ENERGY STORAGE DEVICE AND METHODS OF MANUFACTURE
BACKGROUND OF THE INVENTION Cross-Reference To Related Applications
The present application is a continuation-in-part of U.S. Application Serial No. 07/947,414, filed September 18, 1992, U.S. Application Serial No. 07/947,294, filed September 18, 1992, and U.S. Application Serial No. 07/958,506, filed October 7, 1992, all of which are incorporated by reference in their entirety. Field of the Invention
The present invention generally relates to an energy storage device, and more particularly to a bipolar double layer capacitor-type energy storage device, and to methods for manufacturing the same. Description of the Related Art Enerqv Storage Devices — There has been significant research over the years, relating to useful reliable electrical storage devices, such as a capacitor or a battery. Large energy storage capabilities are common for batteries; however, batteries also display low power densities. In contrast, electrolytic capacitors possess very high power densities and a limited energy density. Further, carbon based double-layer capacitors have a large energy density; but, due to their high equivalent series resistance (ESR), carbon electrodes have low power capabilities. It would therefore be highly desirable to have an electrical storage device that has both a high energy density and a high power density.
A recent review by B.E. Conway in J. Electrochem. Soc, vol. 138 (#6), p. 1 539 (June 1 991 ) discusses the transition from "supercapacitor" to "battery" in electrochemical energy storage, and identifies performance characteristics of various capacitor devices.
D. Craig, Canadian Patent No. 1 , 196,683, in November 1985, discusses the usefulness of electric storage devices based on ceramic-oxide coated electrodes and pseudo-capacitance. However, attempts to utilize this disclosure have resulted in capacitors which have inconsistent electrical properties and which are often unreliable.
These devices cannot be charged to 1 .0 V per cell, and have large, unsatisfactory leakage currents. Furthermore, these devices have a very low cycle life. In addition, the disclosed packaging is inefficient.
M. Matroka and R. Hackbart, US Patent No. 5, 121 ,288, discusses a capacitive power supply based on the Craig patent which is not enabling for the present invention. A capacitor configuration as a power supply for a radiotelephone is taught; however, no enabling disclosure for the capacitor is taught.
J. Kalenowsky, US Patent No. 5,063,340, discusses a capacitive power supply having a charge equalization circuit. This circuit allows a multicell capacitor to be charged without overcharging the individual cells. The present invention does not require a charge equalization circuit to fully charge a multicell stack configuration without overcharging an intermediate cell.
H. Lee, et al. in IEEE Transactions on Magnetics, Vol. 25 (#1 ), p.324 (January 1989), and G. Bullard, et al., in IEEE Transactions on Magnetics. Vol. 25 (#1 ) p. 102 (January 1 989) discuss the pulse power characteristics of high-energy ceramic-oxide based double-layer capacitors. In this reference various performance characteristics are discussed, with no enabling discussion of the construction methodology. The present invention provides a more reliable device with more efficient packaging.
Carbon electrode based double-layer capacitors have been extensively developed based on the original work of Rightmire, U.S. Patent No. 3,288,641 . A. Yoshida et al., in IEEE Transactions on Components, Hybrids and Manufacturing Technology, Vol. CHMT-10, #1 ,P-100 - 103 (March 1987) discusses an electric double-layer capacitor composed of activated carbon fiber electrodes and a nonaqueous electrolyte. In addition, the packaging of this double-layer capacitor is revealed. This device is on the order of 0.4-1 cc in volume with an energy storage capability of around 1 -10 J/cc.
T. Suzuki, et al., in NEC Research and Development, No. 82, pp. 1 18 - 123, July 1986, discloses improved self-discharge characteristics of the carbon electric double- layer capacitor with the use of porous separator materials on the order of 0.004 inches thick. An inherent problem of carbon based electrodes is the low conductivity of the material resulting in a low current density being delivered from these devices. A second difficulty is that the construction of multicell stacks is not done in a true bipolar
electrode configuration. These difficulties result in inefficient packaging and lower energy and power density values.
Additional references of interest include, for example:
The state of solid state micro power sources is reviewed by S. Sekido in Solid State Ionics, vol. 9, 10. pp. 777-782 (1 983).
M. Pham-Thi et al. in the Journal of Materials Science Letters, vol. 5, p. 41 5 ( 1 986) discusses the percolation threshold and interface optimization in carbon based solid electrolyte double-layer capacitors.
Various disclosures discuss the fabrication of oxide coated electrodes and the application of these electrodes in the chlor-alkali industry for the electrochemical generation of chlorine. See for example: V. Hock, et al. US Patent No. 5,055, 1 69 issued October 8, 1 991 ; H. Beer US Patent no. 4,052,271 issued October 4, 1 977; and A. Martinsons, et al. US Patent no. 3,562,008 issued February 9, 1 971 . These electrodes, however, in general do not have the high surface areas required for an efficient double-layer capacitor electrode.
It would be useful to have a reliable long-term electrical storage device, and improved methods to produce the same. It would also be desirable to have an improved energy storage device with energy densities of at least 20-90 J/cc. Packaging of Energy Storage Devices -- As mentioned above, there has been significant research over the years regarding electrical storage devices of high energy and power density. The efficient packaging of the active materials, with minimum wasted volume, is important in reaching these goals. The space separating two electrodes in a capacitor or a battery is necessary to electronically insulate the two electrodes. However, for efficient packaging, this space or gap should be a minimum. It would therefore by highly desirable to have a method to create a space separator or gap that is substantially uniform and of small dimension (less than 5 mil (0.01 27 cm).
A common way to maintain separation between electrodes in an electrical storage device with an electrolyte present (such as a battery or capacitor) is by use of an ion permeable electrically insulating porous membrane. This membrane is commonly placed between the electrodes and maintains the required space separation between the two electrodes. Porous separator material, such as paper or glass, is useful for this
application and is used in aluminum electrolytic and double layer capacitors. However, for dimensions below 1 or 2 mil (0.00254 to 0.00508 cm) in separation, material handling is difficult and material strength of the capacitor is usually very low. In addition, the open cross-sectional areas typical of these porous membrane separators are on the order of 50-70%.
Polymeric ion permeable porous separators have been used in carbon double layer capacitors as discussed by Sanada et al. in IEEE, pp.224-230, 1 982, and by
Suzuki et al. in NEC Research and Development, No. 82, pp. 1 1 8-1 23, July 1 986.
These type of separators suffer from the problem of a small open area which leads to increased electrical resistance.
A method of using photoresist to fill voids of an electrically insulating layer to prevent electrical contact between two electrode layers for use as a solar cell is disclosed by J. Wilfried in US Patent No. 4,774, 1 93, issued September 27, 1 988.
A process of creating an electrolytic capacitor with a thin spacer using a photosensitive polymer resin solution is disclosed by Maruyama et al in US Patent No.
4,764, 1 81 issued August 1 6, 1 988. The use of solution application methods described in a porous double-layer capacitor electrode would result in the undesirable filling of the porous electrode.
Additional references of general interest include U.S. Patents 3,71 8,551 ; 4,052,271 ; and 5,055, 1 69. All of the applications, patents, articles, references, standards, etc. cited in this application are incorporated herein by reference in their entirety.
In view of the above, it would be very useful to have a method to produce a reliable small space separation between electrodes in electrical storage devices with a large open cross-sectional area.
SUMMARY OF THE INVENTION The present invention relates to a novel electrical storage device that has both a high energy density and a high power density.
It is an object of the present invention to provide new methods for manufacturing the storage device.
It is also another object of the present invention to provide a reliable long- term electrical storage device, and improved methods to produce the same.
It is a further object of the present invention to provide efficient packaging of an electrical storage device by reducing the gap between the anode and cathode, which reduces the electrical resistance of the ionically conducting electrolyte.
Briefly, the foregoing and other objects are attained by an energy storage device such as a capacitor, which includes a plurality of cells in a bipolar configuration. The cells are stacked and bonded together, to impart to the device an integral and unitary construction. Each cell includes two electrically conductive electrodes that are spaced apart by a predetermined distance. The cell also includes at least one dielectric gasket that is interposed, in relation to each other, between the electrodes, for separating and electrically insulating these electrodes.
When the electrodes, and the gaskets are bonded together, at least one fill gap is formed for each cell. Each cell also includes a high surface area (porous) electrically conductive coating layer that is formed on one (or, more) surface of each electrode. This coating layer optionally includes a set of closely spaced-apart peripheral microprotrusions, and a set of distally spaced-apart central microprotrusions. These microprotrusions are formed by novel screen printing or photolithographic printing methods. These microprotrusions impart structural support to the cells, and provide additional insulation between the electrodes.
An ionically conductive medium fills the cell gap and pores of the high surface area coating.
BRIEF DESCRIPTION OF THE FIGURES The above and other features of the present invention and the manner of attaining them, will become apparent, and the invention itself will be best understood, by reference to the following description and the accompanying drawings, wherein:
Figure 1 is a perspective view of the preunit 10 a dry energy storage device which is constructed according to the present invention;
Figure 1 A is a perspective view of the electrolyte-filled energy storage device 10A of the present invention;
Figure 2 is a cross-sectional view of the storage device of Figure 1 showing a removable cord 1 17A within the storage device, taken along line 2-2 thereof; Figure 2A is another cross-sectional view of the storage device of Figure 1 , taken along line 2A-2A thereof;
Figure 3 is a schematic representation of an exploded view of the preunit of Figure 1 , illustrating three cells;
Figure 4 is a block diagram of the manufacture steps of the storage device 10A;
Figure 5 is a top plan view of a porous coating layer with microprotrusions which forms a part of the storage device of Figures 1 through 4;
Figure 6 is a diagrammatic illustration of a capacitive circuit, which is equivalent to the device 10A; Figure 7 is a schematic representation of a screen printing method to produce microprotrusions on a coating layer used with the energy storage device according to the present invention;
Figure 8 is a schematic representation of an electrode holder used in the manufacture method of Figure 7; Figure 9 is a schematic representation of a method to photolithographically produce the microprotrusions according to the present invention;
Figure 10 is a schematic isometric view of a pair of hot rollers used for laminating a photoresist to an electrode prior to photolithography;
Figure 1 1 is a schematic isometric view of a mask placed over the photo resist of Figure 10;
Figure 1 2 is a schematic isometric view illustrating the exposure of unprotected portions of the photo resist of Figures 10 and 1 1 ;
Figure 1 3 is a cross-sectional view of an electrode which forms a part of the energy storage device, taken along line 1 3-1 3 of Figure 3; and
Figure 14 is a schematic cross-sectional view of two bipolar electrodes with the high surface area porous coating layer on the electrically conducting substrate forming one cell.
Figure 1 5 is a schematic view of a frame used to hold thin support materials during the dip coating process;
Figure 1 5 A is a schematic view of wire used in the frame of Figure 1 5. DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS Definitions
The definitions of the following terms are not intended to be exclusive: "Cord" refers to the thin strips of material included in the method of manufacture of the dry preunit. After initial heating, the removal of the cord produces the open fill ports.
