WO2007001470A1 - Improved retention and drainage in the manufacture of paper - Google Patents

Abstract

A method of improving retention and drainage in a papermaking process is disclosed. The method provides for the addition of an associative polymer, starch or a starch derivative and optionally a siliceous material to the papermaking slurry. Additionally, a composition comprising an associative polymer and starch or starch derivative and optionally further comprising cellulose fiber is disclosed.

Description

IMPROVED RETENTION AND DRAINAGE IN THE MANUFACTURE OF

PAPER

CROSS REFERENCE TO RELATED APPLICATIONS

[0001] This application claims the benefit of U.S. Provisional Application

No. 60/693,854, filed June 24, 2005, the entire content of which is herein incorporated by reference.

FIELD OF THE INVENTION

[0002] This invention relates to the process of making paper and paperboard from a cellulosic stock, employing a flocculating system.

BACKGROUND

[0003] Retention and drainage is an important aspect of papermaking. It is known that certain materials can provide improved retention and/or drainage properties in the production of paper and paperboard.

[0004] The making of cellulosic fiber sheets, particularly paper and paperboard, includes the following: 1) producing an aqueous slurry of cellulosic fiber which may also contain inorganic mineral extenders or pigments; 2) depositing this slurry on a moving papermaking wire or fabric; and 3) forming a sheet from the solid components of the slurry by draining the water. [0005] The foregoing is followed by pressing and drying the sheet to further remove water. Organic and inorganic chemicals are often added to the slurry prior to the sheet-forming step to make the papermaking method less costly, more rapid, and/or to attain specific properties in the final paper product. [0006] The paper industry continuously strives to improve paper quality, increase productivity, and reduce manufacturing costs. Chemicals are often added to the fibrous slurry before it reaches the papermaking wire or fabric to improve drainage/dewatering and solids retention; these chemicals are called retention and/or drainage aids.

[0007] Drainage or dewatering of the fibrous slurry on the papermaking wire or fabric is often the limiting step in achieving faster paper machine speeds. Improved dewatering can also result in a drier sheet in the press and dryer sections, resulting in reduced energy consumption. In addition, as this is the stage in the papermaking method that determines many of the sheet final properties, the retention and/or drainage aid can impact performance attributes of the final paper sheet.

[0008] With respect to solids, papermaking retention aids are used to increase the retention of fine furnish solids in the web during the turbulent method of draining and forming the paper web. Without adequate retention of the fine solids, they are either lost to the mill effluent or accumulate to high levels in the recirculating white water loop, potentially causing deposit buildup. Additionally, insufficient retention increases the papermakers' cost due to loss of additives intended to be adsorbed on the fiber. Additives can provide opacity, strength, sizing or other desirable properties to the paper.

[0009] High molecular weight (MW) water-soluble polymers with either cationic or anionic charge have traditionally been used as retention and drainage aids. Recent development of inorganic microparticles, when used as retention and drainage aids, in combination with high MW water-soluble polymers, have shown superior retention and drainage efficacy compared to conventional high MW water-soluble polymers. U.S. Patent Nos. 4,294,885 and 4,388,150 teach the use of starch polymers with colloidal silica. U.S. Patent Nos. 4,643,801 and 4,750,974 teach the use of a coacervate binder of cationic starch, colloidal silica, and anionic polymer. U.S. Patent No. 4,753,710 teaches flocculating the pulp furnish with a high MW cationic flocculant, inducing shear to the flocculated furnish, and then introducing bentonite clay to the furnish. [0010] The efficacy of the polymers or copolymers used will vary depending upon the type of monomers from which they are composed, the arrangement of the monomers in the polymer matrix, the molecular weight of the synthesized molecule, and the method of preparation.

[0011] It had been found recently that water-soluble copolymers when prepared under certain conditions exhibit unique physical characteristics. These polymers are prepared without chemical cross linking agents. Additionally, the copolymers provide unanticipated activity in certain applications including papermaking applications such as retention and drainage aids. The anionic copolymers which exhibit the unique characteristics were disclosed in WO 03/050152 A1 , the entire content of which is herein incorporated by reference. The cationic and amphoteric copolymers which exhibit the unique characteristics were disclosed in U.S. serial number 10/728,145, the entire content of which is herein incorporated by reference.

[0012] The use of inorganic particles with linear copolymers of acrylamide, is known in the art. Recent patents teach the use of these inorganic particles with water-soluble anionic polymers (US 6,454,902) or specific crosslinked materials

(US 6,454,902, US 6,524,439 and US 6,616,806).

[0013] However, there still exists a need to improve drainage and retention performance.

SUMMARY OF THE INVENTION

[0014] A method of improving retention and drainage in a papermaking process is disclosed. The method provides for the addition of an associative polymer and starch or a starch derivative to a papermaking slurry. [0015] Additionally, a composition comprising an associative polymer and starch or a starch derivative and optionally further comprising cellulose fiber is disclosed.

[0016] Additionally, a composition comprising an associative polymer, a starch or a starch derivative, a siliceous material and optionally further comprising cellulose fiber is disclosed.

DETAILED DESCRIPTION OF THE INVENTION

[0017] The present invention provides for a synergistic combination comprising a water soluble copolymer prepared under certain conditions (herein after referred to as "associative polymer") and starch or starch derivative. It has surprising been found that this synergistic combination results in retention and drainage performance superior to that of the individual components. Synergistic effects occur when the combination of components are used together. [0018] It has been found, unexpectedly, that the use of starch or starch derivative in combination with an associative polymer, such as the polymer disclosed in WO 03/050152 A1 or US 2004/0143039 A1, results in enhanced retention and drainage.

