WO2012039883A1 - Expandable functional tfe copolymer fine powder, the expanded functional products obtained therefrom and reaction of the expanded products - Google Patents
Expandable functional tfe copolymer fine powder, the expanded functional products obtained therefrom and reaction of the expanded products Download PDFInfo
- Publication number
- WO2012039883A1 WO2012039883A1 PCT/US2011/049058 US2011049058W WO2012039883A1 WO 2012039883 A1 WO2012039883 A1 WO 2012039883A1 US 2011049058 W US2011049058 W US 2011049058W WO 2012039883 A1 WO2012039883 A1 WO 2012039883A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- functional
- tfe
- expanded
- tfe copolymer
- polymer
- Prior art date
Abstract
Description
Claims