"Electrically conducting support material" refers to any electrically conducting metal or metal alloy, electrically conducting polymer, electrically conducting ceramic, electrically conducting glass, or combinations thereof. Metals and metal alloys are preferred for producing stock units. The support material should have a conductivity of greater than about 1 0~4 S/cm.
"Second electrically conducting material" (having a high surface area) refers to a porous electrode coating which may be of the same or different composition on each side of the support material. Preferred metal oxides of the present invention include those independently selected from tin, lead, vanadium, titanium, ruthenium, tantalum, rhodium, osmium, iridium, iron, cobalt, nickel, copper, molybdenum, niobium, chromium, manganese, lanthanum, or lanthanum series metals or alloys or combinations thereof, and possibly containing additives like calcium to increase electrical conductivity.
"Electrolyte" refers to an ionically conductive aqueous or non-aqueous solution or material, which enables the dry preunit to be electrically charged.
"Cab-0-Sil®" refers to silica filler available from Cabot Corporation of Tuscola, Illinois. A variety of sizes are available.
"Epoxy" refers to the conventional definition of the product which is an epoxy resin mixed with a specific curing agent, usually a polyamine. or polyepoxide mixed with a polyamine curing agent.
MYLAR® refers to a polyester of polyethylene terephthalate of DuPont, Inc. of Wilmington, Delaware. It is usually commercially available in sheet form of varying thicknesses.
"Metal oxide" refers to any electrically conducting metal oxide.
"Mixed metal oxide" refers to an electrically conducting oxide compound of two or more metal oxides. "Photoresist" is any photo curable material. Usually, it is an epoxide or acrylate or combinations thereof.
"ConforMASK" is a negative working photopolymer available commercially from Dynachem of Tustin, California. This polymer should be used at 50% or less relative humidity. Dry Preunit Energy Storage Device
Referring now to the drawings, and more particularly to Figures 1 , 2 and 3 thereof, there is illustrated a dry preunit of energy storage device 10 which is constructed according to the present invention. The energy storage device is first an assembled dry preunit 10. After filling the present ceils with an electrolyte, the surface is heated to close and to fuse the exterior surface, to form device 10A which is then electrically charged.
The device preunit 10 generally includes a plurality of cells, such as the cells 1 1 0, 1 1 2 and 1 14, which are formed, prepared, and stacked according to the teaching of the present invention. Figure 1 A illustrates an assembled view of the electrical storage device preunit 10A, formed of twelve superposed cells. It should however be understood to those skilled in the art, after reviewing the present specification that any different number of cells can be used.
For simplicity of illustration, Figure 3 is an exploded view of the preunit 1 0, showing only three exemplary cells 1 1 0, 1 1 2 and 1 14. The cells have generally similar design and construction, and therefore, only the cells 1 14 and 1 1 2 will be described in detail, in relation to Figures 2, 2A, 3 and 1 3.
The cell 1 14 includes a first electrically conductive external electrode or end plate 1 1 1 A, and a second internal, electrically conductive bipolar electrode 1 1 1 B. Both electrodes 1 1 1 A and 1 1 1 B are spaced apart at the edges by means of two dielectric or electrically insulating gaskets 1 21 and 1 23. When the first and second electrodes 1 1 1 A and 1 1 1 B, and the insulating gaskets 1 21 and 1 23 and the electrically conducting porous material (oxide) layers 1 1 9 and 1 20 are bonded together to form the cell 1 14, a central air filled gap 1 30 (Figure 2A) is formed by these elements. When the preunit 10 is ready to be used, the gap 1 30 is filled with an electrolyte (not shown) to produce device 1 0A. For this purpose, an exemplary access or fill port 1 22, is shown in Figure 2A for illustration purpose only, and is formed between the gaskets 1 21 and 1 23, in order to allow the electrolyte to fill the gap 1 30. The fill port 1 22 is formed by means of a tab or cord 1 1 7A, which is inserted between the gaskets 1 21 and 1 23, prior to fusing or bonding the gaskets 1 21 and 1 23. When the gaskets 1 21 and 1 23 are heated, the cord 1 1 7A becomes surrounded by the reflow gasket material, which causes the outline of fill port 1 22 to be formed. The two gaskets become a fused polymer mass covering a minimum of the active electrically conducing coating layers 1 1 9 and 1 20.
Considering now the electrodes 1 1 1 A and 1 1 1 B in greater detail, the methods of manufacturing them will be described later. One difference between the electrodes 1 1 1 A and 1 1 1 B is that the electrode 1 1 1 A optionally includes a tab 1 60A, for connection to a power source (not shown).
A further, but optional distinction between the electrodes 1 1 1 A and 1 1 1 B, is that the electrode 1 1 1 A includes one porous electrically conductive coating layer 1 1 9, which is deposited on a support material or structure 1 1 6, while the bipolar electrode 1 1 1 B includes two porous coating layers 1 20 and 1 31 , which are deposited on either or both sides of the support material or structure 1 1 1 B. As such, the electrode 1 1 1 B is a true bipolar electrode. It should be understood that both sides of the electrode 1 1 1 A could be coated with porous electrically conductive layers.
Yet another optional distinction between the electrodes 1 1 1 A and 1 1 1 B lies in the rigidity of the support structures 1 1 1 A and 1 1 1 B. The electrode 1 1 1 A, acting as an external end plate, should preferably have a more rigid construction, so that it imparts sufficient rigidity to the overall structure of the energy storage device 10A. The electrode 1 1 1 B and other similar internal electrodes do not necessarily need to be as rigid as the external electrode 1 1 1 A. Nonetheless, when the device 10A is large, additional support structure is required, and the internal electrodes, i.e. 1 1 1 B, are used as additional support structure. In this case, it is desirable to rigidity the internal electrodes, i.e. 1 1 1 B. As a result, the support material 1 1 6 is thicker than the support material 1 1 8.
In the preferred embodiment, the support material 1 1 6 has a thickness of about 10 mils (0.0254 cm), while the support material 1 1 8 has a thickness of about 1 mil (0.00254 cm). Other values could alternatively be selected.
The electrodes 1 1 1 A, 1 1 1 B and the remaining electrodes of the storage device 10A, are sized and dimensioned according to the desired application, without departing from the scope of the invention. For instance, in one application, the device 1 0A is miniaturized, e.g. for a cardiac defibrillator. While in another application, the overall volume of the device is one cubic meter or even greater, e.g. for an electric vehicle. The dimensions of the electrodes determine the overall capacitance of the storage device 10A.
In the preferred embodiment, the electrodes, i.e. 1 1 1 A and 1 1 1 B, are rectangularly shaped. However, these electrodes and consequently the preunit 10 could assume various other shapes, such as circular, square, etc. An important feature of the preunit 10 is the flexibility of its design, which enables it to be used in various applications.
Considering now the coating layers 1 1 9 and 1 20 in greater detail, the methods of forming them will be described later. In the preferred embodiment, the coating layer 1 1 9 includes a plurality of microprotrusions, while the coating layer 1 20 does not include such microprotrusions. It should be understood, however, that the coating layer 1 20 could alternatively be designed similarly to the coating layer 1 1 9, without departing from the scope of the invention.
Figure 5 is a top plan view of the coating layer 1 1 9, which includes an array of microprotrusions, and which is deposited on the inner face or flat side of the support material 1 16. The coating layer 1 19 is porous with high surface area, electrically conductive, and relatively thin. The array includes two sets of microprotrusions. The first set includes a plurality of peripheral microprotrusions 1 25, and the second set includes a plurality of centrally located microprotrusions 1 27.
In the preferred embodiment, the peripheral and the central protrusions 125 and 1 27 are similarly designed, and are generally semi-spherically shaped. However, other shapes, for example a rectangular shape, are contemplated within the scope of the present invention. The diameter of each protrusion 1 25 or 1 27 is about 6 mil (0.01 524 cm). Different applications of the device 10 might require that the microprotrusions 125 and 1 27 be differently designed. The center-to-center separation of the peripheral microprotrusions 125 is about 20 mil (0.0508 cm), while the center-to-center separation of the central microprotrusions 127 is about 40 mil (0.1016 cm).
One reason for the higher density of the peripheral microprotrusions 1 25, is to prevent edge shorting. One reason for the lower density of the central microprotrusions 1 27, is to provide separation between the electrodes 1 1 1 A and 1 1 1 B, with minimal masking of the electrode surfaces. For this purpose, the gasket 1 21 is allowed to cover at least part of the microprotrusions 125, but preferably not the microprotrusions 127.
The peripheral microprotrusions 125 are adjacently disposed along an outer periphery of the coating layer 1 19. While only four rows of microprotrusions are illustrated, it should be understood to those skilled in the art, that additional rows may added, depending on the size and application of the device 10. The central microprotrusions 1 27 are similarly adjacently disposed, in an arrayed arrangement, within a central section 132 of the coating layer 1 1 9. As illustrated in Figure 5, the central microprotrusions 127 are surrounded by the peripheral microprotrusions 1 25. The microprotrusions 1 25 and 1 27 are formed on the coating layer 1 1 9 to provide added structural support to the first and second electrodes 1 1 1 A and 1 1 1 B.
For instance, if, the second electrode 1 1 1 B starts to sag or bow toward the first electrode 1 1 1 A, the microprotrusions 1 27 will prevent contact between these electrodes 1 1 1 A and 1 1 1 B.
Figure 5 further shows that the coating layer 1 1 9 further includes a plurality of spacings, i.e. 1 33A through 1 33G, where the cord, i.e., 1 1 7A, are placed, in order to ultimately form the fill port, i.e. 1 22. As illustrated for large electrode sizes the coved only extends partway into the central section 132. For smaller electrode sizes the coved across the electrode surface with the two ends protruding out opposite sides, thus forming simultaneously fill ports 1 1 3C and 1 33D. In this case the width of the cord is smaller than, or equal to the center-to-center separation between the central microprotrusions 1 27. However, the cord is larger than the center-to-center separation between the peripheral microprotrusions 1 25, to prevent the peripheral microprotrusions from pinching the cord, and preventing it from being removed the spacings are increased in the peripheral microprotrusions. Alternatively, the cord may be similar in width to the peripheral microprotrusions separation and no accommodation in the microprotrusion pattern needs to be done.
Considering now the coating layer 1 20, it serves a similar function as the coating layer 1 1 9, and is deposited on the side of the electrode 1 1 1 B, which faces the inner side of the first electrode 1 1 1 A. In the preferred embodiment, the coating layer 1 20 does not include microprotrusions. In an alternative embodiment of the preunit 10, the coating layers 1 1 9 and 1 20 are similarly constructed, and include microprotrusion layers.
Considering now the gaskets 1 21 and 1 23, the methods of producing them will be described later. The gaskets 1 21 and 1 23 are generally identical, and are arranged in registration (adjacent and superposable) with each other. For brevity, only the gasket 1 21 will be described in greater detail. The gasket 1 21 includes a solid peripheral section 143 and a hollow central section 144.
