Numéro de publicationWO2000001745 A1
Type de publicationDemande
Numéro de demandePCT/US1999/014967
Date de publication13 janv. 2000
Date de dépôt1 juil. 1999
Date de priorité2 juil. 1998
Autre référence de publicationEP1091984A1
Numéro de publicationPCT/1999/14967, PCT/US/1999/014967, PCT/US/1999/14967, PCT/US/99/014967, PCT/US/99/14967, PCT/US1999/014967, PCT/US1999/14967, PCT/US1999014967, PCT/US199914967, PCT/US99/014967, PCT/US99/14967, PCT/US99014967, PCT/US9914967, WO 0001745 A1, WO 0001745A1, WO 2000/001745 A1, WO 2000001745 A1, WO 2000001745A1, WO-A1-0001745, WO-A1-2000001745, WO0001745 A1, WO0001745A1, WO2000/001745A1, WO2000001745 A1, WO2000001745A1
InventeursAvinash C. Gadkari, Charles C. Cozewith
DéposantExxon Chemical Patents Inc.
Exporter la citationBiBTeX, EndNote, RefMan
Liens externes:  Patentscope, Espacenet
Propylene olefin copolymers
WO 2000001745 A1
Résumé
This invention relates to propylene-olefin (PO) copolymers having unique properties described herein as a relationship of mole % olefin to: 1) isotactic index, 2) % meso propylene triad, and 3) glass transition temperature. Specifically, the isotactic index of this invention's copolymers is equal to -0.0224O+A wherein O is the mole % olefin present, A is a number from 66 to 89, and the isotactic index is greater than 0. The propylene tacticity of this invention's polymers is also described by % meso triad equal to -0.4492O+B wherein O is the mole % olefin present, B is a number from 93 to 100, and the % meso triad is less than 95 %. Additionally, the copolymers of this invention have a glass transition temperature equal to -1.1082O-C wherein O is the mole % olefin present and C is a number from 1 to 14.
Revendications  (Le texte OCR peut contenir des erreurs.)
CLAIMS:
1. A propylene/olefin copolymer wherein said copolymer has :
(a) an isotactic index equal to -0.0224O + A wherein O is the mole % olefin present, A is a number from 66 to 89, and the isotactic index is greater than
0;
(b) a % meso triad of equal to -0.4492O + B wherein O is the mole % olefin present, B is a number from 93 to 100, and the % meso triad is less than 95%.
The copolymer of claim 1 wherein said olefin is ethylene.
3. The copolymer of claim 1 or 2 having a glass transition temperature equal to -1.1082Et-C wherein Et is the mole % ethylene present and C is a number from 1 to 14.
4. The copolymer of any of the above claims with an ethylene content from 10 to 35 mole %.
5. The copolymer of any of the above claims with number average Mw from
15,000 to 2,000,000 and an MW/MN ratio from 1.5 to 10.
6. The copolymer of any of the above claims having a Tm of from 25-125┬░ C.
7. The copolymer of any of the above claims having a reactivity ratio product
(rlxr2) equal to or less than 2.5.
8. An article of manufacture comprising the copolymer of any of the above claims, optionally blended with one or more of other alpha olefin polymers and copolymers, processing oil, an other additives.
. The article of claim 8 wherein said copolymer is blended with polypropylene.
10. The article of claim 8 or 9 wherein said copolymer blend is oriented.
11. A process for making the copolymer of claim 1 comprising polymerizing propylene and a C2, C4-C20 alpha olefin with a metallocene and an activating cocatalyst.
Description  (Le texte OCR peut contenir des erreurs.)

PROPYLENE OLEFIN COPOLYMERS

FIELD OF THE INVENTION

This invention relates to propylene/olefin copolymers (PO) having unique properties described herein as a relationship of mole % olefin to: 1) isotactic index, 2) % meso propylene triad, and 3) glass transition temperature. The olefins include C2, C4-C20 alpha-olefins, the most preferred olefin being ethylene (C2). Specifically, the isotactic index of this invention's copolymers is equal to -0.0224O + A wherein O is the mole % olefin present, A is a number from 66 to 89 and the isotactic index is greater than 0. The propylene tacticity of this invention's polymers is also described by % meso triad equal to -0.4492EO + B wherein O is the mole % olefin present, B is a number from 93 to 100, and the % meso triad is less than 95%, preferably less than 93%, even more preferably less than 90%. Additionally, the copolymers of this invention have a glass transition temperature equal to -1.1082O -

C wherein O is the mole % olefin present and C is a number from 1 to 14. The PO copolymers of this invention are distinguished over prior art PO copolymers by their unique crystalline characteristics coupled with elastomeric properties which make them useful in a variety of applications such as: thermoplastic elastomers (TPEs), impact modifiers and compatibilizers in thermoplastic olefins (TPOs), in elastic fibers and films, in dynamically vulcanized alloys (DVAs), as curable elastomers, in adhesives, in polyvinyl chloride (PVC) replacements, and in viscosity modifiers. Due to their unique propylene crystallinity, these PO copolymers yield highly compatible blends with crystalline polypropylene (PP). These blends have superior properties relative to those of blends containing crystalline PP and conventional amorphous ethylene-propylene (EP) copolymers. Furthermore, PO copolymers of this invention and their blends with polypropylene (PP) upon orientation give significantly enhanced elastic recovery and tensile strength.

According to another embodiment of the present invention, the PO copolymers of this invention may contain small quantities of a non-conjugated diene to aid in the vulcanization and other chemical modification. For purposes of this invention, the term "copolymer" is intended to include both polymers formed from ethylene and one or more alpha-olefins and polymers formed from ethylene, one or more alpha-olefins, and one or more non-conjugated dienes. The preferred non-conjugated diene is selected from the group consisting of those monomers useful for vulcanization of ethylene-propylene rubbers, such as, but not limited to,

5-ethylidene— 2--norbornene, l,4~hexadiene, 1,6 octadiene, 5— methyl— 1,4 hexadiene, 3,7— dimethyl— 1,6—octadiene, vinylnorbomene, dicyclopentadiene or combinations thereof. The amount of diene is preferably less than 10 wt % and most preferably less than 5 wt %. The polymers of this invention may be prepared by polymerizing a C2, C4-

C20 alpha olefin preferably ethylene and propylene in the presence of a chiral metallocene catalyst with an activator and optional scavenger.

BACKGROUND OF THE INVENTION

Metallocenes have been used to make ethylene propylene (EP) copolymers. For example, European Patent Application 128 046 discloses making an EP copolymer with at least two non-chiral metallocenes. However, achiral metallocenes are inherently incapable of making copolymers having an isotactic index greater than 0 and having the other unique crystalline characteristics coupled with elastomeric properties of EP copolymers of this invention.

EP 0 374 695 discloses the preparation of EP copolymers having an isotactic index greater than 0 using a chiral metallocene catalyst with an alumoxane co- catalyst. However, the copolymers of the present invention have an isotactic index equal to -0.0224Et + A wherein Et is the mole % ethylene present, A is a number from 66 to 89, and the isotactic index is greater than 0. This relationship of mole % ethylene to isotactic index is absent in EP 0 374 695 as seen by figure 1. In general, isotactic index of EP copolymers of this invention is significantly lower than that of EP copolymers of EP 0 374 695. The low isotactic index of EP copolymers of this invention is the key to their excellent elastomeric properties. U.S. Patent No. 5,504,172 discloses the preparation of EP copolymers having a high % meso triad tacticity of propylene units, however, % meso triad tacticity of propylene units of the copolymers of the present invention is significantly low and equal to -0.4492Et + B wherein Et is the mole % ethylene present, B is a number from 93 to 100, and the % meso triad is less than 95%. This relationship of mole % ethylene to triad tacticity is seen in the polymers of U.S. Patent No. 5,504,172 as shown by figure 2. The low % meso triad tacticity of propylene units of the copolymers of the present invention is responsible for their excellent elastomeric properties.

BRIEF DESCRIPTION OF THE DRAWINGS

Figure 1 is a graph depicting mole % ethylene on the x-axis and isotactic index on the y-axis. Figure 2 is a graph depicting mole % ethylene on the x-axis and % meso propylene triad on the y-axis.

Figure 3 is a graph depicting mole % ethylene on the x-axis and glass transition temperature on the y-axis.

DETAILED DESCRIPTION OF THE INVENTION

The catalyst system described below useful for making the PO copolymers of this invention is a metallocene with a non-coordinating anion (NCA) activator, and optionally a scavenging compound. Polymerization is conducted in a solution, slurry or gas phase, preferably in solution phase. The polymerization can be performed in a single- or multiple-reactor process. A slurry or solution polymerization process can utilize sub- or superatmospheric pressures and temperatures in the range of from -25 °C to 110 °C. In a slurry polymerization, a suspension of solid, paniculate polymer is formed in a liquid polymerization medium to which ethylene, alpha-olefin comonomer, hydrogen and catalyst are added. In solution polymerization, the liquid medium serves as a solvent for the polymer. The liquid employed as the polymerization medium can be an alkane or a cycloalkane, such as butane, pentane, hexane, or cylclohexane, or an aromatic hydrocarbon, such as toluene, ethylbenzene or xylene. For slurry polymerization, liquid monomer can also be used. The medium employed should be liquid under the conditions of the polymerization and relatively inert. Preferably, hexane or toluene is employed for solution polymerization. Gas phase polymerization processes are described in U.S. Patent Nos. 4,543,399, 4,588,790, 5,028,670, all of which are herein incorporated by reference for purposes for U.S. Patent Practice. The catalyst may be supported on any suitable particulate material or porous carrier such as polymeric supports or inorganic oxide for example silica, alumina or both.

