WO2003093006A1 - Fluorescent articles having multiple film layers - Google Patents
Fluorescent articles having multiple film layers Download PDFInfo
- Publication number
- WO2003093006A1 WO2003093006A1 PCT/US2003/010841 US0310841W WO03093006A1 WO 2003093006 A1 WO2003093006 A1 WO 2003093006A1 US 0310841 W US0310841 W US 0310841W WO 03093006 A1 WO03093006 A1 WO 03093006A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- article
- film
- fluorescent
- overlayer
- underlayer
- Prior art date
Abstract
Description
Claims