WO2003035486A1 - Oxygen scavenging monolayer bottles - Google Patents
Oxygen scavenging monolayer bottles Download PDFInfo
- Publication number
- WO2003035486A1 WO2003035486A1 PCT/US2002/024280 US0224280W WO03035486A1 WO 2003035486 A1 WO2003035486 A1 WO 2003035486A1 US 0224280 W US0224280 W US 0224280W WO 03035486 A1 WO03035486 A1 WO 03035486A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- oxygen scavenging
- package
- pet
- monolayer
- segments
- Prior art date
Abstract
Description
Claims