WO2004114326A1 - Process for preparing electroconductive coatings - Google Patents

Process for preparing electroconductive coatings Download PDF

Info

Publication number
WO2004114326A1
WO2004114326A1 PCT/EP2004/051073 EP2004051073W WO2004114326A1 WO 2004114326 A1 WO2004114326 A1 WO 2004114326A1 EP 2004051073 W EP2004051073 W EP 2004051073W WO 2004114326 A1 WO2004114326 A1 WO 2004114326A1
Authority
WO
WIPO (PCT)
Prior art keywords
group
latex
compound
reaction medium
units
Prior art date
Application number
PCT/EP2004/051073
Other languages
French (fr)
Inventor
Frank Louwet
Etienne Van Thillo
Bert Groenendaal
Original Assignee
Agfa-Gevaert
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Agfa-Gevaert filed Critical Agfa-Gevaert
Priority to JP2006516142A priority Critical patent/JP2007526925A/en
Priority to EP04741766A priority patent/EP1639607A1/en
Priority to CN200480023731A priority patent/CN100594560C/en
Publication of WO2004114326A1 publication Critical patent/WO2004114326A1/en

Abstract

An aqueous dispersion of latex particles, said latex particles containing a polymer containing monomer units according to formula (I), in which R1 and R2 independently of one another represent hydrogen or a C1-5-alkyl group or together form an optionally substituted C1-5-alkylene residue and at least one polyanion compound, said latex having a primary particle size of less than 40 nm and said dispersion contains an organic compound containing a di­or polyhydroxy- and/or carboxy groups or amide or lactam group or an aprotic compound with a dielectric constant, ϵ, ≥ 15, characterized in that said latex particles contain said at least one polyanion compound and said polymer in a weight ratio of at least 4; a process for preparing an electroconductive coating comprising the steps of: preparing an aqueous solution or dispersion of the abovementioned polymer by polymerization with an initiator in a reaction medium in the presence of at least one polyanion compound under oxidizing or reducing conditions.

Description

PROCESS FOR PREPARING E ECTROCONDϋCTIVE COATINGS
Field of the invention
The present invention relates to a process for preparing electroconductive coatings .
Background of the invention.
Polythiophenes have been studied extensively due to their interesting electrical and/or optical properties. Polythiophenes become electrically conducting upon chemical or electrochemical oxidation or reduction. Their ultimately achievable electrical conductivity is determined by their chemical composition, the stereoregularity of the polymerization of the thiophene monomers in the polythiophene chain and by their π-conjuga ion lengths. Such stereoregularity problems do not arise when unsubstituted thiophenes or thiophenes substituted in the 3- and 4-positions with identical groups are polymerized. . :
EP-A 339 340 discloses a polythiophene containing structural units of the formula:
Figure imgf000002_0001
in which A denotes an optionally substituted Cl-C4-alkylene radical and its preparation by oxidative polymerization of the corresponding thiophene.
EP-A 440 957 discloses dispersions of polythiophenes, constructed from structural units of formula (I) :
Figure imgf000002_0002
in which R1 and R2 independently of one another represent hydrogen or a C1-C4 alkyl group or together form an optionally substituted Cl-C4-alkylene residue, in the presence of a polyanion compound and specifically discloses in Examples the polymerization of 3,4- ethylenedioxythiophene [EDOT] in the presence of poly(styrene sulphonic acid) at a weight ratio of 1:1.29 (Example 2), 1:2.2 (Examples 7 and 8), 1:4 (Examples 1, 3, 4 and 10), 1:6 (Example 5) and 1:8.33 (Example 6) in water.
In 2001, Elschner et al. at ASIA DISPLAY/IDW'Ol held at Nagayo in Japan in October 2001 in paper OEL3-3 disclosed high resistivity PEDOT/PSS for reduced crosstalk in passive matrix OE ' s and presented characteristic data of standard BAYTRON™ P and BAYTRON™ P types AI4083 and CH8000, reproduced below:
Figure imgf000003_0001
Elschner et al. further report that the conductivity decreased by several orders of magnitude relative to standard BAYTRON™ P just be shifting the centre of the particle size distribution from about 100 nm to 20 nm, while noting that the sizes of gel particles are taken in their aqueous swollen state and are of smaller size after dehydration. BAYER' s current commercial literature gives the following characteristics for these three BAYTRON™ P grades:
Figure imgf000003_0002
Aqueous dispersions of PEDOT/PSS are commercially available from BAYER as BAYTRON™ P. The molar ratio in standard BAYTRON™ P analyzed by 13C NMR analysis, as described in 2002 by P. Adriaensens et al. in Polymer, volume 43, pages 7003 to 7006, was found to be' 2.7 (= weight ratio of 3.50) and that in standard aqueous dispersions of PEDOT/PSS commercialized by AGFA-GEVAERT N.V. was found to be 2.1 (= weight ratio of 2.72). Table 1 :
Figure imgf000004_0002
In 1999, M. Lefebvre et al . in Chem. Materials, volume 11, pages 262-268, reported that the electrical conductivity of
PEDOT/PSS prepared from aqueous and acetonitrile (AN) solutions of EDOT and NaPPS with PSS to PEDOT ratios ranging from 0.24 to 3.33 increased with decreasing PSS: PEDOT ratio as would be intuitively expected by one skilled in the art, due to the higher concentration of the intrinsically conductive component PEDOT.
Figure imgf000004_0003
EP-A-686 662 discloses mixtures of A) neutral polythiophenes with the repeating structural unit of formula (I) ,
Figure imgf000004_0001
in which R1 and R2 independently of one another represent hydrogen or a C1-C4 alkyl group or together represent an optionally substituted C1-C4 alkylene residue, preferably an optionally with alkyl group substituted methylene, an optionally with Cl-C12-alkyl or phenyl group substituted 1,2-ethylene residue or a 1,2- cyclohexene residue, and B) a di- or polyhydroxy- and/or carboxy groups or amide or lactam group containing organic compound; and conductive coatings therefrom which are tempered to increase their resistance preferably to < 300 ohm/square. Furthermore, the examples in EP-A 686 662 disclose the polymerization of EDOT in the presence of poly(styrene sulphonic acid) at a weight ratio of 1:3.57 in water.
WO 03/001299A discloses a material for making an electroconductive pattern, said material comprising a support and a light-exposure differentiable element, characterized in that said light-exposure differentiable element comprises an outermost layer containing a polyanion and a polymer or copolymer of a substituted or unsubstituted thiophene, and optionally a second layer contiguous with said outermost layer; and wherein said outermost layer and/or said optional second layer contains a light-sensitive component capable upon exposure of changing the removability of the exposed parts of said outermost layer relative to the unexposed parts of said outermost layer. WO 03/001299A further discloses that conductivity enhancement refers to a process in which the conductivity is enhanced e.g. by contact with high boiling point liquids such as di- or polyhydroxy- and/or carboxy groups or amide or lactam group containing organic compound optionally followed by heating at elevated temperature, preferably between 100 and 250 °C, during preferably 1 to 90 seconds, results in conductivity increase. Alternatively in the case of aprotic compounds with a dielectric constant > 15, e.g. N-methyl-pyrrolidinone, temperatures below 100°C can be used. Such conductivity enhancement is observed with polythiophenes and can take place during the preparation of the outermost layer or subsequently. Particularly preferred liquids for such treatment are N-methyl-pyrrolidinone and diethylene glycol such as disclosed in EP-A 686 662 and EP-A 1 003 179. The PEDOT/PSS dispersion used in all the EXAMPLES of WO 03/001299A had a PEDOT: PSS weight ratio of 1:2.4 and had a narrow particle size distribution determined by CPS disc centrifuge measurements with a maximum at 25 nm and an average particle size of 30-50 nm. EP-A 1 003 179 discloses a method for producing a polymeric conductive layer on an object comprising the steps of: providing an aqueous composition containing a polythiophene, a polyanion compound and an aprotic compound with a dielectric constant, ε, > 15; applying said composition to said object forming a layer; and drying said layer to form a conductive polymeric layer on said object, characterized in that said object and said layer are kept at a temperature below 100°C and said conductive polymeric layer has a resistivity of at most 2 kΩ/square. Furthermore, the examples in EP 1 003 179 disclose the polymerization of EDOT in the presence of poly(styrene sulphonic acid) at a weight ratio of 1:2.46 in water.
