance imaging activity (e.g., iron oxide).
The phrase “polyarginine coating covalently coupled to the surface of the core” refers to coating that substantially surrounds the core and that is covalently coupled to the core's surface. The coating can be directly covalently coupled to the core surface or covalently coupled to the core's surface through one or more other materials (e.g., layers intermediate the core surface and polyarginine coating) that are covalently coupled to the core's surface. The term “polyarginine coating” refers to a coating that is prepared by covalently coupling polyarginine to the core's surface or by covalently coupling polyarginine to a material that is covalently coupled to the core's surface. The nature of the covalent coupling of polyarginine to the core's surface to provide the coating is not particularly critical. Polyarginine can be covalently coupled to the surface by any one of a variety of chemistries known to the skilled person.
In certain embodiments, the nanoparticle of the invention, in addition to the polyarginine coating, includes a poly(alkylene oxide) oligomer coupled to the nanoparticle core through a siloxane layer. In this embodiment, the polyarginine is covalently coupled to the poly(alkylene oxide) oligomer (e.g., poly(ethylene oxide) oligomer). A representative process for covalently coupling polyarginine to a nanoparticle core having poly(ethylene oxide) oligomers coupled thereto is illustrated in FIGS. 1A and 1C. Referring to FIG. 1A, the poly(ethylene oxide) oligomer covalently coupled to the core has a terminal amino (—NH₂) group that is functionalized to provide a reactive group (i.e., iodoacetamide) suitable for reaction with a complementary reactive group (i.e., thiol) introduced into the polyarginine (see FIG. 1C). Reaction provides the nanoparticle having a polyarginine coating. In this embodiment, the nanoparticle comprising a poly(alkylene oxide) oligomer intermediate the core and the polyarginine coating. As illustrated in FIG. 1D, the nanoparticle is further modified to include an siRNA (illustrated as including a fluorescent agent coupled thereto) by further suitable functionalization of the nanoparticle and siRNA. The terminal amino groups of the poly(ethylene oxide) oligomer serve as points for functionalization of the nanoparticle. Polyarginine, therapeutic agents (e.g., siRNA), targeting agents, and diagnostic agents can be covalently coupled to the nanoparticle through these terminal amino groups by a variety of chemistries known to those of skill in the art.
As illustrated in FIG. 1A, in certain embodiments, the poly(alkylene oxide) oligomer is covalently coupled to the core through intermediate siloxane linkages. The siloxane layer forms a coating on the core surface. The siloxane is anchored to the core surface (e.g., oxide surface) by interactions between the core surface and functional groups of the siloxane (i.e., to provide core-siloxane linkages). In this embodiment, amino-functionalized poly(alkylene oxide) oligomer is reacted with a suitably functionalized siloxane layer (e.g., carboxylic acid groups). As shown in FIG. 1A, the siloxane layer is covalently coupled to the nanoparticle core and the amino-functionalized poly(ethylene oxide) is covalently coupled to the siloxane layer by amide linkages.
The representative nanoparticle (NP) illustrated in FIG. 1A that is useful for making the functionalized nanoparticles of the invention has a core having a radius from about 5 to about 20 nm (e.g., about 6 nm), a siloxane layer having a radius from about 1 to about 5 nm (e.g., about 2 nm), and a poly(alkylene oxide) layer having a radius from about 2 to about 15 nm (e.g., about 12 nm). The core of the nanoparticle is relatively small (e.g., 5 to 20 nm; 10-15 nm) and monodispersed.
In certain embodiments, the number of amino groups per nanoparticle prior to reaction to provide the siloxane coated nanoparticle is from about 30 to about 200. In one embodiment the nanoparticle includes about 70 amino groups. The nanoparticles of the invention include from about 0.1 to about 0.8 percent by weight polyarginine per nanoparticle. The weight ratio of nanoparticle to siRNA is from about 5 to about 20 (defined as Fe mass of NP: siRNA mass). In certain embodiments, the polyarginine and the siRNA are coupled to the amino groups provided by the amino-polyethylene oxide (PEG-amino). Targeting and/or diagnostic agents can also be covalently coupled to the nanoparticle through these amino groups.
As described herein, the nanoparticles of the invention advantageously include a polyarginine coating. As noted above, the polyarginine coating is prepared by covalently coupling polyarginine to the nanoparticle core or by covalently coupling polyarginine to a material that is covalently coupled to the core. Suitable polyarginines have a molecular weight from about 2,000 to about 200,000 grams/mole. In certain embodiments, the polyarginine has a molecular weight from about 5,000 to about 100,000 grams/mole. In other embodiments, the polyarginine has a molecular weight from about 10,000 to about 50,000 grams/mole. In further embodiments, the polyarginine has a molecular weight from about 7,500 to about 15,000 grams/mole.
In certain embodiments, in addition to the polyarginine coating, the nanoparticle of the invention includes a poly(ethylene oxide) oligomer coupled to the nanoparticle core through a siloxane layer. Suitable poly(ethylene oxide) oligomers include poly(ethylene oxides) (PEO or PEG) and poly(ethylene oxide) copolymers such as block copolymers that include poly(ethylene oxide) and poly(propylene oxide) (e.g., PEO-PPO and PEO-PPO-PEO). In one embodiment, the poly(ethylene oxide) oligomer is a poly(ethylene oxide). In certain embodiments, poly(ethylene oxide) oligomer has a molecular weight (weight average, Mw) of from about 0.3 to about 40 kDa. In others embodiments, the poly(ethylene oxide) oligomer has a molecular weight of from about 1.0 to about 10 kDa. In certain embodiments, the poly(ethylene oxide) oligomer has a molecular weight of about 10 kDa.
The nanoparticle includes a core material. For magnetic resonance imaging applications, the core material is a material having magnetic resonance imaging activity (e.g., the material is paramagnetic). In certain embodiments, the core material is a magnetic material. In other embodiments, the core material is a semiconductor material. Representative core materials include ferrous oxide, ferric oxide, silicon oxide, polycrystalline silicon oxide, silicon nitride, aluminum oxide, germanium oxide, zinc selenide, tin dioxide, titanium, titanium dioxide, nickel titanium, indium tin oxide, gadolinium oxide, stainless steel, gold, and mixtures thereof.
The particle of the invention has nanoscale dimensions. Suitable particles have a physical size less than about 50 nm. In certain embodiments, the nanoparticles have a physical size from about 10 to about 50 nm. In other embodiments, the nanoparticles have a physical size from about 10 to about 30 nm. As used herein, the term “physical size” refers the overall diameter of the nanoparticle, including core (as determined by TEM) and coating thickness. Suitable particles have a mean core size of from about 2 to about 25 nm. In certain embodiments, the nanoparticles have a mean core size of about 7 nm. As used herein, the term “mean core size” refers to the core size determined by TEM. Suitable particles have a hydrodynamic size less than about 150 nm. In certain embodiments, the nanoparticles have a hydrodynamic size from about 20 to about 150 nm. In certain embodiments, the nanoparticles have a hydrodynamic size of about 33 nm. As used herein, the term “hydrodynamic size” refers the radius of a hard sphere that diffuses at the same rate as the particle under examination as measured by DLS. The hydrodynamic radius is calculated using the particle diffusion coefficient and the Stokes-Einstein equation given below, where k is the Boltzmann constant, T is the temperature, and η is the dispersant viscosity:
$R_{H} = \frac{k T}{6 π η D} .$
A single exponential or Cumulant fit of the correlation curve is the fitting procedure recommended by the International Standards Organization (ISO). The hydrodynamic size extracted using this method is an intensity weighted average called the Z average.
The nanoparticles of the invention include the polyarginine-coated nanoparticles described above that further include one or more other agents. Thus, in other embodiments, the nanoparticles of the invention further include one or more of a therapeutic agent that can be delivered by the particle, a targeting agent to target the nanoparticle to a site of interest, or a diagnostic agent that allows for imaging of the particle. The therapeutic, targeting, and diagnostic agents can be covalently coupled to the nanoparticle.
