DIRECTED ASSEMBLY OF HIGHLY-ORGANIZED CARBON NANOTUBE ARCHITECTURES
STATEMENT REGARDING FEDERALLY SPONSORED RESEARCH OR
DEVELOPMENT
[0001 ] The U.S. Government may have certain rights in this invention pursuant to grant number N0001 4-00-1 -2050 from the Office of Naval Research.
CROSS-REFERENCE TO RELATED PATENT APPLICATIONS
[0002] The present application claims benefit under 35 U.S.C.
§ 1 1 9(e) of United States provisional applications 60/356,069, filed February 1 1 , 2002 and 60/385,393, filed June 3, 2002, both of which are incorporated herein by reference in their entirety.
BACKGROUND OF THE INVENTION
[0003] The present invention relates generally to carbon nanotubes and more particularly to selective growth of carbon nanotubes on template materials.
[0004] It is likely that future devices containing organized structures of various functional materials with new properties will be built from nanoscale building blocks. These nanoscale building blocks can be produced by a variety of synthesis routes. The novel properties of the nanoscale building blocks arising from their low dimensions are known for a wide range of materials.
[0005] Carbon nanotubes are a nanostructured material which promises to have a wide range of applications. However, the present techniques used to controllably build organized architectures of nanotubes with predetermined orientations have several deficiencies. For example, vertically aligned nanotubes has been fabricated on catalyst printed planar substrates by chemical vapor deposition. See, for example, W. Z. Li, et al. Science 274, 1 701 (1 996); R. Sen, A. Govindaraj, C. N . R. Rao, Chem. Phys. Lett. 267, 276 ( 1 997); M. Terrones, et al. Nature 388, 52 (1 997); Z. F. Ren, et al. Science 282, 1 1 05 ( 1 998); S. S. Fan, et al. Science 283, 51 2 (1 999); H. Kind, et al. Adv. Mater. 1 1 , 1 285 (1 999); R.R. Schlittler, et al. Science 292, 1 1 36 (2001 ) and L. Dai, A. W. H. Mau, J. Phys. Chem. B 1 04, 1 891 (2000) . However, this technique requires deposition and patterning, usually in separate processing steps, of catalyst material, typically in nanoparticle assemblies or thin film forms, which complicates the nanotube fabrication method. This also does not allow growth of nanotubes in more than one preselected orientation at different locations in a controllable fashion.
[0006] While growth of vertically aligned nanotubes on planar substrates by CVD has been reported extensively, obtaining nanotubes that are exclusively oriented parallel to the substrate in predetermined orientations has been more difficult. Suspended nanotubes across elevated structures have been produced recently by several different methods. One method involves adjusting the gas flow during CVD. See N. R. Franklin, H. Dai, Adv. Mater. 2000, 1 2, 890; N. R. Franklin, Q. Wang, T. W. Tombler, A. Javey, M. Shim, H. Dai, Appl. Phys. Lett. 2002, 81 , 91 3; and Y. Homma, Y. Kobayashi, T. Ogino, T. Yamashita, Appl. Phys. Lett. 2002, 81 , 2261 . Another method involves applying an electrical field during CVD. See Y. Zhang, A. Chang, J. Cao, Q. Wang, W. Kim, Y. Li, N. Morris, E. Yenilmez, J. Kong, H. Dai, Appl . Phys. Lett.
2001 , 79, 31 55; and A. Ural, Y. Li, H. Dai, Appl. Phys. Lett. 2002, 81 , 3464. However, these approaches require pre-deposition and pre- patterning of nanoscale catalyst particle assemblies. Also, the probability of nanotubes bridging across different catalyst islands is difficult to predict and control. Several articles also note that nanotubes can be aligned in horizontal configurations through electric fields or microfluidic forces. See A. Star, et al., Angewandte Chem. International Edition 40, 1 721 (2001 ) and T. Rueckes, et al., Science 289, 94 (2000) . However, these methods are also complicated, and are difficult to scale (e.g., create them reproducibly on an 8 inch Si wafer) and to control, for developing devices for applications. Moreover, in these cases the nanotubes are not rooted to the substrate (i.e. they are just lying on them, and hence not very robust) .
[0007] Several methods have also been suggested for controlled placement of carbon nanotubes onto electrode pairs, including AC bias- enhanced deposition and chemically modified adsorption. See L. A. Nagahara, I. Amiani, J. Lewenstein, R. K. Tsui, Appl. Phys. Lett. 2002, 80, 3826 and M. Burgard, G. Buesberg, G. Philipp, J. Muster, S. Roth, Adv. Mater. 1 998, 10, 584.
[0008] Some of the present inventors have also previously suggested to selectively grow carbon nanotubes on silica templates located on a silicon substrate without growing the nanotubes on the silicon substrate. See Z. J. Zhang, B. Q. Wei, G. Ramanath, P. M. Ajayan, Appl. Phys. Lett. 77, 3764 (2000). The use of this template structure is advantageous in that it does not require the deposition and patterning of the catalyst material. However, as can be seen in Figure 4 of the Z. J. Zhang et al. article, while roughly vertical and horizontal nanotubes were simultaneously grown on the template structures, it was not possible to controllably align nanotubes during growth in a direction
perpendicular to the silica template structure surfaces. For example, as shown in the insert in Figure 4 of this article, the nanotubes were not aligned precisely and controllably.
SUMMARY OF THE INVENTION
[0009] A preferred embodiment of the invention provides a method of making carbon nanotubes, comprising providing a substrate containing a template structure having at least two surfaces and providing a nanotube source gas onto the template structure. The nanotube source gas preferably comprises a mixture of nanotube forming precursor gas, such as xylenes, and a catalyst gas, such as ferrocene. However, other suitable gases or a single source gas may be used instead. The method further provides for selectively and simultaneously growing the carbon nanotubes on the at least two surfaces of the template structure but not on exposed portions of the substrate (i.e., in exclusion to the substrate material which supports the template structure) . The grown carbon nanotubes are controllably aligned in a direction perpendicular to the respective surfaces of the template structure.