Furthermore, in 2002 Kim et al . in Proceedings of SPIE, volume 4464, pages 85-92, reported a dramatic increase in conductivity of PEDOT/PSS without losing optical transparency by addition of a small amount of a polyalcohol, e.g. glycerol, in which BAYTRON™ P with a mean particle size in the range of 25nm-75nm was used as the starting material and Pettersson et al. in Organic Electronics, volume 3, pages 143-148, reported an increase in conductivity of PEDOT/PSS without losing transparency by addition of sorbitol in which the starting material was also BAYTRON™ P i.e. a weight ratio of PEDOT: PSS of 1:2.5.
A general drawback of conductive polymers which have been prepared and studied up to now, is that their conductivities are still too low for certain applications, their visible light transmittances are insufficiently high and/or they are not processable.
Objects of the invention.
It is therefore an aspect of the present invention to provide 3, 4-alkylenedioxy-thiophenes which upon polymerization provide poly(3,4-alkylenedioxy-thiophene)s, which upon oxidation or reduction exhibit high electrical conductivities, high visible light transmittances and/or good processability.
Further aspects and advantages of the invention will become apparent from the description hereinafter.
Summary of the invention
In unpublished European applicant nr. EP01000780 it was disclosed that the surface resistance of layers containing PEDOT/PSS decreased with decreasing oxygen concentration in the reaction medium with an optimum surface resistance being observed for PEDOT/PSS dispersions produced in a reaction medium containing less than 3 mg of oxygen/L of the reaction medium. Therefore, when investigating the influence of the preparation of PSS/PEDOT latexes upon the properties of layers prepared with such latexes, it is important to use PSS/PEDOT latexes prepared in reaction media containing similar concentrations of oxygen. Surprisingly it has been found that, at variance with the reports of M. Lefebvre et al. in 1999 in Chem. Materials, volume 11, pages 262-268, and Elschner et al. in 2001 at ASIA DISPLAY/IDW'01 held at Nagayo in Japan in October 2001 in paper OEL3-3, which reported a decrease in electrical conductivity with increasing PSS: PEDOT ratio, the surface resistance of layers prepared with aqueous dispersions of PEDOT/PSS latexes prepared in the presence of a particular concentration of oxygen in the reaction medium was found to decrease with increasing PSS: PEDOT ratio if particular additives, e.g. N-methyl-pyrrolidinone and polyhydroxy compounds such as diethylene glycol, were present in the dispersion. Although it is known from EP-A 0 686 662 and EP-A 1 003 179 that such additives enhance the conductivity of layers containing PSS/PEDOT latexes when layers are heated, it is totally unexpected that the conductivity enhancement will be greater for higher PSS/PEDOT ratios i.e. for lower concentrations of PEDOT. Aspects of the present invention are realized by an aqueous dispersion of latex particles, said latex particles containing a polymer consisting of structural units including monomer units according to formula (I) :
Figure imgf000007_0001
1 2 in which R and R independently of one another represent hydrogen or a C_5~alkyl group or together form an optionally substituted C - 5-alkylene residue and at least one polyanion compound, said latex having a primary particle size of less than 40 nm and said dispersion contains an organic compound containing a di- or polyhydroxy- and/or carboxy groups or amide or lactam group or an aprotic compound with a dielectric constant, ε, > 15, characterized in that said latex particles contain said at least one polyanion compound and said polymer in a weight ratio of at least 4.
Aspects of the present invention are also realized by a process for preparing an electroconductive coating comprising the steps of: preparing an aqueous solution or dispersion of a polymer consisting of structural units including monomer units according to formula (I) :
Figure imgf000008_0001
by polymerization with an initiator in a reaction medium in the presence of at least one polyanion compound under oxidizing or reducing conditions, wherein the weight ratio of the at least one polyanion compound to said structural units during the reaction is in the range of 4:1 to 20:1; preparing a first coating composition containing said polymer associated with said at least one polyanion compound and an organic compound containing a di- or polyhydroxy- and/or carboxy groups or amide or lactam group in a aqueous or non- aqueous medium; coating said first coating composition on an object thereby producing a first layer; and heating said first layer at a temperature of at least 100 °C.
Aspects of the present invention are also realized by a process for preparing an electroconductive coating comprising the steps of: preparing an aqueous solution or dispersion of a polymer consisting of structural units including monomer units according to formula (I) :
Figure imgf000008_0002
by polymerization with an initiator in a reaction medium in the presence of at least one polyanion compound under oxidizing or reducing conditions, wherein the weight ratio of said at least one polyanion compound to said structural units during the reaction is in the range of 4:1 to 20:1; preparing a second coating composition containing said polymer associated with said at least one polyanion compound and an aprotic compound with a dielectric constant, ε, > 15 in an aqueous or non-aqueous medium; coating said second coating composition on an object thereby producing a second layer; and heating said second layer at a temperature of at least 50°C. Aspects of the present invention are also realized by a process for preparing an electroconductive coating comprising the steps of: preparing an aqueous solution or dispersion of a polymer containing structural units according to formula (I) :
Figure imgf000009_0001
by polymerization with an initiator in a reaction medium in the presence of polyanions under oxidizing or reducing conditions, wherein the molar ratio of said structural units according to formula (I) to anionic groups in the polyanion during the reaction is in the range of 4:1 to 10:1; preparing a first coating composition containing said polymer associated with said polyanions and an organic compound containing a di- or polyhydroxy- and/or carboxy groups or amide or lactam group in a aqueous or non-aqueous medium; coating said first coating composition on an object thereby producing a first layer; and heating said first layer at a temperature of at least 100 °C.
Aspects of the present invention are also realized by a process for preparing an electroconductive coating comprising the steps of: preparing an aqueous solution or dispersion of a polymer containing structural units according to formula (I) :
Figure imgf000009_0002
by polymerization with an initiator in a reaction medium in the presence of polyanions under oxidizing or reducing conditions, wherein the molar ratio of said structural units according to formula (I) to anionic groups in the polyanion during the reaction is in the range of 4:1 to 10:1; preparing a second coating composition containing said polymer associated with said polyanions and an aprotic compound with a dielectric constant, ε, > 15 in an aqueous or non-aqueous medium; coating said second coating composition on an object thereby producing a second layer; and heating said second layer at a temperature of at least 50°C.
Preferred embodiments of the present invention are disclosed in the detailed description of the invention.
Detailed description of the invention.
Definitions
It should be noted that as used in the specification and the appended claims, the singular forms "a" and "an" include plural references unless the context clearly dictates otherwise. Thus, for example, reference to "a thiophene according to formula (I) " includes more than one such thiophene, reference to polymerization of "a thiophene according to formula (I) " includes copolymerization of more than one such thiophene.