[0019] The present invention also provides for a novel composition comprising an associative polymer and starch or a starch derivative. [0020] The present invention also provides for a composition comprising an associative polymer, starch or a starch derivative a siliceous material. [0021] The present invention also provides for a composition comprising an associative polymer and starch or a starch derivative and cellulose fiber. [0022] The present invention also provides for a composition comprising an associative polymer, starch or a starch derivative, a siliceous material and cellulose fiber.

[0023] The use of multi-component systems in the manufacture of paper and paperboard provides the opportunity to enhance performance by utilizing materials that have different effects on the process and/or product. Moreover, the combinations may provide properties unobtainable with the components individually. Synergistic effects occur in the multi component systems of the present invention.

[0024] It is also observed that the use of the associative polymer as a retention and drainage aid has an impact on the performance of other additives in the papermaking system. Improved retention and/or drainage can have both a direct and indirect impact. A direct impact refers to the retention and drainage aid acting to retain the additive. An indirect impact refers to the efficacy of the retention and drainage aid to retain filler and fines onto which the additive is attached by either physical or chemical means. Thus, by increasing the amount of filler or fines retained in the sheet, the amount of additive retained is increased in a concomitant manner. The term filler refers to particulate materials, typically inorganic in nature, that are added to the cellulosic pulp slurry to provide certain attributes or be a lower cost substitute of a portion of the cellulose fiber. Their relatively small size, on the order of 0.2 to 10 microns, low aspect ratio and chemical nature results in their not being adsorbed onto the large fibers yet too small to be entrapped in the fiber network that is the paper sheet. The term "fines" refers to small cellulose fibers or fibrils, typically less than 0.2 mm in length and /or ability to pass through a 200 mesh screen.

[0025] As the use level of the retention and drainage aid increases the amount of additive retained in the sheet increases. This can provide either an enhancement of the property, providing a sheet with increased performance attribute, or allows the papermaker to reduce the amount of additive added to the system, reducing the cost of the product. Moreover, the amount of these materials in the recirculating water, or Whitewater, used in the papermaking system is reduced. This reduced level of material, that under some conditions can be considered to be an undesirable contaminant, can provide a more efficient papermaking process or reduce the need for scavengers or other materials added to control the level of undesirable material.

[0026] The term additive, as used herein, refers to materials added to the paper slurry to provide specific attributes to the paper and/or improve the efficiency of the papermaking process. These materials include, but are not limited to, sizing agents, wet strength resins, dry strength resins, starch and starch derivatives, dyes, contaminant control agents, antifoams, and biocides. [0027] The associative polymer useful in the present invention can be described as follows:

[0028] A water-soluble copolymer composition comprising the formula:

FB-co-F-f (I) wherein B is a nonionic polymer segment formed from the polymerization of one or more ethylenically unsaturated nonionic monomers; F is an anionic, cationic or a combination of anionic and cationic polymer segment(s) formed from polymerization of one or more ethylenically unsaturated anionic and/or cationic monomers; the molar % ratio of B:F is from 95:5 to 5:95; and the water-soluble copolymer is prepared via a water-in-oil emulsion polymerization technique that employs at least one emulsification surfactant consisting of at least one diblock or triblock polymeric surfactant wherein the ratio of the at least one diblock or triblock surfactant to monomer is at least about 3:100 and wherein; the water-in- oil emulsion polymerization technique comprises the steps of: (a) preparing an aqueous solution of monomers, (b) contacting the aqueous solution with a hydrocarbon liquid containing surfactant or surfactant mixture to form an inverse emulsion, (c) causing the monomer in the emulsion to polymerize by free radical polymerization at a pH range of from about 2 to less than 7. [0029] The associative polymer can be an anionic copolymer. The anionic copolymer is characterized in that the Huggins' constant (k¹) determined between 0.0025 wt. % to 0.025 wt. % of the copolymer in 0.01 M NaCI is greater than 0.75 and the storage modulus (G') for a 1.5 wt. % actives copolymer solution at 4.6 Hz greater than 175 Pa.

[0030] The associative polymer can be a cationic copolymer. The cationic copolymer is characterized in that its Huggins' constant (k¹) determined between 0.0025 wt. % to 0.025 wt. % of the copolymer in 0.01 M NaCI is greater than 0.5; and it has a storage modulus (G') for a 1.5 wt. % actives copolymer solution at 6.3 Hz greater than 50 Pa.

[0031] The associative polymer can be an amphoteric copolymer. The amphoteric copolymer is characterized in that its Huggins' constant (k') determined between 0.0025 wt. % to 0.025 wt. % of the copolymer in 0.01 M NaCI is greater than 0.5; and the copolymer has a storage modulus (G') for a 1.5 wt. % actives copolymer solution at 6.3 Hz greater than 50 Pa.

[0032] Inverse emulsion polymerization is a standard chemical process for preparing high molecular weight water-soluble polymers or copolymers. In general, an inverse emulsion polymerization process is conducted by 1) preparing an aqueous solution of the monomers, 2) contacting the aqueous solution with a hydrocarbon liquid containing appropriate emulsification surfactant(s) or surfactant mixture to form an inverse monomer emulsion, 3) subjecting the monomer emulsion to free radical polymerization, and, optionally, 4) adding a breaker surfactant to enhance the inversion of the emulsion when added to water.