In the preferred embodiment, the cord 1 1 7A, or a part thereof, is placed between the gaskets 1 21 and 1 23, and extends across the hollow section, i.e. 144, of the gaskets, and protrudes outside the peripheral section, i.e. 143. In another embodiment, the cord does not extend across the entire width of the gaskets, and
only a part of the cord is sandwiched between the gaskets and extends beyond both edges of one side of the gasket.
Turning now to Figure 1 , the next adjacent cell 1 1 2 will now be briefly described. The cell 1 1 2 is generally similar in design and construction to the cell 1 14. The cell 1 1 2 includes the bipolar electrode 1 1 1 B, as its first electrode, and a second bipolar electrode 1 1 1 C. The electrodes 1 1 1 B and 1 1 1 C are generally identical, and are spaced-apart, in registration with each other.
A porous coating layer 1 31 , which is identical to the coating layer 1 1 9, is deposited on the surface of the support material 1 1 8, facing the electrode 1 1 1 C. A coating layer 1 33, which is similar to the coating layer 1 20, is deposited on a support material or structure 140, which forms a part of the electrode 1 1 1 C.
The cell 1 1 2 further includes two gaskets 135 and 137 that are identical to each other and to the gaskets 1 21 and 1 23 of the cell 1 14. A cord 1 1 7B forms a fill port 142 between the gaskets 1 35 and 1 37. The cell 1 1 0 is substantially similar to the cell 1 14, and includes a first bipolar electrode 1 1 1 Y, a second electrode 1 1 1 Z, two gaskets 1 57 and 1 59, a cord 1 1 7C, a tab 1 60, and a fill port 1 62. It should be noted that Figure 3 does not show the inner electrode 1 1 1 Y.
Turning now to Figure 6, there is illustrated a diagrammatic view of a capacitive circuit 200 which is representative of, and generally has an equivalent function to the device 10A. The circuit 200 illustrates the cell 1 14 as two capacitors C1 and C2; the cell 1 1 2 as two capacitors C3 and C4; and the cell 1 10 as two capacitors C5 and C6. As a result, the device 10 is generally equivalent to a plurality of capacitors connected in series. The porous electrically conducting coating 1 1 9 in conjunction with an ionically conducting medium (not shown) within the cell 1 14, form the capacitor C1 .
The ionically conducting medium and the coating 1 20 form the capacitor C2. The coating 1 31 and the ionically conducting medium within the cell 1 1 2 form the capacitor C3. The ionically conducting medium within the cell 1 1 2 and the coating 1 33 form the capacitor C4. Similarly, the cell 1 10 is represented by the capacitors
C5 and C6.
An important aspect of the present invention, is the bipolar configuration of the energy storage device. The use of a single electrode, such as the electrode 1 1 1 B to form two back-to-back capacitors, such as the capacitors C2 and C3, result in a bipolar electrode B. This design significantly reduces the overall size of the device 10A.
While not wanting to be bound by theory, an explanation of the operation of the capacitive energy storage device, at the molecular level is helpful to understand the enormous value of the electric double layer. For simplicity, to describe Figure 14, Figure 3 can be used for reference where the same reference numbers are used (and the porous material is a mixed metal oxide) .
Figure 14 is a schematic cross-sectional representation of the magnified edge of the magnified edge of the support 1 1 8 & 148A and electrically conducting coating layers (1 20, 1 31 , 1 33, 1 33B).
The center support 1 88 is depicted as a metal but can be any material which is electrically conducting and provides the support for the coating. The coating which has high surface area provides the structure and geometry for the energy storage. As can be seen in Figure 14, layer 1 20, etc. has a discontinuous surface with many fissures, micropore and mesopore which create the high surface area.
Thus, the porous coatings 1 20 and 1 31 are coated onto support 1 1 8 to form bipolar electrode 1 1 1 B and coatings 133 and 133B are coated onto support 148A to form bipolar electrode 1 1 1 C. After the preunit 1 0 is assembled, the pull tabs are removed creating the fill ports and the preunit 10 is charged with electrolyte 1 90, the fill ports, e,g. 1 17D, are sealed creating device 10A.
The device 10A is then charged electrically producing the following results at the same time:
Coating 1 20 becomes negatively charged. Electrically conducting support 1 1 8 conducts electrons accordingly. Thus, porous coating 1 31 becomes positively charged. The ionically conducting electrolyte ions accordingly. An electric double layer is formed at the electrode-electrolyte interface forming the individual capacities in circuit 200. Thus, the surface of coating 1 33 becomes negatively charged, and the surface of coating 1 33B becomes positively charged. Because the porous high
surface area oxide allows the effective surface area of the electrode to become very high, the corresponding electrical storage capacity of the device increases dramatically.
Methods of Manufacturing the Energy Storage Device Referring to Figures 1 to 5, a general description for the preferred method to produce the dry pre-unit 10 of the energy storage device 10A, is as follows:
(A) Support Material Preparation
The support material are optionally etched or cleaned by a variety of conventional pickling and cleaning procedures. In some experiments, if the metal surface is not etched it is too smooth. This smooth surface sometimes causes inadequate adhesion of the porous coating. The etch creates a suitable rough surface.
1 . Wet Etching - A preferred procedure is to contact the metal support with an aqueous inorganic strong acid, e.g. sulfuric acid, hydrochloric acid, hydrofluoric acid, nitric acid, perchloric acid or combinations thereof. The etching is usually performed at elevated temperatures of 50 to 95 ° C (preferably 75 ° C) for about 0.1 to 5 hr (preferably 0.5 hr) followed by a water rinse. Room temperature acid etching is possible. An alkaline etch or an oxalic acid etch may also used.
2. Dry Etching - The roughened support surface is obtained by sputtering, plasma treatment, and/or ion milling. A preferred procedure is Ar RF sputter etching at between around 0.001 and 1 torr with about 1 KeV energy at 13.5 Mhz. Commonly, 0.1 -10 watts/cm2 power densities for about 1 -60 min. are used to clean and roughen the surface. Another procedure is to plasma etch the support with a reactive gas such as oxygen, tetrafluoromethane, and/or sulfurhexafluoride at around 0.1 -30 torr for about 1 -60 min.
3. Electrcchemical Etching - The roughened surface is obtained by electrochemical oxidation treatment in a chloride or fluoride solution.
(B) Coating of Support Material
The coating (e.g. oxide) is porous and composed of mostly micropores (diameter< 1 7A). Large 0.1 -1 μm wide cracks are present on the surface protruding to depths as thick as the coating. However, greater than 99% of the surface area
arises from these micropores. The average diameter of these micropores are around 6-1 2 A.
After various post-treatments the pore structure can be altered to increase the average pore size. For example, the steam post-treatment creates a bimodal pore distribution. In addition to the micropores, a narrow distribution of mesopores (diameter < 1 7-1 OOOA) having a diameter of about 35 A is created. These treated electrode coatings have 85-95% of the surface area arising from the micropore structure.
With alternate electrode construction methods this pore size distribution can be varied. The effective high surface area of the coating is 1 ,000 to 10,000 to
1 00,000 times larger than the projected surface area of the electrode as a monolith. The pore size, distribution, and surface area controlled with the temperature of pyrolysis and/or high temperature water treatment. In addition, the use of surfactants to create micelles or other organized structure in the coating solution increases the average pore size up to the values around 100-200 A with only 5-1 0% of the surface area coming from micropores.
As illustrated in Figure 1 3, the electrode 1 1 1 A includes a porous and conductive coating layer 1 1 9, which is formed on at least one surface of the support material 1 1 6. The support material 1 1 6 is electrically conductive, and sufficiently rigid to support the coating layer 1 1 9 and to impart sufficient structural rigidity to the device 1 0.
One goal of the present invention, is to optimize the energy density and power density of the device 10. The object is achieved by reducing the thickness of the support material 1 1 6, and maximizing the surface area of the coating layer 1 1 9. The power density of the device 10 is further optimized, by maintaining a low resistance.
The surface area of the coating layer 1 1 9 is determined by the BET methodology, which is well known in the art. The surface enhancement, which is an indication of the optimization of the surface area of the coating layer 1 1 9, is determined according to the following equation:
Surface enhancement = (BET Surface Area / Projected Surface Area)
In the present invention, the surface enhancement values can be as large as 1 0,000 to 100,000.
The coating layer 1 1 9 is porous, and its porosity could range between about five percent (5 %) and ninety-five percent (95%). Exemplary porosity range for efficient energy storage is between about twenty percent (20%) and twenty-five percent (25%).
In conventional double-layer capacitors, the main device resistance is due to the carbon coating layer. In the present invention, most of the device resistance is due to the electrolyte, which has a higher resistance than that of the porous conductive coating layer.
When the preunit device 1 0 is filled with an electrolyte, it becomes ready to be charged to become device 10A. The main criterion for the electrolyte is to be ionically conductive and have bipolar characteristics. The boundary or interface region between the electrode and the electrolyte is referred to in the field, as the "double layer", and is used to describe the arrangement of charges in this region. A more detailed description of the double layer theory is found in "Modern Electrochemistry", by Bockris et al, volume 2, sixth print, chapter 7 (1 977).
The surface area of the coating layer affects the capacitance of the device 1 0A. If for instance, the surface enhancement factor is between 1 ,000 to 20,000, and the double layer capacitance density is between about 1 0 to 500 microfarad per cm2 of the interfacial surface area (i.e. the BET surface area), then surface enhancement capacitance densities of about 0.1 to 10 farads/cm2 electrode are obtained.
While the double layer theory is described herein, it should be understood that other theories or models, such as the proton injection model, could alternatively be used.
The high surface area (porous) electrically conducting coating material is applied onto the support material.
1 . Solution Methods - The porous coating material may originate from various reactive precursors in a solution or a sol-gel composition. Numerous methods of application of these precursor compositions are feasible; but not limited
to the following. A curing, hydrolysis and/or pyrolysis process usually is performed to form the coating on the support. Pyrolysis of the metal salts is usually done in a controlled atmosphere (nitrogen, oxygen, water, and/or other inert and oxidative gasses) by means of a furnace and/or an infrared source. (a) Dip Coating - The electrode or support, is dipped into a solution or sol-gel, coating the support with a precursor coating, and subsequently cured by pyrolytic and other methods. Optionally, this process may be repeated to increase layer thickness. A preferred procedure is to dip the support material in a metal chloride/alcohol solution followed by pyrolysis at between about 250 and 500 ° C for 5-20 min in a 5-100% oxygen atmosphere.
This process is repeated until the desired weight of coating is obtained. A final pyrolysis treatment at 250-450 ° C is done for 1 -10 hr. Typically about 1 -30 mg/cm2 of coating is deposited onto a support for a capacitance density of around 1 - 10 F per square centimeter electrode cross-sectional area. Another procedure is to create a sol-gel solution with ruthenium, silicon, titanium and/or other metal oxides and coat the support as above. By adjusting the pH, water concentration, solvent, and/or the presence of additives like oxalic acid, formamide, and/or surfactants the discharge frequency characteristics of the coating may be adjusted.