The term polymer includes homopolymers, copolymers, terpolymers, graft polymers and block copolymers and both chain and condensation polymers . The term Cι-5-alkylene group represents methylenedioxy, 1,2- ethylenedioxy, 1, 3-propylenedioxy, 1, 4-butylenedioxy and 1,5- pentylenedioxy groups .
The term initiator means a species capable of initiating polymerization . The term alkyl means all variants possible for each number of carbon atoms in the alkyl group i.e. for three carbon atoms: n- propyl and isopropyl; for four carbon atoms: n-butyl, isobutyl and tertiary-butyl; for five carbon atoms: n-pentyl, 1,1-dimethyl-- propyl, 2,2-dimethylpropyl and 2-methyl-butyl etc. The term aqueous medium for the purposes of the present invention means a liquid containing at least 60% by volume of water, preferably at least 80% by volume of water, and optionally containing water-miscible organic solvents such as alcohols e.g. methanol, ethanol, 2-propanol, butanol, iso-amyl alcohol, octanol, cetyl alcohol etc.; glycols e.g. ethylene glycol; glycerine; N- methyl pyrrolidinone; methoxypropanol; and ketones e.g. 2-propanone and 2-butanone etc. The term non-aqueous medium for the purposes of the present invention means all liquids not included in the term aqueous medium.
The term electroconductive means having a surface resistance below 10 Ω/square.
The term ^conductivity enhancement" refers to a process in which the conductivity is enhanced e.g. by contact with high boiling point liquids such as di- or polyhydroxy- and/or carboxy groups or amide or lactam group containing organic compound optionally followed by heating at elevated temperature, preferably between 100 and 250°C, during preferably 1 to 90 seconds, results in conductivity increase. Alternatively in the case of aprotic compounds with a dielectric constant > 15, e.g. N-methyl- pyrrolidinone, temperatures below 100°C can be used. Such conductivity enhancement is observed with polythiophenes and can take place during the preparation of the outermost layer or subsequently. Particularly preferred liquids for such treatment are N-methyl-pyrrolidinone and diethylene glycol such as disclosed in EP-A 0 686 662 and EP-A 1 003 179. PEDOT as used in the present disclosure represents poly (3,4- ethylenedioxythiophene) .
EDOT as used in the present disclosure represents 3,4- ethylenedioxythiophene .
ADOT as used in the present disclosure represents 3,4- alkylenedioxythiophene) .
PSS as used in the present disclosure represents poly (styrenesulphonic acid) or poly (styrenesulphonate) .
PET as used in the present disclosure represents poly (ethylene terephthalate) .
Aqueous dispersion of a latex
According to a first embodiment of an aqueous dispersion of a latex, according to the present invention, said latex has a primary particle size of less than 30 nm.
According to a second embodiment of an aqueous dispersion of a latex, according to the present invention, the weight ratio of said at least one polyanion compound to said polymer corresponds to the weight ratio of said structural units to said at least one polyanion compound during the preparation thereof.
According to a third embodiment of an aqueous dispersion of a latex, according to the present invention, said latex particles contain said at least one polyanion compound and said polymer in a weight ratio of greater than 4 and less than 20.
According to a fourth embodiment of the aqueous dispersion of a latex, according to the present invention, wherein said latex is prepared in a reaction medium with less than 8500 mg of oxygen/L of said reaction medium when the initiator is added.
According to a fifth embodiment of the aqueous dispersion of a latex, according to the present invention, wherein said latex is prepared in a reaction medium with less than 2000 mg of oxygen/L of said reaction medium when the initiator is added.
According to a sixth embodiment of the aqueous dispersion of a latex, according to the present invention, wherein said latex is prepared in a reaction medium with less than 1000 mg of oxygen/L of said reaction medium when the initiator is added. According to a seventh embodiment of the aqueous dispersion of a latex, according to the present invention, wherein said latex is prepared in a reaction medium with less than 500 mg of oxygen/L of said reaction medium when the initiator is added.
According to an eighth embodiment of the aqueous dispersion of a latex, according to the present invention, wherein said latex is prepared in a reaction medium with less than 100 mg of oxygen/L of said reaction medium when the initiator is added.
According to a ninth embodiment of the aqueous dispersion of a latex, according to the present invention, wherein said latex is prepared in a reaction medium with less than 3 mg of oxygen/L of said reaction medium when the initiator is added.
According to a tenth embodiment of the aqueous dispersion of a latex, according to the present invention, wherein said latex is prepared in a reaction medium with less than 1.5 mg of oxygen/L of said reaction medium when the initiator is added.
According to an eleventh embodiment of the aqueous dispersion of a latex, according to the present invention, wherein said latex is prepared in a reaction medium with less than 0.5 mg of oxygen/L of said reaction medium when the initiator is added. According to a twelfth embodiment of the aqueous dispersion of a latex, according to the present invention, the monomer units according to formula (I) are selected from the group consisting of optionally alkyl group-substituted 3, -methylenedioxy-thiophene units, optionally alkyl or aryl-group-substituted 3,4- ethylenedioxythiophene units, optionally alkyl or aryl-group- substituted 3,4-ethylenedioxythiophene units, a unit according to
1 2 formula (I) in which R and R are together a 1,2-cyclohexene group, optionally alkyl or aryl-group-substituted 3,4- propylenedioxythiophene units, optionally alkyl or aryl-group- substituted 3,4-butylenedioxythiophene units and optionally alkyl or aryl-group-substituted 3, 4-pentylenedioxythiophene units. According to a thirteenth embodiment of the aqueous dispersion of a latex, according to the present invention, the polymer is a copolymer of at least one 3, -alkylenedioxythiophene compound with a solubility in water at 25 °C of less than 2.2 g/L with at least one 3, 4-alkylenedioxythiophene compound with a solubility in water at 25°C of at least 2.2 g/L.
According to a fourteenth embodiment of the aqueous dispersion of a latex, according to the present invention, the polymer is a copolymer of at least one 3, -alkylenedioxythiophene compound with a solubility in water at 25 °C of less than 2.2 g/L with at least one 3,4-alkylene-dioxythiophene compound with a solubility in water at 25°C of at least 2.2 g/L and the 3,4-alkylenedioxy-thioρhene compound with a solubility in water at 25CC of at least 2.2 g/L is selected from the group consisting of: 3, 4-dihydro-21f-thieno [3,4- b] [l,4]dioxin-2-yl)methanol, 3, 4-dihydro-2H-thieno [3,4- b] [1, 4] dioxepin-3-ol, (2, 3-dihydro-thieno [3, 4-i>] [1, 4]dioxin-2-yl- methoxy) -acetic acid ethyl ester, (2, 3-dihydro-thieno [3, 4- j ] [1,4] dioxin-2-yl-methoxy) -acetic acid, 2-{2- [2- (2-methoxy- ethoxy) -ethoxy] -ethoxymethyl } -2, 3-dihydro-thieno [3, 4-jb] [1,4] dioxine and 4- (2, 3-dihydro-thieno [3, 4 -b] [1, 4]dioxin-2-ylmethoxy) -butane-1- sulfonic acid sodium salt.