Methods of supporting metallocene catalysts are described in U.S. Patent Nos. 4,808,561, 4,897,455, 4,937,301, 4,937,217, 4,912,075, 5,008,228, 5,086,025, 5,147,949, and 5,238,892, all of which are incorporated by reference for purposes of U.S. Patent Practice. Propylene and ethylene are the preferred monomers to make the PO copolymers of the invention but ethylene may be replaced with another alpha olefin from C4 to C20.

Metallocene The term "metallocene" and "metallocene catalyst precursor" are terms known in the art to mean compounds possessing a Group IV, V, or VI transition metal M, with a cyclopentadienyl (Cp) ligand or ligands which may be may be substituted, at least one non-cyclopentadienyl-derived ligand X, and zero or one heteroatom-containing ligand Y, the ligands being coordinated to M and corresponding in number to the valence thereof. The metallocene catalyst precursors are generally require activation with a suitable co-catalyst (referred to as activator) in order to yield an active metallocene catalyst which refers generally to an organometallic complex with a vacant coordination site that can coordinate, insert, and polymerize olefins. Preferable metallocenes are cyclopentadienyl (Cp) complexes which have two Cp ring systems for ligands. The Cp ligands preferably form a bent sandwich complex with the metal and are preferably locked into a rigid configuration through a bridging group. These cyclopentadienyl complexes have the general formula:

(Cp1R1JR3 a(Cp2 2 p)MXq

Wherein Cp1 of ligand (Cp'R' and Cp2 of ligand (Cp2R2 p) are preferably the same, R1 and R2 each is, independently, a halogen or a hydrocarbyl, halocarbyl, hydrocarbyl-substituted organometalloid or halocarbyl-substituted organometalloid group containing up to 20 carbon atoms, m is preferably 1 to 5, p is preferably 1 to 5, and preferably two R1 and/or R2 substituents on adjacent carbon atoms of the cyclopentadienyl ring associated there with can be joined together to form a ring containing from 4 to 20 carbon atoms, R3 is a bridging group, n is the number of atoms in the direct chain between the two ligands and is preferably 1 to 8, most preferably 1 to 3, M is a transition metal having a valence of from 3 to 6, preferably from group 4, 5, or 6 of the periodic table of the elements and is preferably in its highest oxidation state, each X is a non-cyclopentadienyl ligand and is, independently, a hydrocarbyl, oxyhydrocarbyl, halocarbyl, hydrocarbyl-substituted organometalloid, oxyhydrocarbyl-substituted organometalloid or halocarbyl- substituted organometalloid group containing up to 20 carbon atoms, q is equal to the valence of M minus 2.

Numerous examples of the biscyclopentadienyl metallocenes described above for the invention are disclosed in U.S. Patents 5,324,800; 5,198,401 ; 5,278,119; 5,387,568; 5, 120,867; 5,017,714; 4,871,705; 4,542,199; 4,752,597; 5, 132,262; 5,391,629; 5,243,001; 5,278,264; 5,296,434; and 5,304,614, all of which are incorporated by reference for purposes of U.S. Patent Practice.

Illustrative, but not limiting examples of preferred biscyclopentadienyl metallocenes of the type described in group 1 above for the invention are the racemic isomers of:

μ-(CH3)2Si(indenyl)2M(Cl)2 μ-(CH3)2Si(indenyl)2M(CH3)2 μ-(CH3)2Si(tetrahydroindenyl)2M(Cl)2 μ-(CH3)2Si(tetrahydroindenyl)2M(CH3)2 μ-(CH3)2Si(indenyl)2M(CH2CH3)2 μ-(C6H5)2C(indenyl)2M(CH3)2; Wherein m is chosen from a group consisting of Zr, Hf, or Ti.

Non-coordinating anions

As already mentioned the metallocene or precursor are activated with a non- coordinating anion. The term "non-coordinating anion" means an anion which either does not coordinate to said transition metal cation or which is only weakly coordinated to said cation thereby remaining sufficiently labile to be displaced by a neutral Lewis base. "Compatible" non-coordinating anions are those which are not degraded to neutrality when the initially formed complex decomposes. Further, the anion will not transfer an anionic substituent or fragment to the cation so as to cause it to form a neutral four coordinate metallocene compound and a neutral by-product from the anion. Non-coordinating anions useful in accordance with this invention are those which are compatible, stabilize the metallocene cation in the sense of balancing its ionic charge, yet retain sufficient lability to permit displacement by an ethylenically or acetylenically unsaturated monomer during polymerization. Additionally, the anions useful in this invention are preferably large or bulky in the sense of sufficient molecular size to largely inhibit or prevent neutralization of the metallocene cation by Lewis bases other than the polymerizable monomers that may be present in the polymerization process. Typically the anion will have a molecular size of greater than or equal to 4 angstroms.

Descriptions of ionic catalysts for coordination polymerization comprised of metallocene cations activated by non-coordinating anions appear in the early work in EP-A-0 277 003, EP-A-0 277 004, U.S. Patents 5,198,401 and 5,278,119, and WO 92/00333. These teach a preferred method of preparation wherein metallocenes (bisCp and monoCp) are protonated by an anionic precursors such that an alkyl/hydride group is abstracted from a transition metal to make it both cationic and charge-balanced by the non-coordinating anion. The use of ionizing ionic compounds not containing an active proton but capable of producing both the active metallocene cation and a non-coordinating anion is also known. See, EP-A-0 426 637, EP-A- 0 573 403 and U.S. Patent 5,387,568. Reactive cations other than Bronsted acids capable of ionizing the metallocene compounds include ferrocenium, triphenylcarbonium, and triethylsilylium cations. Any metal or metalloid capable of forming a coordination complex which is resistant to degradation by water (or other Bronsted or Lewis acids) may be used or contained in the anion of the second activator compound. Suitable metals include, but are not limited to, aluminum, gold, platinum and the like. Suitable metalloids include, but are not limited to, boron, phosphorus, silicon and the like. The description of non-coordinating anions and precursors thereto of these documents are incorporated by reference for purposes of U.S. Patent Practice.

An additional method of making the ionic catalysts uses ionizing anionic pre-cursors which are initially neutral Lewis acids but form the cation and anion upon ionizing reaction with the metallocene compounds, for example tris(pentafluorophenyl) boron acts to abstract an alkyl, hydride or silyl ligand to yield a metallocene cation and stabilizing non-coordinating anion, see EP-A-0 427 697 and EP-A-0 520 732. Ionic catalysts for addition polymerization can also be prepared by oxidation of the metal centers of transition metal compounds by anionic precursors containing metallic oxidizing groups along with the anion groups, see EP-A-0 495 375. The description of non-coordinating anions and precursors thereto of these documents are similarly incorporated by reference for purposes of U.S. Patent Practice.

Illustrative, but not limiting, examples of suitable activators capable of ionic cationization of the metallocene compounds of the invention, and consequent stabilization with a resulting non-coordinating anion include: trialkyl-substituted ammonium salts such as; triethylammonium tetraphenylborate, tripropylammonium tetraphenylborate, tri(n-butyl)ammonium tetraphenylborate, trimethylammonium tetrakis(p-tolyl)borate, trimethylammonium tetrakis(o-tolyl)borate, tributyl ammonium tetrakis(pentafluorophenyl)borate, tripropylammonium tetrakis(o,p-dimethylphenyl)borate, tributylammonium tetrakis(m,m-dimethylphenyl)borate, tributylammonium tetrakis(p-trifluoromethylphenyl)borate, tributylammonium tetrakis(pentafluorophenyl)borate, tri(n-butyl)ammonium tetrakis(o-tolyl)borate and the like;

N,N-dialkyl anilinium salts such as;

N,N-dimethylanilinium tetrakis(pentafluorophenyl)borate, N,N-dimethylaniliniumtetrakis(heptafluoronaphthyl)borate, N,N-dimethylanilinium tetrakis(perfluoro-4-biphenyl)borate,

N,N-dimethylanilinium tetraphenylborate, N,N-diethylanilinium tetraphenylborate, N,N-2,4,6-pentamethylanilinium tetraphenylborate and the like; dialkyl ammonium salts such as; di-(isopropyl)ammonium tetrakis(pentafluorophenyl)borate, dicyclohexylammonium tetraphenylborate and the like;

and triaryl phosphonium salts such as; triphenylphosphonium tetraphenylborate, tri(methylphenyl)phosphonium tetraphenylborate, tri(dimethylphenyl)phosphonium tetraphenylborate and the like.