High relative humidity during the pyrolysis step can be used to complete the conversion of starting material to oxide at lower temperatures, a procedure is to pyrolyze at about 300°C without control of humidity. However, an additional procedure is to maintain the relative humidity above about 50% during this pyrolysis at temperatures below 350°C or below.
A preferred method for dip coating thin (e.g. 1 mil) support structures is to use a wire frame structure 300 to keep the support material 1 18 under tension (Figures 15 and 15A).
The wire frame structure 300 includes at least two (2) wires 301 and 301 A of lengths larger than the width of the support material 1 18. Each wire 301 and 301 A includes a single length of wire which is tightly coiled at each end about 360° to form two coils 302 and 303. The coils are wrapped so the ends of the coil are around 1 cm above the plane of the wire. The coils 302 and 303 are placed through
holes 304 and 305, respectively, in the support materials. The holes 304 and 305 are located at two corners on an adjacent side of the support material.
Two additional wires 301 B and 301 C could be similarly used on the remaining two sides of the support material to provide additional support. (b) Spray Coating - The coating solution is applied to the support by a spray method, cured, and optionally repeated to increase the thickness. A preferred procedure is to apply the coating solution to the substrate at a temperature of 0- 1 50 ° C by means of an ultrasonic or other spray nozzle with a flow rate of around 0.1 -5 ml/min in a carrier gas composed of nitrogen, oxygen and/or other reactive and inert gases. The coating characteristics can be controlled by the partial pressure of oxygen and other reactive gasses.
(c) Roll Coating - The precursor coating is applied by a roll coating methodology, cured, and optionally repeated to increase the thickness. The coatings described above for dip coating are usable here. (d) Spin Coating - A spin coating methodology in the conventional art is used to apply the precursor coating, and optionally repeated.
(e) Doctor Blading - A doctor blading methodology is used to apply the precursor coating, and optionally repeated.
2. Electrophoretic Deposition - The porous coating or precursor coating is applied to the support by electrophoretic deposition techniques, and optionally repeated.
3. Chemical Vapor Deposition - The porous coating or precursor coating may be applied by chemical vapor deposition techniques known in the art.
(C) Electrode Pretreatment It has been found that a number of pretreatments (conditioning) or combinations thereof are useful to improve the electrical characteristics of the coating (e.g. electrochemical inertness, conductivity, performance characteristics, etc.). These treatments include for example:
1 . Steam - High temperature water or steam treatment controlled in atmospheres can be used to decrease the leakage current. A method procedure is to
contact the coated electrode with water saturated steam in a closed vessel at between 1 50 and 325 ° C for between 1 to 6 hr. under autogenic pressure.
2. Reactive Gas The coated electrode is contacted one or more times with a reactive gas such as oxygen, ozone, hydrogen, peroxides, carbon monoxide, nitrous oxide, nitrogen dioxide, or nitric oxide at between ambient temperature and 300 ° C at a reduced pressure or under pressure. A preferred procedure is to contact the coated electrode with flowing ozone at between about 5-20 weight percent in air at between ambient and 100 ° C and 0.1 -2000 torr pressure for 0.1 -3 hr.
3. Supercritical Fluid - The coated electrode is contacted with a supercritical fluid such as carbon dioxide, organic solvent, and/or water. A preferred procedure is treatment with supercritical water or carbon dioxide for 0.1 -5 hrs by first raising the pressure then the temperature to supercritical conditions.
4. Electrochemical-The coated electrode is placed in a sulfuric acid electrolyte and contacted with an anodic current sufficient to evolve oxygen gas and subsequently with a cathodic current. In one embodiment the electrode is contacted with 10mA/cm2 in 0.5M sulfuric acid for about 5 min, to evolve oxygen gas. The electrode is then switched to a cathodic current and the open circuit potential is driven back to a potential of between about 0.5V - 0.75V, preferably between 0.5 and 0.6 and more preferably about 0.5 V (vs. NHE) with out hydrogen gas evolution. 5. Reactive iiquid-The coated electrode is contacted with an oxidizing liquid such as aqueous solutions of hydrogen peroxide, ozone, sulfoxide, potassium permanganate, sodium perchlorate, chromium (VI) species and/ or combinations thereof at temperatures around ambient to 100 ° C for 0.1 -6 hr. A preferred procedure uses a 1 0-100 mg/l aqueous solution of ozone at 20-50 ° C for around 0.5-2 hr. followed by an aqueous wash. An additional procedure is to treat the coated electrode in a chromate or dichromate solution. (D) Spacing between Electrodes
A number of methods are available to obtain electrical insulation and properly defined spacing between the electrodes. These methods include, for example: 1 . Microprotrusions - The separator 1 25 and 1 27 between the coatings
1 1 9 and 1 20, includes a matrix of small (in area and height) protrusions, i.e. 1 25
and 1 27, on the surface of at least one side of the electrode. These microprotrusions may be composed of thermosets, thermoplastics, elastomers, ceramics, or other electrically insulating materials.
Several methods of applying these microprotrusions are included, but not limited to:
(a) Screen Printing - The microprotrusions are placed on the electrode surface by conventional screen printing, as described below, in greater detail, under the heading "SCREEN PRINTING". Various elastomers, thermosets, photo curable plastics, and thermoplastics are applied in this way. A preferred procedure is to use an acid resistant epoxy or VITON® solution.
(b) Chemical Vapor Deposition - Microprotrusions are also placed on the electrode surface by depositing silica, titania and/or other insulating oxides or materials through a mask.
(c) Photolithography - Microprotrusions are also produced by means of a photolithographic methods, as is described later, in greater detail, under the heading "PHOTOLITHOGRAPHIC PRODUCTION OF MICROPROTRUSIONS".
2. Physically thin separator sheet - The separator between the electrodes is a thin, substantially open structure material such as glass. A preferred material is 0.001 -0.005 in (0.00254 to 0.01270 cm) porous glass sheet available from Whatman Paper Ltd located in Clifton, NJ.
3. Casting a separator - The separator between the porous material is also obtained by casting a thin, substantially open structure film such as for example NAFION®, polysulfones, or various aero- and sol-gels.
4. Air space - The separator between the electrodes is also an air space which is subsequently occupied by the non-aqueous or aqueous electrolyte.
(E) Gasketing
The materials used for the gaskets, such as the gaskets 1 21 , 123, 135, 137, 1 57 and 1 59, at the edge of the active electrode surface include any organic polymer which is stable in the electrical/chemical environment, and to the processing conditions. Suitable polymers include, for example polyimide, TEFZEL®, polyethylene (high and low density), polypropylene, other polyolefins, polysulfone, KRATON®
other fluorinated or partly fluorinated polymers or combinations thereof. The gasket may be applied as a preformed material, screen printed, or by other methods. (F) Cord for Fill Port
The cord (1 1 7 A, 1 17B and 1 17C) for the creation of the fill ports, such as the fill ports 122 and 142, is of any suitable material having some specific properties, e.g., it is different from the gasket materials, has a higher melting temperature (Tm) than the gasket material, and does not melt, flow or adhere to the gasket material under the heating conditions described herein. Generally, glass, metal, ceramic, and organic polymers or combinations thereof are used. (G) Stacking
A stack is created by starting with an endplate and alternating gasket material, cord, electrode, gasket, cord electrode until the desired number of cells are created finishing with a second endplate, and optionally with a gasket material on the top outside of the stack. (H) Assembling (heating and cooling)
The stack is heated under pressure to cause reflow of the gasket material, adhering and sealing the perimeter of the electrode materials to the adjacent electrode in the stack; thereby, creating isolated celis and an assembled stack unit. This is done in an inert atmosphere. (a) Radio Frequency Induction Heating (RFIH) is used to heat the stack to cause reflow of the gasket material.
(b) Radiant Heating (RH) is used to uniformly heat the stack to cause reflow of the gasket material. A preferred method is to use 1 -100 μm radiation at 0.5-10 watts/cm2 for 1 -20 min. (c) Conductive and/or convective heating in a furnace, optionally in an inert atmosphere, is used to heat the stack to cause reflow of the gasket material. (I) Creating the fill port
The cords are pulled to remove them from the assembled unit to create a dry preunit having at least one fill port per a cell. (J) Post-Conditioning
1 . A number of post-conditioning reactive gas treatments of the stack or assembled stack or combinations thereof are useful to improve the overall and long term electrical characteristics of the electrode and resulting device. These include either before step (H) and/or after step (I) treatment with hydrogen, nitric oxide, carbon monoxide, ammonia, and other reducing gasses or combinations thereof at between ambient temperature and the Tm of the gasket material at a reduced pressure or under pressure.
2. A second post conditioning commonly done is to adjust the open circuit potential of the electrode after step (F) and stack the electrode in an inert atmosphere (e.g. Ar, N2). This is done by using a cathodic current without hydrogen evolution.
(K) Filling of Dry Preunit
The dry preunit is filled with an ionically conducting aqueous or non-aqueous electrolyte. A preferred electrolyte is approximately 30% sulfuric acid in water due to the high conductivity. Non-aqueous electrolytes based on propylene and ethylene carbonate are also used to obtain larger than 1 .2V/cell potentials.
A preferred procedure for filling the dry preunit with liquid electrolyte is to place the preunit in a chamber, evacuate the chamber between about 1 torr to 1 microtorr, preferably about 250 mtorr to less than 1 torr, and introduce the electrolyte; thereby, filling the cell gaps with electrolyte through the fill ports. Alternatively, the preunit may be placed in the electrolyte and a vacuum pulled; thereby causing the gas in the cell gaps to be removed and replaced by the electrolyte. In addition, non liquid based electrolytes (e.g. solid and polymer) may be used. In those cases the electrode is coated with the electrolyte before reflow and a fill port is not required.
(L) Sealing of Fill Ports
The fill ports are sealed by reflowing an additional film of polymer the same or different over the openings to create a sealed device. This is commonly done with an induction heater, which locally heats the film over the fill port opening.
(M) Burn-In
The device is brought to full charge usually by charging the device in 0.1 V/cell steps at a charging current of about 4 mA/cm2.
(N) Testing Termination Methods - Several methods are used to make electrical connections to the ultracapacitor endplates, and are described below.
1 . Endplate Tabs (1 60 and 1 60A) - The endplates (1 1 1 A and 1 1 1 Z) themselves have been cut to extend out beyond the normal gasket perimeter. These extensions allow attachment of a wire or ribbon. Typically, the extension is a stub from which all oxide material is removed down to the bare support material; 5 mil (0.01 27 cm) thick nickel ribbon is spot welded to the stub.
2. Silver Epoxy - The oxide coating is removed from the exposed faces of the endplates or the endplates may be coated only on one side. Clean nickel foil leads or copper plates make electrical connection to the exposed faces by bonding them together with a conductive silver epoxy. Optionally, the oxide coating is present.