Process for preparing an aqueous solution or dispersion of a polymer containing monomer units according to formula (I)
A step in the processes, according to the present invention, is the preparation of an aqueous solution or dispersion of a polymer consisting of structural units including monomer units according to formula (I) :
Figure imgf000013_0001
by polymerization with an initiator in a reaction medium in the presence of at least one polyanion compound under oxidizing or reducing conditions, wherein the weight ratio of the at least one polyanion compound to the structural units during the reaction is in the range of 5:1 to 20:1.
According to a first embodiment of the processes, according to the present invention, the molar ratio of polymer or copolymer of (3, 4-dialkoxythiophene) to at least one polyanion compound in the solution or dispersion is in the range of 1:5 to 1:8.0.
According to a second embodiment of the processes, according to the present invention, said monomer units according to formula (I) are present in a concentration of 60 mM or less in said reaction medium.
The concentration of oxygen in the reaction medium can be regulated by any means e.g. freeze-thaw techniques, prolonged bubbling of an inert gas such as argon, nitrogen or helium through the reaction medium, consumption of oxygen in a sacrificial reaction under an inert gas blanket.
According to a third embodiment of the processes, according to the present invention, the inert atmosphere is a nitrogen, helium or argon atmosphere. The oxidation agents used for the oxidative polymerisation of pyrrole, such as described for example in Journal of the American Chemical Society, volume 85, pages 454-458 (1963) and J. Polymer Science Part A Polymer Chemistry, volume 26, pages 1287-1294 (1988) , can be utilized for the oxidative polymerization of thiophenes .
According to a fourth embodiment of the processes, according to the present invention, the polymerization is oxidative and the inexpensive and easily accessible oxidation agents used for initiating the polymerization are selected from the group consisting of iron (III) salts such as FeCl3, the iron (III) salts of organic acids, e.g. Fe(OTs)3, H2θ2, K2Cr2θ7, alkali and ammonium persulphates, alkali perborates and potassium permanganate.
Theoretically the oxidative polymerization of thiophenes requires 2.25 equivalents of oxidation agent per mole thiophene of formula (I) [see e.g. J. Polymer Science Part A Polymer Chemistry, volume 26, pages 1287-1294 (1988)]. In practice an excess of 0.1 to 2 equivalents of oxidation agent is used per polymerizable unit. The use of persulphates and iron (III) salts has the great technical advantage that they do not act corrosively. Furthermore, in the presence of particular additives oxidative polymerization of the thiophene compounds according to formula (I) proceeds so slowly that the thiophenes and oxidation agent can be brought together as a solution or paste and applied to the substrate to be treated. After application of such solutions or pastes the oxidative polymerization can be accelerated by heating the coated substrate as disclosed in US 6,001,281 and WO 00/14139 herein incorporated by 5 reference .
Reductive polymerization can be performed using the Stille (organotin) or Suzuki (organoboron) routes described in 2002 by Appperloo et al. in Chem. Eur. Journal, volume 8, pages 2384-2396, and as disclosed in 2001 in Tetrahedron Letters, volume 42, pages 10 155-157 and in 1998 in Macromolecules, volume 31, pages 2047-2056 respectively or with nickel complexes as disclosed in 1999 in Bull. Chem. Soc. Japan, volume 72, page 621 and in 1998 in Advanced Materials, volume 10, pages 93-116.
Polymers containing monomer units according to formula (I) may is also be prepared by chemically copolymerizing monomer units according to formula (I) with other poly erizable heterocyclic compounds such as pyrrole.
Oxygen measurements
20
The oxygen concentration can be measured with a Knick Process Unit 73 02, using InPro 6000 Series 02 sensors, available from Mettler Toledo. These sensors are based on a polarographic oxygen measurement. The Clark polarographic sensor consists basically of a
25 working electrode (cathode) , a counter/reference electrode (anode) , and an oxygen-permeable membrane that separates the electrodes from the medium. The transmitter supplies a constant polarization voltage to the cathode, needed to reduce oxygen. The oxygen molecules that migrate through the membrane are reduced at the
30 cathode. At the same time oxidation takes place at the anode and oxidized anode metal (silver) is liberated into the electrolyte. The electrolyte closes the electric circuit between the anode and the cathode (ion conductivity) . The current, produced in this way, is measured by the transmitter and is proportional to the partial 5 pressure of oxygen (02) in the sample medium.
The amount of oxygen in an aqueous 6wt% aqueous solution of pol (styrenesulphonic acid) determined via this technique is 6.5mg/L .
A poly (styrenesulphonic acid) solution at 25°C and 1013 mbar 0 saturated with oxygen by bubbling oxygen through it has an oxygen content of 38,45mg/L. This value may be regarded as the max solubility of oxygen in a poly (styrenesulphonic acid) solution at 25°C and 1013mbar.
Electrochemical polymerization of polymers containing monomer units according to formula (I)
Polymers containing monomer units according to formula (I) can be prepared by electrochemical polymerization. Electrochemical oxidative polymerization of thiophene compounds according to formula (I) carried out at temperatures from -78 °C to the boiling point of the solvent employed, temperatures between -20°C and 60°C is preferred. The reaction time, depending upon the particular thiophene, is generally between a few seconds and several hours. Electrochemical polymerization of thiophene compounds was described in 1994 by Dietrich et al. in Journal Electroanalytical Chemistry, volume 369, pages 87-92.
Inert liquids suitable for use during electrochemical oxidation of thiophene compounds according to formula (I) are: water, alcohols such as methanol and ethanol, ketones such as acetophenone, halogenated hydrocarbons such as methylene chloride, chloroform, tetrachloromethane and fluorohydrocarbons, esters such as ethyl acetate and butyl acetate, aromatic hydrocarbons such as benzene, toluene and xylene, aliphatic hydrocarbons such as pentane, hexane, heptane and cyclohexane, nitriles such as acetonitrile and benzonitrile, sulfoxides such as dimethylsulfoxide, sulfones such as dimethylsulfone, phenylmethylsulfone and sulfolan, liquid aliphatic amides such as methyl acetamide, dimethyl acetamide, dimethyl formamide, pyrrolidone, N-methyl-pyrrolidone, caprolactam, N-methyl- caprolactam, aliphatic and mixed aliphatic and aromatic ethers such as diethylether and anisole, liquid ureas such as tetramethylurea or N,N-dimethyl-imidazolidinone.
Electrolyte additives for use in the electrochemical polymerization of thiophene compounds according to formula (I) are preferably free acids or the usual conducting salts, which exhibit a certain solubility in the solvent used. Particularly suitable electrolytes are alkali, alkaline earth or optionally alkylated ammonium, phosphonium, sulfonium or oxonium cations in combination with perchlorate, tosylate, tetrafluoroborate or hexafluorophosphonate anions .
The electrolyte additives are used in such quantities, that a current of at least 0.1 mA flows during electrochemical oxidation. Electrochemical polymerization can be carried out continuously or discontinuously. Known electrode materials are ITO-covered glass, precious metal or steel mesh, carbon-filled polymers, evaporated metal-coated insulator layers and carbon felt . Current densities during electrochemical oxidation may vary within wide limits. According to an eighth embodiment of the present invention the current densities is 0.0001 to 100 mA/cm2. According to a ninth embodiment of the present invention the current density is 0.01 to 40 mA/cm2. At these current densities voltages of ca. 0.1 to 50 V are set up.
Polymers containing monomer units according to formula (I) may also be prepared by electroche ically copolymerizing monomer units according to formula (I) with other polymerizable heterocyclic compounds such as pyrrole .