[0033] Inverse emulsions polymers are typically water-soluble polymers based upon ionic or non-ionic monomers. Polymers containing two or more monomers, also referred to as copolymers, can be prepared by the same process. These co-monomers can be anionic, cationic, zwitterionic, nonionic, or a combination thereof.

[0034] Typical nonionic monomers, include, but are not limited to, acrylamide; methacrylamide; N-alkylacrylamides, such as N-methylacrylamide; N,N-dialkylacrylamides, such as N,N-dimethylacrylamide; methyl acrylate; methyl methacrylate; acrylonitrile; N-vinyl methylacetamide; N-vinyl formamide; N-vinyl methyl formamide; vinyl acetate; N-vinyl pyrrolidone; hydroxyalky(meth)acrylates such as hydroxyethyl(meth)acrylate or hydroxypropyl(meth)acrylate; mixtures of any of the foregoing and the like.

[0035] Nonionic monomers of a more hydrophobic nature can also be used in the preparation of the associative polymer. The term 'more hydrophobic' is used here to indicate that these monomers have reduced solubility in aqueous solutions; this reduction can be to essentially zero, meaning that the monomer is not soluble in water. It is noted that the monomers of interest are also referred to as polymerizable surfactants or surfmers. These monomers include, but are not limited to, alkylacryamides; ethylenically unsaturated monomers that have pendant aromatic and alkyl groups, and ethers of the formula CH₂=CR¹CH₂OAmR where R' is hydrogen or methyl; A is a polymer of one or more cyclic ethers such as ethyleneoxide, propylene oxide and/or butylene oxide; and R is a hydrophobic group; vinylalkoxylates; allyl alkoxylates; and allyl phenyl polyolether sulfates. Exemplary materials include, but are not limited to, methylmethacrylate, styrene, t-octyl acrylamide, and an allyl phenyl polyol ether sulfate marketed by Clariant as Emulsogen APG 2019.

[0036] Exemplary anionic monomers include, but are not limited to, the free acids and salts of: acrylic acid; methacrylic acid; maleic acid; itaconic acid; acrylamidoglycolic acid; 2-acrylamido-2-methyl-1-propanesulfonic acid; 3- allyloxy-2~hydroxy-1-propanesulfonic acid; styrenesulfonic acid; vinylsulfonic acid; vinylphosphonic acid; 2-acrylamido-2-methylpropane phosphonic acid; mixtures of any of the foregoing and the like. [0037] Exemplary cationic monomers include, but are not limited to, cationic ethylenically unsaturated monomers such as the free base or salt of: diallyldialkylammonium halides, such as diallyldimethylammonium chloride; the (meth)acrylates of dialkylaminoalkyl compounds, such as dimethylaminoethyl (meth)acrylate, diethylaminoethyl (meth)acrylate, dimethyl aminopropyl (meth)acrylate, 2-hydroxydimethyl aminopropyl (meth)acrylate, aminoethyl (meth)acrylate, and the salts and quaternaries thereof; the N₁N- dialkylaminoalkyl(meth)acrylamides, such as N.N-dimethylaminoethylacrylamide, and the salts and quaternaries thereof and mixture of the foregoing and the like. [0038] The co-monomers may be present in any ratio. The resultant associative polymer can be non-ionic, cationic, anionic, or amphoteric (contains both cationic and anionic charge).

[0039] The molar ratio of nonionic monomer to anionic monomer (B: F or Formula I) may fall within the range of 95:5 to 5:95, preferably the range is from about 75:25 to about 25:75 and even more preferably the range is from about 65:35 to about 35:65 and most preferably from about 60:40 to about 40:60. In this regard, the molar percentages of B and F must add up to 100%. It is to be understood that more than one kind of nonionic monomer may be present in the Formula I. It is also to be understood that more than one kind of anionic monomer may be present in the Formula I.

[0040] In one preferred embodiment of the invention the associative polymer, when it is an anionic copolymer, is defined by Formula I where B, the nonionic polymer segment, is the repeat unit formed after polymerization of acrylamide; and F, the anionic polymer segment, is the repeat unit formed after polymerization of a salt or free acid of acrylic acid and the molar percent ratio of B: F is from about 75:25 to about 25:75

[0041] The physical characteristics of the associative polymer, when it is an anionic copolymer, are unique in that their Huggins¹ constant (k¹) as determined in 0.01 M NaCI is greater than 0.75 and the storage modulus (G') for a 1.5 wt. % actives polymer solution at 4.6 Hz is greater than 175 Pa, preferably greater than 190 and even more preferably greater than 205. The Huggins¹ constant is greater than 0.75, preferably greater than 0.9 and even more preferably greater than 1.0

[0042] The molar ratio of nonionic monomer to cationic monomer (B:F of

Formula I) may fall within the range of 99:1 to 50:50, or 95:5 to 50:50, or 95:5 to 75:25, or 90:10 to 60:45, preferably the range is from about 85:15 to about 60:40 and even more preferably the range is from about 80:20 to about 50:50. In this regard, the molar percentages of B and F must add up to 100%. It is to be understood that more than one kind of nonionic monomer may be present in the Formula I. It is also to be understood that more than one kind of cationic monomer may be present in the Formula I.