[0010] Another preferred embodiment of the invention provides a structure, comprising a substrate and a template structure located on the substrate, wherein the template structure comprises at least two surfaces. The structure also comprises a first plurality of carbon nanotubes disposed on a first surface of the template structure, wherein the first plurality of carbon nanotubes are controllably aligned in a first direction perpendicular to the first surface of the template structure, and a second plurality of carbon nanotubes disposed on a second surface of the template structure, wherein the second plurality of carbon nanotubes are controllably aligned in a second direction perpendicular to the second
surface of the template structure, such that the first direction is different than the second direction.
BRIEF DESCRIPTION OF THE DRAWINGS
[001 1 ] Figures 1 A-B, 2A-D, 4A-C, 5, 6A-G, 8A-F, 9C, 1 1 A-B and
1 2C are SEM images of carbon nanotube structures according to preferred embodiments of the present invention.
[0012] Figures 2C, 4D, 6H, 1 1 C and 1 2A-B are three dimensional schematics of carbon nanotube structures according to preferred embodiments of the present invention.
[0013] Figures 3A-3C are SEM images of porous carbon nanotube films according to a preferred embodiment of the present invention.
[0014] Figures 7A-B are side cross sectional schematic views of a method of making carbon nanotube structures according to a preferred embodiment of the present invention.
[0015] Figure 9A is a plot of carbon nanotube length as a function of gold masking material coverage on a SiO2 template structure according to a preferred embodiment of the present invention.
[0016] Figure 9B is an SEM image of gold masking material islands on a surface of a Siθ2 template structure according to a preferred embodiment of the present invention.
[0017] Figure 1 0A is side cross sectional schematic view of carbon nanotube structures according to a preferred embodiment of the present invention.
[0018] Figure 10B is a plot of measured resistance versus a number of carbon nanotube bridges according to a preferred embodiment of the present invention.
DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS
[0019] The present inventors have developed a method of controllably aligning carbon nanotubes to a template structure to fabricate a variety of carbon nanotube containing structures and devices having desired characteristics. For example, by selecting a template structure with a sufficient thickness allows a simultaneous growth of both vertically and horizontally controllably aligned nanotubes in a single process step. In fact, the nanotubes may be aligned in any set of in-plane and/or out of plane orientations and grown in a single process step. The level of control provided by this method provides construction of complex, nanotube based, highly organized 1 -to-3-D architectures for building or use in nanotube based devices and systems in a scalable fashion.
[0020] A template structure, pattern or material is a structure, pattern or material which allows selective growth of carbon nanotubes on it without growing any detectable amount of carbon nanotubes on exposed portions of the substrate which supports the template. Nanotubes grow normal to, and selectively on the template structure, inheriting the topography of the template structure. Thus, the nanotubes are controllably aligned in a direction perpendicular to the surface of the template structure from which they grow such that all the nanotubes which grow from a particular template structure surface are oriented in the same direction. The precise control of nanotube orientation allows the fabrication of a wide variety of organized architectures of differing complexities, shapes, densities, dimensions and orientation. The bottom-
up fabrication approach is easy, scalable, and compatible with silicon microfabrication techniques and processes.
[0021 ] In a preferred aspect of the present invention, the template structure comprises a silicon dioxide structure located on a silicon substrate. However, other suitable template and substrate materials may be used instead. For example, other silicon oxide and metal oxide template structures materials, such as silicon oxynitride, magnesium oxide, aluminum oxide or indium tin oxide, may be used instead. Thus, a carbon nanotube growth catalyst material, such as a metal nanoparticle layer, is not necessary to selectively grow carbon nanotubes, and is preferably omitted to simplify processing. In alternative aspects of the present invention, a metal that does not catalyze nanotube growth, such as gold or copper, can also be used to mask part of the template structure material on the substrate. The substrate material can be any material that does not catalyze nanotube growth. Examples of preferred substrate materials are a single crystal silicon wafer, epitaxial silicon and polysilicon layers. Furthermore, other semiconductor materials, such as ll-VI and III- V semiconductor materials, and non-semiconductor materials, such as ceramics, metals, glasses and plastics that do not catalyze nanotube growth may be used as a substrate by appropriately selecting the template material which allows selective growth of carbon nanotubes.
[0022] In another alternative aspect of the present invention, the substrate may be omitted entirely, and the nanotubes may be fabricated on free standing template structures. For example carbon nanotubes may be formed on the surfaces of oxide particles, such as silica, alumina, MgO and other silicon and metal oxide particles. Preferably, the particles are substantially spherical oxide particles, such as spherical, oval and roughly spherical (i.e., spherical particles with chiseled surfaces) particles. The particles may be micro sized (preferably 1 to 1 ,000 micron diameter) or
macro sized (preferably 1 ,000 microns to 1 cm diameter) . The carbon nanotubes are aligned perpendicular to the oxide particle surfaces.
[0023] In preferred embodiments of the present invention, controllably aligned multiwalled carbon nanotubes are selectively and simultaneously grown in patterns and in multiple directions on lithographically patterned silica templates in a single process. This process is preferably carried out through a CVD method that delivers the nanotube-forming precursor and the catalyst material (in compound or elemental form) from the gas phase either simultaneously or sequentially.
[0024] The specific examples of nanotube structures of the present invention shown are illustrated in SEM images in the Figures. However, the present invention should not be considered limited by the structures and methods of the specific examples, which are provided for illustration of the present invention.
[0025] The nanotube structures shown in the SEM images in the
Figures were selectively grown on non-planar patterns composed of SiO2 and Si surfaces. The substrates were Si (1 00) wafers capped with thermally grown or plasma-enhanced chemical vapor deposition (PECVD) deposited SiO2 template structures having a thickness of 1 00 nm to several microns, such as 2 to 8.5 microns. For example, thick silica layers (up to about 8.5 microns) were deposited by PECVD to create high- aspect-ratio silica features. Patterns of Si/SiO2 of various shapes were generated by photolithography followed by a combination of wet and/or dry etching.