Polyanion compound
The polyanion compounds for use in the dispersion according to the present invention are disclosed in EP-A 440 957 and include polymeric carboxylic acids, e.g. polyacrylic acids, polymethacrylic acids, or polymaleic acids and polysulphonic acids, e.g. poly(styrene sulphonic acid) . These polycarboxylic acids and polysulphonic acids can also be copolymers of vinylcarboxylic acids and vinylsulphonic acids with other polymerizable monomers, e.g. acrylic acid esters, methacrylic acid esters and styrene.
According to a sixteenth embodiment of the aqueous dispersion of a latex, according to the present invention, the at least one polyanion compound includes polystyrene sulphonic acid.
Industrial application
Chemically or electrochemically prepared polymers containing monomer units according to formula (I) exhibit high electrical conductivity together with low absorption of visible light and high absorption to infrared radiation. Therefore layers thereof are highly electrically conducting, highly transparent to visible light and heat shielding. Such polythiophenes can be applied to a wide variety of rigid and flexible substrates, e.g. ceramics, glass and plastics, and are particularly suitable for flexible substrates such as plastic sheeting and the substrates can be substantially bent and deformed without the polythiophene layer losing its electrical conductivity.
Such polythiophenes can therefore be utilized in photovoltaic devices, batteries, capacitors and organic and inorganic electroluminescent devices, in electromagnetic shielding layers, in heat shielding layers, in antistatic coatings for a wide variety of products including photographic film, thermographic recording materials and photothermographic recording materials, in smart windows, in electrochromic devices, in sensors for organic and bio- organic materials, in field effect transistors, in printing plates, in conductive resin adhesives and in free-standing electrically conductive films [see also chapter 10 of the Handbook of Oligo- and Polythiophenes, Edited by D. Fichou, Wiley-VCH, Weinheim (1999)].
The invention is illustrated hereinafter by way of comparative and invention examples . The percentages and ratios given in these examples are by weight unless otherwise indicated.
Subbing layer Nr. 01 used in the EXAMPLES has the composition:
Figure imgf000018_0001
PREPARATION OF 3, 4-ALKYLENEDIOXYTHIOPHENE-POLYMERS
EXAMPLES 1
The quantity of poly(styrene sulphonic acid) [PSS] (Mw=290,000) solution given in Table 2 was mixed with the quantity of deionized water given for the particular PEDOT-type in Table 2 at 25 °C in the appropriate reaction vessel equipped with a stirrer and a nitrogen inlet. After bubbling nitrogen through this mixture for 30 minutes, the quantity of EDOT for the particular PEDOT-type given in Table 2 was then added to this solution. The concentration of oxygen in this solution as measured with a Knick Process Unit 73 02, using InPro 6000 Series 02 is given in Table 2. The quantities of Fe2 (S04) 3.9H2O and a2S2θs corresponding to concentrations of 0.13 and 41.6 mM respectively were then added to initiate the polymerization reaction. The concentration of EDOT in the reaction mixtures was 30 mM and that of PSS was 57 mM. The reaction mixtures were then stirred at 25°C for 7h, after which a further quantity of a2S2θ8 for the particular PEDOT-type was added corresponding to a concentration of 6.95 mM. After an additional reaction time of 16h the reaction mixtures were treated twice with ion exchanger (300mL Lewatit™ S100MB + 500mL Lewatit™ M600MB) . The resulting mixtures were further thermally treated at 95°C for 2h and the resulting viscous mixture treated with high shear [microfluidizer at 60 MPa (600Bar)].
Table 2:
Figure imgf000019_0001
* 4.93 wt% aqueous PSS solution
# 4.68 wt% aqueous PSS solution
Preparing electroconductive layers of type 1 with dispersions based on the dispersions of EXAMPLE 1
Coating dispersions were produced by adding 3-glycidoxypropyl- trimethoxysilane, ZONYL® FSO100, a copolymer latex of vinylidene chloride, methacrylate and itaconic acid (88/10/2) and N-methyl pyrrolidinone to the dispersions of EXAMPLE 1 so as to produce layers of type 1, upon doctor blade-coating onto a subbed 175μm poly (ethylene terephthalate) support and drying at 45°C for 3.5 minutes, with the following composition:
PEDOT) /PSS 100 mg/m
[PEDOT 28.9mg/m2]
ZONYL® FSO100 8 mg/m2
3-glycidoxypropyl-trimethoxysilane lOOmg/m
2
Copolymer latex of vinylidene chloride, 100mg/m methacrylate and itaconic acid (88/10/2)
N-methyl pyrrolidinone 2mL/m
Characterization of electroconductive layers prepared with dispersions based on the dispersions of EXAMPLE 1
The optical density of the layers was determined by measuring a stack of 10 strips with a Macbeth® TD904 densitometer using a visible filter and then obtaining therefrom the optical density of a single strip. The values given in Table 3 include the optical density of the PET-support. The surface resistance of the layers was measured in a room conditioned to a temperature of 25°C and 30% relative humidity by contacting the printed layer with parallel copper electrodes each 35 mm long and 35 mm apart capable of forming line contacts, the electrodes being separated by a Teflon® insulator. This enabled a direct measurement of the surface resistance to be realized. The results are also summarized in Table 3.
Table 3:
Figure imgf000020_0001
The results in Table 3 show that the surface resistance of the PEDOT/PSS-layers with a molar PSS: PEDOT ratio of 1.90 strongly increased with increasing oxygen concentration in the reaction medium.
EXAMPLE 2
The quantity of poly(styrene sulphonic acid) [PSS] (Mw=290,000) solution given in Table 4 was mixed with the quantity of deionized water given for the particular PEDOT-type in Table 4 at 25 °C in the appropriate reaction vessel equipped with a stirrer and a nitrogen inlet. After bubbling nitrogen through this mixture for 30 minutes, the quantity of EDOT for the particular PEDOT-type given in Table 4 was then added to this solution. The concentration of oxygen in this solution was < 1. Omg/L as measured with a Knick Process Unit 73 02, using InPro 6000 Series 02. The quantities of Fe2 (S04) 3.9H20 and Na2S2θ8 corresponding to concentrations of 0.13 and 41.6 mM respectively were then added to initiate the polymerization reaction. The concentration of EDOT in the reaction mixtures was 30 mM and that of PSS was 57 mM. The reaction mixtures were then stirred at 25°C for 7h, after which a further quantity of Na2S20s for the particular PEDOT-type was added corresponding to a concentration of 6.95 mM. After an additional reaction time of 16h the reaction mixtures were treated twice with ion exchanger (300mL Lewatit™ S100MB + 500mL Lewatit™ M600MB) . The resulting mixtures were further thermally treated at 95°C for 2h and the resulting viscous mixture treated with high shear [microfluidizer at 60 MPa (600Bar)].
Table 4:
Figure imgf000021_0001
Preparation and characterization of electroconductive layers of type 1 with dispersions based on the dispersions of EXAMPLE 2 The electroconductive layers of type 1 with dispersions based on the dispersions of EXAMPLE 2 were prepared and characterized as described for the dispersions of EXAMPLE 1. The results are summarized in Table 5.
Table 5:
Figure imgf000022_0001
The results in Tables 3 and 5 taken together show that the initial surface resistance of the PEDOT/PSS-layers is strongly dependent upon the quantity of oxygen in the reaction medium during the polymerization of 3,4-ethylenedioxythiophene in the presence of poly (styrenesulphonic acid), the lower the concentration of oxygen in the reaction medium the lower the surface resistance.