3. Lugs - Threaded titanium nuts are welded to the thick titanium endplates before coating. Electrical connection to the titanium nuts is achieved by screw attachment. 4. Press Contacts - The oxide is removed or the endplates may be coated only on one side from the exposed side of the endplates before assembly into the device stack. The bare support material e.g. titanium, is reverse sputtered to clean the surface, being careful not to overheat the substrate. The clean surface is then sputtered with titanium to lay down a clean adhesion layer, followed by gold. The gold acts as a low contact resistance surface to which electrical contact can be made by pressing or by wire bonding.
5. Deposition of a compatible medium such for example aluminum, gold, silver, etc. outside by CVD or other means.
The device resistance is measured at 1 kHz. The device capacitance is determined by measuring the coulombs needed to bring the device to full charge at a
charging rate of around 4 mA/cm2 of electrode area. Leakage current is measured as the current needed to maintain a full charge after 30 min. of charging.
These devices may be made in various configurations depending on the desired application. By adjusting the device voltage, cell voltage, electrode area, and/or coating thickness in a rational manner, devices made to fit defined and predetermined specifications are constructed.
The electrode capacitance density (C in units of F/cm2) is roughly 1 F/cm2 for every 10 μπ. of coating. Therefore, for large capacitance values a thicker coat is used. The device capacitance (C) is equal to the electrode capacitance density times the electrode area (A in units of cm2) divided by two times the number of cells (n) (equation 1 ).
The leakage current (i") is proportional to the electrode area, while the equivalent series resistance (ESR) is inversely proportional to the electrode area (eqn. 2). Typical values for i" are less than 20 //A/cm2. The total number of cells in a device (n) is equal to the cell voltage (V) divided by the total device voltage (V) (eqn. 3). Cell voltages up to about 1 .2 V can be used with aqueous based electrolytes.
The device height (h), based on a cell gap (h') and a support thickness (h"), is determined from the number of cells and the electrode capacitance density in units of cm by equation 4.
The device ESR is a function of the number of cells times the cell gap (h') times the resistivity of the electrolyte (r) times a factor of about 2 divided by the area (equation 5). eqn. 1 C = C'A/2n eqn. 2 i" σ A σ 1 /ESR eqn. 3 n = V/V eqn. 4 h/cm = n(0.002C' + h' + h") eqn. 5 ESR « 2nh'r/A
Devices are constructed to meet the requirements of various applications by considering the voltage, energy, and resistance requirements. The following examples are not meant to be limiting in any way:
For electric vehicle applications about a 100 KJ to 3 MJ device is used. A large voltage (about 100 to 1000 V) large energy (1 -5 F/cm2) storage device is used with an electrode area of about 1 00 to 10,000 cm2.
For electrically heated catalyst applications for reduction of automobile cold start emissions about a 10 to 80 KJ device is used. This device is about 1 2 to 50 V constructed with around 100 to 1000 cm2 area electrodes of 1 -5 F/cm2. Optionally, a device consisting of several devices in parallel can be constructed to meet the electrical requirements.
For defibrillator applications about a 200-400 V device with 0.5 to 1 0 cm2 area electrodes of 1 -3 F/cm2 are used.
For uninterruptable power source applications various series/parallel device configurations may be used. Screen Printing
Considering now a screenprinting method 250, with respect to Figures 7 and 8, the focus of the method 250, is to produce a series of microprotrusions 1 25 and 1 27 on the surface of the coating layers, to act as a space separator in electrical storage devices, such as a capacitor or a battery, in general, and in the dry preunit energy storage device 10, in particular.
The substrate is usually a thin metal such as titanium, zirconium, or alloys thereof. The substrate is usually in the shape of a thin metal plate as is conventional in the capacitor art.
The substrate is coated on one or both sides with a porous carbon compound or a porous oxide coating. This step is accomplished by methods conventional in the art. The oxide coating serves as the charge storage area for the device. Alternately, a stacked set of battery electrodes (e.g., lead for lead acid) or electrolytic capacitor electrodes (e.g., alumina and tantalum) may be fabricated.
It is important that the flat surfaces of adjacent coated substrates or electrodes do not contact each other and further be of a uniform separation. The epoxy microprotrusions accomplish the desired uniform separation. Sample Holding -- The coated thin flat substrate needs to be secured (or held), so that the formation of the microprotrusions is precise and accurate on the
flat surface of the substrate. For thin metal sheets (0.1 to 5 mil (0.000254 to 0.01 27 cm), especially about 1 mil (0.00254 cm)) an electrode holder 275 is particularly important. If a strong vacuum is pulled on a thin sheet, often reverse dimples are formed in the thin sheet which cause significant undesirable changes in the physical and electrical properties of the final device.
The electrode holder 275 includes a porous ceramic holder 276, which is useful because the pore size is small enough that the dimples do not appear when a mild or stronger vacuum is pulled. The flat ceramic surface of the ceramic holder 276 must be in intimate contact with the surface of the electrode 1 1 1 A, under conditions which do not deform the metal or disrupt the coating present. The vacuum used with the porous ceramic is at least 25 in mercury. Preferably the vacuum is between about 25 and 30 in., especially 26 and 29 in.
Further, the ceramic substrate needs to be flush with the surface of any mechanical holder to assure that uniform extrusion of the epoxy through the screen openings occurs. Flush in this context means that the flat surface of the holder and the surface of the coating for electrical storage differ from each other by between about ± 5 mil (0.01 27 cm) deviation or less from level per 6 linear in.
The electrode holder 275 further includes a metal frame 277, which should also be as flush (flat) as possible so that uniformly sized protrusions are formed from one end of the electrode to the other.
The electrode holder 275 can be purchased from a number of commercial sources for example from Ceramicon Designs, Golden, Colorado. Alternatively, the sample holder 276 can be manufactured using commercially available metals, alloys or ceramics. Usually, a 5 in ( 1 2.7 cm) by 7 in ( 1 7.78 cm) coated sheet electrode is formed.
The metal holder 277 has a plurality of strategically located pins, such as the three pins 278, 279 and 280, which are used to align and position the electrode 1 1 1 A, using a plurality of corresponding holes 281 , 282 and 283, respectively. The holes 281 , 282 and 283 are usually as close to the peripheral edges of the electrode
1 1 1 A, as possible to conserve useful electrode surface. Alternatively, no alignment holes are used, and the pins are used to align the electrode edges.
A stencil (not shown) having a predetermined open pattern, is stretched and secured in a conventional screen printing frame (not shown). The screen mesh is removed.
The epoxy components are mixed and the fluid epoxy is placed on the surface of the stencil, then spread to obtain an even applied coat. This can be accomplished using a pressure bar, doctor bar or a squeegee.
Usually, constant temperature and humidity are important to obtain an even coat.
The stencil is then carefully removed leaving the fluid epoxy protrusions on the surface of the oxide. The epoxide protrusions are then cured using ambient, accelerated heat at from between 100 to 1 50°C. or light.
The electrode having microprotrusions is then combined with other electrodes, and assembled in a wet process or a dry process. If a dry process is used, the dry unit 1 0 is then back filled with electrolyte, when it is to be charged.
It is important that the cured epoxy does not react with the liquid electrolyte eventually used in the fabrication of the capacitor having multiple layers of electrodes. The cured microprotrusions then perform their function by keeping the spacing between the electrodes uniform.
As can be seen from Figure 6, the edges of the flat surface of the electrode have protrusions 1 25 that are closer together than those protrusions 1 27 in the active or central portion of the electrode. These protrusions 1 25 increase the support at the edges to maintain uniform separations. Alternatively, bars may be used.
It is apparent that from these teachings the following are possible: Increasing or decreasing the substrate electrode thickness will allow an increase or decrease in the microprotrusion spacing due to changes in support rigidity.
Other thermosets, thermoelastomers, or photo curable epoxies or epoxy derivatives conventional in the art can be used.
Other microprotrusion pattern elements can be used such as squares, lines, crosses, etc. Specifically, bars on the perimeter can add mechanical support. Optionally the screen may be heated, if necessary to bring the resin flowable epoxy to a temperature when its viscosity becomes suitable for printing for a short time.
This heating step followed by screen printing of the flowable epoxy resin must be performed quickly because the working time for the epoxy is significantly reduced.
The electrical storage devices produced having the microprotusions 1 25 and 1 27 are useful as batteries, capacitors and the like. Photolithographic Production of Microprotrusions
The focus of the present method is to produce a series of microprotrusions on the surface, or alloys of the electrode substrate, using photolithography, with respect to Figures 10, 1 1 and 12. The substrate is usually in the shape of a thin metal plate as is conventional in the capacitor art.
A photo resist film 381 is applied to the surface of the electrode 1 1 1 A, either by vacuum lamination using the commercially available Dynachem ConforMASK film applicator, and Dynachem vacuum applicator Model 724/730, or by passing the photo resist film 381 and electrode 1 1 1 A through a pair of heated rollers 384 and 385.
Exposure is done using a standard 1 -7kW UV exposure source, such as mercury vapor lamps 389. The ConforMask film applicator is developed using standard conditions such as 0.5-1 .0% sodium or potassium carbonate monohydrate in either a developing tank or a conveyorized aqueous developer. Optionally, after developing the electrode with microprotrusions may be neutralized in a dilute 10% sulfuric acid solution. This removes all the unwanted unreacted film to leave the reacted microprotrusions adhered to the electrode surface.
To obtain optimum physical and electrical performance properties the resulting material is put through a final curing process involving both UV irradiation and thermal treatment utilizing conventional UV curing units and convection air ovens.
The multiple electrodes are assembled to produce for instance a capacitor, as described above. The microprotrusions accomplish the desired uniform separation. COMMERCIAL APPLICATIONS
The energy storage device 10A has a multitude of applications, as a primary or back up power supply, and/or as a capacitor. The size is from 0.1 volt to 100,000 volts or 0.1 cm3 to 106 cm3. Typical voltage ranges may include combinations of uses in automotive and other applications.
