WO1999015534A1 - Modified alumoxane catalyst activator - Google Patents
Modified alumoxane catalyst activator Download PDFInfo
- Publication number
- WO1999015534A1 WO1999015534A1 PCT/US1998/019314 US9819314W WO9915534A1 WO 1999015534 A1 WO1999015534 A1 WO 1999015534A1 US 9819314 W US9819314 W US 9819314W WO 9915534 A1 WO9915534 A1 WO 9915534A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- polymerization
- group
- moiety
- catalyst
- occurrence
- Prior art date
Abstract
Description
Claims