WO2005097031A1 - Web materials having both plastic and elastic properties - Google Patents
Web materials having both plastic and elastic properties Download PDFInfo
- Publication number
- WO2005097031A1 WO2005097031A1 PCT/US2005/009995 US2005009995W WO2005097031A1 WO 2005097031 A1 WO2005097031 A1 WO 2005097031A1 US 2005009995 W US2005009995 W US 2005009995W WO 2005097031 A1 WO2005097031 A1 WO 2005097031A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- elastic
- plasto
- strain
- cycle
- materials
- Prior art date
Abstract
Description
Claims