WO2003022899A1 - Binder for abrasive articles, abrasive articles including the same and method of making same - Google Patents
Binder for abrasive articles, abrasive articles including the same and method of making same Download PDFInfo
- Publication number
- WO2003022899A1 WO2003022899A1 PCT/US2002/028875 US0228875W WO03022899A1 WO 2003022899 A1 WO2003022899 A1 WO 2003022899A1 US 0228875 W US0228875 W US 0228875W WO 03022899 A1 WO03022899 A1 WO 03022899A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- coated abrasive
- binder
- formaldehyde resin
- acid
- abrasive article
- Prior art date
Abstract
Description
Claims