Therapeutic Agents.
Therapeutic agents effectively delivered by the nanoparticles of the invention include small organic molecules, peptides, aptamers, proteins, and nucleic acids. In certain embodiments, the therapeutic agent is an RNA or a DNA (e.g., an siRNA).
Suitable therapeutic agents include conventional therapeutic agents, such as small molecules; biotherapeutic agents, such as peptides, proteins, and nucleic acids (e.g., DNA, RNA, cDNA, siRNA); and cytotoxic agents, such as alkylating agents, purine antagonists, pyrimidine antagonists, plant alkaloids, intercalating antibiotics, antitumor antibiotics (e.g., trastuzumab), binding epidermal growth factor receptors (tyrosine-kinase inhibitors), aromatase inhibitors, anti-metabolites (e.g., folic acid analogs, methotrexate, 5-fluoruracil), mitotic inhibitors (e.g., taxol, paclitaxel, docetaxel), growth factor inhibitors, cell cycle inhibitors, enzymes, topoisomerase inhibitors, biological response modifiers, anti-hormones, anti-androgens, and various cytokines for immunotherapy. Representative cytotoxic agents include BCNU, cisplatin, gemcitabine, hydroxyurea, paclitaxel, temozomide, topotecan, fluorouracil, vincristine, vinblastine, procarbazine, dacarbazine, altretamine, cisplatin, methotrexate, mercaptopurine, thioguanine, fludarabine phosphate, cladribine, pentostatin, fluorouracil, cytarabine, azacitidine, vinblastine, vincristine, etoposide, teniposide, irinotecan, docetaxel, doxorubicin, daunorubicin, dactinomycin, idarubicin, plicamycin, mitomycin, bleomycin, tamoxifen, flutamide, leuprolide, goserelin, aminoglutethimide, anastrozole, amsacrine, asparaginase, mitoxantrone, mitotane, and amifostine.
Suitable therapeutic drugs include siRNAs and antitumor tumor drugs than function in cytoplasm.
In one embodiment, the invention provides a nanoparticle, comprising:
(a) a core comprising a magnetic material and having a surface;
(b) a polyarginine coating covalently coupled to the surface; and
(c) a therapeutic agent.
For this embodiment, suitable therapeutic agents are as described above.
For embodiments of the invention that include therapeutic agents, the therapeutic agent can be covalently coupled to the nanoparticle or non-covalently (e.g., ionic) associated with the nanoparticle. For therapeutic agent delivery, the therapeutic agent can be covalently linked (e.g., through a cleavable linkage) or physically adsorbed to (e.g., electrostatic or van der Waals interactions) to the nanoparticle, or embedded within the nanoparticle's coating.
In certain embodiments, the therapeutic agent is covalently coupled to the nanoparticle through a cleavable linkage. Suitable cleavable linkages include linkages cleavable under acidic conditions such as in the acidic microenvironment of cancer cell (e.g., pH less than physiological pH, from about 4.0 to about 6.8. Representative cleavable linkages include acetal, hydrazone, orthoester, and thioester linkages.
For embodiments of the nanoparticle that include a nucleic acid therapeutic agent (e.g., siRNA), the nanoparticle is a nanovector. For these embodiments, the terms “nanoparticle” and “nanovector” are used interchangeably.
Targeting Agents.
Suitable targeting agents include compounds and molecules that direct the nanoparticle to the site of interest. Suitable targeting agents include tumor targeting agents. Representative targeting agents include small molecules, peptides, proteins, aptamers, and nucleic acids. Representative small molecule targeting agents include folic acid and methotrexate (folate receptors), non-peptidic RGD mimetics, vitamins, and hormones. Representative peptide targeting agents include RGD (avβ3 integrin), chlorotoxin (MMP2), and VHPNKK (endothelial vascular adhesion molecules). Representative protein targeting agents include antibodies against the surface receptors of tumor cells, such as monoclonal antibody A7 (colorectal carcinoma), herceptin (Her2/ner), rituxan (CD20 antigen), and ligands such as annexin V (phosphatidylserine) and transferrin (transferrin receptor). Representative aptamer targeting agents include A10 RNA apatamer (prostate-specific membrane antigen) and Thrm-A and Thrm-B DNA aptamers (human alpha-thrombin protein). Targets for the agents noted above are in parentheses. Representative nucleic acid targeting agents include DNAs (e.g., cDNA) and RNAs (e.g., siRNA).
In one embodiment, the invention provides a nanoparticle, comprising:
(a) a core comprising a magnetic material and having a surface;
(b) a polyarginine coating covalently coupled to the surface; and
(c) a targeting agent.
In another embodiment, the invention provides a nanoparticle, comprising:
(a) a core comprising a magnetic material and having a surface;
(b) a polyarginine coating covalently coupled to the surface;
(c) a targeting agent; and
(d) a therapeutic agent.
For these embodiments, suitable targeting agents and therapeutic agents are as described above.
Diagnostic Agents.
Suitable diagnostic agents include optical agents, such as fluorescent agents that emit light in the visible and near-infrared (e.g., fluorescein and cyanine derivatives). Representative fluorescent agents include fluorescein, OREGON GREEN 488, ALEXA FLUOR 555, ALEXA FLUOR 647, ALEXA FLUOR 680, Cy5, Cy5.5, and Cy7.
In one embodiment, the invention provides a nanoparticle, comprising:
(a) a core comprising a magnetic material and having a surface;
(b) a polyarginine coating covalently coupled to the surface; and
(c) a diagnostic agent.
In another embodiment, the invention provides a nanoparticle, comprising:
(a) a core comprising a magnetic material and having a surface;
(b) a polyarginine coating covalently coupled to the surface;
(c) a diagnostic agent; and
(d) a therapeutic agent.
In a further embodiment, the invention provides a nanoparticle, comprising:
(a) a core comprising a magnetic material and having a surface;
(b) a polyarginine coating covalently coupled to the surface;
(c) a diagnostic agent;
(d) a targeting agent; and
(e) a therapeutic agent.
For these embodiments, suitable diagnostic agents, therapeutic agents, and targeting agents are as described above.
The preparation of representative nanoparticles of the invention is described in Example 1 and illustrated schematically in FIGS. 1A-1D. A schematic illustration of a representative nanoparticle of the invention including a therapeutic agent (e.g., siRNA) and a fluorescent agent (e.g., DY547) is shown in FIG. 1D.
In another aspect of the invention, a composition is provided that includes a nanoparticle of the invention and a carrier suitable for administration to a warm-blooded subject (e.g., a human subject). Suitable carriers include those suitable for intravenous injection (e.g., saline or dextrose).
Methods for Using Nanoparticle Having Polyarginine Coating
In other aspects, the invention provides methods for using the nanoparticles of the invention.
In certain embodiments, the invention provides methods for introducing a material (e.g., therapeutic and/or diagnostic agent) to a cell. In other embodiments, the invention provides imaging methods such as magnetic resonance imaging when the core has magnetic resonance activity, and optical imaging when the nanoparticle includes a fluorescent agent. As noted above, the nanoparticles of the invention can also be used for drug delivery when the nanoparticle includes a therapeutic agent. For nanoparticles of the invention that include targeting agents, imaging of and drug delivery to target sites of interest are provided.
In one embodiment, the invention provides a method for introducing a nanovector into a cell via transcytosis. In the method, a cell is contacted with a nanoparticle of the invention. As noted herein, the nanoparticles of the invention advantageously utilize transcytosis rather than endocytosis for transport into a cell. The ability to use a cell transcytosis mechanism renders the nanoparticles of the invention (e.g., nanovectors) particularly well suited for the intracellular delivery of cargo (e.g., therapeutic agents such as siRNA).
In another embodiment, the invention provides a method for silencing or reducing the expression level of a gene. In the method, a cell of interest is contacted with a nanoparticle of the invention in which the nanoparticle comprises a vector (i.e., suitable siRNA) effective to silence or reduce the expression level of the particular gene.
In a further embodiment, the invention provides a method for detecting (or imaging) cells or tissues by magnetic resonance imaging, comprising:
(a) contacting cells or tissues of interest with a nanoparticle of the invention having affinity and specificity for the cells or tissues of interest, wherein the nanoparticle comprises

