WO2004052942A1 - Cationic or amphoteric copolymers prepared in an inverse emulsion matrix and their use in preparing cellulosic fiber compositions - Google Patents
Cationic or amphoteric copolymers prepared in an inverse emulsion matrix and their use in preparing cellulosic fiber compositions Download PDFInfo
- Publication number
- WO2004052942A1 WO2004052942A1 PCT/US2003/039034 US0339034W WO2004052942A1 WO 2004052942 A1 WO2004052942 A1 WO 2004052942A1 US 0339034 W US0339034 W US 0339034W WO 2004052942 A1 WO2004052942 A1 WO 2004052942A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- composition
- document
- water
- acid
- cationic
- Prior art date
Abstract
Description
Claims