[0043] With respect to the molar percentages of the amphoteric copolymers of Formula I, the minimum amount of each of the anionic, cationic and non-ionic monomer is 1 % of the total amount of monomer used to form the copolymer. The maximum amount of the non-ionic, anionic or cationic is 98% of the total amount of monomer used to form the copolymer. Preferably the minimum amount of any of anionic, cationic and non-ionic monomer is 5%, more preferably the minimum amount of any of anionic, cationic and non-ionic monomer is 7% and even more preferably the minimum amount of any of anionic, cationic and non-ionic monomer is 10% of the total amount of monomer used to form the copolymer. In this regard, the molar percentages of anionic, cationic and non-ionic monomer must add up to 100%. It is to be understood that more than one kind of nonionic monomer may be present in the Formula I, more than one kind of cationic monomer may be present in the Formula I, and that more than one kind of anionic monomer may be present in the Formula I.

[0044] The physical characteristics of the associative polymer, when it is a cationic or amphoteric copolymer, are unique in that their Huggins' constant (k¹) as determined in 0.01 M NaCI is greater than 0.5 and the storage modulus (G') for a 1.5 wt. % actives polymer solution at 6.3 Hz is greater than 50 Pa, preferably greater than 10 and even more preferably greater than 25, or greater than 50, or greater than 100, or greater than 175, or greater than 200. The Huggins' constant is greater than 0.5, preferably greater than 0.6, or greater than 0.75, or greater than 0.9 or greater than 1.0.

[0045] The emulsification surfactant or surfactant mixture used in an inverse emulsion polymerization system have an important effect on both the manufacturing process and the resultant product. Surfactants used in emulsion polymerization systems are known to those skilled in the art. These surfactants typically have a range of HLB (Hydrophilic Lipophilic Balance) values that is dependent on the overall composition. One or more emulsification surfactants can be used. The emulsification surfactant(s) of the polymerization products that are used to produce the associative polymer include at least one diblock or triblock polymeric surfactant. It is known that these surfactants are highly effective emulsion stabilizers. The choice and amount of the emulsification surfactant(s) are selected in order to yield an inverse monomer emulsion for polymerization. Preferably, one or more surfactants are selected in order to obtain a specific HLB value.

[0046] Diblock and triblock polymeric emulsification surfactants are used to provide unique materials. When the diblock and triblock polymeric emulsification surfactants are used in the necessary quantity, unique polymers exhibiting unique characteristic result, as described in WO 03/050152 A1 and US 2004/0143039 A1 , the entire contents of each is herein incorporated by reference. Exemplary diblock and triblock polymeric surfactants include, but are not limited to, diblock and triblock copolymers based on polyester derivatives of fatty acids and poly[ethyleneoxide] (e.g., Hypermer® B246SF, Uniqema, New Castle, DE), diblock and triblock copolymers based on polyisobutylene succinic anhydride and poly[ethyleneoxide], reaction products of ethylene oxide and propylene oxide with ethylenediamine, mixtures of any of the foregoing and the like. Preferably the diblock and triblock copolymers are based on polyester derivatives of fatty acids and poly[ethyleneoxide]. When a triblock surfactant is used, it is preferable that the triblock contains two hydrophobic regions and one hydrophilic region, i.e., hydrophobe-hydrophile-hydrophobe.

[0047] The amount (based on weight percent) of diblock or triblock surfactant is dependent on the amount of monomer used to form the associative polymer. The ratio of diblock or triblock surfactant to monomer is at least about 3 to 100. The amount of diblock or triblock surfactant to monomer can be greater than 3 to 100 and preferably is at least about 4 to 100 and more preferably 5 to 100 and even more preferably about 6 to 100. The diblock or triblock surfactant is the primary surfactant of the emulsification system. [0048] A secondary emulsification surfactant can be added to ease handling and processing, to improve emulsion stability, and/or to alter the emulsion viscosity. Examples of secondary emulsification surfactants include, but are not limited to, sorbitan fatty acid esters, such as sorbitan monooleate (e.g., Atlas G-946, Uniqema, New Castle, DE), ethoxylated sorbitan fatty acid esters, polyethoxylated sorbitan fatty acid esters, the ethylene oxide and/or propylene oxide adducts of alkylphenols, the ethylene oxide and/or propylene oxide adducts of long chain alcohols or fatty acids, mixed ethylene oxide/propylene oxide block copolymers, alkanolamides, sulfosuccinates and mixtures thereof and the like.

[0049] Polymerization of the inverse emulsion may be carried out in any manner known to those skilled in the art. Examples can be found in many references, including, for example, Allcock and Lampe, Contemporary Polymer Chemistry, (Englewood Cliffs, New Jersey, PRENTICE-HALL, 1981), chapters 3- 5.

[0050] A representative inverse emulsion polymerization is prepared as follows. To a suitable reaction flask equipped with an overhead mechanical stirrer, thermometer, nitrogen sparge tube, and condenser is charged an oil phase of paraffin oil (135.Og, Exxsol® D80 oil, Exxon - Houston, TX) and surfactants (4.5g Atlas® G-946 and 9.Og Hypermer® B246SF). The temperature of the oil phase is then adjusted to 37°C.

[0051] An aqueous phase is prepared separately which comprised 53-wt. % acrylamide solution in water (126.5g), acrylic acid (68.7g), deionized water (70.Og)₁ and Versenex® 80 (Dow Chemical) chelant solution (0.7g). The aqueous phase is then adjusted to pH 5.4 with the addition of ammonium hydroxide solution in water (33.1g, 29.4 wt. % as NH₃). The temperature of the aqueous phase after neutralization is 39°C.

