WO1998052730A1 - Method of recycling polyester foam - Google Patents
Method of recycling polyester foam Download PDFInfo
- Publication number
- WO1998052730A1 WO1998052730A1 PCT/US1998/010213 US9810213W WO9852730A1 WO 1998052730 A1 WO1998052730 A1 WO 1998052730A1 US 9810213 W US9810213 W US 9810213W WO 9852730 A1 WO9852730 A1 WO 9852730A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- foam
- polyester foam
- pellets
- drying
- polyester
- Prior art date
Abstract
Description
Claims