[0026] Patterned nanotube growth was achieved without metal catalyst predeposition and patterning, thereby simplifying the template preparation by eliminating 2 processing steps. Instead, CVD nanotube growth was stimulated by exposing the substrate and the template
structure on the substrate to vapor mixtures comprising xylenes (CβHio), a nanotube-forming precursor, and ferrocene (Fe(CsH5)2), a nanotube catalyst, at about 600 to 1 100 °C, preferably at about 800 to 900 °C. However, other suitable source gases and temperatures may be used instead. Ferrocene was dissolved in xylenes (which preferably contains different isomers) at concentrations of about 0.01 g/ml, the mixture was pre-heated, co-evaporated and fed into the CVD chamber. Ferrocene preferably comprises 0.001 to 1 percent of the ferrocene/xylenes mixture. Prolonged growth in the temperature range of 600-1 1 00 °C, produced films of densely packed multiwalled carbon nanotubes on the template structures but not on the substrate. Uniform, vertically aligned nanotube films having a thickness of a few microns to several tens of microns were produced in few minutes at growth rates of about 10 microns/minute. The nanotubes in the nanotube films were about 30 nm diameter multiwalled carbon nanotubes. No nanotube growth was observed on pristine Si surfaces, or on the native oxide layer formed on the silicon substrate. Aligned nanotubes grew readily on SiO2 templates in a direction normal to the template growth surface, and the selectivity was retained down to micron size SiO2 templates.
[0027] Using the substrate-selective and normal direction growth process, the nanotubes structures of various shapes and orientations with respect to the Si surface were fabricated on active SiO2 template surfaces. Thus, carbon nanotubes were selectively grown in desired patterns and architectures without further photolithographic patterning.
[0028] The method and structure of the first preferred embodiment will now be described. In the first preferred embodiment, the carbon nanotubes were selectively grown in one direction on various template structure shapes to produce various nanotube structure shapes having the footprint of the template surfaces. These nanotube structures can then
be optionally removed from over the substrate and placed into a suitable device.
[0029] Figures 1 A-B show a striking example of aligned nanotube pillars placed on specific sites on the substrate according to one aspect of the first embodiment. Figure 1 A illustrates an SEM image of pillars of aligned carbon nanotube (CNT) arrays within trenches surrounded by a thick aligned nanotube film grown vertically on the SiO2 pattern on a Si substrate. The nanotube film was selectively grown on a SiO2 pattern or template structure. In the center of box-like regions defined by the nanotube film walls, micro-sized cylindrical blocks or pillars of vertically oriented nanotubes are grown from the underlying template structure constituted by SiO2 patterns in this case. Within each block, the nanotubes are highly oriented and densely packed. Three different pillar packing densities are shown in Figure 1 A, where the separation between pillars in each group is 10 microns (top), 5 microns (bottom) and 2 microns (center).
[0030] Figure 1 B is an enlarged image of the middle array shown in
Figure 1 A showing the alignment of the nanotubes in each of the pillars. Figure 1 C illustrates a schematic of the nanotube pillars on the SiO2 patterns located a Si substrate. Specifically, Figure 1 C shows a silicon substrate 1 0 containing cylindrical SiO2 template structures 1 2 on the upper surface of the substrate 10. Carbon nanotube pillars 1 4 are selectively grown and are located on the upper surfaces of the template structures 1 2. Since the height (i.e., thickness) of the template structures 1 2 is less than a cutoff thickness for growth of nanotubes (such as less than 1 micron, preferably 200 nm or less), the nanotubes do not grow from the sidewalls of the template structures 1 2. The cutoff thickness varies with the template material and with the nanotube growth parameters.
[0031 ] The structures shown in Figures 1 A-C were made by the following method. The SiO2 template structures or patterns 1 2 were formed on a silicon substrate 1 0 by conventional photolithography. The template structures 1 2 were exposed to xylenes/ferrocene gas mixtures at temperatures ranging from 600 to 1 1 00°C, preferably 800 to 900 °C in a CVD tube furnace. The nanotubes 14 grew extremely selectively on the SiO2 patterns 1 2, but did not grow on the silicon substrate 1 0, leaving the exposed silicon substrate blank. Alignment of nanotubes can be easily identified from the sidewalls, which separate the micro pillar arrays of nanotubes. The template structures had a diameter of about 1 0 microns to form cylindrical nanotube pillars having a diameter of about 10 microns in diameter and separations between individual pillars 1 4 of 1 0, 5 and 2 microns for the top, bottom and middle pillar sets, respectively. In addition to the cylindrical pillars 14 and cylindrical template structures 1 2, other suitable pillar 1 4 shapes, such as polygonal (triangular, rectangular, trapezoidal, etc.), oval or irregular shapes, can be fabricated by shaping the template structures 1 2 accordingly. Furthermore, while SiO2 template structures 1 2 on a silicon 1 0 substrate were illustrated, other suitable materials for the template structures 1 2 and the substrate 1 0 may be used instead, as described herein.
[0032] Figure 2A is top view of several "sandwich" or rectangular block structures of platelets of aligned nanotubes grown from parallel silica lines (i.e., template structures) on a silicon substrate according to another preferred aspect of the first embodiment. The different sandwich structures show different nanotube platelet thickness (2-1 0 microns, decreasing from left to right in Figure 2A) and separation between the platelets (2-1 0 microns, decreasing from left to right) . The SiO2 line patterns or template structures were each 1 00 microns in length. They were fabricated using standard photolithography. The nanotube platelets
or lines were selectively grown on the template structures by the CVD method described above. The result shows the excellent control of the placement of the nanotube platelet structures at the desired locations, their thickness, height and the separation between them (density). The height of these structures can be precisely controlled to within a few tenths of microns to several hundreds of microns by tuning the nanotube deposition time. Of course shapes other than rectangular platelets, template materials other than SiO2 and substrate materials other than silicon may be used instead.