Further examples of suitable anionic precursors include those comprising a stable carbonium ion, and a compatible non-coordinating anion. These include; tropyllium tetrakis(pentafluorophenyl)borate, triphenylmethylium tetrakis(pentafluorophenyl)borate, benzene (diazonium) tetrakis(pentafluorophenyl)borate, tropillium phenyltris(pentafluorophenyl)borate, triphenylmethylium phenyl-(trispentafluorophenyl)borate, benzene (diazonium) phenyl-tris(pentafluorophenyl)borate, tropillium tetrakis(2,3,5,6-tetrafluorophenyl)borate, triphenylmethylium tetrakis(2,3, 5, 6-tetrafluorophenyl)borate, benzene (diazonium) tetrakis(3,4,5-trifluorophenyl)borate, tropillium tetrakis(3,4,5-trifluorophenyl)borate, benzene (diazonium) tetrakis(3,4,5-trifluorophenyl)borate, tropillium tetrakis(3,4,5-trifluorophenyl)aluminate, triphenylmethylium tetrakis(3,4,5-trifluorophenyl)aluminate, benzene (diazonium) tetrakis(3,4,5-trifluorophenyl)aluminate, tropillinum tetrakis(l,2,2-trifluoroethenyl)borate, triphenylmethylium tetrakis(l ,2,2-trifluoroethenyl)borate, benzene (diazonium) tetrakis(l,2,2-trifluoroethenyl)borate, tropillium tetrakis(2,3,4,5-tetrafluorophenyl)borate, triphenylmethylium tetrakis(2,3,4,5-tetrafluorophenyl)borate, benzene (diazonium) tetrakis(2,3,4,5-tetrafTuorophenyl)borate, and the like.

A particularly preferred catalyst system if μ-(CH3)2Si(indenyl)2Hf(CH3)2 with a cocatalyst of N,N-dimethylanilinium tetrakis(pentafluorophenyl)borate.

Ethylene Propylene Copolymers EP copolymers of this invention have unique properties as evidenced by the relationship of their isotactic index and propylene triad tacticity to their ethylene content. Isotactic index and triad tacticity were determined for this invention's EP copolymers in the manner described below.

Copolymers of this invention can be blended with processing oil and other common additives such as nucleating agents, antioxidants, fillers, etc. and fabricated into objects used in a variety of applications mentioned above. Also, blends comprising the copolymers of this invention and other alpha- olefin polymers and copolymers, e.g., polypropylene, are fabricated into objects used in a variety of applications mentioned above. Generally, these blends contain processing oil and other common additives such as nucleating agents, antioxidants, fillers, etc.

Polydispersity Index

Copolymers of the invention preferably have a polydispersity index (Mw/Mn) of from 1.5 to 10, more preferably from 1.8 to 8, even more preferably from 2.0 to 5.

Isotactic Index

Polypropylene isotactic index is determined by infra-red (LR) spectroscopy.

The IR spectra of polypropylene yields two observable peaks at 997 cm"1 and 973 cm"1. The quotient of absorbance at 997 cm"1 divided by the absorbance at 973 cm"1 is a recognized measure of isotacticity. Polypropylene isotactic index is defined as this quotient multiplied by 100.

The EP copolymers made by this invention have unique crystalline characteristic as measured by isotactic index. Figure 1 is a graph depicting the relationship of isotactic index of a given copolymer to its mole % ethylene content.

The data from this invention's copolymers and EPA 037659 are plotted on the graph. As shown by Figure 1, the copolymers of this invention have a lower isotactic index for any given ethylene content when compared to EPA 037659. The lower isotactic index corresponds to relatively lower crystallinity that translates into better elastomeric properties such as high tensile strength and elongation at break coupled with very good elastic recovery. Good elastomeric properties are important for some of the potential applications mentioned above.

Triad Tacticity The term "tacticity" refers to the stereogenicity in a polymer. For example, the chirality of adjacent monomers can be of either like or opposite configuration. The term "diad" is used to designate two contiguous monomers; three adjacent monomers are called a triad. If the chirality of adjacent monomers is of the same relative configuration, the diad is called isotactic; if opposite in configuration, it is termed syndiotactic. Another way to describe the configurational relationship is to term contiguous pairs of monomers having the same chirality as meso (m) and those of opposite configuration racemic (r).

When three adjacent monomers posses are of the same configuration, the stereoregularity of the triad is 'mm'. If two adjacent monomers in a three-monomer sequence have the same chirality and that is different from the relative configuration of the third unit, this triad has 'mr' tacticity. An 'rr' triad has the middle monomer unit having an opposite configuration from either neighbor. The fraction of each type of triad in the polymer can be determined and when multiplied by 100 indicates the percentage of that type found in the polymer.

The triad tacticity can be determined from a C-NMR spectrum of the propylene copolymer. The C-NMR spectrum is measured in the following manner. To measure the C-NMR spectrum, 250-350 mg of polymer is completely dissolved in deuterated tetrachloroethane in a NMR sample tube (diameter: 10 mm) at 120° C. The measurement is conducted with full proton decoupling using a 90° pulse angle and at least a 15 second delay between pulses With respect to measuring the chemical shifts of the resonances, the methyl group of the third unit in a sequence of 5 contiguous propylene units consisting of head-to-tail bonds and having the same relative chirality is set to 21.83 ppm. The chemical shift of other carbon resonances are determined by using the above- mentioned value as a reference. The spectrum relating to the methyl carbon region (17.0-23 ppm) can be classified into the first region (21.1-21.9 ppm), the second region (20.4-21.0 ppm), the third region (19.5-20.4 ppm) and the fourth region (17.0-17.5 ppm). Each peak in the spectrum was assigned based on the work described in Polymer, Vol. 30 (1989) p. 1350, or Macromolecules, Vol. 17 (1984) p. 1950. In the first region, the signal of the center methyl group in a PPP (mm) triad is located.

In the second region, the signal of the center methyl group in a PPP (mr) triad and the methyl group of a propylene unit whose adjacent units are a propylene unit and an ethylene unit resonates (PPE-methyl group).

In the third region, the signal of the center methyl group in a PPP (rr) triad and the methyl group of a propylene unit whose adjacent units are ethylene units resonate (EPE-methyl group).

PPP (mm), PPP (mr) and PPP (rr) have the following three-propylene units- chain structure with head-to-tail bonds, respectively.

CH3 CH3

PPP (mr): _ (C I H— CH2 )— (C I H— CH2 )— (CH— CH2 )—

I

CH3

The triad tacticity (mm fraction) of the propylene copolymer can be determined from a 13C-NMR spectrum of the propylene copolymer and the following formula:

PPP (mm) mm Fraction =

PPP (mm) + PPP(mr) + PPP(rr) The peak areas used in the above calculation are not measured directly from the triad regions in the CNMR spectrum. The intensities of the mr and rr triad regions need to have subtracted from them the areas due to EPP and EPE sequencing, respectively. The EPP area can be determined from the signal at 30.8 ppm after subtracting from it one half the area of the sum of the signals between 26 and 27.2 ppm and the signal at 30.1 ppm. The area due to EPE can be determined from the signal at 33.2 ppm.

In addition to the above adjustments to the mr and rr regions for the presence of EPP and EPE other adjustments need to be made to these regions prior to using the above formula. These adjustments are needed to account for signals present due to non-head-to-tail propylene additions. The area of the mr region may be adjusted by subtracting one half of the area between 34 and 36 ppm and the area of the rr region may be adjusted by subtracting the intensity found between 33.7 and 40.0 ppm. Therefore, by making the above adjustments to the mr and rr regions the signal intensities of the mm, mr and rr triads can be determined and the above formula applied.

The EP copolymers made by this invention have unique propylene tacticity as measured by % meso triad. Figure 2 is a graph depicting the relationship of % meso triad of a given copolymer to its mole % ethylene content. The data from this invention's copolymers and U.S. Pat. No. 5,504,172 are plotted on the graph. As shown by figure 2, the copolymers of this invention have a lower % meso triad for any given ethylene content when compared to U.S. Pat. No. 5,504,172. The lower content of % meso triads corresponds to relatively lower crystallinity that translates into better elastomeric properties such as high tensile strength and elongation at break coupled with very good elastic recovery. Good elastomeric properties are important for some of the potential applications mentioned on page 1.

Copolymer Properties Various techniques were used to characterize the copolymers of this invention some of which are described in "Structure Characterization" The Science and Technology of Elastomers, F. Eirich, editor, Academic Press 1978, Chapter 3 by G. Ver Strate which is incorporated by reference for purposes of U.S. Patent Practice.

Glass transition temperature (Tg) of polymer is usually measured by differential scanning calorimetry (DSC). The Tg of EP copolymers reported in this application is determined by either modulated DSC (MDSC) technique or conventional DSC technique.

The copolymer of the invention preferably has a reactivity ratio product (rlxr2) equal to or less than 2.5.

Conventional DSC Technique: DSC has a standard protocol of loading a calorimeter at 20 °C with a specimen free of molding strains, cooling the sample to - 75 °C, scanning to 180 °C at 10 °C/min., cooling to -75 °C, and re-running the scan. The Tg and melting point (TM) are evaluated.