Among these applications are the following:
Automobile Applications Airbags & Seat Restraints
Seat Warmers
Electronically Heated Catalyst
Electric Vehicle Propulsion
Hybrid Electric Vehicle Propulsion Internal Combustion/Ultra
Capacitor Propulsion
Power Steering
Regenerative Braking/Shock Absorption
Starting Lighting and Ignition with battery Starting Lighting and Ignition stand alone
Medical Applications
Cardiac Defibrillators
Pacemakers
Neuro stimulators and like
Implantable and external devices
Surgical Power Tools
Medical Applications (cont)
Ambulatory Monitoring Equipment Automatic Liquid Chromatography
Automated Clinical Lab Analysis
Computerized Tomography (CT) Scanners
Dental Equipment
Digital Radiography Equipment Electrosurgical Instruments
Fiberoptics
Examination Scopes
Hearing Aids
Infusion Devices Magnetic Resonance Imaging (MRI)
Nuclear Medical Diagnostic Equipment
Electric Patient Monitoring Systems
Respiratory Therapy Equipment
Surgical Lasers Electric Surgical Support Systems
Ultrasonic Diagnostic Equipment
Mobile Propulsion Systems
Fork lifts
Golf carts Farm Implements Trains Subways
Regenerative Braking
Business/Commercial Electronics Applications
Calculators
Cellular Telecommunications Commercial Audio Amplifiers
Commercial Flash/Strobe Lights
Commercial Power Tools
Business/Commercial Electronics (cont)
Commercial Video Cameras
Computers Copiers
Dictation Equipment
Electric Motors
Electronic Locks
Electronic Organizers/PDAs Emergency Lighting Systems
Facsimile Equipment
Microphones
Pagers
Printers Security Systems
Slide Projectors
Uninterruptible Power Supplies
Surge Protectors
Wireless Networks
Consumer Electronics Applications
Audio Systems:
Compact/Home Portable Tape/CD Walkman/Personal Stereo CB Radios
HAM Radios
Camcorders
Home Satellite Dishes
Microphones Monitors and Cathode Ray Tubes
Photo Flash
Consumer Electronics Applications (cont)
Receivers, Transceivers
Telephone answering devices Cellular, cordless phones
Toys & Games
Television sets Home Portable VCRs
Video Disk Players
Video Games
Watches/Clocks
Consumer Electric Housewares Applications Air Purifiers
Bag Sealers
Blenders
Clocks-Total
Alarm & Desk Coffee Grinders
Coffee Makers
Convection Ovens
Corn Poppers
Curling Irons/Brushes Deep Fryers
Electric Blankets
Flashlights
Floor Polishers
Food Processors Hair Dryers
Consumer Electric Housewares Applications
Home Security Systems
Irons Knives
Massagers
Mixers
Microwave Ovens
Power Tools Security Systems
Shavers
Smoke Detectors
Timers
Toasters/Toaster Ovens Toothbrushes (Electric)
Vaporizers
Water Pulsators
Whirlpools (Portable)
Consumer Maior Appliances Compactors
Dishwashers
Dryers
Freezers
Ranges Refrigerators
Washers
Water Heaters
Outdoor Appliances
Bug Killers Outdoor Grills
Power Mowers
Outdoor Appliances (cont)
Riding Mowers
Riding Tractors
Rotary Tillers
Snow Plows/Blowers
Other Applications Electro-expulsive Deicing Electronic Fuses Lasers
Phased-Array radar Rail Gun
Multiple devices are placed is series and/or parallel for specific applications to achieve desired performance. Fabrication of Dry Preunit
The following examples are presented to be descriptive and explanatory only. They are not to be construed to be limiting in any manner. EXAMPLE 1
Fabrication of A Dry Preunit (A) Coating Method
The support structure is prepared by etching a 1 mil (0.00254 cm) titanium sheet with 35% HN03/1 .5 % HF at 60 ° C for 5 min. The end plates are 5 mil (0.01 27 cm) titanium.
The oxide coating solution is 0.2 M ruthenium trichloride trihydrate and 0.2 M niobium pentachloride in tert-butanol (reagent grade).
The etched Ti sheets are dip-coated by immersion into the solution at ambient conditions. The coated sheet is submerged into the solution, held for about 1 sec and then removed.
After each coating, the oxide is dried at 70 ° C for 10 min, pyrolyzed at 350 ° C for 10 min and removed to cool to ambient temperature all in ambient atmosphere.
The dip-coating steps are repeated for 10 coats (or any desired number) rotating the Ti sheet so as to dip with alternate sides down. A thickness of about ten microns is achieved.
The fully coated sheet is final annealed at 350 "C for 3 hrs in ambient atmosphere.
(B) Electrode Pretreatment The coated electrode is contacted with saturated steam in a closed vessel at
280 ° C for 3 hrs under autogenic pressure.
(C) Spacing
Microprotrusions are screen printed on one side of the electrode, as described below, in greater detail, under the heading "SCREEN PRINTING". The epoxy compound is EP21 AR from Masterbond, of Hackensack, New Jersey.
The epoxy protrusions are cured at 150 °C for 4 hr. in air. The coated electrodes are next die-stamped to the desired shape.
(D) Gasket
A modified high density polyethylene (HDPE, improved puncture resistance and adhesion) 1 .5 mil (0.00381 cm) thick by 30 mil (0.0762 cm) wide with outside perimeter the same as that of the electrode is placed on the electrodes on the same side as the microprotrusions and impulse heat laminated. The HDPE is grade PJX 2242 from Phillips-Joanna of Ladd, Illinois.
(E) Cord One cord (Dupont T2 TEFZEL® film 90ZM slit in machine direction) 0.9 mil
(0.00229 cm) thick by 10 mil (0.0254 cm) wide is placed across the narrow dimension of the gasket and electrode surface and aligned between microprotrusions. The location of the cord is one of three positions centered, left of center, or right of center. A second HDPE gasket is placed on the first gasket sandwiching the cord between the two gaskets.
The second gasket is impulse heated to adhere to the first gasket and to fix the cord in place.
(F) Stacking Electrode/microprotrusion/gasket/cord/gasket units are stacked in a non- metallic (ceramic) alignment fixture beginning with a 5 mil (0.01 27 cm) end plate unit to the desired number of cells and ending with a plain 5 mil (0.0127 cm) end plate with the cords arranged such that the location is staggered-left, center, right in a three unit repeating cycle (end perspective). Light pressure is applied to the top of the stack through a ceramic piston block to maintain uniform alignment and contact throughout the stack.
(G) Reflow
A radio frequency induction heater (2.5 kW) is used to heat the stack. The stack was placed centrally in the three turn, 3 in (7.62 cm) diameter coil and heated for 90 seconds at a power setting of 32 % . The fused unit is allowed to cool to ambient temperature.
(H) Cord Removal
The cords are removed by carefully pulling the exposed ends of the cord to leave the open fill ports.
EXAMPLE 2 Alternative Fabrication of Dry Preunit
(A) Coating Method
The support structure is prepared by etching a 1 mil (0.00254 cm) titanium sheet with 50% HCI at 75 ° C for 30 min. The end plates are 2 mil (0.00508 cm) titanium. The oxide coating solution is 0.3 M ruthenium trichloride trihydrate and 0.2 M tantalum pentachloride in isopropanol (reagent grade).
The etched Ti sheets are dip-coated by immersion into the solution at ambient conditions. The coated sheet is submerged into the solution, held for about 1 sec and then removed. After each coating, the oxide is dried at 70 ° C for 10 min. in ambient atmosphere, pyrolyzed at 330 ° C for 1 5 min in a 3 cubic feet per hrs. flow of 50 vol.
% oxygen and 50 % nitrogen, and removed to cool to ambient temperature in ambient atmosphere.
The dip-coating steps are repeated for 30 coats (or any desired number) rotating the Ti sheet so as to dip with alternate sides down. The fully coated sheet is final annealed at the above conditions for 3 hr.
(C) Spacing
VITON® microprotrusions are screen printed on one side of the electrode, as described below, in greater detail, under the heading "VII. SCREEN PRINTING" .
The VITON® protrusions are cured at 1 50 ° C for 30 min. in air. The coated electrodes are next die-stamped to the desired shape.
(D) Gasket
A modified high density polyethylene (HDPE, improved puncture resistance and adhesion) 1 .0 mil (0.00254 cm) thick by 20 mil (0.0508 cm) wide with outside perimeter the same as that of the electrode is impulse heat laminated to both sides of the electrode. The HDPE is grade PJX 2242 from Phillips-Joanna of Ladd, Illinois.
(E) Cord
One cord, 1 mil (0.00254 cm) diameter TEFLON® coated tungsten wire is placed across the narrow dimension of the gasket and electrode surface and aligned between microprotrusions. The location of the cord is one of three positions centered, left of center, or right of center.
(F) Stacking Electrode/microprotrusion/gasket/cord/gasket units are stacked beginning with a 2 mil (0.00508 cm) end plate unit to the desired number of cells and ending with a plain 2 mil (0.00508 cm) end plate with the cords arranged such that the location is staggered-left, center, right in a three unit repeating cycle (end perspective) .
(G) Reflow
The HDPE gasket is reflowed in nitrogen at 1 25 ° C for 1 20 min to reflow the thermoplastic. The unit is cooled in nitrogen to ambient temperature. (H) Cord Removal The cords are removed by pulling the exposed ends to leave the open fill ports.
EXAMPLE 3 Alternative Fabrication of Dry Preunit
(A) Coating Method
The support structure is prepared by etching a 1 mil (0.00254 cm) titanium sheet with 50% Hcl at 75 °C for 30 min. The end plates are 10 mil (0.0254 cm) titanium.
The oxide coating solution is 0.2 M ruthenium trichloride trihydrate and 0.2 M tantalum pentachloride in isopropanol (reagent grade).
The etched Ti sheets are dip-coated by immersion into the solution at ambient conditions. The coated sheet is submerged into the solution, held for about 1 sec and then removed.
After each coating, the oxide is dried at 70 ° C for 10 min, pyrolyzed at 300 ° C for 5 min and removed to cool to ambient temperature all in ambient atmosphere. The dip-coating steps are repeated for 10 coats (or any desired number) rotating the Ti sheet so as to dip with alternate sides down.
The fully coated sheet is final annealed at 300 ° C for 3 hrs in ambient atmosphere.
(B) Electrode Pretreatment The coated electrode is contacted with saturated steam in a closed vessel at
260 ° C for 2 hrs under autogenic pressure.
(C) Spacing
Microprotrusions are screen printed on one side of the electrode, as described below, in greater detail, under the heading "SCREEN PRINTING". The epoxy compound is grade EP21 AR from Masterbond, Hackensack, NJ.
The epoxy protrusions are cured at 1 50 ° C for 4 hr. in air. The coated electrodes are next die-stamped to the desired shape.
(D) Gasket
A modified high density polyethylene (HDPE, improved puncture resistance and adhesion) 1 .5 mil (0.00381 cm) thick by 30 mil (0.0762 cm) wide with outside perimeter the same as that of the electrode is placed on the electrodes on same side
as the microprotrusions and impulse heat laminated. The HDPE® is grade PJX 2242 from Phillips-Joanna of Ladd, Illinois.
(E) Cord
One cord (TEFZEL®) 1 mil (0.00254 cm) thick by 10 mil (0.0254 cm) wide is placed across the narrow dimension of the gasket and electrode surface and aligned between microprotrusions. The location of the cord is one of three positions centered, left of center, or right of center.
A second HDPE® gasket is placed on the first gasket sandwiching the cord between the two gaskets. The second gasket is impulse heated to adhere to the first gasket and to fix the cord in place.
(F) Stacking Electrode/microprotrusion/gasket/cord/gasket units are stacked beginning with a 10 mil (0.0254 cm) end plate unit to the desired number of cells and ending with a plain 10 mil (0.0254 cm) end plate with the cords arranged such that the location is staggered-left, center, right in a three unit repeating cycle (end perspective).