[0033] Figure 2B is a higher magnification SEM image showing the alignment of nanotubes within the nanotube platelets. The coordinated deformation and displacement of the individual platelets on the substrate indicate substantial attractive forces between individual nanotubes, suggesting that each platelet may be manipulated individually.
[0034] Figures 2C and 2D illustrate very long, ordered micro fibers of aligned nanotubes grown from silica patterns of two different shapes, resulting in two different fiber cross-sections, according to another aspect of the first embodiment. Figure 2C shows fibers with a circular cross section and Figure 2D shows fibers with a square cross section. Thus, the cross-sections of these nanotube fibers are controlled by the shape of the underlying template patterns on which they grow. Plural nanotubes within each micro-fiber can grow simultaneously to hundreds of micrometers, aligned all along the length. The template structures or patterns 1 2 used to produce these fibers are essentially the same as those used for structures in Figures 1 A-C, but the growth time is longer resulting in flexible ordered fibers, compared to stiffer, shorter pillars of Figures 1 A-C. The fibers can have a length of 1 00 to 500 microns, such as 1 50 to 300 microns, depending on the length of the nanotube deposition time.
[0035] In all cases of the nanotube pillars shown in Figures 1 A-C, the nanotube platelets shown in Figures 2A-B and the nanotube fibers shown in Figures 2C-D, the present inventors observed good adhesion between individual nanotubes within each geometrical block, and between the nanotubes and the substrate. The nanotube blocks, however, can be detached from the substrates by ultrasonic agitation, and can be manipulated individually using any suitable nanotube manipulation method. For example, the removed nanotube pillars, platelets and/or fibers may be selectively placed into a desired device, such as an electronic device.
[0036] The method and structure of the second preferred embodiment will now be described. In the second preferred embodiment, porous carbon nanotube films were fabricated. These porous films were fabricated with a high degree of control over pore sizes, shapes and separations. This is illustrated in Figures 3A-C, which show nanotube films with regular arrays of pores. Three different pore features imprinted in the nanotube film are shown in Figures 3A-C. For example, nanotube films with square and rectangular pores arranged in a rectangular grid are shown in Figures 3A and 3B, respectively. A nanotube film with randomly shaped pores arranged in a random orientation is shown in Figure 3C. The porous carbon nanotube films shown in Figures 3A-C include a plurality of carbon nanotubes aligned lengthwise in a direction away from the template layer and a plurality of first pores extending through the film in the same direction. The bottom ends of the carbon nanotubes are attached to the porous template material such that the pores in the nanotube film have a controlled size and are aligned with the respective pores in the template material. The carbon nanotubes are not disposed on portions of the substrate exposed through the pores.
[0037] The porous nanotube films were obtained by using a porous template structure or layer formed over a substrate. For example, a porous silica template layer was obtained by forming a silica layer on the silicon substrate and then photolithographically masking the layer and etching pores or holes in this layer. Since the pores or holes are formed by photolithography and etching, they have a controlled size. The pores or holes extend down to the silicon substrate and may extend into the silicon substrate if desired. Thus, portions of the substrate are exposed through pores in the porous template layer. Nanotube-forming gases or mixtures were provided onto the porous template layer and the carbon nanotubes were selectively grown on the porous template layer. However, the nanotubes were not formed on portions of the substrate exposed through pores in the porous template layer. Furthermore, the nanotubes did not form on the template layer pore sidewalls because the template layer thickness is not sufficient to allow nanotube growth on side surfaces of the pores in the template layer. For example, the template layer may have a thickness of less than about 200 nm, depending on the exact processing conditions and the template material used, to avoid nanotube growth on the side surfaces of the pores. If desired, after the nanotube film is grown, the substrate may be selectively removed, such as by polishing or by silicon selective etching, to form a free standing porous nanotube film. In an alternative aspect of the second embodiment, the porous nanotube film is produced by a different method. The template material can be selectively covered by non-catalytic masking materials (e.g., gold) through lithography and deposition, at locations where pores are desired. The template material has a plurality of first regions masked by a masking material which does not catalyze nanotubes, such as gold or copper masking material. The ends of the nanotubes are attached to the template material such that the plurality of pores in the nanotube film have a controlled size and are aligned with the plurality of first regions on
the template material masked by the masking material. When the nanotubes are grown on the masked template material, the nanotubes selectively grow on the exposed template material but not on the masked first regions of the template material.
[0038] Thus, the template layer may be considered to be the negative pattern of the one used to make free-standing nanotube blocks shown in Figures 1 and 2. Both the number of nanotubes in each block (e.g., pillar), and the lateral separation between the blocks or pores are limited only by the smallest dimension of silica patterns that can be produced, and these can conceivably be made smaller by using electron- beam lithographed templates or templates made by other submicron lithography or patterning methods.
[0039] The method and structure of the third preferred embodiment will now be described. In the third embodiment, selective nanotube growth on the template structure having at least one, and preferably two or more surfaces. The nanotube growth occurs in a direction normal to the respective surfaces and hence this approach can be harnessed to simultaneously grow nanotubes in several predetermined directions. For example, nanotube growth in mutually orthogonal directions may be carried out by using template structures comprising of deep etched trenches, drilled all the way to silicon substrate, separating several thick SiO2 template structure towers. Preferably, the nanotubes are grown on side surfaces of the template structures, which are preferably thicker than about 200 nm, preferably thicker than 2 microns. For example, the template structure may be several microns thick, such as 2 to 1 0 microns thick, preferably 5 to 8.5 microns thick. However, thickness of the template structure for growing controllably aligned nanotubes on the side surfaces of the template structure varies based on the template material and the nanotube growth conditions. The preference of nanotubes to
grow normal to, and selectively on, silica surfaces, forces the nanotubes to inherit the topography of the substrate templates, enabling the premeditation of both nucleation sites and growth direction.