[0052] The aqueous phase is then charged to the oil phase while simultaneously mixing with a homogenizer to obtain a stable water-in-oil emulsion. This emulsion is then mixed with a 4-blade glass stirrer while being sparged with nitrogen for 60 minutes. During the nitrogen sparge the temperature of the emulsion is adjusted to 50+1⁰C. Afterwards, the sparge is discontinued and a nitrogen blanket implemented.

[0053] The polymerization is initiated by feeding a 3-wt. % solution of 2,2'- azobisisobutyronitrile (AIBN) in toluene (0.213g). This corresponds to an initial AIBN charge, as AIBN, of 250 ppm on a total monomer basis. During the course of the feed the batch temperature was allowed to exotherm to 62°C (~50 minutes), after which the batch was maintained at 62+1⁰C. After the feed the batch was held at 62+1⁰C for 1 hour. Afterwards 3-wt. % AIBN solution in toluene (0.085g) is then charged in under one minute. This corresponds to a second AIBN charge of 100 ppm on a total monomer basis. Then the batch is held at 62+1⁰C for 2 hours. Then batch is then cooled to room temperature, and breaker surfactant(s) is added.

[0054] The associative polymer emulsion is typically inverted at the application site resulting in an aqueous solution of 0.1 to 1% active copolymer. This dilute solution of the associative polymer is then added to the paper process to affect retention and drainage. The associative polymer may be added to the thick stock or thin stock, preferably the thin stock. The associative polymer may be added at one feed point, or may be split fed such that the associative polymer is fed simultaneously to two or more separate feed points. Typical stock addition points include feed point(s) before the fan pump, after the fan pump and before the pressure screen, or after the pressure screen.

[0055] The associative polymer may be added in any effective amount to achieve flocculation. The amount of copolymer could be more than 0.5 Kg per metric ton of cellulosic pulp (dry basis). Preferably, the associative polymer is employed in an amount of at least about 0.03 Ib. to about 0.5 Kg. of active copolymer per metric ton of cellulosic pulp, based on the dry weight of the pulp. The concentration of copolymer is preferably from about 0.05 to about 0.5 Kg of active copolymer per metric ton of dried cellulosic pulp. More preferably the copolymer is added in an amount of from about 0.05 to 0.4 Kg per metric ton cellulose pulp and, most preferably, about 0.1 to about 0.3 Kg per metric ton based on dry weight of the cellulosic pulp.

[0056] The second component of the retention and drainage system is starch and derivatives thereof. Starch is the common name for a polymer of glucose that contains a/pfra-1,4 linkages. Starch is a naturally occurring material; this carbohydrate can be found in the leaves, stems, roots and fruits of most land plants. The commercial sources of starch include, but are not limited to, the seeds of cereal grains (corn, wheat, rice, etc.), and certain roots (potato, tapioca, etc.). Starch is described by its plant source; reference would be made to, for example, corn starch, potato starch, tapioca starch, rice starch, and wheat starch. [0057] Glucose is composed of carbon, hydrogen, and oxygen in the ratio of 6:10:5 (CΘH-IOO_S), placing it in the class of carbohydrate organic compounds. Starch can be considered to be a condensation polymer of glucose. [0058] Most starches consist of a mixture of two polysaccharide types: amylose, an essentially linear polymer, and amylopectin, a highly branched polymer. The relative amounts of amylose and amylopectin vary with the source, with the ratio of amylose to amylopectin typically being 17:83 for tapioca, 21 :79 for potato, 28:72 for corn and 0:100 for waxy maize corn. Although these are the typical starch ratios found the present invention contemplates that any ratio of amylose to amylopectin can be useful in the present invention. For the purposes of this invention waxy maize is consisted a type of corn starch.

[0059] Amylose is a linear polymer consisting of a chain of glucose units connected to each other by alpha-ϊ ,4 linkages. The molecular weight can range from about 30,000 to about 1 ,000,000.

[0060] Amylopectin is a highly branched structure of short amylose chains having molecular weight from about 2000 to about 10,000 connected via alpha-

1 ,6, linkages to form a very complex, very high molecular weight (10,000,000 to

100,000,000) polymer.

[0061] Starch is synthesized by plants and accumulates in granules that are distinctive for each plant. Starch granules are separated from the plant through a milling and grinding process. The granules are insoluble in cold water and must be heated above a critical temperature in order for the granules to swell and rupture, allowing the polymer to dissolve in solution.

[0062] Starch can be modified to provide specific properties of value in selected applications. This includes modification to either or both the physical and chemical structure of the material. Physical modification includes reduction in molecular weight, which is most often achieved by hydrolysis. Such modified materials are often referred to as derivatized starch or starch derivatives.

[0063] Chemical modifications include, but are not limited to, reactions that result in oxidized starches, such as by reaction with hypochlorite; reactions to form crosslinked starch, such as by using crosslinkers such as epichlorohydrin, sodium trimetaphosphate, isocyanates, or N,N-methylenebisacrylamide; reactions to form starch ester, such as by reaction with acetic acid or succinic anhydride; reactions to form hydroxyalkyl starches, such as by reaction with ethylene oxide or propylene oxide; reactions to form phosphate monoesters, such as by reaction with sodium tripolyphosphate; reactions to form cationic starch, such as by reaction with diethylamino ethyl chloride, tertiary amines and epichlorohydrin, or ethyleneamine; reactions to form dialdehyde starch, such as by acid oxidation, or starch xanthates; and the like. For the purposes of this invention, any type of chemically modified starch is contemplated to be useful.