EXAMPLE 3
The quantity of poly(styrene sulphonic acid) [PSS] (Mw=290,000) solution given in Table 6 was mixed with the quantity of deionized water given for the particular PEDOT-type in Table 6 at 25 °C in the appropriate reaction vessel equipped with a stirrer and a nitrogen inlet. After bubbling nitrogen through this mixture for 30 minutes, the quantity of EDOT for the particular PEDOT-type given in Table 7 was then added to this solution, giving a EDOT- concentration of 30 mM. The concentration of oxygen in this solution was < l.Omg/L as measured with a Knick Process Unit 73 O2, using InPro 6000 Series O2. The quantities of Fe2 (SO4) 3.9H2O and Na2S2θ8 corresponding to concentrations of 0.13 and 41.6 mM respectively were then added to initiate the polymerization reaction. The concentration of EDOT in the reaction mixtures was 30 mM and that of PSS is given for the particular PEDOT-type in Table 6.
Table 6:
PEDOT EDOT PSS Fe2(S0 )3. Na2S208 Na2S208 Water type weight weight of final con9H20 weight initially added weight
[g] 4.81 wt% centration [g] added [g] after [g] solution [g] [mM] 7h [g]
Figure imgf000023_0001
* same conditions as for PEDOT type 17 except that no thermal treatment at 95°c for 2h was carried out
# 4.90 wt% aqueous solution of PSS ** 4.93 wt% aqueous solution of PSS
The reaction mixtures were then stirred at 25°C for 7h, after which a further quantity of Na2S20s f°r the particular PEDOT- type was added corresponding to a concentration of 6.95 mM. After an additional reaction time of 16h the reaction mixtures were treated twice with ion exchanger (300mL Lewatit™ SIOOMB + 500mL Lewatit™ M600MB) . The resulting mixtures were further thermally treated at 95°C for 2h and the resulting viscous mixture treated with high shear [microfluidizer at 60 MPa (600Bar) ] . The resulting PSS: PEDOT weight and molar ratios,
PEDOT/PSS-concentrations, viscosity as measured in an Ubbelohde viscometer in a bath thermostatted at 25°C, the peak particle sizes in the bimodal size distribution and the number of particles per mL with a particle size greater than 1 μm are given in Table 7. Table 7 :
Figure imgf000024_0001
Aqueous gel permeation chromatography using UV-vis absorption detection was used to determine the relative quantity of PSS, bound or unbound, as the area of the peak at 254 nm, A254, and the relative quantity of bound PEDOT, otherwise no transport could take place and the PEDOT could not be detected, as the area of the peak at 785 nm, 85- A254/ 8 gives the relative molar quantity of PSS to the bound PEDOT. In order to obtain representative results it was necessary to microfluidize the dispersions at 60 MPa (600 bar) prior to running the GPC. If this was not done the PEDOT-peak was very small due to the agglomerated latex being unable to be transported through the column. The molecular weight of the PEDOT relative to sodium poly(styrene sulphonate) standards was determined at the same time. The results are summarized in Table 8.
The relative PSS/PEDOT ratio from GPC measurements is clearly correlatable with the actual molar ratio present, thereby indicating that the PSS is substantially bound to the PEDOT. Table 8 :
Figure imgf000025_0001
Preparation and characterization of electroconductive layers of type 1 with dispersions based on the dispersions of EXAMPLE 3
The electroconductive layers of type 1 with dispersions based on the dispersions of EXAMPLE 3 were prepared in which the quantities of ZONYL® FSO100, 3-glycidoxyproρryl- trimethoxysilane, copolymer latex and N-methylpyrrolidinone were held constant and the quantity of latex varied to yield a constant coverage of PEDOT [28.9 mg/m2. These layers were characterized as described for the dispersions of EXAMPLE 1 and the results are given in Table 9. The results in Table 9 surprisingly show that the surface resistance decreased with increasing PSS: PEDOT ratio for layers containing PEDOT/PSS produced in the substantial absence of oxygen, according to the present invention. This is at variance with the data available in the literature for PEDOT/PSS which shows that the surface resistance increases with increasing PSS: PEDOT ratio, see, for example, the paper published in 1999 by M. Lefebvre et al. in Chem. Mater., volume 11, pages 262-268, as mentioned above.
Table 9:
Figure imgf000025_0002
Figure imgf000026_0001
Preparing electroconductive layers of type 2 with dispersions based on the dispersions of EXAMPLE 3
Coating dispersions were produced by adding 3-glycidoxypropyl- trimethoxysilane, ZONYL™ FSO100 and diethylene glycol to the aqueous PEDOT/PSS-dispersions produce coverages upon coating on a poly (ethylene terephthalate) support subbed with subbing layer 1 and then drying for 1 minute at 140°C, with the following composition:
PEDOT/PSS: quantity was varied to maintain a constant PEDOT
2 coverage of 20.2 mg/m
2
3-glycidoxypropyltrimethoxysilane: 24 mg/m
ZONYL™ FSO 100: 11 mg/m2 diethylene glycol [DEG] (theoretical) 1.33 mL/m2
Characterization of electroconductive layers of type 2 prepared with dispersions based on the dispersions of EXAMPLE 3
The optical density and surface resistance of the layers was determined as described above for electroconductive layers of type 1. The results are summarized in Table 10.
Table 10:
Figure imgf000026_0002
Figure imgf000027_0001
The results in Table 10 surprisingly show that the surface resistance decreased with increasing PSS: PEDOT ratio for layers containing PEDOT/PSS produced in the substantial absence of oxygen, according to the present invention. This is at variance with the data available in the literature for PEDOT/PSS which shows that the surface resistance increases with increasing PSS: PEDOT ratio, see, for example, the paper published in 1999 by M. Lefebvre et al. in Chem. Mater., volume 11, pages 262-268, as mentioned above.
Determination of actual PSS/PEDOT ratio
Samples of the PEDOT-dispersions of types 10, 13, 17 and 19/20 were freeze dried were freeze dried under high vacuum (0.7 mbar) in a CHRIST BETA2-16 shelf freeze-dryer until all of the water was evaporated (i.e. until the temperature of the shelves was equal to room temperature) and dry powders were obtained.
The resulting freeze-dried samples were then analysed by 13C CP/MAS with a 200 MHz spectrometer at 11 different contact times in the ms range at a spin speed of 6.4 kHz, each measurement being repeated 3000 times to increase the signal to noise ratio. This total procedure as described in 2002 by P. Adriaensens et al., Polymer, volume 43, pages 7003 to 7006, took 30 h for each sample. The C-shift from the EDOT ring (68 ppm) is well-separated from the aliphatic PSS signals (around 40 ppm). The In (Intensity) versus contact time (CT) characteristics were analyzed according to the relationship:
In (Carbon intensity) = In (Initial carbon intensity,,) - t/TιH
and the initial carbon intensities thereby derived used to determine the quantitative molar ratio of PSS : PEDOT. The TlpH relaxation times are different for each signal and also different for each sample. Quantitative results require such long measurement sequence. The TlpH relaxation times for aromatic PSS carbon atoms, aliphatic PSS carbon atoms and carbon atoms of the PEDOT-ether group for each PEDOT-type are given in Table 11 below.
Table 11:
Figure imgf000028_0001
The thereby obtained initial aromatic carbon atom intensities of PSS, the initial aliphatic carbon atom intensity of PSS, the average of the initial carbon atom intensities of PSS, the initial ether carbon atom intensity of PEDOT and the ratios of the average of the initial carbon atom intensities of PSS and of the initial ether carbon atom intensity of PEDOT are given in Table 12 together with the theoretical PSS/PEDOT molar ratio.