- (i) a core comprising a magnetic material and having a surface,
- (ii) a polyarginine coating covalently coupled to the surface, and
- (iii) a targeting agent, wherein the targeting agent has an affinity and specificity to the cells or tissues of interest; and

(b) measuring the level of binding of the nanoparticle to the cells or tissues of interest, wherein an elevated level of binding, relative to normal cells or tissues, is indicative of binding to the cells or tissues of interest.
In the method, the level of binding is measured by magnetic resonance imaging techniques. In a further embodiment of the above method, the nanoparticle further includes a fluorescent agent. In this embodiment, the level of binding can be measured by magnetic resonance and/or fluorescence imaging techniques. The methods are applicable to detecting or imaging cells or tissues in vitro. The methods are also applicable to detecting or imaging cells or tissues in vivo. In this embodiment, the nanoparticles are administered to a subject (e.g., warm-blooded animal) by, for example, intravenous injection.
In another embodiment, the invention provides a method for treating a tissue, comprising contacting a tissue of interest with a nanoparticle of the invention having affinity and specificity for the tissue of interest, wherein the nanoparticle comprises
(a) a core comprising a core material and having a surface,
(b) a polyarginine coating covalently coupled to the surface, and
(c) a targeting agent, wherein the targeting agent has an affinity and specificity to the cells or tissues of interest.
In a further embodiment of the above method, the nanoparticle further comprises a therapeutic agent. In this embodiment, the therapeutic agent can be covalently linked (e.g., through a cleavable linkage) or physically adsorbed to (e.g., electrostatic or van der Waals interactions) the nanoparticle, or embedded within the nanoparticle's coating. The methods are applicable to treating tissues in vitro. The methods are also applicable to treating tissues in vivo. In this embodiment, the nanoparticles are administered to a subject (e.g., warm-blooded animal) by, for example, intravenous injection.
The following is a description of specific nanovectors of the invention and methods of their use.
Magnetic nanoparticles (MNPs) coated with pArg and functionalized with siRNA and their gene-silencing efficiency in tumor cell lines of the brain, breast, and prostate were evaluated. MNPs coated with polylysine (pLys) or PEI were also prepared for comparison. pLys is another commonly used cationic polypeptide to complex siRNA and deliver siRNA to cytoplasm of cells via endocytosis and endosomal escape.
Nanovector Synthesis
FIGS. 1A-1D illustrates the fabrication scheme a representative nanoparticle of the invention involving the covalent attachment of cationic polymers and siRNA to the amine-functionalized MNPs. The MNP consists of a 10-12 nm iron oxide core coated with siloxane to which a 44-mer of PEG-amine is anchored (FIG. 1A). The MNP was then modified with 10-kDa cationic polymers (pLys, pArg, or PEI) to produce NP-pLys, NP-pArg and NP-PEI using the conjugation scheme in FIG. 1C. The chemical structures of the cationic polymers are shown in FIG. 1B.
To assess the gene delivery efficacy, Cy5 fluorescently labeled, thiol modified siRNA (21 base-pairs, 5.7 nm length) designed to silence green fluorescence protein (GFP) transgene expression was covalently attached to the functional amine groups on the surface of NP-pLys, NP-pArg and NP-PEI using the heterobifunctional linker SIA (FIG. 1D) to form NP-pLys-siRNA, NP-pArg-siRNA and NP-PEI-siRNA.
This non-labile covalent attachment of siRNA to a nanocarrier is preferable for in vivo applications because it ensures that the siRNA-carrier construct will remain intact during blood circulation. Furthermore, this conjugation strategy does not compromise the knockdown efficiency of the siRNA. To favor thioether bond formation over electrostatic binding of the negatively charged siRNA with cationic NP, the SIA reaction was performed in a high ionic strength buffer.
Nanovector Physicochemical Characterization
The successful immobilization of cationic polymers onto NP was verified using proton NMR (¹H-NMR). Spectra from base MNPs, relevant constituent polymers, and the three different nanovector formulations confirm the successful immobilization of their expected polymer coatings FIGS. 2A and 2B. PEG on NP was identified at 3.7 ppm corresponding to the protons of the ethylene unit. PEI was identified at 3.75-3 ppm corresponding to the protons of its ethylene units. pLys was identified at 3, 1.75, and 1.45 ppm corresponding to the protons of the ε, δ and β, and γ carbons of the lysine side chain. pArg was identified at 3.25, 1.8, and 1.6 ppm corresponding to the protons of the δ, β, and γ carbons of the arginine side chain, respectively.
siRNA loading onto the nanovector was assessed using gel retardation assays where NP bound siRNA would not migrate down the gel. NP-pLys-siRNA, NP-PEI-siRNA and NP-pArg-siRNA were prepared at 20:1 nanoparticle:siRNA weight ratios (Fe mass of NP:siRNA mass). Without purification, the reaction products were loaded into agarose gels and unbound siRNA (bottom of gel) was separated from MNP-bound siRNA through electrophoresis. Each NP formulation showed complete binding of siRNA as no unbound siRNA was observed in the gels (FIG. 3A). A similar migration profile is demonstrated in the heparin treated samples (FIG. 3A), which disrupts electrostatic interactions, confirming successful covalent attachment of siRNA to MNP for all three nanovector formulations.
The hydrodynamic size of each nanovector formulation before and after siRNA loading was measured by dynamic light scattering (DLS) (FIG. 3B). Z-average diameters of the nanovectors were 53.4 nm for NP-pLys-siRNA, 69.4 nm for NP-PEI-siRNA and 53.5 nm for NP-pArg-siRNA. No significant change in hydrodynamic size was observed after siRNA attachment to nanovectors, reflecting their stability. Notably, the hydrodynamic size falls within the acceptable size range (5<d<200 nm) that facilitates in vivo navigation and evasion of sequestration by macrophages.
TEM images of three nanovector formulations show no signs of aggregation (FIG. 3D, top row). Higher magnification images in FIG. 3D (bottom row) reveal a lower density shell surrounding the MNP cores, which is absent on the base MNPs (FIG. 9). This shell structure further confirms the cationic polymer coating on the MNPs.