[0064] Blends of cationic and anionic starches are useful in the present invention. Low charge starches are also useful in the present invention. [0065] The second component of the retention and drainage system can be added at amounts up to 20 Kg of active material per metric ton of cellulose pulp based on dry weight of the pulp, with the ratio of the associative polymer to second component being 1 :100 to 100:1. It is contemplated that more than one second component can be used in the papermaking system. [0066] Optionally siliceous materials can be used as an additional component of a retention and drainage aid used in making paper and paperboard. The siliceous material may be any of the materials selected from the group consisting of silica based particles, silica microgels, amorphous silica, colloidal silica, anionic colloidal silica, silica sols, silica gels, polysilicates, polysilicic acid, and the like. These materials are characterized by the high surface area, high charge density and submicron particle size. [0067] This group includes stable colloidal dispersion of spherical amorphous silica particles, referred to in the art as silica sols. The term sol refers to a stable colloidal dispersion of spherical amorphous particles. Silica gels are three dimensional silica aggregate chains, each comprising several amorphous silica sol particles, that can also be used in retention and drainage aid systems; the chains may be linear or branched. Silica sols and gels are prepared by polymerizing monomeric silicic acid into a cyclic structure that result in discrete amorphous silica sols of polysilicic acid. These silica sols can be reacted further to produce a three dimensional gell network. The various silica particles (sols, gels, etc.) can have an overall size of 5-50 nm. Anionic colloidal silica can also be used.

[0068] The siliceous material can be added to the cellulosic suspension in an amount of at least 0.005 Kg per metric ton based on dry weight of the cellulosic suspension. The amount of siliceous material may be as high at 50 Kg per metric ton. Preferably, the amount of siliceous material is from about 0.05 to about 25 Kg per metric ton. Even more preferably, the amount of siliceous material is from about 0.25 to about 5 Kg per metric ton based on the dry weight of the cellullosic suspension.

[0069] Optionally, an additional component of the retention and drainage aid system can be a conventional flocculant. A conventional flocculant is generally a linear cationic or anionic copolymer of acrylamide. The additional component of the retention and drainage system is added in conjunction with the aluminum compound and the associative polymer to provide a multi-component system which improves retention and drainage. [0070] The conventional flocculant can be an anionic, cationic or non-ionic polymer. The ionic monomers are most often used to make copolymers with a non-ionic monomer such as acrylamide. These polymers can be provided by a variety of synthetic processes including, but not limited to, suspension, dispersion and inverse emulsion polymerization. For the last process, a microemulsion may also be used.

[0071] The co-monomers of the conventional flocculant may be present in any ratio. The resultant copolymer can be non-ionic, cationic, anionic, or amphoteric (contains both cationic and anionic charge).

[0072] Yet other additional components that can be part of the inventive system are aluminum sources, such as alum (aluminum sulfate), polyaluminum sulfate, polyaluminum chloride and aluminum chlorohydrate. [0073] The components of a retention and drainage system may be added substantially simultaneously to the cellulosic suspension. The term retention and drainage system is used here to encompass two or more distinct materials added to the papermaking slurry to provide improved retention and drainage. For instance, the components may be added to the cellulosic suspension separately either at the same stage or dosing point or at different stages or dosing points. When the components of the inventive system are added simultaneously any two of more of the materials may be added as a blend. The mixture may be formed in-situ by combining the materials at the dosing point or in the feed line to the dosing . point. Alternatively the inventive system comprises a preformed blend of the materials. In an alternative form of the invention the components of the inventive system are added sequentially. A shear point may or may not be present between the addition points of the components. The components can be added in any order.

[0074] The inventive system is typically added to the paper process to affect retention and drainage. The inventive system may be added to the thick stock or thin stock, preferably the thin stock. The system may be added at one feed point, or may be split fed such that the inventive system is fed simultaneously to two or more separate feed points. Typical stock addition points include feed points(s) before the fan pump, after the fan pump and before the pressure screen, or after the pressure screen.

EXAMPLES

[0075] To evaluate the performance of the present invention, a series of drainage tests were conducted utilizing a synthetic alkaline furnish. This furnish is prepared from hardwood and softwood dried market lap pulps, and from water and further materials. First, the hardwood and softwood dried market lap pulp are refined separately. These pulps are then combined at a ratio of about 70 percent by weight of hardwood to about 30 percent by weight of softwood in an aqueous medium. The aqueous medium utilized in preparing the furnish comprises a mixture of local hard water and deionized water to a representative hardness. Inorganic salts are added in amounts so as to provide this medium with a total alkalinity of 75 ppm as CaCO₃ and hardness of 100 ppm as CaCU₃.. Precipitated calcium carbonate (PCC) is introduced into the pulp furnish at a representative weight percent to provide a final furnish containing 80% fiber and 20% PCC filler. The drainage tests were conducted by mixing the furnish with a mechanical mixer at a specified mixer speed, and introducing the various chemical components into the furnish and allowing the individual components to mix for a specified time prior to the addition of the next component. The specific chemical components and dosage levels are described in the data tables.

