WO1999005345A1 - High temperature-stable fluorochemicals as hydrophobic and oleophobic additives to synthetic organic polymers - Google Patents
High temperature-stable fluorochemicals as hydrophobic and oleophobic additives to synthetic organic polymers Download PDFInfo
- Publication number
- WO1999005345A1 WO1999005345A1 PCT/US1997/022227 US9722227W WO9905345A1 WO 1999005345 A1 WO1999005345 A1 WO 1999005345A1 US 9722227 W US9722227 W US 9722227W WO 9905345 A1 WO9905345 A1 WO 9905345A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- fluorochemical
- acid
- fluorochemicals
- fiber
- residue
- Prior art date
Abstract
Description
Claims