Modulated DSC Technique: Thermal analyzer instruments' model 2910 is used. 5- 10 mg of polymer sample is loaded in the instrument at ambient temperature. The general analysis procedure calls for subjecting the sample to the following thermal segments in the order given below:

1. From room temperature, ramp 10 °c/minute to -60 °c.

2. Isothermal for 1.0 minute.

3. Simultaneously modulate +/- 1.0 °C every 60 seconds and ramp 5 °C/minute to l50 °C.

4. Isothermal for 1.0 minute.

5. Ramp 5 °C/minute to - 10 °C .

6. Isothermal for 1.0 minute.

7. Ramp 10 °C/minute to 150 °C. 8. Ramp 10 °C/minute to 25 °C. Data is acquired and analyzed using Thermal Analyzer Instruments' Model

2200 computer and the Tg, Melting Point (Tm) and Crystallization Point (Tc) are evaluated. High-Temperature GPC (HT-GPC)

SCOPE

Gel permeation chromatography (GPC) is a liquid chromatographic technique which separates macromolecules according to their hydrodynamic size. It is employed here to obtain the molecular weight distribution of polyolefin samples (e.g., PE and PP). A dilute solution of the polyolefin in a good solvent (1,2,4- trichlorobenzene, TCB) is carried through a series of separation columns filled with porous packing material (rigid particles of cross-linked styrene/divinyl benzene gel) using a mobile phase (also TCB) at constant flow rate. Separation occurs by repeated exchange of the polymer molecules between the bulk solvent and the pores of the packing material. The distribution of pore sizes thus determines the size range over which separation occurs, as well as the extent of separation, with large molecules eluting before smaller ones. After separation, a Differential Refractive Index (DRI) detector is used to measure polymer concentration as a function of elution time (or elution volume). A pre-established calibration curve, based on polystyrene standards, allows this raw data to be converted into concentration vs molecular weight data. The number, weight, and z-average molecular weights (Mn, Mw, and Mj,, respectively) are then calculated from these results.

CALIBRATION A set of columns are calibrated by running a series of narrow molecular weight polystyrene standards (Tosoh Corp., Japan) and recording their peak retention (elution) times. A total of 16 PS standards are used, covering a molecular weight range of MPS = 500-5,000,000. PE and PP molecular weight vs retention time data are calculated from these results by assigning PE- or PP-equivalent molecular weights for each PS standard. Final calibration curves for PE and PP then consist of 3rd-order polynomial fits of these data sets.

For PP, the "universal calibration" approach is adopted, in which MPS[η]PS = Mpp[η]pP is assumed to hold. The following Mark-Houwink coefficients are employed in the relation [η] = kMα:

RUN CONDITIONS INSTRUMENT: Waters 150-C GPC

COLUMNS: 3 Shodex AT-806MS (mixed bed) MOBILE PHASE: filtered TCB, 300 ppm antioxidant (Santonox) TEMPERATURE: 145 °C (column and injector compartments) RUN TIME: 50 minutes INJECTION VOLUME: 300 μL

FLOW RATE: 1.0 mL/min DRI SENSITIVITY: 256 DRI SCALE FACTOR: 16

SAMPLE PREPARATION

4-6 mg of polymer is weighted into a 4 mL WISP vial, sufficient TCB is added to yield a concentration of 1.5 mg/mL, and the vial is capped with a PTFE septum and labeled with the work request number. Preferably, TCB from a single source is used for both sample preparation and the mobile phase to minimize instability in the DRI signal as the lowest molecular weight components elute (i.e.,

"solvent mis-match" peaks). The sample is placed in the shaker oven at 160-170 °C for 3-4 hours while continuously agitating at a rate of 120-160 rpm. After discarding samples that contain undissolved gel or solid particles, the vials are transferred to a pre-heated sample carousel, and the carousel quickly placed into the heated injector compartment of the GPC. The set of samples are run according to the directions for normal operation in the waters 150-C GPC manual.

DATA ACQUISITION AND ANALYSIS

Data is acquired and analyzed using Waters "Expert Ease" software. Samples are identified by the work request and customer notebook numbers. For a given chromatogram, a linear baseline is established based on the pre-peak trend, and the limits for peak integration are set by estimating the points of initial and final deviation of the signal from that baseline (and excluding "solvent mis-match" or "injection" peaks). The established calibration curve, appropriate for PE or PP, is used to convert the DRI signal vs retention time data to molecular weight distribution data. Mn, Mw, Mz, and recovered mass (relative to the control sample) are calculated by the software. A report is generated that includes these values, a plot of the raw retention time data, and a plot of the molecular weight distribution. A "time slice" report is also available.

The EP copolymers made by this invention have unique properties as measured by Tg. Figure 3 is a graph depicting the relationship of Tg of a given copolymer to its mole % ethylene content. The data from this invention's copolymers are plotted on the graph.

EXAMPLES 1-3

The polymers of Examples 1-3 were made with the following general procedure. Polymerizations were carried in a one liter stirred reactor with continuous flow of feeds to the system and continuous withdrawal of products. Solvent, including hexane, and monomers including ethylene and propylene were purified over beds of alumina and mole sieves. Toluene for preparing catalyst solutions was also purified by the same technique. All feeds were pumped into the reactors by metering pumps except for the ethylene which flowed as a gas under its own pressure through a mass flow meter/controller. Reactor temperature was controlled by circulating water through a reactor cooling jacket. The reactor was maintained at a pressure in excess of the vapor pressure of the reactant mixture to keep the reactants in the liquid phase. The reactor was operated liquid full.

Ethylene and propylene feeds were combined into one stream and then mixed with a pre-chilled hexane stream that had been cooled to at least 0 °C. A hexane solution of triisobutyl aluminum scavenger was added to the combined solvent and monomer stream just before it entered the reactor to further reduce the concentration of any catalyst poisons. A catalyst solution was prepared by dissolving μ-Me2Si(indenyl)2HfMe2 catalyst and (N,N dimethylaniliniumtretakis

(pentafluorophenyl) borate ([DMAH] B(pfp)4] ) activator in dry toluene. This mixture of the catalyst components in toluene was pumped separately to the reactor and entered through a separate port. The product from reactor exited through a pressure control valve that reduced the pressure to atmospheric. This caused the unconverted monomers in the solution to flash into a vapor phase which was vented from the top of a vapor liquid separator. The liquid phase, comprising mainly polymer and solvent, flowed out the bottom of the separator and was collected for polymer recovery. Polymer was recovered from solution by either steam stripping following by drying, or by solvent evaporation under heat and vacuum. Below, Table 1 shows polymerization conditions for Examples 1-3.

TABLE 1

EXAMPLES 4-6

The polymers of Examples 4-6 were made with the following general procedure. A 5 gallon autoclave stirred tank reactor, equipped with an external jacket for temperature control, was charged with 29 pounds of dry toluene (diluent). Hexane or other inert hydrocarbon solvent may be used in place of toluene. Next, 40 grams of 25% solution of triisobutyl aluminum scavenger was charged to the reactor. The contents of the reactor were stirred and maintained at a certain initial temperature shown in table 2. Generally, ethylene (C2) and propylene (C3) feed lines were tied together to obtain a premixed monomer feed that is fed into the reactor via a single dip tube. Alternatively, ethylene and propylene may be fed directly to the reactor through individual entry tubes. The flow rates of ethylene and propylene were adjusted to give desired C3 / C2 monomer ratio. A catalyst solution, containing 121 mg of μ-Me2Si(Indenyl)2HfMe2 and 151 mg of N,N- Dimethylanilinium tetrakis(pentafluorophenyl)boron in 100 ml of dry toluene, was charged in a catalyst bomb. This bomb was a part of a catalyst delivery setup capable of delivering 15 ml of catalyst solution per addition to the reactor. Initially, 30 - 45 ml of catalyst solution was added to the reactor to induce polymerization. Additional catalyst solution is added at desired time intervals during the polymerization. Reactor pressure, temperature and C3 & C2 flow rates were monitored throughout the polymerization run that typically lasts for 10 - 30 minutes.

After a certain time period, the reactor effluent was transferred, under nitrogen pressure, to a devolitizing unit. A continuous flow of steam was introduced in this unit for a long period of time to insure evaporation of diluent. Vacuum was usually applied to accelerate devolitization of diluent. Copolymer floated on top of water when most of the solvent was evaporated. It was isolated, dried and characterized.

Reaction conditions for Examples 4-6 are shown in Table 2 below. Table 2

EXAMPLE #7

600 ml of dry toluene (diluent) was introduced in a dry, deoxygenated 1L autoclave reactor equipped with stirrer and an external jacket for temperature control. Temperature of the reactor is lowered to 0° C. From a propylene feed vessel (volume 1.1L ), 120 psi (ΔP) of purified propylene gas was fed into the reactor. After equilibration of reactor pressure, 25 psi (ΔP) of purified ethylene gas was introduced into the reactor. This procedure gave a desirable C3 / C2 monomer ratio for the synthesis of EP copolymers containing a high amount of C3. The catalyst solution was prepared in a dry box and transferred into A catalyst feed tube. It contained 24 mg of μ-Me2Si(Indenyl)2HfMe2 and 15 mg of N,N- Dimethylanilinium tetrakis(pentafluorophenyl)boron in 5 ml of dry toluene. Polymerization was induced at 0° C by injecting the catalyst solution into the reactor. Reactor pressure and temperature was monitored throughout the polymerization. A temperature jump of 9° C was observed over a period of 6 minutes after the addition of the catalyst solution. After the initial jump, the reactor temperature leveled off and decreased with increasing polymerization time. Reactor pressure decreased gradually during the polymerization. The reactor was vented completely after 20 minutes of polymerization and the contents of the reactor were poured into a beaker containing large excess of acetone. The precipitated polymer was dried under vacuum at 100° C for 24 hours. The polymer yield was 19.3 gm. EXAMPLE #8