[0040] Preferably, the template structure that is located on the substrate has at least one, and preferably two or more surfaces. A first plurality of carbon nanotubes are disposed on a first surface of the template structure. These first plurality of carbon nanotubes are controllably aligned in a first direction perpendicular to the first surface of the template structure. Furthermore, a second plurality of carbon nanotubes are disposed on a second surface of the template structure. This second plurality of carbon nanotubes are controllably aligned in a second direction perpendicular to the second surface of the template structure, such that the first direction is different than the second direction. The same applies for other surfaces of the template structures.
[0041 ] Figures 4A-D illustrate vertically and horizontally aligned nanotube arrays adjacent to each other produced in a single-step growth process. Figure 4A is an SEM image of simultaneously vertically and horizontally aligned nanotube arrays of nanotubes grown on a template structure comprising a thick SiO2 film with deep, etched trenches that separate alternating layers of SiO2 and silicon. Figure 4B is an enlarged area marked by the white box in Figure 4A. Figure 4B illustrates three dimensional aligned vertical and horizontal growth of nanotubes. The length of nanotubes in both vertical and horizontal growth is about 60 microns. The thickness of Siθ2 patterns was 8.5 microns, which is thicker than a threshold required to grow controllably aligned nanotubes on side surfaces. Figure 4C shows a cross-section of the specimen of Figure 4A cut along the white line shown in Figure 4A. The inset in Figure 4C is a higher magnification image that shows the perfect, controlled orthogonal alignment of the nanotube arrays.
[0042] Figure 4D is a schematic illustration of the SEM images of
Figures 4A-C. The rectangular silica template structure 1 2 is formed on a silicon substrate 1 0. The controllably aligned nanotube structures or arrays 1 4 are formed on the upper surface of the template structure 1 2 as well as in two orthogonal directions in the substrate plane itself (i.e., the nanotubes 14 are aligned parallel to the upper plane or surface of the substrate 10) . Thus, the nanotubes 1 4 on the upper template structure 1 2 surface are perpendicular to the nanotubes 1 4 on plurality of side surfaces of the template structure 1 2, and the nanotubes 14 on different template side surfaces are located in different (i.e., perpendicular) directions from each other. Thus, the nanotubes 1 4 are controllably aligned in directions perpendicular to the plurality of the side surfaces of the template structure 1 2.
[0043] Another preferred aspect of the third embodiment is illustrated in Figure 5. In this aspect, the template structure 1 2 shown in Figure 5 comprises a cylindrical pillar having a height of about 5 microns containing one continuous side surface. The carbon nanotubes are controllably aligned in a direction perpendicular to this side surface of the template structure. The nanotube domains or structures 1 4 in Figure 5 includes vertical and horizontal arrays of nanotubes. The short vertical block of nanotubes grown in the center of each pattern is surrounded by radiating nanotube arrays (wings) grown on the side surface of the silica template structure. If wet etching of the thick silica template structure 1 2 creates inclined side surfaces (forming a frustum rather than a perfect cylinder), then the nanotube wings would not be perfectly horizontal (i.e., parallel to the substrate surface), but still perpendicular to the template surface.
[0044] The method and structure of the fourth preferred embodiment will now be described. In the fourth embodiment, the
structure contains nanotubes packed with oblique inclinations, neither orthogonal nor planar or parallel with respect to the upper substrate plane, by using deep-trench template structures, such as silica structures, with inclined side surfaces. Figures 6A-6G show illustrative examples where nanotubes grow normal to the walls of such circular trenches, resulting in membrane iris-shaped structures having the shapes of open truncated cones.
[0045] The term "cone" includes the right circular cone with a circular base or directrix as well as structures having a curved (open or closed curve) or polygonal base or directrix to form pyramidal type structures with irregular or trapezoidal faces extending toward a common vertex. Thus, "cone" includes any structure having a surface generated by a straight line passing though a fixed point and moving along the intersection with a fixed curve.
[0046] Figure 6H is a schematic illustration of the cone shaped nanotube structures. The template structure 1 2 on the substrate 1 0 contains an inclined side surface 1 6 and a flat upper surface. The inclined surface 1 6 has an oblique inclination which is neither orthogonal nor parallel with respect to an upper plane of the substrate 1 0. The nanotubes 1 4 on the upper surface grow perpendicular to this surface of the template structure 1 2. The nanotubes 1 8 on the inclined side surface 1 6 of the template structure extend perpendicular to this surface 1 6 to form the cone shaped membrane.
[0047] The free standing membrane structures 1 8 made of aligned nanotubes created in the shapes of open truncated cones may have any desired size. The width of the membrane or the size of the opening can be controlled by the pattern diameter, the angle of trench wall and the time of growth. Typical examples of different diameter, cone angle, size
of opening of the nanotube membrane are shown in Figures 6A-F. The diameter of the pattern structures are 300, 250, 200, 1 50, 1 00 and 50 microns, respectively. Figure 6G shows an enlarged view of the 1 00 μm diameter structure in Figure 6E to demonstrate the geometry of the nanotube membrane in this 3-D architecture.
[0048] This cone shaped membrane is formed the same way as the previous nanotube structures. The nanotube source gas is provided onto the template structure 1 2 and the carbon nanotubes 1 8 are selectively grown on the inclined surface 1 6 of the template structure but not on exposed portions of the substrate 1 0, such that the grown carbon nanotubes comprise a membrane having an open truncated cone shape. The nanotubes 1 4 may also be grown on the upper surface of the template structure 1 2 or the upper surface of the template structure may be masked, as will be described below, to form only the nanotube membrane 1 8 on the template structure 1 2.
[0049] Figures 6A-G also show the flexibility of the method of the fourth embodiment to obtain radially oriented nanotubes with the entire spectrum of in-plane orientations relative to the substrate plane. The present inventors produced structures with different diameter, cone angle, size of opening and film thickness by tailoring the pattern dimensions, and growth time to control nanotube length. Similarly, complex shapes of nanotube structures can be generated by altering the trench geometry and depth.
