WO1998056662A1 - Uniaxially shrinkable biaxially oriented polypropylene film and method for use as tobacco pack overwrap - Google Patents
Uniaxially shrinkable biaxially oriented polypropylene film and method for use as tobacco pack overwrap Download PDFInfo
- Publication number
- WO1998056662A1 WO1998056662A1 PCT/US1998/010348 US9810348W WO9856662A1 WO 1998056662 A1 WO1998056662 A1 WO 1998056662A1 US 9810348 W US9810348 W US 9810348W WO 9856662 A1 WO9856662 A1 WO 9856662A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- polypropylene
- film
- propylene
- multilayer film
- ethylene
- Prior art date
Abstract
Description
Claims