WO2008079549A2 - Polymer coating for medical devices - Google Patents
Polymer coating for medical devices Download PDFInfo
- Publication number
- WO2008079549A2 WO2008079549A2 PCT/US2007/084948 US2007084948W WO2008079549A2 WO 2008079549 A2 WO2008079549 A2 WO 2008079549A2 US 2007084948 W US2007084948 W US 2007084948W WO 2008079549 A2 WO2008079549 A2 WO 2008079549A2
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- polymer
- composition
- layer
- group
- polymer layer
- Prior art date
Abstract
Description
Claims