[0050] The method and structure of the fifth preferred embodiment will now be described. In the fifth embodiment, a masking layer or material is formed on a portion of the template structure to selectively grow nanotubes only on an exposed portion of the template structure. A masking layer is a layer which inhibits growth of nanotubes on the
template structure. For example, a 2 to 20-nm-thick gold layer can be used as a masking material for silica template structures. Other examples of masking materials include polysilicon, copper, or any other material that does not catalyze nanotube growth. The masking material preferably has a thickness at which it forms a continuous layer. Thus, in a preferred aspect of the fifth embodiment, a template structure is located on the substrate. A masking material covers a first portion of the template structure. A plurality of carbon nanotubes are located on a second portion of the template structure not covered by the masking material. The carbon nanotubes are not located on the masking material or on exposed portions of the substrate. Preferably, a plurality of template structures are located on the substrate.
[0051 ] The method of the fifth preferred embodiment includes providing substrate containing a template structure having at least a portion covered by a masking material and providing a nanotube source gas onto the template structure. The method also includes selectively growing the carbon nanotubes on an exposed portion of the template structure but not on exposed portions of the substrate and not on portions of the template structure covered by the masking material.
[0052] The method provides selective growth of nanotube bundles in controlled directions parallel to the substrate surface, by inhibiting nanotube growth from certain template structure portions or surfaces, such as the upper and/or some of the side surfaces. The lengths of CNTs growing in different directions can be tuned by adjusting the masking material coverage and thickness respective template structure surfaces, the deposition time, and the SiO2 pattern spacing. This allows fabrication of arrays of low-electrical resistance nanotube-metal contact structures that could be used to create nanotube-based electrical devices.
[0053] Figures 7A and 7B are schematic illustrations of a method of forming the masking material on the template structures. As shown in Figure 7A, silicon ridges 1 1 were photolithographically formed on a silicon substrate 1 0. The substrate 10 and the ridges 1 1 were covered with a thermally grown SiO2 layer to form thermally-oxidized SiO2 template structures 1 2. Other suitable methods to form the template structures may be used if desired. For example, a CVD SiO2 layer may be patterned into template structures, as in the first embodiment.
[0054] Figure 7B illustrates selective deposition of the gold masking layer on some surfaces of the template structure 1 2. The substrate 1 0 containing the template structures 1 2 was placed into a sputtering apparatus containing a sputtering target 20 and was tilted at 1 5 to 40 degrees, such as at 20 degrees relative to the target 20. A gold masking layer was then selectively sputtered onto the upper surfaces 22 and the left side surfaces 24 of the template structures. The right side surfaces 26 of the template structures were not covered by the masking layer. In the specific example of forming a gold masking layer, a gold layer was sputtered onto SiO2 covered Si substrates in a 50 mTorr Ar plasma at an anode voltage of 7 V and a current of 25 mA, leading to an average deposition rate of about 1 nm s"1. Inside the sputter chamber, the substrates with SiO2 patterns were placed in a near-vertical configuration, at a tilt angle of about 20 degrees, with a sample-cathode distance of 30 mm. This sample placement geometry results in Au coverage on the top surface and one sidewall of each SiO2 template structure that faces the Au flux, while the opposite sidewall is protected from Au coverage. Rutherford Backscattering Spectrometry (RBS) measurements carried out using a 2 MeV He + + probe beam show that SiO2 surfaces are covered with 1 .1 x 1 017 atoms/cm2 of Au (nominal thickness of about 20 nm) when exposed to the Au sputter-flux for 20 seconds.
[0055] Of course, other masking layer fabrication methods may be used instead. For example, the masking layer may be deposited by evaporation, sputtering, CVD or plating on the entire surface of the substrate and the template structures. The masking layer may then be photolithographically patterned to cover only the desired portions of the template structures 1 2. Alternatively the masking layer can be deposited only at desired locations by using a shadow mask, or through lift-off lithography techniques.
[0056] The Au-coated SiO2 template structures were placed into a
CVD tube furnace to grow carbon nanotubes selectively on exposed SiO2 surfaces using a xylenes-ferrocene mixture. Substrates without Au coating were also loaded in the CVD furnace. A solution of 0.4 g ferrocene dissolved in 40 ml xylenes was fed into the CVD furnace at temperatures between 600 to 1 1 00 °C for time intervals ranging from 5 to 30 minutes. This method produced aligned nanotubes, which were typically multiwalled nanotubes with diameters of about 20 to 50 nm.
[0057] Figures 8A-8B illustrate the growth behavior of carbon nanotubes (CNTs) on SiO2 template structures that were not coated with Au before CVD. Figure 8A illustrates star-like growth of aligned CNTs on a row of SiO2 template structures without Au coverage. The inset shows a schematic sketch of the morphology. Figure 8B is a high magnification view of Figure 8A showing the CNT-CNT interface (see arrow) between SiO2 patterns. The nanotubes grow from all five surfaces of these template structure, i.e., the upper surface and four side surfaces, forming a star-like structure. The CNTs in each direction are well aligned, and have the same length of about 25 microns. CNTs growing in opposite directions, towards each other between patterns, cease to grow when they meet each other and form CNT-CNT interfaces as shown in Figure 8B.
[0058] In contrast, Figures 8C-F illustrate selective CVD in-plane growth of aligned CNT bundles on exposed portions of template structures whose remaining portions were covered by a masking material. The selective growth is clearly in Figure 8C, which shows 50 micron long CNT bridges grown from the left sidewalls of SiO2 template structures whose upper and right sidewall surfaces were coated with Au. The CNTs form continuous nanotube bridges across a row of template structures.
[0059] The CNTs grow straight, in a direction perpendicular to the silica surface seeding them, until they arrive at the next template structure, as shown in Figure 8D. The CNT growth terminates abruptly when the nanotube tips reach the Au masking material covered sidewall of the next template structure, which serves as a barrier to further growth. This feature is illustrated in Figure 8E. Figure 8E is a close-up view of the rectangular box in Figure 8D, and shows a sharp interface between CNT tips and the template structure sidewall covered by Au where CNT growth stops. The inset in Figure 8E is a schematic illustration of the side-view of this interface. Thus, when the masking material is a metal, a metal-nanotube contact structure is formed where the carbon nanotubes contact the metal masking material. Horizontal arrows in Figures 8C, D, E and F indicate the CNT growth direction.
