WO2012040104A2 - Lithium titanate cell with reduced gassing - Google Patents
Lithium titanate cell with reduced gassing Download PDFInfo
- Publication number
- WO2012040104A2 WO2012040104A2 PCT/US2011/052142 US2011052142W WO2012040104A2 WO 2012040104 A2 WO2012040104 A2 WO 2012040104A2 US 2011052142 W US2011052142 W US 2011052142W WO 2012040104 A2 WO2012040104 A2 WO 2012040104A2
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- lithium
- negative electrode
- electrolyte
- lithium titanate
- additive
- Prior art date
Abstract
Description
Claims