500 ml of dry toluene (diluent) was introduced in a dry, deoxygenated IL autoclave reactor equipped with stirrer and an external jacket for temperature control. Temperature of the reactor was lowered to -10° C. A catalyst solution containing 12 mg of μ-Me2Si(Indenyl)2HfMe2 and 10 mg of N,N-Dimethylanilinium tetrakis(pentafluorophenyl)boron in 5 ml of dry toluene was injected in the reactor. The reactor was maintained under a slight positive pressure of dry nitrogen. Polymerization was induced at -10° C by introducing a gaseous mixture of C3 and C2 into the reactor. The moler ratio of C3:C2 in this mixture was 3.5: 1. The flow of monomer mixture continued from the feed vessel to reactor until there is no pressure difference between the two. At this time the reactor inlet valve was shut off and polymerization was continued. Reactor pressure and temperature was monitored throughout the polymerization. A temperature jump was observed of 18° C (-10° C to 8° C) over a period of 5 minutes since the introduction of the monomer mixture in the reactor. After the initial jump, the reactor temperature leveled off and decreased with increasing polymerization time. Reactor pressure decreased gradually during the polymerization. The reactor was vented completely after 20 minutes of polymerization and the contents of the reactor were poured into a beaker containing large excess of acetone. The precipitated polymer was dried under vacuum at 100 °C for 24 hours. The polymer yield was 20 gm.

TABLE 3

( c %mm C3 triads were calculated according to the procedures set forth above supplemented by the teachings of U.S. Patent 5,504,172 rl x r2 product calculated per reference M. Kakugo, et al, Macromolecules, J5, 1150 (1982)

Both references are incorporated by reference for purposes of U.S. practice.

(2) GPC: Polypropylene calibration used

(3) FTIR iPP INDEX: Absorbance ratio at 997 / 973 cm-1

(4) DSC: Reported Tm (melting point) is for 1 st melt. Samples did not crystallize within the time span of DSC test. Therefore, crystallization point was not detected. Generally, high C3 EP copolymers crystallize slowly.

(5) % RECOVERY: Microtensile specimens were pulled at 5 inch/min. Rate in an Instron and held for 10 minutes at 150% elongation and then released.

Residual set was measured after 10 minutes. Recovery, a measure of elasticity, was calculated as follows:

% Recovery = 100 - (% set)

While the present invention has been described and illustrated by reference to particular embodiments, it will be appreciated by those of ordinary skill in the art that the invention lends itself to variations not necessarily illustrated herein. Reference should be made solely to the appended claims and their equivalents for purposes of determining the true scope of the present invention. For example, fabricated products comprising the claimed copolymer of this invention are also part of this invention. Such fabricated products can also optionally comprise one or more of an alpha olefin polymer or copolymer, a processing oil, and other additives. One such particularly preferred alpha olefin polymer is polypropylene.

