WO2011063422A1 - Ceramic composite materials containing carbon nanotube-infused fiber materials and methods for production thereof - Google Patents
Ceramic composite materials containing carbon nanotube-infused fiber materials and methods for production thereof Download PDFInfo
- Publication number
- WO2011063422A1 WO2011063422A1 PCT/US2010/057916 US2010057916W WO2011063422A1 WO 2011063422 A1 WO2011063422 A1 WO 2011063422A1 US 2010057916 W US2010057916 W US 2010057916W WO 2011063422 A1 WO2011063422 A1 WO 2011063422A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- fiber material
- carbon nanotube
- fibers
- carbon
- infused
- Prior art date
Abstract
Description
Claims