The agreement between the theoretical and actual PSS/PEDOT molar ratios is very good, showing the efficacy of the method used. Therefore, the molar ratio obtained from 13C CP/MAS analysis is in total agreement with the theoretical molar ratio.
Table 12:
Figure imgf000028_0002
EXAMPLE 4
The quantity of poly(styrene sulphonic acid) [PSS] (Mn = 160,000 and Mw= 600,000) solution given in Table 13 was mixed with the quantity of deionized water given for the particular PEDOT-type in Table 13 at 25°C in the appropriate reaction vessel equipped with a stirrer and a nitrogen inlet. After bubbling nitrogen through this mixture for 30 minutes, the quantity of EDOT for the particular PEDOT-type given in Table 13 was then added to this solution, giving a EDOT-concentration of 30 mM. The concentration of oxygen in this solution was < l.Omg/L as measured with a Knick Process Unit 73 O2, using InPro 6000 Series 02. The quantities of Fe2 (SO4) 3.9H20 and a2S2θ8 corresponding to concentrations of 0.13 and 41.6 mM respectively were then added to initiate the polymerization reaction. The concentration of EDOT in the reaction mixtures was 30 mM and that of PSS was 46 mM for PEDOT-type 24, 37 mM for PEDOT-type 25, 57 mM for PEDOT-type 26, 69 mM for PEDOT-type 27 and 93 mM for PEDOT-type 28. The reaction mixtures were then stirred at 25°C for 7h, after which a further quantity of Na2S2θs for the particular PEDOT-type was added corresponding to a concentration of 6.94 mM. After an additional reaction time of 16h the reaction mixtures were treated twice with ion exchanger (300mL Lewatit™ SIOOMB + 500mL Lewatit™ M600MB) . The resulting mixtures were further thermally treated at 95°C for 2h and the resulting viscous mixture treated with high shear [microfluidizer at 60 MPa (600Bar) ] .
Table 13:
Figure imgf000029_0001
The resulting PSS:PED0T weight and molar ratios, PEDOT/PSS- concentrations, viscosity as measured in an Ubbelohde viscometer in a bath thermostatted at 25°C, the peak particle sizes in the bimodal size distribution and the number of particles per mL with a particle size greater than 1 μm are given in Table 1 .
Table 14:
Figure imgf000029_0002
Preparation and characterization of electroconductive layers of type 1 with dispersions based on the dispersions of EXAMPLE 4
The electroconductive layers of type 1 with dispersions based on the dispersions of EXAMPLE 4 were prepared and characterized as described for the dispersions of EXAMPLE 3. The results are summarized in Table 15 for the type 1 electroconductive layers .
Table 15:
Figure imgf000030_0001
The results in Table 15 confirm the results in Table 9 surprisingly showing that the surface resistance decreased with increasing PSS: PEDOT ratio for layers containing PEDOT/PSS produced in the substantial absence of oxygen, according to the present invention.
INVENTION EXAMPLE 5
The quantity of poly(styrene sulphonic acid) [PSS] (VERSA TL77 from ALCO with Mn = 25,000 and Mw= 72,000) solution given in Table 13 was mixed with sufficient deionized water at 25 °C to give 2000 g of solution in the appropriate reaction vessel equipped with a stirrer, see quantity in Table 16 for the particular PEDOT-type. The quantity of EDOT for the particular PEDOT-type given in Table 15 was then added to this solution, giving a EDOT-concentration of 30 mM. The concentration of oxygen in this solution was measured with a Knick Process Unit 73 O2, using InPro 6000 Series O2. The quantities of Fe2 (SO4) 3.9H2O and a2S2θs corresponding to concentrations of 0.13 and 41.6 mM respectively were then added to initiate the polymerization reaction. The concentration of EDOT in the reaction mixtures was 30 mM and the final concentration of PSS in the reaction medium is given in Table 16 for the particular PEDOT-type. The reaction mixtures were then stirred at 25°C for 7h, after which a further quantity of a2S2θ8 for the particular PEDOT-type was added corresponding to a concentration of 6.94 mM. After an additional reaction time of 16h the reaction mixtures were treated twice with ion exchanger (300mL Lewatit™ SIOOMB + 500mL Lewatit™ M600MB) . The resulting mixtures were further thermally treated at 95°C for 2h and the resulting viscous mixture treated with high shear [microfluidizer at 60 MPa (600Bar) ] .
Table 16:
Figure imgf000031_0001
The molecular weights of the PEDOT in PEDOT-dispersions type 26 to 30 was determined by aqueous gel permeation chromatography as described in EXAMPLE 3 are given in Table 17.
Table 17:
Figure imgf000031_0002
Preparation and characterization of electroconductive layers of type 1 with dispersions based on the dispersions of EXAMPLE 5
The electroconductive layers of type 1 with dispersions based on the dispersions of EXAMPLE 5 were prepared and characterized as described for the dispersions of EXAMPLE 3. The results are summarized in Table 18 for the type 1 electroconductive layers . Table 18 :
Figure imgf000032_0001
The results in Table 18 surprisingly show that even for PEDOT/PSS- dispersions prepared with a particular concentration of oxygen in the reaction medium the surface resistance decreased with increasing PSS: PEDOT ratio for layers containing PEDOT/PSS produced in the substantial absence of oxygen, according to the present invention. This is at variance with the data available in the literature for PEDOT/PSS which shows that the surface resistance increases with increasing PSS: PEDOT ratio, see, for example, the paper published in 1999 by M. Lefebvre et al. in Chem. Mater., volume 11, pages 262-268, as mentioned above.
Preparation and characterization of electroconductive layers of type 2 with dispersions based on the dispersions of EXAMPLE 5
The electroconductive layers of type 2 with dispersions based on the dispersions of EXAMPLE 5 were prepared and characterized as described for the dispersions of EXAMPLE 3. The results are summarized in Table 19 for the type 1 electroconductive layers . Table 19:
Figure imgf000032_0002
Figure imgf000033_0001
The results in Table 19 surprisingly again show that even for PEDOT/PSS-dispersions prepared with a particular concentration of oxygen in the reaction medium the surface resistance decreased with increasing PSS: PEDOT ratio for layers containing PEDOT/PSS produced in the substantial absence of oxygen, according to the present invention. This is at variance with the data available in the literature for PEDOT/PSS which shows that the surface resistance increases with increasing PSS: PEDOT ratio, see, for example, the paper published in 1999 by M. Lefebvre et al. in Chem. Mater., volume 11, pages 262-268, as mentioned above.
The present invention may include any feature or combination of features disclosed herein either implicitly or explicitly or any generalisation thereof irrespective of whether it relates to the presently claimed invention. In view of the foregoing description it will be evident to a person skilled in the art that various modifications may be made within the scope of the invention.

Claims

An aqueous dispersion of latex particles, said latex particles containing a polymer consisting of structural units including monomer units according to formula (I) :
Figure imgf000034_0001
1 2 in which R and R independently of one another represent hydrogen or a Cι-5-alkyl group or together form an optionally substituted Cι_5-alkylene residue and at least one polyanion compound, said latex having a primary particle size of less than 40 nm and said dispersion contains an organic compound containing a di- or polyhydroxy- and/or carboxy groups or amide or lactam group or an aprotic compound with a dielectric constant, ε, > 15, characterized in that said latex particles contain said at least one polyanion compound and said polymer in a weight ratio of at least 4.