Citations de brevets
Brevet cité Date de dépôt Date de publication Déposant Titre
WO1996006132A1 *21 août 199529 févr. 1996D & S Plastics InternationalEngineered olefinic compositions
EP0302424A1 *30 juil. 19888 févr. 1989Hoechst AktiengesellschaftProcess for preparing 1-olefinpolymers
EP0374695A2 *12 déc. 198927 juin 1990Polysar LimitedEthylene-propylene copolymer
EP0480190A2 *12 sept. 199115 avr. 1992BASF AktiengesellschaftPolymerwaxes of propylene with high hardness and crystallinity
EP0582194A1 *28 juil. 19939 févr. 1994Hoechst AktiengesellschaftProcess for the preparation of polymers using metallocenes with specifically substituted indenyl ligands
EP0890584A1 *2 juil. 199813 janv. 1999Clariant GmbHPolypropylene wax
US5504172 *7 juin 19942 avr. 1996Mitsui Petrochemical Industries, Ltd.Propylene polymer, propylene copolymer, and propylene elastomer prepared using novel bridged indenyl containing metallocenes
Référencé par
Brevet citant Date de dépôt Date de publication Déposant Titre
WO2001046277A2 *21 déc. 200028 juin 2001Exxonmobil Chemical Patents, Inc.Polypropylene-based adhesive compositions
WO2001046277A3 *21 déc. 200010 janv. 2002Exxonmobil Chem Patents IncPolypropylene-based adhesive compositions
WO2002083754A1 *2 avr. 200224 oct. 2002Exxonmobil Chemical Patents Inc.Propylene ethylene polymers and production process
WO2004014972A25 juin 200319 févr. 2004Equistar Chemicals, LpPolyolefin block copolymers
WO2004014972A3 *5 juin 200329 juil. 2004Equistar Chem LpPolyolefin block copolymers
WO2004014998A212 août 200319 févr. 2004Exxonmobil Chemical Patents Inc.Plasticized polyolefin compositions
WO2005080495A19 févr. 20051 sept. 2005Exxonmobil Chemical Patents Inc.Plasticized polyolefin compositions
WO2006065648A1 *9 déc. 200522 juin 2006Exxonmobil Chemical Patents Inc.Homogeneous polymer blend and articles therefrom
WO2006065649A1 *9 déc. 200522 juin 2006Exxonmobil Chemical Patents Inc.Heterogeneous polymer blends and molded articles therefrom
WO2006065664A1 *9 déc. 200522 juin 2006Exxonmobil Chemical Patents Inc.Films from polymer blends
WO2007103271A12 mars 200713 sept. 2007Dow Global Technologies Inc.Aqueous dispersions for use as toners
WO2008052122A125 oct. 20072 mai 2008Dow Global Technologies Inc.Polyolefin dispersions, froths, and foams
WO2008057881A231 oct. 200715 mai 2008Dow Global Technologies Inc.Polyurethane compositions and articles prepared therefrom, and methods for making the same
WO2008098136A17 févr. 200814 août 2008Dow Global Technologies Inc.Flexible conductive polymeric sheet
WO2009086251A122 déc. 20089 juil. 2009Dow Global Technologies Inc.Pe-based crosslinked elastomeric foam with high filler loadings for making shockpads and articles used in footwear and flooring applications
WO2010075251A121 déc. 20091 juil. 2010Dow Global Technologies Inc.Woven carpet coating compounds, associated methods of use, and articles made therefrom
WO2010107534A112 févr. 201023 sept. 2010Dow Global Technologies Inc.Multilayer structure and method of making the same
WO2010107748A116 mars 201023 sept. 2010Dow Global Technologies Inc.A dispersion, and a process for producing the same
WO2010114648A122 févr. 20107 oct. 2010Dow Global Technologies Inc.Hybrid dispersions and methods for producing the same
WO2011009070A116 juil. 201020 janv. 2011Dow Global Technologies, Inc.Coated substrates and packages prepared therefrom
WO2011011705A223 juil. 201027 janv. 2011Dow Global Technologies Inc.A coated container device, method of making the same
WO2011011707A223 juil. 201027 janv. 2011Dow Global Technologies Inc.Coated container device, method of making the same
WO2011017477A15 août 201010 févr. 2011Dow Global Technologies Inc.Radio frequency sealable film, sealed film structure and method of making the same
WO2011022280A112 août 201024 févr. 2011Exxonmobil Research And Engineeing CompanyProcess for making thermoplastic polymer pellets
WO2011041575A130 sept. 20107 avr. 2011Exxonmobil Chemical Patents Inc.Multi-layered meltblown composite and methods for making same
WO2011062809A19 nov. 201026 mai 2011Dow Global Technologies Inc.Thermoplastic elastomer for cold and wet applications
WO2011068525A119 nov. 20109 juin 2011Dow Global Technologies Inc.Extruder screw
WO2011075492A115 déc. 201023 juin 2011Dow Global Technologies LlcFilms and articles prepared from the same
WO2011087728A217 déc. 201021 juil. 2011Exxonmobil Chemical Patents Inc.Processes and apparatus for continuous solution polymerization
WO2011087729A217 déc. 201021 juil. 2011Exxonmobil Chemical Patents Inc.Processes and apparatus for polymer finishing and packaging
WO2011087731A117 déc. 201021 juil. 2011Exxonmobil Chemical Patents Inc.Processes and apparatus for continuous solution polymerization
WO2011112309A111 févr. 201115 sept. 2011Exxonmobil Chemical Patents Inc.Method for producing temperature resistant nonwovens
WO2011112311A111 févr. 201115 sept. 2011Exxonmobil Chemical Patents Inc.Elastic meltblown laminate constructions and methods for making same
WO2011142946A120 avr. 201117 nov. 2011Dow Global Technologies LlcAdhesion promoter system, and method of producing the same
WO2011142947A120 avr. 201117 nov. 2011Dow Global Technologies LlcAdhesion promoter system, and method of producing the same
WO2011142948A120 avr. 201117 nov. 2011Dow Global Technologies LlcAdhesion promoter system, and method of producing the same
WO2011142949A120 avr. 201117 nov. 2011Dow Global Technologies LlcAdhesion promoter system, and method of producing the same
WO2011146338A113 mai 201124 nov. 2011Dow Global Technologies LlcA multilayer sheet, a thermoformed article, and a method for making the same
WO2011156053A118 avr. 201115 déc. 2011Exxonmobil Oil CorporationFilm composition and method of making the same
WO2011159977A117 juin 201122 déc. 2011Dow Global Technologies LlcCoated polymeric particulates, and a process for coating polymeric particulates
WO2011163076A117 juin 201129 déc. 2011Dow Global Technologies LlcMasterbatch composition
WO2012009043A111 mai 201119 janv. 2012Exxonmobil Oil CorporationLaminate film and method of making the same
WO2012014105A230 juin 20112 févr. 2012Kimberly-Clark Worldwide, Inc.Low-density web and method of applying an additive composition thereto
WO2012015624A119 juil. 20112 févr. 2012Dow Global Technologies LlcLow-density web and method of applying an additive composition thereto
WO2012030578A122 août 20118 mars 2012Exxonmobil Chemical Patents Inc.Flame resistant polyolefin compositions and methods for making the same
WO2012037180A114 sept. 201122 mars 2012Dow Global Technologies LlcCoextruded multilayer film structure
WO2012061168A126 oct. 201110 mai 2012Dow Global Technologies LlcA sealant composition, method of producing the same
WO2012079243A117 déc. 201021 juin 2012Dow Global Technologies LlcHalogen-free, flame retardant composition for wire and cable applications
WO2012094315A13 janv. 201212 juil. 2012Dow Global Technologies LlcMicrocapillary films and foams containing functional filler materials
WO2012094317A13 janv. 201212 juil. 2012Dow Global Technologies LlcReinforced microcapillary films and foams
WO2012138348A18 avr. 201111 oct. 2012Dow Global Technologies LlcA coating compositon, and a process for producing the same
WO2013002976A16 juin 20123 janv. 2013Dow Global Technologies LlcClear graphic cling films
WO2013013116A120 juil. 201224 janv. 2013The Procter & Gamble CompanyPolymer composition
WO2013016398A125 juil. 201231 janv. 2013Dow Global Technologies LlcPolymeric blend formulations suitable for synthetic leather applications
WO2013055461A130 août 201218 avr. 2013Exxonmobil Oil CorporationSqueezable and conformable oriented polypropylene label
WO2013066536A127 sept. 201210 mai 2013Exxonmobil Oil CorporationUniaxially shrinkable, biaxially oriented polypropylene films
WO2013096705A121 déc. 201227 juin 2013Dow Global Technologies LlcHigh frequency weldable polyolefin compositions containing zeolites
WO2013096711A121 déc. 201227 juin 2013Dow Global Technologies LlcHigh frequency weldable polyolefin compositions including polar polymers
WO2013096714A121 déc. 201227 juin 2013Dow Global Technologies LlcMicrocapillary films and foams suitable for capillary action fluid transport
WO2013154860A12 avr. 201317 oct. 2013Dow Global Technologies LlcPolyolefin blend composition and articles made therefrom
WO2013166294A12 mai 20137 nov. 2013Tredegar Film Products CorporationLow peel force surface protection film and method of using same
WO2013191825A116 mai 201327 déc. 2013Dow Global Technologies LlcAqueous based blend composition and method of producing the same
WO2013191826A116 mai 201327 déc. 2013Dow Global Technologies LlcAqueous based blend composition and method of producing the same
WO2014003758A128 juin 20123 janv. 2014Dow Global Technologies LlcMethod and apparatus for producing a multi - layer microcapillary film
WO2014003761A128 juin 20123 janv. 2014Dow Global Technologies LlcSystem, method and apparatus for producing a multi-layer, microcapillary film
WO2014003954A230 mai 20133 janv. 2014Dow Global Technologies LlcA composite material method of producing the same, and articles made therefrom
WO2014011450A12 juil. 201316 janv. 2014Exxonmobil Chemical Patents Inc.Carpet comprising a propylene-based elastomer and methods of making the same
WO2014058639A130 sept. 201317 avr. 2014Dow Global Technologies LlcSealant composition
WO2014081516A114 oct. 201330 mai 2014Dow Global Technologies LlcA film composition, film made from the film composition and a multi-layer film including the film and articles made therefrom
WO2014081777A120 nov. 201330 mai 2014Dow Global Technologies LlcA film composition, film made from the film composition and a multi-layer film including the film and articles made therefrom
WO2014081838A120 nov. 201330 mai 2014Dow Global Technologies LlcCoating compositions
WO2014081841A120 nov. 201330 mai 2014Dow Global Technologies LlcCoating compositions
WO2014088791A119 nov. 201312 juin 2014Exxonmobile Chemical Patents Inc.Ethylene-based polymers and articles made therefrom
WO2014099219A119 nov. 201326 juin 2014Dow Global Technologies LlcA multi-layered structure and a method of sealing or shaping using a multi-layered structure
WO2014099305A126 nov. 201326 juin 2014Dow Global Technologies LlcFlexible film composition forheat seals and container with same
WO2014100386A119 déc. 201326 juin 2014Dow Global Technologies LlcFlexible film composition for heat seals and container with same
WO2014105464A113 déc. 20133 juil. 2014Dow Global Technologies LlcCoating compositions
WO2014105466A213 déc. 20133 juil. 2014Dow Global Technologies LlcA coating composition and articles made therefrom