(G) Reflow
The gasket is reflowed in nitrogen at 1 60 ° C for 45 min to reflow the thermoplastic. Tne unit is cooled in nitrogen to ambient temperature. (H) Cord Removal
The cords are removed by carefully pulling the exposed ends to leave the open fill ports.
EXAMPLE 4 Alternative Fabrication of Dry Preunit (A) Coating Method
The support structure is prepared by etching a 1 mil (0.00254 cm) titanium sheet with 50% HCI at 75 " C for 30 min. The end plates are 5 mil (0.01 27 cm) titanium.
The oxide coating solution is 0.2 M ruthenium trichloride trihydrate and 0.2 M Ti(di-isopropoxide)bis 2,4-pentanedionate in ethanol (reagent grade) .
The etched Ti sheets are dip-coated by immersion into the solution at ambient conditions. The coated sheet is submerged into the solution, held for about 1 sec and then removed.
After each coating, the oxide is dried at 70 ° C for 10 min, pyrolyzed at 350 ° C for 5 min in oxygen and removed to cool to ambient temperature all in ambient atmosphere.
The dip-coating steps are repeated for 30 coats (or any desired number) rotating the Ti sheet so as to dip with alternate sides down.
The fully coated sheet is final annealed at 350 ° C for 3 hrs in an oxygen atmosphere.
(C) Spacing
Microprotrusions are thermally sprayed through a mask on one side of the electrode. The thermal spray material is TEFLON® from E.I. DuPont de Nemours & Co., Wilmington, Delaware. The TEFLON8 protrusions are cured at 300 ° C for 0.5 hr. in air. The coated electrodes are next die-stamped to the desired shape.
(D) Gasket
A modified high density polyethylene (HDPE, improved puncture resistance and adhesion) 1 .5 mil (0.00381 cm) thick by 30 mil (0.0762 cm) wide with outside perimeter the same as that of the electrode is placed on the electrodes on same side as the microprotrusions and impulse heat laminated. The HDPE is grade PJX 2242 from Phillips-Joanna of Ladd, Illinois.
(E) Cord
One cord (TEFZEL®) 1 mil (0.00254 cm) thick by 10 mil (0.0254 cm) wide is placed across the narrow dimension of the gasket and electrode surface and aligned between microprotrusions. The location of the cord is one of three positions centered, left of center, or right of center.
A second HDPE® gasket is placed on the first gasket sandwiching the cord between the two gaskets. The second gasket is impulse heated to adhere to the first gasket and to fix the cord in place.
(F) Stacking Electrode/microprotrusion/gasket/cord/gasket units are stacked beginning with a 5 mil (0.01 27 cm) end plate unit to the desired number of cells and ending with a plain 5 mil (0.01 27 cm) end plate with the cords arranged such that the location is staggered-left, center, right in a three unit repeating cycle (end perspective).
(G) Reflow
The gasket is reflowed in nitrogen at 1 90 ° C for 30 min. to reflow the thermoplastic. The unit is cooled in nitrogen to ambient temperature. (H) Cord Removal The cords are removed by carefully pulling the exposed ends to leave the open fill ports.
EXAMPLE 5 Alternative Fabrication of Dry Preunit (A) Coating Method The support structure is prepared by etching a 0.8 mil (0.002032 cm) zirconium sheet with 1 %HF/20% HN03 at 20 " C for 1 min. The end plates are 2 mil (0.00508 cm) zirconium.
The oxide coating solution is 0.2 M ruthenium trichloride trihydrate and 0.1 M tantalum pentachloride in isopropanol (reagent grade). The etched Ti sheets are dip-coated by immersion into the solution at ambient conditions. The coated sheet is submerged into the solution, held for about 1 sec and then removed.
After each coating, the oxide is dried at 85 ° C for 10 min, pyrolyzed at 31 0 ° C for 7 min and removed to cool to ambient temperature all in ambient atmosphere.
The dip-coating steps are repeated for 10 coats (or any desired number) rotating the Ti sheet so as to dip with alternate sides down.
The fully coated sheet is final annealed at 310 ° C for 2 hrs in ambient atmosphere. (C) Spacing
Microprotrusions are thermally sprayed through a mask on one side of the electrode. The thermal spray material is TEFLON® from E.I. DuPont de Nemours & Co., Wilmington, Delaware.
The TEFLON® protrusions are cured at 310 ° C for 1 .0 hr. in air. The coated electrodes are next die-stamped to the desired shape.
(D) Gasket
A polypropylene gasket 1 .5 mil (0.00381 cm) thick by 30 mil (0.0762 cm) wide with outside perimeter the same as that of the electrode is placed on the electrodes on same side as the microprotrusions and impulse heat laminated. (E) Cord
One cord, 1 mil (0.00254 cm) diameter TEFLON® coated tungsten wire, is placed across the narrow dimension of the gasket and electrode surface and aligned between microprotrusions. The location of the cord is one of three positions centered, left of center, or right of center. A second polypropylene gasket is placed on the first gasket sandwiching the cord between the two gaskets.
The second gasket is impulse heated to adhere to the first gasket and to fix the cord in place.
(F) Stacking Electrode/microprotrusion/gasket/cord/gasket units are stacked beginning with a 2 mil (0.00508 cm) end plate unit to the desired number of cells and ending with a plain 2 mil (0.00508 cm) end plate with the cords arranged such that the location is staggered-left, center, right in a three unit repeating cycle (end perspective).
(G) Reflow The gasket is reflowed in nitrogen at 1 95 ° C for 60 min. to reflow the thermoplastic. The unit is cooled in nitrogen to ambient temperature. (H) Cord Removal
The cords are removed by pulling the exposed ends to leave the open fill ports. EXAMPLE 6
Filling of the Cell Gap Space
A dry preunit 10 may be filled with an electrolyte with the following procedure. Any of many possible dry preunit configurations may be used. (H) Back Fill
The cords are removed manually to open the fill port. The stacked unit is placed into an evacuation chamber and evacuated to < 35 mtorr for 5 to 60 min. The liquid electrolyte 3.8 M H2S04 de-airated with nitrogen is introduced into the chamber and fills the evacuated space between the electrodes. (I) Seal Fill Port Openings
The electrolyte filled preunit is removed from the chamber. It is rinsed with deionized water to remove excess electrolyte and dried. HDPE film (1 .5 mil
(0.00381 cm) thick) is placed over the fill port openings and impulse heat sealed over the ports.
(J) Conditioning
The device is charged up to full charge beginning at 0.1 V/cell increasing by 0.1 V/cell until 1 V/ceil is obtained. (K) Testing
The device is tested in the conventional manner, having 1 V/cell with leakage current of less than 25 μA/cm2, and a capacitance density per a cell of greater than about 0.1 F/cm2. A 10 V device has a height of no more than 0.05", a 40 V device has a height of no more than 0.1 3", and a 100 V device has a height of no more than 0.27" .
Performance characteristics for various device geometries and configurations based on a sulfuric acid electrolyte are presented in Table 1 .
Table 1 Ultracapacitor Device Performance Characteristics
Area/cm2 volt C/mF
ESR/mohm vol/cc
J/cc
watt/cc 860 1660 2000 2000 3670 1100
EXAMPLE 7 Alternative Backfill of Dry Preunit A dry preunit 10 may be filled with an electrolyte with the following procedure. Any of many possible dry preunit configurations may be used. (H) Back Fill
The cords are removed to open the fill port. The stacked unit is placed into an evacuation chamber and evacuated to < 35 mtorr for 5 to 60 min. The liquid non-aqueous electrolyte 0.5 M KPF6 in propylene carbonate de-airated with nitrogen is introduced into the chamber and fills the evacuated space between the electrodes. (I) Seal Fill Port Openings
The electrolyte filled preunit is removed from the chamber and excess electrolyte is removed. HDPE film (1 .5 mil (0.00381 cm) thick) is placed over the fill port openings and impulse heat sealed over the ports. (J) Conditioning
The device is charged up to full charge beginning at 0.1 V/cell increasing by 0.1 V/cell until 1 .5 V/cell is obtained. (K) Testing
The device is tested in the conventional manner, having 1 .5 V/cell with leakage current of around 100 /A/cm2, and a capacitance density of around 4 Mf/cm2 for a 10 cell device.
EXAMPLE 8 DEVICE POST-TREATMENT CONDITIONS The following is a list of the electrical properties (Table 3) of devices using various gas postconditioning techniques to adjust the electrode rest potential so that charging to at least 1 V/cell on multicell devices filled with 4.6 M sulfuric acid electrolyte is possible and reduced leakage currents are observed. This treatment is done before, during, and/or after reflow of the gasket material. For gas treatment at temperatures below that used for gasket reflow the atmosphere was exchanged with an inert gas such as nitrogen or argon during reflow. For treatment after reflow of
the gasket material the tabs were removed before treatment. During treatment the atmosphere is evacuated and filled with the reactive gas periodically.
TABLE 3
Application of Epoxy Microprotrusions by Screen Printing onto a Porous Coating on a
Thin Substrate
(A) Screen Preparation - A 325 mesh stainless steel screen is stretched on a standard screen printing frame. To this screen is edge glued (Dexter Epoxy 608 clear) to a smaller 1 -1 .5 mil (0.00254 to 0.00381 cm) thick brass sheet which has holes (6.3 mil (0.01 6 cm) diameter) drilled or etched to the desired pattern. The screen mesh is removed from the area covered by the brass sheet leaving the brass sheet edge glued to the screen mesh attached to the frame.
(B) Sample Holding - A vacuum is pulled on a porous alumina holding plate of 1 0 μm average pore diameter is used to hold the 1 mil (0.00254 cm) thick porous oxide coated material during the printing.
(C) Epoxy - A two component epoxy Master Bond EP21 AR is modified to the desired viscosity (thixotropic, 300,000 to 400,000 cps) by the addition of a silica filler. The filled epoxy having the desired viscosity is available by purchase order from Master Bond, Inc. of Hackensack, New Jersey. The epoxy is prepared as per instructions. The useful lifetime as a flowable fluid is about 30 min.
(D) Screen printer parameters ~ squeegee speed: 1 -2 in/s snap off: 20-30 mil (0.0508 to 0.0762 cm)
Constant temperature and humidity of the epoxy are important to assure an even applied coat. Typical conditions are about 40-70% relative humidity and a temperature of about 20-25 °C.
(E) Printed epoxy pattern -- An array of epoxy bumps essentially 1 mil (0.00254 cm) in height and about 7.5 mil (0.01 9 cm) in diameter are produced. A typical pattern on an electrode consists of an array of microprotrusions deposited on 40 mil (0.1 01 6 cm) center-to-center spacing. In addition, the density of microprotrusions at the perimeter of the electrode is increased by decreasing their center-to-center spacing to 20 mil (0.508 cm). The screen printed epoxy configuration is cured at 1 50°C for a minimum of 4 hr.