2. Aqueous dispersion of a latex according to claim 1, wherein the weight ratio of said at least one polyanion compound to said polymer corresponds to the weight ratio of the monomer (s) constituting said polymer to said at least one polyanion compound during the preparation thereof.
3. Aqueous dispersion of a latex according to claim 1 or 2, wherein said latex particles contain said at least one polyanion compound and said polymer in a weight ratio of greater than 4 and less than 20.
4. Aqueous dispersion of a latex according to any of claims 1 to 3, wherein said latex is prepared in a reaction medium with less than 8500 mg of oxygen/L of said reaction medium when the initiator is added.
5. Aqueous dispersion of a latex according to any of claims 1 to 3, wherein said latex is prepared in a reaction medium with less than 2000 mg of oxygen/L of said reaction medium when the initiator is added.
6. Aqueous dispersion of a latex according to any of claims 1 to 3, wherein said latex is prepared in a reaction medium with less than 1000 mg of oxygen/L of said reaction medium when the initiator is added.
7. Aqueous dispersion of a latex according to any of claims 1 to 6, wherein said monomer units according to formula (I) are selected from the group consisting of optionally alkyl group- substituted 3,4-methylenedioxy-thiophene units, optionally alkyl or aryl-group-substituted 3, 4-ethylenedioxythiophene units, optionally alkyl or aryl-group-substituted 3,4- ethylenedioxythiophene units, a unit according to formula (I)
1 2 in which R and R are together a 1,2-cyclohexene group, optionally alkyl or aryl-group-substituted 3,4- propylenedioxythiophene units, optionally alkyl or aryl-group- substituted 3,4-butylenedioxythiophene units and optionally alkyl or aryl-group-substituted 3, -pentylenedioxythiophene units .
8. Aqueous dispersion of a latex according to any of claims 1 to 7, wherein said polymer is a copolymer of a 3,4- alkylenedioxythiophene compound with a solubility in water at
25°C of less than 2.2 g/L with a 3, 4-alkylenedioxythiophene compound with a solubility in water at 25°C of at least 2.2 g/L.
9. Aqueous dispersion of a latex according to claim 8, wherein said 3, 4-alkylenedioxythiophene compound with a solubility in water at 25°C of at least 2.2 g/L is selected from the group consisting of: 3, 4-dihydro-2JΪ-thieno [3, 4-b] [l,4]dioxin-2- yl)methanol, 3,4-dihydro-2JΪ-thieno[3,4-Jb] [1, 4] dioxepin-3-ol, (2, 3-dihydro-thieno [3, 4-i)] [1, 4] dioxin-2-yl-methoxy) -acetic acid ethyl ester, (2, 3-dihydro-thieno [3, 4-£>] [1, 4] dioxin-2-yl- methoxy) -acetic acid, 2-{2- [2- (2-methoxy-ethoxy) -ethoxy] - ethoxymethyl }-2, 3-dihydro-thieno [3, 4 -b] [14] dioxine and 4-(2,3- dihydro-thieno[3,4-i>] [1, 4] dioxin-2-ylmethoxy) -butane-1- sulfonic acid sodium salt.
10. Aqueous dispersion of a latex according to any of the preceding claims, wherein said at least one polyanion compound includes poly (styrene sulphonic acid) .
11. A process for preparing an electroconductive coating comprising the steps of: preparing an aqueous solution or dispersion of a polymer consisting of structural units including monomer units according to formula (I) :
Figure imgf000036_0001
by polymerization with an initiator in a reaction medium in the presence of at least one polyanion compound under oxidizing or reducing conditions, wherein the weight ratio of said at least one polyanion compound to said structural units during the reaction is in the range of 4:1 to 20:1; preparing a first coating composition containing said polymer associated with said at least one polyanion compound and an organic compound containing a di- or polyhydroxy- and/or carboxy groups or amide or lactam group in a aqueous or non-aqueous medium; coating said first coating composition on an object thereby producing a first layer; and heating said first layer at a temperature of at least 100 °C.
12. A process for preparing an electroconductive coating comprising the steps of: preparing an aqueous solution or dispersion of a polymer consisting of structural units including monomer units according to formula (I) :
Figure imgf000036_0002
by polymerization with an initiator in a reaction medium in the presence of at least one polyanion compound under oxidizing or reducing conditions, wherein the weight ratio of said at least one polyanion compound to said structural units during the reaction is in the range of 4:1 to 20:1; preparing a second coating composition containing said polymer associated with said at least one polyanion compound and an 5 aprotic compound with a dielectric constant, ε, > 15 in an aqueous or non-aqueous medium; coating said second coating composition on an object thereby producing a second layer; and heating said second layer at a temperature of at least 50 °C.
10 13. Process according to claim 11 or 12, wherein when said preparation is carried out under an inert atmosphere such that when said initiator is added less than 850 mg of oxygen per litre of the reaction medium is present in the reaction medium.
15
14. Process according to claim 11 or 12, wherein when said initiator is added less than 200 mg of oxygen per litre of said reaction medium is present in said reaction medium.
20 15. Process according to claim 11 or 12, wherein when said initiator is added less than 100 mg of oxygen per litre of said reaction medium is present in said reaction medium.
16. Process according to any of claims 11 to 15, wherein said 25 monomer units according to formula (I) are selected from the group consisting of optionally alkyl group-substituted 3,4- methylenedioxy-thiophene units, optionally alkyl or aryl- group-substituted 3,4-ethylenedioxythiophene units, optionally alkyl or aryl-group-substituted 3,4-ethylenedioxythiophene
1 2
30 units, a unit according to formula (I) in which R and R are together a 1,2-cyclohexene group, optionally alkyl or aryl- group-substituted 3,4-propylenedioxythiophene units, optionally alkyl or aryl-group-substituted 3,4- butylenedioxythiophene units and optionally alkyl or aryl-
35 group-substituted 3,4-pentylenedioxythiophene units.
17. Process according to any of claims 11 to 16, wherein said polymer is a copolymer of a 3, 4-alkylenedioxythiophene compound with a solubility in water at 25 °C of less than 2.2
40 g/L with a 3, 4-alkylenedioxythiophene compound with a solubility in water at 25°C of at least 2.2 g/L.
18. Process according to claim 17, wherein said 3,4- alkylenedioxythiophene compound with a solubility in water at 25°C of at least 2.2 g/L is selected from the group consisting of: 3,4-dihydro-2iϊ-thieno[3, 4-Jb] [l,4]dioxin-2-yl)methanol, 3,4-dihydro-2tf-thieno[3,4-£>] [l,4]dioxepin-3-ol, (2, 3-dihydro- thieno [3, 4-Jb] [1,4] dioxin-2-yl-methoxy) -acetic acid ethyl ester, (2, 3-dihydro-thieno [3, -b] [1, 4] dioxin-2-yl-methoxy) - acetic acid, 2-{2- [2- (2-methoxy-ethoxy) -ethoxy] -ethoxymethyl} - 2, 3-dihydro-thieno [3, 4-Jb] [14] dioxine and 4- (2, 3-dihydro- thieno [3, 4-Jb] [1, 4]dioxin-2-ylmethoxy) -butane-1-sulfonic acid sodium salt.
19. Process according to any of claims 11 to 18, wherein said at least one polyanion compound includes poly(styrene sulphonic acid) .
PCT/EP2004/051073 2003-06-20 2004-06-09 Process for preparing electroconductive coatings WO2004114326A1 (en)