WO2014120349A117 déc. 20137 août 2014Exxonmobil Chemical Patents Inc.Footwear sole comprising a propylene-based elastomer, footwear comprising said sole, and methods of making them
WO2014134399A128 févr. 20144 sept. 2014Dow Global Technologies LlcA blend composition suitable for injection molding applications
WO2014137516A13 févr. 201412 sept. 2014Dow Global Technologies LlcCoating composition, a film containing the same, and a method for forming a sealable film
WO2015002859A230 juin 20148 janv. 2015Dow Global Technologies LlcPolyolefin/ (meth)acrylic impact modifier and method of preparing same
WO2015012948A122 mai 201429 janv. 2015Exxonmobil Chemical Patents Inc.Polymer compositions, methods of making the same, and articles made therefrom
WO2015021201A16 août 201412 févr. 2015Dow Global Technologies LlcA composite material, articles made therefrom
WO2015057318A15 sept. 201423 avr. 2015Exxonmobil Chemical Patents Inc.Enhanced stretched cling performance polyolefin films
WO2015057423A17 oct. 201423 avr. 2015Dow Global Technologies LlcCompatibilized polyolefin blends
WO2015057501A110 oct. 201423 avr. 2015Dow Global Technologies LlcFlexible film composition for heat seals and container with same
WO2015073132A13 oct. 201421 mai 2015Exxonmobil Chemical Patents Inc.Process and apparatus for continuous solution polymerization
WO2015127023A119 févr. 201527 août 2015Dow Global Technologies LlcMultilayered polyolefin films, methods of manufacture thereof and articles comprising the same
WO2015127071A119 févr. 201527 août 2015Dow Global Technologies LlcMultilayer film, methods of manufacture thereof and articles comprising the same
WO2015127073A119 févr. 201527 août 2015Dow Global Technologies LlcHigh performance sealable co-extruded oriented film, methods of manufacture thereof and articles comprising the same
WO2015153794A11 avr. 20158 oct. 2015Dow Global Technologies LlcMulti-layer films and articles made therefrom
WO2015156890A123 janv. 201515 oct. 2015Exxonmobil Chemical Patents Inc.Compositions comprising propylene-based elastomers, foamed layers made therefrom, and methods of making the same
WO2016003657A118 juin 20157 janv. 2016Dow Global Technologies LlcA composition, injection molded article made therefrom and process to make injection molded article
WO2016028961A120 août 201525 févr. 2016Dow Global Technologies LlcHot melt adhesive composition including a crystalline block composite
WO2016048947A122 sept. 201531 mars 2016Dow Global Technologies LlcA multilayer structure
WO2016089647A123 nov. 20159 juin 2016Dow Global Technologies LlcDynamic vulcanization of a blend composition, methods of manufacture thereof and articles comprising the same
WO2016204874A12 mai 201622 déc. 2016Exxonmobil Chemical Patents Inc.Process for continuous solution polymerization
WO2017070061A118 oct. 201627 avr. 2017Dow Global Technologies LlcSelective sintering additive manufacturing method and powder used therein
WO2017091671A123 nov. 20161 juin 2017Dow Global Technologies LlcAdhesive formulations for fabric/poe adhesion
WO2017106075A112 déc. 201622 juin 2017Dow Global Technologies LlcPackage with peelable and non-peelable heat seals
WO2017120093A129 déc. 201613 juil. 2017Dow Global Technologies LlcThermoformed microcapillary sheeting
CN100396706C5 juin 200325 juin 2008伊奎斯塔化学有限公司Polyolefin block copolymers
CN101111555B9 déc. 200511 avr. 2012埃克森美孚化学专利公司Heterogeneous polymer blends and molded articles therefrom
CN105658688A *10 juin 20158 juin 2016株式会社Lg化学Propylene-based elastomer
DE112010003197T55 août 201028 juin 2012Dow Global Technologies Llc,,Hochfrequenz-siegelbare Folie, gesiegelte Folienstruktur und Verfahren zu deren Herstellung
EP1003814B223 juil. 19989 juin 2010ExxonMobil Chemical Patents Inc.Thermoplastic polymer blends of isotactic polypropylene and alpha-olefin/propylene copolymers
EP1581390B28 janv. 200431 août 2016ExxonMobil Chemical Patents Inc.Elastic articles and processes for their manufacture
EP2080615A118 janv. 200822 juil. 2009Dow Global Technologies Inc.Coated substrates and packages prepared therefrom
EP2264098A125 août 200422 déc. 2010Dow Global Technologies Inc.Method for producing an aqueous dispersion
EP2272910A125 août 200412 janv. 2011Dow Global Technologies Inc.Aqueous dispersion
EP2275254A117 juil. 200919 janv. 2011Dow Global Technologies Inc.Coated substrates and packages prepared therefrom
EP2281859A121 déc. 20059 févr. 2011Dow Global Technologies Inc.Polypropylene-based adhesive compounds
EP2399615A125 oct. 200728 déc. 2011Dow Global Technologies LLCPolyolefin dispersions, froths, and foams
EP2433772A116 oct. 200728 mars 2012Dow Global Technologies LLCAqueous dispersions disposed on glass-based fibers and glass-containing substrates
EP2468807A121 sept. 200727 juin 2012Dow Global Technologies LLCFibrillated polyolefin foam
EP2471861A128 déc. 20114 juil. 2012Braskem America, Inc.Compression blow formed articles
EP2543393A218 sept. 20089 janv. 2013Dow Global Technologies LLCFoam produced from a dispersion of higher crystallinity olefins
EP2543690A218 sept. 20089 janv. 2013Dow Global Technologies LLCFiber coated with a dispersion of higher crystallinity olefin
EP2543691A218 sept. 20089 janv. 2013Dow Global Technologies LLCMethod to make a long fiber concentrate with a dispersion of higher crystallinity olefin
EP2543763A218 sept. 20089 janv. 2013Dow Global Technologies LLCFibrous structure impregnated with a dispersion of higher crystallinity olefin
EP2543764A218 sept. 20089 janv. 2013Dow Global Technologies LLCCellulose-based article with dispersion of higher crystallinity olefin
EP2568023A114 nov. 200813 mars 2013Dow Global Technologies LLCA coated article, and method of forming such articles
EP2737911A225 oct. 20074 juin 2014Dow Global Technologies LLCPolyolefin dispersions, froths, and foams
EP2862712A116 oct. 201322 avr. 2015Dow Global Technologies LLCFlexible film composition for heat seals and container thereof
EP2921519A117 mars 201423 sept. 2015Dow Global Technologies LLCA multilayer structure
EP2982707A130 mai 201310 févr. 2016Dow Global Technologies LLCA composite material method of producing the same, and articles made therefrom
EP2995449A112 févr. 201016 mars 2016Dow Global Technologies LLCMultilayer structure and method of making the same
EP3031835A1 *10 juin 201515 juin 2016LG Chem, Ltd.Propylene-based elastomer
EP3031835A4 *10 juin 20153 mai 2017Lg Chemical LtdPropylene-based elastomer
EP3037472A210 déc. 201529 juin 2016Dow Global Technologies LLCPolyolefin dispersion compositions for making high vapor transport hydrophobic coatings
EP3103832A116 mai 201314 déc. 2016Dow Global Technologies LLCAqueous based blend composition and method of producing the same
EP3115428A213 déc. 201311 janv. 2017Dow Global Technologies LLCA coating composition and articles made therefrom
EP3133107A118 août 201522 févr. 2017Trinseo Europe GmbHPolyolefin compositions containing high concentrations of reinforcing fibers and methods of preparation
EP3150375A113 mai 20115 avr. 2017Dow Global Technologies LLCA multilayer sheet, a thermoformed article, and a method for making the same
EP3202681A123 juil. 20109 août 2017Dow Global Technologies LlcMethod of making a coated container device
US645563429 déc. 200024 sept. 20023M Innovative Properties CompanyPressure sensitive adhesive blends comprising (meth)acrylate polymers and articles therefrom
US648940021 déc. 20003 déc. 20023M Innovative Properties CompanyPressure-sensitive adhesive blends comprising ethylene/propylene-derived polymers and propylene-derived polymers and articles therefrom
US673748730 juil. 200218 mai 2004Equistar Chemicals, LpPolyolefin block copolymers
US674711421 déc. 20008 juin 2004Exxonmobil Chemical Patents Inc.Polypropylene-based adhesive compositions
US7232871 *2 avr. 200219 juin 2007Exxonmobil Chemical Patents Inc.Propylene ethylene polymers and production process
US73190779 déc. 200515 janv. 2008Exxonmobil Chemical Patents Inc.Polymer blends and nonwoven articles therefrom
US74767109 déc. 200513 janv. 2009Exxonmobil Chemical Patents Inc.Heterogeneous polymer blends and molded articles therefrom
US752150724 nov. 200321 avr. 2009Exxonmobil Chemical Patents Inc.Polypropylene-based adhesive compositions
US755053812 mars 200823 juin 2009Dupont Performance Elastomers LlcChlorosulfonated propylene/olefin elastomers
US76190389 déc. 200517 nov. 2009Exxonmobil Chemical Patents Inc.Homogeneous polymer blend and articles therefrom
US76455214 déc. 200612 janv. 2010Dow Global Technologies, Inc.Compositions and aqueous dispersions
US76831299 déc. 200523 mars 2010Exxonmobil Chemical Patents Inc.Films from polymer blends
US774095019 avr. 200522 juin 2010Dow Global Technologies Inc.Composition suitable for single-sided, low-noise, stretch cling film and films made therefrom
US779986418 nov. 200921 sept. 2010Dow Global Technologies Inc.Compositions and aqueous dispersions
US780759324 oct. 20065 oct. 2010Dow Global Technologies Inc.Multi-layer, pre-stretched elastic articles
US785525813 févr. 200621 déc. 2010Exxonmobil Chemical Patents Inc.Propylene olefin copolymers
US789315922 déc. 200622 févr. 2011Dow Global Technologies Inc.Blends of styrenic block copolymers and propylene-alpha olefin copolymers
US789316131 oct. 200622 févr. 2011Dow Global Technologies Inc.Propylene-based elastomeric composition
US794777610 mai 200724 mai 2011Dow Global Technologies LlcAqueous dispersion, its production method, and its use
US798196713 avr. 200619 juil. 2011Dow Global Technologies LlcComposition suitable for high gloss blown film and films made therefrom
US79985314 déc. 200616 août 2011Dow Global Technologies LlcAqueous polyolefin dispersions for textile impregnation
US800797828 févr. 200730 août 2011Dow Global Technologies LlcAqueous dispersions for use as toners
US80172049 janv. 200813 sept. 2011Dow Global Technologies LlcComposition suitable for thin-wall injection molded articles
US802214420 janv. 201120 sept. 2011Dow Global Technologies LlcPropylene-based elastomeric composition
US8026323 *19 avr. 200727 sept. 2011Exxonmobil Chemical Patents Inc.Propylene ethylene polymers and production process
US80296464 déc. 20064 oct. 2011Dow Global Technologies LlcCellulose articles containing an additive composition
US804371315 déc. 200525 oct. 2011Dow Global Technologies LlcCompositions and aqueous dispersions
US810546320 mars 200931 janv. 2012Kimberly-Clark Worldwide, Inc.Creped tissue sheets treated with an additive composition according to a pattern
US814797824 mai 20103 avr. 2012Dow Global Technologies LlcComposition suitable for single-sided, low-noise, stretch cling film and films made therefrom