[0060] The process of selectively coating Au on different SiO2 surfaces can be harnessed to controllably grow CNTs along any sets of in- plane directions. For example, the nanotube growth direction was reversed by coating Au on the upper surface and left sidewall of each template structure, as shown in Figure 8F, compared to the direction shown in Figure 8B.
[0061] The CNT length is solely controlled by deposition time in the absence of physical obstacles in the growth direction. The CNTs grown
from the last template structure in Figure 8F are about 80 microns long, while those grown between template structures are only 50 microns long, identical to the inter structure distance or spacing. This is a useful attribute in order to simultaneously bridge patterns with different inter- pattern distances by a single CVD process, where the growth time can be chosen to allow CNTs to bridge the longest inter structure gaps. Thus, nanotube bridges may be formed between different template structures in a single step even when a distance or spacing between a first and a second template structure differs from a distance or spacing between a second and a third template structure. The nanotube bridges which connect the first template structure to a second template structure differ in length from those which connect the second template structure to the third template structure. These nanotube bridges extend parallel to a surface of the substrate.
[0062] Thus, the nanotube source gas is provided for a sufficient time to allow the carbon nanotubes growing on the exposed portions of a one template structure to contact the masking material covering the covered portion of an adjacent template structure to form a nanotube bridge between these template structures. Furthermore, the nanotube source gas is provided for a sufficient time to simultaneously grow carbon nanotubes of a different length to allow the carbon nanotubes growing on the exposed portions of template structures to contact the masking material covering the covered portions of adjacent template structures. Thus, the growth time is selected to allow the nanotubes to bridge the longest desired structure spacing or distance. Thus, by varying the growth time of nanotubes on an array of differently spaced template structures, only the template structures with the desired maximum inter structure spacing are connected by the bridges.
[0063] Figures 8B and 8F also show that CNTs grown on the two side-walls of SiO2 patterns indicated by two tilted arrows in Figure 8F are curled and shorter compared to the straight nanotube bundles between patterns. This result suggests that a lower Au coverage due to line-of- sight Au deposition on these SiO2 surfaces leads to short nanotubes with less alignment.
[0064] In order to examine this correlation, the present inventors measured the length of CNTs grown on SiO2 surfaces with different Au coverages. The Au coverages were measured by RBS and varied between 0 and 1 .1 x 1 017 atoms/cm2.
[0065] Figure 9A is a plot of CNT length as a function of Au coverage on SiO2. The nominal Au film thickness is also shown on the top axis. For all the cases, CVD conditions were identical and the reaction time was 30 min. Figure 9B is an SEM image of Au islands (white contrast) on SiO2 surface. Figure 9C is an SEM image of CNTs grown from the two sidewalls of a template structure with different lengths, 40 microns leftward from a SiO2 surface partially covered by Au and 1 00 microns downward from a surface not covered by Au during the same deposition step.
[0066] The plot in Figure 9A shows that CNT lengths decrease monotonically with increasing Au-atom coverage, and no nanotube growth is observed for Au coverages above 1 .1 x 1 017 atoms/cm2 (nominal Au thickness of about 20 nm). While present inventors do not want to be bound by any particular theory, they propose that the nanotube length decreases with increasing masking layer thickness according to the following mechanism. For Au coverages less than about 1 .1 x 1 017 atoms/cm2, the as-deposited Au layer on SiO2 is discontinuous and has an island morphology, as shown in Figure 9B. It is assumed that
the Au islands decrease the intake and interactions of carbon/catalyst flux with SiO2, and alter the nanotube growth rate. At higher coverages, the Au layer is continuous and masks the entire SiO2 surface, thus completely preventing CNT growth. The CNT length-dependence on the Au-coverage is useful for obtaining CNTs of tunable lengths along different directions through control of Au coverage on different faces of SiO2 patterns, as shown in Figure 9C.
[0067] Thus, in a method of a preferred aspect of the fifth embodiment, a first material which facilitates growth of carbon nanotubes, such as a silica or other suitable material layer or structure is provided. At least a portion of the first material is covered with a masking material, such as Au or another material which inhibits CNT growth. A nanotube source gas is provided onto the first material. The carbon nanotubes of a first length are selectively grown on an exposed portion of the first material. If the masking material is thicker than a critical thickness at which it comprises a continuous layer (e.g., Au layer with nominal thickness of greater than about 20 nm), then no CNTs are grown on the masking material. If the masking material is thinner than a critical thickness at which it comprises a continuous layer (i.e., such as an about 20 nm or thinner Au layer), then shorter CNTs of a second length less than the first length are growth on the masking material. Thus, if plurality of different masking materials and/or a plurality of masking material portions of different thickness are formed over the first material, then a plurality of CNTs with different lengths may be grown in the same growth step.
[0068] Therefore, by varying the masking material thickness and/or type and/or by varying the spacing the template structure spacing, a plurality of CNTs of different length may be controllably grown during the same deposition step. The growth method includes providing a growth
surface which facilitates growth of carbon nanotubes, providing a nanotube source gas onto the growth surface, and controllably growing the carbon nanotubes of different length during the same deposition step.
[0069] The present inventors carried out electrical resistance measurements with a two-point probe on Au-coated Si02 template structures with and without CNT bridges to explore their use in meso- scale circuits. Figure 10A is a schematic sketch of configuration used to measure the electrical resistance. The unbridged sample was prepared using a short CVD time so that CNTs did not grow long enough to connect adjacent SiO2 template structure. Two bridged samples were also prepared. During the measurements, one probe was fixed at Po, while another probe was moved to different locations from Pi , to P10, to record the resistances across different number of CNT bridges. Figure 1 0B is a plot of resistance as a function of number of CNT bridges. Circles and squares show the resistance behavior for structures with CNT bridges, while triangles show data obtained from unbridged structures. Runbridgβ is due to the Au layer sputtered on the substrate area between SiO2 patterns.