EXAMPLE 1 0 Screen Print Formation of Epoxy Microprotrusions
(A) Screen Preparation -- A 230 or 325 mesh screen (8x1 0 in stainless steel) without an emulsion on the surface, mounted on a standard printing frame, is used as the base piece. An etched, drilled or punched stencil (6.0 x 8.5 molybdenum) is edge glued using Dexter Epoxy 608 Clear from Dexter located to the back side of the screen. MYLAR® is placed over the stencil-screen unit and pressure applied to smooth the epoxy into a uniform layer.
The screen is then flipped, epoxy applied to the top side of the screen, a MYLAR® sheet placed over the area and the epoxy smoothed. The MYLAR® sheet on the top side of the screen is then removed. The screen-stencil assembly is then placed into a 1 20°C oven with ambient atmosphere for 5 min to cure the epoxy. Alternatively, the epoxy can be cured by setting at ambient temperature for 30-60 min.
After removal of the screen-stencil from the oven, the MYLAR® on the back side is carefully peeled away immediately. The mesh screen on the top side is then cut away using a sharp edge, with care being taken to prevent cutting of the stencil. Upon removal of the mesh over the stencil pattern, any heat stable thermoset adhesive (e.g. an epoxy resin) is applied to the cut mesh-stencil perimeter, covered with MYLAR®, and
the epoxy smoothed to ensure edge attachment of the screen to the stencil. The epoxy is cured in the oven for 5 min. The resulting item is a stencil stretched taut by the screen, ready for printing.
(B) Sample Holding - A porous ceramic holding (e.g. Fig. 8) plate (Ceramicon Designs, Golden, Colorado, P-6-C material) of 4.5-6μ pore diameter with a porosity of
36.5% (30-60% porosity is acceptable) is used to hold the 1 mil (0.00254 cm) thick porous oxide coated material during the printing by pulling a vacuum through the porous ceramic plate. The ceramic plate is cut to the appropriate dimensions (the size and shape of the substrate to be printed). This ceramic plate then is inserted into an aluminum (steel, etc) frame 277 and epoxy or other adhesive) that can be mounted to a screen printer. The ceramic plate is then carefully ground flush to the metal frame as flat as possible. Locating pins 278, 279 and 280 are then added to hold the substrate 1 1 I A in appropriate location using holes 281 , 282 and 283.
(C) Epoxy - The Master Bond EP 21 ART® (a two component epoxy (of polyamine hardener, 33 weight percent and a liquid epoxy resin, 67 weight percent) about with a viscosity of 1 50,000 to 600,000 cps). The epoxy is prepared as per the product instructions. The useful lifetime as a flowable fluid is about 30 min.
(D) Screen Printing Parameters - Squeegee Speed 1 -2 in/s (depends upon epoxy viscosity)
Snap Off 20-30 mil (0.0050 to 0.0076 cm) (Related to screen tension; and adjusted accordingly)
(E) Printed epoxy pattern - An array of epoxy bumps essentially about 1 to 1 .25 mil (0.00254 to 0.0031 6 cm) in height and about 7.5 mil (0.01 9 cm) in diameter are produced. A typical pattern on an electrode consists of an array of microprotrusions deposited on 40 mil (0.1 cm) center-to-center spacing. In addition, the density of microprotrusions around the perimeter of the electrode is increased by decreasing their center-to-center spacing to 20 mil (0.0508 cm). The screen printed epoxy configuration is cured at 1 50°C for 4 to 1 2 hrs. in an ambient atmosphere.
EXAMPLE 1 1 ALTERNATIVE SCREEN PRINTING PARAMETERS
(A) Separator Bumps -- Separator bumps range in height from .001 to .004 in. (.00254 to 0.0101 6 cm) and widths of .006 to .01 2 in. (.01 524 to .03038 cm). Separator bumps may take the form of dots, squares, rectangles or a composite of these shapes. The widths of the bumps increase as the bump height is increased.
(B) Separator Pattern - Two patterns are utilized on an electrode substrate, the Active Field Area and the Bounding Border Area. The AFA has the separator bumps located on .040 by .040 in. (.101 6 by .101 6 cm) center to center spacing and are normally dots. The BBA has an increased bump density with a .020 by .020 in. (.0508 by .0508 cm) center to center spacing. Rows of rectangles alternate between arrays of dots.
(C) Screen Preparation - Design of the separator configuration is performed on a CAD (Computer Aided Drafting) system. The CAD electronic data is converted to a Gerber plot file. This plot data is used by the screen manufacture to create the artwork to produce the desired thickness stencil for the screen printer. The screen is sent ready to use by SMT (Screen Manufacturing Technologies of Santa Clara, California).
(D) Electrode Vacuum Plate (Workholder) -- A porous ceramic plate (Ceramicon Designs, Golden, Colorado, P-6-C material) trimmed .050 smaller than the electrode perimeter is fitted and epoxied into an aluminum plate designed to fit the screen printer. The top and bottom surfaces are ground flush and parallel. Multiple pins are inserted around the centered electrode edge creating a corner stop for placement of the electrode substrate.
(E) Epoxy -- A two component epoxy Master Bond EP21 AR is modified to the desired viscosity (thixotropic, 300,000 to 400,000 cps) by the addition of a silica filler.
The filled epoxy having the desired viscosity is available by purchase order from Master Bond, Inc. of Hackensack, New Jersey. The epoxy is prepared as per instructions. The useful lifetime as a flowable fluid is about 30 min.
(F) Screen Printing Parameters Thick Film Screen Printer
Squeegee Durometer 45 to 100 Type A
Squeegee Speed 1 -2 in/s
Squeegee Pressure 10 to 1 5 lbs.
Squeegee Down Stop .01 0 to max. in.
Snap Off .010 to .030 in. (.0254 to .0762 cm.) FORMATION OF MICROPROTRUSIONS BY PHOTOLITHOGRAPHY
EXAMPLE 1 2 Hot Roller Photolithographic Production of Microprotrusions (A) The ConforMASK® 2000 high conformance solder mask of 1 .5 mil (0.0038 cm) in thickness is cut to the same size as the electrode. (B) The photo resist film 381 is applied by placing the ConforMASK® film on the electrode material surface 1 1 1 A, after removing a release sheet 382 between the phoio resist film 381 and the electrode 1 1 1 A, and passing the laminate through heated rollers (384 and 385), at 1 50°F, to adhere the photoresist film 381 to the electrode surface 1 1 1 A. A polyester cover sheet 382A on the outside of the photo resist film 381 is then removed.
(C) A dark field mask 387 containing rows of transparent holes (openings 388) is placed on the photo resist 381 . A typical pattern consists of an array of holes 6 mil (0.021 2 cm) in diameter 40 mil (0.1 cm) center-to-center spacing with a higher density (20 mil (0.0508 cm) center-to-center) for three rows on the perimeter of the electrode.
(D) The film 381 is exposed through the holes 388 and the mask 387, for about 20 seconds, to a conventional UV light source, i.e. mercury vapor lamps 389. The mask is then removed.
(E) The unexposed area of the photo resist is developed or stripped by placing it in a tank with 1 % potassium carbonate for 1 .5 min.
(F) The electrode surface with the microprotrusions (standoffs) are then washed with de-ionized water, placed in a tank with 10% sulfuric acid, for 1 .5 min and a final de-ionized water rinse.
(G) First, the microprotrusions 1 3 are exposed to UV light. A final cure of the microprotrusions (standoffs) is done in a convection air oven at 300 °F for 1 hr.
The finished electrode 1 1 1 A is used directly, or is treated, as described above.
EXAMPLE 1 3 Vacuum Lamination of Photo resist (A) The ConforMASK® 2000 high conformance solder mask of 2.3 mil (0.0058 cm) in thickness is cut slightly larger than the electrode. (B) The photo resist film is 381 vacuum laminated to the electrode 1 1 1 A, and onto a supporting backing plate using standard operating conditions (1 60°C, 0.3 mbars) using a Dynachem vacuum applicator model 724 or 730. The polyester cover sheet 382A is removed.
(C) The dark field mask 387 containing rows of transparent holes 388 is placed on the photo resist film 381 . A typical pattern includes an array of holes 6 mil
(0.001 5 cm) in diameter 40 mil (0.102 cm) center-to-center spacing with a higher density (20 mil (0.0054 cm) center-to-center) for three rows on the perimeter of the electrode.
(D) The film is exposed for 20 to 40 seconds to a non-collimated UV light source of 3-7 KW power.
(E) The unexposed area of the photo resist film is developed or stripped by using 0.5% potassium carbonate in a conveyorized spray developing unit, followed by a de-ionized water rinsing and turbine drying.
(F) A final cure of the microprotrusion standoffs is done in a two step process. First, the microprotrusions are exposed to UV light in a Dynachem UVCS 933 unit and then placed in a forced air oven at 300-310°F for 75 min.
The finished electrode is used directly or further treated as described above.
EXAMPLE 14 Surfactants for Porosity Control
32g of cetyltrimethyl ammonium bromide was added to 1 £ of iso-propanol with stirring and slight heat. After approximately one hour 73 g of TaCI5 and
47 g of RuCI3-H20 was added to the clear solution. The standard coating procedure was performed with interim pyrolysis at 300°C or 5 min. and a final pyrolysis at 300°C for 3 hours. The average pore diameter of the coating increased to around 45 A. After
post-treatment in steam at 260°C at 680 psi for 2 hr. the average pore diameter increased to 1 20 A.
A 25 wt % cetyltrimethyl ammonium chloride in water solution may also be used to modify the pore diameter of the resulting coating.
EXAMPLE 1 5 Thermal Elastomeric Gasket An alternative construction methodology is to sandwich a thermal elastomer gasket (e.g. KRATON®) between the two HDPE gaskets. Device characteristics are similar to those previously described.
EXAMPLE 16 Inclusion of Second Material to Accommodate Electrolyte Volume Increases A porous hydrophobic material is added to each cell to accommodate any volume increase of the electrolyte due to an increase in temperature. This material is placed in the cell as either a gasket material inside the perimeter
HDPE gasket, or as a disk replacing part of the separator material.
A common material used is a PTFE material from W.L. Gore & Associates, Inc. 1 -3 mil thick. Preferably, the PTFE material has water entry pressures from 20 to 100 psi. EXAMPLE 17
Alternate Electrode Pretreatment
After the electrodes have microprotrusions, gaskets, and pull cards (after step
E), the electrodes are placed in 1 M sulfuric acid and the open circuit potential is adjusted to about 0.5V (vs HHE) using cathodic current with no hydrogen evolution. The electrodes are transferred submerged in deionized water to an inert atmosphere
(e.g. Ar) where they are dried and assembled.
While only a few embodiments of the invention have been shown and described herein, it will become apparent to those skilled in the art that various modifications and changes can be made in the improved method to produce an electrical storage device such as a battery or a capacitor having improved lifetime and charge/recharge characteristics and low leakage current, and the device thereof without departing from
the spirit and scope of the present invention. All such modifications and changes coming within the scope of the appended claims are intended to be carried out thereby.