The zeta potential of each nanovector formulation was measured at pH 7.4 in 10 mM HEPES buffer by DLS. All three nanovector formulations were highly cationic prior to siRNA attachment, with zeta potentials of 22 mV for NP-pLys, 39 mV for NP-PEI and 21 mV for NP-pArg (FIG. 3C). After siRNA attachment, the zeta potentials of all formulations dropped significantly confirming successful siRNA conjugation. However, NP-PEI-siRNA remained highly cationic (30 mV) while the NP-pLys-siRNA (0.5 mV), and NP-pArg-siRNA (2.5 mV) displayed near-neutral zeta potentials under physiological pH conditions. A neutral NP formulation generally has better biocompatibility and prolonged circulating time in blood than positively charged formulations.
The three various nanovector formulations were similar in sizes, but had different zeta potentials. They differ in composition and abundance of surface amino groups, providing us an opportunity to compare the influence of these key parameters on siRNA delivery and cytotoxicity. The charge and composition of the cationic polymer coating regulates the buffering capacity and proton sponge behavior of the nanovector. To illustrate this, nanovectors were titrated with HCL and the change in pH was monitored. Resistance to pH change indicates an increase in proton absorption of the nanovector. The buffering capacity was seen to increase in the order of NP-pArg-siRNA<NP-pLys-siRNA<NP-PEI-siRNA (FIG. 4A). This trend minors the buffering capacities of the coating polymers alone (FIG. 4B), indicating they were not affected by attachment to NPs or to siRNA.
To ensure the shell structure did not compromise the magnetic properties of the nanovectors, their magnetic relaxivities on MRI were evaluated. All nanovector formulations showed higher R₂relaxivities compared to the base NP (FIGS. 5A and 5B), suggesting that the attachment of cationic polymers and siRNA to MNPs did not compromise, but rather, improved the magnetic properties. This improvement is likely due to the improved water absorption at the surface of the core MNP due to the presence of the hydrophilic cationic polymers.
Nanovector Internalization, Gene Knockdown and Monitoring of Toxicity
The nanovectors were evaluated in vitro for siRNA delivery and gene silencing in three cancer cell lines (C6/GFP⁺ brain, MCF7/GFP⁺ breast, and TC2/GFP⁺ prostate) that stably express the GFP gene. First, the amount of siRNA delivered to cells by each nanovector formulation was evaluated using the fluorescently labeled siRNA (FIGS. 6A-6C). All three nanovectors delivered similar amounts of siRNA to C6/GFP⁺ cells (FIG. 6A). Conversely, NP-pArg-siRNA delivered a markedly higher quantity of siRNA to MCF7/GFP⁺ cells than NP-pLys-siRNA and NP-PEI-siRNA (FIG. 6B). In TC2/GFP⁺ cells, both NP-pArg-siRNA and NP-pLys-siRNA delivered more siRNA than NP-PEI-siRNA. These data demonstrate that the pArg coating was most broadly effective in facilitating the delivery of siRNA-loaded nanovectors to target cells.
The influence of nanovector treatments on cell viability was evaluated using Alamar blue assays. Cells were treated with each nanovector formulation and a commercial transfection reagent Dharmafect 4 (Dharmacon Inc.) as a reference. The NP-pArg-siRNA treatment was the least toxic to C6/GFP⁺ cells (90% viability (% V)), with NP-pLys-siRNA (70.6% V) and NP-PEI-siRNA (78.9% V) most toxic (FIG. 6D). A similar trend in viability was observed with MCF7/GFP⁺ cells (FIG. 6E) where NP-pArg-siRNA treatment produced the least cytotoxicity (91.2% V), similar to Dharmafect 4 treatment (89% V) and much lower than NP-pLys-siRNA (70.2% V) and NP-PEI-siRNA (49% V) treatments. This trend was again observed in TC2/GFP⁺ cells (FIG. 6F). Both NP-pArg-siRNA (104.3% V) and Dharmafect 4 (92.5% V) treatments were well tolerated, while the NP-pLys-siRNA (77.5% V) and NP-PEI-siRNA (78.7% V) treatments were both moderately toxic.
The GFP gene-silencing efficacy of each nanovector formulation was then evaluated (FIGS. 6G-6I). The NP-pArg-siRNA treatment was most effective in gene silencing in C6/GFP⁺ cells (52.9% GFP knockdown (% GKD)), whereas Dharmafect 4 (36.4% GKD), NP-pLys-siRNA (22.7% GKD) and NP-PEI-siRNA (6.8% GKD) were all significantly less effective (FIG. 6G). A similar trend was observed in MCF7/GFP⁺ cells (FIG. 6H). NP-pArg-siRNA showed the highest potency for silencing (68.2% GKD), whereas Dharmafect 4 (51.3% GKD), NP-pLys-siRNA (39.1% GKD) and NP-PEI-siRNA (32.8% GKD) treatments were all less effective. In TC2/GFP⁺ cells it was again observed that NP-pArg-siRNA (24% GKD) was most effective in gene silencing compared to the other two different nanovector formulations, NP-pLys-siRNA (13.9% GKD) and NP-PEI-siRNA (13.4% GKD) (FIG. 6I). In this cell line Dharmafect 4 (31.3% GKD) was slightly more effective than NP-pArg-siRNA.
To further confirm the siRNA delivery and gene knockdown achieved by NP-pArg-siRNA to the three types of cells (C6/GFP+, MCF7/GFP+, and TC2/GFP+) confocal fluorescence microscopy was performed. Shown in FIGS. 7A-7C are fluorescence images of untreated and NP-pArg-siRNA treated C6/GFP+ (FIG. 7A), MCF7/GFP+ (FIG. 7B), and TC2/GFP+ (FIG. 7C) cells. In all images cell nuclei were stained with DAPI (blue) and membranes with WGA-647 (green). Treatments with NP-pArg-siRNA were administered as described above at a concentration of 1.2 μg of siRNA/ml. As shown in all three-cell lines tested internalized siRNA (red, second column) can be visualized in cells treated with NP-pArg-siRNA. The overlay images (third column) reveal that the delivered siRNA molecules are predominantly localized in the perinuclear region of cells, the region of cell where siRNA molecules are recognized by the RISC complex. This observation confirms the proper trafficking of siRNA within cells. The GFP expression analysis (light green, fourth column) showed that the NP-pArg-siRNA treatment reduced the GFP expression of cells in all cell lines compared to the untreated cells.
Based on the transfection and cell viability studies, NP-pArg-siRNA has the favorable overall properties as a theranostic agent compared to other nanovector formulations studied. This might be attributed to its neutral zeta potential and limited proton sponge effect, which minimizes the potential deleterious effects caused by non-specific interactions with anionic intracellular components (e.g., mRNA, DNA). The arginine-rich nanoparticle may travel across cell membranes through transcytosis without being trapped in endosome vesicles. NP-pArg-siRNA may be similarly trafficked into cells accounting for its high gene silencing efficiency despite limited proton sponge capacity.