[0076] The drainage activity of the invention was determined utilizing a

Vacuum Drainage Test (VDT). The results of this testing demonstrate the ability of the VDT to differentiate drainage aids by the magnitude of the drainage time. The device setup is similar to the Buchner funnel test as described in various filtration reference books, for example see Perry's Chemical Engineers' Handbook, 7^th edition, (McGraw-Hill, New York, 1999) pp. 18-78. The VDT consists of a 300-ml magnetic Gelman filter funnel, a 250-ml graduated cylinder, a quick disconnect, a water trap, and a vacuum pump with a vacuum gauge and regulator. The VDT test is conducted by first setting the vacuum pump with a vacuum gauge and regulator. The VDT test is conducted by first setting the vacuum to the desired level, typically 10 inches Hg, and placing the funnel properly on the cylinder. Next, 25Og of 0.5% wt. % paper stock is charged into a beaker and then the required additives according to treatment program (e.g., starch, alum, and testing flocculants) are added to the stock under the agitation provided by an overhead mixer. The stock is then poured into the filter funnel and the vacuum pump is turned on while simultaneously starting a stopwatch. The drainage efficacy is reported as the time, in seconds, required to obtain 230 ml of filtrate. Lower quantitative drainage time values represent higher levels of drainage or dewatering, which is the desired response.

[0077] The starch materials utilized in the evaluation of the current invention are presented in Table 1. Stalok and lnterbond are trade names of A. E. Staley (Decatur, IL); Cato, Microcat, and Optiplus are trade names of National Starch and Chemical (Bridgewater, NJ). The evaluated starches are described in the table by product designation and starch type or source,. [0078] The starch materials used for evaluation in the present invention are listed in table 1.

TABLE 1

Starch Type

Stalok 400 Potato

Stalok 430 Potato

Stalok 410 Potato

Stalok 300 Dent corn

Stalok 310 Dent corn

Stalok 120 Waxy maize

Stalok 160 Waxy maize

Stalok 180 Waxy maize

Microcat 110 Waxy maize

Microcat 350 Tapioca lnterbond C Dent corn

Cato 235 Waxy maize

Cato 232 Waxy maize

Cato 237 Waxy maize

Cato 247 Waxy maize

Cato 245 Waxy maize

Cato 255 Waxy maize

Optiplus 1030 Waxy maize

Optiplus 1045 Waxy maize

[0079] The drainage activity of the present invention is demonstrated in

Table 2. The additive(s) of interest, as noted in the tables, are added sequentially to the furnish as Kilograms (Kg) of additive per metric ton (MT) of paper furnish (dry basis). The following materials are used in the examples provided in the tables. Alum is aluminum sulfate octadecahydrate as a 50% solution (Delta Chemical Corporation, Baltimore, MD). SP 9232 is PerForm® SP9232, a retention and drainage aid produced under certain conditions (see PCT WO 03/050152 A1), PC8138 is PerForm® PC8138, a cationic copolymer of polyacrylamide, PA8137 is PerForm® PA8137, an anionic copolymer of acrylamide. PerForm is a trade name of Hercules Incorporated, Wilmington, DE

TABLE 2

JN # Starch Starch Alum Additive #3 Kg/MT Additive Kg/MT VDT,

Dose, kg/MT (active) #4 (active)

