WO1992007013A1 - Novel silicone-containing polymers and oxygen permeable hydrophilic contact lenses therefrom - Google Patents
Novel silicone-containing polymers and oxygen permeable hydrophilic contact lenses therefrom Download PDFInfo
- Publication number
- WO1992007013A1 WO1992007013A1 PCT/US1991/007244 US9107244W WO9207013A1 WO 1992007013 A1 WO1992007013 A1 WO 1992007013A1 US 9107244 W US9107244 W US 9107244W WO 9207013 A1 WO9207013 A1 WO 9207013A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- weight
- composition according
- copolymer
- block
- monomers
- Prior art date
Abstract
Description
Claims