Nanovector Intracellular Trafficking

To determine the uptake mechanism of each nanovector formulation, C6/GFP⁺ cells treated with nanovectors were imaged with TEM (FIGS. 8A and 8B). NP-pLys-siRNA and NP-PEI-siRNA could be observed entering the cell through endocytic pathways, whereas NP-pArg-siRNA appeared to transcytose across the cell membrane in the absence of independent endocytic engulfment (FIG. 8A). Furthermore, once inside the cell NP-pLys-siRNA and NP-PEI-siRNA could be seen escaping endosomal vesicles while NP-pArg-siRNA were free in the cytoplasm with no visible endosomal vesicle (FIG. 8B). These TEM images provide an explanation as to why the NP-pArg-siRNA formulation appeared efficient in inducing gene knockdown (FIGS. 6A-6I), despite its limited buffering capacity (FIG. 4A). The NP-pArg-formulation does not require endosome escape properties owing to its ability to completely bypass the endocytosis pathway. Conversely, the NP-pLys-siRNA and NP-PEI-siRNA formulations must escape endosomal vesicles to localize in the cytoplasm.
The present invention provides nanoparticles useful as siRNA carriers that utilize the polyarginine (pArg) peptide as a coating material. pArg is a naturally occurring, biodegradable polypeptide that offers improved biocompatibility (decreased toxicity) over PEI and PAMAM. Furthermore, because cell transcytosing proteins are known to avoid endosomal compartmentalization and are commonly found with arginine-rich domains, the pArg-coated nanovectors of the invention offer the advantage of transcytosing ability and thus offer more efficient siRNA delivery with greatly improved biocompatibility over NPs coated with synthetic polymers such as PEI.
As used herein, the term “about” refers to values +/−5% of the recited value.
The following is provided for the purpose of illustrating, not limiting, the invention.
The Preparation, Characterization, and Properties of Representative Polyarginine-Coated Nanoparticles (NP-pArg and NP-pArg-siRNA)
The following is a description of the preparation and characterization of representative arginine-coated nanoparticles of the invention (NP-Arg). The preparation and characterization of representative arginine-coated nanoparticles conjugated with siRNA (NP-pArg-siRNA) are also described. The particles and their preparation are schematically illustrated in FIGS. 1A-1D.
A10 reagents were purchased from Sigma Aldrich (St. Louis, Mo.) unless otherwise specified.
Amine-Terminated PEG-Coated Nanoparticles
Amine-terminated PEG-coated iron oxide nanoparticles (NPs) with a 12 nm core diameter were synthesized as described in Fang C, Bhattarai N, Sun C, Zhang MQ. Functionalized Nanoparticles with Long-Term Stability in Biological Media. Small. 2009; 5:1637-41, expressly incorporated herein by reference in its entirety. A schematic illustration of the preparation of representative amine-terminated PEG-coated iron oxide nanoparticles (NP-SAS-PEG-NH₂) is shown in FIG. 10.
Oleic acid-coated nanoparticles (NP-OA) were synthesized via thermal decomposition of iron oleate complex. To render the nanoparticles hydrophilic, the NP-OAs were reacted with triethoxysilylpropylsuccinic anhydride (SAS) to form SAS-coated nanoparticles (NP-SAS) via a ligand-exchange and condensation process. Amine-functionalized PEG was attached to NP-SAS via N,N′-dicyclohexylcarbodiimide (DCC) mediated coupling reaction to yield PEGylated nanoparticles (NP-SAS-PEG-NH₂). NP-SAS-PEG-NH₂bears amine groups at the free termini of PEG chains allowing for further conjugation with bioactive molecules or ligands. The PEG coating also serves to prevent nanoparticles from agglomeration and protein adsorption.
Synthesis of NP-SAS-PEG-NH₂.
To a 5 ml of toluene solution containing 50 mg (iron content) of NP-OA, 40 mL of acetone was added, and the nanoparticles were collected by centrifugation. The nanoparticles were redispersed in 50 mL anhydrous toluene and transferred to a three-neck flask equipped with a heater. After the system was sealed and purged with nitrogen, 0.15 mL of SAS was injected, and the solution was heated to 100° C. for 12 hours. The nanoparticles were precipitated by the addition of hexane, and collected using a rare earth magnet. The nanoparticles were washed twice with hexane and redispersed in anhydrous tetrahydrofuran (THF). To this solution, 100 mg of H₂N-PEG-NH₂and 2.5 mg of N,N′-dicyclohexylcarbodiimide (DCC) were added, and the reaction mixture was sonicated in a sonication bath for 12 hrs at 25° C. The nanoparticles was precipitated by the addition of 200 mL of hexane, and collected using a rare earth magnet. The precipitated nanoparticles were redispersed in 50 mL of anhydrous THF, and 250 mg of PEG-bis(amine) and 12.5 mg of DCC were added. The reaction mixture was kept in a sonication bath for 16 hrs at 25° C. The resulting product was precipitated by the addition of hexane, and collected using a rare earth magnet. After two additional cycles of THF-redispersion and ether-precipitation, the residue solvent was evaporated and the nanoparticles were redispersed in 5 mL PBS. After passing through a 0.2 μm syringe filter, the nanoparticles were purified through gel filtration chromatography by Sephacryl S-200 column. The nanoparticles were stored in 0.1 M sodium bicarbonate buffer (pH 8.5). The concentration of nanoparticles was determined by inductively coupled plasma atomic emission spectroscopy (ICP-AES).
