WO2003022912A2 - Ion conducting membrane having high hardness and dimensional stability - Google Patents
Ion conducting membrane having high hardness and dimensional stability Download PDFInfo
- Publication number
- WO2003022912A2 WO2003022912A2 PCT/US2002/027338 US0227338W WO03022912A2 WO 2003022912 A2 WO2003022912 A2 WO 2003022912A2 US 0227338 W US0227338 W US 0227338W WO 03022912 A2 WO03022912 A2 WO 03022912A2
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- membrane
- composite membrane
- composite
- dimensional stability
- hardness
- Prior art date
Abstract
Description
Claims