[0070] For all three samples, the resistance increases linearly with the number of patterns. The circuit contact resistance between the probe and the Au layer on top of SiO2 patterns ( = 2RProbe-Au), obtained from the ordinate intercept of each plot, is also nearly constant at about 200-300 ohms for all samples. However, the average resistance between two adjacent patterns, denoted by the slope of the plots, is more than a factor of two smaller for patterns bridged by CNTs (Rbridged = 54 ± 2 Ω) compared with that of the unbridged patterns (Runbπ ged = 1 20 Ω). This result indicates that the CNT bridges provide a low-resistance electronic transport pathway between the SiO2 patterns. The low resistance of the pattern-CNT-pattern units in the prepared samples is consistent with the
good contact between CNT tips and Au layers observed in Figure 8E, and the well-graphitized multi-walled tube structures.
[0071 ] The fifth preferred embodiment provides in-plane growth of
CNTs in predefined directions and with tunable lengths by selective masking of SiO2 template structures with a metal that does not catalyze nanotube growth compared to silica. This method can be used to create nanotube bridges that interconnect SiO2 patterns and provide low- resistance pathways for electrical transport. The methods which combine CVD with topographical masking of patterned substrates may be used for controllably growing nanotube-metal architectures for electronic switching, memory storage, sensing and actuation devices.
[0072] The method and structure of the sixth preferred embodiment will now be described. A structure of the sixth preferred embodiment includes at least one suspended template material layer. A first aligned carbon nanotube layer is located on a first surface of the template material layer. A second aligned carbon nanotube layer is located on a second surface of the template material layer, located opposite to the first surface. Thus, a bilayer of aligned carbon nanotubes contains a suspended template layer between them. The nanotubes extend away from the respective surface of the template layer. If desired, three or more layers of aligned carbon nanotubes may be formed on two or more template layers.
[0073] The suspended template material layer may be a template material cantilever or membrane supported on a portion of a substrate that does not catalyze carbon nanotube growth. If the template layer has sufficient thickness, then a third aligned carbon nanotube layer is located on an edge surface of the template material layer, such that the third
aligned carbon nanotube layer is located perpendicular to the first and the second aligned carbon nanotube layers.
[0074] Figure 1 1 A illustrates a low magnification SEM image showing a bilayer of aligned carbon nanotubes grown at a 1 80 degree angle with respect to each other (up and down) from the top and bottom surfaces of a suspended, circular SiO2 cantilever layer suspended on a Si base pillar. Any other suitable suspended template material and substrate/base may also be used. If desired, the template layer may comprise a membrane (i.e., a suspended layer supported on two or more sides or on two or more portions of a surface) rather than a cantilever (i.e., a suspended layer supported on one side or on one portion of a surface). The template layer may also contain both edge cantilever portions and a central membrane portion, if desired.
[0075] The two growth directions from the SiO2 surfaces (inset) and a schematic illustration of nanotube bilayer growth are shown in Figure 1 1 B. The SiO2 layer (transparent) is located on the silicon base pillar (opaque), as illustrated in Figures 1 1 B and 1 1 C. This pattern of suspended SiO2 templates with two exposed surfaces was generated by undercutting the silica layer located on a silicon substrate into the substrate during deep etching of about 40-50 microns. The template layer in Figures 1 1 A-B does not have sufficient thickness to grow nanotubes on its edge surface. The nanotube growth directions are shown by the arrows in Figure 1 1 C.
[0076] Figures 1 2A-B are schematic sketches showing simultaneous multilayer and multidirectional growth of oriented nanotubes from thick (e.g., 2 microns or more) SiO2 layer suspended on deep etched Si pillars. Figure 1 2A is a schematic of a silicon substrate with a thick cantilever SiO2 layer suspended on a Si base before nanotube deposition. Figure
1 2B is a schematic of the nanotube growth on the suspended SiO2 layer in three orientations. Since the silica layer is sufficiently thick, a nanotube layer growth from the edge surface of the suspended silica layer. Figure 1 2C is an SEM micrograph showing the aligned nanotubes extending in three directions marked by arrows. Thus, as shown in Figures 1 1 and 1 2, the nanotubes may extend from a suspended template layer toward an upper surface of the substrate at a 90 degree angle. However, the nanotubes may extend towards the substrate at any suitable angle, such as at a 30-1 60 degree angle, depending on the orientation of the template layer.
[0077] Simultaneous multidirectional growth of highly oriented nanotubes with tunable lengths of the preferred embodiments allows formation of complex three dimensional CNT networks, where vertically and horizontally aligned nanotube arrays enable the construction of hierarchical multilevel architectures. Specifically, the nanotube networks may be used in diverse applications such as nanotube-based electronic devices, micro and nano-electromechanical systems, micro- and nano-size porous supports and membranes for catalysis, fluidics and separation, and skeletal reinforcements for composites.
[0078] The present inventors have achieved excellent control and flexibility in designing and fabricating a wide variety of carbon nanotube architectures, as discussed in the preferred embodiments. Several ordered nanotube based structural elements of different orientations may be integrated onto one substrate by combining standard lithography techniques with a substrate-selective CNT CVD growth process effected by gas-phase delivery of catalysts. Structures such as micro-fibers and membranes containing highly aligned nanotubes can fabricated and could find use in nanocomposites and electrode systems. The fabrication method described here is far easier and more versatile than the prior art
methods. The preferred method does not require a metal catalyst patterning step, thus simplifying the method to a great degree and providing better control, particularly for the catalyst particle size, for the growth process. The preferred method is also scalable over large areas for commercial production with the aid of fabrication techniques commonly used in silicon microfabrication technology.
[0079] The foregoing description of the invention has been presented for purposes of illustration and description. It is not intended to be exhaustive or to limit the invention to the precise form disclosed, and modifications and variations are possible in light of the above teachings or may be acquired from practice of the invention. The description was chosen in order to explain the principles of the invention and its practical application. It is intended that the scope of the invention be defined by the claims appended hereto, and their equivalents.