TEM images showed that both NP-OA and NP-SAS-PEG-NH₂were spherical and well dispersed, with a core size of about 12 nm. No aggregation of NP-SAS-PEG-NH₂was observed, indicating that no inter-particle crosslinking occurred during the ligand exchange and PEG modification. Nanoparticle surface modification was confirmed by FTIR and XPS. The IR spectra of oleic acid coated nanoparticles exhibit the characteristic C—H stretch bands of methyl and methylene groups at 2930 and 2849 cm⁻¹and surface-complexed carbonyl stretch peaks at 1553 and 1433 cm⁻¹. After the surface modification of nanoparticles with SAS, the Si—O—R vibrational bands, including a broad peak around 1031 cm⁻¹and a minor peak at 1188 cm⁻¹, were observed indicating the formation of complex siloxane bonds. The relative intensity of surface-complexed carbonyl bands increased, compared to oleic acid-coated NPs, indicative of successful SAS attachment. The absence of characteristic anhydride peaks at 1850-1800 cm⁻¹and 1790-1740 cm⁻¹, suggesting that these groups were either hydrolyzed or bonded to the iron oxide surface. After the surface modification of NP-SAS with amine-functionalized PEG, multiple bands at 1458, 1346, 1244, 1112 and 949 cm⁻¹were observed, corresponding to the different vibrational modes of PEG's C—O—C bonds. The bands at 1642 and 1559 cm⁻¹can be assigned to either primary amine groups or mono-substituted amide, indicating the successful covalent attachment of PEG on the free carboxyl groups of NP-SAS. The number of reactive amine groups on nanoparticles by quantifying pyridine-2-thione following reaction with N-succinimidyl 3-(2-pyridyldithio)propionate (SPDP). The number of amine groups on each nanoparticle was about 70. As the number of amine groups is proportional to the number of PEG chains, this result also suggests the formation of a high density PEG coating on the surface of the nanoparticle.
The hydrodynamic sizes of NP-OA in toluene and NP-SAS-PEG-NH₂in phosphate-buffered saline (PBS) were determined to be 18 nm and 38 nm, respectively, by dynamic light scattering. The size increase (about 20 nm) of the NP-SAS-PEG-NH₂compared to NP-OA can be attributed to the PEG (MW=2,000) coating and the water molecules associated to PEG.
NP-pLys, NP-pArg, and NP-PEI Synthesis
The cationic polymer coated nanoparticles were prepared from amine-terminated PEG-coated iron oxide nanoparticles (NP in FIG. 1A or NP-SAS-PEG-NH₂in FIG. 10). NPs were modified with cationic polymers through the formation of a thioether bond between thiolated polymers and NPs activated with iodoacetyl groups. Specifically, 10.5 mg of NP in 1 mL of thiolation buffer (0.1M sodium bicarbonate, 5 mM EDTA, pH 8.0) was reacted with 10.5 mg succinimidyl iodoacetate (SIA, Molecular Biosciences, Boulder, Colo.) in 112.5 μl DMSO. Concurrently, 15.75 mg of poly-lysine (MW 10,000), poly-arginine (MW 10,000), or PEI (MW 10,000) were dissolved in 1.725 ml thiolation buffer and modified with 26 μl of a 10 mg/ml Traut's reagent (2-iminothiolane, Molecular Biosciences, Boulder, Colo.). All of the reactions were protected from light and ensued under gentle rocking. After 2 hours, excess SIA was removed from NP-SIA using a pre-packed PD-10 desalting column (GE Healthcare, Piscataway, N.J.) equilibrated with thiolation buffer. Upon purification, the NPs were split into three equal volumes, each containing 3.5 mg Fe, and added to the three polymer solutions for reaction. The reaction were protected from light and ensued for 2 hours with gentle rocking and was then stored at 4° C. overnight. The reactants for each reaction were then purified to remove excess polymer using columns packed with S-200 Sephacryl resin (GE Healthcare, Piscataway, N.J.) equilibrated with thiolation buffer.
siRNA Preparation
siRNA sequences designed to knockdown GFP expression: 5′-GCAAGCUGACCCUGAAGUUCUU-3′-antisense (SEQ ID NO: 1) and 5′-GAACUUCAGGGUCAGCUUGCUU-3′-sense (SEQ ID NO: 2) were purchased from Integrated DNA Technologies, Inc. (IDT, San Diego Calif.). These sequences were acquired with protected-thiol modifications on the 5′ end of the sense strand and with Cy5 modification on the 5′ end of the antisense strand. siRNA sequences were received as single strands and were annealed to their complementary strand in annealing buffer (12 mM potassium chloride, 1.2 mM HEPES, 0.04 mM magnesium chloride, pH 7.5) by incubating at 95° C. for five minutes, then 37° C. for 1 hr, and then stored at −20° C.
NP-pLys-siRNA, NP-pArg-siRNA, and NP-PEI-siRNA Synthesis
NP-pLys, NP-pArg, and NP-PEI were modified with SIA at a 5:1 weight ratio of Fe:SIA. The SIA was dissolved in DMSO such that the final reaction volume was 10% DMSO. The reactions were protected from light and ensued for 2 hours with gentle rocking. Meanwhile, a 57.73 mg/ml TCEP (tris (2-carboxyethyl) phosphine hydrochloride) solution was prepared. The TCEP and GFP siRNA were combined at a 1:1 volume ratio, protected from light, and allowed to react for 1 hr with gentle rocking. The resultant siRNA was purified using a 2 ml Zeba column (Thermo Fisher Scientific, Waltham, Mass.) equilibrated with thiolation buffer. The nanoparticles were purified using pre packed PD-10 columns equilibrated with thiolation buffer. Upon purification, the siRNA was added to each of the three types of NPs at a 20:1 Fe:siRNA weight ratio. The reactions were protected from light and allowed to proceed for 2 hrs with gentle rocking and the resultant nanoparticle:siRNA nanovectors were used without any further purification.
Proton NMR Analysis of Cationic Polymer Attachment to NP
Each NP formulation (50 μg Fe) was dissolved in 50 μL of DCl and diluted to 1 mL in D₂O, Similarly, cationic polymers were dissolved in 1 mL D₂O containing 50 μL of DCl. Proton NMR spectra were obtained on a Bruker AVance series spectrometer operating at 300 MHz.
Gel Retardation Assay
Attachment of siRNA to NPs was assessed using gel retardation assays. A 4% low melting point agarose gel was prepared with 0.05 mg/mL ethidium bromide. While maintaining a uniform concentration of siRNA, samples of nanoparticle:siRNA complexes were prepared at a weight ratio of 20:1 (Fe mass of NP: siRNA mass). Samples were either left untreated or treated with heparin (1000 units/ml, 10 mL heparin/mg siRNA), and incubated for 30 min at room temperature to block the electrostatic interaction between the nanoparticles and siRNA. siRNA binding was analyzed by gel electrophoresis at 55 V for 90 min. Images were acquired on a Gel Doc XR (Bio-Rad Laboratories, Hercules, Calif.).
