WO2004065508A2 - Adhesive additives and adhesive compositions containing an adhesive additive - Google Patents
Adhesive additives and adhesive compositions containing an adhesive additive Download PDFInfo
- Publication number
- WO2004065508A2 WO2004065508A2 PCT/US2004/001383 US2004001383W WO2004065508A2 WO 2004065508 A2 WO2004065508 A2 WO 2004065508A2 US 2004001383 W US2004001383 W US 2004001383W WO 2004065508 A2 WO2004065508 A2 WO 2004065508A2
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- adhesive
- castor oil
- oil
- weight ratio
- additive
- Prior art date
Abstract
Description
Claims