Kg/MT

1 None 1.25 PA 8137 0.1 SP 9232 0.2 54.9

2 Stalok 400 9 1.25 PA 8137 0.1 SP 9232 0.2 27.9

3 Stalok 430 9 1.25 PA 8137 0.1 SP 9232 0.2 31.9

4 Stalok 410 9 1.25 PA 8137 0.1 SP 9232 0.2 28

5 Stalok 300 9 1.25 PA 8137 0.1 SP 9232 0.2 29.1

6 Stalok 310 9 1.25 PA 8137 0.1 SP 9232 0.2 29.3

7 Stalok 120 9 1.25 PA 8137 0.1 SP 9232 0.2 28.2

8 Stalok 160 9 1.25 PA 8137 0.1 SP 9232 0.2 28.5

9 Stalok 180 9 1.25 PA 8137 0.1 SP 9232 0.2 27.7

10 Microcat 110 9 1.25 PA 8137 0.1 SP 9232 0.2 27.1

11 Microcat 350 9 1.25 PA 8137 0.1 SP 9232 0.2 29.1

12 lnterbond C 9 1.25 PA 8137 0.1 SP 9232 0.2 31.8

13 Cato 235 9 1.25 PA 8137 0.1 SP 9232 0.2 29.2

14 Cato 232 9 1.25 PA 8137 0.1 SP 9232 0.2 29.2

15 Cato 237 9 1.25 PA 8137 0.1 SP 9232 0.2 28

16 Cato 247 9 1.25 PA 8137 0.1 SP 9232 0.2 29.4

17 Cato 245 9 . 1.25 PA 8137 0.1 SP 9232 0.2 27.4

18 Cato 255 9 1.25 PA 8137 0.1 SP 9232 0.2 28.2

19 Optiplus 1030 9 1.25 PA 8137 0.1 SP 9232 0.2 29.7

20 Optiplus 1045 9 1.25 PA 8137 0.1 SP 9232 0.2 28.5

21 None 1.25 PC 8138 0.15 SP 9232 0.2 36.9

22 Stalok 400 9 1.25 PC 8138 0.15 SP 9232 0.2 31.4

23 Stalok 430 9 1.25 PC 8138 0.15 SP 9232 0.2 31.3

24 Stalok 410 9 1.25 PC 8138 0.15 SP 9232 0.2 31.8

25 Stalok 300 9 1.25 PC 8138 0.15 SP 9232 0.2 31.2

26 Stalok 310 9 1.25 PC 8138 0.15 SP 9232 0.2 31.6

27 Stalok 120 9 1.25 PC 8138 0.15 SP 9232 0.2 31.2

28 Stalok 160 9 1.25 PC 8138 0.15 SP 9232 0.2 31.6

29 Stalok 180 9 1.25 PC 8138 0.15 SP 9232 0.2 31.4

30 Microcat 110 9 1.25 PC 8138 0.15 SP 9232 0.2 27.3

31 Microcat 350 9 1.25 PC 8138 0.15 SP 9232 0.2 28.7

32 lnterbond C 9 1.25 PC 8138 0.15 SP 9232 0.2 31.9

33 Cato 235 9 1.25 PC 8138 0.15 SP 9232 0.2 31.9

34 Cato 232 9 1.25 PC 8138 0.15 SP 9232 0.2 32.4

35 Cato 237 9 1.25 PC 8138 0.15 SP 9232 0.2 31.9

36 Cato 247 9 1.25 PC 8138 0.15 SP 9232 0.2 31

37 Cato 245 9 1.25 PC 8138 0.15 SP 9232 0.2 29.2

38 Cato 255 9 1.25 PC 8138 0.15 SP 9232 0.2 30.6

39 Optiplus 1030 9 1.25 PC 8138 0.15 SP 9232 0.2 31.8

40 Optiplus 1045 9 1.25 PC 8138 0.15 SP 9232 0.2 30.4

[0080] The data in table 2 demonstrate that synergistic combination of the associative polymer and starch or starch derivatives. In addition, the data indicate that low charge waxy maize starches and blends of starch consisting of cationic and anionic starches are preferred.

Claims

CLAIMS:

1. A method of improving retention and drainage in a papermaking process wherein the improvement comprising adding to a papermaking slurry, an associative polymer and at least one starch or starch derivative, wherein the associative polymer comprising the formula:

wherein B is a nonionic polymer segment comprising one or more ethylenically unsaturated nonionic monomers; F is an polymer segment comprising at least one ethylenically unsaturated anionic or cationic monomer; and the molar percent ratio of B:F is 99:1 to 1 :99 and wherein the associative polymer has associative properties provided by an effective amount of at least emulsification surfactant chosen from diblock or triblock polymeric surfactants, and wherein the amount of the at least one diblock or triblock surfactant to monomer is at least about 3:10, wherein the at least one starch or starch derivative is selected from the groups consisting of derivatized starches containing a nitrogen content less than about 0.15% or a blend of cationic and anionic starches.

2. The method of claim 1 wherein the at least one starch or starch derivative comprises a least one of potato starch; corn starch; wheat starch; tapioca starch; rice starch; derivatives thereof and combinations thereof.

3. The method of claim 1 wherein the at least one starch derivative comprises a least one of oxidized starches, crosslinked starch, esterified starches, alkylated starches, cationic starches, dialdehyde starches and combinations thereof.

4. The method of claim 1 wherein the at least one starch derivative comprises a least one physically modified starch.

5. The method of claim 1 further comprising adding a siliceous material.

6. The method of claim 5 wherein the siliceous material is selected from the group consisting of silica based particles, silica microgels, amorphous silica, colloidal silica, anionic colloidal silica, silica sols, silica gels, polysilicates, polysilicic acid, and combinations thereof.

7. The method of claim 1 wherein the at least one starch or derivatized starch and associative polymer are added to the papermaking slurry as a blend, simultaneously or sequentially.

8. The method of claim 1 wherein the associative polymer is anionic.

9. The method of claim 8 wherein associative polymer comprises acrylamide and the anionic monomer comprises a free acid or salt of acrylic acid.

10. The method of claim 1 wherein the associative polymer is cationic.

11. The method of claim 1 wherein the associative polymer comprises both anionic and cationic monomers.

12. A composition comprising an associative polymer and at least one starch or starch derivative wherein the associative polymer comprising the formula:

fB-co-F-] (I) wherein B is a nonionic polymer segment comprising one or more ethylenically unsaturated nonionic monomers; F is an polymer segment comprising at least one ethylenically unsaturated anionic or cationic monomer; and the molar percent ratio of B:F is 99:1 to 1:99 and wherein the associative polymer has associative properties provided by an effective amount of at least emulsification surfactant chosen from diblock or triblock polymeric surfactants, and wherein the amount of the at least one diblock or triblock surfactant to monomer is at least about 3:10., wherein the at least one starch or starch derivative is selected from the groups consisting of derivatized starches containing a nitrogen content less than about 0.15% or a blend of cationic and anionic starches.

13. The composition of claim 12 further comprising cellulosic fiber.

14. The composition of claim 12 wherein the at least one starch or starch derivative comprises at least one potato starch; corn starch; wheat starch;, tapioca starch; rice starch; derivative thereof or combinations thereof.

15. The composition of claim 12 wherein the at least one starch or starch derivative comprises a least one of oxidized starches, crosslinked starch, esterified starches, alkylated starches, catioinic starches, dialdehyde starches or combinations thereof.

16. The composition of claim 12 further comprising a siliceous material.