Nanovector Size and Zeta Potential Characterization
Hydrodynamic sizes and zeta potentials of the different nanoparticle formulations were analyzed at 100 μg/mL in 20 mM HEPES buffer (pH 7.4) using a DTS Zetasizer Nano (Malvern Instruments, Worcestershire, UK).
Evaluation of Nanovector Magnetic Properties by MRI
Nanovector formulations were diluted in PBS, and then mixed with 25 μL of 1% agarose and loaded into an agarose gel phantom block. T2 relaxation measurements were performed on a 4.7-T Bruker magnet (Bruker Medical Systems, Karlsruhe, Germany) equipped with Varian Inova spectrometer (Varian, Inc., Palo Alto, Calif.). A 5 cm volume coil and spin-echo imaging sequence were used to acquire T2-weight images. Images were acquired using a repetition time (TR) of 3000 ms and echo times (TE) of 13.6, 20.0, 40.0, 60.0, 90.0 and 120.0 ms. The spatial resolution parameters were: acquisition matrix of 256×128, field-of-view of 35×35 mm, section thickness of 1 mm and two averages. The T2 map was generated by NIH ImageJ (Bethesda, Md.) based on the equation, SI=Aexp(−TE/T2)+B, where SI is the signal intensity, TE is the echo time, A is the amplitude, and B is the offset. The R2 map was generated by taking the reciprocal of the T2 map.
Evaluation of Nanovector Buffering Capacity
NP-pLys-siRNA, NP-pArg-siRNA, and NP-PEI-siRNA were desalted using pre-packed PD-10 columns equilibrated with DI water. 1 mg of Fe from each condition was then transferred to a 15 ml Falcon tube and brought to pH 11.0 by addition of 0.1 N NaOH. The final volume for each condition was brought up to 2 ml with pH 11.0 DI water making the Fe concentration 500 μg/ml. The titration was performed with 2 μL additions of 0.1 N HCl.
Cell Culture
C6 rat glioma (ATCC, Manassas, Va.) and MCF7 human adenocarcinoma (ATCC, Manassas, Va.) cells were maintained in Dulbecco's Modified Eagle Medium (DMEM, Invitrogen, Carlsbad, Calif.) supplemented with 10% FBS (Atlanta Biologicals, Lawrenceville, Ga.) and 1% antibiotic-antimycotic (Invitrogen, Carlsbad, Calif.) at 37° C. and 5% CO₂. Enhanced green fluorescent protein (EGFP) expressing cells were produced by stably transfecting cells with the pEGFP-N1 vector using the Effectene transfection reagent (Qiagen, Valencia, Calif.) following the manufacturer's protocol. 48 hrs post-transfection, cells were sorted using a FACS Vantage and maintained in fully supplemented DMEM with 1 mg/ml G-418. TC2/GFP+ cells were maintained in Dulbecco's Modified Eagle Medium (DMEM) (Invitrogen, Carlsbad, Calif.) supplemented with 10% FBS (Atlanta Biological, Lawrenceville, Ga.) and 1% antibiotic-antimycotic (Invitrogen, Carlsbad, Calif.) at 37° C. and 5% CO₂.
Cell Transfection
The day before transfection, cells were plated at 50,000 cells per well in 24-well plates. For transfection of cells with nanovector formulations, cells were treated with nanovectors for 8 hrs under normal growth conditions. After the 8-hour incubation the media were replaced and cells incubated for an additional 48 hrs before analyses. Transfections of cells with siRNA using Dharmafect 4 (Dharmacon, Lafayette, Colo.) were performed according to the manufacturer's instructions.
Cell Viability and Gene Silencing
Potential cytotoxicity associated with the nanovector formulations was examined by the Alamar blue assay. After treatment, cells were washed with PBS three times, and incubated for 2 hrs with 10% Alamar blue (Invitrogen) in phenol red-free DMEM (supplemented with 10% FBS and 1% antibiotic-antimycotic). The percent reduction of Alamar blue was determined following the manufacturer's protocol and used to calculate percent viability of treated samples (untreated cells represent 100% viability).
To quantify the degree of GFP gene silencing, treated cells were washed with PBS three times and lysed with 1% Triton X-100 in PBS. GFP protein expression was measured at an excitation and an emission wavelength of 488 and 520 nm, respectively. GFP fluorescence levels were normalized to the total number of viable cells, as determined by the Alamar Blue viability assay. Relative GFP expression levels were then calculated based on the reduction in GFP expression as compared to non-transfected cells.
Confocal Fluorescence Microscopy
50,000 treated cells were plated on each of 24 mm glass cover slips and allowed to attach for 24 hrs. Cells were then washed with PBS and fixed in 4% formaldehyde (Polysciences Inc., Warrington, Pa.) for 30 min. Cells were then washed three times with PBS and membrane-stained with WGA-AF647 (Invitrogen, Carlsbad, Calif.) according to the manufacturer's instructions. Cover slips were then mounted on microscope slides using Prolong Gold antifade solution (Invitrogen, Carlsbad, Calif.) containing DAPI for cell nuclei staining. Images were acquired on a LSM 510 Meta confocal fluorescence microscope (Carl Zeiss Inc., Peabody, Mass.) with the appropriate filters.
Transmission Electron Microscopy (TEM)
One million C6 cells were seeded in 25 cm²flasks 24 hrs before treatment. Cells were then treated with nanovector formulations as described for gene silencing experiments. Cells were then washed three times with PBS and incubated with ice cold Karnovsky's fixative for 24 hrs. Following the fixation, the cells were processed directly from flasks for sectioning. Cell sections were stained with osmium tetroxide, lead citrate, and uranyl acetate for TEM-contrast enhancement. Cell samples were then imaged with a Philips CM100 TEM at 100 kV with a Gatan 689 digital slow scan camera.
While illustrative embodiments have been illustrated and described, it will be appreciated that various changes can be made therein without departing from the spirit and scope of the invention.