US817320911 sept. 20078 mai 2012Dow Global Technologies LlcPolyolefin dispersion technology used for resin coated sand
US817793926 août 201115 mai 2012Dow Global Technologies LlcCellulose articles containing an additive composition
US819328924 nov. 20095 juin 2012Exxonmobil Chemical Patents Inc.Polyolefin adhesive compositions and articles made therefrom
US822234513 févr. 200917 juil. 2012Exxonmobil Chemical Patents Inc.Functionalized olefin polymers
US82275466 oct. 200624 juil. 2012Dow Global Technologies LlcMultilayer elastic film structures
US82628571 juil. 201011 sept. 2012Kimberly-Clark Worldwide, Inc.Process for producing tissue products
US828277621 juin 20079 oct. 2012Kimberly-Clark Worldwide, Inc.Wiping product having enhanced oil absorbency
US831825718 sept. 200827 nov. 2012Dow Global Technologies LlcDispersions of higher crystallinity olefins
US832981227 juil. 201111 déc. 2012Dow Global Technologies LlcAqueous dispersions for use as toners
US834992025 oct. 20078 janv. 2013Dow Global Technologies LlcPolyolefin dispersions, froths, and foams
US834994527 mai 20098 janv. 2013Dow Global Technologies LlcComposite dispersion, method of producing the same, and articles made therefrom
US842592424 nov. 200923 avr. 2013Exxonmobil Chemical Patents Inc.Propylene compositions containing a pyrethroid and products made therefrom
US847587814 oct. 20082 juil. 2013Dow Global Technologies LlcPolyolefin dispersion technology used for porous substrates
US847632622 sept. 20062 juil. 2013Dow Global Technologies LlcFibrillated polyolefin foam
US8501892 *26 août 20116 août 2013Exxonmobil Chemical Patents Inc.Propylene ethylene polymers and production process
US85075895 avr. 201113 août 2013Dow Global Technologies LlcPolyolefin dispersions, froths, and foams
US851251531 janv. 201120 août 2013Kimberly-Clark Worldwide, Inc.Wiping products having enhanced cleaning abilities
US853626821 déc. 200517 sept. 2013Dow Global Technologies LlcPolypropylene-based adhesive compositions
US855790626 mai 201115 oct. 2013Exxonmobil Chemical Patents Inc.Flame resistant polyolefin compositions and methods for making the same
US856887928 mars 201229 oct. 2013Dow Global Technologies LlcPolyolefin dispersion technology used for resin coated sand
US859201323 juil. 201026 nov. 2013Dow Global Technologies, Llc.Coated container device, method of making the same
US860352414 janv. 200810 déc. 2013Dow Agrosciences LlcDelivery of ethylene blocking and/or promoting agents
US860976018 nov. 200917 déc. 2013Exxonmobil Chemical Patents Inc.Blend partner with natural rubber for elastomeric compounds
US861821929 sept. 200631 déc. 2013Exxonmobil Chemical Patents Inc.Propylene copolymers for adhesive applications
US865316929 sept. 200618 févr. 2014Exxonmobil Chemical Patents Inc.Propylene copolymers for adhesive applications
US86801984 déc. 201225 mars 2014Dow Global Technologies LlcComposite dispersion, method of producing the same, and articles made therefrom
US87096078 avr. 201129 avr. 2014Dow Global Technologies LlcCoating composition, and a process for producing the same
US870960824 janv. 200829 avr. 2014Exxonmobil Chemical Patents Inc.Elastic polypropylene-based film compositions
US876585121 juin 20121 juil. 2014H.B. Fuller CompanyFree radical initiator modified hot melt adhesive composition including functionalized polyethylene and propylene-alpha-olefin polymer
US876587329 déc. 20111 juil. 2014Braskem America, Inc.Compression blow formed articles
US87855312 juil. 200722 juil. 2014Dow Global Technologies LlcDispersions of olefin block copolymers
US882908323 nov. 20099 sept. 2014Dow Global Technologies LlcCoating composition, a process of producing a coating composition, a coated article, and a method of making such articles
US882909024 nov. 20109 sept. 2014Dow Global Technologies LlcComposition comprising propylene-alpha-olefin copolymer, olefin block copolymer and DPO-BSA molecular melt
US885966114 nov. 200814 oct. 2014Dow Global Technologies LlcCoating composition, a coated article, and method of forming such articles
US888387015 sept. 201011 nov. 2014Dow Global Technologies LlcPropylene-alpha-olefin copolymer compositions with improved foaming window
US891664028 août 200723 déc. 2014Dow Global Technologies LlcBlended polyolefin dispersions
US89463298 janv. 20133 févr. 2015Dow Global Technologies LlcCoating compositions
US895715910 sept. 201317 févr. 2015Exxonmobil Chemical Patents Inc.Multiple catalyst system for olefin polymerization and polymers produced therefrom
US900633222 août 201114 avr. 2015Exxonmobil Chemical Patents Inc.Weatherable and flame-resistant thermoplastic vulcanizates and methods for making them
US905140421 nov. 20139 juin 2015Exxonmobil Chemical Patents Inc.Propylene copolymers for adhesive applications
US911525229 déc. 200825 août 2015Dow Global Technologies LlcPE-based crosslinked elastomeric foam with high filler loadings for making shockpads and articles used in footwear and flooring applications
US91454984 mars 201329 sept. 2015Dow Global Technologies LlcPolyolefin based formulations for membranes and fabrics
US91569723 déc. 200813 oct. 2015Dow Global Technologies LlcPolypropylene melt-blown sealant films for retort packaging
US916871812 mars 201027 oct. 2015Exxonmobil Chemical Patents Inc.Method for producing temperature resistant nonwovens
US916872024 sept. 200927 oct. 2015Exxonmobil Chemical Patents Inc.Biaxially elastic nonwoven laminates having inelastic zones
US91694068 janv. 201327 oct. 2015Dow Global Technologies LlcCoating compositions
US922194023 nov. 200929 déc. 2015Dow Global Technologies LlcCoating composition, a process of producing a coating composition, a coated article, and a method of forming such articles
US926701020 déc. 201223 févr. 2016Dow Global Technologies LlcRotomolding composition
US926706015 févr. 201323 févr. 2016H.B. Fuller CompanyReaction product of propylene polymer and wax, graft copolymers derived from polypropylene polymer and wax, hot melt adhesive compositions including the same, and methods of using and making the same
US927847319 nov. 20108 mars 2016Union Carbide Chemicals & Plastics Technology LlcExtruder screw
US932191231 déc. 200926 avr. 2016Dow Global Technologies LlcHalogen-free flame retardant thermoplastic compositions for wire and cable applications
US933692717 déc. 201010 mai 2016Dow Global Technologies LlcHalogen-free, flame retardant composition for wire and cable applications
US93883064 mars 200812 juil. 2016Exxonmobil Chemical Patents Inc.Polyethylene stretch film
US941629123 sept. 201516 août 2016Dow Global Technologies LlcCoating compositions
US942244413 déc. 201323 août 2016Dow Global Technologies LlcCoating compositions
US942793819 nov. 201330 août 2016Dow Global Technologies LlcMulti-layered structure and a method of sealing or shaping using a multi-layered structure
US942885721 déc. 200930 août 2016Dow Global Technologies LlcWoven carpet coating compounds, associated methods of use, and articles made therefrom
US94933373 janv. 201215 nov. 2016Dow Global Technologies LlcReinforced microcapillary films and foams
US9498932 *30 sept. 201022 nov. 2016Exxonmobil Chemical Patents Inc.Multi-layered meltblown composite and methods for making same
US952221318 juin 201320 déc. 2016H.B. Fuller CompanyPressure-sensitive hot melt adhesive composition including propylene thermoplastic elastomer and articles including the same
US954724625 févr. 201017 janv. 2017Dow Global Technologies LlcAqueous dispersions for use as toners
US959323515 févr. 201314 mars 2017H.B. Fuller CompanyReaction product of propylene polymer and wax, graft copolymers derived from polypropylene polymer and wax, hot melt adhesive compositions including the same, and methods of using and making the same
US959856930 juin 201421 mars 2017Rohm And Haas CompanyComposite polymer composition
US960537725 juil. 201228 mars 2017Dow Global Technologies LlcPolymeric blend formulations suitable for synthetic leather applications
US961739921 déc. 201211 avr. 2017Dow Global Technologies LlcHigh frequency weldable polyolefin compositions containing zeolites
US96433882 déc. 20119 mai 2017Exxonmobil Chemical Patents Inc.Multilayer films, their methods of production, and articles made therefrom
US967035331 déc. 20126 juin 2017Dow Global Technologies LlcThermoplastic vulcanizate with crosslinked olefin block copolymer
US970182422 déc. 201511 juil. 2017Dow Global Technologies LlcPolyolefin dispersion compositions for making high vapor transport hydrophobic coatings
US97520247 oct. 20145 sept. 2017Dow Global Technologies LlcCompatibilized polyolefin blends
US978366716 sept. 201410 oct. 2017Dow Global Technologies LlcPolymeric blend composition
US20050054800 *18 oct. 200410 mars 2005Li-Min TauFilms comprising isotactic propylene copolymers
US20110081529 *30 sept. 20107 avr. 2011Richeson Galen CMulti-Layered Meltblown Composite and Methods for Making Same
US20110313117 *26 août 201122 déc. 2011Sudhin DattaPropylene Ethylene Polymers And Production Process
US20120118785 *23 juil. 201017 mai 2012Dow Global Technologies Inc.Coated container device, method of making the same
US20160251461 *10 juin 20151 sept. 2016Lg Chem, Ltd.Propylene-based elastomer
Classifications
Classification internationaleC08F4/659, C08F210/06, C08F210/16, C08L23/10
Classification coopérativeC08L2314/06, C08F210/16, C08L23/10, C08F210/06, C08L2205/02, C08F4/65908
Classification européenneC08L23/10, C08F210/06, C08F210/16
Événements juridiques
DateCodeÉvénementDescription
13 janv. 2000AKDesignated states
Kind code of ref document: A1
Designated state(s): AU BR CA CN JP KR MX RU
13 janv. 2000ALDesignated countries for regional patents
Kind code of ref document: A1
Designated state(s): AT BE CH CY DE DK ES FI FR GB GR IE IT LU MC NL PT SE
24 févr. 2000DFPERequest for preliminary examination filed prior to expiration of 19th month from priority date (pct application filed before 20040101)
8 mars 2000121Ep: the epo has been informed by wipo that ep was designated in this application
30 déc. 2000WWEWipo information: entry into national phase
Ref document number: 1020007015119
Country of ref document: KR
11 janv. 2001WWEWipo information: entry into national phase
Ref document number: 1999933644
Country of ref document: EP
18 avr. 2001WWPWipo information: published in national office
Ref document number: 1999933644
Country of ref document: EP
31 juil. 2001WWPWipo information: published in national office
Ref document number: 1020007015119
Country of ref document: KR
12 févr. 2002WWWWipo information: withdrawn in national office
Ref document number: 1999933644
Country of ref document: EP
2 juil. 2004WWWWipo information: withdrawn in national office
Ref document number: 1020007015119
Country of ref document: KR