Claims

1. A nanoparticle, comprising:

(a) a core having a surface and comprising a core material; and

(b) a polyarginine coating covalently coupled to the surface of the core.

2. The nanoparticle of claim 1 further comprising a therapeutic agent.

3. The nanoparticle of claim 1 further comprising a targeting agent.

4. The nanoparticle of claim 1 further comprising a therapeutic agent and a targeting agent.

5. The nanoparticle of claim 1, wherein the polyarginine has an average molecular weight from about 2,000 to about 200,000 g/mole.

6. The nanoparticle of claim 2, wherein the therapeutic agent is selected from the group consisting of a small organic molecule, a peptide, an aptamer, a protein, and a nucleic acid.

7. The nanoparticle of claim 2, wherein the therapeutic agent is an RNA or a DNA.

8. The nanoparticle of claim 2, wherein the therapeutic agent is an siRNA.

9. The nanoparticle of claim 2, wherein the therapeutic agent is covalently coupled to the nanoparticle through a cleavable linkage.

10. The nanoparticle of claim 3, wherein the targeting agent is selected from the group consisting of a small organic molecule, a peptide, an aptamer, a protein, and a nucleic acid.

11. The nanoparticle of claim 3, wherein the targeting agent is selected from the group consisting of a chlorotoxin, folic acid, methotrexate, RGD, VHPNKK, A10 RNA aptamer, transferrin, and herceptin.

12. The nanoparticle of claim 1, wherein the core material comprises a material having magnetic resonance imaging activity.

13. The nanoparticle of claim 1 further comprising a poly(alkylene oxide) oligomer intermediate the core and the polyarginine coating.

14. The nanoparticle of claim 1, wherein the poly(alkylene oxide) oligomer is covalently coupled to the core by siloxane linkages.

15. The nanoparticle of claim 2 further comprising a fluorescent agent.

16. The nanoparticle of claim 3 further comprising a fluorescent agent.

17. The nanoparticle of claim 4 further comprising a fluorescent agent.

18. The nanoparticle of claim 1 further comprising a fluorescent agent.

19. A composition, comprising a nanoparticle of claim 1 and a carrier suitable for administration to a warm-blooded subject.

20-24. (canceled)

25. A method for introducing a nanovector into a cell via transcytosis, comprising contacting a cell with a nanoparticle of claim 1.

26. A method for silencing or reducing the expression level of a gene, comprising contacting a cell of interest with a nanoparticle of claim 1, wherein the nanoparticle comprises a vector effective to silence or reduce the expression level of the gene.

27. A method for detecting cells or tissues by magnetic resonance imaging, comprising:

(a) contacting cells or tissues of interest with a nanoparticle of claim 1; and

(b) measuring the level of binding of the nanoparticle, wherein an elevated level of binding, relative to normal cells or tissues, is indicative of binding to the cells or tissues of interest.

28. A method for treating a tissue, comprising contacting a tissue of interest with a nanoparticle of claim 1.